TY - CONF A1 - Thomas, Maximilian T1 - Digitalisierung in der Heißrissprüfung - Wie viel Information steckt in einer MVT-Probe? N2 - Die im MVT-Test standardmäßig erfasste Gesamtrisslänge erlaubt keine direkten Rückschlüsse auf die Heißrissanfälligkeit des untersuchten Werkstoffs. Der vorliegende Beitrag erläutert, inwiefern aus der Morphologie von Oberflächenrissen an MVT-Proben dennoch auf das Werkstoffverhalten geschlossen werden kann. T2 - Jährl. Sitzung des DIN/DVS Normenausschuss 092-00-05 GA CY - Online meeting DA - 10.03.2021 KW - MVT KW - Varestraint KW - Heißriss KW - Erstarrungsriss PY - 2021 AN - OPUS4-52243 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thomas, Maximilian A1 - Vollert, F. A1 - Weidemann, Jens A1 - Gibmeier, J. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - On the Accuracy of Standard Analysis Methods for (Trans-) Varestraint Solidification Cracking Testing N2 - Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials. The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour. First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach. Subsequently, μCT scans were performed on the specimens. The results consistently show sub surface cracking, to significant, yet varying extents. Different Primary solidification types were found using WDX-analysis, an aspect that is regarded to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics. Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account. T2 - 72th International Assembly of the International Institute of Welding (IIW) CY - Bratislava, Slovakia DA - 08.07.2019 KW - Heißriss KW - Erstarrungsriss KW - Hot Cracking KW - Solidification Cracking KW - MVT KW - Varestraint KW - Low Transformation Temperature KW - LTT PY - 2019 AN - OPUS4-48752 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -