TY - CONF A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dixneit, Jonny T1 - Observation of martensite formation by combined use of synchrotron diffraction and dilatometry N2 - Welding residual stress engineering by means of an adjusted martensite phase transformation would be highly attractive as detrimental tensile residual stresses may be prevented already during welding without time and cost intensive post processing. The present study shows a synchrotron diffraction analysis of a martensitic steel subjected to thermo-mechanical load cycles. Experiments were conducted regarding the microstructural strain response during the austenite to martensite transformation. The strains are a function of the temperature and the specific loads applied during cooling. The relation between the transformation plasticity of the material, the amount of martensite formed and the arising strains can thus be assessed. The lattice plane specific strains were compared to experimental findings from (macro) dilatation tests. It is shown that the microscopic material behavior differs remarkably from the one observed on the macroscopic scale, what leads to characteristic residual stresses in the material. T2 - Material Science & Technology (MS&T16) 3rd International Workshop of In-situ Studies with Photons, Neutrons and Electrons Scattering CY - Salt Lake City, UT, USA DA - 23.10.2016 KW - Residual stress KW - Martensite KW - Dilatometry KW - Synchrotron diffraction KW - Neutron diffraction PY - 2016 AN - OPUS4-37999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Cabeza, Sandra A1 - Onorbe, Elvira A1 - Garces, Gerardo A1 - Perez, Pablo A1 - Klaus, Manuela A1 - Genzel, Christoph A1 - Adeva, Paloma T1 - The evolution of internal strain in Mg-Y-Zn alloys with a long period stacking ordered phase N2 - The load partition in Mg-Y-Zn system is studied by means of synchrotron diffraction. in-situ tensile tests disclose LPSO phases were for the first time proved to behave as an efficient reinforcement in Mg-Y-Zn alloys, therefore they could be treated as “short-fibre composite” for the modeling of mechanical behaviour. T2 - MECASENS CY - Grenoble, France DA - 16.09.2015 KW - Magnesium KW - LPSO KW - Synchrotron diffraction KW - Load partition PY - 2011 AN - OPUS4-38397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -