TY - CONF A1 - Roveda, Ilaria A1 - Serrano Munoz, Itziar A1 - Madia, Mauro T1 - Investigation of residual stresses and microstructure effects on the fatigue behaviour of a L-PBF AlSi10Mg alloy N2 - Laser Powder Bed Fusion (L-PBF) allow the fabrication of lightweight near net shape AlSi10Mg components attractive to the aerospace, automotive, biomedical and military industries. During the build-up process, high cooling rates occur. Thus, L-PBF AlSi10Mg alloys exhibit a Si-nanostructure in the as-built condition, which leads to superior mechanical properties compared to conventional cast materials. At the same time, such high thermal gradients generally involve a deleterious residual stress (RS) state that needs to be assessed during the design process, before placing a component in service. To this purpose post-process heat treatments are commonly performed to relieve detrimental RS. In this contribution two low-temperature stress-relief heat treatments (SRHT) are studied and compared with the as-built state: a SRHT at 265°C for 1 hour and a SRHT at 300°C for 2 hours. At these temperatures microstructural changes occur. In the as-built state, Si atoms are supersaturated in the α-aluminium matrix, which is enveloped by a eutectic Si-network. At 265°C the Si precipitation from the matrix to the pre-existing network is triggered. Thereafter, above 295°C the fragmentation and spheroidization of the Si branches takes place, presumably by Al–Si interdiffusion. After 2 hours the original eutectic network is completely replaced by uniformly distributed blocky particles. The effect of the heat and the microstructure modification on the RS state and the fatigue properties is investigated. Energy dispersive x-ray and neutron diffraction are combined to investigate the near-surface and bulk RS state of a L-PBF AlSi10Mg material. Differences in the endurance limit are evaluated experimentally by high cycle fatigue (HCF) tests and cyclic R-curve determination. T2 - 43rd Materials Mechanics Seminar CY - Sani, Chalkidiki, Greece DA - 05.06.2022 KW - AlSi10Mg KW - Fatigue KW - Neutron diffraction KW - X-ray diffraction PY - 2022 AN - OPUS4-55090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana T1 - 3D imaging and residual stress analysis of AM materials at BAM N2 - The overview of the activity of group 8.5 Micro-NDT (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The research of our group is focused on the 3D imaging of AM materials by means of X-ray Computed Tomography at the lab and at synchrotron, and the residual stress characterization by diffraction (nondestructive technique). T2 - Seminar at Chalmers University and Centre for Additive Manufacture (CAM2) CY - Gothenburg, Sweden DA - 19.05.2022 KW - Additive manufacturing KW - Laser powder bed fusion KW - Residual stress KW - Computed tomography KW - Synchrotron X-ray diffraction KW - X-ray refraction PY - 2022 AN - OPUS4-55019 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Evsevleev, Sergei A1 - Mishurova, Tatiana A1 - Meinel, Dietmar A1 - Koptyug, A. A1 - Surmeneva, M. A1 - Khrapov, D. A1 - Paveleva, A. A1 - Surmenev, R. T1 - Röntgen-Computertomographie-Verfahren zur quantitativen Charakterisierung periodischer Minimalflächenstrukturen (TMPS) N2 - Additiv gefertigte (AM) dreifach periodische metallische minimale Oberflächenstrukturen (TPMSS, aus dem Englischen Triply Periodic Minimum Surface Structures) erfüllen mehrere Anforderungen sowohl im biomedizinischen als auch im technischen Bereich: Abstimmbare mechanische Eigenschaften, geringe Empfindlichkeit gegenüber Herstellungsfehlern, mechanische Stabilität und hohe Energieabsorption. Allerdings stellen sie auch einige Herausforderungen in Bezug auf die Qualitätskontrolle dar, die ihre erfolgreiche Anwendung verhindern können. Tatsächlich ist die Optimierung des AM-Prozesses ohne die Berücksichtigung struktureller Merkmale wie Fertigungsgenauigkeit, interne Defekte sowie Oberflächentopographie und -rauheit unmöglich. In dieser Studie wurde die quantitative zerstörungsfreie Analyse von Ti-6Al-4V-Legierung TPMSS mit Hilfe der Röntgen-Computertomographie (XCT) durchgeführt. Es werden mehrere neue Bildanalyse-Workflows vorgestellt, um die Auswirkungen der Aufbaurichtung auf die Wanddickenverteilung, die Wanddegradation und die Verringerung der Oberflächenrauheit aufgrund des chemischen Ätzens von TPMSS zu bewerten. Es wird gezeigt, dass die Herstellungsgenauigkeit für die Strukturelemente, die parallel und orthogonal zu den hergestellten Schichten gedruckt werden, unterschiedlich ist. Verschiedene Strategien für das chemische Ätzen zeigten unterschiedliche Pulverabtragsfähigkeiten und damit ein Gradient der Wanddicke. Dies wirkte sich auf die mechanische Leistung unter Druck durch die Verringerung der Streckspannung aus. Eine positive Auswirkung des chemischen Ätzens ist die Verringerung der Oberflächenrauhigkeit, die möglicherweise die Ermüdungseigenschaften der Bauteile verbessern kann. Schließlich wurde XCT eingesetzt, um die Menge des zurückgehaltenen Pulvers mit der Porengröße des TPMSS zu korrelieren, wodurch der Herstellungsprozess weiter verbessert werden kann. T2 - DGZfP-Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Additive Fertigung KW - Computertomographie KW - Wändedicke KW - Machine Learning PY - 2022 AN - OPUS4-55021 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Serrano Munoz, Itziar T1 - Multiscale residual stress analysis and synchrotron X-ray refraction of additively manufactured parts N2 - The overview of the activity of group 8.5 Micro-NDT (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The challenges in the residual stress analysis of AM components are discussed on the basis on the show studies performed in BAM. Also, the synchrotron X-ray refraction technique, available in BAM, is presented, showing example of in-situ heating test of Al10SiMg AM material. T2 - Seminar at Grenoble INP, Science et Ingénierie des Matériaux et Procédés (SIMaP) CY - Grenoble, France DA - 01.07.2022 KW - Additive manufacturing KW - Residual stress KW - X-ray refraction KW - Computed tomography PY - 2022 AN - OPUS4-55232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gupta, P. A1 - Karnaushenko, D. D. A1 - Becker, C. A1 - Okur, I. E. A1 - Melzer, M. A1 - Özer, B. A1 - Schmidt, O. G. A1 - Karnaushenko, D. T1 - Large Scale Exchange Coupled Metallic Multilayers by Roll-to-Roll (R2R) Process for Advanced Printed Magnetoelectronics N2 - Till now application of printed magnetoelectronics is hindered by lack of large area exchange coupled metallic multilayers required to produce printable magneto-sensory inks. Large-scale roll-to-roll (R2R) fabrication process is an attractive approach owing to its capabilities for high volume, high throughput, and large area manufacturing. Precise and high performance R2R sputtering technology is developed to fabricate large area giant magnetoresistive (GMR) thin-films stacks that contain 30 metallic bilayers prepared by continuous R2R sputtering of Co and Cu sequential on a hundred meters long polyethylene terephthalate (PET) web. The R2R sputtered Co/Cu multilayer on a 0.2 × 100 m2 PET web exhibits a GMR ratio of ≈40% achieving the largest area exchange coupled room temperature magneto-sensitive system demonstrated to date. The prepared GMR thin-film is converted to magnetosensitive ink that enables printing of magnetic sensors with high performance in a cost-efficient way, which promotes integration with printed electronics. An average GMR ratio of ≈18% is obtained for 370 printed magnetic sensors. The realized precise R2R sputtering approach can also be extended to a wide range of hybrid thin-film material systems opening up a path for new functional inks applied with printing technologies. KW - Printed Electronics KW - Flexible Magnetic Sensors KW - Roll-to-Roll Processing KW - Functional Materials KW - Upscaling PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-552344 SN - 2365-709X SP - 1 EP - 11 PB - Wiley-VCH CY - Weinheim, Deutschland AN - OPUS4-55234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Serrano Munoz, Itziar A1 - Fernández, R. A1 - Saliwan Neumann, Romeo A1 - González-Doncel, G. A1 - Bruno, Giovanni T1 - Dislocation substructures in pure aluminium after creep deformation as studied by electron backscatter diffraction N2 - In the present work, electron backscatter diffraction was used to determine the microscopic dislocation structures generated during creep (with tests interrupted at the steady state) in pure 99.8% aluminium. This material was investigated at two different stress levels, corresponding to the power-law and power-law breakdown regimes. The results show that the formation of subgrain cellular structures occurs independently of the crystallographic orientation. However, the density of these cellular structures strongly depends on the grain crystallographic orientation with respect to the tensile axis direction, with <111> grains exhibiting the highest densities at both stress levels. It is proposed that this behaviour is due to the influence of intergranular stresses, which is different in <111> and <001> grains. KW - Creep KW - Pure aluminium KW - Electron backscatter diffraction KW - Cellular structures KW - Power law and power-law breakdown PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-552003 SN - 0021-8898 SN - 1600-5767 VL - 55 SP - 860 EP - 869 PB - Wiley-Blackwell CY - Copenhagen AN - OPUS4-55200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Mehta, Bharat A1 - Nyborg, L. A1 - Virtanen, E. A1 - Markötter, Henning A1 - Hryda, E. A1 - Bruno, Giovanni T1 - Failure Mechanisms Investigation by Means of in-situ Synchrotron Computed Tomography in Aluminum MMC-based Alloy Tailored for Additive Manufacturing (AM) N2 - Most of the Al alloys used in additive manufacturing (AM), in particular Laser Powder Bed Fusion (LPBF), do not exceed a strength of 200 MPa, whereas conventionally high-performance alloys exhibit strengths exceeding 400 MPa. The availability of such Al alloys in AM is limited due to difficulties in printability, requiring synergetic material and AM process development to satisfy harsh processing conditions during LPBF [1]. One approach is the addition of reinforcement to the based powder, allowing tailoring composition and properties of a Metal Matrix Composite (MMC) by AM. Still, the effect of the reinforcement on the resulting mechanical properties must be studied to understand the performance and limits of the newly developed material. The goal of this work was to investigate the failure mechanism of LPBF Al-based MMC material using in-situ Synchrotron X-ray Computed Tomography (SXCT) during mechanical testing. T2 - International conference on tomography of material and structures CY - Grenoble, France DA - 27.06.2022 KW - Additive manufacturing KW - Laser powder bed fusion KW - Al alloy KW - MMC PY - 2022 AN - OPUS4-55228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Mishurova, Tatiana A1 - Evlevleev, Sergei A1 - Khrapov, D. A1 - Meinel, Dietmar A1 - Surmenev, R. A1 - Surmeneva, M. A1 - Koptyug, A. T1 - Procedures to Quantitatively Characterize Morphological Features of Triply Periodic Minimal Surface Structures N2 - Additively manufactured (AM) metallic sheet-based Triply Periodic Minimal Surface Structures (TPMSS) meet several requirements in both bio-medical and engineering fields: Tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some challenges related to quality control. In fact, the optimization of both the AM process and the properties of TPMSS is impossible without considering structural characteristics as manufacturing accuracy, internal defects, and as well as surface topography and roughness. In this study, the quantitative non-destructive analysis of TPMSS manufactured from Ti-6Al-4V alloy by electron beam melting was performed by means of laboratory X-ray computed tomography (XCT). T2 - International conference on tomography of material and structures 2022 CY - Grenoble, France DA - 27.06.2022 KW - Additive manufacturing KW - Scaffold KW - Lightweight structures KW - Computed tomography PY - 2022 AN - OPUS4-55229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pohl, P. A1 - Serrano Munoz, Itziar A1 - Markötter, Henning A1 - Göken, Mathias A1 - Höppel, H. W. T1 - Toughening mechanisms and enhanced damage tolerant fatigue behaviour in laminated metal composites N2 - In the present study, fatigue crack growth (FCG) in a laminated metal composite (LMC) consisting of Al-based constituents with dissimilar strength was studied. Additionally, the FCG in both monolithic constituent materials was determined and a linear elastic rule of mixture (ROM) concept was calculated as a reference for the FCG of the laminated composite. Crack networks in the laminates were analyzed post-mortem by means of light microscopy and synchrotron X-Ray tomography (SXCT). Significantly reduced FCG rates for the LMC were found at elevated stress intensity ranges compared to both the monolithic constituents as well as the ROM concept. This is the result of the formation of a complex 3D crack network in the laminated architecture caused by the appearance of the two different toughening mechanisms a) crack deflection and b) crack bifurcation at the vicinity of the interfaces. T2 - Ninth International Conference on Low Cycle Fatigue CY - Berlin, Germany DA - 21.06.2022 KW - Laminated metal composite KW - Damage tolerance KW - Fatigue crack growth KW - Toughening mechanism KW - Synchrotron X-ray computed tomography PY - 2022 U6 - https://doi.org/10.48447/LCF9-2022-035 SP - 153 EP - 158 PB - DVM AN - OPUS4-55231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska T1 - Charakterisierung von Salzbeton und alkali-aktivierten Material basierend auf der Schallemissionsanalyse N2 - Nach einer kurzen Einführung in die Schallemissionsprüfung und -Analyse wird ein Versuchsstand vorgestellt, der im Rahmen des Themenfeldprojektes Seal Waste Safe installiert wurde. Schwerpunkt des Vortrages sind die Schallemissionsmessungen an einem 150 l Demonstrator aus Salzbeton und einem weiteren aus alkali-aktiviertem Material. Neben der konventionellen Schallemissionsanaylse mit Aktivitäts- und Intensitätsparametern der Zeitsignale, werden auch frequenzbasierte Parameter zur Analyse andiskutiert. N2 - After a brief introduction to acoustic emission testing and analysis, an experimental test setup is presented, which was part of the Seal Waste Safe project (internal BAM project 2019-2022). Herein, the acoustic emission measurements of a 150 l demonstrator made of salt concrete and another one made of alkali-activated material are focused. In addition to the conventional acoustic emission analysis regarding the activity and intensity parameters of the detected time signals, also frequency-based parameters were discussed for analysis. T2 - Dauerhafte Verschlussbauwerke für Endlager CY - Online meeting DA - 14.2.2022 KW - Acoustic Emission KW - Schallemission KW - Salzbeton KW - Alkali aktiviertes Material KW - Geopolymer PY - 2022 AN - OPUS4-54937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oster, Simon A1 - Fritsch, Tobias A1 - Ulbricht, Alexander A1 - Mohr, Gunther A1 - Bruno, Giovanni A1 - Maierhofer, Christiane A1 - Altenburg, Simon T1 - On the Registration of Thermographic In Situ Monitoring Data and Computed Tomography Reference Data in the Scope of Defect Prediction in Laser Powder Bed Fusion N2 - The detection of internal irregularities is crucial for quality assessment in metal-based additive manufacturing (AM) technologies such as laser powder bed fusion (L-PBF). The utilization of in-process thermography as an in situ monitoring tool in combination with post-process X-ray micro computed tomography (XCT) as a reference technique has shown great potential for this aim. Due to the small irregularity dimensions, a precise registration of the datasets is necessary as a requirement for correlation. In this study, the registration of thermography and XCT reference datasets of a cylindric specimen containing keyhole pores is carried out for the development of a porosity prediction model. The considered datasets show variations in shape, data type and dimensionality, especially due to shrinkage and material elevation effects present in the manufactured part. Since the resulting deformations are challenging for registration, a novel preprocessing methodology is introduced that involves an adaptive volume adjustment algorithm which is based on the porosity distribution in the specimen. Thus, the implementation of a simple three-dimensional image-to-image registration is enabled. The results demonstrate the influence of the part deformation on the resulting porosity location and the importance of registration in terms of irregularity prediction. KW - Selective laser melting (SLM) KW - Laser powder bed fusion (L-PBF) KW - Additive manufacturing (AM) KW - Process monitoring KW - Infrared thermography KW - X-ray computed tomography (XCT) KW - Defect detection KW - Image registration PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-549412 VL - 12 IS - 6 SP - 1 EP - 21 PB - MDPI AN - OPUS4-54941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano Munoz, Itziar A1 - Roveda, Ilaria A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Bruno, Giovanni T1 - Synchrotron x ray refraction detects microstructure and porosity evolution during in situ heat treatments in an LPBF ALSI10MG alloy N2 - The complexity of any microstructural characterization significantly increases when there is a need to evaluate the icrostructural evolution as a function of temperature. To date, this characterization is primarily performed by undertaking elaborative ex-situ experiments where the material’s heating procedure is interrupted at different temperatures or times. Moreover, these studies are often limited to a region smaller than the representative elementary volume, which can lead to partial or even biased interpretations of the collected data. This limitation can be greatly overcome by using in-situ synchrotron X-ray refraction (SXRR). T2 - ICTMS 2022 CY - Grenoble, France DA - 27.06.2022 KW - Synchrotron refraction KW - In situ heating KW - AlSi10Mg alloy KW - Additive manufacturing KW - Microstructural evolution PY - 2022 AN - OPUS4-55199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Becker, Tina A1 - Breese, Philipp Peter A1 - Maierhofer, Christiane T1 - Towards hyperspectral in-situ temperature measurement in metal additive manufacturing N2 - The industrial use of additive manufacturing for the production of metallic parts with high geometrical complexity and lot sizes close to one is rapidly increasing as a result of mass individualisation and applied safety relevant constructions. However, due to the high complexity of the production process, it is not yet fully understood and controlled, especially for changing (lot size one) part geometries. Due to the thermal nature of the Laser-powder bed fusion (L-PBF) process – where parts are built up layer-wise by melting metal powder via laser - the properties of the produced part are strongly governed by its thermal history. Thus, a promising route for process monitoring is the use of thermography. However, the reconstruction of temperature information from thermographic data relies on the knowledge of the surface emissivity at each position on the part. Since the emissivity is strongly changing during the process due to phase changes, great temperature gradients, possible oxidation, and other potential influencing factors, the extraction of real temperature data from thermographic images is challenging. While the temperature development in and around the melt pool, where melting and solidification occur is most important for the development of the part properties. Also, the emissivity changes are most severe in this area, rendering the temperature deduction most challenging. A possible route to overcome the entanglement of temperature and emissivity in the thermal radiation is the use of hyperspectral imaging in combination with temperature emissivity separation (TES) algorithms. As a first step towards the combined temperature and emissivity determination in the L-PBF process, here, we use a hyperspectral line camera system operating in the short-wave infrared region (0.9 µm to 1.7 µm) to measure the spectral radiance emitted. In this setup, the melt pool of the L-PBF process migrates through the camera’s 1D field of view, so that the radiation intensities are recorded simultaneously for multiple different wavelength ranges in a spatially resolved manner. At sufficiently high acquisition frame rate, an effective melt pool image can be reconstructed. Using the grey body approximation (emissivity is independent of the wavelength), a first, simple TES is performed, and the resulting emissivity and temperature values are compared to literature values. Subsequent work will include reference measurements of the spectral emissivity in different states allowing its analytical parametrisation as well as the adaption and optimisation of the TES algorithms. An illustration of the proposed method is shown in Fig.1. The investigated method will allow to gain a deeper understanding of the L-PBF process, e.g., by quantitative validation of simulation results. Additionally, the results will provide a data basis for the development of less complex and cheaper sensor technologies for L-PBF in-process monitoring (or for related process), e.g., by using machine learning. T2 - 21st International Conference on Photoacoustic and Photothermal Phenomena CY - Bled, Slovenia DA - 19.06.2022 KW - Thermography KW - Additive manufacturing KW - L-PBF KW - Hyperspectral PY - 2022 AN - OPUS4-55152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis Alexander A1 - Rehmer, Birgit A1 - Graf, B. A1 - Ulbricht, Alexander A1 - Skrotzki, Birgit A1 - Rethmeier, Michael T1 - Low cycle fatigue behavior of DED-L Ti-6AL-4V N2 - Laser powder-based directed energy deposition (DED-L) is a technology that offers the possibility for 3D material deposition over hundreds of layers and has thus the potential for application in additive manufacturing (AM). However, to achieve broad industrial application as AM technology, more data and knowledge about the fabricated materials regarding the achieved properties and their relationship to the manufacturing process and the resulting microstructure is still needed. In this work, we present data regarding the low-cycle fatigue (LCF) behavior of Ti-6Al-4V. The material was fabricated using an optimized DED-L process. It features a low defect population and excellent tensile properties. To assess its LCF behavior two conventionally manufactured variants of the same alloy featuring different microstructures were additionally tested. The strain-controlled LCF tests were carried out in fully reversed mode with 0.3 % to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behavior and failure mechanisms are described. For characterization, optical microscopy (OM), scanning electron microscopy (SEM), and micro-computed tomography (µCT) were used. The low defect population allows for a better understanding of the intrinsic material’s properties and enables a fairer comparison against the conventional variants. The fatigue lifetimes of the DED-L material are nearly independent of the test temperature. At elevated test temperatures, they are similar or higher than the lifetimes of the conventional counterparts. At room temperature, they are only surpassed by the lifetimes of one of them. The principal failure mechanism involves multiple crack initiation sites. T2 - Ninth International Conference on Low Cycle Fatigue (LCF9) CY - Berlin, Germany DA - 21.06.2022 KW - AGIL KW - Additive Manufacturing KW - Ti-6Al-4V KW - Low-Cycle-Fatigue KW - Microstructure PY - 2022 AN - OPUS4-55123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Altenburg, Simon A1 - Metz, C. A1 - Maierhofer, Christiane T1 - Aktive Laserthermografie im L-PBF-Prozess zur in-situ Detektion von Defekten N2 - Die zerstörungsfreie Prüfung von metallischen Bauteilen hergestellt mit additiver Fertigung (Additive Manufacturing - AM) gewinnt zunehmend an industrieller Bedeutung. Grund dafür ist die Feststellung von Qualität, Reproduzierbarkeit und damit auch Sicherheit für Bauteile, die mittels AM gefertigt wurden. Jedoch wird noch immer ex-situ geprüft, wobei Defekte (z.B. Poren, Risse etc.) erst nach Prozessabschluss entdeckt werden. Übersteigen Anzahl und/oder Abmessung die vorgegebenen Grenzwerte für diese Defekte, so kommt es zu Ausschuss, was angesichts sehr langer Bauprozessdauern äußerst unrentabel ist. Eine Schwierigkeit ist dabei, dass manche Defekte sich erst zeitverzögert zum eigentlichen Materialauftrag bilden, z.B. durch thermische Spannungen oder Schmelzbadaktivitäten. Dementsprechend sind reine Monitoringansätze zur Detektion ggf. nicht ausreichend. Daher wird in dieser Arbeit ein Verfahren zur aktiven Thermografie an dem AM-Prozess Laser Powder Bed Fusion (L-PBF) untersucht. Das Bauteil wird mit Hilfe des defokussierten Prozesslasers bei geringer Laserleistung zwischen den einzelnen gefertigten Lagen unabhängig vom eigentlichen Bauprozess erwärmt. Die entstehende Wärmesignatur wird ort- und zeitaufgelöst durch eine Infrarotkamera erfasst. Durch diese der Lagenfertigung nachgelagerte Prüfung werden auch zum Bauprozess zeitversetzte Defektbildungen nachweisbar. In dieser Arbeit finden die Untersuchungen als Proof-of-Concept, losgelöst vom AM-Prozess, an einem typischen metallischen Testkörper statt. Dieser besitzt eine Nut als oberflächlichen Defekt. Die durchgeführten Messungen finden an einer eigens entwickelten L-PBF-Forschungsanlage innerhalb der Prozesskammer statt. Damit wird ein neuartiger Ansatz zur aktiven Thermografie für L-PBF erforscht, der eine größere Bandbreite an Defektarten auffindbar macht. Der Ansatz wird validiert und Genauigkeit sowie Auflösungsvermögen geprüft. Eine Anwendung am AM-Prozess wird damit direkt forciert und die dafür benötigten Zusammenhänge werden präsentiert. T2 - DGZfP-Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Thermografie KW - Zerstörungsfreie Prüfung KW - Aktive Laserthermografie PY - 2022 AN - OPUS4-55040 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Altenburg, Simon A1 - Metz, C. A1 - Maierhofer, Christiane T1 - Aktive Laserthermografie im L-PBF-Prozess zur in-situ Detektion von Defekten N2 - Die zerstörungsfreie Prüfung von metallischen Bauteilen hergestellt mit additiver Fertigung (Additive Manufacturing - AM) gewinnt zunehmend an industrieller Bedeutung. Grund dafür ist die Feststellung von Qualität, Reproduzierbarkeit und damit auch Sicherheit für Bauteile, die mittels AM gefertigt wurden. Jedoch wird noch immer ex-situ geprüft, wobei Defekte (z.B. Poren, Risse etc.) erst nach Prozessabschluss entdeckt werden. Übersteigen Anzahl und/oder Abmessung die vorgegebenen Grenzwerte für diese Defekte, so kommt es zu Ausschuss, was angesichts sehr langer Bauprozessdauern äußerst unrentabel ist. Eine Schwierigkeit ist dabei, dass manche Defekte sich erst zeitverzögert zum eigentlichen Materialauftrag bilden, z.B. durch thermische Spannungen oder Schmelzbadaktivitäten. Dementsprechend sind reine Monitoringansätze zur Detektion ggf. nicht ausreichend. Daher wird in dieser Arbeit ein Verfahren zur aktiven Thermografie an dem AM-Prozess Laser Powder Bed Fusion (L-PBF) untersucht. Das Bauteil wird mit Hilfe des defokussierten Prozesslasers bei geringer Laserleistung zwischen den einzelnen gefertigten Lagen unabhängig vom eigentlichen Bauprozess erwärmt. Die entstehende Wärmesignatur wird ort- und zeitaufgelöst durch eine Infrarotkamera erfasst. Durch diese der Lagenfertigung nachgelagerte Prüfung werden auch zum Bauprozess zeitversetzte Defektbildungen nachweisbar. In dieser Arbeit finden die Untersuchungen als Proof-of-Concept, losgelöst vom AM-Prozess, an einem typischen metallischen Testkörper statt. Dieser besitzt eine Nut als oberflächlichen Defekt. Die durchgeführten Messungen finden an einer eigens entwickelten L-PBF-Forschungsanlage innerhalb der Prozesskammer statt. Damit wird ein neuartiger Ansatz zur aktiven Thermografie für L-PBF erforscht, der eine größere Bandbreite an Defektarten auffindbar macht. Der Ansatz wird validiert und Genauigkeit sowie Auflösungsvermögen geprüft. Eine Anwendung am AM-Prozess wird damit direkt forciert und die dafür benötigten Zusammenhänge werden präsentiert. T2 - DGZfP-Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Thermografie KW - Zerstörungsfreie Prüfung KW - Aktive Laserthermografie PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-550353 SN - 978-3-947971-25-1 VL - 177 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung e.V. AN - OPUS4-55035 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Soares, A.P. A1 - Kupsch, Andreas A1 - Baum, D. A1 - Hesse, B. A1 - Zaslansky, P. T1 - Untersuchung der Integrität von glasfaserverstärkten Zahnstiften mittels Synchrotron-Röntgenrefraktion N2 - Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden. Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Röntgen-Refraktion KW - Verbundwerkstoffe KW - Zahnstifte PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-549231 SP - 1 EP - 7 AN - OPUS4-54923 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Soares, A.P. A1 - Kupsch, Andreas A1 - Baum, D. A1 - Hesse, B. A1 - Zaslansky, P. T1 - Untersuchung der Integrität von glasfaserverstärkten Zahnstiften mittels Synchrotron-Röntgenrefraktion N2 - Die Integrität der Verstärkungsfasern in Komposit-Zahnstiften ist entscheidend für die Biegefestigkeit und die langfristige Haftung am Zement in den Wurzelkanälen. Es wurde vermutet, dass die Integrität von glasfaserverstärkten Zahnstiften durch das Beschleifen während der zahnmedizinischen Behandlung beeinträchtigt wird. Eine Beschädigung der Fasern führt zu einer erheblichen strukturellen Schwächung über den gesamten Stiftdurchmesser. Glasfragmente, die durch den Kontakt mit dem Zahnbohrer entstehen, können sich vom Stift lösen und die Haftfähigkeit erheblich verringern. Mit Hilfe hochauflösender Synchrotron-Röntgen-Refraktions-Radiographie (SXRR) konnte das Ausmaß der Schäden zuverlässig identifiziert und charakterisiert werden. Dazu wurden die Glasfaserstifte sowohl im Herstellungszustand als auch nach der Bearbeitung mit einem Diamantbohrer untersucht. Die Datensätze wurden zur Visualisierung und Quantifizierung der morphologischen Charakteristika intakter und durch das Beschleifen beschädigter Regionen analysiert. Sie zeigen Schäden im bearbeiteten Bereich (z. B. Brüche, Splitter und Risse) sowie herstellungsbedingte Inhomogenitäten der Fasern mit einer signifikanten Zunahme der inneren Oberflächen in Probenregionen, die durch das Beschleifen beschädigt wurden. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Röntgen-Refraktion KW - Verbundwerkstoffe KW - Zahnstifte PY - 2022 AN - OPUS4-54924 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ehlers, Henrik A1 - Pelkner, Matthias A1 - Thewes, R. A1 - Jutkuhn, D. T1 - Hochauflösende Online Wirbelstromprüfung von PBF LB/M Bauteilen mit GMR Arrays N2 - In den letzten Jahren haben additive Fertigungstechnologien an Bedeutung gewonnen. Für komplexe Funktionsbauteile oder die Produktion von Werkstücken in kleinen Stückzahlen kann das Laser-Pulverbettschmelzen eingesetzt werden. Hohe Sicherheitsanforderungen, z. B. in der Luft- und Raumfahrt, erfordern eine umfassende Qualitätskontrolle. Daher werden nach der Fertigung zerstörungsfreie Offline-Prüfverfahren wie die Computertomographie eingesetzt. In jüngster Zeit wurden zur Verbesserung der Rentabilität und Praktikabilität zerstörungsfreie Online-Prüfverfahren wie die optische Tomographie entwickelt. In diesem Beitrag wird die Anwendbarkeit der Wirbelstromprüfung mit GMR Sensoren für die online Prüfung von PBF-LB/M Teilen demonstriert. Die Ergebnisse einer online Wirbelstromprüfung mit GMR Sensoren und einer Ein-Draht-Anregung werden gezeigt. Während des Produktionsprozesses wird für jede Lage eine Wirbelstromprüfung durchgeführt. Trotz hochauflösender Arrays mit 128 Elementen wird durch eine angepasste Hardware die Prüfdauer geringgehalten. So kann die Messung während des Beschichtungsvorgangs durchgeführt werden, ohne den Fertigungsprozess signifikant zu verlangsamen. Eine online Wirbelstromprüfung eines stufenförmigen Testkörpers aus Haynes282 über 184 Lagen zeigt, dass die Kanten nicht nur in der aktuellen Lage detektiert werden können, sondern auch in einer Tiefe von 400 µm, wenn eine Anregungsfrequenz von 1,2 MHz gewählt wird. T2 - DGZfP Jahrestagung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Wirbelstrom KW - Additive Fertigung KW - GMR KW - PBF PY - 2022 AN - OPUS4-54899 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Serrano Munoz, Itziar A1 - Markötter, Henning A1 - Mehta, Bharat A1 - Hryha, Eduard A1 - Bruno, Giovanni T1 - In-situ imaging of additively manufactured alloys at the BAMline N2 - In this work, we present the recent in-situ imaging developments at the BAMline (of synchrotron BESSY II, HZB), focused on the in-situ characterization and understanding of microstructural evolution of additively manufactured materials subjected to different environments. Two show cases are presented. In the first, X-ray refraction radiography (SXRR) was combined with in-situ heat treatment to monitor the microstructural evolution as a function of temperature in a laser powder bed fusion (LPBF) manufactured AlSi10Mg alloy. We show that SXRR allows detecting the changes in the Si-phase morphology upon heating using statistically relevant volumes. SXRR also allows observing the growth of pores (i.e., thermally induced porosity), usually studied via X-ray computed tomography (XCT), but using much smaller fields-of-view. In the second case study, XCT was combined with in-situ tensile test to investigate the damage mechanism in a LPBF Aluminum Metal Matrix Composite (MMC). In-situ SXCT test disclosed the critical role of the defects in the failure mechanism along with pre-cracks in the reinforcement phase of MMC. We found that cracks were initiated from lack-of-fusion defects and propagated through coalescence with other defects. T2 - New Frontiers in Materials Design for Laser Additive Manufacturing CY - Montabaur, Germany DA - 22.05.22 KW - Additive manufacturing KW - Laser powder bed fusion KW - Synchrotron X-ray computed tomography KW - Synchrotron X-ray Refraction PY - 2022 AN - OPUS4-54900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander A1 - Bruno, Giovanni A1 - Mishurova, Tatiana A1 - Serrano Munoz, Itziar A1 - Roveda, Ilaria A1 - Fritsch, Tobias A1 - Ulbricht, Alexander A1 - Sprengel, Maximilian A1 - Schröder, Jakob T1 - Residual stresses and micromechanical properties of additively manufactured metals: why do we need a paradigm shift? N2 - An overview of the challenges and successes in the methodology to characherise residual stresses and micromechnical properties in additively manufactured metals T2 - CAM2 Annual Seminar 2022 - 5-year journey CY - Gothenburg, Sweden DA - 24.10.2022 KW - Additive Manufacturing KW - Residual stress KW - AGIL KW - MANUFACT KW - Micromechnical properties PY - 2022 AN - OPUS4-56466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ewert, U. A1 - Jaenisch, Gerd-Rüdiger A1 - Schumacher, David A1 - Zscherpel, U. A1 - Deresch, A. A1 - Bircher, B. A1 - Meli, F. T1 - Schnelle Messung und tomographische Rekonstruktion von Brennflecken < 5 μm durch Aufnahmen strukturierter Prüfkörper N2 - Im Europäischen EMPIR-Projekt „NanoXSpot“ (Measurement of the focal spot size of Xray tubes with spot sizes down to 100 nm) werden neue Messmethoden für Brennflecke von Röntgenröhren entwickelt. Teil des Projektes ist die Entwicklung eines zur Lochkameramethode äquivalenten Messverfahrens für kleine Brennflecke. ASTM E 1165-20, Annex A, beschreibt die Bestimmung von Brennfleckgrößen aus Kantenprofilen von Lochaufnahmen für Röntgenröhren mit Brennflecken > 50 μm. Es wurde bereits vorgeschlagen über die Analyse der richtungsabhängigen Kantenunschärfe einer Lochblende und anschließender CT-Rekonstruktion die Intensitätsverteilung des Brennflecks äquivalent zur Lochkameraaufnahme zu berechnen. Die Lochkameramethode, wie in EN 12543-2 und ASTM E 1165-20 beschrieben, ist im unteren Größenbereich für Mikrofokusröhren nicht geeignet, da Pinholes < 10 μm schwer zu fertigen sind und lange Belichtungszeiten erwartet werden. Mit Hilfe exakt gefertigter Lochblenden sowie strukturierter Targets mit konvergierenden Strukturen wird der Bereich mit der Single-Shot-CT-Methode auf die Messung von Mikrofokusröhren, alternativ zur Vermessung von Kanten oder Strichgruppenkörpern, erweitert. Die rekonstruierten Brennfleckformen werden mit Kantenund Lochkameraaufnahmen quantitativ verglichen, um die Messgenauigkeit zu bewerten. Außerdem werden CNR und Messzeit bestimmt, um die Wirtschaftlichkeit der Verfahren zu bewerten. T2 - DGZfP-Jahrestagung CY - Online meeting DA - 10.05.2021 KW - Röntgenröhre KW - Brennfleckmessung KW - Prüfkörper KW - Rekonstruktion PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-561846 SP - 1 EP - 2 AN - OPUS4-56184 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Serrano Munoz, Itziar A1 - Magnier, V. A1 - Brunel, F. A1 - Dufrenoy, P. T1 - Influence of the Composition on the Compressive Behaviour of a Semi-Metallic Brake-Pad Material N2 - The contact interface between the rotation and static part of a friction brake is central to the optimal functioning of the brake system due to the occurrence of heat dissipation, mechanical interaction and thermal exchanges. Generally, braking performances are evaluated by the energetic efficiency and wear rates of the contact surface. However, the compressive behaviour of the contact materials has also a significant contribution to the overall performances. In this work, the meso- and microscopic compressive behaviour of a sintered semi-metallic brake-pad material is investigated mainly via compression testing coupled with Digital Image Correlation (DIC) technique, as well as optical and scanning electron microscopy (SEM) analysis. The composition of a reference material (RM) is simplified to a selection of nine components, as opposed to up to thirty components typically used in commercial brake-pad materials. The retained components are considered as the most crucial for safe-operating performances. At the studied stress levels, the RM material is flexible (E = 5330 MPa), deformable (Ezz−plastic = −0.21%), and exhibits hysteresis loops. Subsequently, the contribution to the mechanical response of each individual component is investigated by producing the so-called dissociated materials, where the number of components is, at a time, further reduced. It is observed that the macroscopic behaviour is mainly controlled by the content (i.e., size distribution, shape and nature) of graphite particles, and that the hysteresis is only related to one of the two types of graphite used (G2 particles). Moreover, RM containing 13 wt% of G2 particles embedded in a relatively soft matrix (10.86 GPa) is able to increase the hysteresis (by 35%) when compared to the dissociated material containing 20 wt% of G2 particles which is embedded in a stiffer matrix (E = 106 GPa). KW - Semi-metallic brake-pad material KW - Powder metallurgy KW - Components influence KW - Graphite induced hysteresis KW - Digital image correlation (DIC) KW - Compression testing PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-562003 VL - 15 IS - 22 SP - 7911 PB - MDPI AN - OPUS4-56200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Evsevleev, Sergei A1 - Mishurova, Tatiana A1 - Meinel, Dietmar A1 - Koptyug, A. A1 - Surmeneva, M. A1 - Khrapov, D. A1 - Paveleva, A. A1 - Surmenev, R. T1 - Procedures for quantitative characterization of periodic minimal surface structures (TMPSS) N2 - Additively manufactured (AM) triply periodic metallic minimum surface structures (TPMSS, from the English Triply Periodic Minimum Surface Structures) fulfill several requirements in both biomedical and engineering fields: tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some quality control challenges that may prevent their successful application. In fact, optimization of the AM process is impossible without considering structural features such as manufacturing accuracy, internal defects, and surface topography and roughness. In this study, quantitative nondestructive analysis of Ti-6Al-4V alloy TPMSS was performed using X-ray computed tomography (XCT). Several new image analysis workflows are presented to evaluate the effects of buildup direction on wall thickness distribution, wall degradation, and surface roughness reduction due to chemical etching of TPMSS. It is shown that the fabrication accuracy is different for the structural elements printed parallel and orthogonal to the fabricated layers. Different strategies for chemical etching showed different powder removal capabilities and thus a gradient in wall thickness. This affected the mechanical performance under compression by reducing the yield stress. A positive effect of chemical etching is the reduction of surface roughness, which can potentially improve the fatigue properties of the components. Finally, XCT was used to correlate the amount of powder retained with the pore size of the TPMSS, which can further improve the manufacturing process. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - Surface roughness KW - Additive manufacturing KW - Computed tomography KW - Wall thickness KW - Machine learning KW - Manufacturing defects PY - 2022 AN - OPUS4-56162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Serrano Munoz, Itziar A1 - Fernandez, R. A1 - Gonzalez-Doncel, G. A1 - Garces, G. T1 - A paradigm shift in the description of creep in metals can only occur through multi-scale imaging N2 - The description of creep in metals has reached a high level of complexity; fine details are revealed by all sorts of characterization techniques and different theoretical models. However, to date virtually no fully microstructure-driven quantitative description of the phenomenon is available. This has brought to interesting inconsistencies; the classic description of (secondary) creep rests on the so-called power law, which however: a- has a pre-factor spanning over 10 orders of magnitude; b- has different reported exponents for the same material; c- has no explanation for the values of such exponents. Recently, a novel description (the so-called Solid State Transformation Creep (SSTC) Model) has been proposed to tackle the problem under a different light. The model has two remarkable features: 1- it describes creep as the accumulation of elementary strains due to dislocation motion; 2- it predicates that creep is proceeding by the evolution of a fractal arrangement of dislocations. Such description, however, needs a great deal of corroborating evidence, and indeed, is still incomplete. To date, we have been able to observe and somehow quantify the fractal arrangement of microstructures through Transmission Electron Microscopy (TEM), observe the accumulation of dislocations at grain boundaries by EBSD-KAM (Electron Back-Scattered Diffraction-Kernel Angular Misorientation) analysis, quantify the kinetic character (solid state transformation) of experimental creep curves, and estimate the sub-grain size of the fractal microstructure through X-ray refraction techniques. All pieces of the mosaic seem to yield a consistent picture: we seem being on the right path to reconstruct the whole elephant by probing single parts of it. What is still missing is the bond between the various scales of investigation. T2 - Korrelative Materialcharakterisierung 2022 CY - Dresden, Germany DA - 13.10.2022 KW - X-ray refraction KW - EBSD KW - Alloys KW - TEM KW - SEM PY - 2022 AN - OPUS4-56163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Van Tran, K. A1 - Woracek, R. A1 - Kardjilov, N. A1 - Markötter, Henning A1 - Abou-Ras, D. A1 - Puplampu, S. A1 - Förster, C. A1 - Penumadu, D. A1 - Dahlberg, C. F. O. A1 - Banhart, J. A1 - Manke, I. T1 - Torsion of a rectangular bar: Complex phase distribution in 304L steel revealed by neutron tomography N2 - Metastable austenitic stainless steel (304L) samples with a rectangular cross-section were plastically deformed in torsion during which they experienced multiaxial stresses that led to a complex martensitic phase distribution owing to the transformation induced plasticity effect. A three-dimensional characterization of the phase distributions in these cm-sized samples was carried out by wavelength-selective neutron tomography. It was found that quantitatively correct results are obtained as long as the samples do not exhibit any considerable preferential grain orientation. Optical microscopy, electron backscatter diffraction, and finite element modeling were used to verify and explain the results obtained by neutron tomography. Altogether, neutron tomography was shown to extend the range of microstructure characterization methods towards the meso- and macroscale. KW - Neutron tomography KW - Phase distribution KW - Rectangular cross-section KW - Torsion KW - Geometrical effect PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-561649 SN - 0264-1275 VL - 222 SP - 111037 PB - Elsevier Ltd. AN - OPUS4-56164 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Bernd R. A1 - Kupsch, Andreas A1 - Bruno, Giovanni T1 - Microstructure characterization of materials using X-ray refraction techniques N2 - X-ray refraction is an excellent tool for the characterization of the microstructure of materials. However, there are only a few (synchrotron) laboratories in the world that use this technique for material characterisation. Therefore, the seminar will first explain the basic principles of X-ray refraction and the measurement techniques installed at the hard X-ray beamline BAMline at BESSY II (Berlin, Germany). This is followed by examples of investigations on fibre-reinforced plastic composites (CFRP) as well as ceramic (Cordierite, ZrO2-SiO2) and metallic materials (Ti-6Al-4V, Inconel). Some of the investigations were carried out both ex-situ and in-situ under mechanical and thermal load. The results are correlated with the mechanical properties of the materials. T2 - LNLS Users Group Seminar Series CY - Campinas, Brasil DA - 25.10.2022 KW - X-ray refraction KW - Analyzer-Based Imaging KW - BAMline PY - 2022 AN - OPUS4-56117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Voloskov, B. A1 - Mishurova, Tatiana A1 - Evlashin, S. A1 - Akhatov, I. A1 - Bruno, Giovanni A1 - Sergeichev, I. T1 - Artificial Defects in 316L Stainless Steel Produced by Laser Powder Bed Fusion: Printability, Microstructure, and Effects on the Very-High-Cycle Fatigue Behavior N2 - The printability of artificial defects inside the additively manufactured laser powder bed fusion (LPBF) 316L stainless steel is investigated. The printing parameters of the LPBF process are optimized to produce artificial defects with reproducible sizes at desired positions while minimizing redundant porosity. The smallest obtained artificial defect is 90 μm in diameter. The accuracy of the geometry of the printed defect depends on both the height and the diameter in the input model. The effect of artificial defects on the very-high-cycle fatigue (VHCF) behavior of LPBF 316L stainless steel is also studied. The specimens printed with artificial defects in the center are tested under VHCF using an ultrasonic machine. Crack initiation is accompanied by the formation of a fine granular area (FGA), typical of VHCF. Despite the presence of relatively large artificial defects, FGA formation is observed around accidental natural printing defects closer to the surface, which can still be considered as internal. The causes for this occurrence are discussed. KW - Additive manufacturing KW - Laser powder bed fusion KW - X-ray computed tomography KW - VHCF PY - 2022 U6 - https://doi.org/10.1002/adem.202200831 SP - 1 EP - 13 PB - Wiley VHC-Verlag AN - OPUS4-56109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Mehta, B. A1 - Nyborg, L. A1 - Virtanen, E. A1 - Markötter, Henning A1 - Hryha, E. A1 - Bruno, Giovanni T1 - Failure Mechanisms Investigation by Means of in-situ Synchrotron Computed Tomography in Aluminum MMC-based Alloy Tailored for Additive Manufacturing (AM) N2 - The availability of high-performance Al alloys in AM is limited due to difficulties in printability, requiring both the development of synergetic material and AM process to mitigate problems such as solidification cracking during laser powder bed fusion (LPBF). The goal of this work was to investigate the failure mechanism in a LPBF 7017 Aluminium alloy + 3 wt% Zr + 0.5 wt% TiC. The processing leads to different categories of Zr-rich inclusions, precipitates and defects. T2 - Alloys for Additive Manufacturing Symposium 2022 (AAMS22) CY - Munich, Germany DA - 11.09.2022 KW - Additive manufacturing KW - Laser powder bed fusion KW - Synchrotron X-ray computed tomography KW - MMC PY - 2022 AN - OPUS4-56110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Rüden, H. A1 - Meinel, Dietmar A1 - Fritsch, Tobias T1 - Röntgen-Computertomographie (CT) für die Kulturguterhaltung N2 - Als bildgebendes und zerstörungsfreies Verfahren eignet sich die Röntgen-Computertomographie (CT) insbesondere bei der Untersuchung von Kunst- und Kulturgütern. Die für Werkstoffprüfung und Materialanalyse konzipierten CT-Anlagen bieten dank hoher Röntgenleistung die Möglichkeit zusätzlich zu Holz, Keramiken und Kunststoffen auch stark schwächende Materialien, wie bspw. Metalle, zu durchdringen. Für eine hohe räumliche Auflösung im unteren Mikrometerbereich (2-200µm) sorgen entsprechend ausgelegte CT-Anlagen. In der Bundesanstalt für Materialforschung und -prüfung (BAM) stehen mehrere solcher CT-Anlagen für unterschiedliche Fragestellungen sowie Probengrößen und - materialien zur Verfügung. Einige Beispiele aus den vergangenen Arbeiten der BAM veranschaulichen das große Potential dieser Untersuchungsmethode. Da bei einer CT-Messung in der Regel das gesamte Untersuchungsobjekt erfasst und in ein digitales Volumenmodell überführt wird, eröffnet sich für Archäologen und Restoratoren die Möglichkeit Untersuchungen hinsichtlich Materialzusammensetzung, Erhaltungszustand und Herstellungstechnik am virtuellen Objekt vorzunehmen, ohne die Originalsubstanz zu beeinträchtigen. Gegenüber der klassischen Radiografie, bei der nur eine zweidimensionale Abbildung erreicht wird, bietet die CT-Untersuchung die Möglichkeit innenliegende Strukturen dreidimensional zu erfassen. Die notwendige Bestimmung der Objektoberfläche erlaubt zudem die Erstellung eines Oberflächenmodells des untersuchten Gegenstandes. Damit lassen sich unter anderem mechanische Simulationen (Belastung, Durchbiegung, Durchströmung) durchführen. Der erzeugte Datensatz kann somit auch zur Herstellung eines Replikats im 3D-Druckverfahren genutzt werden. Anhand der Untersuchung der Mandoline von Smorsone wird gezeigt, wie eine CT-Messung durchgeführt wird und wie in dem anschließend rekonstruierten 3D-Datensatz mittels Koordinatenmesstechnik Maße (Abstände, Wandstärken, Winkel) exakt ermittelt werden können. T2 - Jahrestagung der Gesellschaft für Musikforschung CY - Berlin, Germany DA - 28.09.2022 KW - Mikro-CT KW - Bildverarbeitung KW - Holz KW - Bronze KW - ZfP PY - 2022 AN - OPUS4-56412 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Artzt, K. A1 - Haubrich, J. A1 - Sevostianov, I. A1 - Requena, G. A1 - Bruno, Giovanni T1 - Micromechanical behavior of annealed Ti-6Al-4V produced by Laser Powder Bed Fusion N2 - The micromechanical behavior of an annealed Ti-6Al-4V material produced by Laser Powder Bed Fusion was characterized by means of in-situ synchrotron X-ray diffraction during a tensile test. The lattice strain evolution was obtained parallel and transversal to the loading direction. The elastic constants were determined and compared with the conventionally manufactured alloy. In the plastic regime, a lower plastic anisotropy exhibited by the lattice planes was observed along the load axis (parallel to the building direction) than in the transverse direction. Also, the load transfer from α to β phase was observed, increasing global ductility of the material. The material seems to accumulate a significant amount of intergranular strain in the transverse direction. KW - Additive manufacturing KW - Ti-6Al-4V KW - Anisotropy KW - Intergranular strain KW - Synchrotron X-ray diffraction PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-547406 VL - 2 IS - 1 SP - 186 EP - 201 PB - Taylor & Francis AN - OPUS4-54740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Weise, Frank A1 - Oesch, T. A1 - Wilsch, Gerd A1 - Sigmund, S. A1 - Hünger, K.-J. A1 - Kositz, M. T1 - Analyse des gefügeabhängigen Löslichkeitsverhaltens potenziell AKR-empfindlicher Gesteinskörnungen T1 - Analysis of the microstructure depending solubility behavior of potential ASR sensitive aggregates N2 - Das gefügeabhängige Löslichkeitsverhalten wurde an folgenden vier Gesteinskörnungen unterschiedlicher Alkaliempfindlichkeitsklassen untersucht: • GK1 (EIII-S): quarzreicher Kies • GK2 (EIII-S): Grauwacke (Splitt) • GK3 (EI-S): Quarz-Feldspat-Porphyr (Splitt) • GK4 (EI-S): sandsteinreicher Kies DiePorenstrukturanalyse erfolgte sowohl an Einzelkörnern mittels vergleichender 3D-CT und BET- Untersuchungen als auch an Korngemengen der einzelnen Kornfraktionen (außer Fraktion 16/22 mm) über die Wasseraufnahme und mit BET. Für die Visualisierung und Quantifizierung der von außen zugänglichen Oberflächenanteile der Einzelkörner wurde ein Softwaretool entwickelt, erprobt und erfolgreich angewandt. Es gelang so u.a. den Nachweis zu erbringen, dass die gebrochenen Einzelkörner der Grauwacke und des Rhyoliths einen deutlich geringeren von außen zugänglichen Oberflächenanteil als die gleichartigen Gesteinskörner aus dem Kies besitzen. Aufgrund der limitierten Ortsauflösung der 3D-CT von 11 bis 16,5 μm wurde mit BET eine um drei Zehnerpotenzen höhere spezifische Oberfläche ermittelt. Zu den Porositätsuntersuchungen an den Korngemengen sei angemerkt, dass zum Teil gegenläufige Trends zwischen offener Porosität und spezifischer Oberfläche festgestellt wurden. Dieses ist beim Bezug des bei den Löseversuchen in 0,1 M KOH mit definierter NaCl-Zugabe aus der Gesteinskörnung gelösten SiO2 und Al2O3 von zentraler Bedeutung. Bei den Löseversuchen an den fraktionsspezifischen Korngemengen selbst zeigte sich, dass die stufenweise Erhöhung des NaCl-Gehalts von 0 auf 10 M.-% im Eluat eine erhöhte SiO2-Löslichkeit und eine verminderte Auslaugung von Al2O3 zur Folge hat. Auffallend war hierbei, dass die Al2O3-Löslichkeit bei GK4 ohne und mit geringer NaCl-Zugabe die mit Abstand höchsten Werte annimmt. Bei den zusätzlich durchgeführten Löseversuchen an den tomografierten Einzelkörnern in 1 M KOH-Lösung mit Zugabe von 1 M.-% NaCl zeigte sich, dass nur vereinzelt bei den untersuchten Gesteinsarten eine Korrelation zwischen dem SiO2- bzw. Al2O3-Gehalt im Eluat und der absoluten BET-Oberfläche nachweisbar ist. Dies ist vermutlich darauf zurückzuführen, dass neben der Oberfläche weitere Parameter (z.B. die mineralogische Zusammensetzung der Einzelkörner) das Löseverhalten maßgebend beeinflussen. Bei den parallel zu den Löseversuchen durchgeführten Betonversuchen nach dem ARS 04/2013 zeigte sich, dass die Alkaliempfindlichkeit der GK4 bei beiden Betonversuchen mit Alkalizufuhr unterschiedlich zu bewerten ist. So ist unabhängig von der vorgegebenen pessimalen Betonrezeptur des Fahrbahndeckenbetons ausschließlich bei der Klimawechsellagerung die GK4 als alkaliempfindlich einzustufen. Allerdings konnte der Befund der stark ausgeprägten AKR bei der GK4 mit der Dünnschliffmikroskopie nicht bestätigt werden. Analoges gilt für die Bewertung der Alkaliempfindlichkeit von GK2 mit den Betonversuchen nach der Alkalirichtlichtlinie des DAfStb. So ist auch hier die GK2 nicht im 60 °C-Betonversuch sondern ausschließlich im 40 °C-Betonversuch als alkaliempfindlich einzustufen. Dienach den verschiedenartigen Betonversuchen durchgeführten LIBS-Analysen am Vertikalschnitt der Prüfkörper zeigen, dass im Kernbereich nach dem 60 °C-Betonversuch mit 10 %iger NaCl-Lösung und nach der Klimawechsellagerung mit NaCl-Beaufschlagung annähernd gleich hohe Natrium- und Chloridgehalte vorgefunden werden. Wider Erwarten treten an den beaufschlagten Prüfflächen Abreicherungen von Natrium und Anreicherungen von Chlorid auf. Im 40°C- und 60 °C-Betonversuch wurde das Natrium bis in eine maximale Tiefe von ca. 30 mm bzw. 20 mm ausgelaugt. Die aufbauenden korrelativen Betrachtungen zwischen den Ergebnissen des 60°C Betonversuchs mit Alkalizufuhr und der Löseversuche an den fraktionsspezifischen Korngemengen in 1 M KOH-Lösung mit definierter NaCl-Zugabe sind durchaus vielversprechend. So zeigt sich beispielsweise beim Waschbeton, dass der fraktionsspezifisch gewichtete SiO2-Überschuss im Eluat nach 56 Tagen mit Zugabe von 0,5 M.-% NaCl ohne Bezug auf die BET-Oberfläche zur gleichen Einstufung der vier betrachteten Gesteinskörnungen wie bei den Dehnungen im 60 °C-Betonversuch mit 3 %-iger NaCl-Lösung führt. Außerdem korrelieren die im 60 °C-Betonversuch mit 10 %-iger NaCl-Lösung ermittelten Dehnungen mit dem gewichteten SiO2-Überschuss im Eluat bei Zugabe von 2 M.-% NaCl ohne Bezug auf die BET-Oberfläche. Ausschließlich bei den Betonversuchen nach der Alkali-Richtlinie erwies sich der Bezug des im Eluat ermittelten SiO2-Überschusses auf die BET-Oberfläche als zielführend. Aufgrund des Potenzials der Löseversuche mit NaCl-Zugabe für die Bewertung der Alkaliempfindlichkeit der Gesteinskörnung im Fahrbahndeckenbeton wird empfohlen, die vergleichenden Untersuchungen zwischen den Löseversuchen an Korngemischen der einzelnen Fraktionen und den Betonversuchen nach dem ARS 04/2013 mit einer möglichst hohen Anzahl an Gesteinskörnungen und einem präzisierten Untersuchungsumfang fortzuführen. N2 - The following four aggregates (GK) of varying grades of alkali sensitivity were examined for their microstructure-dependent solubility behavior: • GK1 (EIII-S) gravel with high quarz content • GK2 (EIII-S) greywacke (crushed stone) • GK3 (EI-S) quarz-feldspar-porphyry (crushed stone) • GK4 (EI-S) gravel with high sandstone content Pore structure analysis was carried out both on single grains using comparative 3D-CT and BET tests, and on grain samples of individual grain fractions (excluding the 16/22 mm fraction) using water absorption and BET. A software tool for visualizing and quantifying the externally accessible surfaces of single grains was developed, tested and successfully applied. This enabled us, among other things, to prove that single broken grains of greywacke and rhyolite have a much smaller externally accessible surface than grains of gravel of the same aggregate fraction. Due to the 3D-CT’s limited spatial resolution of 11 to 16.5 μm, BET was used to determine a two to three powers of ten higher specific surface. In relation to the porosity tests of the grain samples, it should be noted that in some cases, counterdirectional trends between open porosity and specific surface were determined. This is of central importance in relation to the SiO2 and Al2O3 dissolved from the aggregate in the solubility tests in 1 M KOH with defined addition of NaCl. The solubility tests on the grain samples of specific fractions showed that the gradual increase of the NaCl content in the eluate from 0 to 10 M.-% resulted in increased SiO2 solubility and reduced leaching of Al2O3. It was striking in this context that the solubility of Al2O3 in GK4 with no or little addition of NaCl gives by far the highest values. The additional solubility tests carried out on single grains, that were previously subjected to CT testing, in 1 M KOH solution with 1 M.-% added NaCl showed that in the types of aggregate examined, a correlation between the SiO2 and Al2O3 in eluate and the absolute BET surface is only occasionally demonstrable. This is probably due to the fact that solubility behavior is decisively influenced by other parameters in addition to the surface (e.g. by the mineralogical composition of individual grains). The concrete tests according to ARS 04/2013 carried out parallel to the solubility tests showed that GK4’s alkali sensitivity in both concrete tests with added alkali must be evaluated differently. For example, independent of the prescribed pessimal road surface concrete formula, GK4 can only be classified as alkali sensitive under cyclic storage. However petrographic microscopy could not confirm the findings of very marked ASR in GK4. The same applies to the evaluation of alkali sensitivity in GK2 with the concrete tests according to the German Committee for Structural Concrete (DAfStb)’s Alkali Guidelines. In this case too, GK2 should not be classified as alkali sensitive in 60 °C concrete testing, but only in 40 °C concrete testing. The LIBS analyses carried out on the vertical cross-section of the test specimens after the various concrete tests showed that almost equally high sodium and chloride levels were found in the core area after the 60 °C concrete prism test with 10 % NaCl solution and after cyclic storage with NaCl application. Contrary to expectations, the surfaces of samples after NaCl application showed a decrease in sodium and an increase in chloride. In the 40°C and 60°C concrete prism tests, sodium was depleted up to a maximum depth of approx. 30 mm and 20 mm respectively. Subsequent correlative observations between the findings of the 60°C concrete prism test with alkali application, and the solubility tests on the samples of specific grain fractions in 1 M KOH solution with defined NaCl addition, are very promising. In the case of exposed aggregate concrete, for example, the fraction-specific weighted excess SiO2 to in the eluate after 56 days with added 0.5 M.-% NaCl unrelated to the BET surface results in the same classification of the four aggregates examined as the expansions in the 60 °C concrete prism test with 3% NaCl solution. In addition, the expansions found in the 60 °C concrete prism test with 10% NaCl solution correlated with the weighted excess SiO2 in eluate with added 2 M.-% NaCl without relation to the BET surface. Only in the case of the concrete test in accordance with the Alkali Guidelines did the relationship of the excess SiO2 in the eluate to the BET surface prove to be productive. Due to the potential of the solubility test with added NaCl for the evaluation of alkali sensitivity of aggregates in road surface concrete, we recommend continuing with comparative tests between solubility tests of grain samples of the various fractions and the concrete tests in accordance with ARS O4/13 with the greatest possible number of aggregates and a precisely defined investigation scope. KW - LIBS KW - Betonfahrbahndecke KW - Alkali-Kieselsäure-Reaktion KW - Gesteinskörnung KW - Alkaliempfindlichkeit KW - 3D-CT KW - Tausalzeintrag PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:hbz:opus-bast-25832 UR - https://bast.opus.hbz-nrw.de/frontdoor/index/index/docId/2583 SN - 978-3-95606-648-1 SN - 0943-9323 VL - S 165 SP - 1 EP - 111 PB - Fachverlag NW in der Carl Ed. Schünemann KG CY - Bremen AN - OPUS4-54755 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Becker, Tina A1 - Breese, Philipp Peter A1 - Scheuschner, Nils A1 - Maierhofer, Christiane A1 - Ulbricht, Alexander A1 - Frisch, Tobias A1 - Mohr, Gunther A1 - Altenburg, Simon T1 - Defect prediction in laser powder bed fusion based on thermographic features utilizing convolutional neural networks N2 - The appearance of irregularities such as keyhole porosity is a major challenge for the production of metal parts by laser powder bed fusion (PBF-LB/M). The utilization of thermographic in-situ monitoring is a promising approach to extract the thermal history which is closely related to the formation of irregularities. In this study, we investigate the utilization of convolutional neural networks to predict keyhole porosity based on thermographic features. Here, the porosity information calculated from an x-ray micro computed tomography scan is used as reference. Feature engineering is performed to enable the model to learn the complex physical characteristics of the porosity formation. The model is examined with regard to the choice of hyperparameters, the significance of thermal features and characteristics of the data acquisition. Based on the results, future demands on irregularity prediction in PBF-LB/M are derived. T2 - GIMC SIMAI YOUNG 2022 CY - Pavia, Italy DA - 29.09.2022 KW - Laser Powder Bed Fusion KW - Thermography KW - In-situ Monitoring KW - Convolutional Neural Networks PY - 2022 AN - OPUS4-56331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Becker, Tina A1 - Breese, Philipp Peter A1 - Scheuschner, Nils A1 - Altenburg, Simon T1 - Machine Learning based defect detection in Laser Powder Bed Fusion utilizing thermographic feature data N2 - The formation of irregularities such as keyhole porosity pose a major challenge to the manufacturing of metal parts by laser powder bed fusion (PBF-LB/M). In-situ thermography as a process monitoring technique shows promising potential in this manner since it is able to extract the thermal history of the part which is closely related to the formation of irregularities. In this study, we investigate the utilization of machine learning algorithms to detect keyhole porosity on the base of thermographic features. Here, as a referential technique, x-ray micro computed tomography is utilized to determine the part's porosity. An enhanced preprocessing workflow inspired by the physics of the keyhole irregularity formation is presented in combination with a customized model architecture. Furthermore, experiments were performed to clarify the role of important parameters of the preprocessing workflow for the task of defect detection . Based on the results, future demands on irregularity prediction in PBF-LB/M are derived. T2 - International Conference on NDE 4.0 CY - Berlin, Germany DA - 24.10.2022 KW - Laser Powder Bed Fusion KW - Thermography KW - In-situ Monitoring KW - Convolutional Neural Networks PY - 2022 AN - OPUS4-56332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Maack, Stefan A1 - Benner, Philipp A1 - Kröll, Mirco A1 - Prager, Jens A1 - Daum, Werner A1 - Casperson, Ralf A1 - Heckel, Thomas A1 - Spaltmann, Dirk A1 - et al., ED - Wahlster, W. ED - Winterhalter, C. T1 - Deutsche Normungsroadmap künstliche Intelligenz Ausgabe 2 N2 - Im Auftrag des Bundesministeriums für Wirtschaft und Klimaschutz haben DIN und DKE im Januar 2022 die Arbeiten an der zweiten Ausgabe der Deutschen Normungsroadmap Künstliche Intelligenz gestartet. In einem breiten Beteiligungsprozess und unter Mitwirkung von mehr als 570 Fachleuten aus Wirtschaft, Wissenschaft, öffentlicher Hand und Zivilgesellschaft wurde damit der strategische Fahrplan für die KI-Normung weiterentwickelt. Koordiniert und begleitet wurden diese Arbeiten von einer hochrangigen Koordinierungsgruppe für KI-Normung und -Konformität. Mit der Normungsroadmap wird eine Maßnahme der KI-Strategie der Bundesregierung umgesetzt und damit ein wesentlicher Beitrag zur „KI – Made in Germany“ geleistet. Die Normung ist Teil der KI-Strategie und ein strategisches Instrument zur Stärkung der Innovations- und Wettbewerbsfähigkeit der deutschen und europäischen Wirtschaft. Nicht zuletzt deshalb spielt sie im geplanten europäischen Rechtsrahmen für KI, dem Artificial Intelligence Act, eine besondere Rolle. KW - Digitalisierung KW - Künstliche Intelligenz KW - Data Sciences KW - Normung Roadmap PY - 2022 SP - 1 EP - 448 AN - OPUS4-56576 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hohendorf, Stefan A1 - Solís del Toro, María A1 - Friedmann, Sonja A1 - Grunwald, Marcel A1 - Redmer, Bernhard T1 - Medea und Jason, Eine Radiologische Untersuchung im Neuen Palais Potsdam N2 - Seit der Antike gehört die Medea-Sage zu den bekanntesten Geschichten der Weltliteratur. Der berühmte französische Künstler Carle Van Loo hat sich dieses Epos um 1759 angenommen und ein beeindruckendes Ölgemälde mit Abmessungen von 2,30x3,28m² erschaffen. Mit Mademoiselle Clairon als Medea und Henri Louis Le Kain als Jason ist ein Kunstwerk entstanden, das seitdem einige Veränderungen und Restaurierungen erfahren hat. Die Bundesanstalt für Materialforschung und -prüfung (BAM) hatte 2020 die Möglichkeit, dieses und ein zweites Kunstwerk, im Neuen Palais in Potsdam, für die Stiftung Preußische Schlösser und Gärten Berlin-Brandenburg, radiografisch zu untersuchen. Hierbei wurden sowohl technologisch als auch kunsthistorisch einige interessante Entdeckungen gemacht, die im vorliegenden Beitrag vorgestellt werden. T2 - DGZfP Jahrestatung 2022 CY - Kassel, Germany DA - 23.05.2022 KW - Röntgen KW - X-Ray KW - Kunsstechnologisch KW - Gemälde KW - Untermalung KW - Speicherfolie KW - Strahlenschutz PY - 2022 AN - OPUS4-56577 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Roveda, Ilaria A1 - Serrano Munoz, Itziar A1 - Mishurova, Tatiana A1 - Madia, Mauro A1 - Pirling, T. A1 - Evans, Alexander A1 - Klaus, M. A1 - Haubrich, J. A1 - Requena, G. A1 - Bruno, Giovanni T1 - Influence of a 265 °C heat treatment on the residual stress state of a PBF-LB/M AlSi10Mg alloy N2 - Laser Powder Bed Fusion (PBF-LB/M) additive manufacturing (AM) induces high magnitude residual stress (RS) in structures due to the extremely heterogeneous cooling and heating rates. As the RS can be deleterious to the fatigue resistance of engineering components, great efforts are focused on understanding their generation and evolution after post-process heat treatments. In this study, one of the few of its kind, the RS relaxation induced in an as-built PBF-LB/M AlSi10Mg material by a low-temperature heat treatment (265 °C for 1 h) is studied by means of X-ray and neutron diffraction. Since the specimens are manufactured using a baseplate heated up to 200 °C, low RS are found in the as-built condition. After heat treatment a redistribution of the RS is observed, while their magnitude remains constant. It is proposed that the redistribution is induced by a repartition of stresses between the a-aluminium matrix and the silicon phase, as the morphology of the silicon phase is affected by the heat treatment. A considerable scatter is observed in the neutron diffraction RS profiles, which is principally correlated to the presence (or absence) of pockets of porosity developed at the borders of the chessboard pattern. KW - Neutron diffraction KW - Additive manufacturing PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-565115 SN - 1573-4803 VL - 57 SP - 22082 EP - 22098 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-56511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Khrapov, D. A1 - Paveleva, A. A1 - Kozadayeva, M. A1 - Evsevleev, Sergei A1 - Mishurova, Tatiana A1 - Bruno, Giovanni A1 - Surmenev, R. A1 - Koptyug, A. A1 - Surmeneva, M. T1 - Trapped powder removal from sheet-based porous structures based on triply periodic minimal surfaces fabricated by electron beam powder bed fusion N2 - Electron Beam Powder Bed Fusion-manufactured (E-PBF) porous components with narrow pores or channels and rough walls or struts can be filled with trapped powder after the manufacturing process. Adequate powder removal procedures are required, especially for high-density porous structures. In the present research, sheetbased porous structures with different thicknesses based on triply periodic minimal surfaces fabricated by EPBF were subjected to different post-processing methods, including a traditional powder recovery system for EPBF, chemical etching and ultrasound vibration-assisted powder removal. Wall thickness, internal defects, microstructure and morphology features, powder distribution inside the specimens, mechanical properties and deformation modes were investigated. A powder recovery system could not remove all residual powder from dense structures. In turn, chemical etching was effective for surface morphology changes and subsurface layers elimination but not for powder removal, as it affected the wall thickness, considerably influencing the mechanical properties of the whole structure. The ultrasound vibration method was quite effective for the removal of residual powder from sheet-based TMPS structures and without a severe degradation of mechanical properties. 10.1016/j.msea.2022.144479 Ultrasound vibration also caused grain refinement. KW - Additive manufacturing KW - Residual powder removal KW - Ti6Al4V alloy KW - Electron beam powder bed fusion KW - TPMS structures PY - 2023 U6 - https://doi.org/10.1016/j.msea.2022.144479 VL - 862 SP - 1 EP - 16 PB - Elsevier B.V. AN - OPUS4-56564 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Damage evolution detection in a pipeline segment under bending by means of acoustic emission N2 - A steel pipeline segment of 2.5 m length was subjected to quasi-static four-point bending load in three steps for studying the initial cracking and damage accumulation based on the Acoustic Emission (AE) technique and by the direct current potential drop (DCPD) technique. For the latter, a new post-test analysis method was established. AE is found more sensitive to crack initiation than DCPD. Formation of mesoscopic and macroscopic cracks as well as their closure and the resulting friction generate weighted peak frequencies below 400 kHz, whereas microscopic cracking produces AE with broad band spectra identifiable by weighted peak frequencies above 400 kHz. Critical states alike the maximum load level and the leak opening were accompanied by peak amplitudes above 85 dBAE. This rather fundamental study provides a data base for possibly developing advanced strategies of detection and alarm systems based on acoustic monitoring of pipelines, or at least, steel structures. KW - Crack KW - Accoustic emission KW - Frequency domain KW - Potential drop technique KW - Fracture PY - 2023 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-565171 SN - 0308-0161 VL - 201 IS - 104863 SP - 1 EP - 9 PB - Elsevier Science CY - Amsterdam AN - OPUS4-56517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Becker, Tina A1 - Altenburg, Simon A1 - Metz, Christian A1 - Breese, Philipp Peter A1 - Oster, Simon A1 - Maierhofer, Christiane T1 - Two approaches for multi measurand in-situ monitoring of the L-PBF process – bicolor- and RGB-optical tomography N2 - Since metal additive manufacturing (AM) becomes more and more established in industry, also the cost pressure for AM components increases. One big cost factor is the quality control of the manufactured components. Reliable in-process monitoring systems are a promising route to lower scrap rates and enhance trust in the component and process quality. The focus of this contribution is the presentation and comparison of two optical tomography based multi measurand in-situ monitoring approaches for the L-PBF process: the bicolor- and the RGB-optical tomography. The classical optical tomography (OT) is one of the most common commercial in-situ monitoring techniques in industrial L-PBF machines. In the OT spatial resolved layer-images of the L-PBF process are taken from an off-axis position in one near infrared wavelength window. In addition to the explanatory powers classical OT, both here presented approaches enable the determination of the maximum surface temperature. In contrast to thermography that may also yield maximum temperature information, the needed equipment is significantly cheaper and offers a higher spatial resolution. Both approaches are implemented at a new in-house developed L-PBF system (Sensor-based additive manufacturing machine - SAMMIE). SAMMIE is specifically designed for the development and characterization of in-situ monitoring systems and is introduced as well. T2 - ICAM2022 CY - Orlando, FL, USA DA - 31.10.2022 KW - Additive Manufacturing KW - L-PBF KW - In-process monitoring KW - Optical tomography PY - 2022 AN - OPUS4-56594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tiebe, Carlo A1 - Zunkel, Astrid A1 - Klein, Ulrich A1 - Schlischka, Jörg A1 - Klinger, Christian T1 - Materialuntersuchungen zur Schadensanalyse an einem explodierten Umlaufkühler N2 - Ein Umlaufkühler ist im Betrieb explodiert. Splitter des zerborstenen Gehäuses aus Kunststoff wurden mit dem Kühlwasser in die Umgebung geschleudert, am Betriebsort entstand Personenschaden. Bei Funktionsprüfungen am beschädigten Gerät traten unerwartet - aber reproduzierbar - Knalleffekte bei Berührung der Außenoberfläche der Kupfer-Kühlschlange auf. Ein möglicher Mechanismus konnte im Labor durch Synthese von Kupferazid auf Kupferproben und Auslösung vergleichbarer Knalleffekte nachgestellt werden. Damit ist die Plausibilität des beschriebenen Schadensereignisses mit diesem oder einem ähnlich reagierenden Stoff belegt. Ein eindeutiger Nachweis darüber, dass bei dem aufgetretenen Schadensfall dieselbe chemische Reaktion stattgefunden hat, war nicht möglich, da die Belag-Überreste aus dem explodierten Kühlgerät für eine Analyse nicht mehr in ausreichender Menge verfügbar gewesen sind. T2 - BG RCI Präventionstagung, Teil 11 - Inkompatible Systeme – Wenn Chemikalien und Werkstoffe heftig reagieren CY - Online meeting DA - 19.01.2022 KW - Explosion KW - Gutachten KW - Kupferazid KW - Materialuntersuchung KW - Schadensanalyse KW - Umlaufkühler PY - 2022 AN - OPUS4-56686 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yu, C.-H. A1 - Sprengel, Maximilian A1 - Schröder, Jakob A1 - Serrano Munoz, Itziar A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Kromm, Arne A1 - Peng, R. L. A1 - Kannengießer, Thomas A1 - Bruno, Giovanni A1 - Moverare, J. T1 - Distribution of subsurface residual stress as a function of wall thickness in stainless steel 316L LPBF structures N2 - The subsurface residual stress in laser powder bed fused 316L structures was analyzed using X-ray diffraction (XRD) and layer removal. The influence of varying structure thicknesses was investigated. In this study the importance of combining surface roughness measurements with XRD was shown. Moreover, a clear relation between the structure thickness and the subsurface residual stress profiles was observed. T2 - The 11th International Conference on Residual Stress CY - Nancy, Frankreich DA - 28.03.2022 KW - AGIL KW - Residual Stress KW - X-ray Diffraction KW - Additive Manufacturing PY - 2022 AN - OPUS4-54581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sprengel, Maximilian A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Evans, Alexander A1 - Serrano Munoz, Itziar A1 - Kromm, Arne A1 - Pirling, T. A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - Surface and bulk residual stress in laser powder bed fused 316L: Influence of inter layer time and scanning velocity N2 - The influence of the inter-layer-time and the scanning velocity on the surface and bulk residual stress in laser powder bed fused 316L specimens was investigated. This study combines X-ray and neutron diffraction results with the thermal history of the specimens acquired through in-situ process monitoring. The process parameter variations were observed to directly influence the thermal history, which gave new insights in the assessment of the residual stress results. T2 - The 11th International Conference on Residual Stress CY - Nancy, Frankreich DA - 28.03.2022 KW - AGIL KW - Residual Stress KW - X-ray and Neutron Diffraction KW - Additive Manufacturing KW - Stainless Steel PY - 2022 AN - OPUS4-54582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Breese, Philipp Peter A1 - Altenburg, Simon T1 - Porosity prediction in metal based additive manufacturing utilizing in situ thermography N2 - Quality assessment of components produced by metal based additive manufacturing (AM) technologies such as laser powder bed fusion is rising in importance due to the increased use of AM in industrial production. Here, the presence of internal porosity was identified as a limiting factor for the final component quality. The utilization of thermography as an in-situ monitoring technique allows the determination of the part’s thermal history which was found to be connected to the porosity formation [1]. Combining the local thermal information derived from thermography with the porosity information obtained by x-ray micro computed tomography, machine learning algorithms can be utilized to predict the porosity distribution in the part. In this study, a first approach for the prediction of keyhole porosity in a cylindric specimen from AISI 316L stainless steel is presented. It is based on data augmentation using the “SmoteR” algorithm [2] to cure the dataset imbalance and a 1-dimensional convolutional neural network. [1] C.S. Lough et al., Local prediction of Laser Powder Bed Fusion porosity by short-wave infrared thermal feature porosity probability maps. Journal of Materials Processing Technology, 302, p. 117473 (2022) https://dx.doi.org/10.1016/j.imatprotec.2021.117473 [2] L. Torgo et al., SMOTE for Regression. Progress in Artificial Intelligence, Chapter 33, p. 378-289 (2013) https://dx.doi.org/10.1007/978-3-642-40669-0_33 T2 - KI-Tag Arbeitskreis Chemometrik & Qualitätssicherung - Chemometrics meets Artificial Intelligence CY - Berlin, Germany DA - 01.04.2022 KW - Laser Powder Bed Fusion KW - Thermography KW - Defect Prediction KW - Convolutional Neural Networks PY - 2022 AN - OPUS4-54621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauzon, C. A1 - Mishurova, Tatiana A1 - Fischer, M. A1 - Ahlström, J. A1 - Fritsch, Tobias A1 - Bruno, Giovanni A1 - Hryha, Eduard T1 - Impact of contour scanning and helium-rich process gas on performances of Alloy 718 lattices produced by laser powder bed fusion N2 - Contour scanning and process gas type are process parameters typically considered achieving second order effects compared to first order factors such as laser power and scanning speed. The present work highlights that contour scanning is crucial to ensure geometrical accuracy and thereby the high performance under uniaxial compression of complex Alloy 718 lattice structures. Studies of X-ray computed tomography visualizations of as-built and compression-strained structures reveal the continuous and smooth bending and compression of the walls, and the earlier onset of internal contact appearance in the denser lattices printed with contour. In contrast, the effect of addition of He to the Ar process gas appears to have limited influence on the mechanical response of the lattices and their microstructure as characterized by electron backscattered diffraction. However, the addition of He proved to significantly enhance the cooling rate and to reduce the amount of the generated spatters as evidenced by in situ monitoring of the process emissions, which is very promising for the process stability and powder reusability during laser powder bed fusion. KW - Additive manufacturing KW - Laser powder bed fusion KW - Gyroid lattice KW - Process atmosphere PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-546632 SN - 0264-1275 VL - 215 SP - 110501 PB - Elsevier Ltd. AN - OPUS4-54663 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - D'Accardi, E. A1 - Krankenhagen, Rainer A1 - Ulbricht, Alexander A1 - Pelkner, Matthias A1 - Pohl, Rainer A1 - Palumbo, D. A1 - Galietti, U. T1 - Capability to detect and localize typical defects of laser powder bed fusion (L‑PBF) process: an experimental investigation with different non‑destructive techniques N2 - Additive manufacturing (AM) technologies, generally called 3D printing, are widely used because their use provides a high added value in manufacturing complex-shaped components and objects. Defects may occur within the components at different time of manufacturing, and in this regard, non-destructive techniques (NDT) represent a key tool for the quality control of AM components in many industrial fields, such as aerospace, oil and gas, and power industries. In this work, the capability of active thermography and eddy current techniques to detect real imposed defects that are representative of the laser powder bed fusion process has been investigated. A 3D complex shape of defects was revealed by a μCT investigation used as reference results for the other NDT methods. The study was focused on two different types of defects: porosities generated in keyhole mode as well as in lack of fusion mode. Different thermographic and eddy current measurements were carried out on AM samples, providing the capability to detect volumetric irregularly shaped defects using non-destructive methods. KW - Additive Manufacturing KW - Defect detection KW - Thermography KW - Eddy-current testing KW - Micro-computed tomography PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-546680 SN - 2363-9512 VL - 7 IS - 6 SP - 1239 EP - 1256 PB - Springer AN - OPUS4-54668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fontoura Barroso, Daniel A1 - Epple, Niklas A1 - Niederleithinger, Ernst T1 - A Portable Low-Cost Ultrasound Measurement Device for Concrete Monitoring N2 - This paper describes a new ultrasonic measuring device called “W-Box”. It was developed based on the requirements of the DFG Forschergruppe (research unit) CoDA for a portable device for monitoring of concrete specimens, models and actual structures using embedded ultrasonic transducers as well as temperature and humidity sensors. The W-Box can send ultrasonic pulses with a variable frequency of 50–100 kHz to one selectable transducer and records signals from up to 75 multiplexed channels with a sample rate of 1 MHz and a resolution of 14 bits. In addition, it measures temperature and humidity with high accuracy, adjustable amplification, restarts automatically after a power failure and can be fully controlled remotely. The measured data are automatically stored locally on-site data quality checks and transferred to remote servers. The comparison of the W-Box with a laboratory setup using commercial devices proves that it is equally reliable and precise, at much lower cost. The W-Box also shows that their measurement capacities, with the used embedded ultrasonic transducers, can reach above 6 m in concrete. KW - Low-cost KW - Coda wave interferometry KW - Ultrasound KW - IoT KW - Non-destructive testing PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-546756 SN - 2411-5134 VL - 6 IS - 2 SP - 1 EP - 17 PB - MDPI CY - Basel, Switzerland AN - OPUS4-54675 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Tim A1 - Giese, Marcel A1 - Rhode, Michael A1 - Schröpfer, Dirk A1 - Michael, Thomas A1 - Fritsch, Tobias T1 - Influence of Surface Preparation on Cracking Phenomena in TIG-Welded High and Medium Entropy Alloys N2 - Multi-element systems with defined entropy (HEA—high entropy alloy or MEA—medium entropy alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcoming of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g., highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research to date. For that reason, in this work, the weldability depending on the surface preparation of a CoCrFeMnNi HEA and a CoCrNi MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected Zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. However, based on the results, the crack mechanism cannot be conclusively identified as either a liquid metal embrittlement (LME) or hot cracking-like liquid film separation. T2 - 2nd International Conference on Advanced Joining Processes CY - Sintra, Portugal DA - 21.10.2021 KW - TIG welding KW - Cracking KW - High entropy alloy KW - Medium entropy alloy KW - Surface preparation PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-541697 SN - 2504-4494 VL - 6 IS - 5 SP - 1 EP - 13 PB - MDPI CY - Basel (CH) AN - OPUS4-54169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Mohr, Gunther A1 - Straße, Anne A1 - Oster, Simon A1 - Gumenyuk, Andrey A1 - Hilgenberg, Kai A1 - Maierhofer, Christiane T1 - Infrared Thermography of the DED-LB/M and PBF LB/M processes N2 - Infrared thermography is a technique that allows to measure the temperatures of objects by analyzing the intensity of the thermal emission without the need of direct contact with very high spatial and temporal resolution. As the temperature is a fundamental factor for the additive manufacturing processes of metals, infrared thermography can provide experimental data that can be used for the validation of simulations and improving the understanding of the processes as well as for in-situ process monitoring for nondestructive evaluation (NDE) for quality control. In this talk we will provide an overview over the possibilities of state of the art thermographic in-situ monitoring systems for the DED-LB/M and PBF-LB/M processes and the challenges such as phase transitions and unknown emissivity values in respect to the determination of real temperatures. We define the requirements for different camera systems in various configurations and give examples on the selection of appropriate measurement parameters and data acquisition techniques as well as on techniques for data analysis and interpretation. Finally, we compare in-situ monitoring methods against post NDE methods by analyzing the advantages and disadvantages of both. This research was funded by BAM within the Focus Area Materials. T2 - Coupled2021 - IX International Conference on Coupled Problems in Science and Engineering CY - Online meeting DA - 13.06.2021 KW - Additive Manufacturing KW - Thermography KW - Direct Energy Deposition PY - 2021 AN - OPUS4-54399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Laquai, René T1 - Extending synchrotron X-ray refraction imaging techniques to the quantitative analysis of metallic materials N2 - In this work, two X-ray refraction based imaging methods, namely, synchrotron X-ray refraction radiography (SXRR) and synchrotron X-ray refraction computed tomography (SXRCT), are applied to analyze quantitatively cracks and porosity in metallic materials. SXRR and SXRCT make use of the refraction of X-rays at inner surfaces of the material, e.g., the surfaces of cracks and pores, for image contrast. Both methods are, therefore, sensitive to smaller defects than their absorption based counterparts X-ray radiography and computed tomography. They can detect defects of nanometric size. So far the methods have been applied to the analysis of ceramic materials and fiber reinforced plastics. The analysis of metallic materials requires higher photon energies to achieve sufficient X-ray transmission due to their higher density. This causes smaller refraction angles and, thus, lower image contrast because the refraction index depends on the photon energy. Here, for the first time, a conclusive study is presented exploring the possibility to apply SXRR and SXRCT to metallic materials. It is shown that both methods can be optimized to overcome the reduced contrast due to smaller refraction angles. Hence, the only remaining limitation is the achievable X-ray Transmission which is common to all X-ray imaging methods. Further, a model for the quantitative analysis of the inner surfaces is presented and verified. For this purpose four case studies are conducted each posing a specific challenge to the imaging task. Case study A investigates cracks in a coupon taken from an aluminum weld seam. This case study primarily serves to verify the model for quantitative analysis and prove the sensitivity to sub-resolution features. In case study B, the damage evolution in an aluminum-based particle reinforced metal-matrix composite is analyzed. Here, the accuracy and repeatability of subsequent SXRR measurements is investigated showing that measurement errors of less than 3% can be achieved. Further, case study B marks the fist application of SXRR in combination with in-situ tensile loading. Case study C is out of the highly topical field of additive manufacturing. Here, porosity in additively manufactured Ti-Al6-V4 is analyzed with a special interest in the pore morphology. A classification scheme based on SXRR measurements is devised which allows to distinguish binding defects from keyhole pores even if the defects cannot be spatially resolved. In case study D, SXRCT is applied to the analysis of hydrogen assisted cracking in steel. Due to the high X-ray attenuation of steel a comparatively high photonenergy of 50 keV is required here. This causes increased noise and lower contrast in the data compared to the other case studies. However, despite the lower data quality a quantitative analysis of the occurance of cracks in dependence of hydrogen content and applied mechanical load is possible. N2 - In der vorliegenden Arbeit werden die zwei, auf Refraktion basierende, Röntgenbildgebungsverfahren Synchrotron Röntgen-Refraktions Radiographie (engl.: SXRR) und Synchrotron Röntgen-Refraktions Computertomographie (engl.: SXRCT) für die quantitative Analyse von Rissen und Porosität in metallischenWerkstoffen angewandt. SXRR und SXRCT nutzen die Refraktion von Röntgenstrahlen an inneren Oberflächen des Materials, z.B. die Oberflächen von Rissen und Poren, zur Bildgebung. Beide Methoden sind daher empfindlich gegenüber kleineren Defekten als ihre auf Röntgenabsorption basierenden Gegenstücke, Röntgenradiographie und Röntgen-Computertomographie. Sie sind in der Lage Defekte von nanometrischer Größe zu detektieren. Bislang wurden die Methoden für die Analyse von keramischen Werkstoffen und faserverstärkten Kunststoffen eingesetzt. Die Analyse von metallischenWerkstoffen benötigt höhere Photonenenergien benötigt werden um eine ausreichende Transmission zu erreichen. Dies hat kleinere Refraktionswinkel, und damit geringeren Bildkontrast, zur Folge, da der Brechungsindex von der Photonenenergie abhängt. Hier wird erstmals eine umfassende Studie vorgelegt, welche die Möglichkeiten zur Untersuchung metallischer Werkstoffe mittels SXRR und SXRCT untersucht. Es wird gezeigt, dass der geringere Kontrast, verursacht durch die kleineren Refraktionswinkel, überwunden werden kann. Somit ist die einzig verbleibende Beschränkung die erreichbare Transmission, die alle Röntgenbildgebungsverfahren gemeinsam haben. Darüber hinaus wird ein Modell für die quantitative Auswertung der inneren Oberflächen präsentiert und verifiziert. Zu diesem Zweck werden vier Fallstudien durchgeführt, wobei jede eine spezifische Herausforderung darstellt. In Fallstudie A werden Risse in einer Probe aus einer Aluminiumschweißnaht untersucht. Diese Fallstudie dient hauptsächlich dazu das Modell für die quantitative Analyse zu verifizieren und die Empfindlichkeit gegenüber Strukturen unterhalb des Auflösungsvermögens zu beweisen. In Fallstudie B wird die Entwicklung der Schädigung in einem aluminiumbasierten partikelverstärktem Metall-Matrix Komposit untersucht. Dabei wird die Genauigkeit und Wiederholbarkeit der SXRR Messungen analysiert und es wird gezeigt das Messfehler kleiner 3% erreicht werden können. Darüber hinaus wird in Fallstudie B erstmals SXRR in Kombination mit in-situ Zugbelastung eingesetzt. Fallstudie C ist aus dem hochaktuellen Bereich der additive Fertigung. Hier wird Porosität in additiv gefertigtem Ti-Al6-V4 analysiert mit besonderem Augenmerk auf der Morphologie der Poren. Es wurde ein Verfahren zur Klassifizierung, basierend auf SXRR Messungen, erfunden, welches Bindefehler und Poren voneinander unterscheiden kann auch wenn die Defekte nicht räumlich aufgelöst werden können. In Fallstudie D wird SXRCT zur Analyse von wasserstoffunterstützter Rissbildung in Stahl angewandt. Wegen der hohen Röntgenschwächung des Stahls muss hier mit 50 keV eine vergleichsweise hohe Photonenenergie genutzt werden. Dadurch zeigen die Daten ein erhöhtes Rauschen und geringeren Kontrast verglichen mit den anderen Fallstudien. Allerdings ist es, trotz der geringeren Datenqualität, möglich das Auftreten von Rissen in Abhängigkeit der Wasserstoffkonzentration und mechanischen Belastung zu untersuchen. KW - Synchrotron X-ray refraction computed tomography KW - Lean duplex steel X2CrMnNiN21-5-1 KW - hydrogen embrittlement KW - Metal-matrix composite KW - Al6061 KW - Ti-Al6-V4 KW - In-situ tensile test PY - 2022 SP - 1 EP - 71 AN - OPUS4-54385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -