TY - JOUR A1 - Andreoli, A. F. A1 - Fantin, Andrea A1 - Kasatikov, S. A1 - Bacurau, V. P. A1 - Widom, M. A1 - Gargarella, P. A1 - Mazzer, E. M. A1 - Woodcock, T. G. A1 - Nielsch, K. A1 - Coury, F. G. T1 - The impact of chemical short-range order on the thermophysical properties of medium- and high-entropy alloys N2 - The unusual behavior observed in the coefficient of thermal expansion and specific heat capacity of CrFeNi, CoCrNi, and CoCrFeNi medium/high-entropy alloys is commonly referred to as the K-state effect. It is shown to be independent of the Curie temperature, as demonstrated by temperature-dependent magnetic moment measurements. CoCrFeNi alloy is chosen for detailed characterization; potential reasons for the K-state effect such as texture, recrystallization, and second-phase precipitation are ruled out. An examination of the electronic structure indicates the formation of a pseudo-gap in the Density of States, which suggests a specific chemical interaction between Ni and Cr atoms upon alloying. Hybrid Monte Carlo/Molecular Dynamic (MC/MD) simulations indicate the presence of non-negligible chemical short-range order (CSRO). Local lattice distortions are shown to be negligible, although deviations around Cr and Ni elements from those expected in a fully disordered structure are experimentally observed by X-ray absorption spectroscopy. The determined bonding distances are in good agreement with MC/MD calculations. A mechanism is proposed to explain the anomalies and calorimetric experiments and their results are used to validate the mechanism. KW - Mechanical Engineering KW - Mechanics of Materials KW - General Materials Science PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595869 DO - https://doi.org/10.1016/j.matdes.2024.112724 SN - 0264-1275 VL - 238 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-59586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lemiasheuski, Anton A1 - Kranzmann, Axel A1 - Pfennig, Anja T1 - Herausforderungen und Möglichkeiten des manuellen metallografischen Serienschnittverfahrens anhand einer quantitativen Gefügeanalyse der Grafite eines Gusseisens T1 - Challenges and possibilities of the manual metallographic serial sectioning process using the example of a quantitative microstructural analysis of graphite in cast iron N2 - Die in dieser Studie vorgestellte 3D-Gefüge-Analyse konzentriert sich auf die Kugelgrafite eines Gusseisens des Typs EN-GJS. Es werden die Form anhand des Formfaktors und des Seitenverhältnisses sowie die durchschnittliche Teilchengröße und -verteilung untersucht. Die Form der Grafite in Gusseisenwerkstoffen ist mitentscheidend für die mechanischen Eigenschaften dieser Legierungen und ist bei der Charakterisierung des Werkstoffs unumgänglich. Mittels Metallografischen Serienschnittverfahrens wird von dem Schicht für Schicht abgetragenen und lichtmikroskopisch schichtweise dargestellten Werkstoff ein digitaler Zwilling erstellt. Von diesem dreidimensionalen Zwilling lassen sich beliebige Ebenen digital projizieren und analysieren. Eine konventionelle quantitative 3D-Analyse untersucht die Voxelmenge und -zusammensetzung eines Körpers im 3D-Raum. Die hier vorgestellte Analyse wendet stereologische 2D-Analyseverfahren auf drei Raumebenen des Werkstoffs an. Dabei sind zwei der Ebenen digitale Projektionen des Zwillings. Die zwei rekonstruierten Ebenen des Werkstoffs sind so gewählt, dass die Richtungsvektoren aller drei Ebenen einen 90°-Winkel zueinander bilden. Diese Methodik wird eingehend beschrieben sowie Herausforderungen und Möglichkeiten des hier vorgestellten Serienschnittverfahrens diskutiert. N2 - The 3D microstructure analysis presented in this study focuses on the nodular graphite of an EN-GJS grade cast iron. The shape is analyzed based on shape factor and aspect ratio as well as average particle size and distribution. The shape of graphites in cast iron materials is critical to the mechanical properties of these alloys and is essential for the characterization of the material. Metallographic serial sectioning creates a digital twin of the material, which is removed layer by layer and visualized layer by layer under an optical microscope. From this three-dimensional twin, any number of planes can be digitally projected and analyzed. Conventional quantitative 3D analysis examines the voxel count and composition of a body in 3D space. The analysis presented here applies stereological 2D analysis methods to three spatial planes of the material. Two of the planes are digital projections of the twin. The two reconstructed planes of the material are chosen so that the direction vectors of all three planes form an angle of 90° to each other. The methodology is described in detail and the challenges and opportunities of the serial section method presented here are discussed. KW - Dreidimensionale Gefügeanalyse KW - Three-dimensional microstructure analysis KW - 3D-Metallografie KW - Serienschnittverfahren KW - Gefügerekonstruktion KW - Quantitative Gefügeanalyse KW - 3D metallography KW - Serial sectioning KW - Microstructure reconstruction KW - Quantitative microstructure analysis PY - 2024 DO - https://doi.org/10.1515/pm-2024-0066 SN - 0032-678X VL - 61 IS - 9-10 SP - 746 EP - 768 PB - De Gruyter CY - Berlin/Boston AN - OPUS4-60976 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cios, G. A1 - Winkelmann, A. A1 - Nolze, Gert A1 - Tokarski, T. A1 - Jany, B. R. A1 - Bala, P. T1 - EBSD and TKD analyses using inverted contrast Kikuchi diffraction patterns and alternative measurement geometries N2 - Electron backscatter diffraction (EBSD) patterns can exhibit Kikuchi bands with inverted contrast due to anomalous absorption. This can be observed, for example, on samples with nanoscale topography, in case of a low tilt backscattering geometry, or for transmission Kikuchi diffraction (TKD) on thicker samples. Three examples are discussed where contrast-inverted physics-based simulated master patterns have been applied to find the correct crystal orientation. As first EBSD example, self-assembled gold nanostructures made of Au fcc and Au hcp phases on single-crystal germanium were investigated. Gold covered about 12% of the mapped area, with only two thirds being successfully interpreted using standard Hough-based indexing. The remaining third was solved by brute force indexing using a contrast-inverted master pattern. The second EBSD example deals with maps collected at a non-tilted surface instead of the commonly used 70◦ tilted one. As TKD example, a jet-polished foil made of duplex stainless steel 2205 was examined. The thin part close to the hole edge producing normal-contrast patterns were standard indexed. The areas of the foil that become thicker with increasing distance from the edge of the hole produce contrast-inverted patterns. They covered three times the evaluable area and were successfully processed using the contrast-inverted master pattern. In the last example, inverted patterns collected at a non-tiled sample were mathematically inverted to normal contrast, and Hough/Radon-based indexing was successfully applied. KW - EBSD KW - TKD KW - Contrast inversion KW - Topography KW - Kikuchi diffraction PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613862 VL - 267 SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-61386 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Mohring, Wencke A1 - Wolf, Marcus T1 - The insignificant improvement of corrosion and corrosion fatigue behavior in geothermal environment applying Boehmit coatings on high alloyed steels N2 - The efficacy of alumina-sol based coatings in a water-free atmosphere at high temperatures suggests a potential solution for enhancing the corrosion resistance of high-alloyed steels in Carbon Capture and Storage (CCS) environments. In this study, coupons of X20Cr13, designed for use as injection pipes with 13% Chromium and 0.20% Carbon (1.4021, AISI 420), were sol-gel coated with water and ethanol-based alumina. These coated coupons were then exposed to CO2-saturated saline aquifer water, simulating conditions in the Northern German Basin, for 1000 h at ambient pressure and 60 °C. Corrosion fatigue experiments were also conducted using specimens of X5CrNiMoCuNb16-4 (1.4542, AISI 630), a suitable candidate for geothermal applications, to assess the impact of the ethanol-based coating on the number of cycles to failure at different stress amplitudes. Unfortunately, the coating exhibited early spallation, resulting in corrosion kinetics and corrosion fatigue data identical to those of uncoated specimens. Consequently, the initially promising Boehmit coating is deemed unsuitable for CCS applications and further research therefore not advisable. KW - Alumina coating KW - High alloyed steel KW - Pitting KW - Surface corrosion KW - CO2 KW - Pipeline KW - Corrosion KW - CCS KW - CO2-storage PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623786 DO - https://doi.org/10.3390/app14041575 SN - 2076-3417 VL - 14 IS - 4 SP - 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-62378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Swaminathan, Srinivasan A1 - Kumar, S. A1 - Kranzmann, Axel A1 - Hesse, Rene A1 - Goldbeck, Hennig A1 - Fantin, Andrea T1 - Corrosion characteristics of 316L stainless steel in oxide-rich molten solar salt at 600◦C N2 - An attempt has been made in this work, to observe the influence on alloy aging by the sodium oxide (Na2O) in solar salt (60 wt% NaNO3 + 40 wt% KNO3). The accelerated aging was established by adding Na2O (0.005, 0.07, 0.135 and 0.2 wt%) to the solar salt and their effect on corrosion of 316L stainless steel (SS) at 600 ◦C in that oxide-rich solar salts for 168 h in synthetic air was investigated. Corrosion is significantly more in oxide-rich solar salt compared to pure solar salt. Strikingly, the oxide scale-base metal interface is wavy in solar salt containing 0.005 % Na2O clearly shows the oxide addition to salt melt influences Cr-rich inner oxide layer formation and its selective dissolution at early stage that leads to non-uniform corrosion. Interestingly, with increase of Na2O to 0.07 %, steel corrosion proceeded uniformly by accelerated disintegration of Cr-rich inner layer and subsequent dissolution. Severe scale spallation and weight loss in nitrate melt containing 0.2 % Na2O fostering more rapid corrosion, alarming that substantial tolerance of oxide content in solar salt is ≥ 0.135 % for an acceptable corrosion of 316L SS. Despite preferential dissolution of Cr and scale degradation/spallation with increased oxide content in solar salt, the corrosion layer in all cases comprised of sodium ferrite, and Cr-rich Cr-Fe mixed oxides with the Ni enrichment at the scale-metal interface. Competing processes between oxide scale growth, degradation and dissolution or even spallation has been discussed with an emphasis of Na2O addition to solar salt. KW - Molten salt corrosion KW - Solar salt KW - Thermal energy storage KW - Stainless steel KW - Concentrating solar power PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610819 DO - https://doi.org/10.1016/j.solmat.2024.113176 VL - 278 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-61081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - INPR A1 - Kalady, Mohammed Fayis A1 - Schultz, Johannes A1 - Weinel, Kristina A1 - Wolf, Daniel A1 - Lubk, Axel T1 - Localization of Hybridized Surface Plasmon Modes on Random Gold Nanoparticle Assemblies N2 - Assemblies of plasmonic nanoparticles (NPs) support hybridized modes of localized surface plasmons (LSPs), which delocalize in geometrically well-ordered arrangements. Here, the hybridization behavior of LSPs in geometrically completely disordered arrangements of Au NPs fabricated by an e-beam synthesis method is studied. Employing electron energy loss spectroscopy in a scanning transmission electron microscope in combination with numerical simulations, the disorder-driven spatial and spectral localization of the coupled LSP modes that depend on the NP thickness is revealed. Below 0.4nm sample thickness (flat NPs), localization increases towards higher hybridized LSP mode energies. In comparison, above 10nm thickness, a decrease of localization (an increase of delocalization) with higher mode energies is observed. In the intermediate thickness regime, a transition of the energy dependence of the localization between the two limiting cases, exhibiting a transition mode energy with minimal localization, is observed. This behavior is mainly driven by the energy and thickness dependence of the polarizability of the individual NPs. KW - Plasmonics KW - Electron-Energy Loss Spectroscopy KW - Discrete Dipole Approximation KW - Nanoparticles PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618323 DO - https://doi.org/10.48550/arXiv.2410.10514 SP - 1 EP - 8 PB - Cornell University CY - Ithaca, NY AN - OPUS4-61832 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Was, G.S. A1 - Bahn, C.-B. A1 - Busby, J. A1 - Cui, B. A1 - Farkas, D. A1 - Gussev, M. A1 - Rigen He, M. A1 - Hesterberg, J. A1 - Jiao, Z. A1 - Johnson, D. A1 - Kuang, W. A1 - McMurtrey, M. A1 - Robertson, I. A1 - Sinjlawi, A. A1 - Song, M. A1 - Stephenson, K. A1 - Sun, K. A1 - Swaminathan, Srinivasan A1 - Wang, M. A1 - West, E. T1 - How irradiation promotes intergranular stress corrosion crack initiation N2 - Irradiation assisted stress corrosion cracking (IASCC) is a form of intergranular stress corrosion cracking that occurs in irradiated austenitic alloys. It requires an irradiated microstructure along with high temperature water and stress. The process is ubiquitous in that it occurs in a wide range of austenitic alloys and water chemistries, but only when the alloy is irradiated. Despite evidence of this degradation mode that dates back to the 1960s, the mechanism by which it occurs has remained elusive. Here, using high resolution electron backscattering detection to analyze local stress-strain states, high resolution transmission electron microscopy to identify grain boundary phases at crack tips, and decoupling the roles of stress and grain boundary oxidation, we are able to unfold the complexities of the phenomenon to reveal the mechanism by which IASCC occurs. The significance of the findings impacts the mechanical integrity of core components of both current and advanced nuclear reactor designs worldwide. KW - Irradiation KW - Stress corrosion cracking KW - Grain boundaries KW - Oxidation KW - Austenitic alloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595748 DO - https://doi.org/10.1016/j.pmatsci.2024.101255 SN - 0079-6425 VL - 143 SP - 1 EP - 15 PB - Elsevier AN - OPUS4-59574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weinel, Kristina T1 - Plasmonic Behavior in Assemblies of Disordered Gold Nanoparticles N2 - Plasmons are collective oscillations of the free electron density in metals which can be described by an electromagnetic field. Surface plasmons are longitudinal waves propagating at the surface of the metallic material coupled to an external field. Localized surface plasmons on a nanoparticle reveal the behavior of standing waves with discrete resonance frequencies whose dominating mode is called dipole mode. Coupling of nanoparticles leads eventually to a hybridization of those dipole modes and therefore to spectral and spatial delocalization which was already investigated in ordered systems. In disordered systems, there are a lot of open questions regarding the propagation behavior which changes from delocalization to localization for instance due to the disorder. This phenomenon is then called Anderson localization. To investigate the propagation behavior of plasmonic waves in an assembly of disordered gold NPs, we combine experimental results of electron energy loss spectroscopy in a scanning transmission microscope with simulation results of the self-consistent dipole modelling. We indeed find experimentally localization of plasmon modes and with the simulation we could exclude other localization mechanism such as life-time damping or retardation. In conclusion, we could found Anderson localization of surface plasmons in assemblies of disordered gold nanoparticles which will enhance the understanding of this kind of vector waves to the Anderson localization as a general wave behavior in disordered systems. T2 - PhD seminar Leipniz Institut for solid state and material research (IFW Dresden) CY - Dresden, Germany DA - 19.06.2024 KW - Plasmonic KW - EELS in STEM KW - Self-consistent dipole model KW - Assemblies of gold nanoparticles PY - 2024 AN - OPUS4-60945 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk T1 - Merkmale von alltäglichen Brüchen und wie wir daraus lernen können N2 - Schadensfälle aus dem Alltag erscheinen oft simpel, sind im Detail aber meist komplexer als erwartet und eröffnen die Möglichkeit, Merkmale zu studieren, Aufnahmetechniken und Bildbearbeitung zu optimieren und die Erfahrungen am Ende ohne Restriktionen weiter zu vermitteln. Beispielsweise verändern sich die mikroskopischen Merkmale von Schwingrissen über ihren Verlauf oft deutlich. Dies hängt von der Art des Werkstoffs und von den Beanspruchungsbedingungen ab. Die Bruchmerkmale werden schließlich systematisch dargestellt und ein Datensatz für die Fraktographische online-Datenbank der DVM/DGM AG Fraktographie erstellt, die fachöffentlich einsehbar ist. T2 - Metallographietagung 2024 CY - Berlin, Germany DA - 18.09.2024 KW - Fraktographie KW - Schadensanalyse PY - 2024 AN - OPUS4-61239 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mohring, Wencke A1 - Karafiludis, Stephanos A1 - Manzoni, Anna Maria A1 - Laplanche, G. A1 - Schneider, M. A1 - Stephan-Scherb, Christiane T1 - High-Temperature Corrosion of High- and Medium-Entropy Alloys CrMnFeCoNi and CrCoNi Exposed to a Multi-Oxidant Atmosphere H2O–O2–SO2 N2 - AbstractThe high-temperature corrosion behaviors of the equimolar CrCoNi medium-entropy alloy and CrMnFeCoNi high-entropy alloy were studied in a gas atmosphere consisting of a volumetric mixture of 10% H2O, 2% O2, 0.5% SO2, and 87.5% Ar at 800 °C for up to 96 h. Both alloys were initially single-phase fcc with a mean grain size of ~ 50 μm and a homogeneous chemical composition. The oxide layer thickness of CrMnFeCoNi increased linearly with exposure time while it remained constant at ~ 1 μm for CrCoNi. A Cr2O3 layer and minor amounts of (Co,Ni)Cr2O4 developed on the latter while three oxide layers were detected on the former, i.e., a thin and continuous chromium rich oxide layer at the oxide/alloy interface, a dense (Mn,Cr)3O4 layer in the center and a thick and porous layer of Mn3O4 and MnSO4 at the gas/oxide interface. Additionally, a few metal sulfides were observed in the CrMnFeCoNi matrix. These results were found to be in reasonable agreement with thermodynamic calculations. KW - high entropy alloys KW - corrosion KW - oxidation KW - scanning electron microscopy KW - sulfidation KW - CrMnFeCoNi PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594189 DO - https://doi.org/10.1007/s44210-023-00026-8 SP - 1 EP - 17 PB - Springer Science and Business Media LLC AN - OPUS4-59418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -