TY - CONF A1 - Erning, Johann Wilhelm T1 - “Grabenkorrosion": How scientific debate leads to an solution. and modern failures due to neglection of well described facts N2 - In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german. Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown. T2 - MTech 2023 CY - Cavtat, Croatia DA - 02.10.2023 KW - Corrosion KW - Grabenkorrosion PY - 2023 SN - 2806-8769 SP - 1 EP - 6 PB - Croatian Society for Heat Treatment and Sufrace Engineering CY - Zagreb AN - OPUS4-58521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotula, Stefan T1 - Zinkbeizen nach alter ISO 8407 N2 - Der Vortrag beschäftigt sich mit der Problemstellung der Entfernung von Korrosionsprodukten auf Zinkoberflächen zur Bewertung des Masseverlustes. Er diskutiert die Diskrepanzen zwischen der alten Version der ISO 8407 und der aktuellen Version. T2 - Sitzung des DIN-Gemeinschaftsarbeitskreises NA 062 01 77 01 GAK CY - Online Meeting DA - 22.09.2022 KW - Atmosphärische Korrosion KW - Deckschichtbildung KW - ISO 8407 KW - Korrosion PY - 2022 AN - OPUS4-55807 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seifert, Lando T1 - Ziele der Jungen GfKORR N2 - Die Junge GfKORR soll ein attraktives Angebot für junge Leute sein, sich fachübergreifend zu vernetzen und einen Einstieg in Querschnittsthemen bieten. Sowohl der Korrosionsschutz zum Zwecke der Nachhaltigkeit und Sicherheit von Bauwerken als auch der Korrosionsschutz bei Energie- und Mobilitätssystemen soll in zukünftigen Veranstaltungen übergreifend betrachtet werden. Dabei wollen wir den fachlichen und informativen Input aus den Arbeitskreisen der GfKORR bei unseren Seminaren suchen. In diesem 1. Netzwerk- und Arbeitstreffen wurde die Fahrtrichtung der Jungen GfKORR genauer abgesteckt und es hat sich eine Leitungsebene gefunden. Weiter wollen wir ab 2024 interessante Präsenzveranstaltungen mit Exkursionen anbieten. T2 - 1. Netzwerk- und Arbeitstreffen Junge GfKORR CY - Berlin, Germany DA - 12.03.2024 KW - Junge GfKORR KW - Netzwerkbildung KW - Corrosion KW - Korrosion PY - 2024 AN - OPUS4-60990 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Wie gehe ich bei einer Schadensuntersuchung vor? N2 - Die Vorgehensweise bei einer Schadensanalyse wird beschrieben. Hinweise zu Methodik, Fehlervermeidung und Verhalten werden gegeben. T2 - Der sichere Einsatz von Werkstoffen aus Kupfer und Kupferlegierungen in der Trinkwasserinstallation CY - Online meeting DA - 12.20.2021 KW - Schadensanalyse KW - Korrosion PY - 2021 AN - OPUS4-53518 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Wie gehe ich bei einer Schadensuntersuchung vor? N2 - Die Vorgehensweise bei einer Schadensanalyse wird beschrieben. Hinweise zu Methodik, Fehlervermeidung und Verhalten werden gegeben. T2 - Der sichere Einsatz von Werkstoffen aus Kupfer und Kupferlegierungen in der Trinkwasserinstallation CY - Online meeting DA - 21.10.2020 KW - Schadnesanalyse KW - Vorgehensweise KW - Korrosion PY - 2020 AN - OPUS4-51453 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Werkstoffe im Kontakt mit Trinkwasser: Von den UBA-Bewertungsgrundlagen nach Europa N2 - Die Grundlagen der hygienischen Bewertung von Werkstoffen im Kontakt mit Trinkwasser werden erläutert. Die regulatorischen Hintergründe und die Überführung der Regeln in den europäischen rahmen werden diskutiert und an Beispielen erläutert T2 - Abschlusskonferenz ZEP-Fittings CY - Lüdenscheid, Germany DA - 05.02.2026 KW - Korrosion KW - Trinkwasserhygiene KW - Europa KW - Werkstoffe PY - 2026 AN - OPUS4-65536 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Werkstoffe im Kontakt mit Trinkwasser: Der Weg nach Europa N2 - Die Veränderungen bei der Regulierung der Werkstoffe im Kontakt mit Trinkwasser durch die neue EU-Trinkwasserrichtlinie werden erläutert. Folgen für die etablierten Werkstoffe und Verfahren werden aufgezeigt T2 - DVGW- Bezirksgruppenveranstaltung Berlin/Potsdam CY - Online meeting DA - 15.04.2025 KW - Korrosion KW - Metallmigration KW - Trinkwasser PY - 2025 AN - OPUS4-62985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Wechselwirkungen in Geothermieanlagen - nicht nur ein Beständigkeitsaspekt N2 - Um Konstrukteuren und Nutzern geothermischer Anlagen grundlegende Informationen über die Korrosionsbeständigkeit zur Verfügung zu stellen, wurden verschiedene metallische Werkstoffe, darunter nichtrostende Duplex- und austenitische Stähle sowie eine Nickellegierung, in künstlichen Geothermalwässern bewertet, die die Bedingungen an verschiedenen Standorten mit geothermischem Potenzial simulieren. Mit Hilfe von elektrochemischen und Langzeittests wurde die Eignung verschiedener metallener Werkstoffe mittels kritischer Potentiale und Korrosionsraten untersucht. In hochsalinaren Umgebungen erwies sich Spaltkorrosion als der entscheidende Mechanismus. Die Nickelbasislegierung zeigt eine ausgezeichnete Beständigkeit gegenüber Lochkorrosion. Abgesehen von ihren hohen Kosten eignet sie sich sehr gut für den Bau von Geothermieanlagen mit stark salzhaltigen Fluiden. Rostfreie Stähle und Duplexstähle weisen eine begrenzte Korrosionsbeständigkeit gegen Loch- und Spaltkorrosion auf. Daher sind sie für stark salzhaltige Fluide nicht geeignet. Der Superaustenit zeigt ein temperaturabhängiges Verhalten. In nichtsalinaren Umgebungen könnten niedrig legierte Stähle (neben den höher legierten Werkstoffen) als Konstruktionsmaterial für Geothermieanlagen eingesetzt werden, sofern eine ausreichende Wandstärke des Materials berücksichtigt wird. Neben Korrosionsaspekten erwies sich auch die Ausfällung von Fluidbestandteilen als interessantes Thema. Beim Betrieb der Forschungsanlage in Groß Schönebeck wurden Kupfer- und Bleieffekte im Bohrloch festgestellt. Die auftretenden Mechanismen und Maßnahmen zur Verhinderung von Ausfällungen und Abscheidungen wurden ebenso untersucht, wie deren mögliche Einflüsse auf die Korrosionsbeständigkeit metallener Werkstoffe für Anlagenkomponenten. Der Vortrag beschreibt die Wechselwirkungen zwischen Geothermalwässern und Ausrüstungs-komponenten. T2 - Geothermiekongress 2024 CY - Potsdam, Germany DA - 22.10.2024 KW - Örtliche Korrosion KW - Edelstahl KW - Geothermie KW - Ni-Legierung KW - Abscheidung PY - 2024 AN - OPUS4-61441 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des WIPANOVerbundforschungsvorhabens GELELEK: Forschungsziele und Ergebnisse N2 - Der Vortrag stellt das WIPANO-Forschungsvorhaben GELELEK vor und fasst die wichtigsten erzielten Ergebnisse zusammen. T2 - Sitzung des GfKORR Arbeitskreises „Korrosion und Korrosionsschutz von Eisen und Stahl“ CY - Online meeting DA - 08.12.2022 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Normung KW - Ringversuch KW - WIPANO KW - Zink KW - Korrosion PY - 2022 AN - OPUS4-56502 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des WIPANOVerbundforschungsvorhabens GELELEK: Forschungsziele und Ergebnisse N2 - Der Vortrag stellt das WIPANOForschungsvorhaben GELELEK vor und fasst die wichtigsten erzielten Ergebnisse zusammen. T2 - 13. Sitzung des GfKORR Arbeitskreises „Korrosionsuntersuchung und -überwachung“ CY - Online meeting DA - 08.12.2021 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Normung KW - Ringversuch KW - Zink KW - WIPANO PY - 2021 AN - OPUS4-53946 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des WIPANO-Vorhabens GELELEK N2 - Der Vortrag stellt das WIPANO-Forschungsvorhaben GELELEK vor und fasst die wichtigsten erzielten Ergebnisse zusammen. T2 - Sitzung des Forschungsbeirats des Gemeinschaftsausschuss Verzinken e.V. CY - Online meeting DA - 07.10.2021 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Normung KW - Ringversuch KW - Zink PY - 2021 AN - OPUS4-53479 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lehmann, Jens T1 - VORSTELLUNG DES NEUEN GFKORR ARBEITSKREISES „ATMOSPHÄRISCHE KORROSION“ N2 - In diesem Vortrag wird ein Überblick über die Themen und Schwerpunkte des Arbeitskreises Atmosphärische Korrosion gegeben. Dabei werden einige Beispiele für relevante Fragestellungen aufgegriffen. T2 - Sitzung des GfKORR AK Eisen und Stahl CY - Online meeting DA - 08.12.2022 KW - Korrosion KW - Atmosphäre KW - Luftqualität KW - Auslagerungsversuche PY - 2022 AN - OPUS4-56546 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des Konzeptes und der Ziele des Arbeitskreises „Atmosphärische Korrosion“ N2 - Der Vortrag wurde im Rahmen der konstituierenden Sitzung des Arbeitskreises "Atmosphärische Korrosion" der GfKORR - Gesellschaft für Korrosionsschutz e.V. gehalten. Er stellt die zur Diskussion stehenden Fragestellungen und Herausforderungen im Bereich der atmosphärischen Korrosion zusammen, denen sich der neue Arbeitskreis widmen wird. T2 - Konstituierende Sitzung des GfKORR-Arbeitskreises „Atmosphärische Korrosion“ CY - Frankfurt a. M., Germany DA - 19.09.2022 KW - Atmosphärische Korrosion KW - Korrosion KW - Korrosionsschutz PY - 2022 AN - OPUS4-55772 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Vorstellung des Forschungsvorhabens GELELEK N2 - Der Vortrag stellt das Forschungsvorhaben GELELEK im Rahmen der Ad hoc Gruppe "GELELEK" des DIN-Normenausschusses Materialprüfung (NMP) vor. T2 - Sitzung der Ad hoc Gruppe "GELELEK" im DIN-Normenausschuss Materialprüfung (NMP) CY - Online Meeting DA - 21.04.2021 KW - Deckschichtbildung KW - Gelartige Elektrolyte KW - Korrosionsuntersuchungen KW - Zink PY - 2021 AN - OPUS4-52541 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Haacke, Nasrin T1 - Vorstellung des Forschungsprojektes RUNOFF: "Neubewertung der Dauerhaftigkeit von Dach- und Fassadenmaterialien und des Eintrags von Schwermetallionen in die Umwelt hervorgerufen durch Runoff„ N2 - Der Vortrag stellt das Forschungsprojekt RUNOFF vor und geht auf das geplante Arbeitsprogramm ein. Darüber hinaus wird die Problemstellung erläutert. T2 - Klempnerfachtagung des Zentralverbands Sanitär-Heizung-Klima CY - Karlstadt a. M., Germany DA - 11.10.2022 KW - Korrosion KW - Kupfer KW - Runoff KW - Zink KW - Atmosphärische Korrosion PY - 2022 AN - OPUS4-56045 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Wolf, J. L. A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Pöllmann, H. A1 - Lempp, C. A1 - Menezes, F. F. A1 - Hagemann, B. T1 - Towards defining reasonable minimum composition thresholds – Impacts of variable CO2 stream compositions on transport, injection and storage N2 - To set up recommendations on how to define “reasonable minimum composition thresholds” for CO2 streams to access CO2 pipeline networks, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the CCS chain. All investigations were based on a generic “CCS cluster scenario” in which CO2 streams captured from a spatial cluster of eleven emitters (seven fossil-fired power plants, two cement plants, one refinery and one steel mill) are collected in a regional pipeline network. The resulting CO2 stream (19.78 Mio t impure CO2 per year) is transported in a trunk line (onshore and offshore) and injected into five generic replicate storage structures (Buntsandstein saline aquifers) offshore. Experimental investigations and modeling of selected impacts revealed beneficial as well as adverse impacts of different impurities and their combinations. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the considered variable compositions and mass flow rates were observed. We recommend to define minimum composition thresholds for each specific CCS project through limiting i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of concentrations of critical impurities, and defining impurity combinations to be avoided. KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-543004 DO - https://doi.org/10.1016/j.ijggc.2022.103589 SN - 1750-5836 VL - 114 SP - 1 EP - 14 PB - Elsevier CY - New York, NY AN - OPUS4-54300 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh Hoa A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Lennard Wolf, J. A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Pöllmann, H. A1 - Lempp, C. A1 - Menezes, F. A1 - Hagemann, B. T1 - Towards Defining Reasonable Minimum Composition Thresholds – Impacts of Variable CO2 Stream Compositions on Transport, Injection and Storage N2 - The collaborative project “Impacts of impurities in CO2 streams captured from different emitters in a regional cluster on transport, injection and storage (CLUSTER)” aimed to set up recommendations on how to define “reasonable minimum composition thresholds” that CO2 streams should meet when accessing CO2 transport pipeline networks. Within CLUSTER, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the whole CCS chain. Investigations included, amongst others, impacts on: • corrosion of pipeline steel, • pipeline network design and related transport costs, • alteration of well bore cements, • pressure development and rock integrity, • geochemical reactions, and • petrophysical and geomechanical rock properties. All investigations are based on a generic CCS chain scenario. In this scenario, CO2 streams are captured from a spatial cluster of eleven emitters and collected in a regional pipeline network. Emitters comprise seven fossil fuel-fired power plants equipped with different capture technologies, two cement plants, one refinery and one integrated iron and steel plant. In total, 19.78 Mio t CO2 (including impurities) are captured in the emitter cluster annually. The combined CO2 stream is transported in a trunk line with a length of 400 km (100 km of these offshore) and is injected into five generic storage structures. The storage reservoirs are saline aquifers of the Buntsandstein. The investigations revealed beneficial and deteriorating impacts of different impurities and combinations thereof. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the modelled variable compositions and mass flow rates were observed. Based on the results, the CLUSTER project team recommends not to define “minimum composition thresholds” for CO2 streams as strict threshold values for each individual impurity in the stream. Instead, CO2 stream compositions and variabilities for specific CCS projects should be constrained with regard to a set of parameters including i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of CO2 stream composition, and iv) impurity combinations to be avoided. T2 - The 15th Greenhouse Gas Control Technologies Conference CY - Online meeting DA - 15.03.2021 KW - Corrosion KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2021 DO - https://doi.org/10.2139/ssrn.3816427 SP - 1 EP - 18 PB - Elservier AN - OPUS4-52940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, H. A1 - Fischer, S. A1 - Le, Quynh A1 - Bettge, Dirk A1 - Bäßler, Ralph A1 - Maßmann, J. A1 - Ostertag-Henning, C. A1 - Wolf, J. Lennard A1 - Pumpa, M. A1 - Lubenau, U. A1 - Knauer, S. A1 - Jaeger, P. A1 - Neumann, A. A1 - Svensson, K. A1 - Lempp, C. A1 - Menezes, F. A1 - Hagemann, B. T1 - Towards defining reasonable minimum composition thresholds – impacts of variable CO2 stream compositions on transport, injection and storage N2 - The collaborative project “Impacts of impurities in CO2 streams captured from different emitters in a regional cluster on transport, injection and storage (CLUSTER)” aimed to set up recommendations on how to define “reasonable minimum composition thresholds” that CO2 streams should meet when accessing CO2 transport pipeline networks. Within CLUSTER, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the whole CCS chain. Investigations included, amongst others, impacts on: Corrosion of pipeline steel, pipeline network design and related transport costs, alteration of well bore cements, pressure development and rock integrity, geochemical reactions, and petrophysical and geomechanical rock properties. All investigations are based on a generic CCS chain scenario. In this scenario, CO2 streams are captured from a spatial cluster of eleven emitters and collected in a regional pipeline network. Emitters comprise seven fossil fuel-fired power plants equipped with different capture technologies, two cement plants, one refinery and one integrated iron and steel plant. In total, 19.78 Mio t CO2 (including impurities) are captured in the emitter cluster annually. The combined CO2 stream is transported in a trunk line with a length of 400 km (100 km of these offshore) and is injected into five generic storage structures. The storage reservoirs are saline aquifers of the Buntsandstein. The investigations revealed beneficial and deteriorating impacts of different impurities and combinations thereof. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the modelled variable compositions and mass flow rates were observed. Based on the results, the CLUSTER project team recommends not to define “minimum composition thresholds” for CO2 streams as strict threshold values for each individual impurity in the stream. Instead, CO2 stream compositions and variabilities for specific CCS projects should be constrained with regard to a set of parameters including i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of CO2 stream composition, and iv) impurity combinations to be avoided. T2 - 15th International Conference on Greenhouse Gas Control Technologies, GHGT-15 CY - Online meeting DA - 15.03.2021 KW - Corrosion KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2021 DO - https://doi.org/10.2139/ssrn.3816427 SP - 1 EP - 18 AN - OPUS4-52418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, R. T1 - Towards defining reasonable minimum composition thresholds – impacts of variable CO2 stream compositions on transport, injection and storage N2 - The collaborative project “Impacts of impurities in CO2 streams captured from different emitters in a regional cluster on transport, injection and storage (CLUSTER)” aimed to set up recommendations on how to define “reasonable minimum composition thresholds” that CO2 streams should meet when accessing CO2 transport pipeline networks. Within CLUSTER, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the whole CCS chain. Investigations included, amongst others, impacts on: Corrosion of pipeline steel, pipeline network design and related transport costs, alteration of well bore cements, pressure evelopment and rock integrity, geochemical reactions, and petrophysical and geomechanical rock properties. All investigations are based on a generic CCS chain scenario. In this scenario, CO2 streams are captured from a spatial cluster of eleven emitters and collected in a regional pipeline network. Emitters comprise seven fossil fuel-fired power plants equipped with different capture technologies, two cement plants, one refinery and one integrated iron and steel plant. In total, 19.78 Mio t CO2 (including impurities) are captured in the emitter cluster annually. The combined CO2 stream is transported in a trunk line with a length of 400 km (100 km of these offshore) and is injected into five generic storage structures. The storage reservoirs are saline aquifers of the Buntsandstein. The investigations revealed beneficial and deteriorating impacts of different impurities and combinations thereof. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the modelled variable compositions and mass flow rates were observed. Based on the results, the CLUSTER project team recommends not to define “minimum composition thresholds” for CO2 streams as strict threshold values for eachindividual impurity in the stream. Instead, CO2 stream compositions and variabilities for specific CCS projects should be constrained with regard to a set of parameters including i) the overall CO2 content, ii) maximum contents of relevant impurities or elements, iii) acceptable variability of CO2 stream composition, and iv)impurity combinations to be avoided. T2 - 15th International Conference on Greenhouse Gas Control Technologies, GHGT-15 CY - Online meeting DA - 15.03.2021 KW - Corrosion KW - Impurities KW - CO2 quality KW - Pipeline network KW - Whole-chain CCS scenario KW - Recommendations PY - 2021 AN - OPUS4-52419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf A1 - Lehmann Schlag, Jens T1 - Systematik und Gefügearten nichtrostender Stähle N2 - Der Vortrag erläutert die Bezeichnungssystematik nichtrostender Stahlsorten und stellt verschiedene Gefügearten und deren spezifische mechanisch-technologischen Eigenschaften gegenüber. T2 - Inhouse Seminar "Korrosionsverhalten nichtrostender Stähle" CY - Ravensburg, Germany DA - 15.10.2025 KW - Korrosion KW - Nichtrostende Stähle KW - Gefügearten KW - Stahlsorten PY - 2025 AN - OPUS4-64444 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erning, Johann Wilhelm A1 - Kamaraj, A. T1 - Susceptibility of 304 Stainless Steel to Crevice Corrosion in Electrochemically Active Fluids N2 - The susceptibility of Type 304 stainless steel (SS) to crevice corrosion upon contacting with electrochemically active fluids was investigated using exposure tests and stepwise potentiostatic polarization. Crevice materials made of 304 SS and polyether ether ketone (PEEK) were focused on in this study. The combined influence of oxidant and chloride concentration on crevice corrosion was examined in detail in the two types of crevice combinations (304 SS-to-PEEK and 304 SS-to-304 SS). The 304 SS specimens were strongly susceptible to crevice corrosion when coupled with 304 SS. Even at a low concentration of 5 mg/L free chlorine and 150 mg/L chloride, which is below nominal dilutions in beverage industries, the examined specimens underwent crevice corrosion in both crevices. The effect of water composition on crevice corrosion was also studied, indicating high susceptibility of 304 SS to crevice corrosion in low pH (pH ≤ 5) solutions. The corroded surface morphology was analyzed using scanning electron microscope, energy dispersive x-ray, and confocal. KW - Crevice corrosion KW - Disinfectants KW - Stainless steel PY - 2020 DO - https://doi.org/10.5006/3324 SN - 0010-9312 VL - 76 IS - 4 SP - 424 EP - 435 PB - Nace International CY - Houston AN - OPUS4-50652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph T1 - Study of Polyaniline/Silicon Dioxide based Coating on Carbon Steel in Artificial Geothermal Brine N2 - By using the available resources in Indonesia, such as silicon dioxide and marine coating base, the PANI/SiO2 modified alkyd coating was able to protect carbon steel in a deaerated artificial geothermal water. The screening of coatings shows that the modification by adding individual pigment was not sufficient to protect carbon steel even during a short-term exposure, indicated by the discoloration after only seven days of exposure. Electrochemical tests indicated that there was no significant change in the Ecorr between the coated and uncoated carbon steel at room temperature. At 150 °C, the coated carbon steel has a lower potential than that of carbon steel, indicating that the coating is protecting carbon steel cathodically or slowing down the corrosion reaction. Finally, a long-term exposure test confirmed that the PANI/SiO2 modified coating successfully protects the carbon steel in the Sibayak artificial geothermal water up to 150 °C for 6 months. T2 - World Geothermal Congress CY - Online meeting DA - 15.06.2021 KW - Coatings KW - Corrosion KW - Polyaniline KW - Sibayak KW - SiO2 KW - Geothermal PY - 2021 AN - OPUS4-52831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Bäßler, Ralph T1 - Study of Polyaniline/Silicon Dioxide based Coating on Carbon Steel in Artificial Geothermal Brine N2 - Geothermal brines are corrosive in nature because of their salt contents and high temperatures. Therefore, they pose a major challenge to geothermal power-plants, which are mostly built of low alloyed steels, e.g., carbon steel. Carbon steel is susceptible to uniform and localized corrosion when exposed to geothermal brines having acidic-saline properties. To overcome this limitation, geothermal power plants should be built by either high alloyed materials or by integrating protection systems on carbon steel, such as coatings and inhibitors. We studied a coating system containing polyaniline/silicon dioxide basing on locally available resources that provides protection against corrosion of carbon steel and enhance the thermal resistance in geothermal environments. Here, exposure and electrochemical tests of coated carbon steels were performed in an artificial geothermal brine. The solution had a pH of 4, with the composition of 1,500 mg/L of chlorides, which is based on the chemical analysis of geothermal brine found in Sibayak, Indonesia. All exposure tests were conducted using autoclaves at 150 °C with a total pressure of 1 MPa, which was performed for up to six months to evaluate the durability of the coating system. Post-experimental analyses were performed by assessing the surface of specimens using optical and electron microscopes. On the other hand, electrochemical tests were performed for seven days at 25 °C and 150 °C to investigate the kinetics of electrochemical reactions by measuring open circuit potential and electrochemical impedance spectra. Experimental results showed the corrosion resistance of PANI/SiO2 composite coatings, where polyaniline and SiO2 play their roles as stabilizers. T2 - World Geothermal Congress CY - Online meeting DA - 30.03.2021 KW - Coatings KW - Corrosion KW - Polyaniline KW - Sibayak KW - SiO2 PY - 2021 SP - 1 EP - 7 AN - OPUS4-52830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Le, Quynh Hoa A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Bäßler, Ralph T1 - Study of Al2O3 Sol-Gel Coatings on X20Cr13 in Artificial North German Basin Geothermal Water at 150 °C N2 - Al2O3 has been widely used as a coating in industrial applications due to its excellent chemical and thermal resistance. Considering high temperatures and aggressive mediums exist in geothermal systems, Al2O3 can be a potential coating candidate to protect steels in geothermal applications. In this study, γ-Al2O3 was used as a coating on martensitic steels by applying AlOOH sol followed by a heat treatment at 600 °C. To evaluate the coating application process, one-, two-, and three-layer coatings were tested in the artificial North German Basin (NGB), containing 166 g/L Cl−, at 150 °C and 1 MPa for 168 h. To reveal the stability of the Al2O3 coating in NGB solution, three-layer coatings were used in exposure tests for 24, 168, 672, and 1296 h, followed by surface and cross-section characterization. SEM images show that the Al2O3 coating was stable up to 1296 h of exposure, where the outer layer mostly transformed into boehmite AlOOH with needle-like crystals dominating the surface. Closer analysis of cross-sections showed that the interface between each layer was affected in long-term exposure tests, which caused local delamination after 168 h of exposure. In separate experiments, electrochemical impedance spectroscopy (EIS) was performed at 150 °C to evaluate the changes of coatings within the first 24 h. Results showed that the most significant decrease in the impedance is within 6 h, which can be associated with the electrolyte penetration through the coating, followed by the formation of AlOOH. Here, results of both short-term EIS measurements (up to 24 h) and long-term exposure tests (up to 1296 h) are discussed. KW - Al2O3 KW - Geothermal KW - Martensitic steels KW - Behmite KW - Corrosion PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525551 DO - https://doi.org/10.3390/coatings11050526 SN - 2079-6412 VL - 11 IS - 5 SP - 526 PB - MDPI CY - Basel AN - OPUS4-52555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf T1 - Statusbericht zum FGS Projekt Gefügeveränderung bei trockener Grobbearbeitung N2 - Der Vortrag gibt eine Übersicht zum Stand des Projekts zum Thema Gefügeveränderung bei trockener Grobbearbeitung. Es wurden vier verschiedene trockene Oberflächenbearbeitungsverfahren an 2 Werkstoffen eingesetzt um Testoberflächen zu schaffen. Die so gefertigten Oberflächen wurden lichtmikroskopisch untersucht und die jeweiligen Rauhigkeitskennwerte bestimmt. Weiterhin wurden metallografische Querschliffe angefertigt um die verfahrens- bzw. materialabhängigen Einflüsse auf mögliche Gefügeveränderungen zu untersuchen. Zusätzlich wurden elektrochemische Polarisationsversuche durchgeführt um die oberflächenspezifische Korrosionsbeständigkeit der nichtrostenden Stahlproben zu quantifizieren. T2 - Jahrestagung der Forschungsgemeinschaft Schleifen (FGS) 2023 CY - Würzburg DA - 21.03.2024 KW - Schleifbearbeitung KW - Korrosion KW - Nichtrostender Stahl KW - Stahl KW - Verformung PY - 2024 AN - OPUS4-59739 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino A1 - Burkert, Andreas T1 - Standortabhängige Dauerhaftigkeitsbetrachtungen von Zink unter atmosphärischer Korrosion N2 - In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergebnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen. T2 - AK-Sitzung Atmosphärische Korrosion CY - Berlin, Germany DA - 24.10.2023 KW - Korrosion KW - Deckschichtbildung KW - Zink PY - 2023 AN - OPUS4-59342 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Stainless steels: Fundamentals and causes for corrosion defects N2 - The presentation gives an overview about the fundamentals on stainless steels. The mechanism of passive layer formation is explained and strategies for securing corrosion protection are given. The influence of a grinding process on corrosion resistance is discussed. T2 - Tech-Day Mettler Toledo CY - Online meeting DA - 23.11.2022 KW - Corrosion KW - Stainless steel KW - Grinding KW - KorroPad KW - Surface PY - 2022 AN - OPUS4-56370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Sprechen wir über Korrosion - aber richtig! N2 - Die Korrosion in ihren zahlreichen Erscheinungsformen beschäftigt Fachleute und Laien. Um-so wichtiger ist es, die einzelnen Phänomene korrekt und eindeutig zu benennen. Nur so kann man eine saubere Beschreibung der Korrosionsvorgänge erreichen und damit in der wörtlichen und schriftlichen Kommunikation richtig verstanden werden. An zahlreichen Beispielen wird der richtige und normgemäße Sprachgebrauch beschrieben. T2 - Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 29.01.2020 KW - Korrosion KW - Nomenklatur PY - 2020 SN - 978-3-935406-72-7 SP - 7 EP - 11 AN - OPUS4-50327 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm T1 - Sprechen wir über Korrosion - aber richtig! N2 - Die Korrosion in ihren zahlreichen Erscheinungsformen beschäftigt Fachleute und Laien. Um-so wichtiger ist es, die einzelnen Phänomene korrekt und eindeutig zu benennen. Nur so kann man eine saubere Beschreibung der Korrosionsvorgänge erreichen und damit in der wörtlichen und schriftlichen Kommunikation richtig verstanden werden. An zahlreichen Beispielen wird der richtige und normgemäße Sprachgebrauch beschrieben. T2 - Korrosionsschutz in der maritimen Technik CY - Hamburg, Germany DA - 29.01.2020 KW - Korrosion KW - Nomenklatur PY - 2020 AN - OPUS4-50328 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Thoralf T1 - Spannungsrisskorrosion an Bauteilen aus nichtrostenden Edelstählen - Bittere Erfahrungen in der Vergangenheit und sichere Verwendung in der Gegenwart N2 - Der Vortrag beschreibt die grundlegenden Voraussetzungen für das Auftreten von Spannungsrisskorrosion an nichtrostenden Stählen und erläutert den Schadensmechanismus bis zum Versagen des Werkstoffs. Abgeleitet von den notwendigen Voraussetzungen für das Auftreten von SpRK werden werkstoff, medien und belastungsabhängige Einflussfaktoren erläutert, die die Beständigkeit der Werkstoffe gegenüber dieser Schädigungsart positiv wie auch negativ verändern. Weiterhin werden historische und aktuelle Schadensfälle präsentiert und Ursachen, Folgen und mögliche Fehlervermeidung disktutiert. Abschließend werden Prüfverfahren zum Nachweis der Empfindlichkeit von nichtrostenden Stählen gegenüber SpRK näher beschrieben. T2 - fkss Infotag 01/2024 CY - Esslingen, Germany DA - 11.01.2024 KW - Korrosion KW - Spannungsrisskorrosion KW - Nichtrostender Stahl KW - Korrosionsprüfung KW - Schwimmhallen PY - 2024 AN - OPUS4-59355 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Burkert, Andreas T1 - Sinn und Unsinn der Wirksumme bei Nichtrostenden Stählen N2 - Anhand der Wirksumme ist eine Abschätzung des legierungsabhängigen Einflusses auf den Korrosionswiderstand gegen chloridhaltige Medien möglich. Die berechneten Werte sind nur bei optimaler Wärmebehandlung und Verarbeitung zutreffend. Die Anwendung einer einfachen Formel unter Berücksichtigung von Chrom, Molybdän und Stickstoff ist in der Regel völlig ausreichend. Das daraus abgeleitete Ranking von Werkstoffen ist für diverse technische Regelwerke und zur Unterstützung der Werkstoffauswahl geeignet. Für die Warenein-/Ausgangskontrolle ist die alleinige Feststellung der Wirksumme unzureichend. Ergänzende Korrosionsuntersuchungen/-prüfungen zur Beschreibung des Korrosionswiderstandes sind dafür notwendig. Gleiches gilt für die Beurteilung von Schadensfällen. Hier sind Verarbeitung, Einsatzbedingungen und die Konstruktion von ausschlaggebender Bedeutung. T2 - fkks Infotag: Charakteristische Kennwerte zur Einschätzung des Korrosionsschutzes CY - Online meeting DA - 12.01.2023 KW - Wirksumme KW - Korrosion KW - Nichtrostende Stähle PY - 2023 AN - OPUS4-56821 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Bäßler, Ralph A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Kohl, Anka T1 - Short-term exposure tests of ɣ-Al2O3 Sol-gel coating on X20Cr13 in artificial geothermal waters with different pH N2 - The suitability of an Al2O3 coating for corrosion protection on X20Cr13 was evaluated in various artificial geothermal brines, focusing on the influence of different pH (4, 6 and 8) and their chemical compositions on the coating properties. All experiments were performed in the laboratory using autoclaves at 150 ◦C and 1 MPa in deaerated condition for 1 and 7 days. Results showed that the pH of geothermal waters is the most detrimental factor in the transformation of ɣ-Al2O3 and its protective abilities. Delaminations were found in the Coating exposed to geothermal brines with pH 4. FTIR spectra indicated a transformation of ɣ-Al2O3 to boehmite AlOOH after exposure to pH 4 and 6, and bayerite Al(OH)3 was formed after exposure to pH 8. Different Crystal structures of the hydrated Al2O3 also contribute to the stability of the coatings, observed by the SEM- EDX of the surface and cross-section of coatings. This study indicated that ɣ-Al2O3 sol-gel coating presents a promising aspect of corrosion protection in geothermal environment with a neutral pH. KW - Al2O3 KW - Corrosion KW - Coating KW - Martensitic steel PY - 2021 DO - https://doi.org/10.1016/j.geothermics.2021.102193 SN - 0375-6505 VL - 96 SP - 102193 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-52931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ebell, Gino T1 - Risiko der Wasserstoffentwicklung an martensitischen Schraubankern unter baupraktischen Bedingungen N2 - Die vorliegende Untersuchung beschäftigt sich mit der Fragestellung ob unter praxisrelevanten Bedingungen die Entstehung von Wasserstoff an vollmartensitischen Schraubankern möglich ist. Im Gegensatz zu austenitischen Werkstoffen besteht bei martensitischen Werkstoffen bei Gegenwart von Wasserstoff stets die Möglichkeit einer wasser-stoffinduzierten Versprödung des Materials. Hierfür wurde ein in der Praxis häufig anzutreffendes Szenario gewählt, das ein galvanisches Element, bestehend aus nichtrostenden Schraubankern (in diesem Fall martensitischen) und einer verzinkten Ankerplatte an einem Betonkörper, umfasst. Zum Nachweis einer Wasserstoffentwicklung wird der Elementstrom zwischen den Bauteilen sowie das Korrosionspotential erfasst. Die Ergebnisse der Versuche zeigen, dass über eine zeitlich begrenzte Dauer eine starke kathodische Polarisation der martensitischen Schraubanker durch die korrosive Auflösung des Zinks erfolgt. Als Folge kommt es zur Wasserzersetzung im Phasengrenzbereich der Schraubanker und zur Entstehung von atomarem Wasserstoff. Das berechnete Gasvolumen des entstandenen Wasserstoffs an den Stahlankern wurde bestimmt und lag im Mittel bei 11,14 ± 1,94 ml. Eine Diffusion des an der Stahloberfläche adsorbierten Wasserstoffs in den martensitischen Werkstoff ist somit theoretisch möglich und impliziert eine mögliche Gefährdung durch wasserstoffinduzierte Rissbildung und spontanem Versagen unter Belastung. T2 - Arbeitskreis Korrosionsschutz im konstruktiven Ingenieurbau CY - Online meeting DA - 24.09.2020 KW - Korrosion KW - Wasserstoff PY - 2020 AN - OPUS4-51309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Zerstörungsfreie Werkstück- und Werkstoffprüfung N2 - Das 1988 erstmalig erschienene und bewährte Fachbuch wurde auf den neuesten Stand gebracht und im Rahmen der „Kontakt & Studium“‐Serie der Technischen Akademie Esslingen als Band 243 neu aufgelegt. In 12 Kapiteln bieten die 12 erfahrenen Autoren einen Überblick über die gebräuchlichsten Formen zerstörungsfreier Prüfverfahren als Grundlage für die Dokumentation der Produktqualität während des gesamten Herstellungsprozesses und deren elementare Bedeutung für die Produkthaftung. Dieses Lehrbuch dient nicht nur Universitäts‐Studierenden, sondern bietet auch jedem interessierten Leser einen Überblick der gebräuchlichen Verfahren. KW - Werkstoffprüfung KW - ZFP PY - 2020 DO - https://doi.org/10.1002/maco.202070076 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 7 SP - 3 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50959 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Schweißen im Stahlbau, Normen für die Herstellerqualifikation nach DIN EN 1090‐1 N2 - Schlosserei‐, Metall‐ und Stahlbaubetriebe müssen seit Juli 2012 für tragende Bauteile aus Stahl und Aluminium, die als Bauprodukte in Verkehr gebracht werden sollen, einen Konformitätsnachweis nach DIN EN 1090‐1 erbringen. Mit der sechsten Auflage des Normen‐Handbuches „Schweißen im Stahlbau“ setzen das Deutsche Institut für Normung e.V. (DIN) und der Deutsche Verband für Schweißen und verwandte Verfahren e.V. (DVS) ihre bewährte Strategie fort, die dieses Thema betreffenden aktuellen Normen und Regelwerke durch J. W. Mußmann in gut aufbereiteter Form kompakt zusammenzustellen. KW - Korrosion KW - Schweißen KW - Schweißnaht PY - 2020 DO - https://doi.org/10.1002/maco.202070116 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 11 SP - 3 EP - 4 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51512 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Polymere ‐ Chemie und Strukturen; Herstellung, Charakterisierung und Werkstoffe N2 - Polymere sind aus unserem Alltag nicht mehr wegzudenken. Häufig haben wir mit Plexiglas, Dichtmassen, Klebestreifen und vielen Verpackungsmaterialien zu tun. Aber auch Spezialanwendungen (z.B. in der Pharmazie) bilden Einsatzbereiche dieser Werkstoffe. Der Vermittlung der Grundlagen polymerer Werkstoffe in den Studienfächern Chemie, Materialwissenschaften und der Ingenieur‐ und Lebenswissenschaften haben sich die Autoren verschrieben, wobei sie zur verständlichen Anschauung bewusst auf das Beispiel Styrol als „Versuchskaninchen“ zurückgreifen. Dieses Lehrbuch wird seinem Anspruch gerecht, einen leichten Einstieg in die Polymerwissenschaften zu ermöglichen. Es liefert eine Übersicht über die Polymerklassen Thermoplaste, Duroplaste und Elastomere mit ihren Eigenschaften und zeigt, welche Synthesestrategie zu dem Produkt mit den gewünschten Eigenschaften führt. Anhand von Beispielen aus dem Alltag werden gängige Vertreter verständlich vorgestellt. KW - Polymerwerkstoff PY - 2020 DO - https://doi.org/10.1002/maco.202070126 SN - 1521-4176 VL - 71 IS - 12 SP - 2 EP - 3 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Materialkunde der Nichteisenmetalle und ‐legierungen N2 - Die Werkstoffklasse der Nichteisenmetalle gewinnt wegen ihrer unzähligen Anwendungsmöglichkeiten nicht nur im Maschinen‐ und Anlagenbau eine immer größere technische und wirtschaftliche Bedeutung, sodass es unabdingbar ist, insbesondere Studierenden der Material‐ und Werkstoffwissenschaften und des Maschinenbaus, den aktuellen Wissensstand auf diesem Gebiet zu vermitteln. Mit dieser Neuerscheinung veröffentlicht der Wiley‐VCH‐Verlag ein solches Lehrbuch. Kompakt und übersichtlich machen die beiden Autoren den Leser in 10 Kapiteln auf verständliche Art mit dieser Thematik vertraut. Dabei kommt ihnen ihre durch langjährige Lehrtätigkeit erworbene didaktische Erfahrung sehr zugute. Alles in allem bietet dieses Lehrbuch durch seinen von den Natur‐, über Material‐ zu Ingenieurwissenschaften weitgespannten Bogen einen interessanten und übersichtlichen Einstieg in die Welt der am häufigsten verwendeten Nichteisenmetalle, wobei es keinen Anspruch auf Vollständigkeit erhebt. KW - Werkstoffprüfung KW - Legierung KW - Korrosion PY - 2020 DO - https://doi.org/10.1002/maco.202070086 SN - 1521-4176 VL - 71 IS - 8 SP - 4 PB - Wiley‐VCH CY - Weinheim AN - OPUS4-51073 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Kurzlehrbuch Physikalische Chemie: für natur‐ und ingenieurwissenschaftliche Studiengänge N2 - Wem das Standardwerk der Physikalischen Chemie „Der Atkins“ zunächst zu überwältigend erscheint, dem gelingt mit diesem, nunmehr in der fünften Auflage erschienenen, Kurzlehrbuch sicherlich der Einstig in die Thematik. Studierenden im Bachelor‐ und Mastergang bietet es ein sehr hilfreiches Nachschlagewerk während des Studiums und zur Prüfungsvorbereitung. Die vielfältigen Übungen und Anwendungen am Ende jedes Kapitels, besser gesagt von jedem Fokus, tragen entscheidend zum Verständnis und Überprüfen des Gelernten bei. Sogenannte „Toolkits“ wiederholen an den entsprechenden Stellen inprägnanter Form mathematische Herangehensweisen und Techniken, die das Textverständnis unterstützen. Bei der Überarbeitung der vorherigen Ausgabe flossen nicht nur Anmerkungen von Lehrenden, sondern auch wertvolle Einblicke aus der Sicht der Lernenden, ein, was sich im Aufbau des Buches widerspiegelt. Dieses didaktisch und inhaltlich sehr gut aufgebaute Lehrbuch erfüllt auf jeden Fall seine Intension und weckt die Neugierde auf das im Frühjahr 2020 erscheinende dazugehörige Arbeitsbuch. KW - Elektrochemie KW - Korrosion PY - 2020 DO - https://doi.org/10.1002/maco.202070036 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 3 SP - 3 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50490 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Rezension: Halliday Physik für natur‐ und ingenieurwissenschaftliche Studiengänge – Lehr‐ und Übungsbuch N2 - Die von Stephan W. Koch herausgegebene Übersetzung der erweiterten zehnten Auflage von ,,Fundamentals of Physics“ liefert ein Schwergewicht geballten Physikwissens und Übungsmaterial. Die Bücher bieten nicht nur Studierenden hilfreiches Lernmaterial, sondern sind auch für allgemein Physik‐Interessierte ein wertvolles Nachschlagewerk. Wer sich bereits mit dem umfassenderen „großen Bruder“ vertraut gemacht hat und diesen nutzt, findet im Lehrbuch nichts Neues. Jedoch liefert das Übungsbuch im Vergleich zum Arbeitsbuch von 2018 neue und übersichtlichere Übungsbeispiele. Die neue Auflage wurde didaktisch komplett neu strukturiert und einige Kapitel vollständig überarbeitet. Ein Novum stellt dabei die modulare Organisation dar, bei der jeder Abschnitt mit Lernzielen und Schlüsselideen beginnt. Kontrollfragen im Text tragen entscheidend zum Rekapitulieren des Gelesenen bei. Jedes Kapitel endet mit einer Zusammenfassung und Fragen zum vermittelten Stoff. Als Ergänzung dient das ausführliche Übungsbuch mit Aufgaben und Lösungen zu den jeweiligen Kapiteln des Lehrbuches. Die 37 Kapitel machen verständlich mit den einzelnen Gebieten der Physik vertraut. KW - Physik KW - Thermodynamik PY - 2020 DO - https://doi.org/10.1002/maco.202070066 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 6 SP - 3 EP - 4 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bäßler, Ralph T1 - Review: Science, Technology and Applications of Metals in Additive Manufacturing N2 - Often 3D‐printing and additive manufacturing are mentioned as the 3rd industrial revolution. In this conjunction this book provides a brief overview on additively manufactured metal pieces. This book fulfills its intension to serve as an educational guide, providing a holistic picture encompassing science, technology and applications for the real‐life use of Metal Additive Manufacturing. KW - Additive manufacturing KW - Corrosion KW - Material properties PY - 2020 DO - https://doi.org/10.1002/maco.202070114 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 11 SP - 1929 EP - 1930 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Polymer Coatings ‐ A Guide to Chemistry, Characterization, and Selected Applications N2 - This book grew out of a course on polymer coatings held by the author at the university. It shall serve as an introduction to the wide field of polymer coatings. It is not intended to cover completely all facts on polymer coatings. All chapters are well structured. Selected figures and formulas illustrate the content and contribute to a good understandability. At the end of each chapter some hints for further reading are provided. Finally, the book fulfills its intention to introduce into the topic by providing basics on science and technology of polymer coatings, suitable for chemists in industry, materials scientists, polymer chemists and physical chemists. KW - Corrosion KW - Coating KW - Polymer PY - 2020 DO - https://doi.org/10.1002/maco.202070024 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 2 SP - 321 EP - 322 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50374 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Nanopatterned and Nanoparticle‐Modified Electrodes N2 - Since nanoscience has a tremendous impact on the development of electrochemistry, Wiley‐VCH paid attention to that by publishing thisbook as volume 17 within the series “Advances in Electrochemical Science and Engineering”. This collection of “nanoaspects”on electrodes provides a helpful overview on principles and current findings to readers interested in such applications. It fulfills its intention of being “a valuable resource for researchers working in such fields as electrochemistry, materials science, spectroscopy, analytical and medicinal chemistry”. KW - Electrochemistry KW - Nanoparticle PY - 2020 DO - https://doi.org/10.1002/maco.202070014 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 1 SP - 179 EP - 180 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Materials Informatics -Metals, Tools and Applications N2 - Since data processing has now also found its way into materials science, there has been a great demand from users for a corresponding textbook. This book provides a guide to the latest advances of materials informatics and data mining for materials science. 46 authors introduce readers to methods, present tools and case studies to illustrate the power of materials informatics within this new field of application. KW - Corrosion KW - Materials behavior PY - 2020 DO - https://doi.org/10.1002/maco.202070114 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 11 SP - 1928 EP - 1929 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Materials Handbook–A Concise Desktop Reference N2 - This concise reference book,consisting of 2 volumes, provides “key scientific and technical properties and data” for “materials scientists, metallurgists, engineers,chemists, and physicists as well as academic staff, technicians, and students” dealing with such kind of materials. Within its 3rd edition the previous work was extended by a chapter on occupational health and safety issues of materials, beside of the update of whole content. Within 22 chapters materials properties and data are summarized in many tables. Some facts are illustrated by drawings and diagrams for better understandability. Each chapter ends with a part on further reading arranged accordingly. KW - Corrosion KW - Materials KW - Corrosivity KW - Resistance PY - 2020 DO - https://doi.org/10.1002/maco.202070034 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 3 SP - 509 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50489 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Magnesium and its Alloys – Technology and Applications N2 - The first edition of this book, published within the series “Materials Science – Metals and Alloys”, provides broad knowledge of this interesting and widely applied metal from manufacturing and production to finishing and application in 13 chapters, written by 29 contributors. Each chapter is separately concluded and ends with references used. This book fulfills its intention of conveying comprehensive and cutting‐edge knowledge of magnesium alloys. It is useful for practicing engineers, researchers and students searching for an instructional and reference source. KW - Magnesium KW - Magnesium Alloy PY - 2020 DO - https://doi.org/10.1002/maco.202070074 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 7 SP - 1229 EP - 1230 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Electrochemical Energy Storage ‐ Physics and Chemistry of Batteries N2 - Currently, storage of electric energy is becoming more and more interesting in terms of applicability and efficiency. One way is the electrochemical storage by already well‐developed battery‐systems. This textbook provides an introduction into physical and chemical processes necessary for battery application. This book fulfills its intension to serve graduate students of electrical engineering as an introduction into the field of batteries. Even students and interested readers of other faculties might find an introduction in physical and chemical background of batteries. KW - Batteries PY - 2020 DO - https://doi.org/10.1002/maco.202070124 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 12 SP - 2084 EP - 2085 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Corrosion‐Resistant Linings and Coatings N2 - This book introduces to aspects to be considered when dealing with coatings and linings. Philip A. Schweitzer covers and compares a variety of specific coatings and their applications. In 18 chapters he divided the content into two main parts: linings and coatings. All professionals involved in design and maintenance processes get by this book a compact survey of necessary considerations which needs to be done when applying surface protection measures. The literature references at the end of some chapters support the readers finding additional information about the special topic, mainly written by the author himself. Since this newly issued paperback edition is a 1:1 re‐print of the 2001 hardcover version, neither current publications are referenced, nor revisions were made. KW - Corrosion KW - Lining KW - Coating KW - Elastomer PY - 2020 DO - https://doi.org/10.1002/maco.202070094 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 9 SP - 1592 EP - 1593 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Corrosion of Linings and Coatings: Cathodic and Inhibitor Protection and Corrosion Monitoring N2 - This paperback issue of the 2007 hardcover version within the “Corrosion Engineering Handbook” series presents various materials and methods for controlling and protecting against corrosion instead of using expensive alloys to construct a tank or processing vessel. This book is a very comprehensive collection of the current knowledge about applied linings and coatings. So, it fulfills its intension, “that regardless of what is being built, … information for … whoever is responsible for the selection of material of construction will be found in this book to enable them to avoid unnecessary loss of material through corrosion”, to a very large extent. KW - Corrosion KW - Coating KW - Lining KW - Cathodic protection PY - 2020 DO - https://doi.org/10.1002/maco.202070104 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 10 SP - 1756 EP - 1757 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Bäßler, Ralph T1 - Review: Corrosion Atlas Case Studies - 2019 Edition N2 - This edition, published as first issue within the series “Corrosion Atlas”, provides 181 corrosion case studies, collected from 29 contributors. These Corrosion Atlas Case Studies provide a helpful tool required for engineers in their daily life to quickly determine and solve their equipment's corrosion problems by compact theoretical background and vivid examples. It fulfills the intension of the editors to be “the first centralized collection of case studies containing challenges paired directly with solutions together in one location”. KW - Corrosion KW - Failure KW - Water-bearing PY - 2020 DO - https://doi.org/10.1002/maco.202070054 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 5 SP - 859 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50757 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Seifert, Lando T1 - Review: Concrete Repair to EN 1504: Diagnosis, Design, Principles and Practice N2 - In 2019 CRC Press published the “Concrete Repair to EN 1504” as paperback. This issue does not differ in terms of content from the hardback publication of 2014. Like the previous version, the book covers both detailed background information on repair procedures of reinforced concrete structures and provides a reference work for technicians and people who are involved with the maintenance of these structures, according to EN 1504. The book presents a high number of figures and tables, i.e., approximately one illustration per page. For readers who prefer a more comfortable to handle paperback, the book is recommended; however, the hardback from 2014 is still up‐to‐date. KW - Corrosion KW - Concrete KW - Bridge PY - 2020 DO - https://doi.org/10.1002/maco.202070064 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 6 SP - 1036 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-50838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -