TY - CONF A1 - Rethmeier, Michael A1 - Suwala, H. A1 - Gumenyuk, Andrey T1 - Development of a test method for determining the cracking susceptibility of resistance spot welded high strength steel sheets N2 - Test procedure to characterize the cracking susceptibility of RSW-steels has been developed During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel Complex phase steels behavior during test procedure: Crack length growth with increasing force could not be determined The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case) 30 T2 - The METEC and 2nd European Steel Technology and Application Days (ESTAD)conference CY - Düsseldorf, Germany DA - 15.06.2015 KW - Externally loaded hot cracking test KW - Variables influencing hot cracking KW - Self-restraint hot cracking KW - Welding jig PY - 2015 AN - OPUS4-38348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -