TY - JOUR A1 - Mull, Birte A1 - Möhlmann, L. A1 - Wilke, Olaf T1 - Photocatalytic degradation of toluene, butyl acetate and limonene under UV and visible light with titanium dioxide-graphene oxide as photocatalyst N2 - Photocatalysis is a promising technique to reduce volatile organic compounds indoors. Titanium dioxide (TiO2) is a frequently-used UV active photocatalyst. Because of the lack of UV light indoors, TiO2 has to be modified to get its working range shifted into the visible light spectrum. In this study, the photocatalytic degradation of toluene, butyl acetate and limonene was investigated under UV LED light and blue LED light in emission test chambers with catalysts either made of pure TiO2 or TiO2 modified with graphene oxide (GO). TiO2 coated with different GO amounts (0.75%–14%) were investigated to find an optimum ratio for the photocatalytic degradation of VOC in real indoor air concentrations. Most experiments were performed at a relative humidity of 0% in 20 L emission test chambers. Experiments at 40% relative humidity were done in a 1 m³ emission test chamber to determine potential byproducts. Degradation under UV LED light could be achieved for all three compounds with almost all tested catalyst samples up to more than 95%. Limonene had the highest degradation of the three selected volatile organic compounds under blue LED light with all investigated catalyst samples. KW - Photocatalysis KW - Emission test chamber KW - Volatile organic compound KW - VOC KW - Degradation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-402955 DO - https://doi.org/10.3390/environments4010009 SN - 2076-3298 VL - 4 IS - 1 SP - Article 9, 1 EP - 9 PB - MDPI CY - Basel AN - OPUS4-40295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pavlovic, Mato A1 - Zoëga, Andreas A1 - Kurz, J. H. A1 - Zanotelli, Christina T1 - Investigations to introduce the probability of detection method for ultrasonic inspection of hollow axles at Deutsche Bahn N2 - The vast experience with the automated, ultrasonic system for the inspection of hollow railway axles used by Deutsche Bahn shows that much smaller flaws are detectable than required. This results in a number of false calls. False calls lead to unnecessary demounting and disassembling of wheelsets, which generates unnecessary additional costs. In order to adjust the sensitivity of the inspection system to reduce the number of false calls without compromising safety, the capability of the system to detect cracks needs to be comprehensively established. This capability can be quantified by using probability of detection (POD) curves for the system. The multi-parameter POD model makes it possible to include several factors that influence the crack detection in the analysis. The analysis presented in this paper shows that crack position, orientation, depth extension, and shape as well as the geometry of the axle all have influence on the ultrasonic response amplitude. For future work, calculation of the POD using multi-parameter POD model with these parameters is planned. T2 - ESIS TC24 Workshop "Integrity of Railway Structures" CY - Leoben, Austria DA - 24.10.2016 KW - Crack KW - Reliability KW - POD KW - Axle KW - Ultrasonic PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-415201 DO - https://doi.org/10.1016/j.prostr.2017.07.002 SN - 2452-3216 VL - 4 SP - 79 EP - 86 PB - Elsevier, B.V. AN - OPUS4-41520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tuma, Dirk A1 - Kumbhar, V. S. A1 - Lee, Y. R. A1 - Ra, C. S. A1 - Min, B.-K. A1 - Shim, J.-J. T1 - Modified chemical synthesis of MnS nanoclusters on nickel foam for high performance all-solid-state asymmetric supercapacitors N2 - Novel MnS nanoclusters were synthesized on nickel foam (NF) using a successive ionic layer adsorption and reaction (SILAR) method. MnS nanoclusters with different sizes were obtained by varying the number of deposition cycles. The crystal structure, chemical composition, and surface microstructure of the electrodes were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, field Emission scanning electron microscopy, and high-resolution transmission electron microscopy. The electrochemical behavior of the MnS nanoclusters was examined by cyclic voltammetry, galvanostatic charge–discharge, cycling test, and electrochemical impedance spectroscopy. The MnS nanoclusters prepared with 90 SILAR cycles showed the best supercapacitance in a 6 M KOH aqueous electrolyte with a specific capacitance of 828 F/g at a scan rate of 5 mV/s and cycling stability of 85.2 % after 5000 charge–discharge cycles. Moreover, an asymmetric supercapacitor (ASC) was assembled with the as-prepared MnS electrode on NF as the positive electrode, hydrothermally prepared reduced graphene oxide (rGO) on NF as the negative electrode, and PVA–KOH gel as the electrolyte. The MnS@NF//rGO@NF ASC showed excellent electrochemical performance with maximum energy and power densities of 34.1 Wh/kg and 12.8 kW/kg, respectively. The ASC also showed a capacitive retention of 86.5 % after 2000 charge–discharge cycles, highlighting its practical application for energy storage. KW - Nanocluster KW - Electrochemical behavior KW - Asymmetric supercapacitor KW - Graphene oxide PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-403147 DO - https://doi.org/10.1039/c7ra00772h SN - 2046-2069 VL - 7 IS - 27 SP - 16348 EP - 16359 PB - The Royal Society of Chemistry CY - London AN - OPUS4-40314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lichtenstein, D. A1 - Ebmeyer, J. A1 - Meyer, T. A1 - Behr, A.-C. A1 - Kästner, Claudia A1 - Böhmert, L. A1 - Juling, J. A1 - Niemann, B. A1 - Fahrenson, C. A1 - Selve, S. A1 - Thünemann, Andreas A1 - Meijer, J. A1 - Estrela-Lopis, I. A1 - Bräuning, A. A1 - Lampen, A. T1 - It takes more than a coating to get nanoparticles through the intestinal barrier in vitro N2 - Size and shape are crucial parameters which have impact on the potential of nanoparticles to penetrate cell membranes and epithelial barriers. Current research in nanotoxicology additionally focuses on particle coating. To distinguish between core- and coating-related effects in nanoparticle uptake and translocation, two nanoparticles equal in size, coating and charge but different in core material were investigated. Silver and iron oxide nanoparticles coated with poly(acrylic acid) were chosen and extensively characterized by small-angle x-ray scattering, nanoparticle tracing analysis and transmission electron microscopy (TEM). Uptake and transport were studied in the intestinal Caco-2 model in a Transwell System with subsequent elemental analysis. TEM and ion beam microscopy were conducted for particle visualization. Although equal in size, charge and coating, the behavior of the two particles in Caco-2 cells was different: while the internalized amount was comparable, only iron oxide nanoparticles additionally passed the epithelium. Our findings suggest that the coating material influenced only the uptake of the nanoparticles whereas the translocation was determined by the core material. Knowledge about the different roles of the particle coating and core materials in crossing biological barriers will facilitate toxicological risk assessment of nanoparticles and contribute to the optimization of pharmacokinetic properties of nano-scaled pharmaceuticals. KW - Silver KW - Nanoparticle KW - Polymer KW - Polyacrylic acid PY - 2017 DO - https://doi.org/10.1016/j.ejpb.2016.12.004 SN - 0939-6411 SN - 1873-3441 VL - 118 SP - 21 EP - 29 PB - Elsevier AN - OPUS4-41170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sieg, H. A1 - Kästner, Claudia A1 - Krause, B. A1 - Meyer, T. A1 - Burel, A. A1 - Böhmert, L. A1 - Lichtenstein, D. A1 - Jungnickel, H. A1 - Tentschert, J. A1 - Laux, P. A1 - Braeuning, A. A1 - Estreal-Lopis, I. A1 - Gauffre, F. A1 - Fessard, V. A1 - Meijer, J. A1 - Luch, A. A1 - Thünemann, Andreas A1 - Lampen, A. T1 - Impact of an artificial digestion procedure on aluminum-containing nanomaterials N2 - Aluminum has gathered toxicological Attention based on relevant human exposure and its suspected hazardous potential. Nanoparticles from food supplements or Food contact materials may reach the human gastrointestinal tract. Here, we monitored the physicochemical fate of aluminum containing nanoparticles and aluminum ions when passaging an in vitro model of the human gastrointestinal tract. Smallangle X-ray scattering (SAXS), transmission electron microscopy (TEM), ion beam microscopy (IBM), secondary ion beam mass spectrometry (TOF-SIMS), and inductively coupled plasma mass spectrometry (ICP-MS) in the singleparticle mode were employed to characterize two aluminumcontaining nanomaterials with different particle core materials (Al0, γAl2O3) and soluble AlCl3. Particle size and shape remained unchanged in saliva, whereas strong Agglomeration of both aluminum nanoparticle species was observed at low pH in gastric fluid together with an increased ion release. The levels of free aluminum ions decreased in intestinal fluid and the particles deagglomerated, thus liberating primary particles again. Dissolution of nanoparticles was limited and substantial changes of their shape and size were not detected. The amounts of particle-associated phosphorus, chlorine, potassium, and calcium increased in intestinal fluid, as compared to nanoparticles in standard dispersion. Interestingly, nanoparticles were found in the intestinal fluid after addition of ionic aluminum. We provide a comprehensive characterization of the fate of aluminum nanoparticles in simulated gastrointestinal fluids, demonstrating that orally ingested nanoparticles probably reach the intestinal epithelium. The balance between dissolution and de novo complex formation should be considered when evaluating nanotoxicological experiments. KW - Small-angle X-ray scattering KW - SAXS KW - Nanoparticle PY - 2017 DO - https://doi.org/10.1021/acs.langmuir.7b02729 SN - 1520-5827 SN - 0743-7463 VL - 33 IS - 40 SP - 10726 EP - 10735 PB - Americal Chemical Society AN - OPUS4-42438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lichtenstein, D. A1 - Meyer, T. A1 - Böhmert, L. A1 - Juling, S. A1 - Fahrenson, C. A1 - Selve, S. A1 - Thünemann, Andreas A1 - Meijer, J. A1 - Estrela-Lopis, I. A1 - Braeuning, A. A1 - Lampen, A. T1 - Dosimetric quantification of coating-related uptake of silver nanoparticles N2 - The elucidation of mechanisms underlying the cellular uptake of nanoparticles (NPs) is an important topic in nanotoxicological research. Most studies dealing with silver NP uptake provide only qualitative data about internalization efficiency and do not consider NP-specific dosimetry. Therefore, we performed a comprehensive comparison of the cellular uptake of differently coated silver NPs of comparable size in different human intestinal Caco-2 cell-derived models to cover also the influence of the intestinal mucus barrier and uptake-specialized M-cells. We used a combination of the Transwell system, transmission electron microscopy, atomic absorption spectroscopy, and ion beam microscopy techniques. The computational in vitro sedimentation, diffusion, and dosimetry (ISDD) model was used to determine the effective dose of the particles in vitro based on their individual physicochemical characteristics. Data indicate that silver NPs with a similar size and shape show coating-dependent differences in their uptake into Caco-2 cells. The internalization of silver NPs was enhanced in uptake-specialized M-cells while the mucus did not provide a substantial barrier for NP internalization. ISDD modeling revealed a fivefold underestimation of dose–response relationships of NPs in in vitro assays. In summary, the present study provides dosimetry-adjusted quantitative data about the influence of NP coating materials in cellular uptake into human intestinal cells. Underestimation of particle effects in vitro might be prevented by using dosimetry models and by considering cell models with greater proximity to the in vivo situation, such as the M-cell model. KW - Silver nanoparticles KW - Small-angle X-ray scattering KW - Saxs PY - 2017 DO - https://doi.org/10.1021/acs.langmuir.7b01851 SN - 0743-7463 VL - 33 IS - 45 SP - 13087 EP - 13097 PB - Americal Chemical Society AN - OPUS4-42875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Falkenreck, Thora A1 - Klein, M. A1 - Böllinghaus, Thomas T1 - Dynamic compressive behaviour of weld joints N2 - Materials used in military applications have to withstand multiple threats like ballistics and explosions. Thus, high-strength low alloyed (HSLA) steels are used. The main joining technique for metals is welding. Therefore, analysing the dynamic impact behaviour of high-strength welds is very important to fulfil these demands. Investigation of welds at high strain rates has rarely been conducted in the past. To determine the dynamic impact behaviour of hybrid laser-arc welds, the Split Hopkinson Pressure Bar (SHPB) technique was used. The base material was a quenched and tempered fine-grained armour steel with yield strength of 1100 MPa. First, a full hybrid laser-arc weld was investigated by extracting specimens consisting of weld metal and heat affected base material. The influence of two variables, the cooling time between 800 °C and 500 °C (t8/5) and strength of filler material, on the impact behaviour was studied. The cooling time t8/5 was varied by preheating to influence the microstructure in the HAZ and to analyse the effect on the hardness and dynamic compressive strength. Subsequent analysis to detail the original Investigation was carried out by dilatometer heat treatment of specimens to create homogenous subzones of the weld. These specimens have a homogenous microstructure of HAZ and were tested by SHPB to determine the stress-strain characteristics for the different microstructures of HAZ. The results of the weld specimen showed the effect of preheating and filler material strength on the dynamic compressive behaviour. The analysis of the different microstructures of the HAZ indicated that especially the tempered microstructure caused a reduction in dynamic compressive strength. KW - SHPB KW - Hybrid laser-arc weld KW - Dilatometry PY - 2017 DO - https://doi.org/10.1016/j.msea.2017.07.032 SN - 0921-5093 SN - 1873-4936 VL - 702 SP - 322 EP - 330 AN - OPUS4-41904 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Silverstein, R. A1 - Sobol, Oded A1 - Böllinghaus, Thomas A1 - Unger, Wolfgang A1 - Eliezer, D. T1 - Hydrogen behavior in SAF 2205 duplex stainless steel N2 - This paper describes austenitic-ferritic duplex stainless steels, SAF 2205, in the presence of hydrogen. The duplex stainless steels (DSS) properties include excellent resistance to stress corrosion cracking, high strength and good weldability. Those steels are preferably used in industries combining hydrogen and loads. Hydrogen location in addition to hydrogen binding energy with the steel's defects are of great importance for the analysis of hydrogen embrittlement model in that steel. It is known from previously published works that the susceptibility to hydrogen embrittlement will depend on the competition between reversible and irreversible traps; meaning a direct relation to the hydrogen's state and position in the steel. In this work, we examine the local hydrogen concentration, trapping and distribution by two modern and advanced techniques: thermal desorption spectrometry (TDS) and we support it by time of flight-secondary ion mass spectrometer (ToF-SIMS). In this paper, we support and give for the first time new insights and better understanding to the hydrogen embrittlement mechanism in SAF 2205. The trapping energies levels were calculated using TDS and Lee and Lee's model. This model revealed reversible in addition to irreversible trapping sites. Also the trapping controlling mechanism was found to be a combination of detrapping controlled mechanism and diffusion controlled mechanism. The use of ToF-SIMS for local imaging the distribution of hydrogen species supports the discussion of the different hydrogen traps in this type of steel. The hydrogen embrittlemet phenomenon in SAF 2205 will be discussed in details in that paper. KW - Hydrogen trapping KW - Duplex stainless steel KW - Thermal desorption spectrometry (TDS) KW - ToF-SIMS PY - 2017 DO - https://doi.org/10.1016/j.jallcom.2016.11.184 SN - 0925-8388 SN - 1873-4669 VL - 695 SP - 2689 EP - 2695 PB - Elsevier B.V. AN - OPUS4-38856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingelhoeffer, Hellmuth A1 - Aegerter, J. A1 - Scherm, T. A1 - Schenuit, E. A1 - Sotheran, S. A1 - Loveday, M. A1 - Bosch, P. A1 - Bloching, H. A1 - Olbricht, Jürgen A1 - McEnteggart, I. T1 - Discussion on "Analysis on the issues in ISO 6892-1 and TENSTAND WP4 report based on the data of confirm tests by 21 laboratories" N2 - The authors, Li et al., of the paper entitled “Analysis on the Issues in ISO 6892-1 and TENSTAND WP4 Report Based on Data to Confirm Tests by 21 Laboratories” (J. Test. Eval. DOI: 10.1520/JTE20150479 (online only)) have expressed views that the authors of this rebuttal believe to be based on fundamental misunderstandings and misinterpretations of the tensile testing standard ISO 6892-1:2009, ISO 6892-1:2016, and its former versions, thus leading to erroneous conclusions. This refutation is intended to clarify the understanding of ISO 6892-1 and to address the misunderstandings and the misinterpretations of the authors of the paper. The present standard ISO 6892-1:2016 has a long history dating back to the 1970s. At that time, the tensile testing procedure was standardized on the National and International scale in parallel. To understand the present standard, the knowledge of the history helps to understand the background of details of the testing procedure implemented today. The history of the tensile testing standard has been discussed extensively during the annual international standardization meeting of ISO committee TC 164 SC1 for the last few years, at which some of the authors of the Li et al. paper attended. The authors continue to disagree with facts that were agreed by the consortium of the European research project TENSTAND and by the present international experts involved in ISO TC 164 SC1. It appears that the principal objective of the authors regarding their present publication was to increase the testing speed during tensile testing. However, the international standardization community has previously declined similar proposals by some of the authors. Many arguments presented by Li et al. were thus refuted. The conclusions of their paper are misleading and the international standardization community for tensile testing refused to revise the present standard, ISO 6892-1 (2016), according the authors’ proposals. KW - Tensile testing procedure KW - ISO 6892-1 KW - TENSTAND WP4 Final Report PY - 2017 DO - https://doi.org/10.1520/JTE20160526 SN - 0090-3973 SN - 1945-7553 VL - 45 IS - 3 SP - 1105 EP - 1114 PB - ASTM International CY - West Conshohocken, PA, USA AN - OPUS4-40267 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sobol, Oded A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Eliezer, D. A1 - Böllinghaus, Thomas A1 - Unger, Wolfgang T1 - Novel approach to image hydrogen distribution and related phase transformation in duplex stainless steels at the sub-micron scale N2 - The effect of electrochemical charging of hydrogen on the structure of a lean duplex stainless steel LDX 2101® (EN 1.4162, UNS S32101) was examined by both Time-of-Flight secondary ion mass spectrometry and electron back-scatter diffraction. The goal is to correlate hydrogen concentration and induced structural changes. Chemical and structural characterizations were done for the same region at the sample's surface with sub-micron spatial resolution. Regions of interest were varying in size between 50 × 50 μm and 100 × 100 μm. The results show a phase transformation of austenite to mainly a defect-rich BCC and scarcely a HCP phase. The phase transformation occurred in deuterium rich regions in the austenite. KW - Time-of-flight secondary ion mass spectrometry KW - ToF-SIMS KW - Electron backscatter diffraction KW - EBSD KW - Hydrogen-assisted cracking KW - Data fusion KW - Lean duplex stainless steel PY - 2017 DO - https://doi.org/10.1016/j.ijhydene.2017.08.016 SN - 0360-3199 VL - 42 IS - 39 SP - 25114 EP - 25120 AN - OPUS4-42022 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adel-Khattab, D. A1 - Giacomini, F. A1 - Gildenhaar, R. A1 - Berger, G. A1 - Gomes, Cynthia A1 - Linow, Ulf A1 - Hardt, M. A1 - Peleska, B. A1 - Günster, Jens A1 - Stiller, M. A1 - Houshmand, A. A1 - Ghaffar, K. A1 - Gamal, A. A1 - El-Mofty, M. A1 - Knabe, C. T1 - Development of a synthetic tissue engineered three- dimensional printed bioceramic-based bone graft with homogenously distributed osteoblasts and mineralizing bone matrix in vitro N2 - Over the last decade there have been increasing efforts to develop three-dimensional (3D) scaffolds for bone tissue Engineering from bioactive ceramics with 3D printing emerging as a promising technology. The overall objective of the present study was to generate a tissue engineered synthetic bone graft with homogenously distributed osteoblasts and mineralizing bone Matrix in vitro, thereby mimicking the advantageous properties of autogenous bone grafts and facilitating usage for reconstructing segmental discontinuity defects in vivo . To this end, 3D scaffolds were developed from a silica-containing calcium alkali orthophosphate, using, fi rst, a replica technique – the Schwartzwalder – Somers method – and, second, 3D printing, (i.e. rapid prototyping). The mechanical and physical scaffold properties and their potential to facilitate homogenous colonization by osteogenic cells and extracellular bone matrix formation throughout the porous scaffold architecture were examined. Osteoblastic cells were dynamically cultured for 7 days on both scaffold types with two different concentrations of 1.5 and 3 × 10⁹ cells/l. The amount of cells and bone matrix formed and osteogenic marker expression were evaluated using hard tissue histology, immunohistochemical and histomorphometric analysis. 3D-printed scaffolds (RPS) exhibited more micropores, greater compressive strength and silica release. RPS seeded with 3 × 10⁹ cells/l displayed greatest cell and extracellular Matrix formation, mineralization and osteocalcin expression. In conclusion, RPS displayed superior mechanical and biological properties and facilitated generating a tissue engineered synthetic bone graft in vitro, which mimics the advantageous properties of autogenous bone grafts, by containing homogenously distributed terminally differentiated osteoblasts and mineralizing bone matrix and therefore is suitable for subsequent in vivo implantation for regenerating segmental discontinuity bone defects. KW - Bone tissue engineering KW - Calcium alkali orthophosphate KW - Rapid prototyping KW - Scaffold KW - Mandible PY - 2017 DO - https://doi.org/10.1002/term.2362 SN - 1932-6254 SN - 1932-7005 VL - 12 IS - 1 SP - 44 EP - 58 PB - Wiley Online Library AN - OPUS4-40745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erdmann, Maren A1 - Trappe, Volker A1 - Sturm, Heinz A1 - Braun, Ulrike A1 - Dümichen, Erik T1 - Cure conversion of structural epoxies by cure state analysis and in situ cure kinetics using nondestructive NIR spectroscopy N2 - Non-isothermal heating rate kinetics was applied to two epoxy resin systems. In situ near-infrared (NIR) measurements were taken with a heatable NIR cell which allowed the cure to be monitored by characteristic absorption bands. An autocatalyzed reaction of the nth order was shown to describe the epoxy conversion curves. Differential Scanning Calorimetry (DSC) was used as a complementary method. The kinetic models developed by both NIR and DSC are in good accordance with experimental epoxy conversion in the in situ NIR setup for single and multiple cure temperature ramps. A linear calibration curve of the characteristic absorption bands of epoxy normalized to aromatic vibrations was introduced. The curing degree of structural epoxies that were cured according to an industrial temperature cure profile was determined by NIR using the calibration curve. The epoxy conversions of the structural components showed good agreement with the experimental in situ NIR. Several degrees of cure for structural specimens were evaluated by NIR and residual reaction enthalpy by DSC. We present the non-destructive NIR spectroscopy as an alternative to determine fast and non-destructive epoxy conversion, particularly suitable for high degrees of cure on structural components. KW - Epoxy resin KW - Curing kinetics KW - In situ near-infrared (NIR) spectroscopy KW - Differential scanning calorimetry (DSC) PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S0040603117300205 DO - https://doi.org/10.1016/j.tca.2017.01.010 SN - 0040-6031 SN - 1872-762X VL - 650 SP - 8 EP - 17 PB - Elsevier B.V. AN - OPUS4-39123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zocca, Andrea A1 - Lima, Pedro A1 - Günster, Jens T1 - LSD-based 3D printing of alumina ceramics N2 - An improved method of powder 3D printing leading to dense ceramic parts is presented. The application of powder-based binder jetting 3D printing technologies to technical ceramics is generally limited by the low packing density of the powder and by the need to use a flowable powder. With layer-wise slurry deposition, it is, however, possible to deposit powder beds with high particle packing and furthermore using submicron powders. This method was combined with the binder jetting technology to develop a novel process, named LSD-print. By means of LSD-print, a submicron Al2O3 powder could be processed to produce samples with a density comparable with that of standard pressed samples, both in the green state and after sintering. KW - Additive manufacturing KW - Layer-wise slurry deposition KW - Dense alumina KW - 3D printing PY - 2017 DO - https://doi.org/10.4416/JCST2016-00103 SN - 2190-9385 VL - 8 IS - 1, SI SP - 141 EP - 147 PB - Göller Verlag GmbH CY - Baden Baden AN - OPUS4-39672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weidner, Steffen A1 - Kricheldorf, H. R. T1 - The Role of Transesterification in SnOct 2 - Catalyzed Polymerizations of Lactides N2 - l-lactide or meso-lactide are polymerized either at 120 °C where the polymerization process of l-lactide is accompanied by crystallization, or at 180 °C where poly(l-lactide) remains in the molten state. Polymerizations at 120 °C initially yield even-numbered chains (with respect to lactic acid units) having relatively low dispersity, but the fraction of odd-numbered chains increases with time and the entire molecular weight distribution changes. Traces of cyclics are only formed after 7 d. Polymerizations at 180 °C yield equilibrium of even and odd-numbered chains from the beginning, but at low monomer/initiator ratios and short reaction times (<4 h) cyclics are again not formed. They appear at longer reaction times and entail higher dispersities. The results are discussed in terms of five different transesterification mechanisms. KW - Polylactides KW - MALDI KW - Transesterification KW - Sn catalysts PY - 2017 DO - https://doi.org/10.1002/macp.201600331 SN - 1022-1352 VL - 218 IS - 3 SP - 1600331 PB - Wiley AN - OPUS4-39753 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kirner, Sabrina A1 - Wirth, Thomas A1 - Sturm, Heinz A1 - Krüger, Jörg A1 - Bonse, Jörn T1 - Nanometer-resolved chemical analyses of femtosecond laser-induced periodic surface structures on titanium N2 - The chemical characteristics of two different types of laser-induced periodic surface structures (LIPSS), so-called high and low spatial frequency LIPSS (HSFL and LSFL), formed upon irradiation of titanium surfaces by multiple femtosecond laser pulses in air (30 fs, 790 nm, 1 kHz), are analyzed by various optical and electron beam based surface analytical techniques, including micro-Raman spectroscopy, energy dispersive X-ray analysis, X-ray photoelectron spectroscopy, and Auger electron spectroscopy. The latter method was employed in a high-resolution mode being capable of spatially resolving even the smallest HSFL structures featuring spatial periods below 100 nm. In combination with an ion sputtering technique, depths-resolved chemical information of superficial oxidation processes was obtained, revealing characteristic differences between the two different types of LIPSS. Our results indicate that a few tens of nanometer shallow HSFL are formed on top of a ∼150 nm thick graded superficial oxide layer without sharp interfaces, consisting of amorphous TiO2 and partially crystallized Ti2O3. The larger LSFL structures with periods close to the irradiation wavelength originate from the laser-interaction with metallic titanium. They are covered by a ∼200 nm thick amorphous oxide layer, which consists mainly of TiO2 (at the surface) and other titanium oxide species of lower oxidation states underneath. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser KW - Oxidation KW - Titanium KW - Auger electron spectroscopy PY - 2017 DO - https://doi.org/10.1063/1.4993128 SN - 0021-8979 VL - 122 IS - 10 SP - 104901, 1 EP - 9 PB - AIP Publishing CY - Melville, NY, USA AN - OPUS4-41905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten A1 - Meng, Birgit T1 - Interactions of polysaccharide stabilising agents with early cement hydration without and in the presence of superplasticizers N2 - Polysaccharides are incorporated into cement based Systems in order to modify the rheological properties. Typically, cellulose ethers, sphingan gums, guar gum or starch ethers are applied. Depending upon their chemistry, molecular architecture, and adsorption tendency, polysaccharides interact differently with the entire cementitious system. Some stabilising agents like diutan gum mainly affect the cementitious paste; other stabilising agents like starch tend to interact with the sand fraction and even with the coarse aggregates. Cellulose and guar gum shows more diverse performances. Typically stabilising admixtures like polysaccharides are used, when sophisticated rheological properties are adjusted. Therefore, polysaccharides are often used in combination with superplasticisers, which are added to reduce the yield stress of concrete. This can cause interactions, particularly when the stabilising Agent shows a strong tendency to adsorb on particle surfaces. Adsorptive stabilising agents may reduce the amount of adsorbed superplasticisers, thus affecting both viscosity and yield stress, while non-adsorptive stabilising agents mainly affect the plastic viscosity independently of the superplasticiser. Due to the strong influence of superplasticisers on the yield stress, influences of the stabilising agent on the yield stress retreat into the background, so that their major effect is an increase of the plastic viscosity. The paper provides a comprehensive overview of how different polysaccharide superplasticisers affect cementitious flowable systems and points out the challenges of the combined use of polysaccharides and superplasticisers. Based on rheometric experiments and observations of the hydration process, time dependent effects on the workability as well as of the hydration of cement are presented and discussed. KW - Concrete KW - Polysaccharides KW - Rheology KW - Stabilising agents KW - Starch KW - Sphingan PY - 2017 DO - https://doi.org/10.1016/j.conbuildmat.2016.11.022 SN - 0950-0618 SN - 1879-0526 VL - 139 SP - 584 EP - 593 PB - Elsevier AN - OPUS4-40597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. A1 - Weidner, Steffen A1 - Scheliga, F. ED - Shaplov, A. T1 - Cyclization and dispersity of polyesters N2 - Two classes of polyesters were prepared by irreversible polycondensations. The dependence of the dispersities on the experimental parameters such as synthetic method, chemical structure, molecular weight and initial monomer concentration was determined. At first it was demonstrated that it is essential for a correct calculation of Mn and Mw to include all oligomers down to the dimers in the evaluation of SEC curves. Furthermore, it was demonstrated for poly(e-caprolactone)s and polylactides that reversible polycondensations and ring-opening polymerizations with equilibration yield identical products. Finally, the dependence of the dispersity on various experimental Parameters was determined for equilibrated poly(e-caprolactone)s and polylactides. KW - Irreversible polycondensation KW - Polycaprolactone KW - Polylactide KW - Dispersity KW - MALDI-TOF MS PY - 2017 DO - https://doi.org/10.1002/masy.201600169 SN - 1022-1360 SN - 1521-3900 VL - 375 IS - 1 SP - Article 1600169, 1 EP - 6 PB - Wiley-VCH AN - OPUS4-42407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Breitenbach, Romy A1 - Silbernagl, Dorothee A1 - Toepel, J. A1 - Sturm, Heinz A1 - Broughton, William J. A1 - Sassaki, G. L. A1 - Gorbushina, Anna T1 - Corrosive extracellular polysaccharides of the rock-inhabiting model fungus Knufia petricola N2 - Melanised cell walls and extracellular polymeric matrices protect rock-inhabiting microcolonial fungi from hostile environmental conditions. How extracellular polymeric substances (EPS) perform this protective role was investigated by following development of the model microcolonial black fungus Knufia petricola A95 grown as a sub-aerial biofilm. Extracellular substances were extracted with NaOH/formaldehyde and the structures of two excreted polymers studied by methylation as well as NMR analyses. The main polysaccharide (~ 80%) was pullulan, also known as α-1,4-; α-1,6-glucan, with different degrees of polymerisation. Αlpha-(1,4)-linked-Glcp and α-(1,6)-linked-Glcp were present in the molar ratios of 2:1. A branched galactofuromannan with an α-(1,2)-linked Manp main chain and a β-(1,6)-linked Galf side chain formed a minor fraction (~ 20%). To further understand the roles of EPS in the weathering of minerals and rocks, viscosity along with corrosive properties were studied using atomic force microscopy (AFM). The kinetic viscosity of extracellular K. petricola A95 polysaccharides (≈ 0.97 × 10-6 m2 s-1) ranged from the equivalent of 2% (w/v) to 5% glycerine, and could thus profoundly affect diffusion-dominated processes. The corrosive nature of rock-inhabiting fungal EPS was also demonstrated by its effects on the aluminium coating of the AFM cantilever and the silicon layer below. KW - Corrosion KW - EPS KW - Melanised microcolonial fungi (MCF) KW - Pullulan KW - Sub-aerial biofilms (SAB) KW - α-1,4- and α-1,6-glucans KW - AFM cantilever vibration KW - Nanoviscosity KW - Nanocorrosion of aluminium and silicon PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-435910 DO - https://doi.org/10.1007/s00792-017-0984-5 SN - 1433-4909 SN - 1431-0651 VL - 22 IS - 2 SP - 165 EP - 175 PB - Springer CY - Berlin AN - OPUS4-43591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröter, Maria-Astrid A1 - Meyer, Susann A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Sturm, Heinz A1 - Kunte, Hans-Jörg T1 - Ectoine protects DNA from damage by ionizing radiation N2 - Ectoine plays an important role in protecting biomolecules and entire cells against environmental stressors such as salinity, freezing, drying and high temperatures. Recent studies revealed that ectoine also provides effective protection for human skin cells from damage caused by UV-A radiation. These protective properties make ectoine a valuable compound and it is applied as an active ingredient in numerous pharmaceutical devices and cosmetics. Interestingly, the underlying mechanism resulting in protecting cells from radiation is not yet fully understood. Here we present a study on ectoine and its protective influence on DNA during electron irradiation. Applying gel electrophoresis and atomic force microscopy, we demonstrate for the first time that ectoine prevents DNA strand breaks caused by ionizing electron radiation. The results presented here point to future applications of ectoine for instance in cancer radiation therapy. KW - Plasmid DNA pUC19 KW - Electron irradiation 30 [kV] KW - Effective irradiation dose 0.2-16 [Gy] KW - Gel electrophoresis KW - AFM intermittent contact KW - Radioprotector ectoine KW - Compatible solute PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428287 DO - https://doi.org/10.1038/s41598-017-15512-4 SN - 2045-2322 VL - 7 IS - 1 SP - 15272, 1 EP - 15272, 7 PB - Nature AN - OPUS4-42828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zeegers, G. P. A1 - Steinhoff, R. F. A1 - Weidner, Steffen A1 - Zenobi, R. T1 - Evidence for laser-induced redox reactions in matrix-assisted laserdesorption/ionization between cationizing agents and target plate material: a study with polystyrene and trifluoroacetate salts N2 - Matrix-assisted laser desorption/ionization mass spectrometry (MALDI-MS) is often applied to assess the dispersity and the end groups of synthetic polymers through the addition of cationizing agents. Here weaddress how these cation adducts are formed using polystyrene (PS) as a model polymer. We analyzed PSby MALDI-MS with a 2-[(2E)-3-(4-tert-butylphenyl)-2-methylprop-2-enylidene]malononitrile (DCTB) as the matrix and a range of trifluoroacetate (TFA) salts as cationizing agents on a range of different targetplate materials (copper, 1.4301 stainless steel, aluminum, Inconel 625, Ti90/Al6/V4 and chromium-, gold-and silver-plated stainless steel). It was found that on a stainless steel substrate the metal cations Al+,Li+, Na+, Cu+and Ag+formed polystyrene adducts, whereas K+, Cs+, Ba2+, Cr3+, Pd2+, In3+, or their lower oxidation states, did not. For the copper and silver substrates, PS and DCTB adduct formation with cations liberated from these target plate materials was observed upon addition of a cationizing agent, which indicates the occurrence of redox reactions between the added TFA salts and the target plate material. Judging from their standard electrode potentials, these redox reactions would not normally occur, i.e.,they require an additional energy input, strongly suggesting that the observed redox reactions are laser-induced. Furthermore, copper granules were found to successfully sequester PS from a tetrahydrofuran(THF) solution, consistent with the view complex formation with the copper target plate can take place prior to the MALDI-MS measurement. KW - Polymer MALDI KW - Cationization KW - Polystyrene KW - Laser-induced redox reactions KW - Target plate material PY - 2017 DO - https://doi.org/10.1016/j.ijms.2016.10.007 SN - 1387-3806 SN - 1873-2798 VL - 416 SP - 80 EP - 89 PB - Elsevier B.V. AN - OPUS4-41146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen A1 - Scheliga, F. T1 - Cyclic poly(L-lactide)s via ring-expansion polymerizations catalysed by 2,2-dibutyl-2- stanna-1,3-dithiolane N2 - L-Lactides were polymerized in bulk at 120 or 160 °C with cyclic dibutyltin catalysts derived from 1,2-dimercaptoethane or 2-mercaptoethanol. Only linear chains having one benzyl ester and one OH-end group were obtained when benzyl alcohol was added. When L-lactides were polymerized with neat dibutyl-2-stanna-1,3-dithiolane, exclusively cyclic polylactides were formed even at 120 °C. The temperature, time and monomer/catalyst ratio (M/C) were varied. These results are best explained by a combination of ring-expansion polymerization and ring-extrusion of cyclic oligo- or polylactides with Elimination of the cyclic catalyst. Neither syntheses of linear polylactides nor of cyclic lactides involved racemization up to 20 h at 160 °C. KW - Ring-expansion polymerization KW - MALDI KW - Polylactides PY - 2017 DO - https://doi.org/10.1039/C6PY02166B SN - 1759-9954 SN - 1759-9962 VL - 8 IS - 9 SP - 1589 EP - 1596 PB - Royal Society of Chemistry AN - OPUS4-39748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wu, C. A1 - Schwibbert, Karin A1 - Achazi, K. A1 - Landsberger, Petra A1 - Gorbushina, Anna A1 - Haag, R. T1 - Active antibacterial and antifouling surface coating via a facile one-step enzymatic cross-linking N2 - Prevention of microbial contamination of surfaces is one of the biggest challenges for biomedical applications. Establishing a stable, easily produced, highly antibacterial surface coating offers an efficient solution but remains a technical difficulty. Here, we report on a new approach to create an in situ hydrogel film-coating on glass surfaces made by enzymatic cross-linking under physiological conditions. The cross-linking is catalyzed by horseradish peroxidase (HRP)/glucose oxidase (GOD)-coupled cascade reactions in the presence of glucose and results in 3D dendritic polyglycerol (dPG) scaffolds bound to the surface of glass. These scaffolds continuously release H2O2 as long as glucose is present in the system. The resultant polymeric coating is highly stable, bacterial-repellent, and functions under physiological conditions. Challenged with high loads of bacteria (OD540 = 1.0), this novel hydrogel and glucose-amended coating reduced the cell viability of Pseudomonas putida (Gram-negative) by 100% and Staphylococcus aureus (Gram-positive) by ≥40%, respectively. Moreover, glucose-stimulated production of H2O2 by the coating system was sufficient to kill both test bacteria (at low titers) with >99.99% Efficiency within 24 h. In the presence of glucose, this platform produces a coating with high effectiveness against bacterial adhesion and survival that can be envisioned for the applications in the glucose-associated medical/oral devices. KW - Antifouling KW - Surface coating KW - Biofilm KW - Bacterial adhesion PY - 2017 DO - https://doi.org/10.1021/acs.biomac.6b01527 SN - 1525-7797 SN - 1526-4602 VL - 18 IS - 1 SP - 210 EP - 216 AN - OPUS4-39003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Leng, Jing A1 - Kang, Nianjun A1 - Wang, De-Yi A1 - Falkenhagen, Jana A1 - Thünemann, Andreas A1 - Schönhals, Andreas T1 - Structure–Property Relationships of Nanocomposites Based on Polylactide and Layered Double Hydroxides – Comparison of MgAl and NiAl LDH as Nanofiller N2 - Nanocomposites based on poly(L-lactide) (PLA) and organically modified Ni/Al layered double hydroxides (NiAl/LDHs) are prepared by melt blending and investigated by a combination of size exclusion chromatography, differential scanning calorimetry (DSC), small-angle X-ray scattering (SAXS), wide-angle X-ray scattering, and broadband dielectric spectroscopy. A detailed comparison to the behavior of the corresponding MgAl/LDH–PLA nanocomposites is made. SAXS investigations show that the morphology of the NiAl/LDH–PLA nanocomposites is more intercalated compared to the MgAl/LDH based PLA nanocomposite, which is more exfoliated. The DSC investigation gives a different dependence of the degree of crystallization on the concentration of LDH for NiAl/LDH–PLA than for MgAl/LDH–PLA nanocomposite system. These differences are discussed taking the differences of the morphologies of both systems into account. Broadband dielectric spectroscopy reveals information about the molecular dynamics where essential differences are observed for all relaxation processes taking place in both systems which were related to the different morphologies. KW - Nanocomposites KW - Polylactide PY - 2017 DO - https://doi.org/10.1002/macp.201700232 SN - 1022-1352 SN - 1521-3935 VL - 218 IS - 20 SP - Article 1700232, 1 EP - 12 PB - Wiley-VCH Verlag AN - OPUS4-42597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Billing, Mark A1 - Gräfe, Christine A1 - Saal, Adrian A1 - Biehl, Philip A1 - Clement, Joachim A1 - Dutz, silvio A1 - Weidner, Steffen A1 - Schacher, Felix T1 - Zwitterionic Iron Oxide (γ-Fe2O3) Nanoparticles Based on P(2VP-grad-AA) Copolymers N2 - This study presents the synthesis and characterization of zwitterionic core–shell hybrid nanoparticles consisting of a core of iron oxide multicore nanoparticles (MCNPs, γ-Fe2O3) and a shell of sultonated poly(2-vinylpyridine-grad-acrylic acid) copolymers. The gradient copolymers are prepared by reversible addition fragmentation chain transfer polymerization of 2-vinylpyridine (2VP), followed by the addition of tert-butyl acrylate and subsequent hydrolysis. Grafting of P(2VP-grad-AA) onto MCNP results in P(2VP-grad-AA)@MCNP, followed by quaternization using 1,3-propanesultone-leading to P(2VPS-grad-AA)@MCNP with a zwitterionic shell. The resulting particles are characterized by transmission electron microscopy, dynamic light scattering, and thermogravimetric analysis measurements, showing particle diameters of ≈70–90 nm and an overall content of the copolymer shell of ≈10%. Turbidity measurements indicate increased stability toward secondary aggregation after coating if compared to the pristine MCNP and additional cytotoxicity tests do not reveal any significant influence on cell viability. KW - Blockcopolymer KW - Controlled radical polymerization KW - Hybrid nanoparticles KW - Iron oxide nanoparticles KW - Sulfobetaines PY - 2017 DO - https://doi.org/10.1002/marc.201600637 SN - 1022-1336 SN - 1521-3927 VL - 38 IS - 4 SP - 1600637-1 EP - 1600637-8 PB - Wiley-VCH AN - OPUS4-39339 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Thermomechanical fatigue of heat-resistant austenitic cast iron EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S) N2 - TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Cast iron KW - Cracks KW - Cyclic softening KW - Microscopy KW - Thermomechanical fatigue PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.01.009 SN - 0142-1123 SN - 1879-3452 VL - 99 IS - 2 (Special issue: Recent developments in thermo-mechanical fatigue) SP - 295 EP - 302 PB - Elsevier CY - Oxford AN - OPUS4-39680 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madkour, Sherif A1 - Szymoniak, Paulina A1 - Radnik, Jörg A1 - Schönhals, Andreas T1 - Unraveling the Dynamics of Nanoscopically Confined PVME in Thin Films of a Miscible PVME/PS Blend N2 - Broadband dielectric spectroscopy (BDS) was employed to investigate the glassy dynamics of thin films (7−200 nm) of a poly(vinyl methyl ether) (PVME)/polystyrene (PS) blend (50:50 wt %). For BDS measurements, nanostructured capacitors (NSCs) were employed, where films are allowed a free surface. This method was applied for film thicknesses up to 36 nm. For thicker films, samples were prepared between crossed electrode capacitors (CECs). The relaxation spectra of the films showed multiple processes. The first process was assigned to the α-relaxation of a bulklike layer. For films measured by NSCs, the rates of α-relaxation were higher compared to those of the bulk blend. This behavior was related to the PVME-rich free surface layer at the polymer/air interface. The second process was observed for all films measured by CECs (process X) and the 36 nm film measured by NSCs (process X2). This process was assigned to fluctuations of constraint PVME segments by PS. Its activation energy was found to be thickness-dependent because of the evidenced thickness dependency of the compositional heterogeneity. Finally, a third process with an activated temperature dependence was observed for all films measured by NSCs (process X1). It resembled the molecular fluctuations in an adsorbed layer found for thin films of pure PVME, and thus, it is assigned accordingly. This process undergoes an extra confinement because of frozen adsorbed PS segments at the polymer/substrate interface. To our knowledge, this is the first example where confinement-induced changes were observed by BDS for blend thin films KW - Thin Films KW - Broadband Dielectric Spectroscopy PY - 2017 DO - https://doi.org/10.1021/acsami.7b10572 SN - 1944-8244 VL - 9 IS - 42 SP - 37289 EP - 37299 PB - ACS Publications AN - OPUS4-42652 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Cabeza, Sandra A1 - Mishurova, Tatiana A1 - Thiede, Tobias A1 - Kromm, Arne A1 - Seyfert, Christoph A1 - Farahbod, Lena A1 - Haberland, Christoph A1 - Schneider, Judith Ann A1 - Portella, Pedro Dolabella A1 - Bruno, Giovanni T1 - Effect of hatch length on the development of microstructure, texture and residual stresses in selective laser melted superalloy Inconel 718 N2 - In the present study, samples fabricated by varying the deposition hatch length during selective laser melting of nickel based superalloy Inconel 718 were investigated. Microstructure and texture of these samples was characterized using scanning electron microscopy, combined with electron back-scattered diffraction, and residual stress assessment, using neutron diffraction method. Textured columnar grains oriented along the sample building direction were observed in the shorter hatch length processed sample. A ten-fold increase in the hatch length reduced the texture intensity by a factor of two attributed to the formation of finer grains in the longer hatch length sample. Larger gradients of transverse residual stress in the longer hatch length sample were also observed. Along the build direction, compressive stresses in the shorter hatch length and negligible stresses for the longer hatch length specimen were observed. Changes to the temperature gradient (G) in response to the hatch length variation, influenced the G to growth rate (R) ratio and the product G × R, in agreement with the microstructures and textures formed. For the residual stress development, geometry of the part also played an important role. In summary, tailored isotropy could be induced in Inconel 718 by a careful selection of parameters during selective laser melting. KW - Additive manufacturing KW - Nickel-based superalloy KW - Microstructure and texture KW - Residual stress KW - Electron back-scattered diffraction KW - Neutron diffraction PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S0264127517308018 DO - https://doi.org/10.1016/j.matdes.2017.08.049 SN - 0264-1275 VL - 134 SP - 139 EP - 150 PB - Elsevier CY - Oxford, UK AN - OPUS4-41606 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cooper, R. A1 - Bruno, Giovanni A1 - Shyam, A. A1 - Watkins, T. A1 - Pandey, A. A1 - Wheeler, M. T1 - Effect of microcracking on the uniaxial tensile response of beta-eucryptite ceramics: Experiments and constitutive model N2 - A constitutive model for the nonlinear or “pseudoplastic” mechanical behavior in a linear-elastic solid with thermally induced microcracks is developed and applied to experimental results. The model is termed strain dependent microcrack density approximation (SDMDA) and is an extension of the modified differential scheme that describes the slope of the stress-strain curves of microcracked solids. SDMDA allows a continuous variation in the microcrack density with tensile loading. Experimental uniaxial tensile response of β-eucryptite glass and ceramics with controlled levels of microcracking is reported. It is demonstrated that SDMDA can well describe the extent of non-linearity in the experimental uniaxial tensile response of β-eucryptite with varying levels of microcracking. The advantages of the SDMDA are discussed in regard to tensile loading. KW - Microcracking KW - β-eucryptite KW - Young's modulus KW - Modeling KW - Tensile behavior PY - 2017 DO - https://doi.org/10.1016/j.actamat.2017.06.033 SN - 1359-6454 SN - 1873-2453 VL - 135 SP - 361 EP - 371 PB - Elsevier Ltd. AN - OPUS4-40859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fedelich, Bernard A1 - Kühn, Hans-Joachim A1 - Rehmer, Birgit A1 - Skrotzki, Birgit T1 - Experimental and analytical investigation of the TMF-HCF lifetime behavior of two cast iron alloys N2 - The combined loading Thermomechanical Fatigue (TMF) with High Cycle Fatigue (HCF) has been experimentally investigated for two cast iron alloys. Both alloys contain globular graphite nodules but the first one has a ferritic structure while the second one has an austenitic crystal structure. In particular, the influences of the HCF frequency, of the HCF loading amplitude and of the location of the superposed HCF cycles have been investigated. It was observed that the HCF frequency has a limited impact on the fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the fatigue life. The experimental results can be understood in terms of a fracture mechanics based damage mechanism: Cracks quickly initiate due to the TMF loading and the growth of the cracks up to a few mm controls the fatigue life. If HCF-loading cycles are superposed, cyclic crack propagation dramatically accelerates after a threshold has been reached. This threshold is regarded as controlling the fatigue life reduction. The previous ideas have been expressed in a model that can be very simply applied to estimate the fatigue life reduction ratio due to the superposed HCF cycles. It only contains two adjustable parameters and can be combined with any TMF life assessment model. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Thermomechanical Fatigue (TMF) KW - High Cycle Fatigue (HCF) KW - Cast iron KW - Fatigue assessment PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2016.11.013 SN - 0142-1123 SN - 1879-3452 VL - 99 IS - 2 (Special issue: Recent developments in thermo-mechanical fatigue) SP - 266 EP - 278 PB - Elsevier CY - Oxford AN - OPUS4-39810 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Pourmand, P. A1 - Wolff, Dietmar A1 - Gedde, U.W. T1 - Influence of ageing on sealability of elastomeric O-rings N2 - At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes the assessment of the service lifetime of elastomeric seals that are part of the container lid system with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1.5 years. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays relatively constant or even decreases until shrinkage combined with the loss of resilience of the aged seal leads to leakage. This demonstrates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity towards the degradation of the seal material. CS data is extrapolated using time-temperature shifts and Arrhenius graphs. An exemplary CS of 50 % would be reached after approx. 1.2, 17 and 29 years at 60 °C for HNBR, EPDM and FKM respectively. T2 - PolymerTec 2016 CY - Merseburg, Germany DA - 15.06.2016 KW - Compression KW - Leakage KW - Degradation KW - Rubber KW - Lifetime PY - 2017 DO - https://doi.org/10.1002/masy.201600157 SN - 1022-1360 SN - 1521-3900 VL - 373 IS - 1 SP - UNSP 1600157, 1 EP - 10 PB - WILEY-V C H VERLAG GMBH CY - Weinheim AN - OPUS4-40958 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wollschläger, Nicole A1 - Palasse, L. A1 - Häusler, Ines A1 - Dirscherl, K. A1 - Oswald, F. A1 - Narbey, S. A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan T1 - Characterization of the inner structure of porous TiO2 nanoparticle films in dye sensitive solar cells (DSSC) by focused ion beam (FIB) tomography and transmission Kikuchi diffraction (TKD) in the scanning electron microscope (SEM) N2 - A combined methodical approach is tested for the first time with respect to the characterization of the inner structure of porous TiO2 layers infiltrated with ruthenium molecular sensitizer as typically used in modern dye sensitized solar cells (DSSC). Their performance is directly linked to the surface area ‘offered’ by the pore Network to the dye. The micrometer thick layer employed was manufactured by screen-printing of a starting TiO2 powder constituted of shape-controlled, bipyramidal anatase nanoparticles (NPs) on FTO/glass substrates. The analytical methods exploited in our study are Focused Ion Beam (FIB) slicing followed by 3D reconstruction as well as the new approach transmission Kikuchi diffraction (TKD) technology in the scanning electron microscope (SEM). While the first method results in the visualization of the 3D pore network within the TiO2 layer, the second one can be successfully applied to analyze the crystal orientation of grains (i.e. NPs in our case) in nanometer resolution. Moreover, size and shape distribution of the TiO2 NPs within the layer can be extracted. SEM in transmission mode and atomic force microscopy (AFM) have been used to verify the dimensional data obtained by the new combined methodical approach. Its analytical benefits but also the challenges and limitations are highlighted. KW - Transmission Kikuchi diffraction KW - Focused ion beam tomography KW - Titanium dioxide KW - Nanoparticles KW - Porosity KW - Particle size KW - DSSC PY - 2017 DO - https://doi.org/10.1016/j.matchar.2017.06.030 SN - 1044-5803 SN - 1873-4189 VL - 131 SP - 39 EP - 48 PB - Elsevier AN - OPUS4-40875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Chatzigiannakis, E. A1 - Beckmann, Jörg A1 - Wachtendorf, Volker A1 - von der Ehe, Kerstin A1 - Braun, Ulrike A1 - Jaunich, Matthias A1 - Schade, U. A1 - Wolff, Dietmar T1 - Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE N2 - Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE. KW - Irradiation KW - UHMWPE KW - Colour center KW - Yellowness index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423992 DO - https://doi.org/10.1155/2017/1362491 SN - 1687-9422 VL - 2017 IS - Article ID 1362491 SP - 1 EP - 10 PB - Hindawi AN - OPUS4-42399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Cabeza, Sandra A1 - Artzt, Katia A1 - Haubrich, J. A1 - Klaus, M. A1 - Genzel, Ch. A1 - Requena, G. A1 - Bruno, Giovanni T1 - An Assessment of Subsurface Residual Stress Analysis in SLM Ti-6Al-4V N2 - Ti-6Al-4V bridges were additively fabricated by selective laser melting (SLM) under different scanning speed conditions, to compare the effect of process energy density on the residual stress state. Subsurface lattice strain characterization was conducted by means of synchrotron diffraction in energy dispersive mode. High tensile strain gradients were found at the frontal surface for samples in an as-built condition. The geometry of the samples promotes increasing strains towards the pillar of the bridges. We observed that the higher the laser energy density during fabrication, the lower the lattice strains. A relief of lattice strains takes place after heat treatment. KW - Selective laser melting KW - Additive manufacturing KW - Heat treatment KW - Ti-6Al-4V KW - Synchrotron X-ray diffraction KW - Residual stress PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-395759 DO - https://doi.org/10.3390/ma10040348 SN - 1996-1944 VL - 10 IS - 4 SP - Article 348, 1 EP - 14 AN - OPUS4-39575 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obaton, A-F. A1 - Fain, J. A1 - Djemaï, M. A1 - Meinel, Dietmar A1 - Léonard, Fabien A1 - Mahé, E. A1 - Lécuelle, B. A1 - Fouchet, J-J. A1 - Bruno, Giovanni T1 - In vivo XCT bone characterization of lattice structured implants fabricated by additive manufacturing N2 - Several cylindrical specimens and dental implants, presenting diagonal lattice structures with different cell sizes (600, 900 and 1200 µm) were additively manufactured by selective laser melting process. Then they were implanted for two months in a sheep. After removal, they were studied by Archimedes’ method as well as X-ray computed tomography in order to assess the penetration of bone into the lattice. We observed that the additive manufactured parts were geometrically conform to the theoretical specifications. However, several particles were left adhering to the surface of the lattice, thereby partly or entirely obstructing the cells. Nevertheless, bone penetration was clearly visible. We conclude that the 900 µm lattice cell size is more favourable to bone penetration than the 1200 µm lattice cell size, as the bone penetration is 84 % for 900 µm against 54 % for 1200 µm cell structures. The lower bone penetration value for the 1200 µm lattice cell could possibly be attributed to the short residence time in the sheep. Our results lead to the conclusion that lattice implants additively manufactured by selective laser melting enable better bone integration. KW - Biomedical engineering KW - Dentistry KW - Medical imaging KW - X-ray computer tomography PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418648 DO - https://doi.org/10.1016/j.heliyon.2017.e00374 SN - 2405-8440 IS - 3 SP - Article e00374, 1 EP - 21 PB - Elsevier Limited CY - 125 London Wall London, EC2Y 5AS United Kingdom AN - OPUS4-41864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rehmer, Birgit A1 - Skrotzki, Birgit A1 - Glaubitz, Steffen T1 - Influence of casting skin on fatigue lifetime of ferritic ductile cast iron N2 - The fatigue behaviour of cast iron is usually investigated on machined specimens. Components of cast iron, however, have a casting skin; therefore the investigation of the influence of the casting skin on the lifetime is of interest. To study this influence isothermal fatigue tests were carried out on heat-resisting spheroidal graphite cast iron EN GJS SiMo 4.05 in 4–point-bending set-up at 400 °C. Specimens with and without casting skin were investigated comparatively. The number of cycles to failure was significantly lower for specimens with casting skin. Metallographic investigations underline the reduction of lifetime caused by casting skin. KW - Cast iron KW - Casting skin KW - Fatigue KW - Lifetime PY - 2017 SN - 0025-5300 VL - 59 IS - 1 SP - 5 EP - 10 PB - Carl Hanser Verlag CY - München AN - OPUS4-38929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stegemann, Robert A1 - Cabeza, Sandra A1 - Lyamkin, V. A1 - Bruno, Giovanni A1 - Pittner, Andreas A1 - Wimpory, Robert A1 - Boin, M. A1 - Kreutzbruck, Marc T1 - Residual stress characterization of steel TIG welds by neutron diffraction and by residual magnetic stray field mappings N2 - The residual stress distribution of tungsten inert gas welded S235JRC+C plates was determined by means of neutron diffraction(ND). Large longitudinal residual stresses with maxima around 600 MPa were found. With these results as reference, the evaluation of residual stress with high spatial resolution GMR (giant magneto resistance) sensors was discussed. The experiments performed indicate a correlation between changes in residual stresses (ND) and the normal component of local residual magnetic stray fields (GMR). Spatial variations in the magnetic field strength perpendicular to the welds are in the order of the magnetic field of the earth. KW - GMR KW - Magnetic stray field KW - Neutron diffraction KW - Residual stress KW - TIG-welding PY - 2017 DO - https://doi.org/10.1016/j.jmmm.2016.11.102 SN - 0304-8853 SN - 1873-4766 VL - 426 SP - 580 EP - 587 PB - Elsevier CY - Amsterdam AN - OPUS4-38678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cabeza, Sandra A1 - Garces, G. A1 - Adeva, Paloma A1 - Kabra, S. A1 - Gan, W. T1 - Effect of Extrusion Temperature on the Plastic Deformation of an Mg-Y-Zn Alloy Containing LPSO Phase Using In Situ Neutron Diffraction N2 - The evolution of the internal strains during in situ tension and compression tests has been measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using neutron diffraction. The alloy was extruded at two different temperatures to study the influence of the microstructure and texture of the magnesium and the LPSO phases on the deformation mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher in compression than in tension. Independently on the stress sign and the extrusion temperature, the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the reinforcement in a metal matrix composite is responsible for this tension–compression asymmetry. KW - Mg-Y-Zn Alloy KW - LPSO Phase KW - Neutron Diffraction PY - 2017 DO - https://doi.org/10.1007/s11661-017-4284-6 VL - 48A IS - 11 SP - 5332 EP - 5343 PB - Spinger AN - OPUS4-42935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klingelhöffer, Hellmuth A1 - Affeldt, E. E. A1 - Bache, M. A1 - Bartsch, M. A1 - Beck, T. A1 - Christ, H. J. A1 - Fedelich, Bernard A1 - Hähner, P. A1 - Holdsworth, S. R. A1 - Lang, K.-H. A1 - McGaw, M. A1 - Olbricht, Jürgen A1 - Remy, L. A1 - Skrotzki, Birgit A1 - Stekovich, S. T1 - Editorial - Special issue: Recent developments in thermo-mechanical fatigue N2 - Components in the Aerospace, Power and Automotive engineering sectors are frequently subjected to cyclic stresses induced by thermal fluctuations and mechanical loads. For the design of such components, reliable material property data are required which need to be acquired using well accepted and reproducible test procedures for thermo-mechanical fatigue (TMF) loading. There is limited availability of proven TMF data indicating there is need for further research and testing. The TMF behaviour of materials is often desired to be simulated in models which describe the cyclic stress-strain behaviour, the fatigue life and the cyclic crack growth behaviour. There is a continuous need for the development and amendment of such models. Models can be validated by using materials in industrial applications which are subjected to TMF loading. The 3rd Workshop on Thermo-Mechanical Fatigue was held on 27–29 April 2016 at BAM, Berlin, Germany. The workshop was attended by 90 attendees coming from 17 countries in the world. 38 presentations including five poster presentations were held. The following topics were covered by the workshop: – TMF of materials coated with Thermal Barrier Coatings. – Thermal Gradient Mechanical Fatigue. – TMF crack growth. – TMF + High Cycle Fatigue. – TMF Modelling and Lifetime Prediction. – TMF Properties of steels, cast iron, Al-, Mg- and Ni-alloys – Advanced TMF Testing Techniques. – Industrial Applications. A panel discussion was held regarding the present state of TMF testing standards (ISO and ASTM) and their potential for improvement. The discussion and contributions were summarized and forwarded to the standard committees. The 3rd TMF-Workshop ensured the continuation of international exchange of knowledge providing a forum to present and discuss all recent developments in the field of thermo-mechanical fatigue. The current special issue publishes eleven selected papers of the 3rd TMF-Workshop 2016. The papers were peer reviewed by a number of experts in the Thermo-Mechanical Fatigue sector. I hope you will enjoy reading papers of this special issue. T2 - 3rd International Workshop on Thermo-Mechanical Fatigue (TMF-Workshop 2016) CY - Berlin, Germany DA - 27.04.2016 KW - Fatigue damage KW - Thermo-mechanical fatigue KW - Fatigue life time KW - Life time prediction KW - TMF PY - 2017 DO - https://doi.org/10.1016/j.ijfatigue.2017.02.002 SN - 0142-1123 VL - 99 IS - 2 SP - 215 PB - Elsevier CY - Oxford AN - OPUS4-40895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cabeza, Sandra A1 - Mishurova, Tatiana A1 - Garces, G. A1 - Requena, G. A1 - Bruno, Giovanni A1 - Sevostianov, I. T1 - Stress-induced damage evolution in cast AlSi12CuMgNi alloy with one- and two ceramic reinforcements N2 - Two composites, consisting of an as-cast AlSi12CuMgNi alloy reinforced with 15%vol. Al2O3 short fibres and with 7%vol. Al2O3 short fibres + 15%vol. SiC particles were studied. Synchrotron computed tomography disclosed distribution, orientation, and volume fraction of the different phases. In-situ compression tests during neutron diffraction in direction parallel to the fibres plane revealed the load partition between phases. Internal damage (fragmentation) of the Si phase and Al2O3 fibres was directly observed in CT reconstructions. Significant debonding between Al-matrix and SiC particles was also found. Finally, based on the Maxwell scheme, a micro-mechanical model was utilized for the new composite with two ceramic reinforcements; it rationalizes the experimental data, and predicts the evolution of all internal stress components in each phase. KW - Computed tomography KW - Metal matrix composite KW - Load partition KW - Neutron diffraction PY - 2017 DO - https://doi.org/10.1007/s10853-017-1182-7 SN - 0022-2461 SN - 1573-4803 VL - 52 IS - 17 SP - 10198 EP - 10216 PB - Springer AN - OPUS4-40572 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shashev, Yury A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Evsevleev, Sergei A1 - Müller, Bernd R. A1 - Osenberg, Markus A1 - Manke, Ingo A1 - Hentschel, Manfred P. A1 - Bruno, Giovanni T1 - Optimizing the visibility of X-ray phase grating interferometry N2 - The performance of grating interferometers coming up now for Imaging interfaces within materials depends on the efficiency (visibility) of their main component, namely the phase grating. Therefore, experiments with monochromatic synchrotron radiation and corresponding simulations are carried out. The visibility of a Phase grating is optimized by different photon energies, varying detector to grating distances and continuous rotation of the phase grating about the grid lines. Such kind of rotation changes the projected grating shapes, and thereby the distribution profiles of phase shifts. This yields higher visibilities than derived from ideal rectangular shapes. By continuous grating rotation and variation of the propagation distance, we achieve 2D visibility maps. Such maps provide the visibility for a certain combination of grating orientation and detector position. Optimum visibilities occur at considerably smaller distances than in the standard setup. KW - Synchrotron, BAMline KW - Talbot-Lau interferometer KW - X-ray imaging KW - X-ray refraction KW - Grating interferometry KW - X-ray phase contrast PY - 2017 DO - https://doi.org/10.3139/120.111097 SN - 0025-5300 VL - 59 IS - 11-12 SP - 974 EP - 980 PB - Hanser Verlag AN - OPUS4-42955 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Bruno, Giovanni T1 - Microstructure Characterization of Ceramics via 2D and 3D X-Ray Refraction Techniques N2 - 3D imaging techniques are very fashionable nowadays, and allow enormous progress in understanding ceramic microstructure, its evolution, and its link to mechanical, thermal, and transport properties. In this feature article, we report the use of a powerful, yet not so wide-spread, set of X-ray techniques based on refraction effects. X-ray refraction allows determining internal specific surface (surface per unit volume) in a non-destructive fashion, position and orientation sensitive, and with a nanometric detectability. While the techniques are limited by the X-ray absorption of the material under investigation, we demonstrate showcases of ceramics and composite materials, where understanding of process parameter influence or simply of microstructural parameters could be achieved in a way unrivalled even by high-resolution techniques such as electron microscopy or computed tomography. KW - X-ray refraction KW - Porosity KW - Specific surface KW - Crack detection KW - Composites PY - 2017 DO - https://doi.org/10.1016/j.jeurceramsoc.2016.12.031 SN - 0955-2219 SN - 1873-619X VL - 37 IS - 5 SP - 1879 EP - 1889 PB - Elsevier CY - Amsterdam AN - OPUS4-39094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosu, Dana-Maria A1 - Ortel, Erik A1 - Hodoroaba, Vasile-Dan A1 - Kraehnert, R. A1 - Hertwig, Andreas ED - Hertwig, Andreas ED - Hinrichs, K. ED - Beck, Uwe ED - Esser, N. T1 - Ellipsometric porosimetry on pore-controlled TiO2 layers N2 - The practical performance of surface coatings in applications like catalysis, water splitting or batteries depends critically on the coating materials’ porosity. Determining the porosity in a fast and nondestructive way is still an unsolved problem for industrial thin-films technology. As a contribution to calibrated, non-destructive, optical layer characterisation, we present a multi-method comparison study on porous TiO2 films deposited by sol-gel synthesis on Si wafers. The ellipsometric data were collected on a range of samples with different TiO2 layer thickness and different porosity values. These samples were produced by templated sol-gel synthesis resulting in layers with a well-defined pore size and pore density. The ellipsometry measurement data were analysed by means of a Bruggeman effective medium approximation (BEMA), with the aim to determine the mixture ratio of void and matrix material by a multi-sample analysis strategy. This analysis yielded porosities and layer thicknesses for all samples as well as the dielectric function for the matrix material. Following the idea of multi-method techniques in metrology, the data was referenced to imaging by electron microscopy (SEM) and to a new EPMA (electron probe microanalysis) porosity approach for thin film analysis. This work might lead to a better metrological understanding of optical porosimetry and also to better-qualified characterisation methods for nano-porous layer systems. 1. IntroductionPorous materials, especially porous thin films play an importantrole in chemical and physical technology in every case where thecontact area between two media has to be maximised. From cataly-sis to photochemistry and photovoltaics, the applications of porouslayer materials are diverse and numerous [1–6].The accurate and non-destructive characterisation of porousfilms for layered systems poses a challenge. This applies especiallyfor the key parameter of porous films, their porosity, i.e. the mix-ing ratio between the Matrix of the film (host material) and thepore volume which is empty or filled with a fluid medium (inclu-sions). This parameter influences most of the physical and chemicalproperties of a porous thin film and is therefore essential for theunderstanding as well as the optimisation of this class of materials. T2 - International Conference on Spectroscopic Ellipsometry (ICSE-7) CY - Berlin, Germany DA - 06.06.2016 KW - Spectroscopic ellipsometry KW - Porous materials KW - Porosimetry KW - Multi-sample analysis KW - Thin film metrology PY - 2017 DO - https://doi.org/10.1016/j.apsusc.2016.11.055 SN - 0169-4332 SN - 1873-5584 VL - 421 IS - Part B SP - 487 EP - 493 PB - Elsevier B.V. AN - OPUS4-42517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Szczerba, Wojciech A1 - Schneider, M. A1 - Żukrowski, J. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Riesemeier, Heinrich A1 - Sikora, M. A1 - Mandel, K. T1 - Spectroscopic Study of the Role of Metal Ions in the Adsorption Process of Phosphate in Nanoscaled Adsorbers Based on Metal (Zn/ Fe/Zr) Oxyhydroxides N2 - Currently great effort is made to find materials and technologies for the recycling of phosphate from wastewater. Herein, we present an in-depth study of the Phosphate adsorption mechanism of a promising adsorber material, a Zn−Fe−Zr oxyhydroxide-based nanostructured precipitate. The behavior of the multicomponent nanomaterial, consisting of both crystalline and amorphous parts, is investigated via X-ray absorption fine structure spectroscopy and Mössbauer spectroscopy, revealing the importance of the nanostructured composition for the phosphate adsorption. We found evidence that adsorption takes place especially in the vicinity of iron sites in the amorphous part of the material. KW - Zn-Fe-Zr nanoparticles KW - Adsorption of phosphate KW - XAFS KW - Catalysis PY - 2017 DO - https://doi.org/10.1021/acs.jpcc.7b04773 SN - 1932-7447 VL - 121 IS - 45 SP - 25033 EP - 25042 PB - ACS Publications AN - OPUS4-43348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, Rui A1 - Russo, Patrícia A. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Jeon, Taeyeol A1 - Pinna, Nicola T1 - Hybrid organic–inorganic transition-metal phosphonates as precursors for water oxidation electrocatalysts N2 - Efficient water oxidation catalysts are required for the development of water splitting technologies. Herein, the synthesis of layered hybrid NiFephenylphosphonate compounds from metal acetylacetonate precursors and phenylphosphonic acid in benzyl alcohol, and their Oxygen evolution reaction performance in alkaline medium, are reported. The hybrid particles are formed by inorganic layers of NiO6 and FeO6 distorted octahedra separated by bilayers of the organic group, and template the Formation in situ of NiFe hydroxide nanosheets of sizes between 5 and 25 nm and thicknesses between 3 and 10 nm. X-ray absorption spectroscopy measurements suggest that the hybrid also acts as a template for the local structure of the metal sites in the active catalyst, which remain distorted after the transformation. Optimum electrocatalytic activity is achieved with the hybrid compound with a Fe content of 16%. The combination of the synergistic effect between Ni and Fe with the structural properties of the hybrid results in an efficient catalyst that generates a current density of 10 mA cm−2 at an overpotential of 240 mV, and also in a stable catalyst that operates continuously at low overpotentials for 160 h. KW - Water oxydation catalysis KW - EXAFS PY - 2017 DO - https://doi.org/10.1002/adfm.201703158 SN - 1616-301X SN - 1616-3028 VL - 27 IS - 40 SP - Article 1703158, 1 EP - 11 PB - WILEY-VCH Verlag CY - Weinheim AN - OPUS4-42783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pasternak, H. A1 - Launert, B. A1 - Kannengießer, Thomas A1 - Rhode, Michael T1 - Advanced residual stress assessment of plate girders through welding simulation N2 - This article provides an impression on potentials in applying nowadays welding simulation tools in construction design. This is carried out exemplary on plate girders from two structural steel grades. The calculated residual stresses are compared with measurements by sectioning method. It has been repeatedly stated that present Eurocode models fail to approximate the residual stresses. Especially for high strength steel (HSS) only limited information is available on realistic occurring residual stresses in typical I-girders. The investigations are aimed to give further guidance on these values. A few proposals on advanced models are discussed. T2 - MBST 2016 - Modern Building Materials, Structures and Techniques CY - Vilnius, Litunia DA - 26.05.2016 KW - Residual stresses KW - Plate girders KW - I-shape sections KW - High-strength steel KW - Welding simulation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392177 UR - http://www.sciencedirect.com/science/article/pii/S1877705817305192 DO - https://doi.org/10.1016/j.proeng.2017.02.013 SN - 1877-7058 IS - 172 SP - 23 EP - 30 PB - Elsevier CY - Amsterdam, Niederlande AN - OPUS4-39217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Omara, Shereen Shabaan A1 - Turky, G. A1 - Ghoneim, A. A1 - Thünemann, Andreas A1 - Abdel Rehim, M. H. A1 - Schönhals, Andreas T1 - Hyperbranched poly(amidoamine)/kaolinite nanocomposites: Structure and charge carrier dynamics N2 - An ex-situ approach was applied to prepare nanocomposites from hyperbranched poly(amidoamine) and modified kaolinite (Ka-DCA). The structure of the polymer and the corresponding nanocomposites was investigated by FTIR, DSC, SAXS and TEM. SAXS might suggest a partly exfoliated structure of the nanocomposites, which was supported by TEM. The molecular dynamics was studied by means of broadband dielectric spectroscopy (BDS). The dielectric spectra are dominated by a conductivity contribution at higher temperatures for all samples investigated. The obtained results further indicated that DC conductivity is increased by 4 orders of magnitude with increasing concentration of Ka-DCA nanofiller. Further, a significant separation between the conductivity relaxation time and that of segmental dynamics was observed. The decoupling phenomenon and the conductivity mechanism were discussed in detail. This study provides insights about the influence of the nanofiller on the structure and the conductivity contribution of nanocomposites of hyperbranched polymers including the decoupling phenomenon and fragility. KW - Hyperbranched polymers KW - Nanocomposites KW - Conductivity PY - 2017 DO - https://doi.org/10.1016/j.polymer.2017.06.017 SN - 0032-3861 VL - 121 SP - 64 EP - 74 PB - Elsevier Ltd. AN - OPUS4-40648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Juling, S. A1 - Niedzwiecka, A. A1 - Böhmert, L. A1 - Lichtenstein, D. A1 - Selve, S. A1 - Braeuning, A. A1 - Thünemann, Andreas A1 - Krause, E. A1 - Lampen, A. T1 - Protein Corona Analysis of Silver Nanoparticles Links to Their Cellular Effects N2 - The breadth of applications of nanoparticles and the access to food-associated consumer products containing nanosized materials lead to oral human exposure to such particles. In biological fluids nanoparticles dynamically interact with biomolecules and form a protein corona. Knowledge about the protein corona is of great interest for understanding the molecular effects of particles as well as their fate inside the human body. We used a mass spectrometry-based toxicoproteomics approach to elucidate mechanisms of toxicity of silver nanoparticles and to comprehensively characterize the protein corona formed around silver nanoparticles in Caco-2 human intestinal epithelial cells. Results were compared with respect to the cellular function of proteins either affected by exposure to nanoparticles or present in the protein corona. A transcriptomic data set was included in the analyses in order to obtain a combined multiomics view of nanoparticle-affected cellular processes. A relationship between corona proteins and the proteomic or transcriptomic responses was revealed, showing that differentially regulated proteins or transcripts were engaged in the same cellular signaling pathways. Protein corona analyses of nanoparticles in cells might therefore help in obtaining information about the molecular consequences of nanoparticle treatment. KW - Silver nanoparticles KW - Protein KW - Small-angle X-ray scattering KW - SAXS PY - 2017 DO - https://doi.org/10.1021/acs.jproteome.7b00412 SN - 1535-3893 SN - 1535-3907 VL - 16 IS - 11 SP - 4020 EP - 4034 PB - Americal Chemical Society AN - OPUS4-42688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bender, P A1 - Balceris, C. A1 - Ludwig, F A1 - Posth, O A1 - Bogart, L. K. A1 - Szczerba, Wojciech A1 - Castro, A A1 - Nilsson, L A1 - Costo, R A1 - Gavilan, H A1 - Gonzalez-Alonso, D A1 - de Pedro, I A1 - Barquin, L. F. A1 - Johansson, C T1 - Distribution functions of magnetic nanoparticles determined by a numerical inversion method N2 - In the present study, we applied a regularized inversion method to extract the particle size, magnetic moment and relaxation-time distribution of magnetic nanoparticles from small-angle x-ray scattering (SAXS), DC magnetization (DCM) and AC susceptibility (ACS) measurements. For the measurements the particles were colloidally dispersed in water. At first approximation the particles could be assumed to be spherically shaped and homogeneously magnetized single-domain particles. As model functions for the inversion, we used the particle form factor of a sphere (SAXS), the Langevin function (DCM) and the Debye model (ACS). The extracted distributions exhibited features/peaks that could be distinctly attributed to the individually dispersed and non-interacting nanoparticles. Further analysis of these peaks enabled, in combination with a prior characterization of the particle ensemble by electron microscopy and dynamic light scattering, a detailed structural and magnetic characterization of the particles. Additionally, all three extracted distributions featured peaks, which indicated deviations of the scattering (SAXS), magnetization (DCM) or relaxation (ACS) behavior from the one expected for individually dispersed, homogeneously magnetized nanoparticles. These deviations could be mainly attributed to partial agglomeration (SAXS, DCM, ACS), uncorrelated surface spins (DCM) and/or intra-well relaxation processes (ACS). The main advantage of the numerical inversion method is that no ad hoc assumptions regarding the line shape of the extracted distribution functions are required, which enabled the detection of these contributions. We highlighted this by comparing the results with the results obtained by standard model fits, where the functional form of the distributions was a priori assumed to be log-normal shaped. KW - SAXS KW - Small-angle X-ray scattering KW - Nanoparticle PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-429373 DO - https://doi.org/10.1088/1367-2630/aa73b4 SN - 1367-2630 VL - 19 SP - 073012, 1 EP - 073012, 19 PB - IOP Publ. Ltd. AN - OPUS4-42937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mirtschin, Nikolaus A1 - Pretsch, T. T1 - Programming of one- and two-step stress recovery in a poly(ester urethane) N2 - This work demonstrates that phase-segregated poly(ester urethane) (PEU) with switching segments of crystallizable poly(1,4-butylene adipate) (PBA) can be programmed to generate two separate stress recovery events upon heating under constant strain conditions. For programming, two elongations are applied at different temperatures, followed by unloading and cooling. During the adjacent heating, two-step stress recovery is triggered. The results indicate that the magnitude of the stress recovery signals corresponds to the recovery of the two deformation stresses in reverse order. As demonstrated by further experiments, twofold stress recovery can be detected as long as the elongation at higher temperature exceeds the strain level of the deformation at lower temperature. Another finding includes that varying the lower deformation temperature enables a control over the stress recovery temperature and thus the implementation of so-called “temperature-memory effects”. Moreover, exerting only one elongation during programming enables a heating-initiated one-step stress recovery close to the deformation temperature. Based on these findings, such polymers may offer new technological opportunities in the fields of active assembly when used as fastening elements and in functional clothing when utilized for compression stockings. KW - DSC KW - Mechanical properties PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393585 DO - https://doi.org/10.3390/polym9030098 SN - 2073-4360 VL - 9 IS - 3 SP - Article 98, 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-39358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauw, Brian Richard A1 - Smith, A. J. A1 - Snow, T. A1 - Terril, N. J. A1 - Thünemann, Andreas T1 - The modular small-angle X-ray scattering data correction sequence N2 - Data correction is probably the least favourite activity amongst users experimenting with small-angle X-ray scattering: if it is not done sufficiently well, this may become evident only during the data analysis stage, necessitating the repetition of the data corrections from scratch. A recommended comprehensive sequence of elementary data correction steps is presented here to alleviate the difficulties associated with data correction, both in the laboratory and at the synchrotron. When applied in the proposed order to the raw signals, the resulting absolute scattering cross section will provide a high degree of accuracy for a very wide range of samples, with its values accompanied by uncertainty estimates. The method can be applied without modification to any pinhole-collimated instruments with photon-counting direct-detection area detectors. KW - Small-angle X-ray scattering KW - SAXS KW - Accuracy KW - Methodology KW - Data correction PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-432114 DO - https://doi.org/10.1107/S1600576717015096 SN - 1600-5767 VL - 50 IS - 6 SP - 1800 EP - 1811 PB - International Union of Crystallography AN - OPUS4-43211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauw, Brian Richard A1 - Kästner, Claudia A1 - Thünemann, Andreas T1 - Nanoparticle size distribution quantification: results of a small-angle X-ray scattering inter-laboratory comparison N2 - This paper presents the first worldwide inter-laboratory comparison of small-angle X-ray scattering (SAXS) for nanoparticle sizing. The measurands in this comparison are the mean particle radius, the width of the size distribution and the particle concentration. The investigated sample consists of dispersed silver nanoparticles, surrounded by a stabilizing polymeric shell of poly(acrylic acid). The silver cores dominate the X-ray scattering pattern, leading to the determination of their radius size distribution using (i) the generalized indirect Fourier transformation method, (ii) classical model fitting using SASfit and (iii) a Monte Carlo fitting approach using McSAS. The application of these three methods to the collected data sets from the various laboratories produces consistent mean number- and volume-weighted core radii of Rn = 2.76 (6) nm and Rv = 3.20 (4) nm, respectively. The corresponding widths of the lognormal radius distribution of the particles were σn = 0.65 (1) nm and σv = 0.71 (1) nm. The particle concentration determined using this method was 3.0 (4) g l−1 or 4.2 (7) × 10−6 mol l−1. These results are affected slightly by the choice of data evaluation procedure, but not by the instruments: the participating laboratories at synchrotron SAXS beamlines, commercial and in-house-designed instruments were all able to provide highly consistent data. This demonstrates that SAXS is a suitable method for revealing particle size distributions in the sub-20 nm region (at minimum), out of reach for most other analytical methods. KW - SAXS KW - Small-angle X-ray scattering KW - Silver nanoparticles PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-422800 DO - https://doi.org/10.1107/S160057671701010X SN - 1600-5767 VL - 50 IS - 5 SP - 1280 EP - 1288 PB - (IUCr) International Union of Crystallography AN - OPUS4-42280 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Szczerba, Wojciech A1 - Costo, R. A1 - Veintemillas-Verdaguer, S. A1 - del Puerto Morales, M. A1 - Thünemann, Andreas T1 - SAXS analysis of single- and multi-core iron oxide magnetic nanoparticles N2 - This article reports on the characterization of four superparamagnetic iron oxide nanoparticles stabilized with dimercaptosuccinic acid, which are suitable candidates for reference materials for magnetic properties. Particles p1 and p2 are single-core particles, while p3 and p4 are multi-core particles. Small-angle X-ray scattering analysis reveals a lognormal type of size distribution for the iron oxide cores of the particles. Their mean radii are 6.9 nm (p1), 10.6 nm (p2), 5.5 nm (p3) and 4.1 nm (p4), with narrow relative distribution widths of 0.08, 0.13, 0.08 and 0.12. The cores are arranged as a clustered network in the form of dense mass fractals with a fractal dimension of 2.9 in the multi-core particles p3 and p4, but the cores are well separated from each other by a protecting organic shell. The radii of gyration of the mass fractals are 48 and 44 nm, and each network contains 117 and 186 primary particles, respectively. The radius distributions of the primary particle were confirmed with transmission electron microscopy. All particles contain purely maghemite, as shown by X-ray absorption fine structure spectroscopy KW - Superparamagnetic nanoparticles KW - Iron oxide KW - Reference materials KW - SAXS KW - Small-angle x-ray scattering KW - XANES KW - X-ray absorption near-edge structure KW - X-ray absorption fine structure PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-395948 DO - https://doi.org/10.1107/S1600576717002370 SN - 1600-5767 VL - 50 IS - Part 2 SP - 481 EP - 488 PB - (IUCr) International Union of Crystallography AN - OPUS4-39594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kästner, Claudia A1 - Lichtenstein, Dajana A1 - Lampen, Alfonso A1 - Thünemann, Andreas T1 - Monitoring the fate of small silver nanoparticles during artificial digestion N2 - The report on the results of an in vitro digestion study of silver nanoparticles in presence and absenceof food. The particles were poly(acrylic acid) stabilized ultra-small silver nanoparticles with a radius of 3.1 nm and a relative size distribution width of 0.2. As food components oil, starch, skimmed milk powderand a mixture thereof were chosen. Aggregation of the particles was quantified with small-angle X-rayscattering in terms of log-normal radii distributions. Complete aggregation of the primary particles wasdetermined in the absence of food. In contrast, the presence of oil and starch initiates a disaggregationin the intestine. Only small aggregates of 6 nm radii and aggregation numbers of 7 were found in thepresence of milk powder. It prevents primary particles from etching in the gastric and intestinal juice.Our results indicate that the silver nanoparticles can pass the digestion process in a nanoscale form butundergo a strong and food-dependent transformation in their state of aggregation. KW - Small-angle X-ray scattering KW - SAXS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-404099 DO - https://doi.org/10.1016/j.colsurfa.2016.08.013 SN - 0927-7757 SN - 1873-4359 VL - 526 SP - 76 EP - 81 PB - Elsevier B.V. AN - OPUS4-40409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wolf, Marcus A1 - Afanasiev, Roman A1 - Böllinghaus, Thomas A1 - Pfennig, A. T1 - Investigation of Corrosion Fatigue of Duplex Steel X2CrNiMoN22-5 3 Exposed to a Geothermal Environment under Different Electrochemical Conditions and Load Types N2 - Corrosion fatigue (CF) of duplex stainless steel (DSS) X2CrNiMoN22-5-3 was investigated in in-situ geothermal conditions of the Northern German Basin (NGB). The influence of the load type on CF behavior of the alloy was examined by applying push/pull and rotating bending cyclic load to failure. The hour-glass shaped specimens with both polished and precisely turned surface finish were tested in corrosion chambers allowing for the permanent circulation of Northern German Basin electrolyte heated to 369 K. Additionally, the influence of a protective cathodic potential on the CF life expectancy was investigated by employing a potentiostat. The rotating bending cyclic load led to a higher CF life expectancy, which decreased with increasing duration of the experiment due to a higher deterioration rate of the material. The application of a cathodic potential caused a significant increase of the CF lifespan from 4.7 x 105 (open-circuit potential (OCP)) to 107 cycles (preset threshold cycle number) for the potential range from USHE = – 450 to – 900 mV. Microstructural analysis of the CF damage revealed horizontal grain attack within corrosion pit cavities, multiple fatigue cracks and preferable deterioration of the austenitic phase. T2 - 13th International Conference on Greenhouse Gas Control Technologies, GHGT-13 CY - Lausanne, Switzerland DA - 14.11.2016 KW - Different load cases KW - Corrosion fatigue KW - DSS KW - Geothermal environment KW - Different electrochemical conditions PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-439231 DO - https://doi.org/10.1016/j.egypro.2017.03.1657 SN - 1876-6102 VL - 114 SP - 5337 EP - 5345 PB - Elsevier Science AN - OPUS4-43923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hernández-Nava, E. A1 - Tammas-Williams, S. A1 - Smith, C. A1 - Léonard, Fabien A1 - Withers, P. J. A1 - Todd, I. A1 - Goodall, R. T1 - X-ray tomography characterisation of lattice structures processed by selective electron beam melting N2 - Metallic lattice structures intentionally contain open porosity; however, they can also contain unwanted closed porosity within the structural members. The entrained porosity and defects within three different geometries of Ti-6Al-4V lattices, fabricated by Selective Electron Beam Melting (SEBM), is assessed from X-ray computed tomography (CT) scans. The results suggest that horizontal struts that are built upon loose powder show particularly high (~20 x 10⁻³ vol %) levels of pores, as do nodes at which many (in our case 24) struts meet. On the other hand, for struts more closely aligned (0° to 54°) to the build direction, the fraction of porosity appears to be much lower (~0.17 x 10⁻³%) arising mainly from pores contained within the original atomised powder particles. KW - Cellular solids KW - Aqdditive manufacturing KW - Computed tomography KW - Titanium alloys PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-413689 UR - http://www.mdpi.com/2075-4701/7/8/300 DO - https://doi.org/10.3390/met7080300 SN - 2075-4701 VL - 7 IS - 8 SP - Article 300, 1 EP - 12 PB - MDPI AN - OPUS4-41368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naresh-Kumar, G. A1 - Vilalta-Clemente, A. A1 - Jussila, H. A1 - Winkelmann, Aimo A1 - Nolze, Gert A1 - Vespucci, S. A1 - Nagarajan, S. A1 - Wilkinson, A. J. A1 - Trager-Cowan, C. T1 - Quantitative imaging of anti-phase domains by polarity sensitive orientation mapping using electron backscatter diffraction N2 - Advanced structural characterisation techniques which are rapid to use, non-destructive and structurally definitive on the nanoscale are in demand, especially for a detailed understanding of extended-defects and their influence on the properties of materials. We have applied the electron backscatter diffraction (EBSD) technique in a scanning electron microscope to non-destructively characterise and quantify antiphase domains (APDs) in GaP thin films grown on different (001)Si substrates with different offcuts. We were able to image and quantify APDs by relating the asymmetrical intensity distributions observed in the EBSD patterns acquired experimentally and comparing the same with the dynamical electron diffraction simulations. Additionally mean angular error maps were also plotted using automated cross-correlation based approaches to image APDs. Samples grown on substrates with a 4° offcut from the [110] do not show any APDs, whereas samples grown on the exactly oriented substrates contain APDs. The procedures described in our work can be adopted for characterising a wide range of other material systems possessing non-centrosymmetric point groups. KW - Polarity KW - Semiconductor KW - Antiphase boundary PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-420167 SN - 2045-2322 VL - 7 SP - Article 10916, 1 EP - 10 AN - OPUS4-42016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bender, P. A1 - Bogart, L.K. A1 - Posth, O. A1 - Szczerba, Wojciech A1 - Rogers, S.E. A1 - Castro, A. A1 - Nilsson, L. A1 - Zeng, L. J. A1 - Sugunan, A. A1 - Sommertune, J. A1 - Fornara, A. A1 - Gonzales-Alonso, D. A1 - Fernandez Barquin, L. A1 - Johansson, C. T1 - Structural and magnetic properties of multi-core nanoparticles analysed using a generalised numerical inversion method N2 - The structural and magnetic properties of magnetic multi-core particles were determined by numerical inversion of small angle scattering and isothermal magnetisation data. The investigated particles consist of iron oxide nanoparticle cores (9 nm) embedded in poly(styrene) spheres (160 nm). A thorough physical characterisation of the particles included transmission electron microscopy, X-ray diffraction and asymmetrical flow field-flow fractionation. Their structure was ultimately disclosed by an indirect Fourier transform of static light scattering, small angle X-ray scattering and small angle neutron scattering data of the colloidal dispersion. The extracted pair distance distribution functions clearly indicated that the cores were mostly accumulated in the outer surface layers of the poly(styrene) spheres. To investigate the magnetic properties, the isothermal magnetisation curves of the multi-core particles (immobilised and dispersed in water) were analysed. The study stands out by applying the same numerical approach to extract the apparent moment distributions of the particles as for the indirect Fourier transform. It could be shown that the main peak of the apparent moment distributions correlated to the expected intrinsic moment distribution of the cores. Additional peaks were observed which signaled deviations of the isothermal magnetisation behavior from the non-interacting case, indicating weak dipolar interactions. KW - Numerical inversion KW - Magnetic nanoparticles KW - Iron oxides KW - Magnetic properties KW - Structural properties PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-400952 DO - https://doi.org/10.1038/srep45990 SN - 2045-2322 VL - 7 SP - Article 45990, 1 EP - 14 AN - OPUS4-40095 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Olejko, Lydia A1 - Bald, Ilko T1 - FRET efficiency and antenna effect in multi-color DNA origami-based light harvesting systems N2 - Artificial light harvesting complexes find applications in artificial photosynthesis, photovoltaics and light harvesting chemical sensors. They are used to enhance the absorption of light of a reaction center which is often represented by a single acceptor. Here, we present different light harvesting systems on DNA origami structures and analyze systematically the light harvesting efficiency. By changing the number and arrangement of different fluorophores (FAM as donor, Cy3 as transmitter and Cy5 as acceptor molecules) the light harvesting efficiency is optimized to create a broadband absorption and to improve the antenna effect 1 (including two energy transfer steps) from 0.02 to 1.58, and the antenna effect 2 (including a single energy transfer step) from 0.04 to 8.7, i.e. the fluorescence emission of the acceptor is significantly higher when the light-harvesting antenna is excited at lower wavelength compared to direct excitation of the acceptor. The channeling of photo energy to the acceptor proceeds by Förster Resonance Energy Transfer (FRET) and we carefully analyze also the FRET efficiency of the different light harvesting systems. Accordingly, the antenna effect can be tuned by modifying the stoichiometry of donor, transmitter and acceptor dyes, whereas the FRET efficiency is mainly governed by the spectroscopic properties of dyes and their distances. KW - DNA origami KW - Light-harvesting KW - FRET KW - Antenna effect PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-405867 UR - http://pubs.rsc.org/en/content/articlelanding/2017/ra/c7ra02114c#!divAbstract DO - https://doi.org/10.1039/C7RA02114C VL - 7 IS - 39 SP - 23924 EP - 23934 PB - The Royal Soc. of Chemistry AN - OPUS4-40586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosemann, Paul A1 - Müller, C. A1 - Baumann, O. A1 - Modersohn, W. A1 - Halle, T. T1 - Influence of the post-weld surface treatment on the corrosion resistance of the duplex stainless steel 1.4062 N2 - The duplex stainless steel 1.4062 (X2CrNiN22-2) is used as alternative material to austenitic stainless steels in the construction industry. The corrosion resistance of welded seams is influenced by the base material, the weld filler material, the welding process and also by the final surface treatment. The scale layer next to the weld seam can be removed by grinding, pickling, electro-polished or blasting depending on the application and the requested corrosion resistance. Blasted surfaces are often used in industrial practice due to the easier and cheaper manufacturing process compared to pickled or electro-polished surfaces. Furthermore blasting with corundum-grain is more effective than blasting with glass-beads which also lower the process costs. In recent years, stainless steel surfaces showed an unusually high susceptibility to pitting corrosion after grinding with corundum. For this reason, it is now also questioned critically whether the corrosion resistance is influenced by the applied blasting agent. This question was specifically investigated by comparing grinded, pickled, corundum-grain- and glass-bead-blasted welding seams. Results of the SEM analyses of the blasting agents and the blasted surfaces will be presented and correlated with the different performed corrosion tests (potential measurement, KorroPad-test and pitting potential) on welding seams with different surface treatments. T2 - 19th Chemnitz Seminar on Materials Engineering – 19. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 16.03.2017 KW - Corrosion resistance KW - Welding KW - Duplex stainless steels KW - Pitting corrosion KW - Surface treatment PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-395374 DO - https://doi.org/10.1088/1757-899X/181/1/012019 SN - 1757-899X SN - 1757-8981 VL - 181 IS - Conference 1 SP - Article UNSP 012019, 1 EP - 9 PB - IOP Publishing CY - Bristol, UK AN - OPUS4-39537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Asadujjaman, Asad A1 - Kent, B. A1 - Bertin, Annabelle T1 - Phase transition and aggregation behaviour of an UCST-type copolymer poly(acrylamide-coacrylonitrile) in water: effect of acrylonitrile content, concentration in solution, copolymer chain length and presence of electrolyte N2 - An UCST-type copolymer of acrylamide (AAm) and acrylonitrile (AN) (poly(AAm-co-AN)) was prepared by reversible addition fragmentation chain transfer (RAFT) polymerization and its temperature-induced phase transition and aggregation behaviour studied by turbidimetry, static and dynamic light scattering, small angle neutron scattering (SANS) and cryo-transmission electron microscopy (cryo-TEM) measurements. The phase transition temperature was found to increase with increasing AN content in the copolymer, concentration of the solutions and copolymer chain length. A significant effect was observed onto the phase transition temperature by addition of different electrolytes into the copolymer solution. The copolymer chains were aggregated below the phase transition temperature and disaggregated above it. The size of the aggregates increases with increasing AN contents and concentration of the copolymer solutions below the phase transition temperature. The copolymer chains were expanded and weekly associated in solution above the phase transition temperature. A model is proposed to explain such association–aggregation behaviour of poly(AAm-co-AN) copolymers depending on AN contents and concentration of the copolymer solutions as a function of temperature. KW - Thermoresponsive polymers KW - UCST-type copolymer PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-394636 DO - https://doi.org/10.1039/c6sm02262f SN - 1744-683X SN - 1744-6848 VL - 13 IS - 3 SP - 658 EP - 669 PB - RSC AN - OPUS4-39463 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Heyn, A. T1 - Dynamic tafel factor adaption for the evaluation of instantaneous corrosion rates on zinc by using gel-type electrolytes N2 - The paper presents a new method for the determination and evaluation of tafel factors using gel-type electrolytes and electrochemical frequency modulation technique (EFM). This relatively new electrochemical method offers the possibility to determine both polarization resistances and tafel factors within one measurement and in short measuring intervals. Starting from a comprehensive parameter study it is shown that a direct relationship between the two values exists that can be described mathematically. This contribution presents the determined tafel factors for the system gel-type electrolyte/zinc and discusses their applicability and their limits. T2 - 19th Chemnitz Seminar on Materials Engineering – 19. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 16.03.2017 KW - Gel-type electrolytes KW - Gelartige Elektrolyte KW - Zinc KW - Zink KW - Stern Geary constant KW - Stern-Geary-Konstante PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-394324 UR - http://iopscience.iop.org/article/10.1088/1757-899X/181/1/012021/pdf DO - https://doi.org/10.1088/1757-899X/181/1/012021 SN - 1757-899X SN - 1757-8981 VL - 181 IS - Conference 1 SP - Article UNSP 012021, 1 EP - 11 PB - IOP Publishing CY - Bristol, UK AN - OPUS4-39432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Baer, Wolfram A1 - Wossidlo, Peter T1 - Validation of a low blow specimen technique for R-curve determination using a drop tower N2 - Fracture mechanics based component design requires appropriate fracture mechanics toughness data with respect to both, loading rate as well as test temperature. Taking high-rate loading into account such as with accidental scenarios, different standards such as ASTM E 1820 or BS 7448-3 provide some information on dynamic fracture mechanics testing. Nevertheless, the designations differ so that a validation of the own material specific test method used for dynamic R-curve determination is mandatory. In order to address this for ductile cast iron materials an experimental method for the reliable determination of dynamic J-integral crack resistance curves at -40 °C following the multiple specimen approach has been established and validated. The experimental concept offers some additional valuable features. Single values of dynamic crack initiation toughness can be determined using a single specimen technique based on crack sensors. Furthermore, an experimentally independent method is provided according to which CTOD δ5 R-curves can be established. The focus of the present paper is on the validation of the experimental low blow technique using a drop tower test system. A drop tower test system was developed and set up to perform low blow tests at temperatures down to -40 °C. The system allows for a variation of the impact mass and height and was optimized for testing of ductile cast iron at stress intensity rates from approximately 5∙10⁴ to 3∙10⁵ MPa√ms⁻¹. This range of loading rate is characteristic for instance with crash scenarios of heavy sectioned DCI casks for radioactive materials. In order to address characteristic challenges of impact tests (test duration of microseconds up to milliseconds, inertial effects, signal oscillations), an appropriate full bridge strain gage method for the measurement of force directly on the specimen as well as a non-contact measurement of load line displacement using an optical extensometer have been developed and validated. The low blow test requires either to prevent bouncing strikes of the hammer by using the stop block technique or to catch the hammer after its first strike. Both options are not part of the experimental concept and setup which have been realized here. The paper describes investigations which have been performed in order to make sure that bouncing strikes of the hammer do not cause additional crack extension in the specimen. This is necessary to ensure a unique relation between the work done and the achieved crack extension. The investigations covered the analysis of limit loads of the specimen with respect to the measured force. The measured stiffness of the specimen was assessed and signals of crack sensors were analyzed. Furthermore, an analysis of the mechanical behavior of the loading system and the specimen by optical observation was performed. Corresponding results are discussed in the paper. It had finally been proven that additional crack extension in the specimen due to bouncing strikes of the hammer is not to be expected under the given conditions of test setup, material and loading. It can be seen as a major experimental advantage that the striker does not have to be catched after the low blow test. T2 - XXIV Italian Group of Fracture Conference CY - Urbino, Italy DA - 01.03.2017 KW - Dynamic fracture mechanics KW - R-curve KW - Low blow KW - Ductile cast iron PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-437686 DO - https://doi.org/10.1016/j.prostr.2017.04.005 SN - 2452-3216 VL - 3 SP - 25 EP - 32 AN - OPUS4-43768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Batzdorf, Lisa A1 - Zientek, Nicolai A1 - Rump, Doreen A1 - Fischer, Franziska A1 - Maiwald, Michael A1 - Emmerling, Franziska T1 - Make and break - Facile synthesis of cocrystals and comprehensive dissolution studies N2 - Mechanochemistry is increasingly used as a ‘green alternative’ for synthesizing various materials including pharmaceutical cocrystals. Herein, we present the mechanochemical synthesis of three new cocrystals containing the API carbamazepine (cocrystals CBZ:Indometacin 1:1, CBZ:Benzamide 1:1, and CBZ:Nifedipine 1:1). The mechanochemical reaction was investigated in situ documenting a fast and complete reaction within one minute. Online NMR spectroscopy proved the direct influence of the dissolution behaviour of the coformers to the dissolution behaviour of the API carbamazepine. The dissolution behaviour of the organic cocrystals is compared to the behaviour of the pure drug indicating a general applicability of this approach for detailed cocrystal dissolution studies. KW - Cocrystals KW - Carbamazepine KW - Mechanochemistry KW - Powder diffraction KW - Online NMR spectroscopy PY - 2017 DO - https://doi.org/10.1016/j.molstruc.2016.11.063 SN - 0022-2860 SN - 1872-8014 VL - 1133 SP - 18 EP - 23 AN - OPUS4-38664 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epping, Ruben A1 - Panne, Ulrich A1 - Falkenhagen, Jana T1 - Critical conditions for liquid chromatography of statistical copolymers: Functionality type and composition distribution characterization by UP-LCCC/ESI-MS N2 - Statistical ethylene oxide (EO) and propylene oxide (PO) copolymers of different monomer compositions and different average molar masses additionally containing two kinds of end groups (FTD) were investigated by ultra high pressure liquid chromatography under critical conditions (UP-LCCC) combined with electrospray ionization time-of flight mass spectrometry (ESI-TOFMS). Theoretical predictions of the existence of a critical adsorption point (CPA) for statistical copolymers with a given chemical and sequence distribution1 could be studied and confirmed. A fundamentally new approach to determine these critical conditions in a copolymer, alongside the inevitable chemical composition distribution (CCD), with mass spectrometric detection, is described. The shift of the critical eluent composition with the monomer composition of the polymers was determined. Due to the broad molar mass distribution (MMD) and the presumed existence of different end group functionalities as well as monomer sequence distribution (MSD), Gradient separation only by CCD was not possible. Therefore, isocratic separation conditions at the CPA of definite CCD fractions were developed. Although the various present distributions partly superimposed the separation process, the goal of separation by end group functionality was still achieved on the basis of the additional dimension of ESI-TOF-MS. The existence of HO-H besides the desired allylO-H end group functionalities was confirmed and their amount estimated. Furthermore, indications for a MSD were found by UPLC/MS/MS measurements. This approach offers for the first time the possibility to obtain a fingerprint of a broad distributed statistical copolymer including MMD, FTD, CCD, and MSD. KW - Polymer KW - Liquid chromatography at critical conditions KW - ESI-TOF-MS PY - 2017 DO - https://doi.org/10.1021/acs.analchem.6b04064 SN - 0003-2700 SN - 1520-6882 VL - 89 IS - 3 SP - 1778 EP - 1786 AN - OPUS4-39240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidel, R. A1 - Kraffert, K. A1 - Kabelitz, Anke A1 - Pohl, M.N. A1 - Kraehnert, R. A1 - Emmerling, Franziska A1 - Winter, B. T1 - Detection of the electronic structure of iron-(III)-oxo oligomers forming in aqueous solutions N2 - The nature of the small iron-oxo oligomers in iron-(III) aqueous solutions has a determining effect on the chemical processes that govern the formation of nanoparticles in aqueous phase. Here we report on a liquid-Jet photoelectron-spectroscopy experiment for the investigation of the electronic structure of the occurring iron-oxo oligomers in FeCl3 aqueous solutions. The only iron species in the as-prepared 0.75 M solution are Fe3+ monomers. Addition of NaOH initiates Fe3+ hydrolysis which is followed by the formation of iron-oxo oligomers. At small enough NaOH concentrations, corresponding to approximately [OH]/[Fe] = 0.2–0.25 ratio, the iron oligomers can be stabilized for several hours without engaging in further aggregation. Here, we apply a combination of non-resonant as well as iron 2p and Oxygen 1s resonant photoelectron spectroscopy from a liquid microjet to detect the electronic structure of the occurring species. Specifically, the oxygen 1s partial electron yield X-ray absorption (PEY-XA) spectra are found to exhibit a peak well below the onset of liquid water and OH (aq) absorption. The iron 2p absorption gives rise to signal centered between the main absorption bands typical for aqueous Fe3+. Absorption bands in both PEY-XA spectra are found to correlate with an enhanced photoelectron Peak near 20 eV binding energy, which demonstrates the sensitivity of resonant photoelectron (RPE) spectroscopy to mixing between iron and ligand orbitals. These various signals from the iron-oxo oligomers exhibit Maximum intensity at [OH]/[Fe] = 0.25 ratio. For the same ratio, we observe changes in the pH as well as in complementary Raman spectra, which can be assigned to the Transition from monomeric to oligomeric species. At approximately [OH]/[Fe] = 0.3 we begin to observe particles larger than 1 nm in radius, detected by small-angle X-ray scattering. KW - Iron-oxo oligomers KW - XPS KW - Electronic structure PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-433468 DO - https://doi.org/10.1039/c7cp06945f SN - 1463-9076 SN - 1463-9084 VL - 19 IS - 48 SP - 32226 EP - 32234 AN - OPUS4-43346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Haferkamp, Sebastian A1 - Fischer, Franziska A1 - Kraus, Werner A1 - Emmerling, Franziska T1 - Mechanochemical Knoevenagel condensation investigated in situ N2 - The mechanochemical Knoevenagel condensation of malononitrile with p-nitrobenzaldehyde was studied in situ using a tandem approach. X-ray diffraction and Raman spectroscopy were combined to yield time-resolved information on the milling process. Under solvent-free conditions, the reaction leads to a quantitative conversion to p-nitrobenzylidenemalononitrile within 50 minutes. The in situ data indicate that the process is fast and proceeds under a direct conversion. After stopping the milling process, the reaction continues until complete conversion. The continuous and the stopped milling process both result in crystalline products suitable for single crystal X-ray diffraction. KW - Mechanochemistry KW - Ball milling KW - C–C coupling KW - In situ KW - Knoevenagel condensation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425388 DO - https://doi.org/10.3762/bjoc.13.197 VL - 13 SP - 2010 EP - 2014 PB - Beilstein-Institut AN - OPUS4-42538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Friedrich, Jörg A1 - Altmann, Korinna A1 - Wettmarshausen, Sascha A1 - Hidde, Gundula T1 - Coating of carbon fibers with adhesion-promoting thin polymer layers using plasma polymerization or electrospray ionization technique—A comparison N2 - Plasma polymers and electrospray-ionization (ESI) polymer layers are compared for most efficient adhesion promotion in carbon fiber-epoxy resin composites. The ultra-thin ESI layers (2–30 nm) of commercial poly(acrylic acid) and poly-(hydroxyethylmethacrylate) produce an significant increase of adhesion measured by single-fiber pull out tests. However, plasma Treatment has also advantages, such as simultaneous activation of the fiber substrate. Chemical structure and composition are rather far from the regular structure of commercial polymers as deposited by ESI processing. KW - Plasma polymers KW - Electrospray ionization polymers KW - Poly(acrylic acid) KW - Poly- (hydroxyethylmethacrylate) PY - 2017 DO - https://doi.org/10.1002/ppap.201600074 SN - 1612-8869 SN - 1612-8850 VL - 14 IS - 3 SP - e1600074-1 EP - 14 AN - OPUS4-40510 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Al-Terkawi, Abdal-Azim A1 - Scholz, G. A1 - Emmerling, Franziska A1 - Kemnitz, E. T1 - Strontium-coordination polymers based on tetrafluorophthalic and phthalic acids: mechanochemical synthesis, ab initio structures determination, and spectroscopic characterization N2 - Two strontium-based dicarboxylate systems [Sr(oBDC-F4)(H2O)2] (1) and [{Sr(oBDC)(H2O)2)·H2O] (2) were synthesized mechanochemically via milling of Sr(OH)2·8H2O with tetrafluorophthalic acid (H2oBDC-F4) or phthalic acid (H2oBDC), respectively. The new structures were determined ab initio from the powder X-ray diffraction (PXRD) data. Both compounds 1 and 2 crystallize in the monoclinic space group P21 /c as two-dimensional coordination polymers (2D-CPs). The determined structures were validated by extended X-ray absorption (EXAFS) data. Compounds 1 and 2 show different thermal stabilities. The fluorinated CP 1 is decomposed at 300 °C while the nonfluorinated CP 2 transforms into a new phase after thermal treatment at 400 °C. The two hydrated CPs exhibit small surface areas which increase after the thermal posttreatment for 1 but remains unchanged for the dehydrated sample of 2. Dynamic vapor sorption (DVS) experiments indicate that both the dehydrated and hydrated samples of 2 depict no significant differences in their adsorption isotherms. The DVS of water indicates that the phase transition after thermal posttreatment of 2 is irreversible. KW - Mechanochemistry KW - XRD KW - NMR PY - 2017 DO - https://doi.org/10.1039/c7dt02564e SN - 1477-9226 SN - 1477-9234 VL - 46 IS - 37 SP - 12574 EP - 12587 PB - The Royal Society of Chemistry CY - Cambridge AN - OPUS4-42261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Joseph, A. A1 - Bernardes, C. E. S. A1 - Druzhinina, A. I. A1 - Varushchenko, R. M. A1 - Nguyen, Thi Yen A1 - Emmerling, Franziska A1 - Yuan, L. A1 - Dupray, V. A1 - Coquerel, G. A1 - Minas da Piedade, M. E. T1 - Polymorphic phase transition in 4′-hydroxyacetophenone: Equilibrium temperature, kinetic barrier, and the relative stability of Z′=1 and Z′=2 forms N2 - Particularly relevant in the context of polymorphism is understanding how structural, thermodynamic, and kinetic factors dictate the stability domains of polymorphs, their tendency to interconvert through phase transitions, or their possibility to exist in metastable states. These three aspects were investigated here for two 4′-hydroxyacetophenone (HAP) polymorphs, differing in crystal system, space group, and number and conformation of molecules in the asymmetric unit. The results led to a ΔfGm°-T phase diagram highlighting the enantiotropic nature of the system and the fact that the Z′=1 polymorph is not necessarily more stable than its Z′=2 counterpart. It was also shown that the form II → form I transition is entropy driven and is likely to occur through a nucleation and growth mechanism, which does not involve intermediate phases, and is characterized by a high activation energy. Finally, although it has been noted that conflicts between hydrogen bond formation and close packing are usually behind exceptions from the hypothesis of Z′=1 forms being more stable than their higher Z′ analogues, in this case, the HAP polymorph with stronger hydrogen bonds (Z′=2) is also the one with higher density. KW - Polymorphism KW - Polymorphic transition KW - 4'-hydroxyacetophenone PY - 2017 DO - https://doi.org/10.1021/acs.cgd.6b01876 SN - 1528-7483 SN - 1528-7505 VL - 17 IS - 4 SP - 1918 EP - 1932 PB - ACS AN - OPUS4-40167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, K. A1 - Schmack, R. A1 - Klemm, H. W. A1 - Kabelitz, Anke A1 - Schmidt, T. A1 - Emmerling, Franziska A1 - Kraehnert, R. T1 - Mechanism and kinetics of hematite crystallization in air: Linking bulk and surface models via mesoporous films with defined nanostructure N2 - Iron can form numerous oxides, hydroxides, and oxide−hydroxides. Despite their relevance, many of the transformation processes between these phases are still poorly understood. In particular the crystallization of quasi-amorphous hydroxides and oxide−hydroxides is difficult to assess, since typical diffraction and scattering methods provide only sampleaveraged information about the crystallized phases. We report a new approach for the investigation of the crystallization of oxide−hydroxides. The approach relies on model-type films that comprise a defined homogeneous nanostructure. The nanostructure allows quantitative linking of Information obtained by bulk-averaging diffraction techniques (XRD, SAXS) with locally resolved information, i.e., Domain sizes (SEM, TEM, LEEM) and phase composition (SAED). Using time-resolved imaging and diffraction we deduce mechanism and kinetics for the crystallization of ferrihydrite into hematite. Hematite forms via nucleation of hematite domains and subsequent Domain growth that terminates only upon complete transformation. A Johnson−Mehl−Avrami−Kolmogorov model describes the kinetics over a wide temperature range. The derived understanding enables the first synthesis of ferrihydrite films with ordered mesoporosity and quantitative control over the films’ hematite and ferrihydrite content. KW - Iron oxide KW - Crystallization KW - Mesoporous films KW - Nanostructure PY - 2017 DO - https://doi.org/10.1021/acs.chemmater.6b05185 SN - 0897-4756 SN - 1520-5002 VL - 29 IS - 4 SP - 1724 EP - 1734 AN - OPUS4-39690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nguyen, Thi Yen A1 - Roessler, Ernst A1 - Rademann, Klaus A1 - Emmerling, Franziska T1 - Control of organic polymorph formation: crystallization pathways in acoustically levitated droplets N2 - Theoretical and experimental studies indicate that crystal nucleation can take more complex pathways than expected on the ground of the classical nucleation theory. Among these pathways are the formation of pre-nucleation clusters and amorphous precursor phases. A direct in situ observation of the different pathways of nucleation from solution is challenging since the paths can be influenced by heterogeneous nucleation sites, such as container walls. Here, we provide insights into the crystallization process using the in situ combination of an acoustic levitator, Raman spectroscopy, and X-ray scattering. The contactless sample holder enables the observation of homogeneous crystallization processes and the detection of intermediates and final crystalline forms. We provide evidence for the existence of multiple pathways of nucleation based on the investigation of the crystallization of organic molecules from different solvents. Starting from a diluted solution, a supersaturation is reached during the experiment due to the evaporation of the solvent. The highly supersaturated solution reveals different pathways of crystallization. Depending on the degree of supersaturation either the thermodynamically stable or the metastable crystal form is observed. KW - Crystallization KW - In situ XRD KW - Polymorphism KW - Polyamorphism KW - Raman spectroscopy PY - 2017 DO - https://doi.org/10.1515/zkri-2016-1964 SN - 2194-4946 SN - 2196-7105 VL - 232 IS - 1-3 SP - 15 EP - 24 PB - De Gruyter CY - Berlin AN - OPUS4-39708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kulla, Hannes A1 - Greiser, Sebastian A1 - Benemann, Sigrid A1 - Rademann, K. A1 - Emmerling, Franziska T1 - Knowing When To Stop-Trapping Metastable Polymorphs in Mechanochemical Reactions N2 - The cocrystal formation of pyrazinamide (PZA) with malonic acid (MA) was studied in situ. The mechanochemical reaction proceeds via conversion of a crystalline intermediate (PZA:MA II) into the thermodynamically more stable form (PZA:MA I) upon further grinding. The information derived from in situ powder X-ray diffraction (PXRD) enabled the isolation of this new metastable polymorph. On the basis of the PXRD data, the crystal structure of the 1:1 cocrystal PZA:MA II was solved. The polymorphs were further characterized and compared by Raman spectroscopy, solid-state NMR spectroscopy, differential thermal analysis/thermogravimetric analysis, and scanning electron microscopy. Our study demonstrates how monitoring mechanochemical reactions by in situ PXRD can direct the discovery and isolation of even short-lived intermediates not yet accessed by conventional methods. KW - Mechanochemistry KW - Polymorphs KW - Metastable KW - In situ PXRD KW - Cocrystal KW - Pyrazinamide PY - 2017 DO - https://doi.org/10.1021/acs.cgd.6b01572 SN - 1528-7483 SN - 1528-7505 VL - 17 IS - 3 SP - 1190 EP - 1196 AN - OPUS4-39420 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kulla, Hannes A1 - Wilke, Manuel A1 - Fischer, Franziska A1 - Röllig, Mathias A1 - Maierhofer, Christiane A1 - Emmerling, Franziska T1 - Warming up for mechanosynthesis – temperature development in ball mills during synthesis N2 - We present a first direct measurement of the temperature during milling combined with in situ Raman spectroscopy monitoring. The data reveal a low temperature increase due to the mechanical impact and clear temperature increases as a consequence of the reaction heat. Based on the data, temperature rises as postulated in the magma plasma and hot spot theory can be excluded for soft matter milling syntheses. KW - Thermography KW - Milling KW - Mechanochemistry KW - Soft matter PY - 2017 DO - https://doi.org/10.1039/c6cc08950j SN - 1364-548X SN - 1359-7345 SN - 0009-241X VL - 53 IS - 10 SP - 1664 EP - 1667 AN - OPUS4-39251 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dietzsch, Michael A1 - Andrusenko, Iryna A1 - Branscheid, Robert A1 - Emmerling, Franziska A1 - Kolb, Ute A1 - Tremel, Wolfgang T1 - Snapshots of calcium carbonate Formation - a step by step analysis N2 - Recent advances in our understanding of CaCO, nucleation from solution have provoked new and challenging questions. We have studied CaC03 formation using precipitation by carbonate ester hydrolysis which ensures precipitation from a strictly homogeneous solution state and allows “titrating” carbonate to a solution with a given Ca2+ concentration on a timescale suited for kinetic studies. Nucleation and crystallization were traced by combining dynamic light Scattering (DLS) and transmission electron microscopy (TEM). DLS served as in situ technique to identify the nucleation time, to monitor particle size evolution, to discriminate different precipitation mechanisms and to validate reproducibility. TEM snapshots taken during different stages of the precipitation process identified different phases and morphologies. At a high level of supersaturation homogeneous nucleation in solution led to the formation of amorphous CaC03 particles (diameter=30 nm), which transformed via vaterite to calcite. Nucleation occurred uniformly in solution which appears to be unique for the CaC03 System. In the presence of Na-polymethacrylate (Na-PMA), heterogeneous nucleation was suppressed and Ca-polymer aggregates were formed in the prenucleation stage. Beyond a critical threshold supersaturation CaC03 particles formed in solution outside of these aggregates. The nucleation process resembled that without additive, indicating that Na-PMA exerts only a minor effect on the CaC03 nucleation. In the postnucleation stage, the polymer led to the formation of extended liquid-like networks, which served as a precursor phase for solid ACC particles that formed alongside the network. KW - biomineralization KW - calcium carbonate KW - nucleation KW - polymer additives PY - 2017 DO - https://doi.org/10.1515/zkri-2016-1973 SN - 2194-4946 SN - 2196-7105 VL - 232 IS - 1-3 SP - 255 EP - 265 PB - De Gruyter CY - Berlin AN - OPUS4-39863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Al-Terkawi, Abdal-Azim A1 - Scholz, G. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Reinsch, Stefan A1 - Kemnitz, E. A1 - Emmerling, Franziska T1 - Ca- and Sr- tetrafluoroisophthalates: mechanochemical synthesis, characterization, and ab initio structure determination N2 - New fluorinated coordination polymers were prepared mechanochemically by milling the alkaline earth metal hydroxides MII(OH)2·xH2O (MII: Ca, Sr) with tetrafluoroisophthalic acid (H2mBDC-F4). The structures of [{Ca(mBDC-F4)(H2O)2}·H2O] and [{Sr(mBDC-F4)(H2O)2}·H2O] were determined based on ab initio calculations and their powder X-ray diffraction (PXRD) data. The compounds are isomorphous and crystallize in the orthorhombic space group P212121. The determined structures were validated by using extended X-ray absorption (EXAFS) data. The new materials were thoroughly characterized using elemental analysis, thermal analysis, magic angle spinning NMR, and attenuated total reflection-infrared spectroscopy. Further characterization methods such as BET, dynamic vapor sorption, and scanning electron microscopy imaging were also used. Our investigations indicate that mechanochemistry is an efficient method for preparing such materials. KW - Mechanochemistry KW - In situ KW - XRD KW - Coordination polymers PY - 2017 UR - http://pubs.rsc.org/-/content/articlehtml/2017/dt/c7dt00734e DO - https://doi.org/10.1039/c7dt00734e VL - 46 IS - 18 SP - 6003 EP - 6012 AN - OPUS4-41516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Matoga, D. A1 - Roztocki, K. A1 - Wilke, Manuel A1 - Emmerling, Franziska A1 - Oszajca, M. A1 - Fitta, M. A1 - Bałanda, M. T1 - Crystalline bilayers unzipped and rezipped: solid-state reaction cycle of a metal–organic framework with triple rearrangement of intralayer bonds N2 - We present a series of remarkable structural transformations for a family of layered metal–organic frameworks (MOFs) in a three-step solid-state reaction cycle. The cycle represents new dynamic behavior of 2D coordination polymers and involves the sequence of reactions: {[Mn2(ina)4(H2O)2]·2EtOH}n (JUK-1) → {(NH4)2[Mn(ina)2(NCS)2]}n·xH2O (JUK-2) → {[Mn2(ina)2(Hina)2(NCS)2]}n (JUK-3) → JUK-1 (Hina = isonicotinic acid), each accompanied by rearrangement of intralayer coordination bonds and each induced by a different external stimulus. In situ investigation of the first step of the cycle by combined synchrotron X-ray diffraction and Raman spectroscopy reveals direct mechanochemical unzipping of JUK-1 bilayers to respective JUK-2 layers with reaction rates dependent on the milling conditions. In contrast, the reverse zipping of JUK-2 layers involves two steps and proceeds through a new MOF (JUK-3) whose structure was elucidated by powder X-ray diffraction. Magnetic measurements confirm conversions of manganese nodes in the reaction cycle. The findings indicate the possibility of developing coordination-based assemblies with large structural responses for use in smart stimuli-responsive systems and sensor technologies. KW - Mechanochemistry KW - In situ KW - XRD KW - MOF PY - 2017 UR - http://pubs.rsc.org/is/content/articlehtml/2017/ce/c7ce00655a DO - https://doi.org/10.1039/C7CE00655A VL - 19 SP - 2987 EP - 2995 AN - OPUS4-41517 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, Manuel A1 - Kabelitz, Anke A1 - Zimathies, Annett A1 - Rademann, K. A1 - Emmerling, Franziska T1 - Crystal structure and in situ investigation of a mechanochemical synthesized 3D zinc N-(phosphonomethyl)glycinate N2 - The mechanochemical synthesis of the zinc N-(phosphonomethyl)glycinate Zn(O₃PCH₂NH₂CH₂CO₂) H₂O is presented. The structure was solved from powder X-ray diffraction (PXRD) data. In the three-dimensional pillared structure, the Zn atoms are coordinated tetrahedrally. In situ investigations of the reaction process with synchrotron PXRD and Raman spectroscopy reveal a two-step process including the formation of an intermediate. KW - Mechanochemistry KW - Metal phosphonate KW - In situ PY - 2017 DO - https://doi.org/10.1007/s10853-017-1121-7 SN - 0022-2461 SN - 1573-4803 VL - 52 IS - 20 SP - 12013 EP - 12020 PB - Springer CY - New York AN - OPUS4-41490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, Manuel A1 - Bach, S. A1 - Gorelik, T. A1 - Kolb, U. A1 - Tremel, W. A1 - Emmerling, Franziska T1 - Divalent metal phosphonates – new aspects for syntheses, in situ characterization and structure solution N2 - Divalent metal phosphonates are promising hybrid materials with a broad field of application. The rich coordination chemistry of the phosphonate linkers enables the formation of structures with different dimensionalities ranging from isolated complexes and layered structures to porous frameworks incorporating various functionalities through the choice of the building blocks. In brief, metal phosphonates offer an interesting opportunity for the design of multifunctional materials. Here, we provide a short review on the class of divalent metal phosphonates discussing their syntheses, structures, and applications. We present the advantages of the recently introduced mechanochemical pathway for the Synthesis of divalent phosphonates as a possibility to generate new, in certain cases metastable compounds. The benefits of in situ investigation of synthesis mechanisms as well as the implementation of sophisticated methods for the structure analysis of the resulting compounds are discussed. KW - Metal phosphonate KW - Mechanochemistry PY - 2017 DO - https://doi.org/10.1515/zkri-2016-1971 SN - 2194-4946 SN - 2196-7105 VL - 232 IS - 1-3 SP - 209 EP - 222 PB - De Gruyter AN - OPUS4-40003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Joester, Maike A1 - Seifert, Stephan A1 - Emmerling, Franziska A1 - Kneipp, Janina T1 - Physiological influence of silica on germinating pollen as shown by Raman spectroscopy N2 - The process of silicification in plants and the biochemical effects of silica in plant tissues are largely unknown. To study the molecular changes occurring in growing cells that are exposed to higher than normal concentration of silicic acid, Raman spectra of germinating pollen grains of three species (Pinus nigra, Picea omorika, and Camellia japonica) were analyzed in a multivariate classification approach that takes into account the variation of biochemical composition due to species, plant tissue structure, and germination condition. The results of principal component analyses of the Raman spectra indicate differences in the utilization of stored lipids, a changed mobilization of storage carbohydrates in the pollen grain bodies, and altered composition and/or structure of cellulose of the developing pollen tube cell walls. These biochemical changes vary in the different species. KW - Silica KW - Raman spectroscopy KW - Principal component analysis PY - 2017 DO - https://doi.org/10.1002/jbio.201600011 SN - 1864-063X SN - 1864-0648 VL - 10 IS - 4 SP - 542 EP - 552 AN - OPUS4-40090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, Hans R. A1 - Weidner, Steffen A1 - Scheliga, Felix T1 - Cyclic poly(l-lactide) via ring-expansion polymerization by means of dibutyltin 4-tert-butylcatecholate N2 - Five new catalysts are prepared from dibutyltin oxide and catechol (HCa), 2,3-dihydroxynaphthalene (NaCa), 4-tert-butyl catechol (BuCa), 4-cyano catechol (CyCa), and 4-benzoyl catechol (BzCa), but only BuCa gives useful results. When benzyl alcohol is used as an initiator, linear chains having benzyl ester end groups are formed in a slow polymerization process. In contrast to cyclic or noncyclic dibutyltin bisalkoxides, neat BuCa yields cyclic poly(l-lactide)s via a fast ring-expansion polymerization. Under certain conditions, a high-melting crystalline phase (Tm = 191 °C) is obtained. At 160 °C and short reaction times even-numbered cycles are slightly prevailing, but, surprisingly, at 120 °C, odd-numbered cycles are predominantly formed. These results definitely prove that a ring-expansion mechanism is operating. KW - Lactides KW - MALDI TOF MS KW - Morphology KW - Ring-opening polymerization KW - Tin catalysts PY - 2017 DO - https://doi.org/10.1002/macp.201700274 SN - 1521-3935 SN - 1022-1352 VL - 218 IS - 22 SP - 1700274, 1 EP - 1700274, 10 PB - Wiley VCH CY - Weinheim AN - OPUS4-43583 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wessig, P. A1 - Schulze, T. A1 - Pfennig, A. A1 - Weidner, Steffen A1 - Prentzel, S. A1 - Schlaad, H. T1 - Thiol–ene polymerization of oligospiroketal rods N2 - The nucleophilic thiol–ene (thia-Michael) reaction between molecular rods bearing terminal thiols and bis-maleimides was investigated. The molecular rods have oligospiroketal (OSK) and oligospirothioketal (OSTK) backbones. Contrary to the expectations, cyclic oligomers were always obtained instead of linear rigid-rod polymers. Replacing the OS(T)K rods with a flexible chain yielded polymeric products, suggesting that the OS(T)K structure is responsible for the formation of cyclic products. The reason for the preferred formation of cyclic products is due to the presence of folded conformations, which have already been described for articulated rods. KW - Oligospiroketals KW - Polymerization KW - MALDI-TOF MS PY - 2017 DO - https://doi.org/10.1039/C7PY01569K SN - 1759-9954 SN - 1759-9962 VL - 8 IS - 44 SP - 6879 EP - 6885 PB - Royal Society of Chemistry AN - OPUS4-42685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -