TY - JOUR A1 - Bernardes, C. E. S. A1 - Feliciano, I.O. A1 - Naese, Christoph A1 - Emmerling, Franziska A1 - Minas da Piedade, M. T1 - Energetics of dehydroepiandrosterone polymorphs I and II from solution and drop-sublimation Calvet microcalorimetry measurements N2 - The lattice enthalpies and monotropic relationship of two dehydroepiandrosterone (DEHA) polymorphs (forms I and II) were evaluated through a combination of differential scanning calorimetry (DSC), isothermal solution microcalorimetry, and drop-sublimation Calvet microcalorimetry experiments. The standard molar enthalpy of transition between both forms was determined as ΔtrsHom (II→I, 298.15 K) = - 0.90 ± 0.07 kJ mol-1 and ΔtrsHom (II→I, 417.8 K) = - 1.7 ± 1.0 kJ mol- 1, from measurements of standard molar enthalpies of solution in dimethyl sulfoxide and enthalpies of fusion, respectively. Drop-sublimation Calvet microcalorimetry experiments on form I led to ΔsubHom (cr I, 298.15 K) = 132.0±3.3 kJ mol - 1. This result, when combined with the more precise ΔtrsHom (II→I) value obtained by solution calorimetry, afforded ΔsubHom (cr II, 298.15 K) = 131.1±3.3 kJ mol - 1. The overall data indicate that on enthalpic grounds form I is more stable than form II from 298.15 K up to fusion. This conclusion, and the fact that DSC experiments indicated that form I has also a considerably higher temperature fusion, namely, Tfus(cr I)= 422.5±0.2 K and Tfus(cr II) = 413.1±0.2 K, suggest that the two polymorphs are monotropically related. KW - Calorimetry KW - Polymorphism KW - Enthalpy of solution KW - Enthalpy of sublimation KW - Thermochemistry KW - Lattice enthalpy PY - 2023 DO - https://doi.org/10.1016/j.jct.2023.107137 SN - 0021-9614 SN - 1096-3626 VL - 186 SP - 1 EP - 7 PB - Elsevier AN - OPUS4-58418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bacurau, V. P. A1 - Moreira, P. A. F. P. A1 - Bertoli, G. A1 - Andreoli, A. F. A1 - Mazzer, E. A1 - de Assis, F. F. A1 - Gargarella, P. A1 - Koga, G. A1 - Stumpf, G. C. A1 - Figueroa, S. J. A. A1 - Widom, M. A1 - Kaufman, M. A1 - Fantin, Andrea A1 - Cao, Y. A1 - Freitas, R. A1 - Miracle, D. A1 - Coury, F. G. T1 - Comprehensive analysis of ordering in CoCrNi and CrNi2 alloys N2 - Chemical Short-Range Order (CSRO) has attracted recent attention from many researchers, creating intense debates about its impact on material properties. The challenges lie in confirming and quantifying CSRO, as its detection proves exceptionally demanding, contributing to conflicting data in the literature regarding its true effects on mechanical properties. Our work uses highprecision calorimetric data to unambiguously prove the existence and, coupled with atomistic simulations, quantify the type of CSRO. This methodology allows us to propose a mechanism for its formation and destruction based on the heat evolution during thermal analysis and facilitates a precise identification of local ordering in CoCrNi alloys. Samples of CoCrNi (Co33Cr33Ni33) and CrNi2 (Cr33Ni66) alloys are fabricated in varying ordered states, extensively characterized via synchrotron X-ray diffraction, X-ray absorption spectroscopy, and transmission electron microscopy. Samples with considerably different ordered states are submitted to tensile tests with in-situ synchrotron X-ray diffraction. We demonstrate, despite inducing varied CSRO levels in CoCrNi, no significant alterations in overall mechanical behavior emerge. However, the CrNi2 alloy, which undergoes long-range ordering, experiences significant shifts in yield strength, ultimate tensile stress and ductility. KW - Mechanical properties KW - Short-range ordering KW - Calorimetry PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611075 DO - https://doi.org/10.1038/s41467-024-52018-w VL - 15 IS - 1 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-61107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kossatz, Philipp A1 - Mezhov, Alexander A1 - Andresen, Elina A1 - Prinz, Carsten A1 - Schmidt, Wolfram A1 - Resch-Genger, Ute T1 - Assessing the Applicability of Lanthanide-Based Upconverting Nanoparticles for Optically Monitoring Cement Hydration and Tagging Building Materials N2 - Chemically stable, lanthanide-based photon upconversion micro- and nanoparticles (UCNPs) with their characteristic multicolor emission bands in the ultraviolet (UV), visible (vis), near-infrared (NIR), and short-wave infrared (SWIR) arepromising optical reporters and barcoding tags. To assess the applicability of UCNPs for the monitoring of early stage cement hydration processes and as authentication tags for cementitious materials, we screened the evolution of the luminescence of Selfmade core-only NaYF4:Yb,Er UCNPs and commercial μm-sized Y2O2S:Yb,Er particles during the first stages of cement hydration, which largely determines the future properties of the hardened material. Parameters explored from the UCNP side included particle size, morphology, surface chemistry or coating, luminescence properties, and concentration in different cement mixtures. From the cement side, the influence of the mineral composition of the cement matrix was representatively examined for ordinary Portland cement (OPC) and its constituents tricalcium aluminate (C3A), tricalcium silicate (C3S), and gypsum at different water to cement ratios. Based on reflection and luminescence measurements, enabling online monitoring, which were complemented by XRD and isothermal heat-flow calorimetric measurements to determine whether the incorporation of these particles could impair cement hydration processes, well suited lanthanide particle reporters could be identified as well as application conditions. In addition, thereby the reporter influence on cement hydration kinetics could be minimized while still preserving a high level of information content. The best performance for the luminescence probing of changes during early stage cement hydration processes was observed for 25 nm-sized oleate (OA)-coated UCNPs added in a concentration of 0.1 wt %. Higher UCNP amounts of 1.0 wt % delayed cement hydration processes size- and surface coatingspecifically in the first 24 h. Subsequent luminescence stability screening studies performed over a period of about one year support the applicability of UCNPs as optical authentication tags for construction materials. KW - Quality assurance KW - Fluorescence KW - Nano KW - Particle KW - Synthesis KW - Quantum yield KW - NIR KW - Mechanism KW - Characterization KW - XRD KW - Calorimetry KW - Advanced material KW - Cement KW - Monitoring KW - Surface KW - Size KW - Lifetime KW - Barcode KW - Lanthanide KW - Upconversion KW - Encoding KW - Method PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638318 DO - https://doi.org/10.1021/acsomega.5c02236 SN - 2470-1343 VL - 10 IS - 29 SP - 31587 EP - 31599 PB - ACS Publications CY - Washington, DC AN - OPUS4-63831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dudziak, Mateusz A1 - Riechers, Birte A1 - Maaß, Robert A1 - Michalchuk, Adam A1 - Schönhals, Andreas A1 - Szymoniak, Paulina T1 - Beyond conventional calorimetry: Unlocking thermal characterization with fast scanning techniques N2 - Fast scanning calorimetry (FSC) has emerged as a transformative technique in thermal analysis, enabling the investigation of rapid and kinetically driven thermal transitions that are inaccessible to conventional differential scanning calorimetry. This review highlights the capabilities enabled by FSC for studying a wide range of materials under extreme thermal conditions, including polymers, pharmaceuticals, metallic glasses, nanocomposites, and hydrogels. By employing ultrafast heating and cooling rates, FSC allows for the suppression of crystallization, resolution of weak transitions, and analysis of thermally labile or size-limited samples. The technique is particularly valuable for probing glass transitions, relaxation phenomena, and phase behavior in systems with complex morphologies or confined geometries. Case studies demonstrate the use of FSC in characterizing vitrification, physical aging, and interfacial dynamics, as well as its application in emerging fields such as additive manufacturing, supramolecular systems, and neuromorphic materials. Together, these examples underscore the role that FSC plays in advancing the understanding of structure-property relationships across diverse material classes. KW - Flash DSC KW - Calorimetry KW - Glass transition PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-647405 DO - https://doi.org/10.1016/j.tca.2025.180177 VL - 754 SP - 1 EP - 14 PB - Elsevier B.V. AN - OPUS4-64740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -