TY - CONF A1 - Weise, Frank A1 - Meng, Birgit A1 - Pirskawetz, Stephan A1 - Voland, K. T1 - Influence of simultaneous cyclic loading and external alkali supply on the alkali-silica reaction in concrete pavements T2 - 15th International Conference on Alkali-Aggregate reaction (ICAAR 2016) N2 - In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR. T2 - 15th International Conference on Alkali-Aggregate reaction (ICAAR 2016) CY - Sao Paulo, Brazil DA - 03.07.2016 KW - concrete pavements KW - alkali-silica-reaction KW - fatigue KW - damage monitoring PY - 2016 SP - Paper 191 AN - OPUS4-37142 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Werner, Steve A1 - Schmidt, Wolfram A1 - Pirskawetz, Stephan A1 - Rogge, Andreas ED - Khayat, Kamal Henry T1 - Fire spalling of self-compacting concrete mixtures with different limestone powder contents T2 - Proceedings of the 8th RILEM Symposium on Self-Compacting Concrete N2 - Self-compacting concrete typically contains a higher content of powder materials than normal concrete. Furthermore it is assumed that the use of superplasticizers yields a more homogenous microstructure in the hardened paste. Both aspects generate a very dense microstructure, which can be assumed to cause material behaviour that differs from than normal concrete when it is exposed to elevated temperatures. However, the paste volumes in SCC can vary significantly based on the mixture composition. At a low paste volumes SCC can be very similar to normal concrete at hardened state while it can vary greatly at higher paste volumes. Since the high temperature behaviour of concrete is strongly affected by the different physical behaviour of the paste and the aggregates, it is likely that the high temperature behaviour is consequently strongly affected by the ratio of these mixture components. In the present study different SCC mixtures were observed with similar mechanical properties, but with significantly differing paste to aggregate ratios. Based on observations of the heat evolution at the fire exposed surface and at different depths inside the specimens as well as based on photogrammetric observations of the spalled dimensions, the results indicate that with increasing paste volumes the heat conductivity is reduced and as a result concrete with higher paste to aggregate ratios shows less spalling. T2 - 8th RILEM Symposium on Self-Compacting Concrete CY - Washington, USA DA - 15.05.2016 KW - Spalling KW - High temperature behaviour KW - Fire exposure KW - Mixture composition KW - Photogrammetry PY - 2016 SN - 978-2-35158-157-5 SP - 353 EP - 363 PB - RILEM Publications S.A.R.L. CY - Paris, France AN - OPUS4-36873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -