TY - JOUR A1 - Tambara, R. F. A1 - Durlo Tambara, Luís Urbano A1 - Venquiaruto, S. D. A1 - Pereira da Costa, F. B. T1 - Evaluation of the mechanical performance and capillary absorption of concretes with incorporation of crystallizing admixtures and subjected to damage at early ages T1 - Avaliação do desempenho mecânico e absorção capilar de concretos com incorporação de aditivos cristalizante submetidos a danos nas primeiras idades N2 - This study assessed the self-healing phenomenon in the mechanical properties and capillary absorption of structural concretes. Two crystalline powder additives were evaluated, dosed according to the manufacturers’ recommendations. Crystalline additives increase the density of the C-S-H gel and form insoluble crystals, effectively blocking fissures. Three concrete mixes were produced: a reference mix, additive-X with 0.8%, and additive-Y with 2.0%, relative to the mass of cement. 75% of the rupture load was applied at 3- and 14-days to induce microfissures for comparison with the reference mix. Subsequently, self-healing was assessed at 28- and 76-days. The property of axial compressive strength was determined at 28-days, revealing that crystalline additives contributed to an average increase of 12% in this property. While the age of loading did not significantly impact axial compressive strength, there were significant variations among the types of additives studied, as indicated by ANOVA. Water absorption properties through capillarity were evaluated at 28- and 76-days, showing an average reduction of 42% in water absorption due to the use of crystalline additives. In conclusion, the inclusion of crystalline additives positively contributed to the self-healing of the studied concretes, suggesting a partial recovery of microfissures. N2 - Esta pesquisa avaliou o fenômeno de autocicatrização nas propriedades mecânicas e absorção capilar de concretos estruturais. Foram avaliados dois aditivos cristalizantes em pó, dosados de acordo com o teor recomendado pelos fabricantes. Aditivos cristalizantes aumentam a densidade do gel C-S-H e formam cristais insolúveis, bloqueando fissuras. Três traços de concreto foram produzidos: referência, aditivo-X com 0,8% e aditivo-Y com 2,0% em relação a massa do cimento. Aplicou-se 75% da carga de ruptura aos 3- e 14-dias para gerar microfissuras e comparar com a referência. Posteriormente, a autocicatrização foi avaliada aos 28- e 76-dias. A propriedade de resistência à compressão axial foi determinada aos 28-dias, revelando que os aditivos cristalizantes contribuíram para um aumento médio de 12% desta propriedade. A idade do carregamento dos concretos não apresentou um impacto significativo na resistência à compressão axial, mas apontou resultados significativos entre os tipos de aditivos estudados, conforme ANOVA. As propriedades de absorção de água por capilaridade foram avaliadas aos 28- e 76-dias, indicando uma redução de absorção de água média de 42% devido ao uso dos aditivos cristalizantes. Em conclusão, a incorporação dos aditivos cristalizantes contribuiu de maneira positiva para a autocicatrização dos concretos estudados, indicando uma recuperação parcial das microfissuras. KW - Self-healing KW - Crystalline admixture KW - Concrete KW - Cracks PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599140 DO - https://doi.org/10.1590/1517-7076-RMAT-2023-0355 SN - 1517-7076 VL - 29 IS - 1 SP - 1 EP - 20 CY - Rio de Janeiro AN - OPUS4-59914 LA - por AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - C. Pardo Pérez, L. A1 - Arndt, A. A1 - Stojkovikj, S. A1 - Y. Ahmet, I. A1 - T. Arens,, J. A1 - Dattila, F. A1 - Wendt, R. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Radtke, Martin A1 - Davies, V. A1 - Höflich, K. A1 - Köhnen, E. A1 - Tockhorn, P. A1 - Golnak, R. A1 - Xiao, J. A1 - Schuck, G. A1 - Wollgarten, M. A1 - López, N. A1 - T. Mayer, M. T1 - Determining Structure-Activity Relationships in Oxide Derived CuSn Catalysts During CO2 Electroreduction Using X-Ray Spectroscopy N2 - The development of earth-abundant catalysts for selective electrochemical CO2 conversion is a central challenge. Cu-Sn bimetallic catalysts can yield selective CO2 reduction toward either CO or formate. This study presents oxide-derived Cu-Sn catalysts tunable for either product and seeks to understand the synergetic effects between Cu and Sn causing these selectivity trends. The materials undergo significant transformations under CO2 reduction conditions, and their dynamic bulk and surface structures are revealed by correlating observations from multiple methods—X-ray absorption spectroscopy for in situ study, and quasi in situ X-ray photoelectron spectroscopy for surface sensitivity. For both types of catalysts, Cu transforms to metallic Cu0 under reaction conditions. However, the Sn speciation and content differ significantly between the catalyst types: the CO-selective catalysts exhibit a surface Sn content of 13 at. % predominantly present as oxidized Sn, while the formate-selective catalysts display an Sn content of ≈70 at. % consisting of both metallic Sn0 and Sn oxide species. Density functional theory simulations suggest that Snδ+ sites weaken CO adsorption, thereby enhancing CO selectivity, while Sn0 sites hinder H adsorption and promote formate production. This study reveals the complex dependence of catalyst structure, composition, and speciation with electrochemical bias in bimetallic Cu catalysts. KW - Electrochemical CO2 conversion KW - Cu catalysts KW - X-ray absorption spectroscopy PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-547116 DO - https://doi.org/10.1002/aenm.202103328 SN - 1614-6832 VL - 12 IS - 5 SP - 2103328 PB - Wiley-VCH GmbH AN - OPUS4-54711 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kunkel, B. A1 - Kabelitz, Anke A1 - de Oliveira Guilherme Buzanich, Ana A1 - Wohlrab, S. T1 - Increasing the Efficiency of Optimized V-SBA-15 Catalysts in the Selective Oxidation of Methane to Formaldehyde by Artificial Neural Network Modelling N2 - The present study investigates the possibility of improving the selective oxidation of methane to formaldehyde over V-SBA-15 catalysts in two different ways. In a classical approach of catalyst optimization, the in situ synthesis of V-SBA-15 catalysts was optimized with regard to the applied pH value. Among the set of catalysts synthesized, a higher amount of incorporated vanadium, a higher content of polymeric VOx species as well as a less ordered structure of the support material were observed by increasing the pH values from 2.0 to 3.0. An optimum in performance during the selective oxidation of methane to formaldehyde with respect to activity and selectivity was found over V-SBA-15 prepared at a pH value of 2.5. With this knowledge, we have now evaluated the possibilities of reaction control using this catalyst. Specifically, artificial neural network modelling was applied after the collection of 232 training samples for obtaining insight into the influence of different reaction parameters (temperature; gas hourly space velocity (GHSV); and concentration of O2, N2 and H2O) onto methane conversion and selectivity towards formaldehyde. This optimization of reaction conditions resulted in an outstanding high space-time yield of 13.6 kgCH2O∙kgcat∙h−1 KW - Artificial neural network modelling KW - Selective oxidation KW - Molecular VOx catalysts KW - Formaldehyde PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517420 DO - https://doi.org/10.3390/catal10121411 VL - 10 IS - 12 SP - 1411 PB - MDPI AN - OPUS4-51742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - de Olivera, Paulo A1 - Michalchuk, Adam A1 - de Oliveira Guilherme Buzanich, Ana A1 - Bienert, Ralf A1 - Torresi, R. A1 - Camargo, P. A1 - Emmerling, Franziska T1 - Tandem X-ray absorption spectroscopy and scattering for in situ time-resolved monitoring of gold nanoparticle mechanosynthesis N2 - Current time-resolved in situ approaches limit the scope of mechanochemical investigations possible. Here we develop a new, general approach to simultaneously follow the evolution of bulk atomic and electronic structure during a mechanochemical synthesis. This is achieved by coupling two complementary synchrotron-based X-ray methods: X-ray absorption spectroscopy (XAS) and X-ray diffraction. We apply this method to investigate the bottom-up mechanosynthesis of technologically important Au micro and nanoparticles in the presence of three different reducing agents, hydroquinone, sodium citrate, and NaBH4. Moreover, we show how XAS offers new insight into the early stage generation of growth species (e.g. monomers and clusters), which lead to the subsequent formation of nanoparticles. These processes are beyond the detection capabilities of diffraction methods. This combined X-ray approach paves the way to new directions in mechanochemical research of advanced electronic materials. KW - Mechanochemistry KW - XANES KW - X-ray diffraction KW - Nano particles PY - 2020 DO - https://doi.org/10.1039/d0cc03862h SN - 1364-548X VL - 56 SP - 10329 EP - 10332 PB - Royal Society of Chemistry AN - OPUS4-51760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Sebastian A1 - Gluth, Gregor ED - Rossignol, S. ED - Gluth, Gregor T1 - Unraveling the hardening mechanism during laser-induced slip casting of lithium aluminate-microsilica slurry N2 - Additive manufacturing (AM) of alkali-activated materials is a promising method for producing ceramic precursors, construction elements and other parts. A recently introduced AM process is laser-induced slip casting of lithium aluminate/microsilica slurries, which yields parts with excellent mechanical strengths. To clarify the underlying mechanisms, μ-Raman spectroscopy was applied to parts produced by the process, and the dissolution and hydration of lithium aluminate was studied inter alia using conventional and in-situ X-ray diffraction. The results show that significant dissolution of lithium aluminate occurs, particularly at increased temperatures during laser interaction, which leads to an increase of pH and precipitation of an akopovaite-like Li-Al-CO3 layered double hydroxide. The increase of the pH is likely to induce dissolution of the microsilica and possibly formation of a hydrous lithium aluminosilicate gel. These observations explain the strength evolution of the studied parts and can also aid the development and improvement of related AM methods. KW - Alkali-activated materials KW - Additive manufacturing KW - Laser-induced slip casting KW - Lithium KW - Layered double hydroxide PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520557 DO - https://doi.org/10.1016/j.oceram.2021.100060 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-52055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Smekhova, A. A1 - Kuzmin, A. A1 - Siemensmeyer, K. A1 - Luo, C. A1 - Taylor, J. A1 - Thakur, S. A1 - Radu, F. A1 - Weschke, E. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Xiao, B. A1 - Savan, A. A1 - Yusenko, Kirill A1 - Ludwig, A. T1 - Local structure and magnetic properties of a nanocrystalline Mn-rich Cantor alloy thin film down to the atomic scale N2 - The huge atomic heterogeneity of high-entropy materials along with a possibility to unravel the behavior of individual components at the atomic scale suggests a great promise in designing new compositionally complex systems with the desired multi-functionality. Herein, we apply multi-edge X-ray absorption spectroscopy (extended X-ray absorption fine structure (EXAFS), X-ray absorption near edge structure (XANES), and X-ray magnetic circular dichroism (XMCD)) to probe the structural, electronic, and magnetic properties of all individual constituents in the single-phase face-centered cubic (fcc)-structured nanocrystalline thin film of Cr20Mn26Fe18Co19Ni17 (at.%) high-entropy alloy on the local scale. The local crystallographic ordering and component-dependent lattice displacements were explored within the reverse Monte Carlo approach applied to EXAFS spectra collected at the K absorption edges of several constituents at room temperature. A homogeneous short-range fcc atomic environment around the absorbers of each type with very similar statistically averaged interatomic distances (2.54–2.55 Å) to their nearest-neighbors and enlarged structural relaxations of Cr atoms were revealed. XANES and XMCD spectra collected at the L2,3 absorption edges of all principal components at low temperature from the oxidized and in situ cleaned surfaces were used to probe the oxidation states, the changes in the electronic structure, and magnetic behavior of all constituents at the surface and in the sub-surface volume of the film. The spin and orbital magnetic moments of Fe, Co, and Ni components were quantitatively evaluated. The presence of magnetic phase transitions and the co-existence of different magnetic phases were uncovered by conventional magnetometry in a broad temperature range. KW - Magnetism KW - High-entropy alloys KW - Reverse Monte Carlo (RMC) KW - Element-specific spectroscopy KW - Extended X-ray absorption fine structure (EXAFS), KW - X-ray magnetic circular dichroism (XMCD), PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578254 DO - https://doi.org/10.1007/s12274-022-5135-3 SN - 1998-0124 SP - 5626 PB - Springer AN - OPUS4-57825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lima, G. T. S. A1 - Silvestro, L. A1 - Durlo Tambara, Luís Urbano A1 - Cheriaf, M. A1 - Rocha, J. C. T1 - Autonomous Self-Healing Agents in Cementitious Materials: Parameters and Impacts on Mortar Properties N2 - The concept of self-healing materials and the development of encapsulated curing agents represent a cutting-edge approach to enhancing the longevity and reducing the maintenance costs of cementitious structures. This systematic literature review aims to shed light on the parameters involved in the autonomous self-healing of cementitious materials, utilizing various encapsulated healing agents such as pellets, granules, and capsules. This review also identifies and selects studies that offer additional insights into the efficacy of the self-healing process in cementitious materials and the influence of these specific encapsulated healing agents on the physical mechanical properties of mortars. This comprehensive approach provides a deep understanding of the interplay between self-healing and the physical–mechanical properties of mortars containing these encapsulated healing agents. The main findings indicate that the cement-to-sand ratio, characteristics of fine aggregates, and encapsulation methods significantly impact crack control, self-healing efficiency, and properties of mortar in both fresh and hardened states. The content of encapsulated healing agents within the cementitious matrix affects both the initial workability or flow and subsequent mechanical properties. While pellets coated with PVA film typically reduce workability in the fresh state and compressive strength, capsules coated with Portland cement and sodium silicate mitigate these effects and improve crack sealing in fresh and hardened states without compromising the self-healing capacity of cracks. The three-point flexural test has emerged as the preferred method for a pre-crack assessment over 28 days, with variations depending on the type of healing agent used. As noted in the literature, water has been identified as the optimal environment for autonomous healing. These findings underscore the potential of encapsulation techniques to enhance self-healing capabilities through the controlled release of agents within the cementitious matrix, thereby advancing the research on and development of intelligent construction materials and increasing the durability of cement-based structures. KW - Self-healing cementitious composite KW - Encapsulated curing agents KW - Pellets KW - Granules KW - Capsules KW - Physical–mechanical properties KW - Autonomous self-healing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611860 DO - https://doi.org/10.3390/buildings14072000 SN - 2075-5309 VL - 14 IS - 7 SP - 1 EP - 23 PB - MDPI CY - Basel AN - OPUS4-61186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Shasmal, Nilanjana T1 - Effects of Direct femtosecond laser writing on chloroborosilicate glasses doped with Eu3+/Eu2+ and CdS quantum dots N2 - Femtosecond (fs) direct laser writing (DLW) is a promising technique for developing nano-inhomogeneous materials with advanced optical properties and for fabricating novel photonic devices such as integrated waveguides, ultrafast optical switches, phase plates, and 3D optical memory. In this study, DLW was applied to chloroborosilicate glasses that were singly and co-doped with Eu and CdS quantum dots (QDs). The glasses were laser-treated within a very narrow range of experimental conditions, resulting in laser-inscribed sites exhibiting enhanced emission, similar to the glass-ceramics crystallized from the as-prepared glass. In the regions crystalized by DLW a significant reduction of Eu3+ to Eu2+ was verified by photoluminescence spectroscopy. However, the characteristics of the emission bands of Eu2+ changed markedly in the laser-treated sites as compared to the emission spectra of the same glass crystallized by heat treatment. A considerable redshift and splitting of the emission band were observed, attributed to changes in the surrounding environment of the rare earth (RE) ions which was, in turn, attributed to an alteration in the coordination number of Ba2 + and/or Eu2+ as a result of the high-power laser treatment. Although there was an issue with homogeneity of the glass in the micro-level, which restricts some of the aspects of the DLW, these findings suggest the potential for structural modifications through laser treatment, which could be harnessed to create new functionalities for advanced optical applications. T2 - ICG 2025 (27th International Congress on Glass) CY - Kolkata, India DA - 20.01.2025 KW - Femtosecond direct laser writing KW - DLW KW - CdS quantum dots KW - Eu/CdS co-doped glass PY - 2025 AN - OPUS4-65285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quosdorf, Heike T1 - Digital object identifier for additively manufactured parts as software package N2 - A method to uniquely identify samples without printed or handwritten labels is an advantage not just for additively manufactured parts. To kickstart industry use cases, it is also important to provide a ready-made implementation kit. Following an open-science and open-source software approach Germanys Federal Institute for Materials Research and Testing (BAM) seeks to promote digital solutions of ongoing research projects. With this software package a novel method based on microstructural features as identifiers – DOI4AM (digital object identifier for additively manufactured parts) – will be explained alongside its implementation as open-source Python software package. The digital object identifier (DOI) links product data clearly and forgery-proof with real components. Its implementation helps to identify and securely authenticate additively manufactured components during its product life cycle by using characteristic microstructure features - just like a fingerprint. To calculate the DOI fingerprint, a few preprocessing steps need to be performed to detect the uniquely distributed microstructure features that occur during the 3D printing process. A go-through guide shows the preprocessing steps that include CT image capturing, feature segmentation, and data distribution with CSV files. While all steps can be followed along in a Jupyter notebook, the software package includes an application for creating and checking of previously created fingerprints, as well, as a containerized API (application programming interface) service for implementation in existing software platforms or workflows. While data visualization is crucial to understanding the methodology and an essential tool to check for data correctness, an implementation in an industry use case needs to be slim and resource efficient. Therefor the software’s API can be used as an independent service. The project's industry partner proofs its first successful implementation in their digital product passport web solution PASS-X. T2 - AI MSE 2025 CY - Bochum, Germany DA - 18.11.2025 KW - Authentication KW - Unique identification KW - Digital object identifier KW - Additive Manufacturing KW - Non-destructive testing KW - Open Source Software KW - Digital fingerprint KW - X-ray Computed Tomography KW - Open Science PY - 2025 AN - OPUS4-65293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sterthaus, Jens A1 - Ballheimer, Viktor A1 - Kuschke, Christian A1 - Wille, Frank T1 - Numerical analysis of bolted trunnion systems of packages for radioactive materials N2 - Packages for the transport of radioactive material are generally equipped with particular components for crane operations and supporting the package during transport. As an example of such components the bolted trunnion system of heavy packages are analysed in this paper. According to the German guideline BAM-GGR 012 created by the BAM Federal Institute for Materials Research and Testing for analysis and assessment of bolted lid and trunnion Systems, the finite element (FE) method is to be used preferably in the analysis of such kind of structures to obtain more accurate and detailed Information about their stressing. The FE model of a trunnion System should include the trunnion itself, the bolts and an appropriate part of the packaging wall with necessary contact conditions on all interfaces between these components. The use of solid finite elements, which is generally recommended in the BAM-GGR 012 guideline, leads to local stress and strain fields as a result of the calculation. The modelling strategy, e.g. the way of modelling interaction between the components of the trunnion System, has an essential impact on these local values. The effect of different assumptions in a FE model is demonstrated in this paper using the calculation results for a reference trunnion System. The approaches for preparation and Interpretation of results in connection with local or nominal assessment criteria are discussed as well. T2 - ASME 2012 Pressure Vessels and Piping Division Conference - PVP 2012 CY - Toronto, Ontario, Canada DA - 15.07.2012 KW - Bolted trunnion KW - German guideline BAM-GGR 012 KW - Local stress and strain fields KW - Local and nominal assessment criteria PY - 2012 SP - 1 EP - 6 PB - American Society of Mechanical Engineers (ASME) CY - New York, NY AN - OPUS4-26835 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fortes Martin, R. A1 - Thünemann, Andreas A1 - Stockmann, Jörg Manfred A1 - Radnik, Jörg A1 - Koetz, J. T1 - From Nanoparticle Heteroclusters to Filament Networks by Self-Assembly at the Water–Oil Interface of Reverse Microemulsions N2 - Surface self-assembly of spherical nanoparticles of sizes below 10 nm into hierarchical heterostructures is under arising development despite the inherent difficulties of obtaining complex ordering patterns on a larger scale. Due to template-mediated interactions between oil-dispersible superparamagnetic nanoparticles (MNPs) and polyethylenimine-stabilized gold nanoparticles (Au(PEI)NPs) at the water–oil interface of microemulsions, complex nanostructured films can be formed. Characterization of the reverse microemulsion phase by UV–vis absorption revealed the formation of heteroclusters from Winsor type II phases (WPII) using Aerosol-OT (AOT) as the surfactant. SAXS measurements verify the mechanism of initial nanoparticle clustering in defined dimensions. XPS suggested an influence of AOT at the MNP surface. Further, cryo-SEM and TEM visualization demonstrated the elongation of the reverse microemulsions into cylindrical, wormlike structures, which subsequently build up larger nanoparticle superstructure arrangements. Such WPII phases are thus proven to be a new form of soft template, mediating the self-assembly of different nanoparticles in hierarchical network-like filaments over a substrate during solvent evaporation. KW - Small-angle X-ray scattering KW - SAXS KW - Nanoparticle KW - Nano structure PY - 2021 DO - https://doi.org/10.1021/acs.langmuir.1c01348 VL - 37 IS - 29 SP - 8876 EP - 8885 PB - American Chemical Society AN - OPUS4-53034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Steppan, Enrico A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - High-energy synchrotron study of the stress-strain behavior of hydrogen-charged high strength steel N2 - The ambition for light weight construction while simultaneously increasing the loading capacity is a main aim of many industries such as crane, vehicle, bridge construction, shipbuilding and plant construction. This aim is achieved by application of high strength structural steels with yield strengths of up to 1300 MPa. The plate thickness can be reduced and consequently the service load is increased. High strength structural steels are quenched and tempered and/or even thermo-mechanically processed. Their superior properties are due to precipitations formed by micro alloying elements finely dispersed in a martensitic matrix. The aim of this study was to observe the influence of hydrogen in the microstructure of high strength structural steel with the yield strength of 1300 MPa by using diffraction methods. Energy dispersive X-ray diffraction (EDXRD) available at the EDDI beam line of the HZB in Berlin Germany was utilized to compare the stress-strain behavior of samples exhibiting varying amounts of hydrogen during tensile loading. T2 - Visual-JW2012 - International Symposium on Visualization in Joining and Welding Science through Advanced Measurements and Simulation CY - Osaka, Japan DA - 28.11.2012 KW - High strength structural steel KW - Hydrogen diffusion KW - Hydrogen assisted cold cracking KW - Energy dispersive X-ray diffraction PY - 2012 IS - IWIS-17 SP - 228 EP - 229 PB - Joining and Welding Research Institute (JWRI) CY - Osaka AN - OPUS4-27396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sterthaus, Jens T1 - Numerical analysis of bolted trunnion systems of packages for radioactive materials T2 - ASME 2012 Pressure Vessels and Piping Division Conference - PVP 2012 CY - Toronto, Ontario, Canada DA - 15.07.2012 PY - 2012 AN - OPUS4-26811 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tu, Z. A1 - Donskyi, Ievgen A1 - Qiao, H. A1 - Zhu, Z. A1 - Unger, Wolfgang A1 - Hackenberger, C. P. R. A1 - Chen, W. A1 - Adeli, M. A1 - Haag, R. T1 - Graphene Oxide-Cyclic R10 Peptide Nuclear Translocation Nanoplatforms for the Surmounting of Multiple-Drug Resistance N2 - Multidrug resistance resulting from a variety of defensive pathways in Cancer has become a global concern with a considerable impact on the mortality associated with the failure of traditional chemotherapy. Therefore, further research and new therapies are required to overcome this challenge. In this work, a cyclic R10 peptide (cR10) is conjugated to polyglycerol-covered nanographene oxide to engineer a nanoplatform for the surmounting of multidrug resistance. The nuclear translocation of the nanoplatform, facilitated by cR10 peptide, and subsequently, a laser-triggered release of the loaded doxorubicin result in efficient anticancer activity confirmed by both in vitro and in vivo experiments. The synthesized nanoplatform with a combination of different features, including active nucleus-targeting, highloading capacity, controlled release of cargo, and photothermal property, provides a new strategy for circumventing multidrug resistant cancers. KW - Graphen Oxide KW - Nanoplatform KW - Cancer PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-510061 DO - https://doi.org/10.1002/adfm.202000933 VL - 30 IS - 35 SP - 2000933 PB - Wiley VCH AN - OPUS4-51006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kulka, M.W. A1 - Nie, C. A1 - Nickl, P. A1 - Kerkhoff, Y. A1 - Garg, A. A1 - Salz, D. A1 - Radnik, Jörg A1 - Grunwald, I. A1 - Haag, R. T1 - Surface-Initiated Grafting of Dendritic Polyglycerol from Mussel-Inspired Adhesion-Layers for the Creation of Cell-Repelling Coatings N2 - Biofouling is a major challenge in the application of textiles, biosensors, and biomedical implants. In the current work, a straightforward method for the solvent-free polymerization of antifouling dendritic polyglycerol (dPG) from mussel-inspired dendritic polyglycerol (MI-dPG) coatings on hydrophilic titanium dioxide (TiO2) and hydrophobic polydimethylsiloxane (PDMS) is reported. Surface characterization is performed by static water contact angle (CA) measurements, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Significant lower CA values are obtained after dPG grafting from MI-dPG-coated TiO2 and MI-dPG coated PDMS. Furthermore, XPS shows a time-dependent increase of the CO bond content upon dPG grafting from MI-dPG-coated TiO2 and MI-dPG-coated PDMS. Analysis of the surface morphology by SEM shows a clear time-dependent increase in the surface roughness upon dPG grafting from MI-dPG-coated TiO2 and MIdPG-coated PDMS. When the viability of two adhesive cell types is studied via LIVE/DEAD staining, a strong reduction in the cell density is observed after the dPG grafting from MI-dPG-coated TiO2 and MI-dPG-coated PDMS (a decrease of >95% in all cases). The combined results show that biocompatible but highly cell-repelling surfaces are efficiently constructed via the grafting of dPG from MI-dPG-coated TiO2 and MI-dPG-coated PDMS. KW - Repelling surface coatings KW - Dendritic polyglycerol KW - Mussel-inspired adhesives KW - Surface-initated grafting PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-516590 DO - https://doi.org/10.1002/admi.202000931 SN - 2196-7350 VL - 7 IS - 24 SP - 931 PB - Wiley VCH AN - OPUS4-51659 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weigert, Florian A1 - Müller, A. A1 - Häusler, I. A1 - Geißler, Daniel A1 - Skroblin, D. A1 - Unger, Wolfgang A1 - Radnik, Jörg A1 - Resch-Genger, Ute T1 - Combining HR‑TEM and XPS to elucidate the core–shell structure of ultrabright CdSe/CdS semiconductor quantum dots N2 - Controlling thickness and tightness of surface passivation shells is crucial for many applications of core–shell nanoparticles (NP). Usually, to determine shell thickness, core and core/shell particle are measured individually requiring the availability of both nanoobjects. This is often not fulfilled for functional nanomaterials such as many photoluminescent semiconductor quantum dots (QD) used for bioimaging, solid state lighting, and display technologies as the core does not show the applicationrelevant functionality like a high photoluminescence (PL) quantum yield, calling for a whole nanoobject approach. By combining high-resolution transmission electron microscopy (HR-TEM) and X-ray photoelectron spectroscopy (XPS), a novel whole nanoobject approach is developed representatively for an ultrabright oleic acid-stabilized, thick shell CdSe/CdS QD with a PL quantum yield close to unity. The size of this spectroscopically assessed QD, is in the range of the information depth of usual laboratory XPS. Information on particle size and monodispersity were validated with dynamic light scattering (DLS) and small angle X-ray scattering (SAXS) and compared to data derived from optical measurements. In addition to demonstrating the potential of this novel whole nanoobject approach for determining architectures of small nanoparticles, the presented results also highlight challenges faced by different sizing and structural analysis methods and method-inherent uncertainties. KW - Photoluminescence KW - Single particle KW - Microscopy KW - Particle architecture KW - Thickness KW - SAXS KW - Shell KW - XPS KW - TEM KW - Semiconductor KW - Quantum dot KW - Photophysics KW - Quantum yield PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517911 DO - https://doi.org/10.1038/s41598-020-77530-z VL - 10 IS - 1 SP - 20712 PB - Springer Nature AN - OPUS4-51791 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Krahl, T. A1 - Radnik, Jörg A1 - Wagner, Andreas A1 - Werner, W. S. M. A1 - Ritter, B. A1 - Kemnitz, E. A1 - Unger, Wolfgang T1 - Chemical in-depth analysis of (Ca/Sr)F2 core–shell like nanoparticles by X-ray photoelectron spectroscopy with tunable excitation energy N2 - The fluorolytic sol–gel synthesis is applied with the intention to obtain two different types of core–shell nanoparticles, namely, SrF2–CaF2 and CaF2–SrF2. In two separate fluorination steps for core and shell formation, the corresponding metal lactates are reacted with anhydrous HF in ethylene glycol. Scanning transmission electron microscopy (STEM) and dynamic light scattering (DLS) confirm the formation of particles with mean dimensions between 6.4 and 11.5 nm. The overall chemical composition of the particles during the different reaction steps is monitored by quantitative Al Kα excitation X-ray photoelectron spectroscopy (XPS). Here, the formation of stoichiometric metal fluorides (MF2) is confirmed, both for the core and the final core–shell particles. Furthermore, an in-depth analysis by synchrotron radiation XPS (SR-XPS) with tunable excitation energy is performed to confirm the core–Shell character of the nanoparticles. Additionally, Ca2p/Sr3d XPS intensity ratio in-Depth profiles are simulated using the software Simulation of Electron Spectra for Surface Analysis (SESSA). In principle, core–shell like particle morphologies are formed but without a sharp interface between calcium and strontium containing phases. Surprisingly, the in-depth chemical distribution of the two types of nanoparticles is equal within the error of the experiment. Both comprise a SrF2-rich core domain and CaF2-rich shell domain with an intermixing zone between them. Consequently, the internal morphology of the final nanoparticles seems to be independent from the synthesis chronology. KW - Metal fluorides KW - Sol-gel synthesis KW - Synchrotron radiation KW - X-ray photoelectron spectroscopy PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522284 DO - https://doi.org/10.1002/sia.6937 SN - 0142-2421 VL - 53 IS - 5 SP - 494 EP - 508 PB - Wiley VCH AN - OPUS4-52228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bennet, Francesca A1 - Müller, Anja A1 - Radnik, Jörg A1 - Hachenberger, Y. A1 - Jungnickel, H. A1 - Laue, P. A1 - Luch, A. A1 - Tentschert, J. T1 - Preparation of Nanoparticles for ToF-SIMS and XPS Analysis N2 - Nanoparticles have gained increasing attention in recent years due to their potential and application in different fields including medicine, cosmetics, chemistry, and their potential to enable advanced materials. To effectively understand and regulate the physico-chemical properties and potential adverse effects of nanoparticles, validated measurement procedures for the various properties of nanoparticles need to be developed. While procedures for measuring nanoparticle size and size Distribution are already established, standardized methods for analysis of their surface chemistry are not yet in place, although the influence of the surface chemistry on nanoparticle properties is undisputed. In particular, storage and preparation of nanoparticles for surface analysis strongly influences the analytical results from various methods, and in order to obtain consistent results, sample preparation must be both optimized and standardized. In this contribution, we present, in detail, some standard procedures for preparing nanoparticles for surface analytics. In principle, nanoparticles can be deposited on a suitable substrate from suspension or as a powder. Silicon (Si) Wafers are commonly used as substrate, however, their cleaning is critical to the process. For sample preparation from suspension, we will discuss drop-casting and spin-coating, where not only the cleanliness of the substrate and purity of the suspension but also its concentration play important roles for the success of the preparation methodology. For nanoparticles with sensitive ligand shells or coatings, deposition as powders is more suitable, although this method requires particular care in fixing the sample. KW - Titania nanoparticles KW - X-ray photoelectron spectroscopy KW - Secondary ion mass spectrometry KW - Surface chemisttry PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520103 UR - https://www.jove.com/video/61758 DO - https://doi.org/10.3791/61758 VL - 163 SP - e61758 AN - OPUS4-52010 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Donskyi, Ievgen A1 - Nie, C. A1 - Ludwig, K. A1 - Trimpert, J. A1 - Ahmed, R. A1 - Quaas, E. A1 - Achazi, K. A1 - Radnik, Jörg A1 - Adeli, M. A1 - Haag, R. A1 - Osterrieder, K. T1 - Graphene Sheets with Defined Dual Functionalities for the Strong SARS-CoV-2 Interactions N2 - Search of new strategies for the inhibition of respiratory viruses is one of the urgent health challenges worldwide, as most of the current therapeutic agents and treatments are inefficient. Severe acute respiratory syndrome coronavirus 2 (SARSCoV-2) has caused a pandemic and has taken lives of approximately two Million people to date. Even though various vaccines are currently under development, virus, and especially its spike glycoprotein can mutate, which highlights a Need for a broad-spectrum inhibitor. In this work, inhibition of SARS-CoV-2 by graphene platforms with precise dual sulfate/alkyl functionalities is investigated. A series of graphene derivatives with different lengths of aliphatic chains is synthesized and is investigated for their ability to inhibit SARS-CoV-2 and feline coronavirus. Graphene derivatives with long alkyl chains (>C9) inhibit coronavirus replication by virtue of disrupting viral envelope. The ability of these graphene platforms to rupture viruses is visualized by atomic force microscopy and cryogenic electron microscopy. A large concentration window (10 to 100-fold) where graphene platforms display strongly antiviral activity against native SARS-CoV-2 without significant toxicity against human cells is found. In this concentration range, the synthesized graphene platforms inhibit the infection of enveloped viruses efficiently, opening new therapeutic and metaphylactic avenues against SARS-CoV-2. KW - Graphene KW - Graphene-based polyglycerol sulfates KW - SARS-CoV2 inhibitor KW - Virucidality PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520858 DO - https://doi.org/10.1002/smll.202007091 VL - 17 IS - 11 SP - 7091 PB - Wiley VCH AN - OPUS4-52085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radnik, Jörg A1 - Knigge, Xenia A1 - Andresen, Elina A1 - Resch-Genger, Ute A1 - Cant, D.J.H. A1 - Shard, A.G. A1 - Clifford, C.A. T1 - Composition, thickness, and homogeneity of the coating of core–shell nanoparticles—possibilities, limits, and challenges of X-ray photoelectron spectroscopy N2 - Core–shell nanoparticles have attracted much attention in recent years due to their unique properties and their increasing importance in many technological and consumer products. However, the chemistry of nanoparticles is still rarely investigated in comparison to their size and morphology. In this review, the possibilities, limits, and challenges of X-ray photoelectron spectroscopy (XPS) for obtaining more insights into the composition, thickness, and homogeneity of nanoparticle coatings are discussed with four examples: CdSe/CdS quantum dots with a thick coating and a small core; NaYF4-based upconverting nanoparticles with a large Yb-doped core and a thin Er-doped coating; and two types of polymer nanoparticles with a poly(tetrafluoroethylene) core with either a poly(methyl methacrylate) or polystyrene coating. Different approaches for calculating the thickness of the coating are presented, like a simple numerical modelling or a more complex simulation of the photoelectron peaks. Additionally, modelling of the XPS background for the investigation of coating is discussed. Furthermore, the new possibilities to measure with varying excitation energies or with hard-energy X-ray sources (hard-energy X-ray photoelectron spectroscopy) are described. A discussion about the sources of uncertainty for the determination of the thickness of the coating completes this review. KW - X-ray spectroscopy KW - Nanoparticles KW - Spectroscopy / Instrumentation KW - Spectroscopy / Theory PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-548305 DO - https://doi.org/10.1007/s00216-022-04057-9 VL - 414 IS - 15 SP - 4331 EP - 4345 PB - SpringerNature AN - OPUS4-54830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -