TY - JOUR A1 - Pirskawetz, Stephan T1 - The burned shield-bearers: a detective story N2 - Severe fires at the Friedrichshain flak bunker in May 1945 destroyed or severely damaged an important part of the collection of the Kaiser-Friedrich-Museum, Berlin, today’s Bode Museum. Fragments of two marble sculptures by Tullio Lombardo, sculptor of the Italian renaissance, have survived and are now stored in the Bode Museum. In preparation for restoration, the condition of the sculptures has been documented in detail in 2010. The study revealed that the fragments are not stable enough to exhibit them in a horizontal nor in an upright position. The intention of a further study in 2012 was to find a correlation between ultrasonic velocity and mechanical properties of burned Carrara marble as a basis for stabilization measures. The results and numerous supplementary experiments show that the current condition of the sculptural fragments can not only be explained by the exposure to fire. KW - Marble sculptures KW - Marble deterioration KW - Fire KW - Ultrasonic velocities KW - Mechanical properties PY - 2018 U6 - https://doi.org/10.1007/s12665-018-7267-z SN - 1866-6280 SN - 1866-6299 VL - 77 IS - 4 SP - Article 130, 1 EP - 12 PB - Springer-Verlag GmbH CY - Berlin Heidelberg AN - OPUS4-44159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Sklorz, Christian T1 - Testing of pressurized vessels N2 - The results are based on data1. Figure 3 displays temperatures of the tank wall and of the gas phase over testing time. It can be seen that a complete coating strongly delayed the heating of tank wall and gas phase, whereas the partly coated tanks only had a minor influence on temperature development. There was no significant difference between a half coated and a thirdly coated tank measurable. Figure 4 shows the internal pressure of tanks over testing time. Only the fully coated tank enabled a low pressure over 90 min testing time. Hence, a complete coating is necessary to guarantee the fire safety of hazmat tanks and a partly coating is not sufficient. T2 - Annual Conference on Engineering and Information Technology CY - Nagoya - Japan DA - 29.03.2017 KW - Fire KW - Testing KW - Vessels KW - Dangerous goods PY - 2017 AN - OPUS4-39843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Powierza, Bartosz A1 - Weise, Frank A1 - Oesch, Tyler A1 - Dlugosch, R. A1 - Meng, Birgit T1 - Analysis of moisture transport in unilateral-heated dense high-strength concrete N2 - Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure. However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process. In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes. In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content. Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis. T2 - 5th International Workshop on Concrete Spalling due to Fire Exposure CY - Boras, Sweden DA - 12.10.2017 KW - Spalling KW - Fire KW - Moisture clog KW - Moisture transport KW - HPC KW - HSC KW - X-ray CT KW - NMR KW - NDT PY - 2017 AN - OPUS4-42972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Powierza, Bartosz A1 - Stelzner, Ludwig A1 - Oesch, Tyler A1 - Weise, Frank A1 - Bruno, Giovanni T1 - In-situ CT observation of water migration in heated concrete N2 - In order to study damage in concrete exposed to fire, a series of continuous X-ray computed tomography (CT) measurements were performed on a concrete sample heated, in-situ, on one side. The water migration relative to time and 3D space and, in particular, the dynamic condensation and vaporization of water droplets in the pores was quantified. This approach shows significant potential for further investigation of fire-related concrete damage. T2 - 3rd International Conference on Tomography of Materials and Structures CY - Lund, Sweden DA - 26.06.2017 KW - In-situ KW - X-ray CT KW - Heated concrete KW - Pores KW - Water migration KW - Fire PY - 2017 UR - http://meetingorganizer.copernicus.org/ICTMS2017/ICTMS2017-29.pdf AN - OPUS4-43062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stelzner, Ludwig A1 - Powierza, Bartosz A1 - Weise, Frank A1 - Oesch, Tyler A1 - Dlugosch, R. A1 - Meng, Birgit T1 - Analysis of moisture transport in unilateral-heated dense high-strength concrete N2 - Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure. However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process. In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes. In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content. Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis. T2 - 5th International Workshop on Concrete Spalling due to Fire Exposure CY - Boras, Sweden DA - 12.10.2017 KW - Spalling KW - Fire KW - Moisture clog KW - Moisture transport KW - HPC KW - HSC KW - X-ray CT KW - NMR KW - NDT PY - 2017 SN - 0284-5172 SP - 227 EP - 239 AN - OPUS4-42983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Otremba, Frank A1 - Bradley, Ian T1 - Pressure vessel subjected by fire N2 - Test facilities at BAM, Types of fire test, Vessel testing, Modelling of vessel response to fire, Current research, Future research T2 - COTEQ 2017 CY - Rio de Janeiro, Brazil DA - 15.05.2017 KW - Vessels KW - Fire KW - Modelling PY - 2017 AN - OPUS4-40307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oesch, Tyler A1 - Stelzner, Ludwig A1 - Weise, Frank T1 - Non-destructive evaluation of the contribution of polymer-fiber orientation and distribution characteristics to concrete performance during fire N2 - Although concrete itself is not a combustible material, concrete mixtures with high density, such has high-performance concretes (HPCs), are susceptible to significant damage during fires due to explosive spalling. Past research has shown that the inclusion of polymer fibers in high density concrete can significantly mitigate fire damage due to the contribution of the fibers to increased permeability levels at high temperature. This allows vapor pressures caused by the evaporation of internal water during fire to escape from the material without causing significant spalling. Recent microscopic investigations have also shown that the addition of polypropylene (PP) fibers to high-density HPC with a high amount of fine-aggregate has a considerable influence on the nature and character of crack formation due to autogenous shrinkage. Initial cracks, which originate from the fiber beds, undergo further expansion and propagation when concrete is subjected to thermal exposure in excess of 170 °C. It is thus of interest to determine whether the resulting cracks join the adjacent fiber beds and therefore contribute to a significant increase in the permeability of the concrete, which is directly correlated to lower pore pressures and reduced spalling during fire. In this study, X-ray Computed Tomography (CT) was applied to provide a clear demonstration of the interaction between polymer fibers and cracking during thermal exposure. For this purpose, two concrete samples containing different polymer fiber types were subjected to incremental application of a defined thermal exposure. CT images were acquired before and after each thermal exposure and powerful image processing tools were used to segment the various material components, such as polymer fibers, cracks, aggregates and cement matrix, in each image. This enabled a detailed analysis of crack formation and propagation as well as the visualization and quantification of polymer fiber characteristics within the concrete. This paper will provide a description of the distribution and orientation characteristics of the polymer fibers within each sample obtained through the CT-based analysis. Using these results, the impact of fiber distribution and orientation characteristics on actual cracking geometries have been measured and visualized. This paper will also provide recommendations for further optimization of the selected materials and propose improved methods for future CT-based analysis techniques. T2 - European Mechanics Society Colloquium 582: Short Fibre Reinforced Cementitious Composites and Ceramics CY - Tallinn, Estonia DA - 20.03.2017 KW - High-performance concrete KW - X-ray computed tomography KW - Polypropylene fibers KW - Fire KW - Orientation PY - 2017 AN - OPUS4-39649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Powierza, Bartosz A1 - Stelzner, Ludwig A1 - Oesch, Tyler A1 - Gollwitzer, Christian A1 - Weise, Frank A1 - Bruno, Giovanni T1 - Water migration in one-side heated concrete: 4D in-situ CT monitoring of the moisture-clog-effect N2 - Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water Migration in concrete due to surface heating was undertaken. During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based Image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials. T2 - 8th Conference on Industrial Computed Tomography (iCT 2018) CY - Wels, Austria DA - 06.02.2018 KW - In-Situ X-ray CT KW - Digital Volume Correlation KW - Heated concrete KW - Water migration KW - Fire PY - 2019 U6 - https://doi.org/10.1007/s10921-018-0552-7 SN - 1573-4862 SN - 0195-9298 VL - 38 IS - 1 SP - 15, 1 EP - 11 PB - Springer US CY - New York / Heidelberg AN - OPUS4-47147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Souza, Roberto A1 - Knaust, Christian A1 - Andreini, M. A1 - La Mendola, S. T1 - Probability Distribution Sensitivity on the Thermo-Mechanical FEM of a Concrete Tunnel Exposed to Fire N2 - A probabilistic approach for finite element analysis (FEA) for tunnel linings exposed to the nominal fire is presented. The probabilistic FEA accounted for the uncertainties distributions tied to the conductivity and specific heat as well as of the compressive strength, tensile strength, Young’s modulus, and ultimate strain in compression. To get an understanding on the influence of different probability density functions on the distribution of maximum displacements of the tunnel lining, a sensitivity analysis was performed. Four sets of FEAs were carried out with different probability distributions of the conductivity, the specific heat, and the compressive strength of the concrete, respectively. An experimental design based on a Latin Hypercube Sampling algorithm was performed to define the input parameters which describe each analysis case. A reliability analysis was executed considering a limit state function based on the temperature-dependent ultimate strain. The results show that, depending on the distribution adopted, the standard deviation of the maximum displacements can vary up to 47,4% of the minimum standard deviation. The large standard deviation is associated with the possibility of a greater displacement and, hence, to a structure more vulnerable to fire. T2 - 4th Symposium Structural Fire Engineering Braunschweig CY - Brunswick, Germany DA - 12.09.2017 KW - Probabilistic analysis KW - Fire KW - Concrete KW - Finite elements analysis PY - 2017 SP - 1 EP - 13 AN - OPUS4-42681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Powierza, Bartosz A1 - Stelzner, Ludwig A1 - Oesch, Tyler A1 - Weise, Frank A1 - Bruno, Giovanni T1 - Water Migration in One-Side Heated Concrete: 4D In-Situ CT Monitoring of the Moisture-Clog-Effect N2 - In order to study damage in concrete exposed to fire, a series of continuous X-ray computed tomography (CT) measurements were performed on a concrete sample heated, in-situ, on one side. The water migration relative to time and 3D space and, in particular, the dynamic condensation and vaporization of water droplets in the pores was quantified. This approach shows significant potential for further investigation of fire-related concrete damage. T2 - 8th Conference on Industrial Computed Tomography (iCT 2018) CY - Wels, Austria DA - 06.02.2018 KW - CT KW - X-ray KW - In-Situ KW - Pores KW - Heated Concrete KW - Water Migration KW - Fire PY - 2018 AN - OPUS4-46381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -