TY - JOUR A1 - Üstündağ, Ö. A1 - Fritzsche, André A1 - Avilov, V. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser-arc welding of thick-walled ferromagnetic steels with electromagnetic weld pool support N2 - The hybrid laser-arc welding (HLAW) process provides many advantages over laser welding and arc welding alone, such as high welding speed, gap bridgeability, and deep penetration. The developments in hybrid laser-arc welding technology using modern high-power lasers allow single-pass welding of thick materials. This technology can be used for the heavy metal industries such as shipbuilding, power plant fabrication, and line-pipe manufacturing. The obvious problem for single-pass welding is the growth of the hydrostatic pressure with increasing thickness of materials leading to drop-out of molten metal. This phenomenon is aggravated at slow welding velocities because of increasing weld seam width followed by a decrease of Laplace pressure compensating the hydrostatic pressure. Therefore, weld pool support is necessary by welding of thick materials with slow welding velocities. The innovative electromagnetic weld pool support system is contactless and has been used successfully for laser beam welding of aluminum alloys and austenitic and ferromagnetic steels. The support system is based on generating Lorentz forces within the weld pool. These are produced by an oscillating magnetic field orientated perpendicular to the welding direction. The electromagnetic weld pool support facilitates a decrease in the welding speed without a sagging and drop-out of the melt thus eliminating the limitations of weldable material thickness. KW - Hybrid laser-arc welding KW - Thick-walled steel KW - Electromagnetic weld pool support KW - Ferromagnetic steels KW - High-power laser beam PY - 2018 DO - https://doi.org/10.1007/s40194-018-0597-3 SN - 1878-6669 VL - 62 IS - 4 SP - 767 EP - 774 PB - Springer AN - OPUS4-46825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser-arc welding of thick-walled pipe segments with optimization of the end crater N2 - The study deals with the application of the high-power hybrid-laser arc welding process on up to 15 mm thick pipe segments with the intention to avoid end crater imperfections during closing of the circumferential welds, where the pipes were turned during welding in 1G- and 2Gpositions. Different techniques such as laser power ramp-down, abrupt switch-off of the laser power and change of the magnification of the laser spot diameter and defocusing of the laser beam relative to the workpiece were tested to remove the laser energy from the process. It could be shown that a high defocusing of the optic system above 40 mm with a resulting beam diameter > 2.9 mm in a short overlap length of approx. 20 mm leads to the formation of a cup-shaped weld seam, which is preferred for avoidance of cracks and pores in the end crater. A laser optics with motor-driven lens system was used for the welding experiments to defocuse the laser beam without changing the position of the arc. KW - Hybrid laser-arc welding KW - Circumferential weld KW - Thick-walled steel KW - Single-pass welding KW - End crater PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-513260 DO - https://doi.org/10.1016/j.procir.2020.09.106 VL - 94 SP - 676 EP - 679 PB - Elsevier B.V. AN - OPUS4-51326 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Pittner, Andreas A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Einlagiges MSG-Hochleistungsschweißen von dickwandigen Baustählen mit kontaktloser elektromagnetischer Schmelzbadsicherung N2 - Diese Arbeit zeigt erstmals die Anwendung einer elektromagnetischen Schmelzbadsicherung beim einlagigen MSG-Schweißen von dickwandigen Stählen. Die innovativen Entwicklungen im Bereich des Lichtbogenschweißverfahrens ermöglichen eine Erhöhung der Abschmelzleistung, um die Einschweißtiefe zu steigern. Somit kann die Lagenanzahl reduziert und die Produktivität gesteigert werden. Allerdings besteht insbesondere beim einlagigen Schweißen von dickwandigen Bauteilen in PA-Position ein erhöhtes Risiko für das gravitationsbedingte Austropfen der Schmelze an der Wurzel. Zur Verhinderung werden Badsicherungen eingesetzt, die mechanisch angebracht und nach dem Schweißen entfernt werden müssen, was zeit- und kostenintensiv ist. Die im Rahmen dieser Studie eingesetzte elektromagnetische Schmelzbadsicherung wirkt dem gravitationsbedingten Austropfen der Schmelze entgegen und kompensiert den hydrostatischen Druck. Sie wirkt kontaktlos, was im Gegensatz zu herkömmlichen Badsicherungen vorteilhaft ist, so dass auf eine zeit- und kostenintensive Nachbearbeitung der Schweißnahtwurzel verzichtet werden kann. Das auf extern angelegten oszillierenden Magnetfeldern beruhende Verfahren wird dabei unterhalb des zu schweißenden Bauteils positioniert. Die Magnetfeldlinien sind quer zur Schweißrichtung ausgerichtet, sodass längs zur Schweißrichtung Wirbelströme im Werkstück und eine stets nach oben gerichtete Lorentzkraft generiert werden. Mit Hilfe der elektromagnetischen Badsicherung konnten beim einlagigen MSG-Schweißen von bis zu 10 mm dicken Blechen die Tropfenbildung vermieden werden. Die innovative Technologie ermöglicht es, dickwandige Bauteile einlagig zu schweißen und reduziert die Nachbearbeitungszeiten und -kosten deutlich. T2 - DVS Congress 2022 - Große Schweißtechnische Tagung CY - Koblenz, Germany DA - 19.09.2022 KW - Elektromagnetische Schmelzbadsicherung KW - Hochleistungsschweißen KW - MSG-Schweißen PY - 2022 SN - 978-3-96144-189-1 VL - 382 SP - 640 EP - 645 PB - DVS Media GmbH AN - OPUS4-56371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Elektromagnetische Schmelzbadbeeinflussung beim Laserhybridschweißen von Dickblechen N2 - Die technischen Entwicklungen in der Lasertechnologie in den letzten Jahrzehnten haben eine neue Generation von Hochleistungslasersystemen im Leistungsbereich bis zu 100 kW auf den Markt gebracht. Dennoch ist die industrielle Anwendung des Hochleistungslaserstrahlschweißens auf bis zu 15 mm dicke Bleche beschränkt. Mögliche Ursachen der Einschränkungen des Verfahrens sind z.B. die Sensibilität des Verfahrens auf Fertigungstoleranzen wie Spalt und Kantenversatz, die erhöhte Tropfenbildung bei höheren Blechdicken und eine inhomogene Verteilung des Zusatzwerkstoffes beim Laserhybridschweißen. In dieser Studie wird ein auf extern angelegte Magnetfelder basierte elektromagnetische Schmelzbadstütze eingesetzt, um die Grenzen des Verfahrens zu erweitern und die Herausforderungen zu minimieren. Der wesentliche Vorteil der elektromagnetischen Schmelzbadstütze ist, dass sie berührungslos arbeitet. Mit Hilfe der elektromagnetischen Schmelzbadstütze konnten bei 20 mm dicken Proben aus S355J2 die Tropfenbildung an der Wurzel vermieden werden. Zudem wurde der Einfluss der Kantenqualität auf die Schweißnahtqualität untersucht, wobei verschiedene Schneidverfahren zur Kantenvorbereitung eingesetzt wurden, wie z.B. Plasma-, Brenn- oder Laserschneiden. Es konnte gezeigt werden, dass auch bei schlechteren Kantenvorbereitung im Gegensatz zu gefrästen Bauteilen die Werkstoffe einlagig mittels Laserhybridschweißen bei einer hohen Schweißnahtqualität gefügt werden konnten. Bei plasmageschnittenen Proben wurden zudem eine Spaltüberbrückbarkeit bzw. Kantenversatz von bis zu 2 mm sicher überbrückt. Des Weiteren war es mit Hilfe der externen Magnetfelder möglich, die Durchmischung des Zusatzwerkstoffes über die gesamte Schweißnahttiefe deutlich zu homogenisieren. T2 - 42. Assistentenseminar der Wissenschaftlichen Gesellschaft Fügetechnik e.V. CY - Blankenau, Germany DA - 06.10.2021 KW - Elektromagnetische Schmelzbadstütze KW - Laserhybridschweißen KW - Dickblech PY - 2022 VL - 385 SP - 1 EP - 7 PB - DVS Media GmbH AN - OPUS4-56375 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of an external applied AC magnetic field on the melt pool dynamics at high-power laser beam welding N2 - The study deals with the determination of the influence of an externally applied oscillating magnetic field on the melt pool dynamics in high power laser beam and hybrid laser arc welding processes. An AC magnet was positioned under the workpiece which is generating an upward directed electromagnetic force to counteract the formation of the droplets. To visualise the melt flow characteristics, several experiments were carried out using a special technique with mild steel from S355J2 with a plate thickness of up to 20 mm and a quartz glass in butt configuration. The profile of the keyhole and the melt flow were recorded with a highspeed camera from the glass side. Additionally, the influence of the magnetic field orientation to the welding direction on the filler material dilution on laser hybrid welding was studied with variating oscillation frequency. The element distribution over the whole seam thickness was measured with X-ray fluorescence (XRF). The oscillation frequency demonstrated a great influence on the melt pool dynamics and the mixing of the elements of the filler wire. The highspeed recordings showed, under the influence of the magnetic field, that the melt is affected under strong vortex at the weld root, which also avoids the formation of droplets. T2 - 18th Nordic Laser Materials Processing Conference (18th NOLAMP) KW - Laser beam welding KW - AC magnetic field KW - Melt pool dynamics KW - Filler wire mixing PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539231 DO - https://doi.org/10.1088/1757-899X/1135/1/012017 VL - 1135 IS - 012017 SP - 1 EP - 10 PB - IOP Publishing AN - OPUS4-53923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Investigation of the gap bridgeability at high-power laser hybrid welding of plasma-cut thick mild steels with AC magnetic support N2 - One of the challenges of the high-power hybrid laser welding of thick steels is the sensitivity of the process of the process to manufacturing tolerances. This usually leads to a time-consuming preparation of the welding edges, such as milling. The study deals with the influence of the edge quality of milled and plasma-cut steel made of S355J2 with a wall thickness of 20 mm on the laser hybrid welded seam quality. Furthermore, the gap bridgeability and the tolerances towards edge misalignment was investigated. An AC magnet was used as backing support to prevent sagging and positioned under the workpiece, to generate an upwards directed electromagnetic pressure. The profiles of the edges and the gap on the top and root side were measured using a digital camera. Single-pass laser hybrid welds of plasma-cut edges could be welded using a laser beam power of just 13.7 kW. A gap bridgeability up to 2 mm and misalignment of edges up to 2 mm could be achieved successful. Additionally, the independence of the cutting side and the welding side was shown, so that samples were welded to the opposite side to their cutting. For evaluation of internal defects or irregularities, X-ray images were carried out. Charpy impact strength tests were performed to determine the toughness of the welds. T2 - X International Conference «Beam Technologies & Laser Application» KW - Laser hybrid welding KW - Magnetic bath support KW - Plasma-cut samples KW - Thick plate welding PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-539248 DO - https://doi.org/10.1088/1742-6596/2077/1/012007 VL - 2077 IS - 012007 SP - 1 EP - 8 PB - IOP Publishing AN - OPUS4-53924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Improvement of Charpy impact toughness by using an AC magnet backing system for laser hybrid welding of thick S690QL steels N2 - The study deals with the influence of the heat input and the resulting cooling times on the microstructure and Charpy impact toughness of single-pass laser hybrid welded 20-mm thick high-strength steel S690QL. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured in-situ using a pyrometer and an optical fibre in three different depths of the seam where Charpy impact test specimens were also later taken. Thereby, three different heat inputs from 1.3 kJ/mm to 2 kJ/mm were investigated. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required impact toughness of 38 J/cm2 could be reached in dependance on applied heat input, especially at the heat input of 1.6 kJ/mm. T2 - 12th CIRP conference on photonic technologies [lane 2022] CY - Fürth, Germany DA - 04.09.2022 KW - Thick-plate welding KW - Laser hybrid welding KW - Electromagnetic backing KW - Charpy impact toughness KW - Thermal cycles PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-563731 DO - https://doi.org/10.1016/j.procir.2022.08.067 VL - 111 SP - 462 EP - 465 PB - Elsevier B.V. AN - OPUS4-56373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of oscillating magnetic field on the keyhole stability in deep penetration laser beam welding N2 - The stability of the keyhole decreases for deep penetrated high-power laser beam welding. The keyhole tends to collapse with increasing laser power and e.g. keyhole induced porosity can occur. This study deals with the observation of the keyhole during high-power laser beam welding in partial penetration mode by means of a high-speed camera. A butt configuration of 25 mm thick structural steel and transparent quartz glass was used for the experiments. An oscillating magnetic field was applied perpendicular to the welding direction on the root side of the steel plate. The keyhole was highlighted with a coaxial diode laser. It was ascertained that the stability of the keyhole and the weld penetration depth were increased by applying an oscillating magnetic field with an oscillating frequency of 1.2 kHz and a magnetic flux density of 50 mT. KW - Magnetic field KW - Laser beam welding KW - Keyhole stability PY - 2021 DO - https://doi.org/10.1016/j.optlastec.2020.106715 SN - 0030-3992 VL - 135 SP - 106715 PB - Elsevier Ltd. AN - OPUS4-52007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Thermal Cycles and Charpy Impact Toughness of Single-Pass Hybrid Laser-Arc Welded Thick-Walled Structures N2 - The study deals with the influence of the heat input on the thermal cycles and Charpy impact toughness for hybrid laser-arc welding of 25 mm thick structural steel S355J2 using a 20-kW high-power laser in combination with an electromagnetic weld pool support. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured using a pyrometer in combination with an optical fibre in three different locations near to fusion lines corresponding to different heights of the seam. Also, Charpy impact specimens were taken from different parts of the weld joint corresponding to the different heights. The influence of the heat input was investigated for 1.8 kJ mm-1 and 3.2 kJ mm-1. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required values could be reached in dependance on applied heat input. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - laser hybrid welding KW - Charpy impact toughness KW - thick plate welding KW - thermal cycles PY - 2021 SP - 1 EP - 8 AN - OPUS4-53926 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Neueste Entwicklungen im Bereich des Hochleistungslaserstrahl- und Hybridschweißens von hohen Blechdicken N2 - Bislang kommt das Laserstrahlschweißen bzw. Laserhybridschweißen hauptsächlich bei Dickblechen mit einer Wandstärke von bis zu 15 mm zum Einsatz. Für Anwendungen über 20 mm war dieses Verfahren aufgrund einiger Herausforderungen bisher nur bedingt realisierbar. Eine von der Bundesanstalt für Materialforschung und -prüfung (BAM) entwickelte elektromagnetische Schmelzbadunterstützung ermöglicht nun ein einlagiges Schweißen von bis zu 30 mm Wandstärke. KW - Laserstrahlschweißen KW - Laserhybridschweißen KW - Modellierung KW - Elektromagnetische Schmelzbadunterstützung KW - Kaltzähe Stähle PY - 2020 VL - 2 SP - 26 EP - 30 PB - DVV Media Group GmbH CY - Hamburg AN - OPUS4-51632 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser‑arc welding of laser‑ and plasma‑cut 20‑mm‑thick structural steels N2 - It is already known that the laser beam welding (LBW) or hybrid laser-arc welding (HLAW) processes are sensitive to manufacturing tolerances such as gaps and misalignment of the edges, especially at welding of thick-walled steels due to its narrow beam diameter. Therefore, the joining parts preferably have to be milled. The study deals with the influence of the edge quality, the gap and the misalignment of edges on the weld seam quality of hybrid laser-arc welded 20-mm-thick structural steel plates which were prepared by laser and plasma cutting. Single-pass welds were conducted in butt joint configuration. An AC magnet was used as a contactless backing. It was positioned under the workpiece during the welding process to prevent sagging. The profile of the edges and the gap between the workpieces were measured before welding by a profile scanner or a digital camera, respectively. With a laser beam power of just 13.7 kW, the single-pass welds could be performed. A gap bridgeability up to 1 mm at laser-cut and 2 mm at plasma-cut samples could be reached respectively. Furthermore, a misalignment of the edges up to 2 mm could be welded in a single pass. The new findings may eliminate the need for cost and time-consuming preparation of the edges. KW - Hybrid laser-arc welding KW - Thick-walled steel KW - Edge quality KW - Gap bridgeability KW - Laser cutting KW - Plasma cutting PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552013 DO - https://doi.org/10.1007/s40194-022-01255-y SN - 0043-2288 VL - 66 SP - 507 EP - 514 PB - Springer AN - OPUS4-55201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid Laser-Arc Welding of Thick-Walled, Closed, Circumferential Pipe Welds N2 - The application of hybrid laser-arc welding (HLAW) for joining closed circumferential welds is a challenge due to the high risk of forming a defective overlap area with a shrinkage void or solidification cracks in the material thickness. A series of HLAW experiments were performed to understand the development of a faulty overlap area when closing the circumferential weld. Welding trials on flat specimens and pipe segments were supported by numerical analyses in which the thermomechanical behavior of the welds in the overlap area was investigated. Different process control strategies were tested, including variations in defocusing levels and the overlap length. The newly developed HLAW head, including laser optics with a motor-driven collimation system, made it possible to defocus the laser beam during welding without disturbing the stability of the welding process. High-level defocusing of the laser beam of more than 40 mm relative to the specimen surface with a resulting beam diameter of > 2.9 mm, and in combination with a short overlap length of 15 mm, was promising with respect to the formation of a desired cup-shaped weld profile that is resistant to solidification cracks. KW - Hybrid Laser-Arc Welding KW - Thick-Walled Steel KW - High-Power Welding KW - Crater KW - Pipe Welding PY - 2022 DO - https://doi.org/10.29391/2022.101.002 SN - 0043-2296 VL - 101 IS - 1 SP - 15 EP - 26 PB - American Welding Society CY - New York, NY AN - OPUS4-55508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Brunner-Schwer, C. A1 - Knöfel, F. A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laserstrahlhybridschweissen von Türmen für Windkraftanlagen Ökonomische und ökologische Vorteile N2 - Das Laserstrahlhybridschweißen ist beim Schweißen von Türmen für Windkraftanlagen eine Alternative zum Unterpulverschweißen von Dickblechen in Mehrlagentechnik und bietet hier ökonomische und ökologische Vorteile. Der industrielle Einsatz des Verfahrens ist jedoch durch prozessspezifische Herausforderungen eingeschränkt. Die im Beitrag beschriebene kontaktlose elektromagnetische Badstütze dient zur Erweiterung des Verfahrenspotenzials im Dickblechbereich >15 mm. KW - Elektromagnetische Badstütze KW - Laserhybridschweißen KW - Windkraftanlagen KW - Ökonomische und ökologische Vorteile PY - 2022 VL - 7 SP - 340 EP - 347 PB - DVS Media GmbH AN - OPUS4-56372 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - High-power hybrid laser arc welding of thick materials with electromagnetic weld pool support N2 - In addition to the many advantages of deep penetration, increased welding speed and a low sensitivity to manufacturing tolerances such as gap and edge offset, the hybrid laser arc welding (HLAW) process is used increasingly in industrial applications such as shipbuilding or pipeline manufacturing. Nonetheless, thick-walled sheets with a wall thickness of 20 mm or more are still multi-pass welded using the arc welding process, due to increased process instability by increasing laser power. Welding at reduced speed, especially in a flat position, leads to an irregular formation of the root part such as dropping. The hydrostatic pressure exceeds the surface tension, which decreases with increasing seam width. In order to prevent gravity drop-outs, the use of a melt pool support is necessary. Usual weld pool supports such as ceramic or powder supports require time-consuming mechanical detachment. The electromagnetic weld pool support system, which is described in this study, operates without contact and based on generating Lorentz forces in the weld pool. An externally applied oscillating magnetic field induces eddy currents and generates an upward directed Lorentz force, which counteracts the hydrostatic pressure. This allows single-pass welds up to 30 mm by hybrid laser arc welding process with a 20-kW fibre laser. Moreover, it is favoured by the diminished welding speed the cooling rate which leads to an improvement of the mechanical-technological properties of the seams – the lower formation of martensite in the microstructure enables better Charpy impact toughness. The electromagnetic weld pool support extends the limitation of the laser hybrid welding process in the thick sheet area. By adapting the electromagnetic weld pool support to the laser and laser hybrid welding process, the application potential of these technologies for industrial implementation can be drastically increased. T2 - 23rd Technical Conference on Welding and Joining Technologies CY - Irun, Spain DA - 07.03.2023 KW - Laser hybrid welding KW - Thick-walled steel KW - Electromagnetic backing KW - High-power laser PY - 2023 AN - OPUS4-58613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Influence of shielding gas on filler wire mixing at laser hybrid welding of thick high strength steels N2 - The laser hybrid welding process offers many advantages during welding oft hick-walled steels, such as the increased penetration depth and, thus, reduced number of layers, reduced heat input and decreased distortion compared to arc-based welding processes. Especially, when welding high-strength steels (HSS), the reduced heat input plays an essential role. However, a major challenge when laser hybrid welding of thick-walled steels is the limited filler wire mixing over the entire seam thickness, which can lead to changed mechanical properties over the depth. To overcome this issue, the add of oxygen into the shielding gas and its influence on the filler wire mixing and finally to the mechanical properties were investigated within this work. Therefore, 20 mm thick S690QL steels were laser hybrid welded in a single-pass. A contactless electromagnetic backing was used to avoid sagging. The admixture of oxygen was performed by a gas mixer, where the oxygen content was varied between 0 % and 7.2 %. The experiments were also accompanied by laser beam welding tests in steel/glass configuration, where the melt pool geometry as well as the melt flow characteristics were captured by a high-speed camera. It can be concluded, that adding of 2 % to 4 % oxygen into the shielding gas had a positive effect on the filler wire mixing, were up to a depth of 18 mm elements of the filler wire could be observed. T2 - 19th Nordic Laser Material Processing Conference CY - Turku, Finland DA - 22.08.2023 KW - Laser hybrid welding KW - Electromagnetic backing KW - Shielding gas KW - Charpy impact toughness KW - Thick-plate welding KW - Filler wire mixing PY - 2023 AN - OPUS4-58615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Einlagiges MSG-Hochleistungsschweißen von dickwandigen Baustählen mit kontaktloser elektromagnetischer Schmelzbadsicherung N2 - Diese Arbeit zeigt erstmals die Anwendung einer elektromagnetischen Schmelzbadstütze beim einlagigen MSG-Schweißen von dickwandigen Stählen. Die innovativen Entwicklungen im Bereich des Lichtbogenschweißverfahrens ermöglichen eine Erhöhung der Abschmelzleistung, um die Einschweißtiefe zu steigern. Somit kann die Lagenanzahl reduziert und die Produktivität gesteigert werden. Allerdings besteht insbesondere beim einlagigen Schweißen von dickwandigen Bauteilen in PA-Position ein erhöhtes Risiko für das gravitationsbedingte Austropfen der Schmelze an der Wurzel. Zur Verhinderung werden Badstützen eingesetzt, die mechanisch angebracht und nach dem Schweißen entfernt werden müssen, was zeit- und kostenintensiv ist. Die im Rahmen dieser Studie eingesetzte elektromagnetische Schmelzbadstütze wirkt dem gravitationsbedingten Austropfen der Schmelze entgegen und kompensiert den hydrostatischen Druck. Sie wirkt kontaktlos, was im Gegensatz zu herkömmlichen Badstützen vorteilhaft ist, so dass auf eine zeit- und kostenintensive Nachbearbeitung der Schweißnahtwurzel verzichtet werden kann. Das auf extern angelegten oszillierenden Magnetfeldern beruhende Verfahren wird dabei unterhalb des zu schweißenden Bauteils positioniert. Die Magnetfeldlinien sind quer zur Schweißrichtung ausgerichtet, sodass längs zur Schweißrichtung Wirbelströme im Werkstück und eine stets nach oben gerichtete Lorentzkraft generiert werden. Mit Hilfe der elektromagnetischen Badstütze konnten beim einlagigen MSG-Schweißen von 8 mm bis 12 mm die Tropfenbildung vermieden werden. Die innovative Technologie ermöglicht es dickwandige Bauteile einlagig zu schweißen und reduziert die Nachbearbeitungszeit deutlich. T2 - DVS Congress 2022 - Große Schweißtechnische Tagung CY - Koblenz, Germany DA - 19.09.2022 KW - Hochleistungsschweißen KW - MSG-Schweißen KW - Elektromagnetische Schmelzbadsicherung PY - 2022 AN - OPUS4-56368 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Hybrid laser-arc welding of thick-walled pipe segments with optimization of the end crater N2 - The study deals with the application of the high-power hybrid-laser arc welding process on up to 15 mm thick pipe segments with the intention to avoid end crater imperfections during closing of the circumferential welds, where the pipes were turned during welding in 1G- and 2G-positions. Different techniques such as laser power ramp-down, abrupt switch-off of the laser power and change of the magnification of the laser spot diameter and defocusing of the laser beam relative to the workpiece were tested to remove the laser energy from the process. It could be shown that a high defocusing of the optic system above 40 mm with a resulting beam diameter > 2.9 mm in a short overlap length of approx. 20 mm leads to the formation of a cup-shaped weld seam, which is preferred for avoidance of cracks and pores in the end crater. A laser optics with motor-driven lens system was used for the welding experiments to defocuse the laser beam without changing the position of the arc. T2 - 11th CIRP Conference on Photonic Technologies LANE 2020 CY - Online Meeting DA - 07.09.2020 KW - End crater KW - Hybrid laser-arc welding KW - Circumferential weld PY - 2020 AN - OPUS4-51634 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Influence of heat input on cooling rates and mechanical properties of laser hybrid welded thick structural steels N2 - The laser hybrid welding process offers many advantages such as the high penetration depth and high welding speed, and it is characterized by its low heat input compared to the arc-based welding processes, which makes the laser hybrid welding process as a suitable alternative process when welding thick-walled steels. However, there are some challenges when using laser hybrid welding process for thick steels. Due to the uneven cooling conditions and the inhomogeneous filler wire mixing, a typical laser hybrid weld can be divided into two different zones over the depth: the arc-dominated zone on the upper part and the laser-dominated zone in the root part. This leads to different mechanical properties in a laser hybrid welded joint. Due to the high cooling rates and the lack of filler wire in the laser-dominated zone, this area is more critical regarding the mechanical properties, especially the Charpy impact toughness. A low heat input can lead to undesired microstructure consisting of martensite, hardening and deteriorated impact toughness due to the high cooling rate, where higher heat inputs can lead to grain-coarsening and even loss of impact strength. This study deals with the influence of the welding speed and resulting heat input on the cooling rates, the microstructure and the mechanical properties of single-pass laser hybrid welded steels of S355J2 with thickness up to 30 mm. The experiments were performed with a 20-kW fibre laser system and a contactless electromagnetic weld backing on up to 30 mm thick steels in butt-joint configuration in 1G welding position. The cooling time was measured in three different locations near to fusion lines corresponding to different heights of the seam using a special configuration with pyrometers, collimators, and optical fibres. The test specimens for the Charpy impact testing and tensile testing were extracted in up to three different depths. Based on the experiments, a heat input of 1.3 kJ/mm - 1.6 kJ/mm, 2 kJ/mm - 2.4 kJ/mm and 3.7 kJ/mm were recommended when single-pass laser hybrid welding of 20 mm, 25 mm and 30 mm thick structural steels in regard to the minimum requirements of the mechanical properties, respectively. The optical measurement of the cooling times in different depths could be carried out reproducibly. T2 - Advances in Welding and Metal Additive Manufacturing Technologies 2023 CY - Istanbul, Türkiye DA - 30.10.2023 KW - Laser hybrid welding KW - Electromagnetic backing KW - Charpy impact toughness KW - Thick-plate welding KW - Thermal cycles PY - 2023 AN - OPUS4-58942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Thermal Cycles and Charpy Impact Toughness of Single-Pass Hybrid Laser-Arc Welded Thick-Walled Structures N2 - The study deals with the influence of the heat input on the thermal cycles and Charpy impact toughness for hybrid laser-arc welding of 25 mm thick structural steel S355J2 using a 20-kW high-power laser in combination with an electromagnetic weld pool support. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured using a pyrometer in combination with an optical fibre in three different locations near to fusion lines corresponding to different heights of the seam. Also, Charpy impact specimens were taken from different parts of the weld joint corresponding to the different heights. The influence of the heat input was investigated for 1.8 kJ mm-1 and 3.2 kJ mm-1. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required values could be reached in dependance on applied heat input. T2 - Lasers in Manufacturing Conference 2021 CY - Online meeting DA - 21.06.2021 KW - Hybrid laser-arc welding KW - Thick-walled structures KW - Charpy impact toughness KW - Thermal cycles PY - 2021 AN - OPUS4-53576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Üstündag, Ömer T1 - Improvement of Charpy impact toughness by using an AC magnet backing system at laser hybrid welding of thick S690QL steels N2 - The study deals with the influence of the heat input and the resulting cooling times on the microstructure and Charpy impact toughness of single-pass laser hybrid welded 20-mm thick high-strength steel S690QL. The main focus is on the change of the mechanical properties over the entire seam thickness. The cooling times were measured in-situ using a pyrometer and an optical fibre in three different depths of the seam where Charpy impact test specimens were also later taken. Thereby, three different heat inputs from 1.3 kJ/mm to 2 kJ/mm were investigated. Despite the observed decreased values of both t8/5-cooling time and the Charpy impact toughness in the root part of the seam, the required impact toughness of 38 J/cm2 could be reached in dependance on applied heat input, especially at the heat input of 1.6 kJ/mm. T2 - LANE 2022: 12th CIRP Conference on Photonic Technologies CY - Fürth, Germany DA - 04.09.2022 KW - Laser hybrid welding KW - Electromagnetic backing KW - Charpy impact toughness KW - Thick-plate welding KW - Thermal cycles PY - 2022 AN - OPUS4-56369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -