TY - JOUR A1 - Griesche, Axel A1 - Pfretzschner, B. A1 - Taparli, Ugur Alp A1 - Kardjilov, N. T1 - Time-Resolved Neutron Bragg-Edge Imaging: A Case Study by Observing Martensitic Phase Formation in Low Temperature Transformation (LTT) Steel during GTAW N2 - Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam). The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature Ms since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging. KW - Austenite-to-martensite transformation KW - Neutron radiography KW - Bragg-edge imaging KW - Gas tungsten arc welding (GTAW) KW - Debye–Waller factor KW - Low transformation temperature (LTT) steel PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-538016 VL - 11 IS - 22 SP - 10886 PB - MDPI CY - Basel AN - OPUS4-53801 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Taparli, Ugur Alp A1 - Kardjilov, N. T1 - Time-Resolved Neutron Bragg-Edge Imaging: A Case Study by Observing Martensitic Phase Formation in Low Temperature Transformation (LTT) Steel during GTAW N2 - Polychromatic and wavelength-selective neutron transmission radiography were applied during bead-on-plate welding on 5 mm thick sheets on the face side of martensitic low transformation temperature (LTT) steel plates using gas tungsten arc welding (GTAW). The in situ visualization of austenitization upon welding and subsequent α’-martensite formation during cooling could be achieved with a temporal resolution of 2 s for monochromatic imaging using a single neutron wavelength and of 0.5 s for polychromatic imaging using the full spectrum of the beam (white beam). The spatial resolution achieved in the experiments was approximately 200 µm. The transmitted monochromatic neutron beam intensity at a wavelength of λ = 0.395 nm was significantly reduced during cooling below the martensitic start temperature M s since the emerging martensitic phase has a ~10% higher attenuation coefficient than the austenitic phase. Neutron imaging was significantly influenced by coherent neutron scattering caused by the thermal motion of the crystal lattice (Debye–Waller factor), resulting in a reduction in the neutron transmission by approx. 15% for monochromatic and by approx. 4% for polychromatic imaging. KW - Neutron radiography KW - Debye–Waller factor KW - Austenite-to-martensite transformation KW - Low transformation temperature (LTT) steel KW - Bragg-edge imaging KW - Gas tungsten arc welding (GTAW) PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-559077 VL - 11 IS - 22 PB - MDPI AN - OPUS4-55907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Griesche, Axel A1 - Große, M. A1 - Schillinger, B. ED - Fritzsche, H. ED - Huot, J. ED - Fruchart, D. T1 - Neutron imaging N2 - Neutron imaging methods are appropriate to investigate hydrogen distributions in several metallic systems. The large total neutron cross section of hydrogen compared to those of elements or isotopes, respectively, in usual structural materials like steels or zirconium alloys allows the detection even of small amounts of hydrogen in such materials. The dependence of the total macroscopic neutron cross section of the sample or component on the hydrogen concentration can be determined experimentally by means of calibration specimens with known hydrogen concentrations. Such a calibration allows for a full quantitative determination of the local hydrogen concentration with a spatial resolution better than 20 μm. Because neutron radiography is fast and non-destructive, in situ investigations of time-dependent processes like hydrogen absorption and release or hydrogen bulk diffusion can be performed. This chapter gives an introduction into the main neutron imaging methods, radiography and tomography, and gives as examples results of neutron imaging investigations of hydrogen in different steels and in zirconium alloys,respectively. KW - Neutron imaging KW - Neutron radiography KW - Hydrogen PY - 2016 SN - 978-3-319-22792-4 SN - 978-3-319-22791-7 U6 - https://doi.org/10.1007/978-3-319-22792-4_7 SN - 1868-0380 SN - 1868-0372 SP - Chapter 7, 193 EP - 225 PB - Springer Nature CY - Zurich, Switzerland AN - OPUS4-36365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Dabah, Eitan A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Schulz, M. A1 - Kardjilov, N. T1 - Measurement of hydrogen distributions in metals by neutron radiography and tomography N2 - In recent years, the optimization of the imaging stations at research reactors and especially the further development of the neutron detectors allowed the measurement of hydrogen distributions with increasing spatial and temporal resolution at lower detection limits at the same time. Hydrogen has compared to iron a high total neutron cross section, which allows with basic radiographic methods the visualization of hydrogen in two and three dimensions inside the microstructure of components. This enables the in situ measuring of hydrogen mass flows inside cm thick steel samples with a temporal resolution of 20 s as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples. For the first time, we detected directly gaseous hydrogen in the crack cavities and we could measure the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of damage mechanisms, e.g. of hydrogen embrittlement. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm, which is not accessible with common methods as e.g. thermal desorption spectroscopy. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography method in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching. T2 - 2016 International Hydrogen Conference CY - Moran, Wyoming, USA DA - 11.09.2016 KW - Neutron imaging KW - Hydrogen embrittlement KW - Neutron tomography KW - Neutron radiography PY - 2016 AN - OPUS4-37700 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Dabah, Eitan A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Imaging of Hydrogen in Steels with Neutrons N2 - Cold neutrons are predominantly scattered at hydrogen when penetrating hydrogen-charged samples, resulting in a high image contrast between hydrogen and e.g. iron. The used radiographic set-ups consist of a neutron source, state-of-the-art scintillator screens and digital cameras. This allows monitoring diffusive hydrogen fluxes two-dimensionally with 20s temporal resolution. Such hydrogen fluxes can be quantified by using standards with known hydrogen content and similar sample thickness. Neutron tomography generates three-dimensional models of the hydrogen distribution in steel. Such models gain new insight for damage analysis by showing the hydrogen accumulations around cracks and by enabling the hydrogen gas pressure estimation inside cracks. The capabilities and limitations, as well as perspectives of this method will be discussed and illustrated with help of selected examples. T2 - MS&T 2016 CY - Salt Lake City, Utah, USA DA - 23.10.2016 KW - Hydrogen embrittlement KW - Neutron imaging KW - Neutron radiography KW - Neutron tomography PY - 2016 AN - OPUS4-38066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Schillinger, B. A1 - Schulz, M. A1 - Kardjilov, N. A1 - Manke, I. T1 - Measurement of Hydrogen Distributions in Metals by Neutron Radiography and Tomography N2 - Neutron imaging is a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Time-resolved neutron radiography allows to measure hydrogen mass flow inside cm thick steel samples with ~10 s temporal resolution. Hydrogen accumulations around cracks in embrittled iron samples can be visualized three-dimensionally by neutron tomography. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g. of hydrogen blistering. Even the gas pressure of molecular hydrogen in crack cavities has been measured from tomographic reconstructions to be in the range of 5 MPa to 15 MPa for technical iron. Further, this method is non-destructive and provides local information in situ and in all three dimensions with a spatial resolution of 20 - 30 µm. The combination with other methods gives a new quality of information, e.g. of the hydrogen allocation on fractured surfaces. T2 - Symposium on large scale facilities CY - Berlin, Germany DA - 09.03.2020 KW - Hydrogen embrittlement KW - Neutron imaging KW - Hydrogen diffusion KW - Neutron radiography KW - Neutron tomography PY - 2020 AN - OPUS4-50548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Kardjilov, N. ED - Somerday, B. P. ED - Sofronis, P. T1 - Measurement of hydrogen distributions in metals by neutron radiography and tomography N2 - Neutron imaging has become a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Hydrogen mass flow can be measured inside cm thick Steel samples with 10 s temporal resolution. Hydrogen accumulations around craclcs in embrittled iron samples can be visualized three-dimensionally. The gas pressure of hydrogen in crack cavities has been measured to be in the ränge of 5 MPa to 15 MPa. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g., of hydrogen blistering. Further, this method is nondestructive and provides local information in situ and in three dimensions with a spatial resolution of 20 µm - 30 µm. T2 - International Hydrogen Conference 2016 CY - Jackson Lake Lodge, Wyoming, USA DA - 11.09.2017 KW - Hydrogen KW - Neutron imaging KW - Neutron radiography KW - Neutron tomography PY - 2017 SN - 978-0-7918-6138-7 U6 - https://doi.org/10.1115/1.861387_ch46 SP - 416 EP - 422 AN - OPUS4-42505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -