TY - CONF A1 - Babutzka, Martin A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - Stainless steels: Fundamentals and causes for corrosion defects N2 - The presentation gives an overview about the fundamentals on stainless steels. The mechanism of passive layer formation is explained and strategies for securing corrosion protection are given. The influence of a grinding process on corrosion resistance is discussed. T2 - Tech-Day Mettler Toledo CY - Online meeting DA - 23.11.2022 KW - Corrosion KW - Stainless steel KW - Grinding KW - KorroPad KW - Surface PY - 2022 AN - OPUS4-56370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des Programms WIPANO sowie aktueller Projektskizzen der BAM im Fachbereich 7.6 N2 - Der Vortrag erläutert die Förderschwerpunkte der Förderinitiative WIPANO des BMWi und zeigt aktuelle Projektskizzen sowie Projekte des Fachbereiches 7.6. T2 - Arbeitskreissitzung „Korrosionsuntersuchung und -überwachung“ des GfKORR e. V. CY - Berlin, Germany DA - 08.10.2018 KW - Korrosion KW - Corrosion KW - Zink KW - Spannstahl KW - KorroPad PY - 2018 AN - OPUS4-46379 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Reinemann, Steffi A1 - Lehmann, Jens A1 - Babutzka, Martin A1 - Rosemann, Paul T1 - Optimierung industrieller Korund-Schleifprozesse zur Sicherstellung der Korrosionsbeständigkeit nichtrostender Stähle N2 - In diesem Vortrag werden Ergebnisse des gleichnamigen AiF Forschungsvorhabens gezeigt, die einen deutlichen Einfluss verschiedener Schleifmittel auf die Korrosionsbeständigkeit von damit geschliffenen nichtrostender Stahloberflächen belegen. Es konnten ein signifikanter Einfluss durch die Verwendung von Granulatschleifbändern festgestellt werden, der die Korrosionsbeständigkeit der Oberflächen drastisch reduziert. Grund sind auf der Oberfläche zurückbleibende Materialaufplattungen von Eigenmaterial aus dem Schleifprozess. Es wurden unterschiedliche Korrosionsuntersuchungen durchgeführt und mittels Oberflächenanalytik untermauert. T2 - ISER Kursleiter-Fortbildungsseminar 2018 CY - Aurich, Germany DA - 24.09.2018 KW - Nichtrostender Stahl KW - KorroPad KW - Schleifen KW - Korund PY - 2018 AN - OPUS4-46067 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Rosemann, Paul A1 - Lehmann, Jens A1 - Baumann, O. T1 - Einfluss der Oberflächennachbearbeitung auf die Korrosionsbeständigkeit von Schweißnähten und erfolgreiche Anwendung der KorroPad Prüfung N2 - Anlauffarben, die beim Schweißprozess entehen machen den nichtrostenden Stahl korrosionsanfällig und müssen entfernt werden. Dafür haben sich in der Praxis unterschiedliche Methoden etabliert. Im Vortrag werden verschiedene Nachbehandlungsverfahren verglichen. Die erreichte Korrosionsbeständigkeit wird mit verschiedenen Methoden bestimmt und die Ergebnisse gegenübergestellt. T2 - Praktiker-Tagung im Metallhandwerk CY - Kaiserslautern, Germany DA - 14.11.2018 KW - Korrosion KW - Schweißnahtnachbearbeitung KW - KorroPad KW - Schweißnaht KW - Nichtrostender Stahl PY - 2018 AN - OPUS4-46830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas A1 - Lehmann, Jens T1 - Einfach und echt schnell - Der KorroPad Test N2 - In diesem dritten Teil wird die KorroPad Prüfmethode vorgestellt und erläutert. T2 - ISER Kursleiterfortbildung 2022 CY - Düsseldorf, Germany DA - 26.09.2022 KW - Korrosion KW - nichtrostender Stahl KW - KorroPad KW - Korrosionsprüfung KW - Schnelltest PY - 2022 AN - OPUS4-55858 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dieck, S. A1 - Ecke, M. A1 - Rosemann, Paul A1 - Halle, T. T1 - Reversed austenite for enhancing ductility of martensitic stainless steel N2 - Quenching and partitioning (Q&P) heat Treatment increases the deformability of high-strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP effect). The austenitic-martensitic microstructure is gained by an increased austenitization temperature, water quenching and additional partitioning. The partitioning enables local carbon diffusion, which stabilizes retained austenite and leads to partial reversion of martensite to austenite. The influence of partitioning time was studied for the martensitic stainless steel AISI 420 (X46Cr13, 1.4034). In line with these efforts, metallographic, XRD and EBSD measurements were performed to characterize the microstructural evolution. The mechanical properties were tested using tension and compression loading. Additional corrosion investigations showed the benefits of Q&P heat treatment compared to conventional tempering. The reversion of austenite by the partitioning treatment was verified with EBSD and XRD. Furthermore, the results of the mechanical and corrosion testing showed improved properties due to the Q&P heat treatment. T2 - International Conference on Martensitic Transformations CY - Chicago, IL, USA DA - 09.07.2017 KW - Heat treatment KW - High ductility KW - Martensitic stainless steels KW - Quenching and partitioning KW - Transformation induced plasticity KW - KorroPad KW - EBSD KW - Mechanical testing PY - 2018 SN - 978-3-319-76968-4 U6 - https://doi.org/10.1007/978-3-319-76968-4_19 SP - 123 EP - 128 PB - Springer AN - OPUS4-44689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dieck, S. A1 - Ecke, M. A1 - Rosemann, Paul A1 - Halle, T. T1 - Enhanced properties of martensitic stainless steel due to austenite reversion N2 - The novel heat treatment concept of “Quenching and Partitioning” (Q&P) enables producing low alloyed martensitic steels with high strength and formability. Therefore austenite, retaining from a quenching temperature between Mf and Ms, is stabilised by carbon diffusion. This stabilised austenite transforms in martensite (TRIP effect) under mechanical loading. Current investigations on the Q&P heat treatment of martensitic stainless steels reveal a further enhancement of mechanical properties due to higher amounts of austenite. Thus a tensile strength of 1.800 MPa and a maximum elongation of 20 % are possible, while mechanical properties under compression are much higher due to a distinct SD effect. The presentation aims to gain a further understanding of the Q&P heat treatment and the resulting mechanical properties for the steel X46Cr13, especially the mechanical behaviour under dynamic mechanical loading condition. Results of drop work and Split Hopkinson Pressure Bar test confirms the findings of quasi static compression test. Furthermore, Charpy impact tests show higher impact toughness compared to the common heat treatment of quenching and tempering (Q&T). Complementary investigations indicate a higher corrosion resistance of Q&P compared to Q&T. T2 - 12th International Nordmetall Colloquium CY - Chemnitz, Germany DA - 05.12.2017 KW - Corrosion resistance KW - Heat treatment KW - Martensite KW - Quenching and partitioning KW - Stainless steel KW - KorroPad PY - 2017 AN - OPUS4-43339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dieck, S. A1 - Ecke, M. A1 - Rosemann, Paul A1 - Halle, T. T1 - Verbesserung der Eigenschaften vom martensitischen, nichtrostenden Stahl X46Cr13 durch Q&P-Wärmebehandlung N2 - Das innovative Wärmebehandlungskonzept des „Quenching and Partitioning“ (Q&P) ermöglicht die Herstellung hochfester, martensitischer Stähle mit hoher Verformbarkeit und Duktilität. Dabei wird Restaustenit im Prozessabschnitt des Partitionierens durch Kohlenstoffdiffusion stabilisiert. Dies ermöglicht die dehnungsinduzierte Phasenumwandlung von Austenit in Martensit und erhöht die Verformbarkeit, ohne dabei die Festigkeit zu reduzieren. Bisher wenig erforscht ist die Anwendung des Q&P-Prozesses bei korrosionsbeständigen Stählen. Die vorliegende Arbeit ergänzt erste Untersuchungen von YUANG und RAABE um wichtige werkstofftechnische Kennwerte sowie um die erreichbare Korrosionsbeständigkeit. Es konnte gezeigt werden, dass im Vergleich zur standardmäßig angewandten Wärmebehandlung die mechanischen und korrosiven Eigenschaften enorm durch den Q&P-Prozess gesteigert werden. T2 - Sommerkurs Werkstoffe und Fügen am Institut für Werkstoff- und Fügetechnik CY - Magdeburg, Germany DA - 08.09.2017 KW - Martensitischer nichtrostender Stahl KW - Wärmebehandlung KW - Q+P KW - Korrosion KW - KorroPad PY - 2017 SN - 978-3-944722-58-0 U6 - https://doi.org/10.24352/UB.OVGU-2017-75 SP - 95 EP - 104 AN - OPUS4-41892 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Heyn, A. A1 - Rosemann, Paul T1 - How to Detect Sensitivity on Aged Lean-Duplex Stainless Steel With Electrochemical Methods N2 - The influence of isothermal ageing on microstructure, sensitisation and pitting corrosion resistance of the lean duplex stainless steel (LDSS) X2CrNiN23-4 was investigated with various electrochemical methods. The aging at 600 °C (from 0.1 h up to 20 h) lead to the formation of precipitations at the ferrite-ferrite (α/α) and ferrite-austenite (α/γ) grain boundaries, inducing sensitisation due to chromium depletion. The degree of sensitisation was evaluated with the double loop electrochemical potentiokinetic reactivation method (DL-EPR) according to ASTM G108 and correlated with critical pitting potentials (Epit) as well as critical pitting temperature (CPT) measured in an electrolyte according to ASTM G48 using electrochemical noise. Up to an ageing time of 1 h, the sensitisation did rise significantly, stabilising at a nearly constant level with a slight drop at 20 h. This behaviour correlated perfectly with the potentiodynamically determined pitting potentials Epit and sensitisation. The CPT showed a higher sensitivity at short ageing times compared to the DL-EPR and Epit. Finally, the KorroPad method was applied to visualise the sensitisation induced reduction of pitting corrosion resistance. The “KorroPad” is an agar-based gel-electrolyte containing 0.1 mol/l sodium chloride (NaCl) and 0.1 mol/l potassium ferricyanide III (K3[Fe(CN)6]), invented at the Federal Institute of Materials Research and Testing in Berlin (Germany) to detect surfaces of stainless steel prone to pitting corrosion. The standard configuration of the KorroPad showed no differentiation for the various aging conditions. Increasing the concentration of both NaCl and potassium ferrocyanide III to 0.5 M shifts the detection limit of the KorroPad method to stainless steels with higher corrosion resistance, producing the same trends detected by standard electrochemical pitting corrosion values (Epit, CPT) and sensitisation (DL-EPR). By that, the KorroPad method was successfully adjusted to the lean-duplex stainless steel X2CrNiN23-4, enabling short-time testing to detect sensitization. T2 - Electrochemical Methods in Corrosion Research 2018 CY - Cambridge, UK DA - 22.07.2018 KW - Corrosion testing KW - Duplex stainless steels KW - Corrosion KW - KorroPad KW - Pitting corrosion KW - EPR KW - Electrochemical noise KW - Stainless steel PY - 2018 AN - OPUS4-45615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kauss, N. A1 - Rosemann, Paul T1 - Sensibilisierungsverhalten vom nichtrostenden Lean-Duplexstahl 1.4062 N2 - Der nichtrostende Lean-Duplexstahl 1.4062 (X2CrNiN22-2) verbindet die hohe Festigkeit des Ferrits mit der Duktilität und Zähigkeit des Austenits in einem zweiphasigen Gefüge mit sehr hoher Korrosionsbeständigkeit. Die höchste Korrosionsbeständigkeit wird erreicht, wenn das ferritisch-austenitische Gefüge frei von weiteren Sekundärphasen ist. Dies wird durch ein gezieltes Lösungsglühen bei 1050 °C mit anschließender Abschreckung in Wasser erreicht. Durch thermische Beeinflussung (z.B. beim Schweißen) können Sekundärphasen ausgeschieden und die Korrosionsbeständigkeit des Werkstoffs gesenkt werden. Dies wurde durch eine isotherme Warmauslagerung bei 500 °C bis 900 °C für 0,1 h bis zu 72 h simuliert. Die Veränderung der Korrosionsbeständigkeit wurde mit dem DL-EPR-Verfahren und durch die angepasste KorroPad-Prüfung ermittelt. Die ermittelten Anfälligkeitsbereiche wurden miteinander Verglichen und in zwei Sensibilisierungsschaubildern zusammengefasst. T2 - GfKORR-Jahrestagung CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Duplexstahl KW - Nichtrostender Stahl KW - Wärmebehandlung KW - Korrosion KW - EPR KW - KorroPad KW - Sensibilisierung PY - 2017 AN - OPUS4-42834 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -