TY - CONF A1 - Tang, Chi-Long T1 - Sub-4 nm particles from FFF-3D printing measured with the TSI 1 nm CPC and the Airmodus A11 nCNC N2 - Concerns have been raised as Fused Filament Fabrication (FFF) desktop 3D printer emits harmful ultrafine particles (dP < 100 nm) during operation in indoor spaces. However, the vast majority of previous emission studies have neglected the possible occurrence of sub-4 nm particles by using conventional condensation particle counter (CPC) for detection. Thus, the total particle emission could be systematically underestimated. This study has compared two diethylene glycol (DEG) based instruments to evaluate their suitability for measuring organic FFF particles in the sub-4 nm size range either as particle counter or as a particle size spectrometer. T2 - European Aerosol Conference 2024 CY - Tampere, Finland DA - 25.08.2024 KW - Air pollution KW - Emission testing KW - FFF-3D printing KW - Sub-4nm particles KW - Ultrafine particles PY - 2024 AN - OPUS4-60930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Strzelczyk, Rebecca T1 - Zeolites loaded with VOCs as reference for material emissions testing N2 - Nowadays, people spend most of their time indoors. Thus, a good indoor air quality is important. Emissions of volatile organic compounds (VOCs) from furniture and building materials can cause health complaints1. Quantitative VOC-emission testing is carried out under standardized conditions in emission test chambers. In the presented project an emission reference material (ERM) is developed that emits a defined mixture of VOCs which is required for quality assurance and -control (QA/QC) measures. Porous materials (e.g zeolites, activated carbons, MOFs or aerogels) are used as reservoir materials and impregnated with VOC. The porous materials are selected, among others, by their pore size, pore size distribution, polarity and availability. Due to their regular pore structure zeolites are tested at first. For a prediction of the emission profile, the ERM is supposed to exhibit a constant emission rate over time. The aim is a stability of ≤ 10 % change in the emission rate over a minimum of 14 days. Method For impregnation, the material is placed into an autoclave inside a rotatable basket. The VOC is added and the autoclave is closed. Afterwards, CO2 is inserted. The closed system is then heated to the supercritical point of CO2 (31 °C, 73.75 bar). In this state, the CO2 acts as solvent for the VOC. By rotating the basket, the distribution of the VOC is ensured. After a few minutes, the pressure is decreased slowly and the CO2 is released. For the determination of the emission profile, the impregnated sample is placed into an emission test chamber. These chambers can be operated either with dry or humid air (50 ± 5 % rel. humidity). Every second to third day, air samples are taken and analyzed by gas chromatography. For an ideal impregnation, several different pressures and temperatures as well as impregnation times are tested. Results Two zeolite materials tested in dry air conditions reach emission profiles with a decrease of less than 10 % over 14 days (heptane and toluene, respectively). Further it was discovered that smaller pellets of the same zeolite show better results than bigger particles. When the pore size of a zeolite is too small, e.g. 0.3 nm, the VOC cannot be absorbed sufficiently. The main disadvantage of zeolites is their hygroscopicity because it has a large impact on the release of VOC when they are used in emission test chambers under standardized test conditions (23 °C, 50 % rel. humidity). Activated carbons have emission profiles with a larger change over 14 days. However, the high hydrophobicity allows measurements in humid air conditions which was not possible with the before mentioned hygroscopic zeolites. It is possible to impregnate powdered materials as well, and thus powdered non-hygroscopic (n.h.) zeolites were impregnated. Their emission profiles are comparable to those of the activated carbons. The use of methylated hygroscopic zeolites with a decrease in hygroscopicity did not yield successful emission measurements. The change over 14 days is calculated only for the stable phase (~250–300 h). The desired stability of ≤ 10 % change of the emission rate over 14 days could already be reached under dry testing conditions. Further investigations under humid conditions show that zeolites with high Si/Al-ratios are non-hygroscopic and comparable to activated carbons (20–30 % change). The next step is to reduce the change in the emission rate of these materials to the aimed ≤ 10 % over 14 days. T2 - Deutsche Zeolithtagung CY - Jena, Germany DA - 28.02.2024 KW - VOC KW - Emission KW - Quality assurance KW - Reference material KW - Zeolite PY - 2024 AN - OPUS4-59843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davenport, Rebecca T1 - Regulations versus practice and the Divine Name: Ink analysis in medieval Torah scrolls N2 - The medieval Rabbis had very strict rules for the construction of a Sefer Torah. The Divine Names should be written • by a qualified scribe • who is ritually pure • in the presence of a minyan (10 adult Jewish men) • in an appropriate frame of mind • without being interrupted However, when these scrolls were written it would have been impossible to verify any of this after the fact. While we do not currently have any way to determine how recently the scribes had bathed, or what they might have been thinking as they wrote, we can now know much more about the inscription of the Divine Name than these scribes ever would have guessed. It is sometimes apparent from a visual inspection of the text that the Divine Name has been written in a second stage, from irregular letter kerning or a different ink colour. Using XRF, we have been able to discover more instances of a different ink used for the Name, and have shown that in some cases the secondary ink was also used to correct the main text, suggesting that the later writing was done by a master scribe who also proofread the entire scroll. Using a Brucker M6 Jetstream, it has been possible to produce elemental “heat maps” of whole paragraphs or even large sections of a parchment sheet. Using such large samples of text, we can usefully compare the levels of copper and zinc used to write individual letters or words despite their relatively low concentration, which permits very fine differentiation of the inks used. The techniques presented here would also be highly applicable to assessing ink degradation, as they are able to detect much smaller differences in ink composition than had previously been possible. T2 - The International Iron Gall Ink Meeting 2025 CY - Lisboa, Portugal DA - 07.05.2025 KW - XRF spectroscopy KW - Torah scrolls KW - Jewish studies KW - XRF mapping PY - 2025 AN - OPUS4-65036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Misra, Archismita T1 - Polyoxometalate Ionic Liquids as Protective Coatings for Industrial Infrastructure and Cultural Heritage against Microbiologically Influenced Corrosion (MIC) N2 - Corrosion of stone and metal due to acid rain and biodeterioration poses significant challenges for industrial and residential infrastructure, as well as cultural heritage, including statues and historical artefacts. A promising mitigation strategy involves thin, transparent films of polyoxometalate-based ionic liquids (POM-ILs) as chemical shields. Stone samples coated with acid-resistant, biocidal POM-ILs exhibited negligible corrosion when exposed to simulated acid rain, in stark contrast to the severe deterioration of unprotected samples. Additionally, their biocidal properties effectively prevent biofilm formation on coated surfaces. Following studies successfully explored the effectiveness of the coating against lampenflora growing in the Pommery Champagne cellar; and the long-term performance of POM-ILs under outdoor environmental conditions. So, POM-ILs have already demonstrated remarkable anticorrosion and antimicrobial properties against aerobic microorganisms and, being water-insoluble, do not leach into aquatic ecosystem. The current research project repurposes the POM-ILs, extending their application to metals, specifically targeting microbiologically influenced corrosion (MIC) in cultural heritage artefacts made of brass, carbon steel, cast iron, and bronze. This involves optimizing nanocoating adhesion to the metal surface and evaluating its protective efficacy against MIC caused by anaerobic microorganisms such as methanogenic archaea and sulfate reducing bacteria (SRB). This presentation will highlight POM-ILs as sustainable, high-performance nanocoatings for biocorrosion mitigation. It will showcase published success stories, discuss ongoing research and proof-of-concept results, and explore future prospects for these advanced materials in safeguarding metal infrastructure and artefacts across different industrial sectors as well as in the context of cultural heritage conservation. T2 - Euro-MIC COST Action - Closing Workshop Conference CY - Horsens, Denmark DA - 17.09.2025 KW - Polyoxometalates KW - Corrosion KW - Microbiologically Influenced Corrosion KW - Ionic Liquid PY - 2025 AN - OPUS4-64549 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -