TY - JOUR A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Study on Duplex Stainless Steel Powder Compositions forthe Coating of Thick Plates for Laser Beam Welding N2 - Duplex stainless steels combine the positive properties of its two phases, austenite and ferrite. Due to its good corrosion resistance, high tensile strength and good ductility it has multiple applications. But laser beam welding of duplex steels changes the balanced phase distribution in favor of ferrite. This results in a higher vulnerability to corrosion and a lower ductility. In this study different powder combinations consisting of duplex and nickel for coating layers by laser metal deposition are investigated. Afterwards laser tracks are welded, and the temperature cycles measured. The ferrite content of the tracks are analyzed by feritscope, metallographic analysis and Electron Backscatter Diffraction. The goal is the development of a powder mixture allowing for a duplex microstructure in a two-step process, where firstly the edges of the weld partners are coated with the powder mixture by LMD and secondly those edges are laser beam welded. The powder mixture identified by the pretests is tested in the two-step process and analyzed by metallographic analysis, energy dispersive X-ray spectroscopy and Vickers hardness tests. The resulting weld seams show a balanced duplex microstructure with a homogenous nickel distribution and a hardness of the weld seam similar to the base material. KW - Duplex AISI 2205 KW - Stainless Steel KW - Laser Beam Welding KW - Nickel KW - Laser Metal Deposition PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-554663 SN - 1438-1656 VL - 24 IS - 6 SP - 1 EP - 11 PB - Wiley-VCH CY - Weinheim AN - OPUS4-55466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, Torsten A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up strategies for generating components of cylindrical shape with laser metal deposition N2 - Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process. T2 - Lasers in Manufacturing Conference 2015 CY - Munich, Germany DA - 22.06.2015 KW - Ti - 6Al - 4V KW - Additive Manufacturing KW - Build - up Strategy KW - Laser Metal Deposition KW - Stainless Steel PY - 2015 UR - http://www.wlt.de/lim/Proceedings/Stick/sessions.html SP - 1 EP - 6 AN - OPUS4-37829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Build-up Strategies for Laser Metal Deposition in Additive Manufacturing N2 - Laser Metal Deposition (LMD) as a technology for additive manufacturing allows the production of large components outside of closed working chambers. Industrial applications require a stable process as well as a constant deposition of the filler material in order to ensure uniform volume growth and reproducible mechanical properties. This paper deals with the influence of travel path strategies on temperature profile and material deposition. Meandering and spiral hatching strategies are used in the center as well as in the edge of a specimen. The temperature is measured with thermocouples attatched to the backside of the specimen. The tests are carried out on the materials S235JR and 316L. The results show a strong dependence of the maximum temperatures on the travel path strategy and the welding position on the component. T2 - Fraunhofer Direct Digital Manufacturing Conference (DDMC) CY - Berlin, Germany DA - 14.03.2018 KW - Additive Manufacturing KW - Temperature behavior KW - Laser Metal Deposition KW - Stainless Steel KW - 316L KW - Edge effects PY - 2018 SN - 978-3-8396-1320-7 VL - 1 SP - 1 EP - 6 PB - Fraunhofer-Gesellschaft CY - München AN - OPUS4-44719 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, Erik A1 - Altenburg, Simon A1 - Mohr, Gunther A1 - Thiede, Tobias A1 - Maierhofer, Christiane A1 - Bruno, Giovanni A1 - Rethmeier, Michael A1 - Hilgenberg, Kai A1 - Mishurova, Tatiana A1 - Straße, Anne T1 - AM activities at BAM with focus on process monitoring N2 - The presentation gives an overview of current projects in additive manufacturing at BAM. In particular, the results of the ProMoAm project were presented. T2 - VAMAS - Materials Issues in Additive Manufacturing CY - Berlin, Germany DA - 25.06.2018 KW - Additive Manufacturing KW - Laser Metal Deposition KW - Thermography KW - Data Fusion KW - In-situ monitoring PY - 2018 AN - OPUS4-45620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiel, Erik A1 - Altenburg, Simon A1 - Myrach, P. A1 - Mohr, Gunther A1 - Gumenyuk, Andrey T1 - Crack detection in metal additive manufacturing with laser thermography N2 - BAM ensures and represents high standards for safety in technology and chemistry. Additive manufacturing (AM) changes the requirements for conventional non-destructive testing (NDT) as new processes of defect creation occur. Especially in safety critical areas, such as aerospace and automotive, new manufacturing processes and materials always require reliability tests and new standards which is a big challenge for NDT. T2 - Internationales Laser- und Fügesymposium CY - Dresden, Germany DA - 27.02.2018 KW - Laser Beam Melting KW - Laser Metal Deposition KW - Thermography KW - In-situ monitoring PY - 2018 AN - OPUS4-45619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - In-situ Thermografie in der additiven Fertigung mittels Laser-Pulver-Auftragsschweißen N2 - Im Rahmen des Themenfeld Projektes „Process Monitoring of AM“ (ProMoAM) evaluiert die BAM gegenwärtig die Anwendbarkeit verschiedenster ZfP-Verfahren, darunter die Thermografie, zur Prozessüberwachung in der additiven Fertigung von Metallen in Hinblick auf die Qualitätssicherung. In diesem Beitrag werden SWIR-Thermografiemessungen während des Bauprozesses mittels Laser Pulver Auftragsschweißen (LPA) vorgestellt. Eine Herausforderung im Rahmen dieser Messungen liegt in der Positionierung der Kamera, welche entweder fixiert am Schweißarm, also mitbewegt, oder fixiert in der Baukammer, also stationär, erfolgen kann, wobei beide Varianten mit individuellen Vor- und Nachteilen verbunden sind. Eine stationäre Befestigung der Kamera ermöglicht zwar eine einfachere Zuordnung der Messdaten zu der jeweiligen Position im Bauteil, führt jedoch bei komplexeren Geometrien zwangsläufig zu Problemen durch Abschattungen und zu defokussierten Bereichen. Zur Auswertung von Thermogrammen, welche durch eine mit dem Schweißarm mitbewegte Kamera aufgenommen wurden, sind hingegen für jedes Bild akkurate Positionsdaten der Kamera nötig um die Messdaten einer Position im Bauteil zuzuordnen. Da die Positionsdaten des Schweißarmes im allgemeinen Fall durch die Anlagensoftware nicht zur Verfügung gestellt werden, muss diese Information durch zusätzliche Messungen aufgezeichnet werden. Hierzu verwenden wir einen an der Kamera befestigten Beschleunigungssensor. Dieser ermöglicht einen zeitlichen Abgleich mit dem vorprogrammierten Verfahrweg des Schweißarmes, welcher im Allgemeinen noch Unsicherheiten bezüglich genauer Geschwindigkeiten und Beschleunigungen offenlässt. Weiterhin untersuchen wir den Einfluss des empfindlichen Spektralbereiches der IR-Kamera durch den Vergleich von Messungen mit verschiedenen schmalbandigen Bandpassfiltern (25 nm FWHM) in einem Bereich von 1150 nm bis 1550 nm. T2 - Thermographie-Kolloquium 2019 CY - Halle (Saale), Germany DA - 19.09.2019 KW - Additive manufacturing KW - 3D printing KW - Thermography KW - Direct energy deposition KW - Laser Metal Deposition KW - 3D Druck KW - Laser Pulver Auftragsschweißen KW - Additive Fertigung KW - Thermografie PY - 2019 AN - OPUS4-49078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - In-situ thermographic monitoring of the laser metal deposition process N2 - In this paper shortwave infrared (SWIR) thermographic measurements of the manufacturing of thin single-line walls via laser metal deposition (LMD) are presented. As the thermographic camera is mounted fixed to the welding arm, an acceleration sensor was used to assist in reconstructing the spatial position from the predefined welding path. Hereby we could obtain data sets containing the size of the molten pool and the oxide covered areas as functions of the position in the workpiece. Furthermore, the influence of the acquisition wavelength onto the thermograms was investigated in a spectral range from 1250 nm to 1550 nm. All wavelengths turned out to be usable for the in-situ process monitoring of the LMD process. The longer wavelengths are shown to be beneficial for the lower temperature range, while shorter wavelengths show more details within the molten pool. T2 - Sim-AM 2019 - 2. International Conference on Simulation for Additive Manufacturing CY - Pavia, Italy DA - 11.09.2019 KW - Additive manufacturing KW - 3D printing KW - Thermography KW - Direct energy deposition KW - Laser Metal Deposition KW - 3D Druck KW - Laser Pulver Auftragsschweißen KW - Additive Fertigung KW - Thermografie PY - 2019 UR - http://congress.cimne.com/SIM-AM2019/frontal/Doc/proceedings.pdf SN - 978-84-949194-8-0 SP - 246 EP - 255 AN - OPUS4-49086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Altenburg, Simon A1 - Scheuschner, Nils T1 - Prozessüberwachung in der additiven Fertigung von Metallen - das Projekt ProMoAM N2 - Prozessüberwachung in der additiven Fertigung von Metallen - das Projekt ProMoAM. In diesem Vortrag wird das gesamte Projekt vorgestellt. Dabei wird auf die Thermografie im LMD und L-PBF Prozess näher eingegangen. Hierbei werden sowohl stationäre als auch mit bewegte Systeme vorgestellt. T2 - Webinar: Inline-Messtechnik und –Prozessüberwachung CY - Online meeting DA - 01.07.2020 KW - Pulverbettverfahren KW - Laser Metal Deposition KW - Thermografie KW - Optische Tomografie PY - 2020 UR - https://quality-engineering.industrie.de/webinarreihe-additive-verfahren/#Inline-Messtechnik AN - OPUS4-50962 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Altenburg, Simon A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - In-situ thermographic monitoring of the laser metal deposition process N2 - By allowing economic on demand manufacturing of highly customized and complex workpieces, metal based additive manufacturing (AM) has the prospect to revolutionize many industrial areas. Since AM is prone to the formation of defects during the building process, a fundamental requirement for AM to become applicable in most fields is the ability to guarantee the adherence to strict quality and safety standards. A possible solution for this problem lies in the deployment of various in-situ monitoring techniques. For most of these techniques, the application to AM is still very poorly understood. Therefore, the BAM in its mission to provide safety in technology has initiated the project “Process Monitoring of AM” (ProMoAM). In this project, a wide range of in-situ process monitoring techniques, including active and passive thermography, optical tomography, optical emission and absorption spectroscopy, eddy current testing, laminography, X-ray backscattering and photoacoustic methods, are applied to laser metal deposition (LMD), laser powder bed fusion and wire arc AM. Since it is still unclear which measured quantities are relevant for the detection of defects, these measurements are performed very thoroughly. In successive steps, the data acquired by all these methods is fused and compared to the results of reference methods such as computer tomography and ultrasonic immersion testing. The goal is to find reliable methods to detect the formation of defects during the building process. The detailed acquired data sets may also be used for comparison with simulations. Here, we show first results of high speed (> 300 Hz) thermographic measurements of the LMD process in the SWIR range using 316L as building material. For these experiments, the camera was mounted fixed to the welding arm of the LMD machine to keep the molten pool in focus, regardless of the shape of the specimen. As the thermograms do not contain any information about the current spatial position during the building process, we use an acceleration sensor to track the movement and synchronize the measured data with the predefined welding path. This allows us to reconstruct the geometry of the workpieces and assign the thermographic data to spatial positions. Furthermore, we investigate the influence of the acquisition wavelength on the thermographic data by comparing measurements acquired with different narrow bandpass filters (50 nm FWHM) in a spectral range from 1150 nm to 1550 nm. This research was funded by BAM within the Focus Area Materials. T2 - Sim-AM 2019 - 2. International Conference on Simulation for Additive Manufacturing CY - Pavia, Italy DA - 11.09.2019 KW - Additive manufacturing KW - 3D printing KW - Thermography KW - Direct energy deposition KW - Laser Metal Deposition KW - 3D Druck KW - Laser Pulver Auftragsschweißen KW - Additive Fertigung KW - Thermografie PY - 2019 AN - OPUS4-49070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Biegler, M. A1 - Khazan, P. A1 - Gazen, M. A1 - Rethmeier, Michael T1 - Improvement of numerical simulation model setup and calculation time in additive manufacturing-laser-metal-deposition components with an advanced modelling strategy N2 - Rapid localized heating and cooling during additive manufacturing using laser deposition method (LMD) lead to loss of dimensional accuracy as well as cracking of built parts. Finite-Element welding simulations allow prediction of geometrical deviations and accumulated residual stresses as well as their optimization before conducting experiments. Due to the great length of stacked welds, calculation times for fully transient thermomechanical simulations are currently long, the calculation stability suffers from the high number of contact bodies in the model and the modelling effort is high, as the geometries need to be sliced and positioned layer-wise. In this contribution, an integrated modelling approach is demonstrated for a thin-walled LMD component made from 30 layers of 1.4404 (316L) stainless steel: Instead of the layer-by-layer modelling strategy commonly found in the literature, the whole component mesh is kept in one piece and the fully transient, layer-by-layer material deposition is implemented via element sets. In contrast to prior simulations, nonlinear contact between the layers does not have to be considered, significantly decreasing calculation times. The calculated distortions are compared to recently published, in-situ digital image correlation (DIC) measurements as well as numerical simulations conducted with the established layer-wise modelling strategy to judge result quality. Finally, the improvement in calculation time and ease-of-use is compared between both modelling approaches and conclusions regarding future usage for industrial-scale components are drawn. T2 - 12th International Seminar ‘Numerical Analysis of Weldability' CY - Graz, Austria DA - 23.09.2018 KW - Additive Manufacturing KW - Laser Metal Deposition KW - Distortion simulation KW - Calculation time KW - Directed energy deposition KW - Efficient modelling PY - 2019 SN - 978-3-85125-615-4 SN - 978-3-85125-616-1 U6 - https://doi.org/10.3217/978-3-85125-615-4-52 SN - 2410-0544 VL - 2019 SP - 979 EP - 1003 PB - Verlag der Technischen Universität Graz CY - Graz AN - OPUS4-49274 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Uhlmann, E. A1 - Düchting, J. A1 - Petrat, T. A1 - Graf, B. A1 - Rethmeier, Michael T1 - Heat treatment of SLM-LMD hybrid components N2 - Additive manufacturing is no longer just used for the production of prototypes but already found its way into the industrial production. However, the fabrication of massive metallic parts with high geometrical complexity is still too time-consuming to be economically viable. The combination of the powder bed-based selective laser melting process (SLM), known for its geometrical freedom and accuracy, and the nozzle-based laser metal deposition process (LMD), known for its high build-up rates, has great potential to reduce the process duration. For the industrial application of the SLM-LMD hybrid process chain it is necessary to investigate the interaction of the processes and its effect on the material properties to guarantee part quality and prevent component failure. Therefore, hybrid components are manufactured and examined before and after the heat treatment regarding the microstructure and the hardness in the SLM-LMD transition zone. The experiments are conducted using the nickel-based alloy Inconel 718. T2 - LiM 2019 CY - München, Germany DA - 23.06.2019 KW - Additive Manufacturing KW - Selective Laser Melting KW - Hybrid components KW - Inconel 718 KW - Laser Metal Deposition PY - 2019 SP - 1 EP - 9 AN - OPUS4-48410 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Quality improvement of laser welds on thick duplex plates by laser cladded buttering N2 - Because of its excellent corrosion resistance, high tensile strength and high ductility, duplex stainless steel 2205 offers many areas of application. Though laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal as the base metal, which leads to a reduction of ductility and corrosion resistance of the weld joint. To overcome this problem, a solution, based on buttering the plate edges by laser metal deposition (LMD) with material containing higher Ni concentrations prior to laser welding was suggested. In this context different process parameters for LMD and different mixtures of duplex and nickel powder, were investigated. In a second step the possibility of welding those edges defect free while achieving balanced austenite-ferrite ratio was verified with metallographic analysis, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance was observed with ASTM G48 standard test method. T2 - Lasers in Manufacturing- LiM 2019 CY - Munich, Germany DA - 24.07.2019 KW - Stainless Steel KW - Laser Metal Deposition KW - Laser Beam Welding KW - Duplex PY - 2019 AN - OPUS4-49365 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of cladded buffering on thick duplex plates for laser welding N2 - Because of its excellent corrosion resistance, a high tensile strength together with a high ductility, duplex stainless steel 2205 offers many areas of application in the chemical and the offshore industry, to name just two. Though welding, especially laser beam welding accompanied by high cooling rates, duplex steels tend to perform higher ferrite contents in weld metal upon cooling down from melting temperature as the base metal. This trend leads to a reduction of the ductility as well as the corrosion resistance of the weld joint. To overcome this problem a solution, based on buffering the plate edges by laser metal deposition with material containing higher Ni concentrations prior to the laser welding was suggested. This method offers more benefits in comparison to conventional usage of higher Ni-alloyed filler wire due to the better control over Ni-distribution in the weld seam, resulting in balanced austenite- ferrite ratio everywhere in the weld metal. In this context different mixtures of duplex and nickel powder were investigated as well as different process parameters, that enable a smooth surface structure with slightly reduced ferrite contents. In a second step the possibility of welding those edges defect free with standard parameters while achieving balanced austenite- ferrite ratio was verified with metallographic analysis of the microstructure, Electron Backscatter Diffraction (EBSD) and impact testing according to Charpy. The improved corrosion resistance of the welds in comparison to unbuffered ones was observed with the ASTM G48 standard test method. T2 - IIW 2019 CY - Bratislava, Slowakia DA - 07.07.2019 KW - Stainless Steel KW - Laser Metal Deposition KW - Laser Beam Welding KW - Duplex PY - 2019 AN - OPUS4-49366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winterkorn, R. A1 - Petrat, T. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Temperature generation of different travel path strategies to build layers using laser metal deposition N2 - Laser Metal Deposition offers the chance to build near net shape parts. The temperature evolution within the process has an influence on track and layer geometries. There are special travel path strategies required to produce near net shape components and reduce shape deviation resulting of error propagation. This paper deals with the temperature progression of individual layers and the maximum heating of deeper substrate regions. Spiral and zig-zag strategies are examined. The investigations are carried out using S235JR as substrate and 316L as powder material. The influence of different strategies on temperature evolution is discussed. The results from the experiments show that various production strategies are associated with different temperature fields. Furthermore, the extent of the temperature variations of layer strategies and layer position are strongly dependent on the production direction. These results demonstrate the importance of developing suitable build-up strategies for parts of complex shape to ensure a stable process with constant temperature as well as even layers. T2 - Lasers in Manufacturing Conference 2017 CY - Munich, Germany DA - 26.06.2017 KW - 316L KW - Additive Manufacturing KW - Temperature behavior KW - Laser Metal Deposition KW - Stainless Steel KW - Edge effects PY - 2017 SP - 1 EP - 5 AN - OPUS4-42878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Maierhofer, Christiane T1 - Neue Abenteuer an der BAM: die Projekte AGIL und ProMoAM N2 - Zwei neue Projekte wurden in der BAM gestartet: AGIL und ProMoAM, die mit der Charakterisierung additiv gefertigter Wrkstoffe und mit dem Prozessmonitoring in der AF sich befassen. Die sind in diesem Vortrag dargestellt T2 - Symposium Materialcharakterisierung CY - BAM, Berlin, Germany DA - 28.11.2017 KW - Additive Fertigung KW - Prozess Monitoring KW - Alterung KW - Metallische Werkstoffen KW - Laser Metal Deposition KW - Selective Laser Melting PY - 2017 AN - OPUS4-43273 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hilgenberg, Kai A1 - Spranger, Felix A1 - Graf, B. A1 - Schuch, M. A1 - Rethmeier, Michael T1 - Build-up strategies for additive manufacturing of three-dimensional Ti-6Al-4V-parts produced by Laser Metal Deposition N2 - Laser metal deposition (LMD) has been applied as coating technology for many years. Today, the technologies capacity to produce 3D depositions leads to a new field of application as additive manufacturing method. In this paper, 3D laser metal deposition of titanium alloy Ti-6Al-4V is studied with special regard to the demands of additive manufacturing. Therefore, only the powder nozzle is used to create the shielding gas atmosphere, which ensures high geometric flexibility. Furthermore, specimen with high aspect ratio and hundreds of layers are manufactured, which represent typical features in additive manufacturing. T2 - ICALEO CY - Atlanta, USA DA - 22.10.2017 KW - Additive manufacturing KW - Ti-6Al-4V KW - Laser Metal Deposition PY - 2017 AN - OPUS4-42865 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -