TY - CONF A1 - Trappe, Volker A1 - Müller, Alexander A1 - Hickmann, Stefan T1 - Infinite life of CFRP evaluated non-destructively with X-ray-refraction topography in-situ mechanical loading N2 - Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles. T2 - 19th World Conference on Non-Destructive Testing CY - Munich, Germany DA - 13.06.2016 KW - CFRP KW - NDT KW - Fatigue KW - Damage evolution PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-375015 UR - https://www.ndt.net/?id=19360 SN - 978-3-940283-78-8 VL - 2016 SP - 1 EP - 9 PB - DGZFP CY - Berlin AN - OPUS4-37501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weise, Frank T1 - Influence of simultaneous cyclic loading and external alkali supply on the alkali-silica reaction in concrete pavements N2 - In recent years the German highway network has seen an increase in the occurrence of damage in concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastic reduction in life expectancy experienced by concrete pavements due to ASR, research activity in this field has notably increased. Until now the main research focus has been, alongside preventative measures in concrete technology, the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali supply on concrete pavements. The effects of pre-damage from the additionally interacting cyclic traffic loading had previously not been taken into consideration. Since 2011, a five-partner research group from the German Research Foundation has been pursuing research on the effects of simultaneous cyclic loading and external alkali supply on the destructive ASR in concrete pavements. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires a close interaction between experiments and their multi-scale modelling. This contribution aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a NaCl solution, with simultaneous tracking of crack development. Thereafter, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks with X-ray 3D-computed tomography. Additionally, the effects of fatigue-induced cracks on moisture and alkali transport were investigated using 3D-CT and Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment was then able to shed light on the influence of fatigue-induced pre-damage on the ASR. T2 - 15th International Conference on Alkali-Aggregate Reaction (ICAAR 2016) CY - Sao Paulo, Brazil DA - 03.07.2016 KW - Concrete pavements KW - Alkali-silica-reaction KW - Fatigue KW - Damage monitoring PY - 2016 AN - OPUS4-36950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Glaubitz, Steffen T1 - Influence of casting skin on fatigue lifetime of ferritic ductile cast iron N2 - The fatigue behaviour of cast iron is usually investigated on machined specimens. Components of cast iron, however, have a casting skin; therefore the investigation of the influence of the casting skin on the lifetime is of interest. To study this influence isothermal fatigue tests were carried out on heat-resisting spheroidal graphite cast iron EN GJS SiMo 4.05 in 4–point-bending set-up at 400 °C. Specimens with and without casting skin were investigated comparatively. The number of cycles to failure was significantly lower for specimens with casting skin. Metallographic investigations underline the reduction of lifetime caused by casting skin. KW - Cast iron KW - Casting skin KW - Fatigue KW - Lifetime PY - 2017 SN - 0025-5300 VL - 59 IS - 1 SP - 5 EP - 10 PB - Carl Hanser Verlag CY - München AN - OPUS4-38929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel T1 - Potential of martensitic stainless steel X5CrNiCuNb 16-4 as pipe steel in corrosive CCS environment N2 - Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Additionally fatigue tests were performed via push-pull tests with a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). Best corrosion resistance in the liquid phase is achieved via normalizing prior to exposure and hardening+tempering at 670 °C leads to lowest corrosion rates in the supercritical phase. With no regard to atmosphere discontinuously ellipsoidal surface corrosion regions appear after exposure of 4000 h and more. The endurance limit of X5CrNiCuNb16-4 measured in air is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa) The scatter range TN = 1:34 is disproportionately large contributing to an overall unusual corrosion behaviour. KW - Corrosion KW - CCS KW - Carbon storage KW - Aquifer KW - Heat treatment KW - Fatigue KW - Endurance limit PY - 2017 DO - https://doi.org/10.18178/ijesd.2017.8.7.998 SN - 2010-0264 VL - 8 IS - 7 SP - 466 EP - 473 AN - OPUS4-41863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David T1 - Impact of thermal loads on the damage onset of fiber reinforced plastics N2 - In this study, quasi-static material tests on unidirectional and multi-angle glass fiber reinforced epoxy laminates at ambient temperatures from -213 K to 353 K (-60 °C to +80 °C) are performed. In addition, neat resin is investigated under tension and compression loads at different temperatures. The coefficient of thermal expansion is determined for neat resin and unidirectional reinforced specimens. The dependence of the resin’s thermomechanical properties on the ambient temperature is shown. The point of damage onset at which first cracks appear within the matrix under quasi-static loading is investigated by means of optical grey scale analysis. The correlation between damage onset and effective matrix stress at different ambient temperatures is identified. An approach for the calculation of thermomechanical loads and the prediction of the damage onset by means of inverse calculations is presented. The impact of the strain blocking effect of the matrix is considered as well as residual thermal stresses due to curing and resin shrinkage. T2 - International Conference of Composite Materials 21, ICCM21 CY - Xi'an, China DA - 20.08.2017 KW - Fatigue KW - Composite KW - Thermomechanics KW - Fiber reinforced plastics PY - 2017 AN - OPUS4-42074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David A1 - Trappe, Volker T1 - Impact of thermal loads on the damage onset of fiber reinforced plastics N2 - In this study, quasi-static material tests on unidirectional and multi-angle glass fiber reinforced epoxy laminates at ambient temperatures from -213 K to 353 K (-60 °C to +80 °C) are performed. In addition, neat resin is investigated under tension and compression loads at different temperatures. The coefficient of thermal expansion is determined for neat resin and unidirectional reinforced specimens. The dependence of the resin’s thermomechanical properties on the ambient temperature is shown. The point of damage onset at which first cracks appear within the matrix under quasi-static loading is investigated by means of optical grey scale analysis. The correlation between damage onset and effective matrix stress at different ambient temperatures is identified. An approach for the calculation of thermomechanical loads and the prediction of the damage onset by means of inverse calculations is presented. The impact of the strain blocking effect of the matrix is considered as well as residual thermal stresses due to curing and resin shrinkage. T2 - ICCM21 - 21th International conference on composite materials CY - Xi'an, China DA - 20.08.2017 KW - Fatigue KW - Composite KW - Thermomechanics KW - Fiber reinforced plastics KW - Damage onset PY - 2017 SP - 1 EP - 12 AN - OPUS4-42075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unger, Jörg F. A1 - Kindrachuk, Vitaliy T1 - A Fourier transformation-based temporal integration scheme for viscoplastic solids subjected to fatigue deterioration N2 - Using continuum damage mechanics (CDM) for lifetime prediction requires numerical integration of evolving damage until the onset of failure. The primary challenge for the simulation of structural fatigue failure is caused by the enormous computational costs due to cycle-by-cycle temporal integration throughout the whole loading history, which is in the order of 103–107 cycles. As a consequence, most approaches circumvent this problem and use empirical methods such as Wöhler curves. They are well suited for approximating the lifetime, but they are not capable to capture a realistic degradation of the material including redistribution of stresses. The main objective of the paper is to provide a technique for finite element (FE) simulations of structures under fatigue loading while reducing computational costs. A Fourier transformation-based temporal integration (FTTI) scheme is proposed, which adapts the conventional FE method for modeling the viscoplastic deterioration in a structure subjected to cyclic loading. The response fields are represented by a Fourier series which assumes a temporal scale separation: a microchronological (short time) scale arises from the oscillatory loading and a macrochronological (long time) scale is due to the slow material relaxation resulting from yielding and damage evolution. The original dynamic boundary value problem (BVP) is approximated by the stationary BVP on the microchronological scale. Alternation of the displacement field on the macrochronological scale is correlated with evolution of the history variables by means of a high order adaptive cycle jump method. Performance and significant acceleration of the FE simulations is demonstrated at different loading scenarios for a constitutive damage model where the progressive damage accumulation is driven by viscoplastic yielding. KW - Fatigue KW - Accelerated time integration KW - Continuum damage mechanics KW - Fourier series PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.03.015 SN - 0142-1123 SN - 1879-3452 VL - 100 IS - 1 SP - 215 EP - 228 PB - Elsevier Ltd. AN - OPUS4-39616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boller, Ch. A1 - Mueller, Bernd R. A1 - Heckel, Thomas A1 - Starke, P. A1 - Gohlke, Daniel A1 - Venkat, R. S. A1 - Bruno, Giovanni T1 - Nonlinearities based inverse approach for the characterisation of the damage evaluation process in very high cycle fatigued CFRP specimens N2 - This paper focuses on the aspect on how damage evolution processes in composite materials and structures including matrix fracture, delamination, fibre-matrix debonding, and fibre fracture can be detected by taking advantage of the material’s inherit mechanical properties. These properties can be described on the basis of non-linear mechanical phenomena measurable as an inert frequency response signal. The approach is proposed as a means for residual life structural assessment specifically in the context of VHCF. T2 - The Seventh International Conference on Very High Cycle Fatigue - VHCF7 CY - Dresden, Germany DA - 03.07.2017 KW - Composite materials KW - Damage KW - Non-destructive testing KW - Fatigue KW - Structural simulation KW - Non-linear vibration PY - 2017 VL - 2017 SP - 1 EP - 8 PB - DVM AN - OPUS4-41102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krütt, Enno A1 - Weise, Frank A1 - Meng, Birgit ED - Ye, G. ED - Yuan, Y. ED - Romero Rodriguez, C. ED - Zhang, H. ED - Savija, B. T1 - Fatigue induced degradation in pavement concrete and its effect on the alkali-silica reaction N2 - In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced service life of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology i.e. the usage of low-alkali cements, the main research focus up to now has been on the development of performance-oriented testing procedures for ASR prevention. The effects of mechanicallyinduced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration. The assessment of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and corresponding multi-scale models. This contribution is focused on the experiments utilizing innovative testing techniques. The research is founded on a series of fatigue tests performed on large-scale beams with simultaneous tracking of the degradation process using non-destructive evaluation methods. Subsequently, smaller test specimens were extracted from the predamaged beams for further experiments. These experiments included investigation of the influence of fatigue-induced cracks on moisture and alkali transport. Subsequent storage of the small-scale test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced degradation on the ASR. The results show that the degradation process can be well observed with the test Setup developed for the fatigue experiments. Further, a small but noticeable increase of mass Transport due to fatigue-induced degradation was measured, which correspondingly indicated an increased ASR damage potential. T2 - 4th International Conference on Service Life Design for Infrastructures (SLD4) CY - Delft, The Netherlands DA - 27.08.2018 KW - Fatigue KW - Pavement KW - ASR KW - Concrete PY - 2018 SN - 978-2-35158-213-8 SP - 112 EP - 121 PB - RILEM Publication S.A.R.L. CY - Paris, France AN - OPUS4-46197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krütt, Enno T1 - Fatigue induced degradation in pavement concrete and its effect on the alkali-silica-reaction N2 - In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced service life of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology i.e. the usage of low-alkali cements, the main research focus up to now has been on the development of performance-oriented testing procedures for ASR prevention. The effects of mechanicallyinduced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration. The assessment of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and corresponding multi-scale models. This contribution is focused on the experiments utilizing innovative testing techniques. The research is founded on a series of fatigue tests performed on large-scale beams with simultaneous tracking of the degradation process using non-destructive evaluation methods. Subsequently, smaller test specimens were extracted from the predamaged beams for further experiments. These experiments included investigation of the influence of fatigue-induced cracks on moisture and alkali transport. Subsequent storage of the small-scale test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced degradation on the ASR. The results show that the degradation process can be well observed with the test Setup developed for the fatigue experiments. Further, a small but noticeable increase of mass Transport due to fatigue-induced degradation was measured, which correspondingly indicated an increased ASR damage potential. T2 - 4th International Conference on Service Life Design for Infrastructures (SLD4) CY - Delft, The Netherlands DA - 27.08.2018 KW - Fatigue KW - Pavement KW - ASR KW - Concrete PY - 2018 AN - OPUS4-46199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David A1 - Trappe, Volker T1 - Cyclic fatigue behavior of glass fiber reinforced epoxy resin at ambient and elevated temperatures N2 - The fatigue behavior of ±45° glass fiber reinforced epoxy resin under cyclic mechanical and constant thermal loading is investigated in this study. Tests at three different temperature levels in the range 296 K to 343 K have been performed in order to create S-N curves for each temperature level. The specimen damage is measured in-situ using optical grayscale analysis. The characteristic damage state (CDS) is evaluated for each specimen. It is shown that the point of CDS is suitable as a failure criterion to compare the resulting S-N curves. With micromechanical formulations, the temperature-dependent matrix effort is calculated for each stress-temperature level. In terms of matrix effort, the longest fatigue life is reached at high temperatures, while, in terms of stress, the lowest fatigue life is reached at the highest temperatures. T2 - ECCM18 - 18th European conference on composite materials CY - Athens, Greece DA - 24.06.2018 KW - Composite KW - Fatigue KW - Thermomechanics KW - Residual stresses KW - Temperature PY - 2018 SP - 1 EP - 7 PB - European society for composite materials AN - OPUS4-45338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraus, David T1 - Cyclic fatigue behavior of glass fiber reinforced epoxy resin at ambient and elevated temperatures N2 - The fatigue behavior of ±45° glass fiber reinforced epoxy resin under cyclic mechanical and constant thermal loading is investigated in this study. Tests at three different temperature levels in the range 296 K to 343 K have been performed in order to create S-N curves for each temperature level. The specimen damage is measured in-situ using optical grayscale analysis. The characteristic damage state (CDS) is evaluated for each specimen. It is shown that the point of CDS is suitable as a failure criterion to compare the resulting S-N curves. With micromechanical formulations, the temperature-dependent matrix effort is calculated for each stress-temperature level. In terms of matrix effort, the longest fatigue life is reached at high temperatures, while, in terms of stress, the lowest fatigue life is reached at the highest temperatures. T2 - ECCM18 - 18th European conference on composite materials CY - Athens, Greece DA - 24.06.2018 KW - Composite KW - Fatigue KW - Thermomechanics KW - Residual stresses KW - Temperature PY - 2018 AN - OPUS4-45346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kindrachuk, Vitaliy T1 - A novel computational method for efficient evaluation of structural fatigue N2 - The methods of computational damage mechanics are well-established for the description of degradation of materials under monotone loading. An extension to structural damage induced by cyclic loading is however significantly limited. This is due to enormous computational costs required to resolve each load cycle by conventional temporal incremental integration schemes while a typical fatigue loading history comprises between thousands and millions of cycles. Despite the permanent increase of computational resources and algorithmic performance, a successful approach is rather based on the development of novel multiscale in time integration schemes. A Fourier transformation-based temporal integration (FTTI) is represented, which takes advantage of temporal scale separation incorporated into the cycle jump method. The response fields are approximated by a Fourier series whose coefficients undergo the evolution on a long-time scale. This is correlated with the evolution of the history variables, including damage, by means of the adaptive cycle jump method of various orders. The necessary extrapolation rates are obtained from the underlying solution of a short-time scale problem, which results from the oscillatory boundary condition and fulfills the global equilibrium of the Fourier coefficients. In this way, a remarkable speedup is achieved because the number of cycles to be fully integrated dramatically decreases. The key idea behind the FTTI method is that the global in space equilibrium problem is linear since it is decoupled from the evolution equations. The latter are solved in the quadrature points under response fields prescribed throughout the whole load cycle. Consequently, integration of a single load cycle is much more efficient than the conventional single scale integration where the global equilibrium iteration and the local iteration of the evolution equations are coupled. This results in an additional speedup of the FTTI method. The performance of the FTTI technique is demonstrated for two different constitutive behaviors: a viscoplastic model with a damage variable governed by the local equivalent viscoplastic strain; a quasi-brittle response where the damage variable is driven by a non-local equivalent strain. The latter is implicitly introduced as proposed by Peerlings. Both, the explicit and implicit extrapolation schemes are validated. The FTTI solutions agree very well with the reference cycle-by -cycle solutions, while significantly reducing the computational costs. The adaptive determination of the jump length can properly recognize the particular responses throughout the fatigue loading history (stationary fatigue, acceleration of fatigue damage when approaching failure) as well as stress redistribution phenomena. T2 - International Fatigue International Fatigue International Fatigue International Fatigue International Fatigue International Fatigue Congress Congress Congress 2018 CY - Poitiers, France DA - 27.05.2018 KW - Fatigue KW - Accelerated integration scheme PY - 2018 AN - OPUS4-46975 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen T1 - Cyclic loading and creep-fatigue performance of P92 N2 - 9-12% Cr ferritic-martensitic stainless steels are widely used as high temperature construction materials in power plants due to their excellent creep and oxidation resistance. The growing share of renewable energy sources in power generation forces many of these plants into more flexible operation with frequent load shifts or shutdowns. These cyclic operation profiles constitute a major lifetime issue. The present contribution reports on current findings obtained in a multidisciplinary project which combines cyclic mechanical and cyclic oxidation testing of different 9-12% Cr grades with detailed microstructural analyses. Mechanical analyses are carried out on P92 and P91 steel grades to give an overview of softening phenomena and lifetimes obtained in isothermal cyclic loading (low cycle fatigue, LCF), non-isothermal cyclic loading (thermo-mechanical fatigue, TMF), and service-like combinations of creep and fatigue periods. Complementary microstructural investigations by scanning and transmission electron microscopy plus EBSD are used for phase identification, substrate/oxide interface characterization and quantification of the microstructure evolution under cyclic conditions. T2 - 44th MPA-Seminar CY - Leinfelden/Stuttgart, Germany DA - 17.10.2018 KW - Ferritic-martensitic steels KW - Fatigue KW - Creep-fatigue PY - 2018 AN - OPUS4-47116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Alexander A1 - Trappe, Volker A1 - Hickmann, Stefan A1 - Ortwein, H.-P ED - Christ, Hans-Jürgen T1 - Investigation of the infinite life of fibre-reinforced plastics using X-ray refraction topography for the in-situ, nondestructive evaluation of micro-structural degradation processes during cyclic fatigue loading N2 - The described investigation of carbon-fibre-reinforced plastics (CFRP) documents that damage evolution can be observed by means of X-ray refractography. Comparative investigations with synchrotron technique on CFRP and grey-scale analysis on glass fibre-reinforced-plastics (GFRP) confirm these results. Moreover it was found that the fracture mechanical properties of the matrix system influence damage nucleation and propagation in the laminate during static and fatigue loads. Single-step fatigue tests were carried out on Laminates with RIM135 and LY556 matrix systems made from non-crimped fabric (NCF) or twill weave in different fibre orientations. The damage to the LY556 laminates was characterized by laminate cracks growing rapidly over the whole specimen width, whereas the damage on the RIM135 laminates was characterized by an earlier onset of micro-cracking followed by laminate cracks. The specimens were fatigued up to 108 (very high cycle fatigue (VHCF) regime) load cycles. S-N-curves of damage initiation were drawn and boundaries were identified for endurance within the VHCF regime. A phenomenology based model focusing on matrix stress was applied to reproduce the first inter-fibre failure (IFF) under static and fatigue loads. KW - Carbon fibre-reinforced-plastics KW - Fatigue KW - Damage evolution KW - X-ray refractography KW - Very high cycle fatigue PY - 2018 SN - 978-3-658-24531-3 DO - https://doi.org/10.1007/978-3-658-24531-3 VL - 2018 SP - 417 EP - 439 PB - Springer Spektrum CY - Wiesbaden ET - 1. Auflage AN - OPUS4-50096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Pirskawetz, Stephan A1 - Thiele, Marc A1 - Rogge, Andreas T1 - Experimental investigation of size effect on fatigue behavior of high strength concrete - concept and preliminary results N2 - The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring. T2 - 5th International fib Congress: Better - Smarter - Stronger CY - Melbourne, Australia DA - 08.10.2018 KW - Acoustic emission testing KW - Compressive cyclic loading KW - Fatigue KW - High-strength concrete KW - Non-destructive testing KW - Size effect KW - Slenderness effect KW - Ultrasonic testing PY - 2018 SN - 978-1-877040-14-6 SP - 1 EP - 11 AN - OPUS4-46408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian T1 - Experimental investigation of size effect on fatigue behavior of high strength concrete - concept and preliminary results N2 - The worldwide spread of windfarms brings new challenges, especially for concrete structures as a part of towers, connecting joints and foundations of wind turbines. High-cyclic loadings in such structures lead to a high relevance of the subject of fatigue. A proper assessment of the fatigue strength of concrete demands therefore a basis of reliable experimental data and the development of standardized testing methods. This article presents first results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung) which is a part of a joint project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject investigates the effects of size and slenderness of the specimens on the fatigue behaviour of high strength concrete at different stress levels. Not only the fatigue strength, but also the fatigue process itself is monitored by means of several measurement methods. Strain measurements are used to calculate the load dependent elastic modulus in the fatigue hysteresis as indicators for fatigue development. Furthermore, the application of non-destructive methods like acoustic emission analysis and ultrasonic measurement in laboratory tests gives a deeper insight into damage processes under cyclic loading. The results shall be used to improve design rules for concrete members under fatigue load and to develop or improve non-destructive techniques for in-service structural health monitoring. T2 - 5th International fib Congress: Better - Smarter - Stronger CY - Melbourne, Australia DA - 08.10.2018 KW - Acoustic emission testing KW - Compressive cyclic loading KW - Fatigue KW - High-strength concrete KW - Non-destructive testing KW - Size effect KW - Slenderness effect KW - Ultrasonic testing PY - 2018 AN - OPUS4-46366 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindrachuk, Vitaliy A1 - Fedelich, Bernard A1 - Rehmer, Birgit A1 - Peter, Frauke T1 - Computational methods for lifetime prediction of metallic components under high-temperature fatigue N2 - The issue of service life prediction of hot metallic components subjected to cyclic loadings is addressed. Two classes of lifetime models are considered, namely, the incremental lifetime rules and the parametric models governed by the fracture mechanics concept. Examples of application to an austenitic cast iron are presented. In addition, computational techniques to accelerate the time integration of the incremental models throughout the fatigue loading history are discussed. They efficiently solve problems where a stabilized response of a component is not observed, for example due to the plastic strain which is no longer completely reversed and accumulates throughout the fatigue history. The performance of such an accelerated Integration technique is demonstrated for a finite element simulation of a viscoplastic solid under repeating loading–unloading cycles. KW - Fatigue KW - Incremental lifetime models KW - Finite element analysis PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-481215 UR - https://www.mdpi.com/2075-4701/9/4/390 DO - https://doi.org/10.3390/met9040390 SN - 2075-4701 VL - 9 IS - 4 SP - 390, 1 EP - 24 PB - mdpi CY - Basel, Switzerland AN - OPUS4-48121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Meng, Birgit A1 - Rogge, Andreas T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete fpr Energy Infrastructure under Severe Operating Conditions CY - Ghent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 SN - 978-9-463-88638-3 SP - 1 EP - 4 AN - OPUS4-49500 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Frei, Vivian T1 - Characterizing the Fatigue Behavior of High-Performance Concrete for Wind Energy Structures N2 - Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally. Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring. T2 - LORCENIS - Long Lasting Reinforced Concrete for Energy Infrastructue under Severe Operating Conditions CY - Gent, Belgium DA - 10.09.2019 KW - Compressive Cyclic loading KW - Fatigue KW - High-strength concrete KW - Non destructive testing KW - Ultrasonic testing PY - 2019 AN - OPUS4-49474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -