TY - CONF A1 - Breitenbücher, R. A1 - Przondziono, R. A1 - Meng, Birgit A1 - Krütt, Enno A1 - Weise, Frank T1 - Alkali-Silica Reaction in concrete pavements considering traffic and de-icing agents N2 - In concrete pavements, damages occurred which are related to an Alkali-Silica-Reaction (ASR). Although the background for such an ASR has been studied extensively, special conditions in pavements increase this reaction significantly. These are especially the superposition of microstructural degradation caused by cyclic loading with an external alkali supply. Previous investigations of ASR focused mainly on the material itself (aggregates, cements, assessment of the concrete) while these special circumstances have not been considered. Concrete pavements are subjected to cyclic loadings by traffic and climate changes. Within cooperative research projects the different interdependent influencing factors for a damaging ASR in concrete pavements are studied by experiments as well as by numeric modelling. On the micro-level the ASR-related processes within the aggregate, such as gel-formation or ion-transport, are investigated. On the meso-level, the project focuses on the characterization of degradation effects in the concrete microstructure due to cyclic loading. Further, special attention is paid to the transport behavior of fluids in such pre-damaged concrete structures with and without the effect of overrunning tires as well as the impact on the ASR itself. Finally, on the macro-level the risk of an ASR-damage is assessed. T2 - 13th International Symposium on Concrete Roads CY - Berlin, Germany DA - 19.06.2018 KW - Alkali-Silica Reaction KW - Degradation KW - Cyclic loading KW - Fluid transport KW - Traffic PY - 2018 SP - 1 EP - 15 AN - OPUS4-46354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Olbricht, Jürgen A1 - Agudo Jácome, Leonardo A1 - Jürgens, Maria A1 - Roohbakhshan, Farshad A1 - Fedelich, Bernard A1 - Skrotzki, Birgit T1 - Cyclic loading performance and related microstructure evolution of ferritic-martensitic 9-12% Cr steels N2 - The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach. T2 - 44th MPA-Seminar CY - Leinfelden/Stuttgart, Germany DA - 17.10.2018 KW - Ferritic-martensitic steels KW - Cyclic loading KW - Microstructure evolution PY - 2018 SP - 259 EP - 265 AN - OPUS4-47118 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -