TY - CONF A1 - Ávila Calderón, Luis T1 - Assessing the low cycle fatigue behaviour of additively manufactured Ti-6Al-4V: Challenges and first results N2 - The understanding of process-microstructure-property-performance (PMPP) relationships in additive manufacturing (AM) of metals is highly necessary to achieve wide-spread industrial application and replace conventionally manufactured parts, especially regarding safety-relevant applications. To achieve this understanding, reliable data and knowledge regarding material’s microstructure-property relationships (e.g. the role of defects) is needed, since it represents the base for future more targeted process optimizations and more reliable calculations of performance. However, producing reliable material data and assessing the AM material behaviour is not an easy task: big challenges are e.g. the actual lack of standard testing methods for AM materials and the occasional difficulties in finding one-to-one comparable material data for the conventional counterpart. This work aims to contribute to end this lack of reliable material data and knowledge for the low cycle fatigue behaviour of the most used titanium alloy in aerospace applications (Ti-6Al-4V). For this purpose, two sets of test specimens were investigated. The first set was manufactured from cylindrical rods produced by an optimized DED-L process and the second was manufactured from a hot formed round bar. The test specimens were cyclically loaded until failure in the low-cycle-fatigue (LCF) regime. The tests were carried out according to ISO 12106 between 0.3 to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behaviour is described and compared between materials and with literature values based on cyclic deformation curves and strain-based fatigue life curves. Besides, the parameters of Manson-Coffin-Basquin relationship were calculated. The microstructures (initial and after failure) and fracture surfaces were comparative characterized. Thereby, the focus lied on understanding the role of grain morphology and defects on the failure mechanisms and fatigue lifetimes. For this latter characterization, optical microscopy (OM), scanning electron microscopy (SEM) and micro computed tomography (µCT) were used. T2 - 4th International Symposium on Fatigue Design and Material Defects CY - Online meeting DA - 26.05.2020 KW - Ti-6Al-4V KW - Additive manufacturing KW - Low cycle fatigue KW - Micro computed tomography KW - Microstructure PY - 2020 AN - OPUS4-50893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas T1 - Wire arc additive manufacturing of high strength AL-MG-SI alloys N2 - Gas metal arc-based direct energy deposition (DED) additive manufacturing technologies hold significant promise for producing large-scale metal components. However, determining optimal process parameters to achieve the desired near-net shape design and mechanical performance is a complex challenge due to the intricate interplay between process parameters and material properties. This presentation highlights the use of a newly developed solid welding wire doped with TiB to improve grain refinement in metals deposited via DED-Arc for high-strength precipitation-hardening AlMgSi aluminum alloys. This wire stems from our initial metallurgical investigations into grain refinement in aluminum weld metals. The research emphasizes the relationship between process parameters and component quality, aiming to uncover the mechanisms that influence performance. This is essential for establishing a reliable range of parameters that meet quality standards, many of which are derived from traditional welding practices. Component quality was assessed by studying pore size, pore distribution, and grain morphology. To further enhance the mechanical properties of the deposited material, post-weld heat treatments—including solution treatment, quenching, and artificial aging—were applied. The study also explores how different heat treatment strategies affect the final mechanical properties. To validate the feasibility of 3D printing high-strength aluminum alloys, a more complex demonstrator component was fabricated. The results demonstrate that DED-Arc technology can produce large aluminum parts with a quality comparable to subtractive manufacturing techniques. Furthermore, the entire additive manufacturing workflow has been digitally integrated, enabling full traceability of all key process steps. This digital integration is critical for ensuring reliable quality assessments of the finished components. T2 - 77th IIW Annual Assembly and International Conference Joint Meeting of C-I, C-IV, and C-XII CY - Rhodos, Greece DA - 07.07.2024 KW - DED-Arc KW - High-strength aluminium alloys KW - Porosity assessment KW - Component testing KW - CT-analyses PY - 2024 AN - OPUS4-62014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas T1 - Additive Manufacturing of High Strength Al-Mg-Si Alloys with DED-Arc N2 - Direct energy deposition additive manufacturing technologies that utilize an electric arc have great potential for generating large volume metal components. However, selecting process parameters that yield the desired near net shape design and requested mechanical component behavior is not a trivial task due to the complex relationship between all process parameters and material characteristics. This presentation exemplifies the application of a newly developed solid welding wire doped with TiB to enhance grain refinement in the deposited metal for additive manufacturing based on DED-Arc of high-strength precipitation hardening AlMgSi-aluminum alloys. It is worth noting that the solid wire is the result of our preliminary metallurgical studies on grain refinement in aluminum weld metal. Consequently, research focuses on the correlation between process parameters and component quality to understand the underlying mechanisms. This is crucial for evaluating a robust process parameter space that yields component quality in line with corresponding standards which are mainly taken from welding technology. Specifically, we examine component quality by analyzing pore size and distribution, as well as grain morphology. To enhance the mechanical properties of the deposited metal, a post-weld heat treatment was conducted, comprising of solution treatment, quenching, and artificial aging. The study also evaluates the effects of various heat treatment strategies on the final mechanical properties of the material. To demonstrate the applicability of 3D metal printing of high-strength aluminium alloys, a more complex demonstrator was created. It has been shown that DED-Arc can produce high-volume aluminium parts with the same quality as the corresponding subtractive processing strategy. Additionally, the entire additive manufacturing chain has been digitally integrated, enabling traceability of all relevant process steps, which is essential for reliable subsequent quality assessment. T2 - 4th Symposium on Materials and Additive Manufacturing - Additive 2024 CY - Berlin, Germany DA - 12.06.2024 KW - DED-Arc KW - High-stength aluminium alloys KW - Grain refinement KW - Quality assurance PY - 2024 AN - OPUS4-60248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Bachmann, Marcel A1 - Rethmeier, Michael A1 - Meng, Xiangmeng T1 - Project title: Multi-physical simulation of the influence of an auxiliary magnetic field on the process porosity formation during high-power laser beam welding N2 - In this project, a multiphysically coupled numerical model will be developed to quantitatively describe porosity reduction in high-power laser beam welding of up to 10 mm thick AlMg3 using an oscillating magnetic field. The aim is to gain fundamental insights into the physical dependencies of the introduced electromagnetic forces on the melt pool behavior and the reduction of porosity. With the help of the numerical model, the transient, multi-coupled, three-dimensional problem of heat transfer, liquid flow, free surface deformation, and magnetic induction is to be solved, taking into account temperature-dependent material properties. The numerical modelling of the heat source will integrate all relevant physical mechanisms, for instance, multiple reflections of the laser radiation by an advanced ray tracing model, as well as local Fresnel absorption at the keyhole wall. This allows an analysis of the keyhole fluctuations, which have a dominant influence on the formation of process spores during deep penetration welding, based on physical principles. In addition, further physical factors such as the ablation pressure of the evaporating metal, the Laplace pressure, and Marangoni shear stresses are also to be integrated into the model. To evaluate the pore formation and reduction by means of the electromagnetic forces introduced in the molten pool, suitable models for describing the movement of the pores in the melt are to be developed. For the process pores, their movement can be implemented by tracking their surface under consideration of their internal pressure and temperature. With the help of the simulation model, all key factors for the formation of process pores during laser beam welding of the used aluminum alloy, as well as their avoidance, can be decoupled and analyzed. Accompanying welding tests are planned at BAM on a 20 kW fiber laser and a 16 kW disk laser. The magnetic flux density will be up to 500 mT at a maximum frequency of 5 kHz. The experimental results, in particular temperature measurements, weld cross sections, computer tomography, and X-ray examinations, will be used to verify the multiphysical model and its calibration. Moreover, the models will be validated and quantified by in situ high-speed imaging of the keyhole dynamics in a metal/quartz glass configuration with keyhole illumination by a diode laser coaxial to the processing laser. On the basis of the numerical and experimental results, the dependencies between applied magnetic field, melt pool behavior, and porosity formation will be revealed in this project. KW - Laser beam welding KW - Electromagnetic weld pool control KW - Numerical simulation KW - Process porosity PY - 2026 DO - https://doi.org/10.34657/27669 SP - 1 EP - 14 AN - OPUS4-65335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marquardt, R. A1 - Gook, S. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Handgeführtes Laserstrahlschweissen am T-Stoss eines niedrig legierten Stahls N2 - Das handgeführte Laserstrahlschweißen gewinnt in der Industrie zunehmend an Bedeutung, da die hohe Produktivität und die einfache Handhabung Unternehmen wirtschaftliche Vorteile bieten. Derzeit ist der Einsatz in der Industrie jedoch auf Teile mit ästhetischen Anforderungen beschränkt, die häufig aus hochlegiertem Stahl bestehen. Um das Handschweißen mit Laserstrahl auch für Bauteile aus kostengünstigen Stähle mit guten mechanischen Eigenschaften einsetzen zu können, untersucht diese Studie den Einfluss des Schutzgases auf die Porosität am mikrolegierten Stahl HX340LAD mit einer Dicke von 1,5 mm. Getestet wurden die Gase Argon, Stickstoff, CO2 sowie Mischungen aus Argon und CO2 an T-Stöße mit Zusatzdraht. Die Qualifizierung der Porosität erfolgte gemäß DIN EN ISO 13919-1 an Querschliffen als auch mittels Röntgenuntersuchung. Die Ergebnisse zeigen, dass für diesen Stahl die Bewertungsgruppe B mittels CO2 als Schutzgas erreicht werden kann. Stickstoff führt zu Gruppe C, Argon zu D. KW - Handgeführtes Laserstrahlschweißen, HHLW, Stahl, Laser KW - HHLW KW - Stahl KW - Laser PY - 2025 SP - 22 EP - 25 PB - Schweizerischer Verein für Schweisstechnik SVS AN - OPUS4-65041 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Kising, Pascal A1 - Yang, Fan A1 - Rethmeier, Michael T1 - Prediction of weld pool and keyhole geometries in high-power laser beam welding through a physics-informed generative artificial intelligence approach N2 - The weld pool and keyhole geometries are critical characteristics in evaluating the stability of the high-power laser beam welding (LBW) process and determining the resultant weld quality. However, obtaining these data through experimental or numerical methods remains challenging due to the difficulties in experimental measurements and the high computational demands of numerical modelling. This paper presents a physics-informed generative approach for predicting weld pool and keyhole geometries in the LBW process. With the help of a well experimentally validated numerical model considering the underlying physics in the LBW, the geometries of the weld pool and keyhole under various welding conditions are calculated, serving as the dataset of the generative model. A Conditional Variational Autoencoder (CVAE) model is employed to generate realistic 2D weld pool and keyhole geometries from the welding parameters. We utilize a β-VAE model with the Evidence Lower Bound (ELBO) loss function and include Kullback-Leibler divergence annealing to better optimize model performance and stability during training. The generated results show a good agreement with the ground truth from the numerical simulation. The proposed approach exhibits the potential of physics-informed generative models for a rapid and accurate prediction of the weld pool geometries across a diverse range of process parameters, offering a computationally efficient alternative to full numerical simulations for process optimization and control in laser beam welding processes. T2 - International Congress of Applications of Lasers & Electro-Optics 2025 CY - Orlando, USA DA - 12.10.2025 KW - Laser beam welding KW - Generative artificial intelligence KW - Machine learning KW - numerical simulation PY - 2025 SP - 1 EP - 10 AN - OPUS4-65075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Fasselt, Janek Maria A1 - Klötzer-Freese, Christian A1 - Kruse, Tobias A1 - Kleba-Ehrhardt, Rafael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Recycling nickel aluminium bronze grinding chips to feedstock for directed energy deposition via impact whirl milling: Investigation on processability, microstructure and mechanical properties N2 - During the production of ship propellers, considerable quantities of grinding chips from nickel aluminium bronze areproduced. This paper examines the mechanical comminution of such chips via impact whirl milling and the utilization of twochip-powder batches as feedstock for a laser-based directed energy deposition process. The materials are characterized viadigital image analysis, standardized flowability tests, scanning electron microscopy and energy dispersive X-ray spectroscopyand are compared to conventional, gas atomized powder. The specimens deposited via directed energy deposition areanalyzed for density, hardness and microstructure and tensile properties for vertical and horizontal build up directions arecompared. At elevated mill rotation speeds, the comminution with impact whirl milling produced rounded particles, favorableflow properties and particle size distribution, making them suitable to deposit additive specimens. The microstructureexhibited characteristic martensitic phases due to the high cooling rates of the additive manufacturing process. The presenceof ceramic inclusions was observed in both the powder and on the tensile fracture surfaces, partly impairing the mechanicalproperties. However, specimens in the vertical build-up direction (Z) showed competitive tensile results, with 775 MPa intensile strength, 455 MPa in yield strength and 12.6 % elongation at break. The findings of this study indicate that recyclingof machining chips to additive manufacturing feedstock can be a viable option for reducing material costs and environmentalimpact. KW - Nickel aluminium bronze KW - Grinding chips KW - Recycling KW - Directed energy deposition KW - Material characterization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651214 DO - https://doi.org/10.1016/j.addma.2025.104804 SN - 2214-8604 VL - 105 SP - 1 EP - 9 PB - Elsevier B.V. AN - OPUS4-65121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huo, Wenjie A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - An illumination based backdoor attack against crack detection systems in laser beam welding N2 - Deep neural networks (DNNs) have been wildly used in engineering and have achieved state-of-the-art performance in prediction and measurement tasks. A solidification crack is a serious fault during laser beam welding and it has been proven to be successfully detected using DNNs. Recently, research on the security of DNNs is receiving increasing attention because it is necessary to explore the reliability of DNNs to avoid potential security risks. The backdoor attack is a serious threat, where attackers aim to inject an inconspicuous pattern referred to as trigger into a small portion of training data, resulting in incorrect predictions in the reference phase whenever the input contains the trigger. In this work, we first generate experimental data containing actual cracks in the welding laboratory for training a crack detection model. Then, targeting this scenario, we design a new type of backdoor attack to induce the model to predict the crack as a normal state. Considering the stealthiness of the attack, a common phenomenon during the welding process, illumination, is used as the backdoor trigger. Experimental results demonstrate that the proposed method can successfully attack the crack detection system and achieve over 90% attack success rate on the test set. T2 - 8th ML4CPS 2025 – Machine Learning for Cyber-Physical Systems CY - Berlin, Germany DA - 06.03,2025 KW - System security KW - Welding crack detection KW - Backdoor attack KW - Deep neural networks PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651357 DO - https://doi.org/10.24405/20021 VL - 2025 SP - 12 EP - 21 PB - Universitätsbibliothek der HSU/UniBw H CY - Hamburg AN - OPUS4-65135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lemke, J. T1 - Water and gas atomized AISI 316L powder for DED-LB: A comparative study on powder properties and build quality N2 - Powder properties are considered a key factor in part quality in laser additive manufacturing, although few studies have investigated the effects in directed energy deposition (DED). Water atomized (WA) and gas atomized (GA) powders are frequently used but may result in different part properties due to powder properties. To examine their qualification for DED-LB, this work examines powders and build quality of AISI 316L. Also, examination techniques are compared. The results show that the powder production has no relevant influence on porosity and Archimedian density of built parts. WA powders show good processability in DED-LB, despite unfavorable morphology. In contrast, WA specimen reach only 10% fracture elongation in tensile testing whereas GA-based specimen achieve 30%. Tensile strength of both is above 500 MPa. The reason for the lower mechanical property values can be attributed to defects and oxides. WA powders may provide a cost-effective alternative for DED-LB when mechanical load requirements are not important. T2 - Lasers in Manufacturing Conference CY - Munich, Germany DA - 23.06.2025 KW - DED-LB KW - Porosity KW - AISI 316L KW - Water atomized KW - Gas atomized KW - Powder PY - 2025 AN - OPUS4-65120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne T1 - Werkstoffsichere Dickblechschweißung und KI N2 - Der Vortrag zeigt, welche Herausforderungen beim Schweißen sogenannter Dickblechverbindungen bestehen und welche Strategien zur Lösung genutzt werden können. Ansätze zur Fehlerprävention werden vorgestellt. Es wird dargestellt, wie KI-basierte Methoden die Fehlererkennung erleichtern. Letztlich werden Potentiale zur effizienten Fehlerbeseitigung aufgezeigt und der Anwendernutzen herausgestellt. T2 - Mitgliederversammlung der Forschungsvereinigung Stahlanwendung e. V. CY - Essen, Germany DA - 17.12.2025 KW - UP-Schweißen KW - Eigenspannungen KW - Künstliche Intelligenz KW - Reparatur PY - 2025 AN - OPUS4-65210 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Chaurasia, Prashant Kumar A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Tandem-GMAW: advanced pulsed and short cicuiting process mode experimental data N2 - This dataset consists of raw recordings for 5 Tandem gas metal arc welding experiments (Tandem-GMAW / T-GMAW). KW - T-GMAW KW - High power welding KW - Deposition efficiency KW - Life Cycle Assessment PY - 2025 DO - https://doi.org/10.5281/zenodo.17951724 PB - Zenodo CY - Geneva AN - OPUS4-65206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Chaurasia, Prashant Kumar A1 - Cagtay, Fabry A1 - Andreas, Pittner A1 - Rethmeier, Michael T1 - Automated in situ monitoring and analysis of process signatures and build profiles during wire arc directed energy deposition N2 - Wire arc directed energy deposition (DED-Arc) is an emerging metal additive manufacturing process to build near-net shaped metallic parts in a layer-by-layer with minimal material wastage. Automated in situ monitoring and fast-responsive analyses of process signatures and deposit profiles during DED-Arc are in ever demand to print dimensionally consistent parts and reduce post-deposition machining. A comprehensive experimental investigation is presented here involving real-time synchronous measurement of arc current, voltage, and the deposit profile using a novel multi-sensor monitoring framework integrated with the DED-Arc set-up. The recorded current–voltage transients are used to estimate the time-averaged arc power, and energy input in real time for an insight of the influence of wire feed rate and printing travel speed on the deposit characteristics. A unique attempt is made to represent the geometric profiles of the single-track deposits in a generalized mathematical form corresponding to a segmented ellipse, which has exhibited the minimum root-mean-square error of 0.03 mm. The dimensional inconsistency of multi-track deposits is evaluated quantitatively in terms of waviness using build profile monitoring and automated estimation, which is found to increase with an increase in step-over ratio and energy input. For the multi-track mild steel deposits, the suitable range of step-over ratio for the minimum surface waviness is observed to lie between 0.6 and 0.65. Collectively, the proposed framework of synchronized process monitoring and real-time analysis provides a pathway to achieve dimensionally consistent and defect-free parts, and highlights the potential for closed-loop control systems for a wider industrial application of DED-Arc. T2 - IIW Annual Assembly 2025 CY - Genova, Italy DA - 23.06.2025 KW - Additive Manufacturing KW - Arc welding KW - Real-time monitoring and control KW - Dimensional inconsistency KW - DED-arc PY - 2025 AN - OPUS4-65231 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bevilacqua, Tommaso A1 - Gumenyuk, Andrey A1 - Habibi, Niloufar A1 - Hartwig, Philipp A1 - Klawonn, Axel A1 - Lanser, Martin A1 - Rethmeier, Michael A1 - Scheunemann, Lisa A1 - Schröeder, Jöerg T1 - Large-scale thermo-mechanical simulation of laser beam welding using high-performance computing: A qualitative reproduction of experimental results N2 - Laser beam welding (LBW) is a non-contact joining technique that has gained significant importance in modern industrial manufacturing. One potential problem, however, is the formation of solidification cracks, which particularly affects alloys with a pronounced melting range. The aim of the present work is the development of computational methods and software tools to numerically simulate LBW. In order to obtain a sufficiently accurate solution, a large number of finite elements has to be used. Therefore, a highly parallel scalable solver framework, based on the software library PETSc, was used to solve this computationally challenging problem on a high-performance computing architecture. Finally, the experimental results and the numerical simulations are compared. They are found to be in good qualitative agreement, which confirms the validity of the numerical simulations and allows for a better interpretation of the experimentally observed strain distribution. KW - Laser beam welding KW - Termo-mechanical processes KW - Solidification cracking KW - High-performance computing KW - Domain decomposition methods PY - 2025 DO - https://doi.org/10.1016/j.rineng.2025.108827 SN - 2590-1230 SP - 1 EP - 33 PB - Elsevier B.V. AN - OPUS4-65290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Phase-field simulation of the dendrite fragmentation by electromagnetic stirring in AA5754 aluminum alloy laser beam welding N2 - A phase-field model including magnetic field induced dendrite fragmentation was established and applied to the cases with different initial crystal nuclear positions for AA5754 aluminum alloy electromagnetic laser beam welding. Compare the calculated results that include dendrite fragmentation caused by the thermal electromagnetic Lorentz force with the results that consider only the thermal electromagnetic Lorentz force, without fragmentation, at the characteristic time instants. Both in the early and late stages, the small fragmentation at the dendrite tip promotes the number of higher-order branches and their growth, especially in the direction perpendicular to the solidification. The later stage fragmentation has the possibility of breaking one grain into several, which verifies the possibility of grain refinement caused by dendrite fragmentation. The fracture surface caused by fragmentation also makes more solid-liquid interfaces and their growth. In addition, the cases with different initial nuclear positions were compared. The grain growth in the low-temperature zone can be inhibited by the equiaxed grains' fragmentation at the high-temperature area (179.8 μm² and 14.7 % start at the center, 115.4 μm² and 9.4 % start at the high-temperature corner, 134.3 μm² and 10.9 % start at the low-temperature corner), which is another kind of grain refinement by the dendrite fragmentation. This kind of inhibition effect on grain growth in the low-temperature region will be enhanced with the increasing time interval between the two crystal nuclei’ appearance (179.8 μm² and 14.7 % when virtual grains appear at t = 4.3803 s and t = 4.3803 s, 134.3 μm² and 10.9 % at t = 4.0977 s and t = 3.9564 s, and 115.4 μm² and 9.4 % at t = 3.8151 s and t = 3.5325 s). KW - Laser beam welding KW - Electromagnetic KW - Aluminum alloys KW - Phase field method KW - Equiaxed grain KW - Dendrite fragmentation PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-656610 DO - https://doi.org/10.1016/j.cwe.2025.100014 SN - 3117-4159 VL - 35 IS - 1 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-65661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -