TY - JOUR A1 - Poyet, S. A1 - Dridi, W. A1 - L'Hostis, V. A1 - Meinel, Dietmar T1 - Microstructure and diffusion coefficient of an old corrosion product layer and impact on steel rebar corrosion in carbonated concrete JF - Corrosion Science N2 - Corrosion is the major degradation pathway affecting reinforced concrete structures. In the long-term, the rust layer might become thick and slow down the diffusion of oxygen from the atmosphere to the steel. With this in mind, the mineralogy, microstructure and diffusion properties of an old and thick corrosion product layer were investigated. Despite the presence of macropores, the gas diffusion coefficient was found to be low. The impact of the layer on the oxygen diffusion was evaluated using Fick’s law. The results showed that the layer could reduce the flux of oxygen only in a specific configuration. KW - Steel reinforced concrete KW - Rust KW - X-ray computed tomography KW - Micro-CT PY - 2017 DO - https://doi.org/10.1016/j.corsci.2017.06.002 VL - 2017 IS - 125 SP - 48 EP - 58 PB - Elsevier B.V. CY - Radarweg 29, 1043 NX Amsterdam, The Netherlands AN - OPUS4-41784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -