TY - JOUR A1 - Petrushin, N. V. A1 - Epishin, A. I. A1 - Svetlov, I. L. A1 - Nolze, Gert A1 - Elyutin, E. S. A1 - Solov'ev, A. E. T1 - Influence of the Sign of the γ/γ' Misfit on the Structure and Creep Strength of Single Crystals of Nickel-Based Superalloys N2 - Using the method of directional solidification, single crystals of experimental nickel-based superalloys with negative, zero, and positive γ/γ' misfits are obtained. The γ' solvus, solidus, and liquidus temperatures of the alloys are determined, and the microstructures of the alloys after directional solidification, heat treatment, and creep tests are investigated. Creep tests are performed at temperatures of 800 and 1000°C. It is found that single crystals of the alloy with a negative γ/γ' misfit have the highest creep resistance and lifetime (the crystal lattice period of the γ' phase is smaller than that of the γ matrix). KW - Nickel-based superalloys KW - Single crystal KW - Creep KW - Creep strength KW - Microstructure, γ/γ' misfit PY - 2023 DO - https://doi.org/10.1134/s207511332301029x SN - 2075-1133 VL - 14 IS - 1 SP - 13 EP - 22 AN - OPUS4-59505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Abel, Andreas T1 - Microstructural and mechanical characterisation of cast Fe-Al-Mo-Ti-B alloys N2 - With the advent of variable renewable energies, long-term energy storage capacities and flexible power generation technologies will be required for reliable grid stability. Hence, power plant technologies and turbomachinery components will continue to be developed and employed for efficient re-conversion of stored energy. With the introduction of new working fluids for higher thermal efficiencies, the working conditions of exposed components and materials will require higher corrosion resistance, but with the same mechanical performance, manufacturability and cost. Intermetallic iron aluminide alloys with their outstanding oxidation and corrosion resistance and good high-temperature properties depict a possible candidate for use in high-temperature structural applications. A quinary Fe-26Al-4Mo-0.5Ti-1B solid-solution alloy with eutectic particle hardening particularly demonstrated competitive mechanical properties compared to high-alloy P92 steels in previous studies. To derive standard material specifications with industrially relevant casting strategies, centrifugal investment-cast Fe-25Al-3.7Mo-0.4Ti-1B was characterised with respect to microstructure, thermophysical properties and mechanical properties under quasi-static tensile and creep loading up to 700 °C. Compared to P92 steel, the alloy demonstrated superior tensile strength above 550 °C and lower creep rates at 650 °C if stresses increase above 170 MPa. At lower temperatures though, the mechanical properties were inferior to P92 steel and related Fe-Al-Mo-Ti-B alloys, which was correlated to large grain sizes, a high tendency to surface and bulk cracking and a pronounced effect of tension-compression asymmetry. In further studies on alloy composition with varying Al, Mo and B concentration, a non-linear relationship of solid-solution hardening with solute Mo concentration was found. In this regard, halving Mo was the most effective measure for reducing brittleness without decreasing strength at room and elevated temperatures. Higher solidification rates and grain refinement down to 30 µm by die casting had a positive effect on ambient tensile strength, but were not achievable by investment casting. Dilatometry and hardness measurements indicated a low thermal vacancy hardening effect which was less sensitive to low-temperature annealing than in B2 FeAl alloys. Although mechanical properties up to 550 °C could be considerably improved by alloy development and processing, ductility at room temperature generally remained below 1%, necessitating substantial design margins for components from Fe-Al-Mo-Ti-B alloys. Despite the inherent limitations of alloy and casting process, the gained insights will help to prioritise future areas of research to mature cost-effective higher-order Fe Al alloys for high-temperature structural applications. KW - Hardness KW - Iron aluminide alloy KW - Micro structure KW - Tensile strength KW - Creep strength PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632810 DO - https://doi.org/10.5445/IR/1000181739 SP - 1 EP - 179 PB - Karlsruher Institut für Technologie (KIT) CY - Karlsruhe AN - OPUS4-63281 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -