TY - CONF A1 - Eggert, Lara T1 - Offshore-Reparaturbeschichtungen mit Chloridvorbelastung N2 - Bei maritimen Reparaturbeschichtungen ist eine chloridfreie Oberfläche nicht immer zu gewährleisten. Zur Untersuchung des Einflusses chloridhaltiger Verunreinigungen auf die Schutzwirkung maritimer Epoxid-Reparaturbeschichtungen wurden gestrahlte Stahlproben (Sa 2½) mit künstlichem Meerwasser besprüht. So entstanden drei Verunreinigungszustände: sauber (C0), leicht verunreinigt (C1) und stark verunreinigt (C2). Zwei Beschichtungen (A1 und A2) wurden appliziert und durch Ritzen und Impact-Schäden zusätzlich beansprucht. T2 - H2Mare-Abschlusskonferenz CY - Rostock, Germany DA - 23.09.2025 KW - Reperaturbeschichtung KW - Maritime Korrosion KW - Wechselzyklustest PY - 2025 AN - OPUS4-64235 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reuter, T. T1 - Measurement-based Detector Characteristics for Digital Twins in aRTist 2 N2 - Various software products for the simulation of industrial X-ray radiography have been developed in recent years (e.g., aRTist 2, CIVA CT, Scorpius XLab, SimCT, Wilcore) and their application potential has been shown in numerous works. However, full systematic approaches to characterise a specific CT system for these simulation software products to obtain a truthful digital twin are still missing. In this contribution, we want to present two approaches to obtain realistic grey values in X-ray projections in aRTist 2 simulations based on measured projections. In aRTist 2, the displayed grey value of a pixel is based on the energy density incident on that pixel. The energy density is calculated based on the X-ray tube spectrum, the attenuation between source and detector as well as an energy-dependent sensitivity curve of the detector. The first approach presented in this contribution uses the sensitivity curve as a free modelling parameter. We measured the signal response at different thicknesses of Al EN-AW6082 at different tube voltages (i.e., different tube spectra). We then regarded the grey values displayed by these projections as a data regression respectively an optimisation problem and obtained the sensitivity curve that is best able to reproduce the measured behaviour in aRTist 2. The resulting sensitivity curve does not necessarily hold physical meaning but is able to simulate the real system behaviour in the simulation software. The second approach presented in this contribution is to estimate the sensitivity curve based on assumptions about the characteristics of the scintillation detector (e.g., scintillator material, scintillator thickness and signal processing characteristics). For this approach, a linear response function (linear relationship between the deposited energy per pixel and the resulting grey value) is assumed. If the detector characteristics, which affect the simulated deposited energy, are properly modelled, the slope and offset of the response function to match the measured grey values should be the same for different tube spectra. As the offset is constant and given by the grey values measured at no incident radiation, the slope is the remaining parameter to evaluate the success of the detector modelling. We therefore adapted the detector characteristics by changing the detector setup until the slope was nearly the same for all measured tube spectra. We are aware that the resulting parameters of the scintillator material and thickness might not be the real ones, but with those modelling parameters we are able to simulate realistic grey values in aRTist 2. Both of those approaches could potentially be a step forward to a full systematic approach for a digital twin of a real CT system in aRTist 2. T2 - 20th World Conference on Non-Destructive Testing (WCNDT 2024) CY - Incheon, South Korea DA - 27.05.2024 KW - Computed Tomography KW - Digital Twin KW - Simulation PY - 2024 AN - OPUS4-61776 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feiler, Torvid A1 - Bhattacharya, Biswajit T1 - Mechanically flexible crystals: materials for new generation of responsive materials N2 - Based on the nature of the deformation, molecular crystals can be defined as being plastically (irreversible) or elastically (reversible)bendable. The mechanical response of crystals is thereby directly related to they structure.The structural elements required for a specific mechanical behavior are known, so that compounds with these properties can be synthesized by applying the rules of crystal engineering. T2 - Berlin Science Week CY - Berlin, Germany DA - 01.11.2021 KW - Flexible crystals PY - 2021 AN - OPUS4-53907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, U. T1 - Detection of plastics in soil N2 - Soil acts as a final sink for pollutants. Microplastics from different sources such as plastic mulching, littering, compost, sewage sludge, sedimentary deposition, and tyre abrasion are expected to be found in soil. However, representative and comprehensive information is missing on the sources, transport, and fate. Therefore, a reliable analysis method for microplastics in soils needs to be developed. The presented work describes the development of a procedure for microplastics analysis in soils. A representative sampling based on the on-site conditions and a sample preparation method was established and comprised of a drying step, the separation of microplastic particles > 1 mm, and a density separation for particles < 1 mm. The detection of the large microplastic particles (> 1 mm) was conducted with Attenuated Total Reflection - Fourier Transform infrared Spectroscopy (ATR-FTIR) , while Thermal Extraction Desorption - Gas Chromatography / Mass Spectrometry (TED-GC/MS) was applied for particles < 1 mm, gaining information on the type of polymer and mass fraction. Based on the established method, 14 environmental soil samples ? with different exposure of microplastics from agriculture, industrial sites, roads, and floods were investigated. Due to the arbitrary microplastic particle distribution among the samples for large microplastics, it was reasoned that the found particles were unrepresentative. In contrast, microplastic particles < 1 mm were discovered in a high mass in soil samples exposed to plastic mulching or fertilization with sewage sludge or compost (0 – 115 mg/kg). On average, microplastic contents detected in soil samples taken from a construction site and an inner-city lake were higher (13 – 238 mg/kg). As expected, microplastic content in soil sampled in proximity to roads was more pronounced in the upper soil layers. In contrast, very remote sampling sites, expectably uncontaminated, did not lead to the detection of microplastic regarding to thermoanalytical detection method. In a proof of concept experiment several in vivo and in vitro ecotoxicological tests were applied to evaluate the effect of microplastics (tyre abrasion, polystyrene containing hexabromocyclododecane) in natural soils. In summary, while no effects of the examined probes could be detected on higher levels of biological organization after exposures to earthworm E. andrei, significant changes in several oxidative stress related biomarkers were observed. T2 - SETAC Europe 2022 CY - Kopenhagen, Denmark DA - 15.05.2022 KW - Microplastic KW - TED-GC/MS KW - Soil PY - 2022 AN - OPUS4-55872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dittmann, Daniel T1 - Aktivkohle-Charakterisierung als weiterer Schlüssel für das Verständnis der Spurenstoffadsorption in der 4. Reinigungsstufe N2 - Aktivkohle ≠ Aktivkohle, Adäquate Materialcharakterisierung - Voraussetzung für Adsorptionsprognosen und Wasserspezifische Auswahl von Aktivkohleprodukten. Ausblick: Publikationen zu Aktivkohlecharakterisierung und Adsorptionsprognose in Vorbereitung T2 - Wasser 2021 - Jahrestagung der Wasserchemischen Gesellschaft CY - Online meeting DA - 10.05.2021 KW - Aktivkohle KW - Thermogravimetrie KW - Zersetzungsgasanalyse KW - Proximatanalyse PY - 2021 AN - OPUS4-52742 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linberg, Kevin T1 - Tipping the Energy Scales to Control Mechanochemical Polymorphism N2 - Control of ball milling conversions is required before the full potential of mechanochemical processing can be realized. It is well known that many parameters affect the outcome of mechanochemical polymorphism, but the energy of ball milling itself is often overlooked. We show here how this parameter alone can exert a significant influence on the polymorphic outcome of ball mill grinding by allowing the selective isolation of two polymorphic forms in their pure form under the same grinding conditions. Furthermore, we show how apparent mechanochemical equilibria can be deceptive. Our results clearly demonstrate the need for careful design and interpretation of ball milling experiments beyond current thinking. T2 - SALSA make and measure CY - Online meeting DA - 16.09.2021 KW - Mechanochemistry KW - Energy KW - Polymorph KW - Cocrystal PY - 2021 AN - OPUS4-53293 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feiler, Torvid T1 - Polymorphic tuning of a flexible organic crystal optical waveguide N2 - Crystalline molecular materials are usually brittle and are prone to break upon external mechanical force. This fragility poses challenges for their application in next-generation technologies, including sensors, synthetic tissues, and advanced opto-electronics. The recent discovery of mechanical flexibility in single crystals of molecular materials has solved this problem and enable the design of smart flexible device technologies. Mechanical flexibility of organic crystals can be tuned by altering the weak interactions in the crystal structure, for examples through polymorphism. Here we report 4-bromo-6-[(6-chlorolpyridin-2-ylimino)methyl]phenol (BCMPMP) as a promising candidate for future waveguide technologies. It turns out that BCMPMP has two different polymorphs with distinct optical and mechanical properties. Form I shows brittle behavior under mechanical stress and exhibits very weak emission at 605 nm (λex = 425 nm) together with a low fluorescence quantum yield (Φ = 0.4 %).In contrast, Form II has a large plastic (irreversible bending) regime and a bright emission at 585 nm (λex = 425 nm; Φ = 8.7 %). Making use of favorable mechanical fexiblity and optical properties, form II was explored as a bendable optical waveguide. Light was successfully propagated through a straight-shaped and mechanically deformed BCMPMP crystal. Depending on the light source, active or passive waveguiding could be achieved. So BCMPMP can also be used as a flexible wavelength filter. T2 - Congress of the International Union of Crystallography - IUCr 2021 CY - Online meeting DA - 14.08.2021 KW - Flexible crystals KW - Polymorphism KW - Waveguide PY - 2021 AN - OPUS4-53906 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Linberg, Kevin T1 - Controlled Polymorphism by Elevated Temperature Ball Milling N2 - Mechanochemistry provides polymorphs that are difficult to obtain by conventional solution-based methods. Based on the nicotinamide and pimelic acid cocrystal, we demonstrated that the ball size, frequency, and temperature are essential parameters. Our results indicate that fine-tuning the energy input during a mechanochemical reaction can provide control over polymorphism. T2 - Bessy User Meeting 2023 CY - Berlin, Germany DA - 22.06.2023 KW - Mechanochemistry KW - Temperature KW - Cocrystal KW - Energy input KW - Polymorph PY - 2023 AN - OPUS4-57985 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - Material Selection Strategy N2 - This poster is a summary of the material used in the PlasticsFatE project. It indicates the strategies for testing of various polymer properties next to each other according to risk and hazard assessment. T2 - CUSP annual meeting and conference CY - Utrecht, Netherlands DA - 12.09.2023 KW - Microplastics KW - CUSP KW - Material selection PY - 2023 AN - OPUS4-58311 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Drago, Claudia T1 - Rapid sample preparation to detect microplastics in baby milk powder N2 - Microplastics, ubiquitous as it is, could be released into food during production chain, through packaging and by consumer´s use. To determinate human exposure to microplastics is crucial to monitor microplastics in food matrices. The current absence of standard sample preparation procedures to identify and quantify different microplastics according to number and mass have generate time-consuming protocols and lack of comparability among different analytical methods, laboratories and time scales. Monitoring microplastics in complex matrices as food, and in particular in baby milk powder, requires an accurate approach that need to be validate, to ensure the comparability of results. Bottled drinking water or surface waters, for example, can be measured with mass-based methods (TED-GC/MS or Py-GC/MS) directly after filtration. Baby milk powder, instead is more challenging, due to the proteins and fatty acid that clog the filters and contaminate the measuring devices with heavy carry over. In this study, we characterize the baby milk powder by thermogravimetric analysis (TGA) and we tested different treatments for matrix reduction: water, H2O2, citric acids. In particular, the use of citric acid was tested for protein reduction before filtration. Our hypothesis was that citric acid will induce the precipitation of proteins and amino acids, leading to a strong matrix reduction. In fact, this sample pre treatment, allowed us to use a higher intake, necessary for representative quantification. Finally, the milk powder was spiked with reference material tablets containing polyethylene terephthalate (PET). The PET was not degraded by the citric acid and high recovery rate was achieved by TED-GC/MS and Py-GC/MS methods. Considering the simplicity and accessibility of this sample preparation and its robust results, this procedure could be easily proposed as a simple sample preparation approach to monitor microplastics by mass-based methods. T2 - MICRO 2024 CY - Arrecife, Spain DA - 23.09.2024 KW - Microplastics KW - Milk KW - Polymer 3R KW - TED-GC/MS PY - 2024 AN - OPUS4-61273 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meurer, Maren T1 - Is olypropylene relevant for microplastic analytics? N2 - Nowadays, in every terrestrial and aquatic ecosystem, even in the remotest areas, small residues of plastics, the so called microplastic (MP) can be found. MPs are particles with a size of 1-1000 µm (ISO/TR 21960:2020), mainly containing synthetic polymers like polyethylene (PE), polypropylene (PP), polystyrene (PS) or polyethylene terephthalate (PET). Even styrene-butadiene rubber (SBR) as an indication for tire wear is included due to similar particle formation. To understand the MPs consequences to the environment, it is of high priority to capture its extent of contamination. It is surprising that in the analysis of polymer masses in environmental samples, PE, PS and SBR are often detected, but only small amounts of PP, although this is the second most commonly produced standard plastic and many MP particles originate from carelessly disposed packaging materials. This presentation provides hypotheses about the reasons of rare PP identification and mass quantification in environmental samples. Different investigations of pristine PP and representative environmental samples, including the pre-treatment by Accelerated Solvent Extraction (ASE) or with density separation followed by the thermal extraction / desorption gas chromatography-mass spectrometry (TED-GC/MS) are presented. The results are discussed according to the material properties and a possible degradation mechanism under different weathering conditions which indicate less stability under relevant storage conditions. T2 - Society of Environmental Toxicology and Chemistry CY - Dublin, Ireland DA - 30.04.2023 KW - Sample preparation KW - Polypropylene KW - Microplastic KW - Degradation PY - 2023 AN - OPUS4-57474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Miclea, P.-T. T1 - Real-life airborne micro- and nano-plastic particles and fibres on a porous membrane filter system from a textile factory suitable for both: vibrational and mass spectrometry N2 - The poster presents an application of Si wafer filter system on indoor air sampling. A textile factory producing PP fibres was sampled. T2 - SETAC Europe 2023 CY - Dublin, Ireland DA - 30.04.2023 KW - Microplastics KW - Polymer 3R KW - Textile fibres KW - Si wafer filter KW - Microplastics sampling PY - 2023 AN - OPUS4-57462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Simone T1 - Influence of the pH Value to the Degradation of Ester-Based Thermoplastic Polyurethanes N2 - Microplastics are solid polymeric particles with a size of 1-1000 μm (ISO/TR21960:2020), which can be emitted from mismanaged waste into the environment, where microplastic is now ubiquitous. What happens to the microplastics after ending up in the environment, which risks entail and what effects it has are not sufficiently clarified up to now. The most certain issue is that the plastic particles in the environment are exposed to natural ageing, are fragmenting and degrading, such that the potential risk to ecosystems and humans is increasing due to the formation of smaller and smaller particles, potentially even including nanoplastics, if these are ingested before their further degradation. Therefore, and in view of a possible registration of polymers under REACH in the future, it is necessary to investigate the degradation of thermoplastic polyurethanes (TPU) regarding hydrolysis stability to evaluate possible risks and effects to the environment. In the present studies, one thermoplastic polyurethane – with and without hydrolysis stabilizer – is exposed to different pH buffers at 50°C for 14 days to investigate hydrolysis depending to different pH values (acid, alkali and neutral) based on OECD guideline TG111. The hydrolysis behavior of the TPUs is characterized by surface sensitive techniques and on bulk properties. First degradation effects can be detected by SEC. Hydrolysis, especially under acidic and basic conditions, leads to chain scissions to lower molecular masses. Furthermore, the degradation products which indicate the structure of the bulk material were detected by thermo-analytical methods like TGA-FTIR for the small degradation products and the thermo extraction/desorption-gaschromatography/mass spectrometry (TED-GC/MS) for bigger degradation products. Acidic and basic hydrolysis shows the same degradation behavior which is caused by a preferred scission of the ester and urethane functionalities. Surface-sensitive techniques such as XPS demonstrate less carboxylic acid formation at acidic than at alkaline pH value in the TPU without stabilator, where as the TPU with stabilator ages to the same extent in both pH ranges. Altogether, the hydrolysis of TPUs – independently of added stabilizer or not – in acid and alkali environment is accelerated compared to the neutral hydrolysis. T2 - SETAC CY - Dubin, Ireland DA - 30.04.2023 KW - Degradation KW - Thermoplastic Polyurethane KW - Microplastic KW - Polymer Hydrolysis KW - Polymer 3R KW - REACH PY - 2023 AN - OPUS4-58906 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strzelczyk, Rebecca T1 - Zeolites loaded with VOCs as reference for material emissions testing N2 - Nowadays, people spend most of their time indoors. Thus, a good indoor air quality is important. Emissions of volatile organic compounds (VOCs) from furniture and building materials can cause health complaints1. Quantitative VOC-emission testing is carried out under standardized conditions in emission test chambers. In the presented project an emission reference material (ERM) is developed that emits a defined mixture of VOCs which is required for quality assurance and -control (QA/QC) measures. Porous materials (e.g zeolites, activated carbons, MOFs or aerogels) are used as reservoir materials and impregnated with VOC. The porous materials are selected, among others, by their pore size, pore size distribution, polarity and availability. Due to their regular pore structure zeolites are tested at first. For a prediction of the emission profile, the ERM is supposed to exhibit a constant emission rate over time. The aim is a stability of ≤ 10 % change in the emission rate over a minimum of 14 days. Method For impregnation, the material is placed into an autoclave inside a rotatable basket. The VOC is added and the autoclave is closed. Afterwards, CO2 is inserted. The closed system is then heated to the supercritical point of CO2 (31 °C, 73.75 bar). In this state, the CO2 acts as solvent for the VOC. By rotating the basket, the distribution of the VOC is ensured. After a few minutes, the pressure is decreased slowly and the CO2 is released. For the determination of the emission profile, the impregnated sample is placed into an emission test chamber. These chambers can be operated either with dry or humid air (50 ± 5 % rel. humidity). Every second to third day, air samples are taken and analyzed by gas chromatography. For an ideal impregnation, several different pressures and temperatures as well as impregnation times are tested. Results Two zeolite materials tested in dry air conditions reach emission profiles with a decrease of less than 10 % over 14 days (heptane and toluene, respectively). Further it was discovered that smaller pellets of the same zeolite show better results than bigger particles. When the pore size of a zeolite is too small, e.g. 0.3 nm, the VOC cannot be absorbed sufficiently. The main disadvantage of zeolites is their hygroscopicity because it has a large impact on the release of VOC when they are used in emission test chambers under standardized test conditions (23 °C, 50 % rel. humidity). Activated carbons have emission profiles with a larger change over 14 days. However, the high hydrophobicity allows measurements in humid air conditions which was not possible with the before mentioned hygroscopic zeolites. It is possible to impregnate powdered materials as well, and thus powdered non-hygroscopic (n.h.) zeolites were impregnated. Their emission profiles are comparable to those of the activated carbons. The use of methylated hygroscopic zeolites with a decrease in hygroscopicity did not yield successful emission measurements. The change over 14 days is calculated only for the stable phase (~250–300 h). The desired stability of ≤ 10 % change of the emission rate over 14 days could already be reached under dry testing conditions. Further investigations under humid conditions show that zeolites with high Si/Al-ratios are non-hygroscopic and comparable to activated carbons (20–30 % change). The next step is to reduce the change in the emission rate of these materials to the aimed ≤ 10 % over 14 days. T2 - Deutsche Zeolithtagung CY - Jena, Germany DA - 28.02.2024 KW - VOC KW - Emission KW - Quality assurance KW - Reference material KW - Zeolite PY - 2024 AN - OPUS4-59843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strzelczyk, Rebecca T1 - Constant emitting reference material for emissions test procedures N2 - Since nowadays people spend most of their time indoors, a healthy environment is essential. Volatile organic compounds (VOCs) emitted from furniture and building materials are reported to cause health complaints. Therefore, the usage of low emitting materials will improve the indoor air quality. Quantitative VOC emission testing is usually conducted in emission test chambers under specified controlled conditions as described in DIN 16000-9 and DIN EN 16516. For reasons of quality control/quality assurance (QC/QA) and for a better comparability of test results from different laboratories, suitable emission reference materials (ERM) are needed. Here, it is important to have a homogenous material with known emission rates over a specific time. Different approaches can be found in literature, inter alia polymer films loaded with the target compound to be released again, or a lacquer material to which a VOC mixture is added. After curing of the lacquer, the material can be loaded into a test chamber. Drawback of those approaches are their relatively fast decreasing emission profiles. For QC/QA purposes according to the test standards, VOC sources with constant emission profiles are desirable. The EU-funded research project MetrIAQ “Metrology for the determination of emissions of dangerous substances from building materials into indoor air” is working on a multi-component ERM with an envisaged instability of ≤ 10 % in the emission rate over at least 14 days. Within a doctoral thesis porous materials are impregnated with VOCs. Supercritical CO2 is used as solvent. Thus, the impregnated material does not contain any solvent that may show a measurable amount of emission in the emission test chamber. Furthermore, CO2 has the benefits to have a good availability and low costs. For the selection of porous materials several properties like the pore size, the surface, and the interaction with the components in the atmosphere need to be considered. The impregnation method is optimised while the different porous materials are tested. For the selection of porous materials the pores need to be large enough for the VOC molecules, further influence of the pore size is tested. T2 - Healthy Buildings CY - Aachen, Germany DA - 11.06.2023 KW - VOC KW - Emission KW - Quality assurance KW - Reference material PY - 2023 AN - OPUS4-59842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Drago, C. T1 - Standardization Methods for the Analysis of Microplastics (10 100µm) in Food Matrix: Sample Preparation and Digestion of Milk Powder. N2 - Monitoring of microplastics in food matrices is crucial to determinate the human exposure. By direct ingestion microplastics could be released in the food during the production, through packaging and by consumer’s use. The absence of standard methods to quantify and detect different size range and type of microplastics has led to difficult and time consuming procedural steps, poor accuracy and lack of comparability. In this work, matrix characterization and laboratory experiments were used to investigate the efficiency of sample preparation in milk powder. This information is crucial to compile a standard procedure for sample preparation and digestion of common milk powder to detect different particle sizes and types of polymers. Charaterisation is done by TGA and TOC measurements. T2 - SETAC Europe 2024 CY - Sevilla, Spain DA - 05.05.2024 KW - Microplastics KW - Harmonisation in microplastics KW - Polymer 3R KW - Microplastics in milk PY - 2024 AN - OPUS4-60034 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - Seasonal microplastic concentrations along the rivers Rhine and Danube N2 - Over the last 20 years, many researchers, politicians and citizens have become increasingly aware of the growing plastic problem of our time. A lack of recycling concepts and plastic collection points as well as careless dumping lead to accumulation of plastic products in the environment. Natural weathering can cause these plastics to degrade and fractionate, meaning that microplastics (1 1,000 µm, ISO/TR 21960:2020) and nanoplastics (< 1 µm, ISO/TR 21960:2020) of various synthetic polymer materials can now be detected in all parts of the world. Whether microplastics or nanoplastics pose a toxicological hazard is being investigated in a variety of ways. Valid results are still pending. However, the EU precautionary principle applies to micro- and nanoplastics. Monitoring of microplastics is already required in the revision of the Drinking Water and Wastewater Framework Directive. Reliable monitoring of rivers can be carried out by sampling with sedimentation boxes and microplastic detection by using thermal extraction desorption gas chromatography/mass spectrometry (TED-GC/MS) in routine operation (Figure 1). The river Rhine was sampled for microplastic masses at three different sampling locations over a period of one year and in addition the Danube at randomized sampling locations The TED-GC/MS results showed that various synthetic polymers frequently produced in industry, such as polyethylene, polypropylene or polystyrene as well as the tire compound styrene-butadiene rubber were found. The work not only shows a possible workflow for monitoring concepts, but also provides information on environmentally relevant concentrations of microplastics and tire components in surface waters. This in turn is necessary for ecotoxicological studies. T2 - ESOPS CY - Berlin, Germany DA - 09.09.2024 KW - Microplastics KW - TED-GC/MS KW - Polymer 3R PY - 2024 AN - OPUS4-61016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuerlein, T1 - Mechanical properties of the HL-LHC 11 Tesla Nb3Sn magnet constituent materials N2 - A test campaign was launched to determine the mechanical properties of the HL-LHC 11 T Nb3Sn magnet components in order to accurately model the mechanical properties in Finite Element simulations that predict the stress and strain distribution in These magnets. Static and dynamic test methods have been applied for determining elastic materials behavior, and highly accurate Young’s moduli are obtained with the dynamic methods resonance and impulse excitation. These non-destructive methods also enable temperature dependent modulus measurements during in situ heat cycles. T2 - Applied Superconductivity Conference CY - Denver, Colorado, USA DA - 04.09.2016 KW - Young's modulus KW - Tensile test KW - Resonanz KW - Impact excitation PY - 2016 AN - OPUS4-37414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Benjamin, Merz T1 - Advanced camera calibration for lens distortion correction in hybrid additive manufacturing processes N2 - Hybrid additive manufacturing is becoming increasingly important in the field of additive manufacturing. Hybrid approaches combine at least two different manufacturing processes. The focus of this work is the build-up of geometries onto conventionally manufactured parts using laser-based powder bed fusion of metals (PBF-LB/M). The hybrid build-up requires a precise position detection system inside the PBF-LB/M machines to determine the exact position of the existing component. For this purpose, high-resolution camera systems can be utilized. However, the use of a camera system is associated with several challenges. The captured images are subject to various distortions of the optical path. Due to these distortions, it is not possible to use the images for measurements and, therefore, it is not possible to calculate the positions of objects. In this study a homography matrix is calculated to correct keystone distortion in the images. Different calibration patterns have been tested for the calculation of the homography matrix. The influence of the number of calibration points on the precision of position detection of objects is determined. Furthermore, the influence of an additional camera calibration by using ChArUco boards is evaluated. The result is a camera calibration workflow with associated calibration pattern for a precise position detection of parts inside PBF-LB/M machines allowing a hybrid build-up with minimum physical offset between base component and build-up. T2 - euspen’s 24th International Conference & Exhibition CY - Dublin, Ireland DA - 10.06.2024 KW - Aditive Manufacturing KW - Hybrid build-up KW - Position detection KW - Camera calibration PY - 2024 AN - OPUS4-60600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Hydrogen distribution in multi-layer welds of steel S960QL N2 - High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing im-portance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints sig-nificantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To min-imize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydro-gen amount and its distribution in the weld seam and (2) options to lower the amount of intro-duced hydrogen. Existing standards recommend heat treatment procedures (interpass tempera-ture or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water imme-diately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concen-trations were measured. T2 - 3rd International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Welding KW - High-strength steels KW - Heat treatment KW - Carrier gas hot extraction PY - 2018 AN - OPUS4-45076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -