TY - CONF A1 - Voigt, Marieke A1 - Hirsch, T. A1 - Meng, Birgit A1 - Stephan, D. T1 - Hydration and crystallization of Portland cement at 100 C N2 - For the construction of hot water storage tanks, ultra high performance concrete proofed to be a suitable building material to ensure water tightness. Common storage tanks build with concrete are designed to endure temperatures up to 90 °C. To increase the energy efficiency however, modern tanks need to withstand temperatures above 100 °C. With increasing temperature and correlating water vapor pressures, the cement must meet new requirements. Thermodynamic modelling is a promising tool for predicting the phase stabilities of minerals in the cement within these temperature and pressure ranges (T/P). Thus, mixture designs can be investigated and optimized with regard to the expected mineral phases in selected T/P-ranges. Additionally, predictions of the long-term material behavior can be derived from thermodynamic data and subsequently the experimental effort can be reduced notably. On the other hand, validation of predictions is needed. The base for the thermodynamic model is a thermodynamic equilibrium and thus, the experimental data for validation should approach the presumed conditions of the equilibrium. This study investigates variable experimental conditions for the hydration of Portland cement at 100 °C to reach a sufficiently progressed development of the phase composition. In case of Portland cement, the highest degree of hydration achievable within a reasonable time span is the most significant parameter. Therefore, Portland cement pastes with w/c ratios from 0.4 to 0.6 and dwell times up to three weeks were examined with powder X-ray diffraction to identify mineral phase changes. At 100 °C and high humidity, Portland cement paste shows the expected mineral phases like portlandite, katoite, and remaining clinker phases. The cement pastes with high water content and long dwell time seem to have the highest degree of hydration, even though the AFm phases stabilize with increasing w/c ratio. A dwell time of two weeks and a w/c ratio of 0.5 was found to provide the mineral composition with the highest degree of hydration including the major phase transitions. T2 - 4th International Conference on the Chemistry of Construction Materials (ICCCM) CY - Karlsruhe, Germany DA - 26.09.2022 KW - Hydration KW - High temperature KW - Portland cement PY - 2022 AN - OPUS4-56866 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Weba, Luciana A1 - Silbernagl, Dorothee A1 - Mota Gassó, Berta A1 - Höhne, Patrick A1 - Sturm, Heinz A1 - Pauli, Jutta A1 - Resch-Genger, Ute A1 - Steinborn, Gabriele ED - Khayat, Kamal Henry T1 - Influences of nano effects on the flow phenomena of self-compacting concrete N2 - Chemical admixtures like superplasticisers or stabilising agents are of ever increasing importance for modern concrete technology. They liberate the workability of concrete from its dependency on water content, and thus, open the gate towards innovative and future oriented concrete technologies such as selfcompacting concrete. Meanwhile admixtures have become common practice in concrete technology, but the understanding of these highly complex polymers in the entire concrete system lags far behind their application. Due to its complex time-dependent, multi-phase and multi-scale behaviour, flowable concrete systems are highly complicated and cannot be described comprehensively by simple models. It is therefore extremely challenging to identify the relevant parameters that predominantly control flow phenomena on different size scales, since these may occur on any scale between the nano scale (e.g. superplasticizer adsorption) and macro scale (e.g. grading of the aggregates). The present study discusses fundamental mechanisms at the interface between particle or hydrate surfaces and the fluid phase at a very early stage of concrete formation, and links these effects to macroscopic flow phenomena. Methods are discussed that appear promising interdisciplinary tools for enhancement of the understanding of the relevant interactions that are responsible for the macroscopic flow of flowable concrete. T2 - 8th International RILEM Symposium on Self-Compacting Concrete CY - Washington, D.C., USA DA - 15.05.2016 KW - Adsorption KW - Analytics KW - Hydration KW - Polycarboxylate ether KW - Rheology PY - 2016 SP - 245 EP - 254 AN - OPUS4-36882 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stroh, Julia A1 - Emmerling, Franziska T1 - In situ cement hydration in levitated droplets N2 - Building materials consist of cement, water and chemical admixtures, which adjust cement paste properties. They can act beyond their aimed functions causing changes in hydration course. The mechanisms are still under investigation. We investigate cement hydration in levitated droplets using an ultrasonic levitator. Hydrate phase formation is followed in situ by synchrotron XRD. The data allows detailed conclusions about the mechanisms of the admixture action in the ongoing hydration reactions. T2 - 7th GACM Colloquium on Computational Mechanics CY - Stuttgart, Germany DA - 11.10.2017 KW - Portland cement KW - Hydration KW - Levitation KW - Admixtures PY - 2017 AN - OPUS4-43165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigt, Marieke A1 - Gardei, Andre A1 - Meng, Birgit T1 - The adaption of the set-up for gas permeability measurements for ultra-high performance concrete N2 - In the framework of this project, a steam pressure vessel was to be developed from ultra-high perfor-mance concrete (UHPC) to withstand process temperatures of 200 °C and the respective steam pressure of 15,5 bar. To guarantee the long-term water vapour tightness of the system, the permeability of two UHPC mixtures were tested after long-term cyclic autoclaving. As UPHC shows a high density and therefore low permeability, measurements after the RILEM-Recommendation (TC 116-PCD) reached their detection limit. Therefore, the measurement set-up was adapted to measure the permeability of highly dense UHPC more reliably and quickly. This adaption includes measurements in a higher pres-sure range, the change of sample size thickness and the usage of Ar as a medium compared with the RILEM Recommendation. Additionally, the system was equipped with two pressure sensors and Ar-flowmeters to guarantee a continuous record of the experimental parameters. The new system was tested and evaluated by comparing measurements with the RILEM recommended system. Preliminary results show that the adapted system is capable to provide efficient and reliable results of concrete with low permeability. T2 - 14th fib PhD Symposium in Civil Engineering CY - Rome, Italy DA - 05.09.2022 KW - Hydration KW - High temperature KW - Portland cement PY - 2022 AN - OPUS4-56859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cunningham, P. R. A1 - Mezhov, Alexander A1 - Schmidt, Wolfram T1 - Revealing Value from Bioderived Polymers: Effects of Locally Sourced Polysaccharides on the Rheology of Limestone Mixtures N2 - Admixtures are important constituents to enhance the performance of concrete. They allow for more efficient use of binders which can mitigate negative environmental impacts from producing cement-based materials. Commonly used rheology modifying agents like polycarboxylate ethers or cellulose ethers are synthetic or semi-synthetic, respectively. This requires additional energy consumption for their production and global supply chains particularly for many developing regions, which will be large consumers of concrete in the future. However, many locally available bio-based polysaccharides could be effectively used instead. These polymers are often overlooked by engineers and scientists due to their limited distribution and inherent complexity, yet they represent an underleveraged source of precursors for admixtures. This study investigates the action mechanisms of some bio-based rheology modifying agents, i.e., acacia gum and miscanthus gum, and provides a comparison to a conventionally modified starch. The results show that the mechanism of action of these polymers is closely related to the composition of the mixture, mixing regime, and the composition of the aqueous phase. Depending on the agent, either plasticizing or stabilizing effects on rheology can be revealed. T2 - ICBBM: International Conference on Bio-Based Building Materials CY - Vienna, Austria DA - 21.06.2023 KW - Polysaccharides KW - Superplasticizers KW - Hydration KW - Cement PY - 2023 U6 - https://doi.org/10.1007/978-3-031-33465-8_60 SN - 2211-0852 VL - 45 SP - 782 EP - 792 PB - Springer Nature Switzerland AG CY - Switzerland AN - OPUS4-58726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kruschwitz, Sabine A1 - Lorenzoni, Renata A1 - Telong, Melissa A1 - Lauinger, Robert A1 - Munsch, Sarah A1 - Schmidt, Wolfram T1 - Investigation of the hydration of clinker-reduced cementitious binders by 1H NMR N2 - In this paper, we demonstrate the value of 1H NMR relaxometry for studying the hydration of clinker-reduced, more climate-friendly cementitious binders. The results were obtained on typical CEM I cements and samples containing two different reactive agricultural ashes as well as non-reactive biochars as supplementary cementitious materials. The findings prove that time-resolved NMR measurements provide valuable additional information when combined with classical heat flow calorimetry. T2 - ISEMA Down Under 2023 CY - Brisbane, Australia DA - 25.09.2023 KW - 1H NMR relaxometry KW - Heat flow calorimetry KW - Clinker reduction, carbon emission KW - Cement KW - Hydration PY - 2023 AN - OPUS4-58569 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Durlo Tambara, Luis Urbano A1 - Batista, I. D. A1 - Carneiro, J. C. A1 - Silva, L. G. C. H. A1 - Taborda-Barraza, M. A1 - Azevedo, A. R. G. T1 - Influence of dredging mud on the calcium sulfoaluminate cement hydration N2 - Dredging sediment refers to materials removed from the bottom of a water body during dredging operations. Mainly the dreading mud contains clay, silt, sand, water, and alkalis. This work incorporated dredging mud into the calcium sulfoaluminate cement at replacement levels of 0%, 10%, 30%, and 50% by weight. Pastes were evaluated after 1d, 28d, and 90d- hydration through mechanical strengths and the reaction rate by isothermal conduction calorimetry. XRD and MIP characterized the reaction products. The findings showed that small replacements (10% and 30%) increased early strength with higher ettringite formation in the system at 1d of curing. However, the evolution of mechanical strength was lower than the reference (0% replacement) over time. The results showed that in low replacement dosages, the dredging mud act as a nucleation site for the hydration of calcium sulfoaluminate phases. T2 - 7th International Conference Non-Traditional Cement & Concrete (NTCC) CY - Brno, Czech Republic DA - 25.06.2023 KW - Calcium sulfoaluminate cement KW - Dredging mud KW - Hydration KW - Paste PY - 2023 AN - OPUS4-58054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -