TY - CONF A1 - Kauss, N. A1 - Rosemann, Paul A1 - Halle, T. T1 - Age-hardening behaviour, microstructure and corrosion resistance of the copper alloyed stainless steel 1.4542 N2 - The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion. T2 - EUROCORR 2018 CY - Krakow, Poland DA - 09.09.2018 KW - Corrosion KW - Stainless steel KW - Corrosion resistance KW - EPR KW - Corrosion testing KW - Heat treatment KW - ThermoCalc KW - REM KW - Martensitic stainless steels PY - 2018 AN - OPUS4-45955 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gardei, André T1 - Probenpräparation für LIBS-Messungen - ein häufig unterschätztes Thema N2 - Die Probenpräparation ist ein Teil im Prozess der Baustoffuntersuchung und muss dementsprechend sorgfältig geplant werden. Die Probenpräparation ist letztendlich der Grundstein für alle folgenden Untersuchungen, somit wirken sich alle hier getroffenen Entscheidungen direkt auf die Qualität der Ergebnisse aus. T2 - Fachtagung Bauwerksdiagnose CY - Berlin, Germany DA - 15.02.2018 KW - Probenpräparation KW - LIBS PY - 2018 AN - OPUS4-44656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Manolov, Manol T1 - Bestimmung der Maschinennachgiebigkeit beim Einsatz sphärischer Indenter in der Instrumentierten Eindringprüfung N2 - Der Einfluss der Maschinennachgiebigkeit einschließlich der elastischen Verformung des Indenters ist bei der Bestimmung der entsprechenden Werkstoffcharakteristiken insbesondere beim Einsatz von sphärischen Indentern unter höheren Prüfkräften von Bedeutung. Mit zunehmender Prüfkraft wird die Maschinennachgiebigkeit kraftabhängig und kann im idealen Fall als Funktion von Prüfkraft und gemessener Eindringtiefe für vorgegebene Indenterradien dargestellt werden. Angegeben ist ein vereinfachtes Verfahren zur Bestimmung der Maschinennachgiebigkeit. T2 - Sensoren und Messsysteme CY - Nürnberg, Germany DA - 26.06.2018 KW - Maschinennachgiebigkeit KW - Instrumentierte Eindringprüfung KW - Sphärische Indenter KW - Vereinfachtes Verfahren KW - Kraftabhängige Funktion KW - Härtevergleichsplatten KW - Eindringmodul PY - 2018 AN - OPUS4-45390 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lüth, Peter A1 - Brandes, E. A1 - Frost, K. A1 - Kurth, Lutz A1 - Schmidt, Martin A1 - Michael-Schulz, Heike A1 - Uhlig, S. T1 - CEQAT-DGHS Ringversuchsprogramm für die Chemikaliensicherheit -Methodenvalidierung N2 - Bei der Bewertung der Verlässlichkeit der im Labor gewonnenen Prüfergebnisse spielen Ringversuche eine entscheidende Rolle. Die Bundesanstalt für Materialforschung und –prüfung (BAM) unterstützt deshalb den weiteren Ausbau des Ringversuchsprogramms des im Jahr 2007 gegründeten Kompetenzzentrums zur Qualitätssicherung für Prüfungen von Gefahrgütern und Gefahrstoffen auf physikalische Gefahren (Centre for quality assurance for testing of dangerous goods and hazardous substances, CEQAT-DGHS). Bei allen bisher untersuchten Prüfmethoden besteht ein Verbesserungsbedarf. Die RV müssen daher zunächst auf die Methodenentwicklung, -verbesserung und -validierung und auf die Bestimmung der Messunsicherheit der jeweiligen Prüfmethode abzielen und nicht auf Leistungstests. T2 - Behörden-Erfahungsaustausch CY - Berlin, Germany DA - 4. Juni 2018 KW - Prüfmethode KW - Methodenvalidierung KW - Gefahrgut KW - Gefahrstoff KW - Qualitätssicherung PY - 2018 AN - OPUS4-45297 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rosemann, Paul T1 - Einfluss der Schweißnaht-Nachbehandlung auf die Korrosionsbeständigkeit von nichtrostenden Duplexstählen N2 - Der Duplexstahl 1.4062 (X2CrNiN22-2) hat sich im Bauwesen als Werkstoffalternative zu den nichtrostenden Austeniten etabliert. Die Korrosionsbeständigkeit von Schweißverbindungen wird, neben dem Grundwerkstoff, dem Schweißzusatzwerkstoff und dem Schweißverfahren, auch sehr stark von der Oberflächennachbehandlung der Schweißnaht beeinflusst. Je nach zukünftigem Anwendungsbereich und geforderter Optik sowie Korrosionsbeständigkeit wird der Schweißnahtbereich anschließend geschliffen, gebeizt, elektropoliert, oder gestrahlt, um die beim Schweißen entstehenden Zunderschicht zu entfernen. Gestrahlte Oberfläche sind in der industriellen Praxis häufig anzutreffen, da sie deutlich einfacher und kostengünstiger herzustellen sind als gebeizte oder elektropolierte Oberflächen. Die Auswahl des Strahlmittels bestimmt auch die Prozesskosten, wobei das Strahlen mit Korund effektiver als das Strahlen mit Glasperlen ist. In den letzten Jahren wurden bei nichtrostenden Stählen korrosionsanfällige Oberflächen beobachtet, wenn diese mit Korund geschliffen wurden. Daher wird nun auch beim Strahlen kritisch hinterfragt, ob das Strahlmittel die Korrosionsbeständigkeit verändert. Diese Fragestellung wird beantwortet indem geschliffene, gebeizte, mit Korund gestrahlte und mit Glasperlen gestrahlte Schweißverbindungen vergleichend untersucht werden. Die Ergebnisse der REM-Untersuchungen von den Strahlmitteln und den gestrahlten Oberflächen werden dazu mit den Ergebnissen verschiedener Korrosionsuntersuchungen (KorroPad-Indikatortest, Potentialmessungen und Bestimmung der kritischen Lochkorrosionspotentiale) korreliert und vorgestellt. T2 - Werkstoffwoche 2017 CY - Dresden, Germany DA - 27.09.2017 KW - Duplexstahl KW - Korrosion KW - Nichtrostender Stahl KW - Oberflächenbearbeitung KW - Schweißen KW - Strahlen PY - 2017 AN - OPUS4-42830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Einfluss von Korundschleifprozessen auf die Korrosionsbeständigkeit nichtrostender Stähle N2 - Das Poster stellt aktuelle Eregbnisse des AiF-Vorhabens 18823 N/1 zum Einfluss von Schleifprozessen auf die Korrosionsbeständigkeit nichtrostender Stähle vor. T2 - Jahrestagung 2017 der GfKORR CY - Frankfurt a. M., Germany DA - 07.11.2017 KW - Korrosion KW - Corrosion KW - Korundschleifen KW - Corundum grinding KW - Nichtrostende Stähle KW - Stainless Steels PY - 2017 AN - OPUS4-42773 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulte, Petra T1 - Kritische Bewertung der Prüfergebnisse in chemikalienrechtlichen Verfahren: Wie agiert die Behörde? Welche Folgen haben die Ergebnisse für die Rechtsetzung? N2 - Mit nicht-konformen oder schlecht dokumentierten Prüfergebnissen können weder Behörden noch Unternehmen etwas anfangen. Belastbare und eindeutige Informationen aus den Registrierungsdossiers sind entscheidend, damit industrielle und gewerbliche Verwender der Stoffe das Gefahrenpotenzial einschätzen und ggf. Maßnahmen zum Schutz von Menschen und Umwelt treffen können. Darüber hinaus benötigen die Behörden verlässliche Daten aus den Registrierungen, um ihrer Verantwortung bei der Identifizierung regulierungsbedürftiger Stoffe nachkommen zu können. T2 - Behörden-Erfahrungsaustausch CY - Berlin, Germany DA - 04.06.2018 KW - Prüfmethode KW - Einstufung KW - REACH KW - CLP KW - IUCLID KW - ECHA KW - OECD PY - 2018 AN - OPUS4-45808 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Falk, Florian T1 - Early oxidation and sulfidation of high temperature model alloys: An EDXRD in situ study N2 - The fundamental impact of sulfur and water on corrosion rates and potential failure of the exposed material is well known. However, the access to the related corrosion mechanism causing material degradation is often a problem to solve. This study investigates the effect of SO2 and water vapor in the initial stages of corrosion of an Fe9Cr0.5Mn model alloy at 650 °C in situ. The analysis was carried out under laboratory conditions using energy-dispersive X-ray diffraction (EDXRD). T2 - Dechema EFC Workshop CY - Frankfurt am Main, Germany DA - 26.09.2018 KW - Sulfidation KW - Model alloy KW - Oxidation PY - 2018 AN - OPUS4-46134 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wolter, Christian T1 - Metallsulfide als Reibungsstabilisatoren in Bremsbelägen - tribologische Untersuchungen an Modellsystemen N2 - Der Posterbeitrag handelt davon, wie das Reibverhalten und die Temperaturabhängikgeit durch den Einsatz von Metallsulfiden maßgeblich beeinflusst wird und zur Stabilität beiträgt. T2 - 59. Tribologie-Fachtagung CY - Goettingen, Germany DA - 24.09.2018 KW - Metallsulfide KW - Bremsbeläge KW - Tribologie PY - 2018 AN - OPUS4-46187 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munsch, Sarah Mandy T1 - Ermittlung der Porosität von Sandsteinen - Vergleich von Quecksilberporosimetrie, Tauchwägung und NMR N2 - Die Porosität sowie die Porengrößenverteilung (PSD) eines Baustoffs sind wichtige petrophysikalische Eigenschaften, die Transportprozesse im Material beeinflussen und im direkten Zusammenhang mit der Schadensanfälligkeit stehen (Frost-Tau-Schäden, Schäden durch Salzeinträge und sauren Regen). Verfahren zur Ermittlung der Porosität stellen die Quecksilberporosimetrie (MIP), das Prinzip der Tauchwägung nach Archimedes (triple weighing method, TWM) und die Nuklear Magnetische Resonanz (NMR) dar. Das Hauptziel dieser Arbeit ist der Vergleich der drei Methoden für die Porositätsbestimmung. Als Untersuchungsmaterial wurde Sandstein gewählt. Als Baustoff wird Sandstein trotz einer teilweise geringen Festigkeit, aber aufgrund seiner Farbvielfalt häufig für Kulturbauten, Gehwegmaterial und Fassaden eingesetzt. Sandsteine weisen zudem meist eine hohe effektive Porosität (bis zu ca. 30 %) und teilweise breite Porengrößenspektren auf, wodurch Feuchte- und Ioneneinträge begünstigt werden und zu z. B. langfristigen Verfärbungen an Sandsteinfassaden führen können. Im Rahmen dieser Arbeit werden die Porositäten von 10 verschiedenen Sandsteinen aus Deutschland und Tschechien bestimmt. Für die Untersuchungen mittels TWM und NMR wurden für jede Sandsteinart zwei zylinderförmige Proben unter Unterdruck mit Leitungswasser aufgesättigt. Beim Vergleich der Verfahren liegt der Fokus insbesondere auf NMR und der verwendeten Gerätetechnik, die mit einer minimalen Echozeit von 50 µs ein Wasserstoffsignal in Sandsteinen aus bis zu ca. 2 nm kleine Poren erfassen kann. Darüber hinaus wird das Auflösungsvermögen von MIP und NMR bezüglich der Poren- bzw. Poreneingangsgrößen diskutiert. Für den Vergleich von NMR und MIP werden an ausgewählten Sandsteinproben ebenfalls die zusätzlich ermittelten PSD in Korrelation zueinander gebracht. Erste Ergebnisse zeigen eine gute Korrelation von NMR- und TWM-Daten, aber teilweise starke Abweichungen zu den mit MIP bestimmten Porositäten. Ergebnisse zu den PSD zeigen teilweise nahezu identische Kurvenverläufe. Jedoch ist die Abschätzung des Umrechnungsfaktors für die NMR-Daten ohne Hinzuziehen von zusätzlichen Referenzverfahren wie Röntgen-Computer-Tomographie oder Spektral Induzierte Polarisation teilweise sehr schwierig. T2 - Bauwerksdiagnose CY - Berlin, Germany DA - 13.02.2020 KW - NMR KW - Porosität KW - Sandsteine KW - Quecksilberporosimetrie KW - Tauchwägung PY - 2020 N1 - Geburtsname von Munsch, Sarah Mandy: Nagel, S. M. - Birth name of Munsch, Sarah Mandy: Nagel, S. M. AN - OPUS4-50405 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -