TY - JOUR A1 - Lauhoff, Christian A1 - Degener, Sebastian A1 - Bolender, Artjom A1 - Liehr, Alexander A1 - Hübner, Leoni A1 - Frenck, Johanna-Maria A1 - Molotnikov, Andrey A1 - Niendorf, Thomas T1 - In Situ Synchrotron Diffraction Assessment of Reversibility of the Martensitic Transformation in Single-Crystalline Co–Ni–Ga Shape Memory Alloy Under Torsion N2 - AbstractHeusler-type Co–Ni–Ga shape memory alloys attracted significant attention due to their excellent functional properties in single-crystalline state under both compressive and tensile loading. The present study investigates the superelastic deformation behavior under torsion. Using a newly installed torsion testing setup, in situ synchrotron diffraction was carried out on single-crystalline material in order to investigate the martensitic phase transformation. Incremental deformation experiments reveal a fully reversible martensitic transformation under torsional loading at room temperature, leading to excellent strain recovery after deformation to 6.5% shear strain. Furthermore, relevant aspects towards the analysis of powder diffraction data obtained for single-crystalline material in transmission mode under torsional loading are presented and critically discussed. KW - Shape memory alloy KW - Pseudoelasticity KW - Martensitic transformation KW - Synchrotron diffraction KW - In situ testing KW - Torsion PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621872 DO - https://doi.org/10.1007/s40830-024-00496-8 VL - 10 SP - 326 EP - 333 PB - Springer Science and Business Media LLC AN - OPUS4-62187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Brinkmann, M. A1 - Wiehle, Philipp A1 - Thiele, Marc A1 - Graubner, C.-A. ED - Schermer, D. ED - Brehm, E. T1 - Grundlagen zur Bemessung druckbeanspruchten Lehmmauerwerks N2 - Lehmmauerwerk bietet sich aufgrund seiner zahlreichen ökologischen Vorteile für die Errichtung klimafreundlicher und ressourcenschonender Gebäude an. Um den Anwendungsbereich tragenden Lehmmauerwerks durch eine zeitgemäße Nachweisführung zu erweitern, werden in diesem Beitrag Grundlagen für die Entwicklung eines eurocodekonformen Bemessungskonzepts erarbeitet. Hierzu werden die Ergebnisse umfangreicher experimenteller Untersuchungen an Lehmmauerwerk sowie Lehmsteinen und -mörteln nach Konditionierung bei unterschiedlichen Klimata vorgestellt. Darauf aufbauend erfolgt eine Traglastanalyse druckbeanspruchter Lehmmauerwerkswände mittels numerischer und analytischer Methoden. Die daraus gewonnenen Erkenntnisse werden abschließend in einen an DIN~EN~1996-3/NA angelehnten Bemessungsvorschlag überführt, welcher die materialspezifischen Besonderheiten von Lehmmauerwerk berücksichtigt und eine fundierte Grundlage für eine wirtschaftliche und zuverlässige Nachweisführung darstellt. KW - Druckfestigkeit KW - Lehm KW - Mauerwerk KW - Bemessung KW - Feuchte PY - 2023 SN - 978-3-433-03373-9 DO - https://doi.org/10.1002/9783433611142.ch4 VL - 48 SP - 79 EP - 110 PB - Ernst & Sohn GmbH CY - Berlin ET - 1 AN - OPUS4-57509 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hering, Marcus A1 - Sievers, Jürgen A1 - Curbach, Manfred A1 - Beckmann, Birgit T1 - An Approach to Predicting the Ballistic Limit of Thin Textile-Reinforced Concrete Plates Based on Experimental Results N2 - In this article, a partial selection of experiments on enhancing the impact resistance of structural components with non-metallic, textile-reinforced concrete is discussed. The focus is on the experimental investigations in which the impact resistance of thin, textile-reinforced concrete plates is characterized. The article discusses the materials, fabrics and test setup used. For the experimental work, a drop tower from the Otto Mohr Laboratory, which belongs to the Technische Universtät Dresden, was used. Furthermore, the experimental results are presented and evaluated using different methods. Based on the collected data, a suitable approach to determining the perforation velocity of an impactor through the investigated thin, textile-reinforced concrete plates is shown. KW - Building and Construction KW - Civil and Structural Engineering PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586692 DO - https://doi.org/10.3390/buildings13092234 VL - 13 IS - 9 SP - 1 EP - 14 PB - MDPI AN - OPUS4-58669 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ratkovac, Mirjana A1 - Gerards-Wünsche, Paul A1 - Thiele, Marc A1 - Brackrock, Daniel A1 - Stamm, Michael T1 - Detection and monitoring of the fatigue crack growth on welds – Application-oriented use of NDT methods N2 - Early detection of fatigue cracks and accurate measurements of the crack growth play an important role in the maintenance and repair strategies of steel structures exposed to cyclic loads during their service life. Observation of welded connections is especially of high relevance due to their higher susceptibility to fatigue damage. The aim of this contribution was to monitor fatigue crack growth in thick welded specimens during fatigue tests as holistically as possible, by implementing multiple NDT methods simultaneously in order to record the crack initiation and propagation until the final fracture. In addition to well-known methods such as strain gauges, thermography, and ultrasound, the crack luminescence method developed at the Bundesanstalt für Materialforschung und -prüfung (BAM), which makes cracks on the surface particularly visible, was also used. For data acquisition, a first data fusion concept was developed and applied in order to synchronize the data of the different methods and to evaluate them to a large extent automatically. The resulting database can ultimately also be used to access, view, and analyze the experimental data for various NDT methods. During the conducted fatigue tests, the simultaneous measurements of the same cracking process enabled a comprehensive comparison of the methods, highlighting their individual strengths and limitations. More importantly, they showed how a synergetic combination of different NDT methods can be beneficial for implementation in large-scale fatigue testing but also in monitoring and inspection programs of in-service structures - such as the support structures of offshore wind turbines. T2 - Fatigue Design 2023 (FatDes 2023) CY - Senlis, France DA - 29.11.2023 KW - Fatigue KW - Welded KW - NDT KW - Crack growth PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600238 DO - https://doi.org/10.1016/j.prostr.2024.03.062 VL - 57 SP - 560 EP - 568 PB - Elsevier B.V. AN - OPUS4-60023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Artinov, Antoni T1 - Modeling the Relationship between Weld Pool Dynamics and Centerline Solidification Cracking in High Power Laser Beam Welding N2 - The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high-speed camera, and two thermal imaging cameras is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs above 10 mm penetration depth. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root. T2 - Gastvortrag an der Universität Innsbruck, Institut für Konstruktion und Materialwissenschaften CY - Innsbruck, Austria DA - 18.06.2023 KW - Laser beam welding KW - Centerline solidification cracking KW - Bulging KW - Numerical simulation PY - 2024 AN - OPUS4-60333 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frenck, Johanna-Maria A1 - Frenck, Georg A1 - Degener, Sebastian A1 - Vollmer, Malte A1 - Niendorf, Thomas T1 - Interrelationships of stress-induced martensitic phase transformation and pitting corrosion in iron-based shape memory alloys N2 - Orientation dependence of stress-induced martensitic transformation under compression and the influence of a corrosion attack on superelastic properties were investigated for Fe42.7Mn34.7Al13.4Ni7.7Cr1.5 (at.−%) single crystals. The results of incremental strain tests show that the crystallographic orientation has a considerable impact on the superelastic performance, eventually resulting from the formation of twinned or detwinned martensite to accommodate strain as well martensite variant interaction. In order to investigate the effect of a corrosive environment on the mechanical performance and martensitic transformation, compression specimens were immersed in a 5.0 wt.−% NaCl solution for 24 h before tested in incremental strain tests. The immersion of the compression specimens revealed a partial surface corrosion attack including localized pitting corrosion. The localized corrosion attack increased the number of active martensite plates, most probably due to an induced multiaxial stress state. Further investigations on specimens subjected to −6% compressive strain revealed that areas with retransformed martensite serve as nucleation zones for corrosion damage. Stress-induced corrosion cracks developed, which eventually deteriorate functional response. KW - Shape memory alloy (SMA) KW - In situ characterization KW - Corrosion KW - Austenite-to-martensite phase transformation PY - 2024 DO - https://doi.org/10.1016/j.mtla.2023.102001 VL - 33 SP - 1 EP - 11 PB - Elsevier BV AN - OPUS4-61283 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Costard, René T1 - Explosionsauswirkungen auf Strukturen Versuche und Simulationen N2 - Vorstellung der Versuche von Explosionsversuchen auf dem TTS. Diese werden ergänzt durch die Ergebnisse durchgeführter Simulationen und zeigen die Wirkung von zivilen Explosivstoffen auf Gebäudestrukturen und die aufgetretenen Schädigungen. T2 - 46. Informationstagung Sprengtechnik CY - Siegen, Germany DA - 25.04.2025 KW - Explosivstoff KW - Skalierung KW - Strukturauswirkung KW - Numerische Simulation PY - 2025 AN - OPUS4-62998 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wiehle, Philipp T1 - Einfluss der Feuchtigkeit auf das Tragverhalten von Lehmmauerwerk N2 - Im Mittelpunkt der vorliegenden Arbeit steht der Einfluss der Feuchte auf die mechanischen Eigenschaften von Lehmmauerwerk. Der Wissensstand zum feuchteabhängigen Tragverhalten von Lehm(mauerwerk) ist bisher lückenhaft, sodass keine explizite Berücksichtigung der Bauteilfeuchte bei der Bemessung tragender Konstruktionen erfolgt. Aktuelle und verlässliche Daten zum Einfluss der Feuchte auf die mechanischen Kenngrößen moderner Lehmbaustoffe fehlen bisher ebenso wie Messwerte in Bezug auf die Bauteilfeuchte unter natürlichen Klimabedingungen. Deswegen wurden im Rahmen dieser Arbeit umfangreiche Untersuchungen zum mechanischen und hygrothermischen Verhalten von Lehmmauerwerk durchgeführt. Die experimentellen Untersuchungen bestehen im Wesentlichen aus Druckversuchen an Lehmsteinen, -mörteln, kleinformatigen Lehmmauerwerksprobekörpern und geschosshohen Lehmmauerwerkswänden. Um das Feuchteverhalten beschreiben zu können, fanden außerdem erstmalig magnetresonanzspektroskopische Messungen an Lehmsteinen statt und es wurden die tatsächlich auftretenden Feuchtegehalte an einer Lehmmauerwerkswand unter natürlichen Klimabedingungen in Form von Langezeitmessungen ermittelt. Es konnte festgestellt werden, dass ein linearer Zusammenhang zwischen Druckfestigkeit und relativer Luftfeuchte besteht, wobei sich die Druckfestigkeit umgekehrt proportional zur relativen Luftfeuchte verhält. Je Prozent Steigerung der relativen Luftfeuchte kommt es zur Abnahme von einem Prozent der Druckfestigkeit. Gleiches gilt für das Elastizitätsmodul. Weiterhin konnte auf Basis der feuchtetechnischen Untersuchungen ein numerisches Modell zur Berechnung des instationären hygrothermischen Verhaltens für Lehmbaustoffe kalibriert werden. Anhand dieses Modells gelang es die bemessungsrelevanten Feuchtegehalte unter Berücksichtigung des instationären hygrothermischen Verhaltens realitätsnah zu berechnen. Die maximalen Feuchtegehalte im Lehmmauerwerk konnten somit in Form einer Parameterstudie in Abhängigkeit des Anwendungsfalls ermittelt werden, wodurch eine explizite Berücksichtigung des Feuchtegehaltes bei der Bemessung ermöglicht wurde. Die Verknüpfung der Erkenntnisse aus den mechanischen und hygrothermischen Untersuchungen dieser Arbeit bildet die Grundlage für das Bemessungskonzept der im Juni 2023 veröffentlichten DIN 18940: Tagendes Lehmsteinmauerwerk. KW - NMR KW - Lehm KW - Mauerwerk KW - Druckfestigkeit KW - Feuchtigkeit PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637794 DO - https://doi.org/10.14279/depositonce-20800 SP - 1 EP - 114 CY - Berlin AN - OPUS4-63779 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiehle, Philipp A1 - Baier, Johanna A1 - Thiele, Marc T1 - Structural Design of Earth Masonry in Accordance with Eurocode 6 – Considering Moisture Content and E/fk Ratio N2 - The load‐bearing behaviour of earth masonry is similar to conventional masonry, with two key differences: compressive strength and Young's modulus are dependent on moisture content, and the ratio between Young's modulus and characteristic compressive strength (E/fk) is significantly lower. The current design concept according to the Lehmbau Regeln does not explicitly address these factors, relying instead on a general safety margin, leading to an underestimation of the load‐bearing capacity of modern earth masonry.Compression tests on small‐scale masonry specimens and storey‐high walls revealed that compressive strength and Young's modulus decrease inversely proportional to the increase in relative humidity. Additionally, it was found that conventional masonry design guidelines overestimate the buckling resistance of earth masonry due to its low E/fk ratio of ∼440. However, this ratio remains independent of moisture content, simplifying structural design, as the load‐bearing capacity is only influenced by wall slenderness.The study's findings form the foundation for the newly published German design standard DIN 18940, which explicitly considers moisture content through service classes with moisture factors and addresses the low E/fk ratio with a bilinear adaptation of the reduction factor considering the slenderness. Along with the introduction of the semi‐probabilistic design concept and rigid‐plastic determination of cross‐sectional load‐bearing capacity, modern earth masonry can now be applied in buildings up to four storeys. T2 - Earth Builder Summit CY - Biberach, Germany DA - 06.03.2025 KW - Service class KW - Earth masonry KW - Structural design KW - Moisture PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637803 DO - https://doi.org/10.1002/cepa.3287 SN - 2509-7075 VL - 8 IS - 1 SP - 9 EP - 21 PB - Ernst & Sohn GmbH AN - OPUS4-63780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Farhat, Abbas A1 - Luu, Li-Hua A1 - Doghmane, Alexis A1 - Cuéllar, Pablo A1 - Benahmed, Nadia A1 - Wichtmann, Torsten A1 - Philippe, Pierre T1 - Micro and macro mechanical characterization of artificial cemented granular materials N2 - The focus of this study is the experimental characterization of cemented granular materials, with the aim of identifying the microscopic properties of the solid bonds and describing the extension to macroscopic mechanical strength of cemented samples.We chose to use artificially bonded granular materials, made of glass beads connected by solid paraffin bridges. The results of several sets of laboratory tests at different scales are presented and discussed. Micromechanical tests investigate the yield strength of single solid bonds between particles under traction, shearing, bending and torsion loading, as a function of variations in particle size, surface texture and binder content. Macro-scale tensile tests on cemented samples explore then the scale transition, including influence of confining walls through homothetic variations of the sample size. Despite the large statistical dispersion of the results, it was possible to derive and validate experimentally an analytical expression for micro tensile yield force as a function of the binder content, coordination number and grain diameter. In view of the data, an adhesive bond strength at the contact between bead and solid bond is deduced with very good accuracy and it is even reasonable to assume that the other threshold values (shear force, bending and torsion moments) are simply proportional to the tensile yield, thus providing a comprehensive 3D model of cemented bond. However, the considerable dispersion of the data at the sample scale prevents validation of the extended model for macroscopic yield stress. A final discussion examines the various factors that may explain intrinsic variability. By comparison with other more realistic systems studied in the literature in the context of bio-cementation, our artificial material nevertheless appears suitable for representing a cemented granular material. Being easy to implement, it could thus enable the calibration of discrete cohesion models for simulation of practical applications. KW - Cemented granular material KW - Micro-mechanical characterisation KW - Artificial soils KW - Yield tensile stress PY - 2024 DO - https://doi.org/10.1007/s10035-024-01426-2 SN - 1434-5021 VL - 26 IS - 3 SP - 1 EP - 20 PB - Springer CY - Berlin AN - OPUS4-63507 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -