TY - CONF A1 - Ghasem Zadeh Khorasani, Media A1 - Silbernagel, Dorothee A1 - Sturm, Heinz T1 - Long range influence of boehmite nanoparticles on the nanomechanics of epoxy matrix used in carbon-fiber composites N2 - Boehmite nanoparticles (AlOOH) were recently found to improve properties such as crack resistance, shrinkage and compressive strength in epoxy composites. Concentration and surface modification of boehmite nanoparticles are key factors for abovementioned enhancements. To understand the underlying mechanisms, more detailed research of micro- and nanoscopic mechanical properties is required. The presented study aims to investigate the influence of concentration and surface modification of boehmite on the stiffness of the bulk epoxy by means of AFM-based approaches: Force-Distance curves (FDC) on the sub- microscale and Intermodulation AFM and amplitude-dependent force spectroscopy (ADFS) on the nanoscale. For this purpose, stiffness-maps of epoxy filled with boehmite, with and without surface modification (HAc-boehmite) were obtained by FDC. These measurements showed a slight increase in overall stiffness of composite with increasing the nanoparticle content. The stiffening effect was observed to be intensified with HAc-boehmite. Since the lateral resolution of FDC is not high enough to distinguish nanoparticles, this effect was assumed to be due to the inevitable inclusion of nanoparticles in the measurement. By using Intermodulation-AFM, yielding ADFS stiffness maps with the resolution of <10 nm, we were able to calculate the average stiffness of bulk epoxy without the interference of nanoparticles. It was expected that the stiffness of regions faraway from particles would be equal to neat epoxy. In contrast, the results showed a drastic increase in stiffness of epoxy with increasing boehmite concentration (0, 1, 2.5, and 15%) especially in case of introducing 15wt% HAc-boehmite. Another important observation was formation of a spatial structure with non-homogenous stiffness distribution in bulk epoxy with HAc-boehmite. The underlying mechanisms of described observations are not fully understood yet. One hypothesis is the local increase in crosslinking density which we aim to investigate in our further studies by combining Dynamic Mechanical Thermal Analysis (DMTA) and Intermodulation-AFM. T2 - Frontiers in Polymer Science CY - Seville, Spain DA - 17.05.2017 KW - AFM KW - Boehmite KW - Epoxy nanocomposite PY - 2017 AN - OPUS4-50688 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghasem Zadeh Khorasani, Media A1 - Silbernagl, Dorothee A1 - Elert, Anna Maria A1 - Sturm, Heinz T1 - Studies on interphase formation of cured epoxy resin near boehmite surface N2 - The application of inorganic nanoparticles as reinforcement agent for polymer composites is constantly growing. Improving the performance of the material with desirable properties requires understanding of the interaction between polymer chains and nanoparticles and the properties of the interphase as well. Boehmite, a mineral of aluminum with basic unit of AlO(OH), is a novel and promising nanofiller which leads to enhanced performance of polymer composites. It has been recently reported that boehmite nanoparticles have reinforcing effect on epoxy matrix in carbon-fiber composites. It was primarily assumed that these improvements are due to very high Young’s modulus of boehmite particles. However, in our latest study we presented new values for the Young’s modulus of boehmite much lower than those reported earlier. This brings up the importance of interphase properties, e.g. the crosslink density, which can have the dominant role in the overall material property. Nevertheless, due to resolution limitations of conventional nanoprobing approaches, characterization of the interphase between individual particles and matrix is a challenge. In this study, the main goal is to investigate the interphase of the epoxy/boehmite nanocomposites using AFM-based methods. We simplify the three-dimensional nanocomposite system to a two-dimensional horizontally layered sample with a large and easy to access interphase area. For this purpose, 1µm coatings of hydrothermally synthesized boehmite are prepared as the substrate on which the epoxy is later molded and cured. AFM surface potential and force maps were obtained on the cross-sectional cut of epoxy/ boehmite sample. The results show unexpectedly a large interphase area (approx. 1 µm) with different electrical and mechanical properties comparing to bulk epoxy. The average force-distance curves from this region showed more elastic behavior compared to bulk. The underlying mechanism of this influence is not fully understood yet. Thus, further investigation on the interphase region using the novel Nano-IR approach provides more information about the chemical characteristics. Numerical simulation will give complementary information to understand the effect of nanoparticles on the crosslinking density of the interphase. This can be different to bulk epoxy due to either different local temperature gradients or due to a surface selectivity of boehmite towards the monomer molecules. T2 - ICCS20–20th International Conference on Composite Structures CY - Paris, France DA - 04.09.2017 KW - AFM KW - AFM-IR KW - ImAFM KW - Boehmite KW - Epox KW - Nanocomposite KW - Interphase KW - Nanomechanics PY - 2017 AN - OPUS4-50689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -