TY - JOUR A1 - Cabeza, Sandra A1 - Garces, G. A1 - Adeva, Paloma A1 - Kabra, S. A1 - Gan, W. T1 - Effect of Extrusion Temperature on the Plastic Deformation of an Mg-Y-Zn Alloy Containing LPSO Phase Using In Situ Neutron Diffraction N2 - The evolution of the internal strains during in situ tension and compression tests has been measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using neutron diffraction. The alloy was extruded at two different temperatures to study the influence of the microstructure and texture of the magnesium and the LPSO phases on the deformation mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher in compression than in tension. Independently on the stress sign and the extrusion temperature, the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the reinforcement in a metal matrix composite is responsible for this tension–compression asymmetry. KW - Mg-Y-Zn Alloy KW - LPSO Phase KW - Neutron Diffraction PY - 2017 DO - https://doi.org/10.1007/s11661-017-4284-6 VL - 48A IS - 11 SP - 5332 EP - 5343 PB - Spinger AN - OPUS4-42935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wollschläger, Nicole A1 - Palasse, L. A1 - Häusler, Ines A1 - Dirscherl, K. A1 - Oswald, F. A1 - Narbey, S. A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan T1 - Characterization of the inner structure of porous TiO2 nanoparticle films in dye sensitive solar cells (DSSC) by focused ion beam (FIB) tomography and transmission Kikuchi diffraction (TKD) in the scanning electron microscope (SEM) N2 - A combined methodical approach is tested for the first time with respect to the characterization of the inner structure of porous TiO2 layers infiltrated with ruthenium molecular sensitizer as typically used in modern dye sensitized solar cells (DSSC). Their performance is directly linked to the surface area ‘offered’ by the pore Network to the dye. The micrometer thick layer employed was manufactured by screen-printing of a starting TiO2 powder constituted of shape-controlled, bipyramidal anatase nanoparticles (NPs) on FTO/glass substrates. The analytical methods exploited in our study are Focused Ion Beam (FIB) slicing followed by 3D reconstruction as well as the new approach transmission Kikuchi diffraction (TKD) technology in the scanning electron microscope (SEM). While the first method results in the visualization of the 3D pore network within the TiO2 layer, the second one can be successfully applied to analyze the crystal orientation of grains (i.e. NPs in our case) in nanometer resolution. Moreover, size and shape distribution of the TiO2 NPs within the layer can be extracted. SEM in transmission mode and atomic force microscopy (AFM) have been used to verify the dimensional data obtained by the new combined methodical approach. Its analytical benefits but also the challenges and limitations are highlighted. KW - Transmission Kikuchi diffraction KW - Focused ion beam tomography KW - Titanium dioxide KW - Nanoparticles KW - Porosity KW - Particle size KW - DSSC PY - 2017 DO - https://doi.org/10.1016/j.matchar.2017.06.030 SN - 1044-5803 SN - 1873-4189 VL - 131 SP - 39 EP - 48 PB - Elsevier AN - OPUS4-40875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yin, Huajie A1 - Chapala, P. A1 - Bermeshev, M. A1 - Schönhals, Andreas A1 - Böhning, Martin T1 - Molecular Mobility and Physical Aging of a Highly Permeable Glassy Polynorbornene as Revealed by Dielectric Spectroscopy N2 - Polymeric membranes represent a cost- and energy efficient solution for gas separation. Recently superglassy polymers with high free volume outperform many conventional dense polymers in terms of gas permeability and selectivity. However, such polymers are prone to pronounced physical aging, resulting in a dramatic reduction in the gas permeability. Molecular mobility of polymer segments plays an important role in the physical aging and the gas transport performance of polymeric membranes. Molecular mobility and physical aging of a representative superglassy polynorbornene with very high gas permeability, PTCNSi2g, was monitored by using dielectric spectroscopy with state-of-the-art high-resolution analyzers. This work helps to shed some light on the structure−property relationship of superglassy polymers on a molecular level and to provide practical “design rules” for the development of high performance polymers for gas separation. KW - Molecular mobility KW - Gas separation membrane KW - Broadband dielectric spectroscopy KW - Polymer KW - Physical ageing PY - 2017 DO - https://doi.org/10.1021/acsmacrolett.7b00456 SN - 2161-1653 VL - 6 IS - 8 SP - 813 EP - 818 PB - ACS CY - Washington DC, USA AN - OPUS4-41354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ward, H. A1 - Burger, M. A1 - Chang, Y.-J. A1 - Fürstmann, P. A1 - Neugebauer, S. A1 - Radebach, A. A1 - Sproesser, G. A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Uhlmann, E. A1 - Steckel, J. Ch. T1 - Assessing carbon dioxide emission reduction potentials of improved manufacturing processes using multiregional input output frameworks N2 - Evaluating innovative process technologies has become highly important within the last decades. As standard tools different Life Cycle Assessment methods have been established, which are continuously improved. While those are designed for evaluating single processes they run into difficulties when it comes to assessing environmental impacts of process innovations at macroeconomic level. In this paper we develop a multi-step evaluation framework building on multi regional inputeoutput data that allows estimating macroeconomic impacts of new process technologies, considering the network characteristics of the global economy. Our procedure is as follows: i) we measure differences in material usage of process alternatives, ii) we identify where the standard processes are located within economic networks and virtually replace those by innovative process technologies, iii) we account for changes within economic systems and evaluate impacts on emissions. Within this paper we exemplarily apply the methodology to two recently developed innovative technologies: longitudinal large diameter steel pipe welding and turning of high-temperature resistant materials. While we find the macroeconomic impacts of very specific process innovations to be small, its conclusions can significantly differ from traditional process based approaches. Furthermore, information gained from the methodology provides relevant additional insights for decision makers extending the picture gained from traditional process life cycle assessment. KW - Economic wide technology replacement KW - Sustainability assessment KW - Multi-regional inputeoutput data KW - Life-cycle assessment KW - Greenhouse gas mitigation KW - Process innovations PY - 2017 DO - https://doi.org/10.1016/j.jclepro.2016.02.062 SN - 0959-6526 SN - 1879-1786 VL - 163 SP - 154 EP - 165 PB - Elsevier Ltd. AN - OPUS4-41356 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Woydt, Mathias T1 - VGP 2013 - Propelling marine lubricants N2 - This letter to the Editor directs attention to EN 16807-2016:12, Liquid Petroleum products - Bio lubricants - Criteria and requirements of bio lubricants and bio-based lubricants. KW - Bio lubricants KW - Liquid petroleum products KW - EN 16807-2016:12 PY - 2017 SN - 1545-858X VL - 73 IS - 7 SP - 7 PB - Society of Tribologists and Lubrication Engineers CY - Park Ridge, IL AN - OPUS4-41342 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hernández-Nava, E. A1 - Tammas-Williams, S. A1 - Smith, C. A1 - Léonard, Fabien A1 - Withers, P. J. A1 - Todd, I. A1 - Goodall, R. T1 - X-ray tomography characterisation of lattice structures processed by selective electron beam melting N2 - Metallic lattice structures intentionally contain open porosity; however, they can also contain unwanted closed porosity within the structural members. The entrained porosity and defects within three different geometries of Ti-6Al-4V lattices, fabricated by Selective Electron Beam Melting (SEBM), is assessed from X-ray computed tomography (CT) scans. The results suggest that horizontal struts that are built upon loose powder show particularly high (~20 x 10⁻³ vol %) levels of pores, as do nodes at which many (in our case 24) struts meet. On the other hand, for struts more closely aligned (0° to 54°) to the build direction, the fraction of porosity appears to be much lower (~0.17 x 10⁻³%) arising mainly from pores contained within the original atomised powder particles. KW - Cellular solids KW - Aqdditive manufacturing KW - Computed tomography KW - Titanium alloys PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-413689 UR - http://www.mdpi.com/2075-4701/7/8/300 DO - https://doi.org/10.3390/met7080300 SN - 2075-4701 VL - 7 IS - 8 SP - Article 300, 1 EP - 12 PB - MDPI AN - OPUS4-41368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Al-Terkawi, Abdal-Azim A1 - Scholz, G. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Reinsch, Stefan A1 - Kemnitz, E. A1 - Emmerling, Franziska T1 - Ca- and Sr- tetrafluoroisophthalates: mechanochemical synthesis, characterization, and ab initio structure determination N2 - New fluorinated coordination polymers were prepared mechanochemically by milling the alkaline earth metal hydroxides MII(OH)2·xH2O (MII: Ca, Sr) with tetrafluoroisophthalic acid (H2mBDC-F4). The structures of [{Ca(mBDC-F4)(H2O)2}·H2O] and [{Sr(mBDC-F4)(H2O)2}·H2O] were determined based on ab initio calculations and their powder X-ray diffraction (PXRD) data. The compounds are isomorphous and crystallize in the orthorhombic space group P212121. The determined structures were validated by using extended X-ray absorption (EXAFS) data. The new materials were thoroughly characterized using elemental analysis, thermal analysis, magic angle spinning NMR, and attenuated total reflection-infrared spectroscopy. Further characterization methods such as BET, dynamic vapor sorption, and scanning electron microscopy imaging were also used. Our investigations indicate that mechanochemistry is an efficient method for preparing such materials. KW - Mechanochemistry KW - In situ KW - XRD KW - Coordination polymers PY - 2017 UR - http://pubs.rsc.org/-/content/articlehtml/2017/dt/c7dt00734e DO - https://doi.org/10.1039/c7dt00734e VL - 46 IS - 18 SP - 6003 EP - 6012 AN - OPUS4-41516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Matoga, D. A1 - Roztocki, K. A1 - Wilke, Manuel A1 - Emmerling, Franziska A1 - Oszajca, M. A1 - Fitta, M. A1 - Bałanda, M. T1 - Crystalline bilayers unzipped and rezipped: solid-state reaction cycle of a metal–organic framework with triple rearrangement of intralayer bonds N2 - We present a series of remarkable structural transformations for a family of layered metal–organic frameworks (MOFs) in a three-step solid-state reaction cycle. The cycle represents new dynamic behavior of 2D coordination polymers and involves the sequence of reactions: {[Mn2(ina)4(H2O)2]·2EtOH}n (JUK-1) → {(NH4)2[Mn(ina)2(NCS)2]}n·xH2O (JUK-2) → {[Mn2(ina)2(Hina)2(NCS)2]}n (JUK-3) → JUK-1 (Hina = isonicotinic acid), each accompanied by rearrangement of intralayer coordination bonds and each induced by a different external stimulus. In situ investigation of the first step of the cycle by combined synchrotron X-ray diffraction and Raman spectroscopy reveals direct mechanochemical unzipping of JUK-1 bilayers to respective JUK-2 layers with reaction rates dependent on the milling conditions. In contrast, the reverse zipping of JUK-2 layers involves two steps and proceeds through a new MOF (JUK-3) whose structure was elucidated by powder X-ray diffraction. Magnetic measurements confirm conversions of manganese nodes in the reaction cycle. The findings indicate the possibility of developing coordination-based assemblies with large structural responses for use in smart stimuli-responsive systems and sensor technologies. KW - Mechanochemistry KW - In situ KW - XRD KW - MOF PY - 2017 UR - http://pubs.rsc.org/is/content/articlehtml/2017/ce/c7ce00655a DO - https://doi.org/10.1039/C7CE00655A VL - 19 SP - 2987 EP - 2995 AN - OPUS4-41517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pavlovic, Mato A1 - Zoëga, Andreas A1 - Kurz, J. H. A1 - Zanotelli, Christina T1 - Investigations to introduce the probability of detection method for ultrasonic inspection of hollow axles at Deutsche Bahn N2 - The vast experience with the automated, ultrasonic system for the inspection of hollow railway axles used by Deutsche Bahn shows that much smaller flaws are detectable than required. This results in a number of false calls. False calls lead to unnecessary demounting and disassembling of wheelsets, which generates unnecessary additional costs. In order to adjust the sensitivity of the inspection system to reduce the number of false calls without compromising safety, the capability of the system to detect cracks needs to be comprehensively established. This capability can be quantified by using probability of detection (POD) curves for the system. The multi-parameter POD model makes it possible to include several factors that influence the crack detection in the analysis. The analysis presented in this paper shows that crack position, orientation, depth extension, and shape as well as the geometry of the axle all have influence on the ultrasonic response amplitude. For future work, calculation of the POD using multi-parameter POD model with these parameters is planned. T2 - ESIS TC24 Workshop "Integrity of Railway Structures" CY - Leoben, Austria DA - 24.10.2016 KW - Crack KW - Reliability KW - POD KW - Axle KW - Ultrasonic PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-415201 DO - https://doi.org/10.1016/j.prostr.2017.07.002 SN - 2452-3216 VL - 4 SP - 79 EP - 86 PB - Elsevier, B.V. AN - OPUS4-41520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Moldenhauer, Laura A1 - Helmerich, Rosemarie A1 - Köppe, Enrico A1 - Haamkens, Frank A1 - Wittmann, Jochen ED - Emri, Igor T1 - Experimental feasibility study about moisture in building materials measured with Bluetooth N2 - Structural health monitoring contributes to early damage detection in the built infrastructure. During the last two decades, sensor networks transferred from wired to wireless sensor networks. Several methods exist to measure moisture in building materials. Most of the introduced commercial moisture measurement methods provide information about the local or near surface moisture. A feasibility study is presented to demonstrate, how the Received Signal Strength Indicator (RSSI) of a Bluetooth Low Energy (BLE) signal, transmitted from the BLE-module embedded in building materials, correlate with changing moisture content. The feasibility of this influence was investigated in the presented study. The maximum and minimum RSSI were systematically recorded and analysed. T2 - 33nd Danubia Adria Symposium on Advances in Experimental Mechanics CY - Portoroz, Slovenia DA - 20.09.2016 KW - BLE KW - Long-Term Monitoring KW - Network KW - Structural Health Monitoring KW - Moisture Measurement KW - RSSI KW - Bluetooth Low Energy KW - Sensor PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S2214785317308398 DO - https://doi.org/10.1016/j.matpr.2017.06.053 SN - 2214-7853 VL - 4 IS - 5, Part 1 SP - 5889 EP - 5892 PB - Elsevier Ltd. AN - OPUS4-41585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weltschev, Margit A1 - Heming, Frank A1 - Haufe, Manuela A1 - Heyer, Martina T1 - The influence of the age of biodiesel and heating oil with 10 % biodiesel on the resistance of sealing materials at different temperatures T1 - Der Einfluss des Alters von Biodiesel und Heizöl mit 10 % Biodiesel auf die Beständigkeit der Dichtungswerkstoffe bei verschiedenen Temperaturen N2 - The objective of this research was to determine the resistance of frequently used sealing materials such as fluorocarbon rubber (FKM), fluorosilicone rubber (FVMQ), silicone rubber (VMQ), ethylene-propylene-diene rubber (EPDM), chloroprene rub-ber (CR), chlorosulfonated polyethylene (CSM), butyl rubber (IIR), acrylonitrile buta-diene rubber (NBR), polyester urethane rubber (PUR) and polyamide (PA) in non-aged/aged biodiesel and heating oil with 10 % biodiesel at 20 °C, 40 °C and 70 °C. Mass, tensile properties and Shore hardness A/D (for polyamide) of the test speci-mens were determined before and after the exposure for 84/42 days in the aged and non-aged fuels of different age. Biodiesel fuels are easily oxidized and contain acids and water. The sealing materi-als: acrylonitrile butadiene rubber, butyl rubber, chloroprene rubber, chlorosulfonated polyethylene and ethylene-propylene-diene rubber and were generally not resistant to biodiesel and heating oil with 10 % biodiesel. Fluorocarbon rubber, fluorosilicone rubber and polyamide were the most resistant materials in all tested fuels up to 70 °C. The degree of damage to the sealing materials increased with higher test temperatures and the age of the fuels. KW - Sealing materials KW - Biofuels KW - Tensile properties KW - Shore hardness PY - 2017 DO - https://doi.org/10.1002/mawe.201700058 SN - 0933-5137 SN - 1521-4052 VL - 48 IS - 9 SP - 837 EP - 845 PB - Wiley-VCH Verlag GmbH & Co.KGaA CY - Weinheim AN - OPUS4-42077 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krütt, Enno T1 - Ermüdungsbedingte Degradation von Fahrbahnbeton - Einfluss auf den Stofftransport T1 - Fatigue-induced degradation of deck concrete influence on the material transport N2 - In den letzten 15 Jahren hat im deutschen Autobahnnetz die Anzahl von Schäden an Betonfahrbahnen, die vor 2005 er-richtet wurden zugenommen. Dies führt oft zu einer Vermin-derung der Lebensdauer von 30 auf 10 bis 15 Jahre. Trotz umfassender Untersuchungen wurde die Ursache bis jetzt nicht eindeutig geklärt, jedoch scheint die Alkali-Kieselsäure-Reaktion (AKR) hierbei eine Rolle zu spielen. Vor diesem Hintergrund wurden AKR-Performance-Tests entwickelt, die jedoch die mechanischen Einwirkungen aus Klima und Ver-kehr nicht berücksichtigen. Aus diesem Grund wurde eine AKR-Forschergruppe von der Deutschen Forschungsgemein-schaft ins Leben gerufen, welche sich experimentell und auf Simulationsebene mit diesem Thema befasst. Inhalt dieses Beitrages sind ausgewählte Ergebnisse des an der BAM bear-beiteten experimentellen Projektteils, welche in eine auf die Auswirkung einer mechanischen Degradation fokussierte Promotionsarbeit einfließen. Ziel der ausgewählten Untersuchung ist es, den Einfluss einer mechanisch induzierten Betondegradation auf den Stofftrans-port herauszuarbeiten. Hierzu wird ein großformatiger Balken einem zyklischen Vier-Punkt Biegezugversuch mit einer Anzahl von 5 Mio. Lastwechseln unterzogen. Während des Versuches findet ein Schadensmonitoring mit verschiedenen zerstörungsfreien Prüftechniken statt. Hierzu zählen Deh-nungsmessungen, Schallemissionsanalyse und Ultraschall-messungen. Nach dem zyklischen Belastungs-versuch werden kleinformatige Probekörper aus dem belasteten Balken entnommen. Als Referenz dienen unbelas-tete Probekörper aus der gleichen Herstellungscharge. Die Oberflächen der entnommenen Probekörper werden in einem kapillaren Saugversuch zum einen mit deionisiertem Wasser und zum anderen mit einer 3,6 %igen NaCl-Lösung beauf-schlagt. Während der Saugversuche dienen verschiedene zerstörungsfreie bzw. -arme Messmethoden dazu, die Feuch-teaufnahme bzw. -verteilung in den Probekörpern zu messen. Hierzu gehören neben der Gravimetrie die Messung mit NMR (Nuclear-Magnetic-Resonance) sowie TDR (Time-Domain-Reflectometry). Nach den Saugversuchen wird die Na- und Cl-Verteilung an den mit NaCl-Lösung beaufschlagten Pro-bekörpern zerstörend mittels LIBS (Laser-Induced-Breakdown-Spectroscopy) ermittelt. Erste Ergebnisse zeigen, dass die zyklische Ermüdungsdegradation den Stofftransport tendenziell verstärkt. KW - Degradation KW - Stofftransport KW - Fahrbahnbeton PY - 2017 SN - 0005-9900 SN - 1437-1006 VL - 112 IS - 7 SP - 458 EP - 458 AN - OPUS4-41097 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bochnig, M. S. A1 - Oh, M.-J. A1 - Nagel, T. A1 - Jost-Brinkmann, P.-G. A1 - Ziegler, Fred T1 - Comparison of the shock absorption capacities of different mouthguards N2 - In this in vitro study, the protective qualities of different mouthguard types were examined during small hard object collisions. The aim was to investigate inconclusive aspects of hard inserts, nylon nets, and air spaces as reinforcements in the anterior region and the protection qualities of ethylene vinyl acetate (EVA). Five different mouthguards with a labial thickness between 2 mm and 11 mm made of materials of varying stiffness were investigated. As a negative control, the same experiments were performed without a mouthguard. Different combinations of EVA and labial inserts ((polyethylene terephthalate glycol-modified [PETG]), nylon mesh, air space) were tested. Using a stainless steel pendulum device, blows of different energy (0.07-2.85 joules) were applied to the center of the crown of a pivoted tooth in a custom-built jaw model. A laser Doppler vibrometer measured the tooth deflection, while an acceleration sensor attached to the pendulum measured the braking accelerations. Tooth deflection was reduced up to 99.7% compared to no mouthguard, and the braking acceleration was reduced up to 72.2% by increasing the mouthguards' labial thickness in combination with labial inserts of different stiffness and a built-in air space between the front teeth and the mouthguard. The mouthguards made of soft materials (EVA with nylon mesh) showed slightly better protection qualities than the more rigid mouthguards of similar thickness (PETG; P<.05). However, with increasing impact energy, their protective capacities decreased to a greater extent than the stiffer mouthguards. The combination of increased labial thickness and labial inserts of varying stiffness and eventually an air space offers the best protection capacities for hard, small object collisions. KW - Shock absorbtion KW - Hard object collisions KW - Mouthguard PY - 2017 DO - https://doi.org/10.1111/edt.12324 SN - 1600-4469 VL - 33 IS - 3 SP - 205 EP - 213 PB - John Wiley & Sons, Ltd CY - Hoboken, NJ, USA AN - OPUS4-41098 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adel-Khattab, D. A1 - Giacomini, F. A1 - Gildenhaar, R. A1 - Berger, G. A1 - Gomes, Cynthia A1 - Linow, Ulf A1 - Hardt, M. A1 - Peleska, B. A1 - Günster, Jens A1 - Stiller, M. A1 - Houshmand, A. A1 - Ghaffar, K. A1 - Gamal, A. A1 - El-Mofty, M. A1 - Knabe, C. T1 - Development of a synthetic tissue engineered three- dimensional printed bioceramic-based bone graft with homogenously distributed osteoblasts and mineralizing bone matrix in vitro N2 - Over the last decade there have been increasing efforts to develop three-dimensional (3D) scaffolds for bone tissue Engineering from bioactive ceramics with 3D printing emerging as a promising technology. The overall objective of the present study was to generate a tissue engineered synthetic bone graft with homogenously distributed osteoblasts and mineralizing bone Matrix in vitro, thereby mimicking the advantageous properties of autogenous bone grafts and facilitating usage for reconstructing segmental discontinuity defects in vivo . To this end, 3D scaffolds were developed from a silica-containing calcium alkali orthophosphate, using, fi rst, a replica technique – the Schwartzwalder – Somers method – and, second, 3D printing, (i.e. rapid prototyping). The mechanical and physical scaffold properties and their potential to facilitate homogenous colonization by osteogenic cells and extracellular bone matrix formation throughout the porous scaffold architecture were examined. Osteoblastic cells were dynamically cultured for 7 days on both scaffold types with two different concentrations of 1.5 and 3 × 10⁹ cells/l. The amount of cells and bone matrix formed and osteogenic marker expression were evaluated using hard tissue histology, immunohistochemical and histomorphometric analysis. 3D-printed scaffolds (RPS) exhibited more micropores, greater compressive strength and silica release. RPS seeded with 3 × 10⁹ cells/l displayed greatest cell and extracellular Matrix formation, mineralization and osteocalcin expression. In conclusion, RPS displayed superior mechanical and biological properties and facilitated generating a tissue engineered synthetic bone graft in vitro, which mimics the advantageous properties of autogenous bone grafts, by containing homogenously distributed terminally differentiated osteoblasts and mineralizing bone matrix and therefore is suitable for subsequent in vivo implantation for regenerating segmental discontinuity bone defects. KW - Bone tissue engineering KW - Calcium alkali orthophosphate KW - Rapid prototyping KW - Scaffold KW - Mandible PY - 2017 DO - https://doi.org/10.1002/term.2362 SN - 1932-6254 SN - 1932-7005 VL - 12 IS - 1 SP - 44 EP - 58 PB - Wiley Online Library AN - OPUS4-40745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dutto, Paola A1 - Stickle, M. M. A1 - Pastor, M. A1 - Manzanal, D. A1 - Yague, A. A1 - Tayyebi, S. A1 - Lin, C. A1 - Elizalde, M. D. ED - Cervera, Miguel T1 - Modelling of fluidised geomaterials: the case of the Aberfan and the Gypsum tailings impoundment flowslides N2 - The choice of a pure cohesive or a pure frictional viscoplastic model to represent the rheological behaviour of a flowslide is of paramount importance in order to obtain accurate results for real cases. The principal Goal of the present work is to clarify the influence of the type of viscous model—pure cohesive versus pure frictional—with the numerical reproduction of two different real flowslides that occurred in 1966: the Aberfan flowslide and the Gypsum tailings impoundment flowslide. In the present work, a depth-integrated model based on the v-pw Biot–Zienkiewicz formulation, enhanced with a diffusion-like equation to account for the pore pressure Evolution within the soil mass, is applied to both 1966 cases. For the Aberfan flowslide, a frictional viscous model based on Perzyna viscoplasticity is considered, while a pure cohesive viscous model (Bingham model) is considered for the case of the Gypsum flowslide. The numerical approach followed is the SPH method, which has been enriched by adding a 1D finite difference grid to each SPH node in order to improve the description of the pore water evolution in the propagating mixture. The results obtained by the performed simulations are in agreement with the documentation obtained through the UK National Archive (Aberfan flowslide) and the International Commission of large Dams (Gypsum flowslide). KW - Aberfan flowslide KW - SPH KW - Landslide propagation modelling KW - Perzyna viscoplasticity PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-410493 DO - https://doi.org/10.3390/ma10050562 SN - 1996-1944 VL - 10 IS - 5 SP - 562, 1 EP - 562, 21 AN - OPUS4-41049 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mushtaq, S. A1 - Steers, E.B.M. A1 - Barnhart, D. A1 - Churchill, G. A1 - Kasik, M. A1 - Richter, Silke A1 - Pfeifer, Jens A1 - Putyera, K. T1 - The production of doubly charged sample ions by “charge transfer and ionization” (CTI) in analytical GD-MS N2 - Normally, in analytical GD-MS, the doubly charged metallic ion signals from the sample are several orders of magnitude less than the corresponding singly charged signals. However, we have observed that using a neon plasma, the M++ signals of some elements, which have double ionization energies close to the first ionization energy of neon, are of the same order as the M+ signal. Doubly charged ions may be produced directly in the discharge cell by electron ionization (EI), and also by two electron Penning ionization (TEP), but these processes cannot explain the above effect. In this paper, we suggest that an additional process named as ‘Charge Transfer and Ionization’ (CTI) produces such ions either in their ionic ground state or in an excited state. To confirm that this process is typical of the discharges used in GD-MS and not an artefact of any particular form of cell and ion extraction system, we have carried out comprehensive experimental measurements using three different GD-MS instruments, viz., Nu Astrum, VG9000 and ELEMENT GD and our results provide clear evidence for CTI. This is the first time the process has been identified as an ionization process in analytical GD-MS. CTI must be differentiated from Asymmetric Charge Transfer (ACT), which is a “selective” process and requires a close energy match (e.g. ΔE < 0.5 eV for a strong effect). On the other hand, CTI is “non-selective” in the sense that a close energy match is not required (e.g. a strong effect is observed with ΔE ∼ 2 eV), although the process only occurs for a limited number of elements, depending on the plasma gas used and the total energy required to doubly ionize the metallic atom. KW - Titanium KW - Glow discharge processes KW - Doubly charged ions KW - The charge transfer and ionization process (CTI) KW - Krypton KW - Neon PY - 2017 DO - https://doi.org/10.1039/C6JA00415F SN - 0267-9477 SN - 1364-5544 VL - 32 IS - 9 SP - 1721 EP - 1729 PB - Royal Society of Chemistry AN - OPUS4-41108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Optimization of welding loads with narrow groove and application of modified spray arc process N2 - Current efforts for lightweight design result in a growing application of high-strength fine-grained structural steel in modern constructions, e.g. mobile cranes, with yield strength from 960 MPa. The design of welded structures and welding processes becomes more challenging with increasing material strength and elastic ratios. High residual stresses are able to diminish lifetime, load capacity and component safety and should be avoided. Recent analyses have shown strong influences of heat control and restraint of the weld due to arising reaction stresses, superimposing with local residual welding stresses. Modern inverter technologies allowed the development of numerous modified spray arc processes driven by power source manufacturers, which provide virtually similar features and several benefits, enabling welding of narrower seams with reduced weld volumes and total heat inputs. This research focuses on welding loads due to modified weld seams. The global reaction forces and moments and their superposition with local residual stresses in welded components due to external shrinkage restraints were investigated using a special testing facility and XRD. The restraint intensity, weld seam geometry and welding process were varied for statistical evaluations of resulting welding loads. When welding under restraint, a reduction of the weld seam volume causes significantly lower reaction stress levels. KW - Residual stresses KW - MAG welding KW - Restraint KW - High-strength steels KW - Process parameters PY - 2017 DO - https://doi.org/10.1007/s40194-017-0484-3 SN - 1878-6669 SN - 0043-2288 VL - 61 IS - 6 SP - 1077 EP - 1087 PB - Springer CY - Berlin Heidelberg AN - OPUS4-41071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kohler, C. A1 - Nikfalazar, M. A1 - Heunisch, Andreas A1 - Schulz, Bärbel A1 - Mikolajek, M. A1 - Rabe, Torsten A1 - Jakoby, R. A1 - Binder, J. T1 - Implementation of Ba0.6Sr0.4TiO3-ZnO-B2O3 based tunable microwave phase shifters in LTCC technology N2 - Tunable dielectric Ba0.6Sr0.4TiO3-ZnO-B2O3 thick-films were analyzed regarding their integration potential into the LTCC technology. Therefore, tunable loaded line phase shifters based on metal-insulator-metal varactors with single- and double- printed BST thick-films were fabricated and co-sintered inside a four layer LTCC module. Microstructural and chemical investigations showed a sufficient compatibility and adhesion between the silver, BST composite and LTCC layers and a resulting morphology depending on the processing route. The microwave characterization of the LTCC-embedded phase shifters revealed comparable results to phase shifters with the same design on alumina substrates. KW - Thick films KW - Dielectric materials KW - Electroceramics PY - 2017 DO - https://doi.org/10.1111/ijac.12687 SN - 1546-542X SN - 1744-7402 VL - 14 IS - 4 SP - 574 EP - 582 PB - Wiley CY - Hoboken, NY, USA AN - OPUS4-41086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiedmann, A. A1 - Weise, Frank A1 - Kotan, E. A1 - Müller, H. S. A1 - Meng, Birgit T1 - Effects of fatigue loading and alkali-silica reaction on the mechanical behaviour of pavement concrete N2 - The primary aim of this paper is to analyze the impact of mechanical pre-damage and alkali–silica reaction (ASR) on the fracture mechanical properties of pavement concrete. For this purpose, a four point bending test was applied to large format beams to produce a defined level of cyclic pre-damage. The fatigue-induced concrete degradation process was simultaneously recorded using a testing procedure specifically developed for the purpose. In addition, fatigue-induced cracks on extracted drilling cores were spatially visualized and quantified using micro X-ray 3D-computed tomography (3D-CT). The storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment showed that pre-damage leads to an increase in ASR damage processes. Subsequent structural mechanical investigations on small format specimens with and without pre-damage show that fatigue loading and ASR significantly influence fracture mechanical parameters of the concrete. KW - Acoustic emissions analysis KW - Alkali-silica reaction KW - Concrete pavement KW - Fatigue loading KW - Fracture energy KW - Monitoring of damage KW - Tensile strength KW - Ultrasonic velocity PY - 2017 DO - https://doi.org/10.1002/suco.201600179 SN - 1751-7648 SN - 1464-4177 VL - 18 IS - 4 SP - 539 EP - 549 PB - Ernst & Sohn AN - OPUS4-41007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Przondziono, R. A1 - Timothy, J. J. A1 - Weise, Frank A1 - Krütt, Enno A1 - Breitenbücher, R. A1 - Meschke, G. A1 - Hofmann, M. T1 - Degradation in concrete structures due to cyclic loading and its effect on transport processes - Experiments and modeling N2 - According to the objectives of the research group 1498, this paper deals with degradation effects in concrete structures that are caused by cyclic flexural loading. The goal is to determine their influence on the fluid transport processes within the material on the basis of experimental results and numerical simulations. The overall question was, to which extent the ingress of externally supplied alkalis and subsequently an alkali-silica reaction are affected by such modifications in the microstructure. Degradation in the concrete microstructure is characterized by ultrasonic wave measurements as well as by microscopic crack analysis. Furthermore, experiments on the penetration behavior of water into the investigated materials were performed. The penetration behavior into predamaged concrete microstructures was examined by the classical Karsten tube experiment, nuclear magnetic resonance method, and time domain reflectometry techniques. In order to create an appropriate model of the material's degradation on the water transport, the Darcy law was applied to describe the flow in partially saturated concrete. Material degradation is taken into account by an effective permeability that is dependent on the state of degradation. This effective permeability is obtained by the micromechanical homogenisation of the flow in an Representative Elementary Volume (REV) with distributed ellipsoidal microcracks embedded in a porous medium. The data gained in the microscopic crack analysis is used as input for the micromechanical model. Finite element simulations for unsaturated flow using the micromechanical model were compared with the experimental results showing good qualitative and quantitative agreement. KW - Alkali ingress KW - Alkali-silica reaction KW - Computational model for unsaturated flow KW - Cyclic loading KW - Degradation KW - Micromechanics model KW - Transport processes PY - 2017 DO - https://doi.org/10.1002/suco.201600180 SN - 1751-7648 SN - 1464-4177 VL - 18 IS - 4 SP - 519 EP - 527 PB - Ernst & Sohn AN - OPUS4-41008 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zeegers, G. P. A1 - Steinhoff, R. F. A1 - Weidner, Steffen A1 - Zenobi, R. T1 - Evidence for laser-induced redox reactions in matrix-assisted laserdesorption/ionization between cationizing agents and target plate material: a study with polystyrene and trifluoroacetate salts N2 - Matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS) is often applied to assess the dispersity and the end groups of synthetic polymers through the addition of cationizing agents. Here weaddress how these cation adducts are formed using polystyrene (PS) as a model polymer. We analyzed PSby MALDI-MS with a 2-[(2E)-3-(4-tert-butylphenyl)-2-methylprop-2-enylidene]malononitrile (DCTB) as the matrix and a range of trifluoroacetate (TFA) salts as cationizing agents on a range of different targetplate materials (copper, 1.4301 stainless steel, aluminum, Inconel 625, Ti90/Al6/V4 and chromium-, gold-and silver-plated stainless steel). It was found that on a stainless steel substrate the metal cations Al+,Li+, Na+, Cu+and Ag+formed polystyrene adducts, whereas K+, Cs+, Ba2+, Cr3+, Pd2+, In3+, or their lower oxidation states, did not. For the copper and silver substrates, PS and DCTB adduct formation with cations liberated from these target plate materials was observed upon addition of a cationizing agent, which indicates the occurrence of redox reactions between the added TFA salts and the target plate material. Judging from their standard electrode potentials, these redox reactions would not normally occur, i.e.,they require an additional energy input, strongly suggesting that the observed redox reactions are laser-induced. Furthermore, copper granules were found to successfully sequester PS from a tetrahydrofuran(THF) solution, consistent with the view complex formation with the copper target plate can take place prior to the MALDI-MS measurement. KW - Polymer MALDI KW - Cationization KW - Polystyrene KW - Laser-induced redox reactions KW - Target plate material PY - 2017 DO - https://doi.org/10.1016/j.ijms.2016.10.007 SN - 1387-3806 SN - 1873-2798 VL - 416 SP - 80 EP - 89 PB - Elsevier B.V. AN - OPUS4-41146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Boin, M. A1 - Wimpory, Robert A1 - Kannengießer, Thomas A1 - Gibmeier, J. A1 - Schröpfer, Dirk T1 - Residual stresses of LTT welds in large-scale components N2 - Residual stresses of welds become more and more important influencing cold cracking as well as the fatigue life of welded components. Low transformation temperature (LTT) filler materials offer the opportunity to alter the residual stresses already during the welding process by means of ad- justed martensite phase transformation temperature (MS). In the current paper, welding residual stresses are studied putting the focus on MS while joining heavy steel sections with a thickness of 20 and 25 mm, respectively. The residual stress state was determined at the top surface using X-ray diffraction as well as in the bulk by neutron diffraction. The results com- pare the residual stresses present in a conventional weld and LTT welds when multi-pass welding of large-scale compo- nents was applied. Repeated phase transformation in the case of the LTT weld is more vital for the residual stresses present in the real-life-like joints. This accounts for the top surface in longitudinal direction but is most pronounced for the bulk of the welds. Detrimental tensile residual stresses are mainly re- duced in the bulk in comparison to a conventional filler wire even in multi-pass welds of thick steel sections. T2 - IIW AA 2016 CY - Melbourne, Australia DA - 10.07.2016 KW - LTT KW - Welding residual stress KW - Phase transformation KW - Interpass temperature PY - 2017 DO - https://doi.org/10.1007/s40194-017-0502-5 SN - 0043-2288 SN - 1878-6669 VL - 61 IS - 6 SP - 1089 EP - 1097 PB - Springer CY - Heidelberg AN - OPUS4-41169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel A1 - Wolthusen, Helmut T1 - Unusual Corrosion Behavior of 1.4542 Exposed a Laboratory Saline Aquifer Water CCS-Environment N2 - Differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Surface corrosion layers are homogeneous but unusually discontinuously ellipsoidal. After 8000 h at 100 bar maximum corrosion rate in the liquid phase is approximately 0.014 mm/year, with normalizing providing best corrosion resistance and approximately 0.003 mm/year in the supercritical phase where hardening+tempering at 670 °C leads to lowest corrosion rates. KW - CO2-storage KW - Supercritical CO2 KW - Steel KW - Pipeline KW - Corrosion KW - CCS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418472 DO - https://doi.org/10.1016/j.egypro.2017.03.1679 VL - 114 SP - 5229 EP - 5240 PB - Elsevier Ltd. AN - OPUS4-41847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taabache, Soraya A1 - Bertin, Annabelle T1 - Vesicles from amphiphilic dumbbells and Janus dendrimers: bioinspired self-assembled structures for biomedical applications N2 - The current review focuses on vesicles obtained from the self-assembly of two types of dendritic macromolecules, namely amphiphilic Janus dendrimers (forming dendrimersomes) and amphiphilic dumbbells. In the first part, we will present some synthetic strategies and the various building blocks that can be used to obtain dendritic-based macromolecules, thereby showing their structural versatility. We put our focus on amphiphilic Janus dendrimers and amphiphilic dumbbells that form vesicles in water but we also encompass vesicles formed thereof in organic solvents. The second part of this review deals with the production methods of these vesicles at the nanoscale but also at the microscale. Furthermore, the influence of various parameters (intrinsic to the amphiphilic JD and extrinsic—from the environment) on the type of vesicle formed will be discussed. In the third part, we will review the numerous biomedical applications of these vesicles of nano- or micron-size. KW - Janus dendrimers KW - Amphiphilic dumbbells KW - Self-assembled structures KW - Dendrimersomes KW - Artificial cells PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418245 DO - https://doi.org/10.3390/polym9070280 SN - 2073-4360 VL - 9 IS - 7 SP - Article 280, 1 EP - 36 AN - OPUS4-41824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hentrich, D. A1 - Taabache, Soraya A1 - Brezesinski, G. A1 - Lange, Nele A1 - Unger, Wolfgang A1 - Kübel, C. A1 - Bertin, Annabelle A1 - Taubert, A. T1 - A dendritic amphiphile for efficient control of biomimetic calcium phosphate mineralization N2 - The phase behavior of a dendritic amphiphile containing a Newkome-type dendron as the hydrophilic moiety and a cholesterol unit as the hydrophobic segment is investigated at the air–liquid interface. The amphiphile forms stable monomolecular films at the air–liquid interface on different subphases. Furthermore, the mineralization of calcium Phosphate beneath the monolayer at different calcium and phosphate concentrations versus mineralization time shows that at low calcium and Phosphate concentrations needles form, whereas flakes and spheres dominate at higher concentrations. Energy-dispersive X-ray spectroscopy, X-ray photoelectron spectroscopy, and electron diffraction confirm the formation of calcium phosphate. High-resolution transmission electron microscopy and electron diffraction confirm the predominant formation of octacalcium phosphate and hydroxyapatite. The data also indicate that the final products form via a complex multistep reaction, including an association step, where nano-needles aggregate into larger flake-like objects. KW - Dendritic amphiphile KW - Calcium phosphate KW - Biomineralization PY - 2017 DO - https://doi.org/10.1002/mabi.201600524 SN - 1616-5187 SN - 1616-5195 VL - 17 IS - 8 SP - Article 1600524, 1 EP - 14 AN - OPUS4-41825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stelzner, Ludwig A1 - Powierza, Bartosz T1 - Thermisch induzierter Feuchtetransport in HPC T1 - Thermally induced Moisture Transport in structure density High-performance Concrete N2 - Die Entwicklung von leistungsfähigen Fließmitteln in den letzten Jahrzehnten ermöglicht die Herstellung von Beton mit sehr geringem w/z-Wert, bei gleichzeitig guter Verarbeitbar-keit. Die Reduzierung des w/z-Wertes geht dabei mit einer Erhöhung der Festigkeit und einer Verdichtung der Gefü-gestruktur einher. Aufgrund der hohen Druckfestigkeit finden diese Hochleistungsbetone vermehrten Einsatz im Hoch-, Brücken-, und Tunnelbau. Unter Brandbeanspruchung neigen diese Hochleistungsbetone allerdings zu explosionsartigen Abplatzungen. Diese werden nach derzeitigem Stand auf thermomechanische und thermohydraulische Prozesse zurückgeführt. Letztere beruhen auf der Generierung hoher Wasserdampfdrücke in einseitig brandbeanspruchten Beton-bauteilen, die zum einen auf die geringe Permeabilität des Hochleistungsbetons und zum anderen auf die Bildung einer wassergesättigten Zone, der sogenannten „moisture clog“ zurückzuführen sind. Dabei spielen Verdampfungs- und Kondensationsvorgänge sowie der vorhandene Temperatur-gradient eine wichtige Rolle. Die Interaktion des Feuchtetra-nsportes mit den Gefügeveränderungen während der thermi-schen Beanspruchung soll im Rahmen weiterer Versuche eingehend untersucht werden. Zur Analyse des Feuchtetransports während der thermischen Beanspruchung wurden miniaturisierte Prüfkörper aus Hoch-leistungsbeton hergestellt, die mit Hilfe eines elektrischen Heizelements einseitig erwärmt wurden. Zur Sicherstellung eines eindimensionalen Wärme- und Feuchtetransportes ist der Betonprüfkörper mit einer speziellen Glaskeramik und einer Hochtemperaturwolle ummantelt. Simultan zur Erwär-mung werden eine Reihe röntgentomographischer Aufnah-men durchgeführt. Durch Differenzbildung aufeinanderfol-gender Aufnahmen können Dichteveränderungen lokal und zeitlich aufgelöst werden. Diese lassen Rückschlüsse auf Än-derungen der Feuchteverteilung im Prüfkörper während der Erwärmung zu. Parallel dazu werden Untersuchungen mittels NMR-Relaxometrie (nuclear magnetic resonance) vor und nach der thermischen Beanspruchung durchgeführt. Diese Prüfmethodologie ermöglicht es erstmals, die Veränderungen der Feuchteverteilung infolge thermischer Beanspruchung im Hochleistungsbeton von den Gelporen bis hin zu vorhande-nen Verdichtungsporen abzubilden. So zeigen erste Ergebnis-se, dass die gewählten Untersuchungsmethoden Veränderun-gen der Feuchteverteilung im Prüfkörper räumlich und zeitlich auflösen können. KW - Abplatzen KW - Spalling KW - Brand KW - Feuchtetransport KW - Hochleistungsbeton KW - Röntgen-3D-Computertomographie KW - NMR KW - Fire KW - Moisture clog KW - Moisture transport KW - HPC KW - HSC KW - X-ray CT PY - 2017 DO - https://doi.org/10.1002/best.201700022 SN - 0005-9900 SN - 1437-1006 VL - 112 IS - 7 SP - 486 EP - 486 PB - Ernst & Sohn CY - Berlin AN - OPUS4-41826 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meißner, G. A1 - Dirican, D. A1 - Jäger, Christian A1 - Braun, T. A1 - Kemnitz, E. T1 - Et3GeH versus Et3SiH: controlling reaction pathways in catalytic C–F bond activations at a nanoscopic aluminum chlorofluoride† N2 - Catalytic C–F bond activation reactions of mono- and polyfluoroalkanes at Lewis acidic amorphous aluminum chlorofluoride (ACF) are presented. The hydrogen sources Et3GeH or Et3SiH control the selectivity of the conversions. The immobilization of Et3GeH at ACF resulted in catalytic dehydrohalogenation reactions to yield olefins under very mild conditions. In contrast, if Et3SiH is immobilized at ACF, C–C coupling occured and the formation of Friedel–Crafts products was observed. MAS NMR spectroscopic studies revealed information about the surface binding of the substrates. KW - Vapor-phase hydrofluorination KW - Carbon-fluorine bonds KW - Vinyl fluoride KW - Phosphine-ligands KW - Room-temperature KW - Building-blocks KW - Etal-complexes KW - Germylium ions KW - Lewis-acids KW - Hydrodefluorination PY - 2017 DO - https://doi.org/10.1039/c7cy00845g SN - 2044-4753 SN - 2044-4761 VL - 7 IS - 15 SP - 3348 EP - 3354 PB - The Royal Society of Chemistry AN - OPUS4-41836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Böhning, Martin A1 - Oehler, H. A1 - Alig, I. A1 - Niebergall, Ute T1 - Environmental stress cracking of polyethylene high density (PE-HD) induced by liquid media – Validation and verification of the full-notch creep test (FNCT) T1 - Umgebungsinduzierte Spannungsrissbildung von Polyethylen- Werkstoffen hoher Dichte durch flüssige Medien – Validierung und Verifizierung des Kriechversuchs an Probekörpern mit umlaufender Kerbe N2 - The full-notch creep test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure. The test is of greatest importance for pipe and blow molding types of polyethylene, high density (PE-HD). Usually the full-notch creep test is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100. In our study, selected relevant polyethylene, high density materials are investigated also in real media – practical formulations as well as representative pure chemicals – and influences of temperature and geometry of specimen and notch are explicitly addressed. Furthermore, the investigations comprise also the environmental stress cracking behavior of polyethylene, high density in media that are sorbed to a significant extent – examples are diesel and biodiesel – based on comparison with samples previously saturated with those media. Thus, also the underlying diffusion controlled sorption process has to be assessed before. The investigations were performed using a full-notch creep testing device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation. N2 - Der Kriechversuch an Probekörpern mit umlaufender Kerbe (FNCT) wird flächendeckend angewendet, um das Verhalten von Polyolefinen sowohl gegenüber langsamen Risswachstums (SCG) bei Kontakt mit „inerten“ Medien als auch gegenüber umgebungsbedingtem Spannungsrisswachstum (ESC), bei welchem das umgebende Medium entscheidenden Einfluss auf den Schädigungsmechanismus und die Standzeit hat, zu charakterisieren. Der Test ist von großer Bedeutung bei der Analyse von hochdichten Polyethylen-Typen, die als Rohr- und Blasformwerkstoffe angewendet werden – dabei besonders für Transport und Verpackung von Gefahrstoffen, aber auch für weitere Hochleistungsanwendungen. Üblicherweise wird der Kriechversuch an Probekörpern mit umlaufender Kerbe als Normmethode (ISO 16770) unter Verwendung einiger weniger universeller Modellflüssigkeiten, wie z. B. Arkopal N 100, durchgeführt. In dieser Studie werden ausgewählte, marktrelevante Polyethylen-Werkstoffe hoher Dichte in realen Medien – praktisch verwendete Gefahrgüter sowie repräsentative reine Chemikalien – untersucht und explizit die Einflüsse von Temperatur und Prüfkörper- sowie Kerbgeometrie adressiert. Weiterhin beinhalten die Untersuchungen die Analyse des umgebungsbedingten Spannungsriss-Verhaltens von Polyethylen hoher Dichte in Medien, die maßgeblich vom Werkstoff sorbiert sind – beispielsweise mit Kraftstoffen wie diesel und biodiesel – basierend auf dem Vergleich mit vorgesättigten Probekörpern. Der dabei vorliegende diffusionsgesteuerte Sorptionsprozess muss dementsprechend zuvor evaluiert werden. Alle Untersuchungen wurden mithilfe einer Kriechversuchsanlage an Probekörpern mit umlaufender Kerbe mit 12 Stationen durchgeführt, welche jeweils mit einer individuell ansteuerbaren elektronischen Spannungs- und Temperatursteuerung sowie fortwährender Online-Überwachung der Prüfkörperdehnung ausgestattet sind. KW - Full-notch creep test (FNCT) KW - Polyethylene (PE-HD) KW - Environmental stress cracking (ESC) KW - Slow crack growth (SCG) KW - Biodiesel PY - 2017 DO - https://doi.org/10.1002/mawe.201700065 SN - 1521-4052 SN - 0933-5137 VL - 48 IS - 9 SP - 846 EP - 854 PB - Wiley-VCH CY - Weinheim AN - OPUS4-41885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Falkenreck, Thora A1 - Klein, M. A1 - Böllinghaus, Thomas T1 - Dynamic compressive behaviour of weld joints N2 - Materials used in military applications have to withstand multiple threats like ballistics and explosions. Thus, high-strength low alloyed (HSLA) steels are used. The main joining technique for metals is welding. Therefore, analysing the dynamic impact behaviour of high-strength welds is very important to fulfil these demands. Investigation of welds at high strain rates has rarely been conducted in the past. To determine the dynamic impact behaviour of hybrid laser-arc welds, the Split Hopkinson Pressure Bar (SHPB) technique was used. The base material was a quenched and tempered fine-grained armour steel with yield strength of 1100 MPa. First, a full hybrid laser-arc weld was investigated by extracting specimens consisting of weld metal and heat affected base material. The influence of two variables, the cooling time between 800 °C and 500 °C (t8/5) and strength of filler material, on the impact behaviour was studied. The cooling time t8/5 was varied by preheating to influence the microstructure in the HAZ and to analyse the effect on the hardness and dynamic compressive strength. Subsequent analysis to detail the original Investigation was carried out by dilatometer heat treatment of specimens to create homogenous subzones of the weld. These specimens have a homogenous microstructure of HAZ and were tested by SHPB to determine the stress-strain characteristics for the different microstructures of HAZ. The results of the weld specimen showed the effect of preheating and filler material strength on the dynamic compressive behaviour. The analysis of the different microstructures of the HAZ indicated that especially the tempered microstructure caused a reduction in dynamic compressive strength. KW - SHPB KW - Hybrid laser-arc weld KW - Dilatometry PY - 2017 DO - https://doi.org/10.1016/j.msea.2017.07.032 SN - 0921-5093 SN - 1873-4936 VL - 702 SP - 322 EP - 330 AN - OPUS4-41904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obaton, A-F. A1 - Fain, J. A1 - Djemaï, M. A1 - Meinel, Dietmar A1 - Léonard, Fabien A1 - Mahé, E. A1 - Lécuelle, B. A1 - Fouchet, J-J. A1 - Bruno, Giovanni T1 - In vivo XCT bone characterization of lattice structured implants fabricated by additive manufacturing N2 - Several cylindrical specimens and dental implants, presenting diagonal lattice structures with different cell sizes (600, 900 and 1200 µm) were additively manufactured by selective laser melting process. Then they were implanted for two months in a sheep. After removal, they were studied by Archimedes’ method as well as X-ray computed tomography in order to assess the penetration of bone into the lattice. We observed that the additive manufactured parts were geometrically conform to the theoretical specifications. However, several particles were left adhering to the surface of the lattice, thereby partly or entirely obstructing the cells. Nevertheless, bone penetration was clearly visible. We conclude that the 900 µm lattice cell size is more favourable to bone penetration than the 1200 µm lattice cell size, as the bone penetration is 84 % for 900 µm against 54 % for 1200 µm cell structures. The lower bone penetration value for the 1200 µm lattice cell could possibly be attributed to the short residence time in the sheep. Our results lead to the conclusion that lattice implants additively manufactured by selective laser melting enable better bone integration. KW - Biomedical engineering KW - Dentistry KW - Medical imaging KW - X-ray computer tomography PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418648 DO - https://doi.org/10.1016/j.heliyon.2017.e00374 SN - 2405-8440 IS - 3 SP - Article e00374, 1 EP - 21 PB - Elsevier Limited CY - 125 London Wall London, EC2Y 5AS United Kingdom AN - OPUS4-41864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Pourmand, P. A1 - Wolff, Dietmar A1 - Gedde, U.W. T1 - Influence of ageing on sealability of elastomeric O-rings N2 - At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes the assessment of the service lifetime of elastomeric seals that are part of the container lid system with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1.5 years. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays relatively constant or even decreases until shrinkage combined with the loss of resilience of the aged seal leads to leakage. This demonstrates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity towards the degradation of the seal material. CS data is extrapolated using time-temperature shifts and Arrhenius graphs. An exemplary CS of 50 % would be reached after approx. 1.2, 17 and 29 years at 60 °C for HNBR, EPDM and FKM respectively. T2 - PolymerTec 2016 CY - Merseburg, Germany DA - 15.06.2016 KW - Compression KW - Leakage KW - Degradation KW - Rubber KW - Lifetime PY - 2017 DO - https://doi.org/10.1002/masy.201600157 SN - 1022-1360 SN - 1521-3900 VL - 373 IS - 1 SP - UNSP 1600157, 1 EP - 10 PB - WILEY-V C H VERLAG GMBH CY - Weinheim AN - OPUS4-40958 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröder, Volkmar A1 - Molnarne, Maria T1 - Flammability of gases in focus of European and US standards N2 - The presentation will discuss the difference between EU and US standards for the determination of explosion (flammability) limits and limiting oxygen concentration. Small differences observed in measured values can be traced back to the different test apparatuses and criteria. The discrepancies can be much greater in the case of limiting oxygen concentration because of the high amount of inert gases and the corresponding low laminar burning velocities. The paper describes some examples and the influence of the chosen criteria on the results. The European and US standards use the criteria of flame propagation in open test vessels and of pressure rise in closed ones. The examples discussed show that flame propagation is still possible at very small pressure rise values, as observed much below the pressure rise criterion of usual standards. However, flame propagation in a process plant can cause an accident or explosion and must be avoided. Therefore, the flame propagation criterion is recommended to be used in chemical safety engineering. The European safety database CHEMSAFE contains expertevaluated safety data for cases where the determination method and criteria are known. Flammability characteristics based on the pressure rise criterion may suffice in certain cases, e.g. for explosion protection in closed vessels without any connecting pipes. KW - Flammability KW - Limiting oxygen concentration KW - Test methods KW - Standards PY - 2017 DO - https://doi.org/10.1016/j.jlp.2017.05.012 SN - 0950-4230 SN - 1873-3352 VL - 48 SP - 297 EP - 304 PB - Elsevier CY - Amsterdam AN - OPUS4-40980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Resch-Genger, Ute A1 - Gorris, H.H. T1 - Perspectives and challenges of photon-upconversion nanoparticles - Part I: routes to brighter particles and quantitative spectroscopic studies N2 - Lanthanide-doped photon-upconversion nanoparticles (UCNPs) have been the Focus of many Research activities in materials and life sciences in the last 15 years because of their potential to convert light between different spectral regions and their unique photophysical properties. To fully exploit the application potential of These facinating nanomaterials, a number of challenges have to be overcome, such as the low brightness, particularly of small UCNPs, and the reliable quantification of the excitation-power-density-dependent upconversion luminescence. In this series of critical Reviews, recent developments in the design, Synthesis, optical-spectroscopic characterization, and application of UCNPs are presented with Special Focus on bioanalysis and the life sciences. Here we guide the reader from the Synthesis of UCNPs to different concepts to enhance their luminescence, including the required optical-spectroscopic assessment to quantify material Performance; surface modification strategies and bioanalytical applications as well as selected examples of the use of UCNPs as reporters in different Assay formats are addressed in part II. Future Trends and challenges in the field of upconversion are discussed with Special emphasis on UCNP Synthesis and material characterization, particularly quantitative luminescence studies. KW - Fluorescence KW - Lanthanide KW - Upconversion KW - Brightness KW - Quantification KW - Nanoparticle KW - Absolute fluorometry KW - NIR KW - IR KW - Quantum yield PY - 2017 DO - https://doi.org/10.1007/s00216-017-0499-z SN - 1618-2650 SN - 1618-2642 VL - 409 IS - 25 SP - 5855 EP - 5874 PB - Springer AN - OPUS4-41665 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Interactions of polysaccharide stabilising agents with early cement hydration without and in the presence of superplasticizers N2 - Polysaccharides are incorporated into cement based Systems in order to modify the rheological properties. Typically, cellulose ethers, sphingan gums, guar gum or starch ethers are applied. Depending upon their chemistry, molecular architecture, and adsorption tendency, polysaccharides interact differently with the entire cementitious system. Some stabilising agents like diutan gum mainly affect the cementitious paste; other stabilising agents like starch tend to interact with the sand fraction and even with the coarse aggregates. Cellulose and guar gum shows more diverse performances. Typically stabilising admixtures like polysaccharides are used, when sophisticated rheological properties are adjusted. Therefore, polysaccharides are often used in combination with superplasticisers, which are added to reduce the yield stress of concrete. This can cause interactions, particularly when the stabilising Agent shows a strong tendency to adsorb on particle surfaces. Adsorptive stabilising agents may reduce the amount of adsorbed superplasticisers, thus affecting both viscosity and yield stress, while non-adsorptive stabilising agents mainly affect the plastic viscosity independently of the superplasticiser. Due to the strong influence of superplasticisers on the yield stress, influences of the stabilising agent on the yield stress retreat into the background, so that their major effect is an increase of the plastic viscosity. The paper provides a comprehensive overview of how different polysaccharide superplasticisers affect cementitious flowable systems and points out the challenges of the combined use of polysaccharides and superplasticisers. Based on rheometric experiments and observations of the hydration process, time dependent effects on the workability as well as of the hydration of cement are presented and discussed. KW - Concrete KW - Polysaccharides KW - Rheology KW - Stabilising agents KW - Starch KW - Sphingan PY - 2017 DO - https://doi.org/10.1016/j.conbuildmat.2016.11.022 SN - 0950-0618 SN - 1879-0526 VL - 139 SP - 584 EP - 593 PB - Elsevier AN - OPUS4-40597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hönig, Gerald A1 - Westerkamp, S. A1 - Hoffmann, A. A1 - Callsen, G. T1 - Shielding electrostatic fields in polar semiconductor nanostructures N2 - Polar semiconductor materials enable a variety of classic and quantum-light sources, which are optimized continuously. However, one key problem—the inherent electric crystal polarization of such materials—remains unsolved and deteriorates the radiative exciton decay rate. We suggest a sequence of reverse interfaces to compensate these polarization effects, while the polar, natural crystal growth direction is maintained. Former research approaches, like growth on less-polar crystal planes or even the stabilization of unnatural phases, never reached industrial maturity. In contrast, our concept provides a way for the development of ultrafast devices based on established growth processes for polar materials, while the electric potential landscape becomes adjustable. KW - Piezopolarisation KW - Spontane Polarisation KW - Halbleiterphysik KW - Nanophysik KW - Optoelektronik PY - 2017 DO - https://doi.org/10.1103/PhysRevApplied.7.024004 SN - 2331-7019 VL - 7 IS - 2 SP - 024004-1 EP - 024004-12 PB - American Physical Society CY - College Park, MD 20740-3844 AN - OPUS4-39125 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Myrach, Philipp A1 - Jonietz, Florian A1 - Meinel, Dietmar A1 - Suwala, Hubert A1 - Ziegler, Mathias T1 - Calibration of thermographic spot weld testing with X-ray computed tomography N2 - The paper presents an attempt for the calibration of an active thermography method that is suitable for the non-destructive evaluation of spot welds. Nowadays, the quality of spot welds is commonly characterised by the application of random chisel tests, which are time consuming, expensive and destructive. Recently a non-destructive testing method by means of active thermography was proposed that relies on the fact that the mechanical connection formed by the spot weld also serves as a thermal bridge between the two steel sheets joined in the welding process. It is shown in this paper that this thermal bridge can be thermographically characterised by extracting a measure for the spot weld diameter and hence the quality of the spot weld. The determination of the absolute value of the diameter hereby relies on a calibration of the testing system, which is performed by means of X-ray computed tomography in this study. The experiments were carried out using different experimental approaches, namely transmission as well as reflection geometry wSetup in reflectionith laser illumination. A comprehensive evaluation of samples produced using different welding currents, hence different quality, was carried out in order to validate the thermographic results. KW - Thermography KW - Spot welds KW - Spot welding KW - Computed thomography KW - Non-destructive testing PY - 2017 DO - https://doi.org/10.1080/17686733.2017.1281554 SN - 1768-6733 SN - 2116-7176 VL - 14 IS - 1 SP - 122 EP - 131 PB - Taylor & Francis CY - London AN - OPUS4-40180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madkour, Sherif A1 - Szymoniak, Paulina A1 - Heídari, M. A1 - von Klitzing, R. A1 - Schönhals, Andreas T1 - Unveiling the dynamics of self-assembled layers of thin films of poly(vinyl methyl ether) (PVME) by nanosized relaxation spectroscopy N2 - A combination of nanosized dielectric relaxation (BDS) and thermal spectroscopy (SHS) was utilized to characterize the dynamics of thin films of Poly(vinyl methyl ether) (PVME) (thicknesses: 7 nm – 160 nm). For the BDS measurements, a recently designed nano-structured electrode system is employed. A thin film is spin-coated on an ultra-flat highly conductive silicon wafer serving as the bottom electrode. As top electrode, a highly conductive wafer with non-conducting nanostructured SiO2 nano-spacers with heights of 35 nm or 70 nm is assembled on the bottom electrode. This procedure results in thin supported films with a free polymer/air interface. The BDS measurements show two relaxation processes, which are analyzed unambiguously for thicknesses smaller than 50 nm. The relaxation rates of both processes have different temperature dependencies. One process coincidences in its position and temperature dependence with the glassy dynamics of bulk PVME and is ascribed to the dynamic glass transition of a bulk-like layer in the middle of the film. The relaxation rates were found to be thickness independent as confirmed by SHS. Unexpectedly, the relaxation rates of the second process obey an Arrhenius-like temperature dependence. This process was not observed by SHS and was related to the constrained fluctuations in a layer, which is irreversibly adsorbed at the substrate with a heterogeneous structure. Its molecular fluctuations undergo a confinement effect resulting in the localization of the segmental dynamics. To our knowledge, this is the first report on the molecular dynamics of an adsorbed layer in thin films. KW - Broadband dielectric spectroscopy KW - AC-nanochip calorimetry KW - Nanostructured capacitors KW - Thin films PY - 2017 UR - http://pubs.acs.org/doi/pdf/10.1021/acsami.6b14404 DO - https://doi.org/10.1021/acsami.6b14404 SN - 1944-8244 VL - 9 IS - 8 SP - 7535 EP - 7546 PB - ACS Publications CY - Washington DC AN - OPUS4-39291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madkour, Sherif A1 - Szymoniak, Paulina A1 - Schick, Ch. A1 - Schönhals, Andreas T1 - Unexpected behavior of ultra-thin films of blends of polystyrene/poly(vinyl methyl ether) studied by specific heat spectroscopy N2 - Specific heat spectroscopy (SHS) employing AC nanochip calorimetry was used to investigate the glassy dynamics of ultra-thin films (thicknesses: 10 nm–340 nm) of a polymer blend, which is miscible in the bulk. In detail, a Poly(vinyl methyl ether) (PVME)/Polystyrene (PS) blend with the composition of 25/75 wt. % was studied. The film thickness was controlled by ellipsometry while the film topography was checked by atomic force microscopy. The results are discussed in the framework of the balance between an adsorbed and a free surface layer on the glassy dynamics. By a self-assembling process, a layer with a reduced mobility is irreversibly adsorbed at the polymer/substrate interface. This layer is discussed employing two different scenarios. In the first approach, it is assumed that a PS-rich layer is adsorbed at the substrate. Whereas in the second approach, a PVME-rich layer is suggested to be formed at the SiO2 substrate. Further, due to the lower surface tension of PVME, with respect to air, a nanometer thick PVME-rich surface layer, with higher molecular mobility, is formed at the polymer/air interface. By measuring the glassy dynamics of the thin films of PVME/PS in dependence on the film thickness, it was shown that down to 30 nm thicknesses, the dynamic Tg of the whole film was strongly influenced by the adsorbed layer yielding a systematic increase in the dynamic Tg with decreasing the film thickness. However, at a thickness of ca. 30 nm, the influence of the mobile surface layer becomes more pronounced. This results in a systematic decrease in Tg with the further decrease of the film thickness, below 30 nm. These results were discussed with respect to thin films of PVME/PS blend with a composition of 50/50 wt.%as well as literature results. KW - Ultra thin polymer films PY - 2017 DO - https://doi.org/10.1063/1.4978505 SN - 0021-9606 SN - 1089-7690 VL - 146 IS - 20 SP - 203321-1 EP - 203321-9 PB - AIP Publishing AN - OPUS4-39558 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröter, Maria-Astrid A1 - Meyer, Susann A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Sturm, Heinz A1 - Kunte, Hans-Jörg T1 - Ectoine protects DNA from damage by ionizing radiation N2 - Ectoine plays an important role in protecting biomolecules and entire cells against environmental stressors such as salinity, freezing, drying and high temperatures. Recent studies revealed that ectoine also provides effective protection for human skin cells from damage caused by UV-A radiation. These protective properties make ectoine a valuable compound and it is applied as an active ingredient in numerous pharmaceutical devices and cosmetics. Interestingly, the underlying mechanism resulting in protecting cells from radiation is not yet fully understood. Here we present a study on ectoine and its protective influence on DNA during electron irradiation. Applying gel electrophoresis and atomic force microscopy, we demonstrate for the first time that ectoine prevents DNA strand breaks caused by ionizing electron radiation. The results presented here point to future applications of ectoine for instance in cancer radiation therapy. KW - Plasmid DNA pUC19 KW - Electron irradiation 30 [kV] KW - Effective irradiation dose 0.2-16 [Gy] KW - Gel electrophoresis KW - AFM intermittent contact KW - Radioprotector ectoine KW - Compatible solute PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428287 DO - https://doi.org/10.1038/s41598-017-15512-4 SN - 2045-2322 VL - 7 IS - 1 SP - 15272, 1 EP - 15272, 7 PB - Nature AN - OPUS4-42828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bonse, Jörn T1 - Scattering on scattering N2 - Ultrafast experiments can reveal the spatiotemporal dynamics of nanostructure formation via scattering in background-free optical dark-field microscopy. KW - Ultrafast microscopy KW - Scattering KW - Darkfield microscopy KW - Laser ablation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-411596 DO - https://doi.org/10.1038/lsa.2017.88 SN - 2047-7538 VL - 6 SP - e17088, 1 EP - 2 PB - Springer Nature AN - OPUS4-41159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madkour, Sherif A1 - Szymoniak, Paulina A1 - Radnik, Jörg A1 - Schönhals, Andreas T1 - Unraveling the Dynamics of Nanoscopically Confined PVME in Thin Films of a Miscible PVME/PS Blend N2 - Broadband dielectric spectroscopy (BDS) was employed to investigate the glassy dynamics of thin films (7−200 nm) of a poly(vinyl methyl ether) (PVME)/polystyrene (PS) blend (50:50 wt %). For BDS measurements, nanostructured capacitors (NSCs) were employed, where films are allowed a free surface. This method was applied for film thicknesses up to 36 nm. For thicker films, samples were prepared between crossed electrode capacitors (CECs). The relaxation spectra of the films showed multiple processes. The first process was assigned to the α-relaxation of a bulklike layer. For films measured by NSCs, the rates of α-relaxation were higher compared to those of the bulk blend. This behavior was related to the PVME-rich free surface layer at the polymer/air interface. The second process was observed for all films measured by CECs (process X) and the 36 nm film measured by NSCs (process X2). This process was assigned to fluctuations of constraint PVME segments by PS. Its activation energy was found to be thickness-dependent because of the evidenced thickness dependency of the compositional heterogeneity. Finally, a third process with an activated temperature dependence was observed for all films measured by NSCs (process X1). It resembled the molecular fluctuations in an adsorbed layer found for thin films of pure PVME, and thus, it is assigned accordingly. This process undergoes an extra confinement because of frozen adsorbed PS segments at the polymer/substrate interface. To our knowledge, this is the first example where confinement-induced changes were observed by BDS for blend thin films KW - Thin Films KW - Broadband Dielectric Spectroscopy PY - 2017 DO - https://doi.org/10.1021/acsami.7b10572 SN - 1944-8244 VL - 9 IS - 42 SP - 37289 EP - 37299 PB - ACS Publications AN - OPUS4-42652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Leng, Jing A1 - Kang, Nianjun A1 - Wang, De-Yi A1 - Falkenhagen, Jana A1 - Thünemann, Andreas A1 - Schönhals, Andreas T1 - Structure–Property Relationships of Nanocomposites Based on Polylactide and Layered Double Hydroxides – Comparison of MgAl and NiAl LDH as Nanofiller N2 - Nanocomposites based on poly(L-lactide) (PLA) and organically modified Ni/Al layered double hydroxides (NiAl/LDHs) are prepared by melt blending and investigated by a combination of size exclusion chromatography, differential scanning calorimetry (DSC), small-angle X-ray scattering (SAXS), wide-angle X-ray scattering, and broadband dielectric spectroscopy. A detailed comparison to the behavior of the corresponding MgAl/LDH–PLA nanocomposites is made. SAXS investigations show that the morphology of the NiAl/LDH–PLA nanocomposites is more intercalated compared to the MgAl/LDH based PLA nanocomposite, which is more exfoliated. The DSC investigation gives a different dependence of the degree of crystallization on the concentration of LDH for NiAl/LDH–PLA than for MgAl/LDH–PLA nanocomposite system. These differences are discussed taking the differences of the morphologies of both systems into account. Broadband dielectric spectroscopy reveals information about the molecular dynamics where essential differences are observed for all relaxation processes taking place in both systems which were related to the different morphologies. KW - Nanocomposites KW - Polylactide PY - 2017 DO - https://doi.org/10.1002/macp.201700232 SN - 1022-1352 SN - 1521-3935 VL - 218 IS - 20 SP - Article 1700232, 1 EP - 12 PB - Wiley-VCH Verlag AN - OPUS4-42597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Agudo Jácome, Leonardo A1 - Göbenli, G. A1 - Eggeler, G. ED - Göken, M. T1 - Transmission electron microscopy study of the microstructural evolution during high-temperature and low-stress (011) [01-1] shear creep deformation of the superalloy single crystal LEK 94 N2 - The present work describes the shear creep behavior of the superalloy LEK 94 at temperatures between 980 and 1050 °C and shear stresses between 50 and 140 MPa for loading on the macroscopic crystallographic shear system (MCSS) (011)[01-1]. The strain rate versus strain curves show short primary and extended secondary creep regimes. We find an apparent activation energy for creep of Qapp = 466 kJ/mol and a Norton-law stress exponent of n = 6. With scanning transmission electron microscopy, we characterize three material states that differ in temperature, applied stress, and accumulated strain/time. Rafting develops perpendicular to the maximum principal stress direction, gamma channels fill with dislocations, superdislocations cut gamma' particles, and dislocation networks form at gamma/gamma' interfaces. Our findings are in agreement with previous results for high-temperature and low-stress [001] and [110] tensile creep testing, and for shear creep testing of the superalloys CMSX-4 and CMSX-6 on the MCSSs (111)[01-1] and (001)[100]. The parameters that characterize the evolving gamma/gamma' microstructure and the evolving dislocation substructures depend on creep temperature, stress, strain, and time. KW - Dislocations KW - Microstructure KW - Scanning transmission electron microscopy (STEM) KW - Creep KW - Shear test PY - 2017 DO - https://doi.org/10.1557/jmr.2017.336 SN - 0884-2914 SN - 2044-5326 VL - 32 IS - 24 SP - 4491 EP - 4502 PB - Cambridge University Press CY - Cambrigde AN - OPUS4-43756 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madkour, Sherif A1 - Szymoniak, Paulina A1 - Hertwig, Andreas A1 - Heidari, M. A1 - von Klitzing, R. A1 - Napolitano, S. A1 - Sferrazza, M. A1 - Schönhals, Andreas T1 - Decoupling of dynamic and thermal glass transition in thin films of a PVME/PS blend N2 - The discussions on the nanoconfinement effect on the glass transition and glassy dynamics phenomena have yielded many open questions. Here, the thickness dependence of the thermal glass transition temperature of thin films of a PVME/PS blend is investigated by ellipsometry. Its thickness dependence was compared to that of the dynamic glass transition (measured by specific heat spectroscopy), and the deduced Vogel temperature (T0). While and T0 showed a monotonous increase, with decreasing the film thickness, the dynamic glass transition temperature () measured at a finite frequency showed a non-monotonous dependence that peaks at 30 nm. This was discussed by assuming different cooperativity length scales at these temperatures, which have different sensitivities to composition and thickness. This non-monotonous thickness dependence of disappears for frequencies characteristic for T0. Further analysis of the fragility parameter, showed a change in the glassy dynamics from strong to fragile, with decreasing film thickness. KW - Thin polymeric films KW - Ellipsometry KW - Specific heat spectroscopy PY - 2017 DO - https://doi.org/10.1021/acsmacrolett.7b00625 SN - 2161-1653 VL - 6 IS - 10 SP - 1156 EP - 1161 PB - ACS Publications AN - OPUS4-42266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jensen, S. A. A1 - Rosu, Dana Maria A1 - Hertwig, Andreas A1 - Hansen, P.-E. T1 - Use of Rayleigh-Rice Theory for Analysis of Ellipsometry Data on Rough CIGS Films N2 - Ellipsometry is a useful tool for studying the optical properties of thin films such as photovoltaic devices. We employ Müller matrix ellipsometry to study the thin film photovoltaic material copper indium gallium selenide Cu(In,Ga) Se2 (CIGS), a commercially relevant material with high energy conversion efficiency. Confocal microscopy reveals an rms roughness of 68 nm, which greatly affects the ellipsometry data. Rayleigh-Rice theory is employed to account for the optical properties of the surface roughness in the ellipsometry experiment, and a library search method is used to compare Müller parameters calculated for various CIGS compositions, to the measured data. The Müller parameters calculated with the Rayleigh-Rice model are found to correspond well with the measured data, and a surface roughness of 37nm and a correlation length of 125nm are extracted. KW - Photovoltaics KW - Thin Films KW - Ellipsometry KW - Scattering Theory KW - Optical Wavefield KW - Simulation KW - Müller Polarimetry KW - Multidimensional Spectroscopy PY - 2017 DO - https://doi.org/10.1002/pssc.201700217 SN - 1862-6351 VL - 14 IS - 12 SP - 1700217, 1 EP - 5 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-43390 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Breitenbach, Romy A1 - Silbernagl, Dorothee A1 - Toepel, J. A1 - Sturm, Heinz A1 - Broughton, William J. A1 - Sassaki, G. L. A1 - Gorbushina, Anna T1 - Corrosive extracellular polysaccharides of the rock-inhabiting model fungus Knufia petricola N2 - Melanised cell walls and extracellular polymeric matrices protect rock-inhabiting microcolonial fungi from hostile environmental conditions. How extracellular polymeric substances (EPS) perform this protective role was investigated by following development of the model microcolonial black fungus Knufia petricola A95 grown as a sub-aerial biofilm. Extracellular substances were extracted with NaOH/formaldehyde and the structures of two excreted polymers studied by methylation as well as NMR analyses. The main polysaccharide (~ 80%) was pullulan, also known as α-1,4-; α-1,6-glucan, with different degrees of polymerisation. Αlpha-(1,4)-linked-Glcp and α-(1,6)-linked-Glcp were present in the molar ratios of 2:1. A branched galactofuromannan with an α-(1,2)-linked Manp main chain and a β-(1,6)-linked Galf side chain formed a minor fraction (~ 20%). To further understand the roles of EPS in the weathering of minerals and rocks, viscosity along with corrosive properties were studied using atomic force microscopy (AFM). The kinetic viscosity of extracellular K. petricola A95 polysaccharides (≈ 0.97 × 10-6 m2 s-1) ranged from the equivalent of 2% (w/v) to 5% glycerine, and could thus profoundly affect diffusion-dominated processes. The corrosive nature of rock-inhabiting fungal EPS was also demonstrated by its effects on the aluminium coating of the AFM cantilever and the silicon layer below. KW - Corrosion KW - EPS KW - Melanised microcolonial fungi (MCF) KW - Pullulan KW - Sub-aerial biofilms (SAB) KW - α-1,4- and α-1,6-glucans KW - AFM cantilever vibration KW - Nanoviscosity KW - Nanocorrosion of aluminium and silicon PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435910 DO - https://doi.org/10.1007/s00792-017-0984-5 SN - 1433-4909 SN - 1431-0651 VL - 22 IS - 2 SP - 165 EP - 175 PB - Springer CY - Berlin AN - OPUS4-43591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rudenko, A. A1 - Colombier, J.-P. A1 - Höhm, S. A1 - Rosenfeld, A. A1 - Krüger, Jörg A1 - Bonse, Jörn A1 - Itina, T.E. T1 - Spontaneous periodic ordering on the surface and in the bulk of dielectrics irradiated by ultrafast laser: a shared electromagnetic origin N2 - Periodic self-organization of matter beyond the diffraction limit is a puzzling phenomenon, typical both for surface and bulk ultrashort laser processing. Here we compare the mechanisms of periodic nanostructure formation on the surface and in the bulk of fused silica. We show that volume nanogratings and surface nanoripples having subwavelength periodicity and oriented perpendicular to the laser polarization share the same electromagnetic origin. The nanostructure orientation is defined by the near-field local enhancement in the vicinity of the inhomogeneous scattering centers. The periodicity is attributed to the coherent superposition of the waves scattered at inhomogeneities. Numerical calculations also support the multipulse accumulation nature of nanogratings formation on the surface and inside fused silica. Laser surface processing by multiple laser pulses promotes the transition from the high spatial frequency perpendicularly oriented nanoripples to the low spatial frequency ripples, parallel or perpendicular to the laser polarization. The latter structures also share the electromagnetic origin, but are related to the incident field interference with the scattered far-field of rough non-metallic or transiently metallic surfaces. The characteristic ripple appearances are predicted by combined electromagnetic and thermo-mechanical approaches and supported by SEM images of the final surface morphology and by time-resolved pump-probe diffraction measurements. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser KW - Nanostructures KW - Dielectrics KW - Electromagnetic scattering PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-421747 UR - https://www.nature.com/articles/s41598-017-12502-4 DO - https://doi.org/10.1038/s41598-017-12502-4 SN - 2045-2322 VL - 7 SP - Article 12306, 1 EP - 14 PB - Springer Nature AN - OPUS4-42174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seuthe, T. A1 - Mermillod-Blondin, A. A1 - Grehn, M. A1 - Bonse, Jörn A1 - Wondraczek, L. A1 - Eberstein, M. T1 - Structural relaxation phenomena in silicate glasses modifed by irradiation with femtosecond laser pulses N2 - Structural relaxation phenomena in binary and multicomponent lithium silicate glasses were studied upon irradiation with femtosecond (fs) laser pulses (800 nm central wavelength, 130 fs pulse duration) and subsequent thermal annealing experiments. Depending on the annealing temperature, micro-Raman spectroscopy analyses evidenced different relaxation behaviours, associated to bridging and non-bridging oxygen structures present in the glass network. The results indicate that the mobility of lithium ions is an important factor during the glass modification with fs-laser pulses. Quantitative phase contrast imaging (spatial light interference microscopy) revealed that these fs-laser induced structural modifications are closely related to local changes in the refractive index of the material. The results establish a promising strategy for tailoring fs-laser sensitivity of glasses through structural mobility. KW - Femtosecond laser KW - Silicate glasses KW - Raman spectroscopy KW - Structural relaxation KW - Refractive index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393045 DO - https://doi.org/10.1038/srep43815 SN - 2045-2322 VL - 7 SP - 43815, 1 EP - 43815, 10 PB - Nature Publishing Group CY - London, UK AN - OPUS4-39304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heitz, J. A1 - Plamadeala, C. A1 - Muck, M. A1 - Armbruster, O. A1 - Baumgartner, W. A1 - Weth, A. A1 - Steinwender, C. A1 - Plessberger, H. A1 - Kellermair, J. A1 - Kirner, Sabrina V. A1 - Krüger, Jörg A1 - Bonse, Jörn A1 - Guntner, A. S. A1 - Hassel, A. W. T1 - Femtosecond laser-induced microstructures on Ti substrates for reduced cell adhesion N2 - Miniaturized pacemakers with a surface consisting of a Ti alloy may have to be removed after several years from their implantation site in the heart and shall, therefore, not be completely overgrown by cells or tissue. A method to avoid this may be to create at the surface by laser-ablation self-organized sharp conical spikes, which provide too little surface for cells (i.e., fibroblasts) to grow on. For this purpose, Ti-alloy substrates were irradiated in the air by 790 nm Ti:sapphire femtosecond laser pulses at fluences above the ablation threshold. The laser irradiation resulted in pronounced microstructure formation with hierarchical surface morphologies. Murine fibroblasts were seeded onto the laser-patterned surface and the coverage by cells was evaluated after 3–21 days of cultivation by means of scanning electron microscopy. Compared to flat surfaces, the cell density on the microstructures was significantly lower, the coverage was incomplete, and the cells had a clearly different morphology. The best results regarding suppression of cell growth were obtained on spike structures which were additionally electrochemically oxidized under acidic conditions. Cell cultivation with additional shear stress could reduce further the number of adherent cells. KW - Laser Processing KW - Femtosecond laser KW - Titanium alloy KW - Cell adhesion KW - Anodic oxidation KW - Pacemaker PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-427681 UR - https://link.springer.com/article/10.1007/s00339-017-1352-0 DO - https://doi.org/10.1007/s00339-017-1352-0 SN - 0947-8396 SN - 1432-0630 VL - 123 IS - 12 SP - 734, 1 EP - 9 PB - Springer-Verlag CY - Berlin AN - OPUS4-42768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosu, Dana-Maria A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan A1 - Kraehnert, R. A1 - Hertwig, Andreas ED - Hertwig, Andreas ED - Hinrichs, K. ED - Beck, Uwe ED - Esser, N. T1 - Ellipsometric porosimetry on pore-controlled TiO2 layers N2 - The practical performance of surface coatings in applications like catalysis, water splitting or batteries depends critically on the coating materials’ porosity. Determining the porosity in a fast and nondestructive way is still an unsolved problem for industrial thin-films technology. As a contribution to calibrated, non-destructive, optical layer characterisation, we present a multi-method comparison study on porous TiO2 films deposited by sol-gel synthesis on Si wafers. The ellipsometric data were collected on a range of samples with different TiO2 layer thickness and different porosity values. These samples were produced by templated sol-gel synthesis resulting in layers with a well-defined pore size and pore density. The ellipsometry measurement data were analysed by means of a Bruggeman effective medium approximation (BEMA), with the aim to determine the mixture ratio of void and matrix material by a multi-sample analysis strategy. This analysis yielded porosities and layer thicknesses for all samples as well as the dielectric function for the matrix material. Following the idea of multi-method techniques in metrology, the data was referenced to imaging by electron microscopy (SEM) and to a new EPMA (electron probe microanalysis) porosity approach for thin film analysis. This work might lead to a better metrological understanding of optical porosimetry and also to better-qualified characterisation methods for nano-porous layer systems. 1. IntroductionPorous materials, especially porous thin films play an importantrole in chemical and physical technology in every case where thecontact area between two media has to be maximised. From cataly-sis to photochemistry and photovoltaics, the applications of porouslayer materials are diverse and numerous [1–6].The accurate and non-destructive characterisation of porousfilms for layered systems poses a challenge. This applies especiallyfor the key parameter of porous films, their porosity, i.e. the mix-ing ratio between the Matrix of the film (host material) and thepore volume which is empty or filled with a fluid medium (inclu-sions). This parameter influences most of the physical and chemicalproperties of a porous thin film and is therefore essential for theunderstanding as well as the optimisation of this class of materials. T2 - International Conference on Spectroscopic Ellipsometry (ICSE-7) CY - Berlin, Germany DA - 06.06.2016 KW - Spectroscopic ellipsometry KW - Porous materials KW - Porosimetry KW - Multi-sample analysis KW - Thin film metrology PY - 2017 DO - https://doi.org/10.1016/j.apsusc.2016.11.055 SN - 0169-4332 SN - 1873-5584 VL - 421 IS - Part B SP - 487 EP - 493 PB - Elsevier B.V. AN - OPUS4-42517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -