TY - CONF A1 - Klobes, Peter A1 - Rübner, Katrin A1 - Prinz, Carsten A1 - Hempel, S. T1 - Investigation on the microstructure of ultra high performance concrete N2 - Ultra-high performance concrete (UHPC) is characterised by compressive strengths above 150 MPa and an outstanding durability. These properties are achieved by optimisation of the mixture composition, the mixing procedure as well as the curing conditions of the concrete. Heat curing as well as the use of vacuum mixers may contribute to the high strength. The very high brittleness of UHPC can be compensated by the addition of steel or polymer fibres. UHPC is produced using a very low water/cement ratio of 0.25 or smaller in combination with adding of polycarboxylate ether based superplasticisers. Furthermore, finest cements with contents of 500 kg/m³, defined selections of coarse and fine aggregates with a maximum grain size between 0.5 and 8 mm and fine pozzolanic (silica fume, fly ash) and inert additives (quartz filler) are used. In doing so, the aim is to obtain a very high packing density of the cement paste matrix and the aggregate/paste interface while a very homogeneous microstructure with a high calcium silicate hydrate (CSH) portion is formed. In the case of optimal mixing and curing conditions, UHPC contains almost no pores and microcracks. Therefore, studies of porosity and pore structure are very important to characterise UHPC materials in connection with the mixture optimisation. Here, the experimental results for UHPC are presented in comparison with those of high-strength concrete (100 MPa) and normal-strength concrete (35 MPa), respectively. T2 - 8th International Symposium on the characterisation of Porous Solids CY - Edinburgh, Scotland DA - 11.06.2008 PY - 2008 AN - OPUS4-16396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten T1 - Pore structure of concrete with recycling aggregates N2 - Processed building rubble containing about 90 % of crushed concrete can be used as recycling aggregates. The reuse for the production of new high-grade concrete requires a knowledge of the engineering properties as well as the pore structure of These materials. Two recycling aggregates and the concretes made with them were studied. T2 - 33th International Geological Congress (IGC) Symposium on Mineral Resources - Constructions Materials (MRC) CY - Oslo, Norway DA - 06.08.2008 PY - 2008 AN - OPUS4-16778 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel A1 - Stephan, Ina T1 - Untersuchungen biegebeanspruchter Holzstäbe aus dem Erdbereich mit optischem Verfahren N2 - Holzschutzmittel gegen den biologischen Angriff von Insekten, Pilzen und Bakterien besitzen eine erhebliche volkswirtschaftliche Bedeutung. Zur Vermeidung einer in der DIN EN 252 beschriebenen rein visuellen Beurteilung wurde 1996 durch die BAM auf Grundlage des in der DIN 52186 enthaltenen Biegeversuchs eine alternative Strategie vorgeschlagen. In weiterführenden Untersuchungen soll ergänzend zur Prüfmaschine die Stereo-Fotogrammetrie als optisches 3D-Messverfahren eingesetzt werden. Die Entwicklung eines möglichst objektiven und technisch einfachen Nachweisverfahrens der Schutzwirkung und die vergleichende Bewertung der Aussagekraft beider Normen sind von besonderem Interesse. T2 - DACH Jahrestagung 2008 - ZfP in Forschung, Entwicklung und Anwendung CY - St. Gallen, Switzerland DA - 28.04.2008 KW - DIN EN 252 KW - DIN 52186 KW - Holzprüfung PY - 2008 AN - OPUS4-17521 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbst, Tristan A1 - Rübner, Katrin A1 - Meng, Birgit A1 - Hauer, B. T1 - Nachhaltiges Bauen mit Beton - Einsatz sekundärer Gesteinskörnungen N2 - Im Hinblick auf eine nachhaltige Entwicklung sollen nach dem KrW/AbfG der Rohstoffeintrag und der Abfallaustrag in den Lebensphasen eines Bauwerks durch weitgehende Verwertung von Sekundärrohstoffen (Reststoffen) möglichst gering gehalten werden. Ein Einsatz von Reststoffen wie Hausmüllverbrennungsaschen (MV-Aschen) im Betonbau kann potenziell einen wesentlichen Beitrag zur nachhaltigen Entwicklung leisten. T2 - 17. IBAUSIL CY - Weimar, Germany DA - 23.09.2009 PY - 2009 AN - OPUS4-19731 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel T1 - Bewegungs- und Verformungsanalyse unter Fallbeanspruchungen N2 - Diese Untersuchung enthält die Qualifizierung eines Laservibrometers, die Kinematik in Fallbeanspruchung und das Messverfahren, den Prüfstand und Proben. T2 - Tag der offenen Tür der BAM im Rahmen der Initiative "Deutschland, Land der Ideen" CY - Horstwalde, Germany DA - 09.09.2009 PY - 2009 AN - OPUS4-20191 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bahlmann, Stefanie A1 - Rübner, Katrin A1 - Meng, Birgit T1 - Untersuchungen zur Verwertung industrieller Reststoffe als Ersatz von Primärrohstoffen in Mörtel und Beton N2 - Um den Abbau primärer Rohstoffe zu reduzieren, wurden deponierte oder niederwertig eingesetzte industrielle Reststoffe hinsichtlich einer höherwertigen Verwendung im Betonbau untersucht. Zur Bewertung des Einsatzpotentials als Zementbestandteil oder Betonzusatzstoff erfolgte zunächst eine chemisch-mineralogische und betontechnologische Charakterisierung der Materialien. Reststoffe, die die normativen Anforderungen hinsichtlich der Zementzusammensetzung erfüllen, wurden anschließend zu verschiedenen Anteilen als Zementsubstitut in Mörtel eingesetzt. In vergleichenden Untersuchungen erfolgte die Ermittlung der Frisch- und Festmörteleigenschaften. Kalorimetrische Untersuchungen sollten die Auswirkungen der Reststoffe auf die Zementhydratation zeigen. Ausgewählte Untersuchungsergebnisse an Reststoffen aus der Industrieabwasseraufbereitung, dem Altpapierrecycling, der Biomasseverbrennung und der Metallurgie werden vorgestellt. T2 - 17. Internationale Baustofftagung IBAUSIL 2009 CY - Weimar, Germany DA - 23.09.2009 KW - Industrieabwasseraufbereitung KW - Altpapierrecycling KW - Biomasseverbrennung KW - Metallurgie PY - 2009 AN - OPUS4-36516 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Kranzmann, Axel T1 - Carburization and Oxidation of Power Plant Steels under Oxyfuel-Conditions N2 - Modern CO2-reduced power plants with Oxyfuel-Combustion operate with gas compositions of high CO2 partial pressure and steam (Boiler, Recycling). The corrosion process occurring under such service conditions is different from that under current conditions with air combustion. The effect of temperature, pressure, chromium content on the corrosion reaction of typical power plant steels in CO2 -H2O and CO-H2O-O2 was investigated. T2 - 3rd World Materials Research Institute Forum & Energy Symposium (WMRIF) CY - Gaithersburg, MD, USA DA - 21.06.2009 PY - 2009 AN - OPUS4-22625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbst, Tristan A1 - Rübner, Katrin A1 - Meng, Birgit A1 - Hauer, B. T1 - Einsatzpotenzial und nachhaltige Verwertung von Hausmüllverbrennungsaschen als Gesteinskörnungen im Beton N2 - Im Hinblick auf eine nachhaltige Entwicklung sollen nach dem KrW/AbfG der Rohstoffeintrag und der Abfallaustrag in den Lebensphasen eines Bauwerks durch weitgehende Verwertung von Sekundärrohstoffen (Reststoffen) möglichst gering gehalten werden. Ein Einsatz von Reststoffen wie Hausmüllverbrennungsaschen (MV-Aschen) im Betonbau kann potenziell einen wesentlichen Beitrag zur nachhaltigen Entwicklung leisten. T2 - Tagung Bauchemie CY - Freiberg, Germany DA - 08.10.2009 PY - 2009 AN - OPUS4-22966 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feigl, Michael A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dressler, Martin A1 - Pulz, Robert A1 - Rehmer, Birgit A1 - Feldmann, Ines A1 - Sabel, Martin T1 - Aluminiumoxidschichten für den Oxidationsschutz von Hochtemperaturlegierungen N2 - Effektive Al2O3-Keramik-Schutzschichten könnten die Verwendung preiswerterer Legierungen für Hochtemperaturanwendungen ermöglichen. Die Anforderungen an diese Schichten sind eine gute Haftung, chemische Stabilität und Dichtheit gegen die Umgebungsatmosphäre. T2 - DKG-Jahrestagung/Symposium Hochleistungskeramik CY - Aachen, Germany DA - 23.03.2009 KW - Schichtherstellung KW - Schichttestung KW - Hochtemperaturanwendungen PY - 2009 AN - OPUS4-35836 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ried, Peter A1 - Gaber, Martin A1 - Kluge, Martin A1 - Müller, Ralf A1 - Holtappels, Kai A1 - Eliezer, Dan T1 - H2-permeability and burst pressure of glass capillaries N2 - This publication deals with the topics: pressure loading, permeability and burst pressure T2 - Intern. Con. on Glass ICG 2010 CY - Bahia, Brazil DA - 20.09.2010 KW - Pressure loading KW - Permeability KW - Burst pressure PY - 2010 N1 - Geburtsname von Kluge, Martin: Beckmann-Kluge, M. - Birth name of Kluge, Martin: Beckmann-Kluge, M. AN - OPUS4-22296 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günther, Alexander A1 - Muschik, Bernd A1 - Gründer, Klaus-Peter T1 - Bi-spektrale Messung der Reflexionseigenschaften von fluoreszierenden Materialien N2 - Beim bispektralen Verfahrensprinzip (auch 2-Monochromatoren-Methode genannt) zur Charakterisierung fluoreszierender Reflexionsproben wird das Probenmaterial monochromatisch bestrahlt und für jede dieser anregenden Wellenlängen das emittierte Spektrum monochromatisch gemessen. Dies hat gegenüber einer polychromatischen Anregung (z. B. Normlichtart D65) den Vorteil, dass spektrale Materialfunktionen (Gesamt-, Reflexions- und Lumineszenz-Strahldichtefaktoren sowie das Lumineszenz-Anregungsspektrum) und diverse Farbmaßzahlen (Sicherheits- und Kontrastfarben; Referenzmaterial) für beliebige Anregungsspektren (Normlichtarten) bestimmt werden können. T2 - Licht 2010 (Gemeinschaftstagung der deutschen, niederländischen, schweizerischen und österreichischen lichttechnischen Verbände) CY - Vienna, Austria DA - 17.10.2010 PY - 2010 AN - OPUS4-22050 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ramge, Peter A1 - Rübner, Katrin A1 - Kühne, Hans-Carsten T1 - Einflüsse der Mischungszusammensetzung auf die Porenstruktur von Instandsetzungsmörteln N2 - Untersucht wurde der Einfluss der Applikationsart (konventionelle und gespritzte Herstellung, Wasserlagerung bis zur Prüfung), der Einfluss von Fasern (konventionelle Herstellung, Wasserlagerung bis zur Prüfung) und der Einfluss von Schwindreduzierern (konventionelle Herstellung, Luftlagerung bis zur Prüfung). T2 - XV. Workshop über die Charakterisierung von feinteiligen und porösen Festkörpern (Porotec-Workshop) CY - Bad Soden, Germany DA - 16.11.2010 PY - 2010 AN - OPUS4-22634 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalies, G. A1 - Rockmann, R. A1 - Tuma, Dirk A1 - Arnrich, S. A1 - Bräuer, P. T1 - Reliable information on solids from liquid-Phase adsorption N2 - For the characterization of disperse and porous solids, usually single gas adsorption(GA) is employed. In the case of liquid adsorption (LA), the extraction of information on solids immediately becomes a more sophisticated matter since information on geometric as well energetic parameters of the solids is both superposed by liquid-mixture effects and displayed in excess terms. We have to ask if reliable solid parameters can be also obtained from LA isotherms. The enlarged data bank of gas and liquid adsorption measurements enables us to change systematically solid parameters (e.g., the pore width of MCM-41, the pore entrances of SBA-16, chemical heterogeneity) and to study in this way the influence of solid parameters on LA. T2 - The FOA 10, 10th International Conference on Fundamentals of Adsorption CY - Awaji Island, Japan DA - 23.05.2010 KW - porous solids KW - gas adsorption KW - excess isotherms PY - 2010 AN - OPUS4-35945 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jakubcová, Petra A1 - Rübner, Katrin A1 - Schnell, A. T1 - Leichtgranulate aus heterogenem Bauschutt zur Herstellung von Beton N2 - Untersucht wird die Entwicklung einer Technologie zur Herstellung hochwertiger Leichtgranulate (Blähgranulate) mit definierten Produkteigenschaften aus heterogenen Bau- und Abbruchabfällen, Anwendung der Granulate als leichte Gesteinskörnung im Beton und die Möglichkeit des rohstofflichen Recyclings mineralischer Bauabfälle T2 - r2- Statusseminar 2011, "Innovative Technologien für Ressourceneffizienz - rohstoffintensive Produktionsprozesse, Fraunhofer-Institut CY - Berlin, Germany DA - 26.10.2011 PY - 2011 AN - OPUS4-24717 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterhus, Lennart A1 - Rübner, Katrin T1 - Kieselsäurehaltiger Filterrückstand aus industrieller Abwasserbehandlung für den Einsatz als hydraulisches Bindemittel N2 - - 5.000 bis 10.000 t wasserhaltiger Filterrückstand (FR) entstehen jährlich pro Produzent bei der Neutralisation der Abwässer aus der Silicon- oder Kieselsäureherstellung - Anfall als fester, feuchter, schollenartiger Filterkuchen - Verwertung heute: Deponierung, Tagebauverfüllung -> ungenutzte Sekundärrohstoffquelle - Untersuchung der Einsatzmöglichkeiten der aufbereiteten Filterrückstände zur Eigenschaftsverbesserung zementgebundener Baustoffe analog der wohlbekannten Anwendung von hochdisperser Kieselsäure und Silicastaub T2 - GDCh-Tagung Bauchemie CY - Hamburg, Germany DA - 06.10.2011 PY - 2011 AN - OPUS4-24819 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dörfel, Ilona A1 - Rooch, Heidemarie A1 - Österle, Werner A1 - Kranzmann, Axel T1 - Vanadium and chromium containing precipitates in heat resistant steel T92 T2 - "Current Developments in TEM" (JEOL user meeting) CY - Freiberg, Germany DA - 10.03.2011 PY - 2011 AN - OPUS4-22678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Heidmann, G. T1 - Monitoring von Hochspannungskabel-Muffen und -Endverschlüssen N2 - - Zunehmender Energiebedarf erfordert höhere Übertragungskapazitäten - Dezentrale ökologische Energiegewinnung, z. B. Offshore, erfordert Übertragung großer Energiemengen in die Ballungszentren (Nord-Süd-Trassen) - Hohe Auslastung der Netze erfordert Beherrschbarkeit der im Fehlerfall auftretenden Risiken für Menschen, Umwelt und energietechnische Anlagen - Etwa 90 % der Anlagenausfälle sind verursacht durch Teilentladungen (TE) in Endverschlüssen und Muffen mit modernen polymeren Isoliersystemen - Etablierte elektrische Verfahren erlauben nur externe Schadensdetektion. T2 - Expertenforum Strukturmonitoring auf der Sensor+Test-Messe CY - Nuremberg, Germany DA - 08.06.2011 PY - 2011 AN - OPUS4-24054 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ried, Peter A1 - Gaber, Martin A1 - Müller, Ralf A1 - Holtappels, Kai A1 - Schmidtchen, Ulrich A1 - Deubener, J. T1 - Wasserstoffpermeations-messung an Gläsern T2 - Glastechn. Tagung, HVG-DGG CY - Saarbrücken, Germany DA - 30.05.2011 PY - 2011 AN - OPUS4-24012 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Habel, Wolfgang A1 - Basedau, Frank T1 - Langzeitmonitoring der Ederstaumauer N2 - Die Fixierung der Stahlanker im Felsfundament zur Stabilisierung der Schwergewichtsmauer werden mit integrierten faseroptischen Dehnungssensoren überwacht. In die Glasfaser sind Reflektoren eingebaut; zwei Reflektoren bilden jeweils eine Messstrecke, die Auskunft über die Fixierung geben. Am Ankerkopf wird der Zustand der Messstrecken abgefragt. T2 - Expertenforum Strukturmonitoring auf der Sensor+Test-Messe CY - Nuremberg, Germany DA - 08.06.2011 PY - 2011 AN - OPUS4-24047 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Wolfram A1 - Priebe, Nsesheye Susan A1 - Kühne, Hans-Carsten T1 - SPIN- Spearhead network for innovative,clean and safe cement & concrete technologies N2 - Worldwide, cement and concrete experts are at the cutting-edge to sustainable, green, healthy but nonetheless high-Performance concrete. The current relatively low development of the cement and concrete industry in Africa offers the unique opportunity to start directly on the best achievable and sustainable Level, if only Expertise is sufficiently available. It should not be neglected that concrete is a product with comparably low Transport ranges, which means that an improved concrete market will mainly Support the local economy without exceeding financial Drains to the international market, thus fostering the fight against poverty, which is an urgent Need in most African countries. T2 - Workshop Cement and Concrete for Africa CY - Berlin, Germany DA - 17.08.2011 PY - 2011 N1 - Geburtsname von Priebe, Nsesheye Susan: Msinjili, N. S. - Birth name of Priebe, Nsesheye Susan: Msinjili, N. S. AN - OPUS4-24728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbst, Tristan A1 - Rübner, Katrin A1 - Meng, Birgit T1 - Integrated and holistic suitability assessment of recycling options for masonry rubble N2 - Behandelt den Bausektor und die Verarbeitsungsqualität T2 - European Geosciences Union (EGU) General Assembly 2012 CY - Vienna, Austria DA - 22.04.2012 PY - 2012 AN - OPUS4-25868 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herbst, Tristan A1 - Rübner, Katrin A1 - Müller, A. A1 - Seidemann, M. T1 - Verwertung kieselsäurehaltiger Filterrückstände in mineralischen Baustoffen N2 - - jährlicher Anfall von 5.000 bzw. 10.000 Tonnen wasserhaltiger Filterrückstände (FR) pro Produzent bei der Abwasser-Neutralisation aus der Kieselsäure- bzw. Chlorsilanherstellung (FR1, FR2) - heute: Deponierung, Tagebauverfüllung - ungenutzte Sekundärrohstoffquelle - Untersuchung möglicher Anwendungsbereiche für FR T2 - GDCh Tagung Bauchemie CY - Dübendorf, Switzerland DA - 11.10.2012 PY - 2012 AN - OPUS4-26673 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Meinel, Dietmar A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Klobes, Peter A1 - Schnell, A. A1 - Hempel, S. T1 - Porenstruktur leichter Gesteinskörnungen aus Mauerwerkbruch N2 - Leichte Gesteinskörnungen mit Kornrohdichten < 2 g/cm³ werden industriell aus natürlichen Rohstoffen, wie Ton und Schiefer, hergestellt. Dabei fallen hohe Energiekosten an, während außerdem fortwährend die Verfügbarkeit geeigneter Rohstoffe sinkt. Eine Alternative stellen Leichtgranulate, die aus mineralischen Bau- und Abbruchabfällen hergestellt werden, dar. Im Forschungsprojekt „Aufbaukörnungen“ wurde eine Technologie zur Herstellung hochwertiger leichter Gesteinskörnungen aus Mauerwerkbruch entwickelt. Ziegelhaltige Bau- und Abbruchabfälle fallen in Deutschland mit bis zu 26 Mio. t pro Jahr an und weisen größere Verwertungsdefizite als Betonbruch auf. Der neuen Verwertungsstrategie liegt die Idee des rohstofflichen Recyclings zu Grunde. Die leichten Gesteinskörnungen werden am Ende eines mehrstufigen Herstellungsprozesses durch thermische oder hydrothermale Erhärtung im Labor- und halbtechnischen Maßstab produziert. Für Herstellungstechnologie und Eigenschaften der Leichtbetone sind neben Kornfestigkeit und Rohdichte die Porosität und Wasseraufnahme der leichten Gesteinskörnungen entscheidende Größen, die wiederum von Kornform, Oberflächenrauigkeit, Sinterschale und Porenstruktur der Körnungen beeinflusst werden. T2 - XVI. Porotec-Workshop über die Charakterisierung von feinteiligen und porösen Festkörpern CY - Bad Soden, Germany DA - 13.11.2012 PY - 2012 AN - OPUS4-27160 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Daum, Werner A1 - Tkachenko, Viktoriya A1 - Habel, Wolfgang T1 - Sensitive pultrudierte Tragwerke N2 - - Innovative Konstruktionskonzepte für den Leichtbau verwenden neue Material-Kombinationen - Erweiterte Anwendung der Sensortechnik bei der Entwicklung neuer Materialen - Integration von Sensoren in die Struktur, um synergetische Effekte effizienter auszunutzen und Eigenschaften zu steuern T2 - 2. TSB-TransferTreff "Materialeffizienz und Gestaltung" CY - Berlin, Germany DA - 11.06.2012 PY - 2012 AN - OPUS4-26464 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marzok, Ulrich A1 - Müller, Ralf A1 - Schadrack, Reinhard A1 - Krauhausen, M. A1 - Reetz, R. T1 - Hochtemperatur-Laserprofilometrie für keramische Proben N2 - Das Hochtemperatur-Laserprofilometer der BAM4 ermöglicht eine 3D-Formerkennung an keramischen Folien oder anderen flachen Objekten während thermischer Behandlungen wie zum Beispiel bei laufenden Entbinderungs- oder Sinterprozessen. Mit dem Lasertriangulationssensor werden das Höhenprofil, die lateralen und axialen Schwindungen und andere charakteristische Maße der Probe wie die Folienbreite und -dicke, Abstände zwischen spezifischen Merkmalen oder Krümmungen bestimmt. Somit können insbesondere auch Deformationen und Verwerfungen der Objekte sowie Schwindungsinhomogenitäten an strukturierten Objekten erkannt und mit dem Herstellungsprozess verknüpft werden. T2 - DKG Jahrestagung 2012 CY - Nuremberg, Germany DA - 05.03.2012 KW - 3D-Formerkennung KW - Lasertriangulationssensor KW - Deformationen KW - Schwindungsinhomogenitäten PY - 2012 AN - OPUS4-35787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maurer, G. A1 - Tuma, Dirk A1 - Chobanov, K. A1 - Kumełan, J. A1 - Pérez-Salado Kamps, Á. T1 - Gas solubility in ionic liquids: Solubility of a binary gas mixture in a pure ionic liquid as well as of a single gas in a binary liquid mixture N2 - Ionic Liquids (ILs) are employed in various fields, for example, reaction engineering (reactions with gases, such as hydroformylation (CO, H2), hydrogenation (H2), oxidation (O2)) or separation technology (separations of gases, reactants, and high-volatility reaction products). For the basic engineering of such processes, knowledge of phase equilibria, particularly of mixtures, over a broad (p,T) range is mandatory. This contribution reports on recent experimental results from our laboratory: – for the simultaneous solubility of a binary gas mixture in a pure ionic liquid – for the solubility of a single gas in a binary liquid solvent mixture. T2 - EUCHEM 2012 Conference on Molten Salts and Ionic Liquids CY - Celtic Manor, Wales, United Kingdom DA - 05.08.2012 KW - ionic liquids KW - gas solubility KW - Henry's constant PY - 2012 AN - OPUS4-35947 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Spranger, Holger T1 - THz-ToFD Tomography with Synthetic-Aperture-Aperture N2 - Terahertz-radiation (T-ray) are electromagnetic waves within a frequency range between 0,3 to 6 THz. T-rays are nonionising! They penetrate plastic, paper, ceramic and fabric. It is promising to use T-Rays for CT-applications to reveal uncertainties in dielectric materials. T2 - 8. THz-PhD-meeting CY - Marburg, Germany DA - 06.08.2013 KW - Terahertz Tomography synthetic aperture PY - 2013 AN - OPUS4-36223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sojref, Regine A1 - Schreiber, R. A1 - Makrlik, A. A1 - Schadrack, Reinhard A1 - Müller, Ralf T1 - Fused Silica Containing Powders for Low Sintering (1650°C) Mullite-Zirconia Composites T2 - 23rd International Congress on Glass CY - Prague, Czech Republic DA - 01.07.2013 PY - 2013 AN - OPUS4-30851 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan A1 - Agea Blanco, Boris A1 - Müller, Ralf T1 - Sintering and bloating phenomena of barium disilicate glass powders T2 - 88. Glastechnische Tagung DGG - ACerS GOMD 2014 CY - Aachen, Germany DA - 26.05.2014 PY - 2014 AN - OPUS4-30810 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel T1 - Hydrogen in Iron visualized in 3D by neutron tomography N2 - Presented are neutron tomographies on hydrogen charged iron samples. T2 - RACIRI Summer School 2015 CY - Sellin, Rügen, Germany DA - 22.08.2015 KW - Tomographie KW - Wasserstoff KW - Neutronen KW - Hydrogen KW - Neutron KW - Tomography PY - 2014 AN - OPUS4-44838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Prewitz, Marc A1 - Müller, Ralf A1 - Marotzke, Christian A1 - Holtappels, Kai T1 - Characterization of glass capillary storage modules considering permeability and mechanical stress via finite elements N2 - Glass capillaries are potential candidates for long term hydrogen storage under high pressure. Burst pressure strongly drops with surface damaging, a polymer coating is needed. The aim is to study stress distribution within single coated glass capillaries sealed to metal fittings T2 - 88. Glastechnische Tagung DGG – ACerS GOMD 2014 CY - Aachen, Germany DA - 25.05.2014 KW - Burst test KW - Hydrogen storage KW - Polymer coating PY - 2014 AN - OPUS4-35784 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfretzschner, Beate A1 - Griesche, Axel T1 - Hydrogen in blistered iron visualized in 3D by neutron tomography N2 - Presented are neutron tomographies on hydrogen charged iron samples. T2 - RACIRI Summerschool CY - Sellin, Germany DA - 22.08.2015 KW - Eisen KW - Neutronenradiographie KW - Wasserstoff PY - 2014 AN - OPUS4-47786 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maurer, G. A1 - Tuma, Dirk A1 - Chobanov, K. A1 - Kumełan, J. A1 - Pérez-Salado Kamps, Á. T1 - High-pressure gas solubility in mixtures with one compound being an „alternative“ solvent N2 - The term „Alternative Solvents“ often refers to ionic liquids (ILs), mainly to distinguish these substances from traditional (i.e., molecular) solvents. In applications, any „alternative“ is required to perform better than something that is proven and tested. To bring ILs into practical use, availability and costs are the fundamental points to be addressed. There are two ways to proceed: ▬ tailoring a molecule, implanting the expected characteristics advantage: optimization of the targeted performance possible risks: outcome not always foreseeable, costly and time-intensive (“trial and error“) ▬ to target on mixtures of well-characterized ILs with molecular solvents advantage: substance characteristics are known, less costly, less time-consuming, mixture composition another tunable parameter risks: the same but with less impact For the basic engineering of technical processes, knowledge of phase equilibria, particularly of mixtures, over a broad (p,T) range is mandatory. This contribution reports on recent experimental results from our laboratory: ▬ the solubility of CO2 in a mixture of water and [bmim][CH3SO4] ▬ the solubility of CO2 in a mixture of methanol and [bmim][PF6] T2 - EUCHEM 2014 5th Conference on Molten Salts and Ionic Liquids CY - Tallinn, Estonia DA - 06.07.2014 KW - Ionic liquids KW - Gas solubility KW - Henry's constant PY - 2014 AN - OPUS4-35944 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Sebastian A1 - Meng, Birgit A1 - Selleng, Christian T1 - A new sample holder for fast xrd investigation on UHPC N2 - A new sample holder is described in this poster. It was developed in BAM for fast XRD investigation on UHPC (ultra high performance concrete). Results measuring solid, i.e. not pulverized, samples are shown. T2 - GeoBerlin 2015 CY - Berlin, Germany DA - 04.10.2015 KW - Building Materials KW - UHPC KW - X-ray diffractometry PY - 2015 AN - OPUS4-36949 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf A1 - Behrens, H. A1 - Deubener, J. T1 - Impact of structure and relaxation on fatigue and micromechanical properties of oxide glasses: the role of volatiles and bonding state N2 - As subcritical crack growth (SCCG) can reduce tensile strength of glasses by many orders of magnitude, the potential for improvement of fatigue behaviour is most intriguing in developing ultra-strong glasses. An essential bottleneck is the basic understanding of the numerous interplaying pressure-, temperature- and water-affected relaxation phenomena at the crack tip and related toughening strategies. Therefore, the present project aims to advance the basic understanding of structural relaxation effects and local properties caused by increased water concentration and tensile stresses at the crack tip as they are a key for structural toughening designs to develop SCCG-free glasses and glass surfaces. Our first studies give clear evidence that glass structure and dynamics is strongly modified upon hydration of glasses. These changes are highly related to the nature of network formers but are affected as well by the counter ions (network modifier). Results of the 1st project part suggest that structural relaxation below glass transition temperature, i.e. overlapping of short-range (beta) and long-range (alpha) interactions can contribute to SCCG in water-free environments and that structurally dissolved water in the glasses can have decisive impact on this effect. In the 2nd project stage specific glasses compositions will be investigated to gain an improved understanding on the relation of sub-Tg relaxation and inert SCCG as well as to shed light to the related effects of dissolved water and its speciation. These glasses cover a broader range of different glass topologies and binding partners, whereby the coupling of alpha and beta relaxations is varied systematically by alkali-, alkaline earth ions and water species concentrations. Preparation of hydrous glasses (up to 8 wt% water) will be performed by high pressure syntheses. Structure will be resolved by NMR, Raman and IR spectroscopy while structural relaxation is accessed in the temperature and frequency domain using dynamic mechanical spectroscopy and ultrasonic damping. We will focus on measurements of inert SCCG (region III) conducting experiments in vacuum and dry gas atmospheres using indentation techniques and stressing of glass specimens in DCB geometry. Experimental data on SCCG will be provided to SPP groups, which deals with fatigue in metallic glasses and vice versa we will test theoretical predictions of ab-initio simulations of partner within SPP 1594 in order to quantify the effect of water on the crack tip. In summa topological factors controlling the subcritical crack growth with respect to water will be identified from which structural toughening designs for highly fatigue resistant-glasses can be derived. N2 - Subkritisches Risswachstum (SCCG) kann die Zugfestigkeit von Glas um viele Größenordnungen erniedrigen. Deshalb birgt die Verbesserung des Ermüdungsverhaltens ein hohes Potential für das topologische Design hochfester Gläser. Ein diesbezüglicher Engpass ist das Verständnis der zahlreichen interagierenden druck-, temperatur- und wasserbeeinflussten Relaxationsphänomene an der Rissspitze und hieraus abgeleitete Verstärkungsstrategien. Ziel des Projekts ist es daher, das grundlegende Verständnis der Effekte, die infolge erhöhter Wasserkonzentrationen und Zugspannungen an der Rissspitze entstehen, zu vertiefen, da sie als ein Schlüssel für künftige strukturelle Designprinzipien zur Entwicklung schadenstoleranter Gläser und Glasoberflächen gelten. Unsere ersten Studien zeigen, dass die Struktur und Dynamik von Gläsern nach einer Hydration stark verändert sind. Diese Modifikationen sind mit der Art der Netzwerkbildner stark verknüpft, aber auch von ihren Gegenionen (Netzwerkwandler) abhängig. Die Ergebnisse des ersten Projektabschnitts legen nahe, dass strukturelle Relaxation unterhalb der Glasübergangstemperatur, d. h. ein Überlappen von kurz-reichweitigen (beta) und lang-reichweitigen (alpha) Wechselwirkungen, zum subkritisches Risswachstum in wasserfreien Umgebungen beitragen kann und, dass strukturell gelöstes Wasser in Gläsern sich entscheidend auf diese Effekt auswirken kann. Im zweiten Projektabschnitt werden daher spezielle Glaszusammensetzungen untersucht, die zu einem besseren Verständnis der Verbindung zwischen sub-Tg Relaxation und SCCG führen aber auch den Einfluss von gelöstem Wasser und dessen Speziation näher beleuchten. Diese Gläser weisen eine großen Breite an verschiedenen Topologien und Bindungspartnern auf, wobei die Kopplung von alpha und beta Relaxation durch Veränderungen in den Gehalten von Alkali-, Erdalkalionen und der Wasserspezies systematisch variiert wird. Die Präparation hydratisierter Gläser (bis zu 8 Ma.%) erfolgt mittels Hochdrucksynthesen. Die Glasstruktur wird durch NMR, Raman und IR Spektroskopie aufgeklärt während die Strukturrelaxation anhand dynamische mechanische Spektroskopie und Ultraschalldämpfung im Temperatur- und Frequenzraum erfasst wird. Im Fokus werden Messungen des inerten subkritischen Risswachstums (Region III) stehen, die Indenter-Experimente im Vakuum und trockenen Gasatmosphären sowie Verspannen von Glasproben in DCB Geometrie beinhalten. Experimentelle SCCG Daten werden Gruppen im Schwerpunktprogramm zur Verfügung stellen, die sich mit Ermüdung in metallischen Gläsern beschäftigen und im Gegenzug werden wir theoretische Vorhersagen aus ab initio Simulationen der Partner im SPP 1594 testen, um den Einfluss von Wasser auf die mechanischen Eigenschaften an der Rissspitze und deren Einfluss auf SCCG zu quantifizieren. In summa werden topologische Faktoren bezüglich Wasser, die SCCG kontrollieren, identifiziert, um daraus Designprinzipien für hoch ermüdungsresistente Gläser abzuleiten. T2 - Kolloquium des DFG-PP 1594 CY - Jena, Germany DA - 17.9.2015 KW - Glass KW - Fatigue PY - 2015 AN - OPUS4-38334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Groh, D. A1 - Döhler, F. A1 - Brauer, D. S. T1 - Sintering and crystallization of new bioactive glasses N2 - Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during the sintering, which results in poor mechanical properties and reduced bioactivity. Recently, new bioactive glasses with improved crystallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. The aim of this study was to investigate the sintering and crystallization behavior of these new bioactive glasses. Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases are detected. The thermal properties of all glasses were studied by DTA measurements, and the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles progressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization of beta-HAp. T2 - ICG 2016 CY - Shanghai, China DA - 07.04.2016 KW - Bioactive KW - Glass KW - Crystallization KW - Sintering PY - 2015 AN - OPUS4-38304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Groh, D. A1 - Döhler, F. A1 - Brauer, D. S. T1 - New bioactive glasses with improved sintering behavior N2 - Nowadays, the use of bioactive glasses is established for bone regeneration; however glasses are used mostly as powders, granules or in a paste. Sintered scaffolds are not used clinically, because of the in inherent problem of crystallization during the sintering process, resulting in poor mechanical properties and reduced bioactivity. The aim of this study was therefore to design new bioactive glasses, which combine improved processing and sintering with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkalioxide ratio was increased, sodiumoxide was partially replaced by potassiumoxide and up to 8 mol% calciumflorid were added, in order to stabilize the glass against crystallization. The sintering behavior of the new glasses was characterized by heating microscopy and compared to Bioglass® 45S5. The results showed that the new glasses achieved a sintered density of 88-99 % in contrast to only 57-67% for Bioglass® 45S5. In addition FTIR and XRD analyses showed that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases were detected. The thermal properties of all glasses were studied by DTA and DSC measures, and the influence of grain size and heating rate were characterized. These studies showed a shift of start and end temperature of sintering process as well as the final density. The structure of sintered specimens during and after sintering was examined using light and electron microscopy (REM). T2 - Crystallization 2015 CY - Nagaoka, Japan DA - 11.10.2015 KW - Bioactive KW - Glass KW - Crystallization KW - Sintering PY - 2015 AN - OPUS4-38308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Bruno, Giovanni A1 - Kannengießer, Thomas T1 - 3D imaging of hydrogen assisted cracking using analyser-based imaging N2 - To better understand the mechanism of hydrogen assisted cracking (HAC), it is important to investigate the 3D structure of the cracks non-destructively. Since, cracks introduced by HAC are usually very small, conventional x-ray imaging methods often lack the required spatial resolution. However, the detection of those cracks can be enhanced by taking advantage of refraction at interfaces within the sample. To image this refractive deflection we employ analyser based imaging (ABI). In this work we aim at proving the enhanced crack detection of ABI by investigating an alluminum alloy weld. T2 - BESSY User Meeting 2015 CY - Berlin, Germany DA - 09.12.2015 KW - X-ray refraction KW - Synchrotron KW - Analyser-based imaging KW - Hydrogen assisted cracking KW - Welding PY - 2015 AN - OPUS4-38278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shashev, Yuri A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Britzke, Ralf A1 - Bruno, Giovanni A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. T1 - Optimizing the performance of phase gratings for better visibility in Talbot- Lau interferometry N2 - We investigated the efficiency of phase gratings, i.e., the visibility upon variation of different parameters. Rotating around an axis parallel to the grid lines of the phase grating changes the grating’s shape and thereby the initial distribution of phase shifts. This yields high visibilities for shorter propagation distances than derived from box shapes. Tilting the grating in the scattering plane allows continuous tuning of the grating’s height that corresponds to an ideal phase shift for a particular photon energy. This opens the way for tuning the design energy suitable for the material under investigation. Our study included simulations for monochromatic sources with the sampling procedure. T2 - PhD Day 2015 CY - Berlin, Germany DA - 14.7.2015 KW - Talbot-Lau interferometry PY - 2015 AN - OPUS4-38325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cabeza, Sandra A1 - Garcés, G. A1 - Pérez, P. A1 - Andrade, C. A1 - Adeva, Paloma T1 - Low alloyed Mg-Y/RE-Zn alloys: mechanical and corrosion behaviour N2 - Mg-Y,RE-Zn systems present second phases with high thermal stability, promoting the increase of strength and creep resistance at high temperatures. Mg and its alloys have a potential application as biomaterials due to their biocompatibility and degradation behaviour. The dominant corrosion mechanism in those alloys is the microgalvanic corrosion through coupling of the more noble second phases with the Mg matrix, and therefore a low concentration of those was sought. T2 - Mg 2015 CY - Jeju, South Korea DA - 12.10.2015 KW - Magnesium KW - LPSO KW - Corrosion behaviour KW - Mechanichal behaviour PY - 2015 AN - OPUS4-38398 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Selleng, Christian A1 - Gröger, K. A1 - Fontana, Patrick A1 - Meng, Birgit A1 - Altenberger, U. T1 - Effect of 90°C thermal treatment on Ultra-High Performance Concrete N2 - Ultra High Performance Concrete (UHPC) is characterized by high strength and high durability. This is achieved by an optimized grain size distribution, especially within fine grains, and addition of superplasticizer, which allow the reduction of the water/cement ratio in the cement paste and thereby the increase of the density of UHPC. Thermal treatment, i.e. curing at elevated temperature and pressure, contributes to a further increase of compressive strength. The aim of the presented study was to analyze the effect of thermal treatment at 90 ◦C and atmospheric pressure on UHPC samples. Varying factors were the age of the samples when heat treatment started (initial storage time), the duration of heat treatment and the type of heat treatment. It was applied in three ways: 1. treated without any protection, 2. sealed in plastic foil and 3. treated in hot water. Afterwards the samples were analyzed with respect to their mechanical properties and their phase composition. Furthermore, the weight (water absorption) of the samples was observed over 28 days and was correlated with the strength test results. The development of strength depends on the combination of initial storage time and the duration of heat treatment and is also influenced by the type of thermal treatment. The highest compressive strengths have been observed by implementing the hot water treatment. Thereby the weight of the samples increase due to additional absorbed water. This enables an increased hydration of cement clinker inducing a higher strength. T2 - GeoBerlin 2015: Dynamic Earth - from Alfred Wegener to today and beyond CY - Berlin, FU Berlin DA - 04.10.2015 PY - 2015 AN - OPUS4-34504 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rübner, Katrin A1 - Prinz, Carsten A1 - Zimathies, Annett A1 - Adolphs, Jürgen A1 - Hempel, Simone A1 - Schnell, Alexander T1 - Studies on the Pore Structure of Lightweight Recycling Granules N2 - Lightweight granules are mineral, spherical and porous particles with bulk density less than 2000 kg m . New types of lightweight granules are made from masonry -3 rubble as an alternative to the commonly used expanded clay and shale. They are produced in a multistage manufacturing process by thermal or hydrothermal treatment. Studies of the microstructure of the new lightweight granules are very important to optimise the engineering properties with regard to different applications from lightweight concrete to planting substrates and wastewater treatment. Here, the results of porosity and pore structure measurements are presented. Characteristic samples with different bulk densities of both thermally and hydrothermally hardened granules have been analysed by means of various methods. T2 - 27. Deutsche Zeolith-Tagung CY - Oldenburg, Germany DA - 25.02.2015 PY - 2015 AN - OPUS4-32835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Kneib, G. T1 - Elastic wave propagation of ultrasound in bituminous road surfaces – simulations and measurements N2 - Maintenance costs of road infrastructure are increasing steadily. Adverse environmental impacts on infrastructure get more and more important as well. Therefore, it is important to determine how limited financial resources can be directed with an optimum pay-out. The present study takes first steps towards the usage of low-frequency ultrasound as a tool to evaluate the road condition. T2 - International Symposium Non-Destructive Testing in Civil Engineering 2015 CY - Berlin, Germany DA - 15.09.2015 KW - Wave propagation KW - Ultrasonic KW - NDT KW - Simulation PY - 2015 AN - OPUS4-38837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wu, Cheng-Chieh A1 - Weisbrich, S. A1 - Neitzel, F. T1 - Inverse finite element adjustment of material parameters from integrated analysis of displacement field measurement N2 - The integration of finite element method (FEM) into the least-squares adjustment presented in is further extended for a joint evaluation of an elastostatic model and displacement field measurement. For linear solids which obey the Hooke's law, the material parameters determination from measurements is being examined. T2 - 32nd Danubia-Adria Symposium on advances in experimental mechanics CY - Starý Smokovec, Slovakia DA - 22.09.2016 KW - Integrated analysis KW - Inverse problem KW - Finite element method KW - Least-squares adjustment KW - Model and measurement based analysis PY - 2015 AN - OPUS4-35648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stroh, Julia A1 - Nguyen, Thi Yen A1 - Emmerling, Franziska T1 - High resolution in situ monitoring of the initial cement hydration influenced by organic admixtures N2 - Numerous admixtures are used in the building practice to customize the properties of the cement paste during application. The influences of admixtures on the course of cement hydration and formation of hydrate phases have to be considered. Polycarboxylate ether (PCE) based polymeric superplasticizers (SPs) are known to retard the setting of the cement paste. The extent of the retardation differs depending on the molecular structure of the SP. Additionally, the presence of a stabilizing agent (SA) in the cement paste has a retarding side effect on the setting. The initial cement hydration processes and the detailed mechanisms of the retardation influenced by PCEs, as well as their interactions with particular SAs, are insufficiently understood. Up to now, only the results of phenomenological studies were taken into account to describe this retardation process. A detailed structure analysis monitoring the change of the phase composition during the hydration was never applied. Both SP and SA affect the adsorption of the sulphate ions on the clinker particles, causing changes in the formation of ettringite during the initial hydration, and are therefore a crucial part of the setting process itself. Here, the initial hydration of cement influenced by the interaction of SP and SA was monitored in situ by synchrotron X-ray diffraction. The high time resolution of the measurements allowed a continuous detection of the hydrates formed. The hydration was followed from the starting point of water addition and for couple of hours afterwards. The hydration of the levitated cement pellets containing starch as SA was initialized by adding aqueous solutions of different commercial SPs. Changes in the ettringite formation were detected in comparison to the reference hydration of pure cement. T2 - Early Age Concrete: From the Research Lab to the Construction Site CY - Tomsk, Russia DA - 02.06.2015 KW - Portland cement KW - Initial hydration KW - Superplasticizer KW - Stabilizer KW - Synchrotron XRD PY - 2015 AN - OPUS4-35470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rütters, H. A1 - May, Franz A1 - Bettge, Dirk A1 - Fischer, S. A1 - Ganzer, L. A1 - Jäger, P. A1 - Kather, A. A1 - Lempp, C. A1 - Lubenau, U. T1 - Combining CO2 Streams from Different Emitters – A Challenge For Transport And Storage Infrastructure N2 - The European Directive 2009/31/EC on the geological storage of CO2 envisages an open access of CO2 streams from different emitters to a nation- or even EUwide CO2 pipeline network if CO2 stream compositions meet “reasonable minimum composition thresholds”. As of today it is not known how such “composition thresholds” may be defined and which impurity levels may be viable in practical application. To set up recommendations for criteria and respective threshold values for CO2 stream compositions, the project “CLUSTER” will investigate how a dynamic interplay – both in terms of mass fluxes and compositions – of CO2 streams from regionally clustered CO2 sources sharing a transport and storage infrastructure will impact corrosion, e.g., of pipelines and plant components, and geochemical alteration of cap rocks and reservoir rocks. In addition, the behaviour of such a highly dynamic CCS system will be considered for an overall optimization of system design including CO2 stream mixing schemes and facilities or interim CO2 storage. T2 - TCCS-8 – The 8th Trondheim Conference on CO2 Capture, Transport and Storage CY - Trondheim, Norway DA - 16.06.2015 KW - Carbon capture KW - Carbon dioxide KW - Corrosion KW - CCS PY - 2015 AN - OPUS4-47018 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonardo A1 - Mosquera Feijoo, Maria A1 - Nolze, Gert A1 - Rizzo, F. T1 - Nano-sized precipitates in an Fe-13Cr alloy formed under oxidizing water vapor atmosphere N2 - Oxidation of a Fe-13Cr alloy under water vapor at 600 °C produced a zone of nano-sized precipitation underneath the outside scale formed by iron oxides and Fe‒Cr spinel. The majority of the spinel layer shows a mixed orientation relationship to the ferritic matrix {100}α || {100}sp & <011>α || <001>sp. However, also the discovered precipitated particles are characterized by the same crystallographic orientation relationship to the respective ferritic parent grain. The habit of the precipitates is best described by a lath morphology with their main axis parallel to <100> of ferrite. Energy dispersive X-ray spectroscopy (EDX) and electron backscatter diffraction (EBSD) in an scanning electron microscope (SEM) have been applied to characterize the oxide layer in the micrometer scale. The clearly smaller precipitates were subsequently investigated by transmission electron microscopy (TEM). Specimens have been prepared by focused ion-beam (FIB) milling at an area previously characterized by EBSD. They cover the ferritic base material, but mainly the precipitation zone and the Fe‒Cr spinel layer. Energy filtered selected area diffraction (SAD) in the conventional (C)TEM and high-angle annular darkfield (HAADF) imaging in the scanning (S)TEM mode were employed in the characterization of the specimens. T2 - International Conference on Solid-Solid Phase Transformations in Inorganic Materials (PTM) 2015 CY - Whistler, British Columbia, Canada DA - 28.06.2015 KW - Precipitation KW - Oxidation KW - Microscopy KW - Topotactic transformation KW - Spinel PY - 2015 AN - OPUS4-42169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Sensorgestütztes MSG-Engspaltschweißen mit modifizierter Prozessführung (IGF-Nr. 17.923N / DVS-Nr. 03.111) N2 - Präsentation von Versuchsaufbau und Ergebnissen zu IGF-Projekt 17.923N. Darstellung einer Methodik zur automatisierten Regressionsmodellierung eines Lichtbogensensors zur Höhenführung mittels künstlicher neuronaler Netze durch Einbindung optischer Sensorik als Referenzmesswert. T2 - Sitzung DVS AG V 2.4 „Schweißen mit abschmelzender Elektrode MIG/MAG” CY - Berlin, Germany DA - 16.04.2018 KW - MSG-Engspaltschweißen KW - Automatisierung KW - Lichtbogensensorik KW - Künstliche neuronale Netze KW - Digitalisierung PY - 2015 AN - OPUS4-44543 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marzok, Ulrich A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Gaber, Martin A1 - Welter, T. A1 - Deubener, J. T1 - Bestimmung der H2-Permeabilität von Gläsern mit der VHE-Methode N2 - Die Entwicklung von Wasserstoffbarrieren aus Glas erfordert die genaue Messung geringster H2-Permeabililtäten. Bisherige Untersuchungen haben gezeigt, dass die VHE-Pulvermethode diesbezüglich eine besonders hohe Empfindlichkeit bietet. Hierbei wird die isotherme Gasabgabe aus sphärischen Partikeln im Rahmen klassischer Diffusionsmodelle gefittet und daraus der Diffusionskoeffizient bestimmt. Für die Untersuchung von Gläsern mit möglichst geringer H2-Permeabilität ist jedoch eine Validierung der Genauigkeit der Methode notwendig. Vor diesem Hintergrund erfolgte die numerische Modellierung der H2-Abgabe mit Hilfe des Programms COMSOL Multiphysics®. Im Poster wird der Einfluss der Korngrößenverteilung der Glaspulverpartikel, der Partikelform sowie der Effekt einer nichthomogenen H2-Startverteilung auf die mittels Pulvermethode ermittelten Diffusionskoeffizienten diskutiert. T2 - 90. Glastechnische Tagung (Deutsche Glastechnische Gesellschaft e.V.) CY - Goslar, Germany DA - 06.06.2016 KW - Wasserstoffpermeation KW - Glas KW - Vakuumheißextraktion KW - Pulvermethode KW - Simulation PY - 2016 AN - OPUS4-36528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marzok, Ulrich A1 - Müller, Ralf A1 - Reetz, R. A1 - Trunkhardt, M. T1 - High-temperature laser profilometry N2 - Advanced methods for 3D green density characterization like computed tomography and 3D FE sinter modeling can be utilized for increasing the reliability of sintered components. The experimental in situ observation of sin-tering, however, is currently restricted to silhouette methods, i.e. heating microscopy. For complex shaped sam-ples, in situ shape screening during shrinkage would allow better validation of 3D sinter simulation models. Further, by revealing temporary sinter warpage, 3D high-temperature shape screening would allow to locate potential defects of complex sintered components. Against this background, BAM developed a testing device for in situ 3D high-temperature shape screening for ceramic and glass-ceramic tapes up to 1000°C [1-3]. Current work is focused on dropping this restriction in sample shape and temperature. The poster illustrates the current state of this work and possible applications of the method e.g. in detecting sinter warpage of metallized glass-ceramic LTCC tapes. T2 - 90. Glastechnische Tagung (Deutsche Glastechnische Gesellschaft e.V.) CY - Goslar, Germany DA - 06.06.2016 KW - Laser profilometry KW - 3D High-temperature shape screening KW - Sintering PY - 2016 AN - OPUS4-36510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -