TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Rapid solidification during welding of duplex stainless steels – in situ measurement of the chemical Concentration by Laser-Induced Breakdown Spectroscopy (LIBS) N2 - Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process. T2 - 6th International Conference on Advances in Solidification Processes CY - Le Bischenberg, France DA - 20.06.2022 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding PY - 2022 AN - OPUS4-55116 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Rapid solidification during welding of duplex stainless steels – in situ measurement of the chemical concentration by Laser-Induced Breakdown Spectroscopy (LIBS) N2 - Nichtrostende Duplexstähle (DSS) werden häufig verwendet, insbesondere bei Anwendungen, die eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien erfordern. Beispiele hierfür sind Kraftwerkskomponenten und maritime Anwendungen. Beim Schweißen dieser Stähle kann es zu lokalen Schwankungen in der chemischen Zusammensetzung kommen. Dies führt zu einer Ferritisierung des Werkstoffs und beeinträchtigt die mechanischen Eigenschaften der Bauteile. In dieser Arbeit wurden Versuche zum Wolfram-Inertgas-Schweißen (WIG) mit DSS durchgeführt. Die Analyse der chemischen Zusammensetzung wurde in situ mit Hilfe der laserinduzierten Plasmaspektroskopie (LIBS) durchgeführt. Ziel der Arbeit ist es, die chemische Zusammensetzung in der Schweißnaht verschiedener DSS quantitativ zu messen und mögliche Einflüsse der Schweißparameter auf die Mikrostruktur des Werkstoffs zu ermitteln. Gemessen wurden die chemischen Konzentrationen der Hauptlegierungselemente Cr, Ni, Mn auf der Oberfläche der Probe während des Schweißprozesses und des Abkühlungsprozesses. Mn und Ni sind Austenitstabilisatoren, deren Gehalt beim Schweißen durch die Verwendung bestimmter hochlegierter Schweißzusatzwerkstoffe zunimmt. Die Spektren wurden alle 1,3 s in einem Abstand von etwa 2 mm aufgezeichnet. Während des Abkühlungsprozesses wurde der Ort der Messung nicht verändert. Die LIBS-Methode eignet sich nachweislich zur quantitativen Darstellung der chemischen Zusammensetzungen während des Schweißvorgangs. T2 - BMDK der Universität Magdeburg CY - Magdeburg, Germany DA - 19.05.2022 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Evaporation PY - 2022 AN - OPUS4-54865 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Chemical Concentrations in the weld pool measured in situ by Laser-Induced Breakdown Spectroscopy (LIBS) during GTAW N2 - Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). We could quantitatively measure the chemical composition in the weld seam of various DSS and identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. T2 - IIW joint intermediate meeting Comm.I,IV,XII_2022_ON-LINE CY - Online Meeting DA - 21.03.2022 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding PY - 2022 AN - OPUS4-54527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Erstellung von Tiefenprofilen auf Schweißnähten mittels Laserinduzierter plasmaspektroskopie (LIPS) N2 - Duplexstähle sind hochlegierte, nichtrostende Stähle. Sie bieten aufgrund des ausgewogenen Phasenverhältnisses von Austenit und Ferrit einige physikalische Vorteile gegenüber anderen nichtrostenden Stählen. Beim Schweißen können sich durch die Kondensation von Schweißrauch und verdampftem Material verschiedene chemische Elemente auf der Oberfläche der erstarrten Schweißnaht anreichern. Dann ist die Bildung einer schützenden Chromoxidschicht nicht mehr gewährleistet und es kann an diesen Stellen zu Lochfraß kommen. Frühere Arbeiten haben gezeigt, dass die Anreicherung von Mangan und Chrom an der Oberfläche der Wärmeeinflusszone des geschweißten Edelstahls 304L mit LIBS gemessen werden kann. Wir stellen die Ergebnisse der Optimierung der LIBS-Parameter für präzise Dickenmessungen solcher dünnen Schichten und für Tiefenprofilmessungen vor. Dazu haben wir galvanisch beschichtete Kupferproben mit bekannten Schichtdicken verwendet. Die Mangankonzentration im Schweißgut ist reduziert. Dies hat einen großen Einfluss auf die metallografische Struktur des Materials. T2 - BMDK der Universität Magdeburg CY - Online Meeting DA - 25.11.2021 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Evaporation PY - 2021 AN - OPUS4-53821 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - In situ investigation of chemical composition during TIG welding in duplex stainless steels using Laser-Induced Breakdown Spectroscopy (LIBS) JF - Forces in mechanics N2 - Many applications in industry require a material-to-material joining process of Duplex Stainless Steels (DSS). Therefore, it is essential to investigate the material’s properties during a welding process to control the weld quality. With the help of Laser-Induced Breakdown Spectroscopy (LIBS), the chemical composition during the Tungsten Inert Gas (TIG) welding process of DSS could be monitored in situ. The chemical composition could be quantitatively measured using pre-established calibration curves. Although the surface temperature and the welding plasma have a high influence on the spectral intensities, reliable composition measurements were possible. The concentration of alloying elements could be mapped during the TIG welding process. T2 - 2nd International Conference on Advanced Joining Processes CY - Sintra, Portugal DA - 21.10.2021 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - TIG welding KW - Duplex stainless steels PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542026 DO - https://doi.org/10.1016/j.finmec.2021.100063 SN - 2666-3597 VL - 6 SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-54202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Investigation of the chemical element distribution on the surface of duplex stainless steel welds using laser-induced breakdown spectroscopy (LIBS) N2 - Duplex steels are high-alloyed, stainless steels. They offer some physical advantages over other stainless steels due to the balanced phase ratio of austenite and ferrite. During welding processes, when welding fumes and vaporized material condensates, different chemical elements can accumulate on the surface of the solidified weld. Then, the formation of a protective chromium oxide layer is no longer guaranteed and pitting corrosion can occur at these places. Previous work has shown that the accumulation of manganese and chromium on the surface of the heat-affected zone of the welded high-grade steel 304L can be measured by LIBS. We present the results of the optimization of LIBS parameters for precise thickness measurements of such thin films and for depth profile measurements Therefore, we used galvanically coated copper samples with known film thicknesses. The Concentration of manganese is reduced in the weld metal. This has a high impact on the metallografic structure of the material. T2 - EMSLIBS 2021 CY - Online meeting DA - 29.11.2021 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Evaporation PY - 2021 AN - OPUS4-53869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - In situ investigation of phase distribution and weld solidification in duplex stainless steels using laser-induced breakdown spectroscopy (LIBS) N2 - Welding processes of duplex stainless steels cause an unbalanced austenite (γ)/ferrite (δ) ratio due to high cooling rates and changes in chemical composition. That causes a degradation of mechanical properties and corrosion resistance. In situ monitoring of the weld pool is to be realized with the help of laser-induced breakdown spectroscopy (LIBS). A major advantage of this technique is the highly accurate time and spatially resolved measurement of the chemical composition during welding. Previous research has established that the LIBS method is suitable to detect chemical elements during welding and to show a distribution of selected elements. Chemical composition in the WM and HAZ can now be quantified using calibration curves generated by certified reference materials (CRM). Furthermore, a cooling rate can be plotted against the measured electron temperature. T2 - 2nd International Conference on Advanced Joining Processes CY - Sintra, Portugal DA - 21.10.2021 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - duplex stainless steel KW - TIG welding PY - 2021 AN - OPUS4-53613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - First measurements of chemical composition changes during cooling of duplex stainless steel during TIG welding using laser-induced breakdown spectroscopy (LIBS) N2 - Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process. T2 - MSE 2022 CY - Darmstadt, Germany DA - 27.09.2022 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding PY - 2022 AN - OPUS4-55922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - Rapid solidification during welding of duplex stainless steels – in situ measurement of the chemical concentration by Laser-Induced Breakdown Spectroscopy (LIBS) JF - IOP Conference Series: Materials Science and Engineering N2 - Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process. T2 - ICASP-6 CY - Le Bischenberg, France DA - 20.06.2022 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Evaporation PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571308 DO - https://doi.org/10.1088/1757-899X/1274/1/012018 VL - 1274 SP - 1 EP - 8 PB - IOP Publishing CY - Bristol AN - OPUS4-57130 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taparli, Ugur Alp A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Jacobsen, Lars A1 - Michalik, Katarzyna A1 - Mory, David T1 - In situ laser-induced breakdown spectroscopy monitoring during TIG welding N2 - Chemical composition of the welding seam and HAZ has significant effect on weld quality. Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. T2 - Forschungsseminar OvGU Magdeburg CY - Magdeburg, Germany DA - 27.06.2018 KW - LIBS TIG welding KW - Austenitic stainless steels KW - Chemical composition KW - In situ measurement PY - 2018 AN - OPUS4-45350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taparli, Ugur Alp A1 - Kannengießer, Thomas A1 - Griesche, Axel T1 - Tungsten inert gas bead-on-plate weld chemical composition analysis by laser-induced breakdown spectroscopy JF - IOP conference series: Materials science and engineering N2 - Chemical compositions of a weld can be varying locally as a result of the welding process. These local variations can be due to the vaporization of individual alloying elements. In this work, tungsten inert gas (TIG) bead-on-plate stainless steel welds of EN grade 1.4404 and 1.4435 were investigated using laser-induced breakdown spectroscopy (LIBS) on the completed welds. This study aims to reveal the welding parameters’ influence on the resulting local chemical compositions of the stainless steel welds. We demonstrated Mn vaporize before Cr due to its lower latent enthalpy of vaporization. Hence, Mn accumulates on the heat-affected zone (HAZ) both sides across the weld bead by being swept away through the circulation flow of the welding plasma. Additionally, increasing the heat input tends to enhance the accumulated Mn content on the HAZ as well as increasing the shielding gas flow rate. The results are in good agreement with the literature and proved that LIBS is an effective method to inspect completed welds. T2 - Symposium on Materials and Joining Technology CY - Magdeburg, Germany DA - 07.09.2020 KW - LIBS TIG welding KW - Austenitic stainless steels KW - Chemical composition KW - In situ measurement PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511595 DO - https://doi.org/10.1088/1757-899X/882/1/012023 SN - 1757-8981 SN - 1757-899X VL - 882 IS - 012023 SP - 1 EP - 8 PB - IOP Publishing CY - Bristol AN - OPUS4-51159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taparli, Ugur Alp A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Michalik, K. A1 - Mory, D. T1 - Online TIG-Weld Monitoring by Laser-Induced Breakdown Spectroscopy N2 - Chemical compositions of the welds have significant effect on weld quality. Current inspection methods for the weld seams employ mostly post factum methods and cannot prevent weld defects.Elemental burn offs may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. T2 - Forschungsseminar OvGU Magdeburg CY - Magdeburg, Germany DA - 27.11.2019 KW - In situ measurement KW - LIBS TIG welding KW - Austenitic stainless steels KW - Chemical composition PY - 2019 AN - OPUS4-49831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taparli, Ugur Alp A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Jacobsen, L. A1 - Michalik, K. A1 - Mory, D. T1 - In situ TIG-Welding monitoring using Laser-Induced Breakdown Spectroscopy N2 - Chemical composition of the welding seam and HAZ has significant effect on weld quality. Current inspection methods for weld seams measure and investigate post factum and cannot prevent weld defects. Element burn-off may significantly affect solidification leading to embrittlement or cracking. Control of weld chemical compositions insures a controlled solidification and resistance to related weld defects. “Industry 4.0” is the current trend of automation and data exchange in manufacturing technologies. With this trend “intelligent” welding machines will be developed. LIBS can provide significantly important online data for such systems. T2 - Forschungsseminar OvGU Magdeburg CY - Magdeburg, Germany DA - 24.01.2019 KW - In situ measurement KW - LIBS TIG welding KW - Austenitic stainless steels KW - Chemical composition PY - 2019 AN - OPUS4-47266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, K. A1 - Gehling, T. A1 - Eissel, A. A1 - Wesling, V. T1 - In situ Messung der chemischen Konzentration in der Schmelze während des WIG-Schweißens von Duplexstählen T2 - Fortschrittsberichte der Materialforschung und Werkstofftechnik N2 - Duplexstähle besitzen ein zweiphasiges Gefüge und werden aufgrund ihrer verbesserten Schweißeignung gegenüber den Vollausteniten häufig im Anlagen- bzw. Apparatebau eingesetzt. Aufgrund der hohen Abkühlgeschwindigkeit und dem Abbrand von Legierungselementen kommt es zu einer Ferritisierung des Schweißguts und damit zu einer Degradation der mechanischen Eigenschaften. Zur Vorhersage des Phasenverhältnisses im Schweißgut wird das WRC1992-Diagramm genutzt. Dieses Diagramm zeigt einige Ungenauigkeiten und benötigt zur genaueren Vorhersage der Phasenverhältnisse eine Überarbeitung. Um den Einfluss einzelner Elemente auf das Schweißnahtmikrogefüge besser zu verstehen, wurden drahtförmige Schweißzusatzwerkstoffe mit dem Ferrit-Bildner Nb und dem Austenit-Bildner Cu beschichtet und für Schweißungen verwendet. Die Messmethode der Laser-induzierten Plasmaspektroskopie (LIBS) bietet hier eine gute Möglichkeit der in situ Überwachung der chemischen Konzentrationen, während des WIG-Schweißens von Duplexstählen. Die LIBS-Messergebnisse, konnten mit der Ferritnummer und der Schweißnahtmikrostruktur korreliert werden. T2 - Symposium Materialtechnik der TU Clausthal CY - Clausthal-Zellerfeld, Germany DA - 23.02.2023 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - Dduplex stainless steel KW - TIG welding PY - 2023 VL - 12 SP - 612 EP - 627 PB - Shaker CY - Aachen AN - OPUS4-57991 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - In situ Messung chemischer Konzentrationen im Schmelzbad von Duplexstählen während des WIG-Schweißens N2 - Die Kombination aus hoher Korrosionsbeständigkeit und guten mechanischen Eigenschaften von Duplexstählen (DSS) ist auf ihre chemische Zusammensetzung und das ausgewogene Phasenverhältnis von Ferrit (α) und Austenit (γ) zurückzuführen. Viele industrielle Anwendungen erfordern eine stoffschlüssige Verbindung von DSS. Das Wolfram-Inertgas-Schweißen (WIG) ist relativ einfach zu handhaben, benötigt nur wenig Platz und ermöglicht ein automatisiertes Schweißen, mit sehr hoher Reproduzierbarkeit und ist daher hervorragend zum Schweißen von DSS. Während der Erstarrung dieser Dualphasenstähle kann es zu kritischen Phasenverhältnissen von α und γ kommen, was zu Erstarrungsrissen, Korrosionsanfälligkeit, geringerer Duktilität und kritischen Festigkeitswerten führt. Um die gewünschten Werkstoffeigenschaften zu erhalten, muss daher die α/γ-Verteilung zuverlässig vorhergesagt werden. Dies geschieht in der Regel mit Hilfe des WRC1992-Diagramms. Die Vorhersagegenauigkeit des Ferritgehalts in diesem Diagramm ist jedoch meist nicht genau genug und muss daher optimiert werden. Daher ist es notwendig, selbst kleinste Veränderungen in der chemischen Zusammensetzung des Schweißguts idealerweise während des Schweißens zu überwachen. Dies wird in diesen Experimenten mit Hilfe der laser-induzierten Plasmaspektroskopie (LIBS) durchgeführt. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. In vorherigen Arbeiten wurde bereits die chemische Zusammensetzung im Schweißgut und der WEZ quantifiziert. In der präsentierten Untersuchung wird der Einfluss einzelner Elemente, wie Nb und Cu, auf das resultierende Schweißmikrogefüge untersucht. T2 - BMDK der Universität Magdeburg CY - Magdeburg, Germany DA - 08.11.2023 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Calibration free PY - 2023 AN - OPUS4-58777 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas T1 - In situ Messung der chemischen Konzentration in der Schmelze während des WIG-Schweißens von Duplexstählen zur Analyse der Phasenverteilung N2 - Die Kombination aus hoher Korrosionsbeständigkeit und guten mechanischen Eigenschaften von Duplexstählen (DSS) ist auf ihre chemische Zusammensetzung und das ausgewogene Phasenverhältnis von Ferrit (α) und Austenit (γ) zurückzuführen. Viele industrielle Anwendungen erfordern eine stoffschlüssige Verbindung von DSS. Das Wolfram-Inertgas-Schweißen (WIG) ist relativ einfach zu handhaben, benötigt nur wenig Platz und ermöglicht ein automatisiertes Schweißen, mit sehr hoher Reproduzierbarkeit und ist daher hervorragend zum Schweißen von DSS. Während der Erstarrung dieser Dualphasenstähle kann es zu kritischen Phasenverhältnissen von α und γ kommen, was zu Erstarrungsrissen, Korrosionsanfälligkeit, geringerer Duktilität und kritischen Festigkeitswerten führt. Um die gewünschten Werkstoffeigenschaften zu erhalten, muss daher die α/γ-Verteilung zuverlässig vorhergesagt werden. Dies geschieht in der Regel mit Hilfe des WRC1992-Diagramms. Die Vorhersagegenauigkeit des Ferritgehalts in diesem Diagramm ist jedoch meist nicht genau genug und muss daher optimiert werden. Daher ist es notwendig, selbst kleinste Veränderungen in der chemischen Zusammensetzung des Schweißguts idealerweise während des Schweißens zu überwachen. Dies wird in diesen Experimenten mit Hilfe der laser-induzierten Plasmaspektroskopie (LIBS) durchgeführt. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. In vorherigen Arbeiten wurde bereits die chemische Zusammensetzung im Schweißgut und der WEZ quantifiziert. In der präsentierten Untersuchung wird der Einfluss einzelner Elemente, wie Nb und Cu, auf das resultierende Schweißmikrogefüge untersucht. T2 - BMDK der Universität Magdeburg CY - Magdeburg, Germany DA - 25.01.2023 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - Duplex stainless steel KW - TIG welding PY - 2023 AN - OPUS4-56902 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, Kai A1 - Wesling, Volker T1 - Analyzing the impact of individual alloying elements on weld microstructure: In situ chemical composition measurement during TIG welding of Duplex Stainless Steels microstructure N2 - Various industrial applications require the joining of DSS components. Tungsten Inert Gas (TIG) welding is particularly well-suited for this purpose due to the ability to achieve highly reproducible automated welds. However, during solidification of the weld pool, critical phase ratios of ferrite (α) and austenite (γ) may occur, leading to solidification cracking, increased corrosion susceptibility, lower ductility and critical strength values. Hence, in order to achieve the desired material characteristics, it is crucial to accurately predict the α/γ phase ratio within the weld. Conventionally, the WRC-1992 diagram is employed for this purpose. In our study, we used Laser-Induced Breakdown Spectroscopy (LIBS) to track alterations in the chemical composition of the weld metal on the surface throughout the welding process. One significant benefit of this method is its capability to provide precise and real-time measurements of chemical compositions during welding, both temporally and spatially. In previous investigations, we could develop routines to quantify the measurement of chemical compositions within the weld metal and the Heat-Affected Zone (HAZ). The conducted research focuses on examining the alterations in chemical concentrations of specific alloying elements, namely Cu and Mn as γ-forming elements, and Nb and Cr as α-forming elements, during welding. These changes are measured in real-time using Laser-Induced Breakdown Spectroscopy (LIBS). To achieve this, both the ferrite number, determined through magnetic-inductive techniques, and the weld microstructure are analyzed. Through image-analytical methods, a correlation is established between the microstructure and the LIBS data obtained. T2 - AJP 2023 CY - Braga, Portugal DA - 19.10.2023 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding PY - 2023 AN - OPUS4-58657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, Kai A1 - Wesling, Volker T1 - Analyse der chemischen Konzentrationen während des WIG-Schweißens von Duplexstählen mittels Laser induzierter Plasmaspektroskopie (LIPS) N2 - Die Kombination aus hoher Korrosionsbeständigkeit und guten mechanischen Eigenschaften von Duplexstählen (DSS) ist auf ihre chemische Zusammensetzung und das ausgewogene Phasenverhältnis von Ferrit (α) und Austenit (γ) zurückzuführen. Viele industrielle Anwendungen erfordern eine stoffschlüssige Verbindung von DSS. Das Wolfram-Inertgas-Schweißen (WIG) ist relativ einfach zu handhaben, benötigt nur wenig Platz und ermöglicht ein automatisiertes Schweißen, mit sehr hoher Reproduzierbarkeit und ist daher hervorragend zum Schweißen von DSS. Während der Erstarrung dieser Dualphasenstähle kann es zu kritischen Phasenverhältnissen von α und γ kommen, was zu Erstarrungsrissen, Korrosionsanfälligkeit, geringerer Duktilität und kritischen Festigkeitswerten führt. Um die gewünschten Werkstoffeigenschaften zu erhalten, muss daher die α/γ-Verteilung zuverlässig vorhergesagt werden. Dies geschieht in der Regel mit Hilfe des WRC1992-Diagramms. Die Vorhersagegenauigkeit des Ferritgehalts in diesem Diagramm ist jedoch meist nicht genau genug und muss daher optimiert werden. Daher ist es notwendig, selbst kleinste Veränderungen in der chemischen Zusammensetzung des Schweißguts idealerweise während des Schweißens zu überwachen. Dies wird in diesen Experimenten mit Hilfe der laser-induzierten Plasmaspektroskopie (LIBS) durchgeführt. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. In vorherigen Arbeiten wurde bereits die chemische Zusammensetzung im Schweißgut und der WEZ quantifiziert. In der präsentierten Untersuchung wird der Einfluss einzelner Elemente, wie Nb und Cu, auf das resultierende Schweißmikrogefüge untersucht. T2 - BMDK der Universität Magdeburg CY - Magdeburg, Germany DA - 05.07.2023 KW - LIBS KW - In situ measurement KW - WRC 1992 diagram KW - TIG welding KW - Duplex stainless steels PY - 2023 AN - OPUS4-57873 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quackatz, Lukas A1 - Gornushkin, Igor A1 - Griesche, Axel A1 - Kannengießer, Thomas A1 - Treutler, Kai A1 - Wesling, Volker T1 - LIBS In situ Chemical Analysis in Duplex Stainless Steel Welding N2 - The high corrosion resistance and good mechanical properties of duplex stainless steel (DSS) are due to its special chemical composition, which is a balanced phase ratio of ferrite (α) and austenite (γ). Many industrial applications require the integration of DSS components. For this, tungsten inert gas welding (TIG) is an excellent choice, as it allows an automated operation with high reproducibility. However, when the weld pool solidifies, critical ratios of α- and γ- phases can occur, which leads to solidification cracking, increased susceptibility to corrosion, and a decrease in ductility and critical strength. Previous studies have shown that these defects can be caused by the accumulation of manganese and chromium in the heat affected zone (HAZ), and this accumulation can be detected using LIBS. Unlike conventional LIBS analyses, which requires reference samples to generate a calibration curve, calibration-free LIBS (CF-LIBS) can determine the chemical composition solely from the emission spectrum of the plasma. Numerous publications show that CF-LIBS is a fast and efficient analytical method for quantitative analysis of metal samples. We present the results of in situ CF-LIBS analysis during TIG DSS welding. Using a new approach, it is possible to quantitatively determine the chemical composition of the weld metal directly in the welding process. The results of the CF-LIBS analysis are compared with the results of the calibration-based PLS analysis and reasonable agreement is found. Thus, the CF-LIBS method offers the significant advantage of quickly measuring in situ the concentrations of the main alloying elements that prevent the formation of welding defects, without the tedious calibration procedure. T2 - EMSLIBS 2023 CY - Porto, Portugal DA - 04.09.2023 KW - LIBS KW - In situ measurement KW - Duplex stainless steel KW - TIG welding KW - Calibration free PY - 2023 AN - OPUS4-58314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -