TY - JOUR A1 - Mazzeo, P A1 - Lampronti, G A1 - Michalchuk, Adam A1 - Belenguer, A A1 - Bacchi, A A1 - Emmerling, Franziska T1 - Accurate extrinsic and intrinsic peak broadening modelling for time-resolved in situ ball milling reactions via synchrotron powder X-ray diffraction N2 - The debate on the mechanisms which underpin mechanochemical reactions via ball mill grinding is still open. Our ability to accurately measure the microstructural (crystal size and microstrain) evolution of materials under milling conditions as well as their phase composition as a function of time is key to the in-depth understanding of the kinetics and driving forces of mechanochemical transformations. Furthermore, all ball milling reactions end with a steady state or milling equilibrium – represented by a specific phase composition and relative microstructure – that does not change as long as the milling conditions are maintained. The use of a standard sample is essential to determine the instrumental contribution to the X-ray powder diffraction (XRPD) peak broadening for time-resolved in situ (TRIS) monitoring of mechanochemical reactions under in operando conditions. Using TRIS-XRPD on a ball milling setup, coupled with low-energy synchrotron radiation, we investigated different data acquisition and analysis strategies on a silicon standard powder. The diffraction geometry and the microstructural evolution of the standard itself have been studied to model the instrumental contribution to XRPD peak broadening throughout the grinding activity. Previously proposed functions are here challenged and further developed. Importantly, we show that minor drifts of the jar position do not affect the instrumental resolution function significantly. We here report and discuss the results of such investigations and their application to TRIS-XRPD datasets of inorganic and organic ball mill grinding reactions. KW - Mechanochemistry KW - In situ diffraction KW - Synchrotron radiation KW - Sustainable chemisry PY - 2022 U6 - https://doi.org/10.1039/d2fd00104g SP - 1 EP - 17 PB - Royal Society of Chemistry AN - OPUS4-55932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stephan-Scherb, Christiane A1 - Nützmann, Kathrin T1 - Real time observation of crystallization and growth of corrosion products by energy dispersive X-ray diffraction N2 - Ferritic-martensitic high temperature alloys are widely used as boiler tube and heat exchanger materials in combustion based power plants. All technologies have in common that the applied materials are exposed to different temperatures, process pressures and reactive atmospheres which lead to a change of the material properties and a further degradation of the material. To date corrosion analytics mainly proceeds via the use of various microscopic techniques and the analysis of the corrosion products after the reaction is completed. Comprehensive efforts have been made to study high temperature corrosion by the use of environmental SEM’s or in-situ TEM technologies. The here presented work will show a different approach to study high temperature gas corrosion in a multiple gas atmosphere by energy dispersive X-ray diffraction (EDXRD). For this technique high energetic white X-ray radiation (10-100 keV) was used as radiation source instead of conventional monochromatic radiation. It enables us to study crystallization procedures on short and medium time scales (1 min < t < 24 h) and the collection of Bragg-Signals of the phases of interest as a function of process time. Their occurrence can directly be correlated with thermodynamic and kinetic parameters. A special designed corrosion reactor was used to combine high temperature gas corrosion experiments with the collection of diffraction patter. The crystallization and reaction paths for oxide and sulfide formation was followed in-situ on Fe-Cr and Fe-Cr-Mn model alloys in a hot SO2 containing (T=650 °C) atmosphere. T2 - Gordon Research Conference on High Temperature Corrosion and Protection of Materials CY - New London, NH, USA DA - 09.07.2017 KW - Corrosion KW - In situ diffraction KW - Crystallization PY - 2017 AN - OPUS4-44717 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stephan-Scherb, Christiane A1 - Nützmann, Kathrin A1 - Kranzmann, Axel A1 - Klaus, M. A1 - Genzel, C. T1 - Real time observation of high temperature oxidation and sulfidation of Fe-Cr model alloys N2 - Insights into early damage mechanisms during high-temperature gas corrosion provide important aspects for the prediction of the long-term stability of hightemperature materials exposed to a hot and corrosive environment. The current work presents a real time study concerning the combined oxidation and sulfidation of ferritic model alloys in a hot SO2 containing atmosphere using energy dispersive X-ray diffraction. The applied high temperature reactor allows the transmittance of high energetic X-rays in order to collect X-ray diffraction pattern of the sample surface in situ during the reaction with the reactive environment. The results revealed that the first phases crystallizing on iron with 2 wt% chromium and with 9 wt% chromium are oxides. The aging experiments at T = 650° C with 0.5% SO2 and 99.5% Ar were followed in situ and caused an external mixed oxide-sulfide layer on top of iron with 2 wt% chromium. On the higher alloyed material the external scale consists of iron oxides and the inner scale of mixed (Fe,Cr)-oxides and chromium-sulfides. The oxide content continuously increases parallel to an increase of the sulfide amount. Thus, the initially formed (Fe,Cr)-oxides do not have a protective character and support the transport of sulfur through the growing oxide scale. KW - High temperature corrosion KW - In situ diffraction KW - Sulfidation PY - 2018 U6 - https://doi.org/10.1002/maco.201709892 SN - 0947-5117 VL - 69 IS - 6 SP - 678 EP - 689 PB - Wiley VCH Verlag AN - OPUS4-44776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -