TY - CONF A1 - Voigt, Marieke A1 - von Werder, Julia A1 - Meng, Birgit T1 - Thermally treated UHPC: a durability study N2 - Ultra high performance concrete (UHPC) is known for its high compressive strength of more than 150 MPa and its high durability. Thermal treatment at 90°C can accelerate the strength development so that the 28-days-strength can be achieved immediately after the treatment and an additional increase up to 30 % in some cases. The reason for the strength development is an accelerated hydration of the clinker minerals and an intensified pozzolanic reaction leading to a denser microstructure. In previous research inhomogeneities in form of a zonation after unprotected thermal treatment were observed and analysed in respect to changes in the microstructure. This zonation is defined by a different microstructure in the core compared to the outer zone in the matter of porosity, mineral phase composition and a significant change in the potassium and sulphur concentration of the zones is measurable. To isolate different transport mechanisms responsible for these element distributions UHPC samples were thermally treated at 90 °C and the microstructure was investigated under dry conditions and after immersion in water to investigate the influence of dehydration during and rehydration after the thermal treatment on the microstructure. Through durability testing via water absorption, water vapour diffusion, permeability testing and sulfuric acid resistance transport mechanisms like diffusion, migration, capillary suction are under investigation in correlation with the microstructure analysis. For the microstructure analysis measurements with µXRF, mercury intrusion porosity, XRD and SEM were conducted. T2 - HiPerMat 2020 CY - Kassel, Germany DA - 11.03.2020 KW - UHPC KW - Thermal treatment KW - Zonation KW - Transport mechanism KW - Durability PY - 2020 AN - OPUS4-52372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Voigt, Marieke A1 - von Werder, Julia A1 - Meng, Birgit ED - Middendorf, B. ED - Fehling, E. T1 - Microstructure analysis of thermally treated ultra high performance concrete in the context of the durability performance T2 - Schriftenreihe Baustoffe und Massivbau: Ultra-High Performance Concrete and High Performance Materials N2 - Ultra high performance concrete (UHPC) is known for its high compressive strength of more than 150 MPa and its high durability. Thermal treatment at 90°C can accelerate the strength development so that the 28-days-strength can be achieved immediately after the treatment and an additional increase up to 30 % in some cases. The reason for the strength development is an accelerated hydration of the clinker minerals and an intensified pozzolanic reaction leading to a denser microstructure. In previous research inhomogeneities in form of a zonation after unprotected thermal treatment were observed and analysed in respect to changes in the microstructure. This zonation is defined by a different microstructure in the core compared to the outer zone in the matter of porosity, mineral phase composition and a significant change in the potassium and sulphur concentration of the zones is measurable. To isolate different transport mechanisms responsible for these element distributions UHPC samples were thermally treated at 90 °C and the microstructure was investigated under dry conditions and after immersion in water to investigate the influence of dehydration during and rehydration after the thermal treatment on the microstructure. Through durability testing via water absorption, water vapour diffusion, permeability testing and sulfuric acid resistance transport mechanisms like diffusion, migration, capillary suction are under investigation in correlation with the microstructure analysis. For the microstructure analysis measurements with µXRF, mercury intrusion porosity, XRD and SEM were conducted. T2 - HiPerMat 2020 CY - Kassel, Germany DA - 11.03.2020 KW - UHPC KW - Thermal treatment KW - Zonation KW - Transport mechanism KW - Durability PY - 2020 SN - 978-3-7376-0828-2 DO - https://doi.org/10.17170/kobra-202002271026 VL - 23 SP - 151 EP - 152 PB - Kassel University Press CY - Kassel AN - OPUS4-52373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -