TY - JOUR A1 - Ulbricht, Alexander A1 - Ávila Calderón, Luis A1 - Sommer, Konstantin A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit A1 - Bruno, Giovanni T1 - Evolution of Creep Damage of 316L Produced by Laser Powder Bed Fusion N2 - The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed. KW - Creep KW - Computed Tomography KW - PBF-LB/M/316L KW - Laser Powder Bed Fusion KW - Microstructure KW - AISI 316L KW - Additive Manufacturing PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-574127 DO - https://doi.org/10.1002/adem.202201581 SP - 1 EP - 9 PB - Wiley-VCH GmbH CY - Weinheim AN - OPUS4-57412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beygi Nasrabadi, Hossein A1 - Klotz, Ulrich E. A1 - Tiberto, Dario A1 - Vafaeenezhad, Hossein A1 - Mishurova, Tatiana A1 - Skrotzki, Birgit T1 - Effect of keyhole and lack-of-fusion pores on the anisotropic microstructure and mechanical properties of PBF-LB/M-produced CuCrZr alloy N2 - Due to the high reflectance and heat conductivity of copper and its alloys, the processing window for laser-based powder bed fusion (PBF-LB/M) processing of high-density copper components fundamentally overlaps with conduction and keyhole melting zones, resulting in the emergence of certain pores in the structure of printed parts. The present research aims to study how the development of process-induced lack-of-fusion or keyhole porosities during the PBF-LB/M process can affect the anisotropic microstructure and mechanical properties of the produced copper alloys. For this purpose, several samples were produced utilizing a similar CuCrZr-feedstock composition but varied process parameters from different areas of the PBF-LB/M processing window, specifically at laser powers of 300 W and 380 W which define the boarders of the conduction and keyhole regimes. X-ray computed tomography (XCT) revealed that the 300-W and 380-W samples achieved relative densities of 98.88% and 99.99%, respectively, with elongated lack-of-fusion pores forming at 300 W and semi-spherical keyhole pores at 380 W. Microstructural analyses employing scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) demonstrated strong anisotropy in different build directions of the samples, owing to the growth of long columnar grains with intense < 101  orientation along the build directions. Here, the emergence of different types of pores can cause competition between the epitaxial growth of columnar grains and the heterogeneous nucleation of new grains on the layers’ interfaces, thereby significantly varying the grain size, preferred orientation, crystallographic texture, and microstructural anisotropy of the samples. Furthermore, compression tests and nanoindentation measurements of the printed alloys in the longitudinal and transverse directions revealed that the 300 W and 380 W samples exhibited compressive strength anisotropies of 0.061 and 0.072, and average nanoindentation hardness values of 1.3 GPa and 1.5 GPa, respectively. The orientation of elongated lack-of-fusion porosities perpendicular to the loading axis was identified as the most damaging factor, significantly reducing mechanical performance compared to the uniformly distributed keyhole pores. KW - Copper Alloy KW - Laser-based powder bed fusion KW - Microstructure KW - Mechanical properties KW - X-ray computed tomography (XCT) KW - Porosity KW - Anisotropy PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625655 DO - https://doi.org/10.1007/s40964-025-00972-2 SN - 2363-9520 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-62565 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Suárez Ocaño, Patricia A1 - Ávila Calderón, Luis A1 - Agudo Jácome, Leonardo A1 - Rehmer, Birgit A1 - Mohr, Gunther A1 - Evans, Alexander A1 - Skrotzki, Birgit T1 - Effect of 700–900 °C heat treatments and room and high temperature tensile deformation on the microstructure of laser powder bed fused 316L stainless steel N2 - The effect of post-processing heat treatments on the hierarchical microstructure evolution and mechanical strength of the austenitic stainless steel 316L produced by laser powder bed fusion has been investigated. Heat treatments between 700 and 900 ◦C and 0.5 to 3 h, were applied to samples treated at 450 ◦C for 4 h. The results showed a stable microstructure at all studied temperatures and times in terms of grain size, morphology, aspect ratio, density of low-angle grain boundaries, and texture. However, temperature and time promoted the diffusion of segregated elements together with a reduction in dislocation density and disappearance of the cellular structure. This was associated with a reduction in hardness and tensile proof strength at both room and high temperature. In addition, microstructural characterization coupled with thermodynamic CALPHAD-based equilibrium calculations showed that the formation of carbides and intermetallic phases was already visible after annealing at 800 ◦C for 3 hours, although these intermetallics did not affect the tensile properties at this level. Analysis of the microstructure evolution after tensile deformation showed differences in the deformation mechanisms at room and high temperature, with twinning and martensitic transformation occurring at room temperature, the latter not widely reported for additively manufactured 316L. Finally, comparisons with similar materials produced under comparable conditions showed differences in the tensile properties, attributed to differences in chemical composition and the associated presence of stacking faults in the undeformed state. KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632471 DO - https://doi.org/10.1016/j.msea.2025.148469 SN - 0921-5093 VL - 939 SP - 1 EP - 24 PB - Elsevier CY - Amsterdam AN - OPUS4-63247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -