TY - CONF A1 - Lin, Xuebao A1 - Tan, Yi A1 - Wachtendorf, Volker A1 - Klack, Patrick A1 - Schoch, R. A1 - Lang, M. A1 - Schartel, Bernhard T1 - Weathering Resistance of Halogen-free Flame Retardance in E&E Polymeric Materials N2 - Nowadays, various polymeric materials are used in E&E applications with sufficient flame retardance by adding rather different flame retardants. It doesn’t matter whether cables are used outdoor or are installed indoor as building products, the weathering exposures such as UV radiation, humidity and variation in temperature occur and influence the flame-retardant property. Recently, the lifetime of the flame retardance itself becomes an increasingly important factor. In this work, several devices were used to perform accelerated artificial ageing simulating different environment exposures. The comprehensive and global understanding of the durability of flame retardance in dependence on the weathering or ageing conditions is still a matter of discussion. Therefore, the weathering resistance of various halogen-free fire-retarded polymers was investigated in this work. Polymeric systems with different kinds of fire retardants were chosen, including various fire retardant mechanisms. Ethylene Vinyl Acetate (EVA) blends with high amounts of inorganic flame retardant such as aluminum hydroxide (ATH), boehmite and synergists, which mainly dilutes the polymer resin work as heat sink and cooling agent, and enhance residue formation was examined. Thermoplastic Polyurethane (TPU) was modified with melamine cyanurate (MC), which mainly acts by changed melt flow and dripping behavior as well as fuel dilution. Additionally, aluminum diethylphosphinate and boehmite are induced as assistant flame retardant. Furthermore, glass fiber reinforced Polyamide 66 (PA) was investigated containing different kinds of aluminum diethylphosphinate based flame retardant mixtures, which acts by flame inhibition and additional char formation. The degradation of the surface was analyzed after the different weathering conditions. Most of the specimens exhibited an intensive material degradation at the top surface accompanied by a distinct discoloration, e.g. getting darker or showing yellowing. The weathering of the EVA samples lead to numerous cracks (already) after 4000 h. The corresponding changes in the chemical structure was investigated by ATR FT-IR for all materials. The flammability was investigated by cone calorimeter, UL-94 burning chamber, and oxygen index (LOI) using plate and bar specimens. The flame retardance of most of the materials studied degrades only slightly or were rather stable for the investigated exposure times. Interestingly, also some opposite results were found. EVA modified by different inorganic flame retardants such as ATH achieved higher LOI after exposing in the humidity chamber and the accelerated oxidation under water in the autoclaves. It is suggested that the particle size of ATH and boehmite plays an important role, when these flame retardants agglomerate at the surface during accelerated weathering. Both materials, EVA and TPU, were also investigated as cable jackets. While EVA modified with inorganic flame retardants exhibits low-smoke and non-dripping fire behavior, TPU flame-retarded with MC yields cables with pronounced melt-dripping. Cone calorimeter tests were carried out using cable rafts of the size of 100 mm * 100 mm as well as our self-made cable module test, which simulates the vertical full-scale test of a bundle of cables at the bench-scale. Both methods were used to investigate the weathering resistance of the flame retardance in cables. The results of the cable module test for the flame-retarded EVA cables were only slightly affected even when a long time hydrothermal ageing was carried out. This is because of inorganic residue which just delays the fire growth but does not extinguish. However, for the flame-retarded TPU cable jackets, the cable module test exhibited an accelerated fire spread and a melt-dripping behavior which was promoted by weathering exposure. T2 - FRPM 2019, 17th European Meeting on Fire Retardant Polymeric Materials CY - Turku, Finland DA - 26.06.2019 KW - Cable KW - Flame retardant KW - Weathering resistance KW - Durability KW - ethylene vinyl acetate KW - Thermoplastic polyurethane KW - Flammability PY - 2019 AN - OPUS4-48553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rabe, Sebastian A1 - Sánchez-Olivares, Guadalupe A1 - Schartel, Bernhard T1 - Rummaging through industrial waste: Natural fibers in flame retarded thermoplastic starch biocomposites N2 - Thermoplastic starch polymer blends as biodegradable materials are well known and used mainly as packaging material. In order to exploit new application fields for these materials, additional properties such as flame retardancy or increased mechanical strength are required. This work focuses on the flammability and fire behavior of a thermoplastic starch/polyester blend reinforced with natural fibers derived from Mexican industry processes wastes, such as keratin fibers from the tannery industry or coconut fibers[1]. Different fiber contents as well as combinations of varying contents of aluminum trihydroxide, expandable graphite or ammonium polyphosphate were tested in LOI, UL94, cone calorimeter and TG-FTIR in order to investigate and assess the concentration dependence of the fibers and flame retardants as well as synergistic effects between both components. In combination with ammonium polyphosphate, the coconut fibers induce a synergistic effect by reinforcing the char residue and creating a more stable heat barrier during forced flaming combustion in the cone calorimeter. Synergism is also observed in the oxygen test. The recycling of otherwise wasted material is a true challenge in material development, thus this work is a first step in the direction of sustainable and biodegradable materials. T2 - Second International Conference on ECO-friendly Flame Retardant Additives and Materials (ECOFRAM) CY - Metz, France DA - 28.03.2018 KW - Biocomposite KW - Natural fibres KW - Industry processes wastes KW - Flammability KW - Sustainable PY - 2018 AN - OPUS4-44658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -