TY - JOUR A1 - Babutzka, Martin A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - Field exposure study under sheltered and open exposure conditions at different test sites in Germany: First‐year corrosion rate and atmospheric corrosivity JF - Materials and Corrosion N2 - The corrosivity of atmospheres in Europe has changed significantly in recent decades. For the Federal Republic of Germany, no current values for the corrosion rate based on 1‐year atmospheric exposure of standard specimens can be found in the scientific literature after 2000. This paper presents results from a field exposure study in the Berlin metropolitan area and Helgoland in 2016. Based on standard specimens, values for the corrosion rate and the corresponding atmospheric corrosivity category are determined for open exposure and indirect weathering in a ventilated enclosure as sheltering after 1 year of exposure. The results prove that determined corrosivity categories are material‐specific. Sheltered exposure is a typical atmospheric situation for many building components. It allows statements on the effect of the concentration of airborne substances on the corrosivity beyond the normative requirements. KW - Atmospheric corrosion KW - Corrosivity category KW - ISO 9223 KW - Mass loss KW - Atmosphärische Korrosion PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-565099 DO - https://doi.org/10.1002/maco.202213582 SN - 0947-5117 (print) SN - 1521-4176 (online) SP - 1 EP - 15 PB - Wiley-VCH GmbH CY - Weinheim AN - OPUS4-56509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Leonhard, H. T1 - More certainty in corrosion prevention JF - Processing N2 - Protective passive coatings of stainless-steel piping systems and tanks in chemical plants are at risk – and not only from the harsh conditions prevalent during production operations. Even in new systems, defects can be caused by grinding or by incomplete removal of temper colours after welding. TÜV SÜD Chemie Service participated in the assessment of a rapid test for corrosion developed by the German Institute for Materials Research and Testing (Bundesanstalt für Materialforschung und -prüfung, BAM). In only 15 minutes, KorroPads deliver valid information about the condition of passive coatings on material surfaces. KW - Nichtrostender Stahl KW - Korrosionsschnelltest KW - KorroPad KW - Passivschicht PY - 2018 UR - http://digital.processingmagazine.com/July2018#&pageSet=11 SN - 0896-8659 VL - 31 IS - 07 SP - 20 EP - 21 PB - Endeavor Business Media CY - Birmingham, Alabama AN - OPUS4-45722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations proofing the passive layer stability of stainless steels JF - Materials and Corrosion N2 - The presented investigations have proved the principal suitability of the KorroPad method to assess the passive layer stability of stainless steels. The electrochemical mode of action could be described in detail and limitations of the applicability have been demonstrated. The influence of different surface finishes has been investigated and verified by known methods for describing corrosion resistances. As a result, the increased corrosion susceptibility of two ground surfaces has been detected, but also the corrosion resistance of further surface finishes could be confirmed. KW - Stainless steel KW - KorroPad KW - Passive layer PY - 2016 DO - https://doi.org/10.1002/maco.201408202 VL - 1 IS - 67 SP - 84 EP - 91 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-35545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Long-term corrosion behaviour of stainless steels in marine atmosphere JF - Materials and Corrosion N2 - Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404. KW - Corrosion KW - Free weathering KW - Marine atmosphere KW - Stainless steels PY - 2018 DO - https://doi.org/10.1002/maco.201709636 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 1 SP - 20 EP - 28 PB - Wiley-VCH Verlag GmbH & Co KGaA CY - Weinheim AN - OPUS4-43625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - Corrosion resistance of ferritic stainless steels studied with various methods on different time scales N2 - The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - Stainless steel KW - Corrosion resistance KW - EPR KW - Corrosion testing KW - Pitting corrosion KW - Atmospheric corrosion KW - Surface treatment PY - 2018 AN - OPUS4-45940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reinemann, Steffi A1 - Rosemann, P. A1 - Babutzka, Martin A1 - Lehmann, Jens A1 - Burkert, Andreas T1 - Influence of grinding parameters on the corrosion behavior of austenitic stainless steel JF - Materials and Corrosion N2 - Samples of the austenitic stainless steel grade X5CrNi18‐10 (1.4301, AISI 304) were ground industrially with various grinding parameters to study their influence on corrosion resistance. The ability of the mechanically ground surfaces to form a stable passive layer was evaluated by KorroPad test and a modified electrochemical potentiodynamic reactivation test based on a single loop (EPR‐SL). Furthermore, the surfaces were characterized by surface analytical methods. The main influence was determined regarding abrasive belt type. Surfaces mechanically ground with granulate abrasive belts constantly had a lower corrosion resistance than surfaces ground with single‐coated grain. The granulate abrasive belts generated more sensitized surface areas and left formations of welded sample material on the mechanically ground surfaces. A post‐treatment with a nonwoven abrasive proved to be an effective finishing process by which the surface defects and sensitized material got removed and the surfaces regained the expected corrosion resistance. KW - Abrasive belt KW - Austenitic stainless steel KW - Electrochemical potentiodynamic reactivation KW - Grinding KW - KorroPad KW - Surface KW - Corrosion PY - 2019 DO - https://doi.org/10.1002/maco.201910874 SN - 0947-5117 SN - 1521-4176 VL - 70 IS - 10 SP - 1776 EP - 1787 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-47871 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -