TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Improved Deposition of Nanoparticles vy Electrospray Analaysis with SEM/TEM and EDS N2 - Although there are many experimental techniques for measuring particle sizes and size distributions, electron microscopy (EM) is still considered as the gold standard in this field, especially when it comes to particle sizes in the nanorange (1 nm – 100 nm). Furthermore, high-resolution X-ray spectroscopy (EDS) can be applied to individual nanoparticles. To be able to extract accurate information from the EM micrographs and EDS elemental maps that are representative for the material under investigation, one needs to assure the representativity of the particles as sampled on the substrate and their homogeneous spatial distribution, to avoid operator bias when selecting the imaged area. Furthermore, agglomeration should be avoided as far as possible. Several sample preparation techniques exist since a long time, the most common way being suspending the particles in a liquid and depositing them on the grid. However, this procedure includes the drying of larger solvent amounts on the substrate itself, which can affect the spatial distribution of the deposited particles. One possibility to overcome this problem is the use of an electrospray system, where the suspension of particles is sprayed onto the substrate in charged droplets that are so small that they either dry off on the substrate immediately without affecting the position of particles, or even already during their flight time to the substrate. No dedicated commercial instruments are available for the preparation of TEM grids yet, only electrostatic deposition of aerosols on TEM grids has been reported so far. To test the prototype and assess its performance, several materials have been sprayed onto TEM grids and the resulting particle distributions were compared to more traditional sample preparation strategies like the “drop on grid” method. Operation parameters such as the sample flow-rate, capillary – substrate distance, electric field strength and sampling period length have been optimised. It was found that the particles deposited by electrospray generally show a much more homogeneous spatial distribution on the substrate and a substantial increase of the number of single particles, which are much better suited to an automatic image evaluation procedure than the agglomerated particles observed otherwise. The applicability of the technique to a broad range of materials is demonstrated by various examples, but also the influence of the substrate, the choice of the particular TEM grid, on the obtained spatial particle distribution is assessed. T2 - EMAS 2017 - 15th European Workshop on MODERN DEVELOPMENTS AND APPLICATIONS IN MICROBEAM ANALYSIS and IUMAS-7 Meeting CY - Konstanz, Germany DA - 07.05.2017 KW - Electrospray deposition KW - TEM grids KW - Nanoparticles KW - Agglomeration PY - 2017 AN - OPUS4-40257 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Organic surface modification and analysis of TiO2 nanoparticles for self-assembly in multiple layers N2 - Parameters of TiO2 coatings can greatly influence their final performance in largescale applications such as photocatalytic measurements, orthopedic and/or dental prostheses, cell cultures, and dye-sensitized solar cells. From different film deposition procedures, self-assembly of TiO2 NPs in multiple layers was selected for systematic characterization. EDX, AES and ToF-SIMS analysis have been carried out in order to evaluate the functionalization of several types of TiO2 NPs differing in size, shape and surface area. T2 - Microscopy & Microanalysis 2017 Meeting CY - St. Louis, MO, USA DA - 06.08.2017 KW - TiO2 KW - Nanoparticles KW - EDX KW - ToF-SIMS KW - XPS KW - Auger electron spectroscopy KW - Functionalization PY - 2017 AN - OPUS4-41662 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rades, Steffi A1 - Hodoroaba, Vasile-Dan A1 - Ortel, Erik A1 - Wirth, Thomas A1 - Borghetti, P. A1 - Garcia, S. A1 - Gómez, E. A1 - Blanco, M. A1 - Alberto, Gabriele A1 - Martra, G. T1 - Organic surface modification and analysis of titania nanoparticles for self-assembly in multiple layers N2 - Parameters of TiO2 coatings can greatly influence their final performance in largescale applications such as photocatalytic measurements, orthopedic and/or dental prostheses, cell cultures, and dye-sensitized solar cells. From different film deposition procedures, self-assembly of TiO2 NPs in multiple layers was selected for systematic characterization. EDX, AES and ToF-SIMS analysis have been carried out in order to evaluate the functionalization of several types of TiO2 NPs differing in size, shape and surface area. KW - TiO2 KW - Nanoparticles KW - Surface modification KW - Functionalization PY - 2017 UR - https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/organic-surface-modification-and-analysis-of-titania-nanoparticles-for-selfassembly-in-multiple-layers/66776A4CA7FD059CE39041A99A922D90 DO - https://doi.org/10.1017/S1431927617010029 SN - 1431-9276 SN - 1435-8115 VL - 23 IS - S1 (July) SP - 1872 EP - 1873 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-42457 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Radnik, Jörg T1 - XPS at BAM - Some insights into our activities N2 - Some examples will be given showing the application of XPS in different fields, like polymers, nanoparticles, solar cells and inorganic thin films. T2 - Besuch beim GFZ Potsdam CY - Potsdam, Germany DA - 18.05.2018 KW - XPS KW - Surface analytics KW - Nanoparticles KW - Polymers KW - Solar cells PY - 2018 AN - OPUS4-44981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mrkwitschka, Paul T1 - Comparative study of suitable preparation methods to evaluate irregular shaped, polydisperse nanoparticles by scanning electron microscopy (SEM). N2 - Reliable characterization of materials at the nanoscale regarding their physio-chemical properties is a challenging task, which is important when utilizing and designing nanoscale materials. Nanoscale materials pose a potential toxicological hazard to the environment and the human body. For this reason, the European Commission amended the REACH Regulation in 2018 to govern the classification of nanomaterials, relying on number-based distribution of the particle size. Suitable methods exist for the granulometric characterization of monodisperse and ideally shaped nanoparticles. However, the evaluation of commercially available nanoscale powders is problematic. These powders tend to agglomerate, show a wide particle size distribution and are of irregular particle shape. Zinc oxide, aluminum oxide and cerium oxide with particle sizes less than 100 nm were selected for the studies and different preparation methods were used comparatively. First, the nanoparticles were dispersed in different dispersants and prepared on TEM-supported copper grids. Furthermore, individual powders were deposited on carbon-based self-adhesive pads. In addition, the samples were embedded by hot mounting and then ground and polished. The prepared samples were investigated by scanning electron microscopy (including the transmission mode STEM-in-SEM) and Dynamic Light scattering. The software package ImageJ was used to segment the SEM images and obtain the particle sizes and shapes and finally the number-based particles size distribution with size expressed as various descriptors. T2 - Ceramics 2021 CY - Online meeting DA - 19.04.2021 KW - Nanoparticles KW - Preparation KW - Characterization PY - 2021 AN - OPUS4-53272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - New reference material candidates for traceable size measurement of non-spherical nanoparticles N2 - New model nanoparticles with well-controlled shape were synthesized within the EMPIR project nPSize - Improved traceability chain of nanoparticle size measurements. Their systematic characterization takes place by the traceable methods scanning/transmission electron microscopy, atomic force microscopy and small angle X-ray scattering. Following reference nanoparticle candidates are under investigation with respect to their homogeneity and stability: titania nanoplatelets (10-15 nm x 50-100 nm), titania bipyramides (~60 nm x 40 nm), titania acicular particles (100 nm x 15-20 nm; aspect ratio 5.5/6), gold nanorods (~10 nm x 30 nm), and gold nanocubes (~55 nm x 55 nm x 55 nm). T2 - HyMET Workshop on optical surface analysis methods for nanostructured layers CY - Berlin, Germany DA - 10.10.2019 KW - Nanoparticles KW - Reference materials KW - Traceability KW - Particle size distribution PY - 2019 AN - OPUS4-49285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Surface and Microbeam Analytical Methods @BAM N2 - An overview of the activities in the field of surface and microbeam analysis at BAM-6.1 is given with focus on physico-chemical characterization at the nanoscale. Ideas of potential joint activities are presented: structural and chemical analysis of graphene, deposition techniques for nanoparticles, EBSD on steel for a broader range of methods, instruments and types of steel, soft X-ray Analysis of low-Z materials, analysis of mesoporous thin films, etc. T2 - BAM-IFW Workshop CY - Dresden, Germany DA - 28.03.2019 KW - PC characterisation KW - Nanoscale KW - Nanoparticles PY - 2019 AN - OPUS4-47860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Analysis of Fluorine Traces in TiO2 Nanoplatelets by SEM/EDX, AES and TOF-SIMS N2 - The synthesis of TiO2 nanoplatelets with fluorine-containing reactants is carried out using Ti (IV) butoxide as precursor and concentrated HF as shape controller, the final product requires a working up in order to eliminate or at least to reduce the amount of residual fluorides, which is realized here by well-defined thermal treatment. Qualitative investigation of the bulk elemental composition by means of EDX of TiO2 nanoparticles (NPs) has identified fluorine in case of the as-synthesized samples. EDX spectra of thermally treated products exhibit either a fluorine content close to the limit of detection. The latter holds also true for the reference sample, TiO2 NPs of bipyramidal shape and prepared by a different synthesis route. For differentiation whether fluorine is present in the bulk or at the surface of the TiO2 nanoplatelets, top-surface sensitive AES and ToF-SIMS has been applied. Secondary ions of fluorine are detected in ToF-SIMS spectra of all samples, but could be roughly quantified by measurement of same reference sample as for EDX, namely TiO2 nano-bipyramids. This revealed that the amount of fluorine within1 nm depth beneath the surface is reduced in the thermally treated specimen compared to the raw product down to a content about as low as in the reference sample. AES allows analyzing analysis of the first few nanometers from the top-surface of individual NPs by point analysis. An F KLL peak has been detected at the surface of samples of as-prepared TiO2 nanoplatelets under optimized measurement conditions, but was not detectable after their calcination, which is in agreement with ToF-SIMS results. Moreover, high resolution AES on single TiO2 nanoplatelets elucidated that the surface atomic layers surrounding the TiO2 nanopaltelet contain fluorides before thermal treatment of the NPs. T2 - 17th European Conference on Applications of Surface and Interface Analysis ECASIA 2017 CY - Montpellier, France DA - 24.09.2017 KW - Titania KW - Nanoparticles KW - Fluorine KW - SEM/EDX KW - Auger Electron Spectroscopy KW - Nanoplatelets PY - 2017 AN - OPUS4-42656 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - SETNanoMetro advances: Fabrication and measurement of TiO2 engineered nanoparticles N2 - The press conference on the results of the European Project FP7 constitutes a dissemination event dedicated to the production and characterization of "Shape-engineered TiO2 nanoparticles for metrology of functional properties: setting design rules from material synthesis to nanostructured devices" with the main large-scale applications in the three reference sectors: energy, health and environment. T2 - Press conference on the results of the European Project FP7 CY - Istituto Nazionale di Ricerca Metrologica (INRiM), Torino, Italy DA - 31.03.2017 KW - TiO2 KW - Nanoparticles KW - Measurement KW - Metrology KW - Shape-enegineered nanoparticles PY - 2017 AN - OPUS4-39622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - nPSize - Improved traceability chain of nanoparticle size measurements N2 - The overall objective of project Improved traceability chain of nanoparticle size measurements is to improve the traceability chain for nanoparticle size measurements. The main impact will be achieved by manifold contributions to standard documents for CEN/TC 352 “Nanotechnologies”, which directly addresses the research needs of CEN, CENELEC and ETSI mandated by EC to develop standards for methods and reference materials to accurately measure the size and size distribution of nanoparticles. This will take place in collaboration with ISO/TC229 ‘Nanotechnologies’, ISO/TC24/SC4 ‘Particle characterization’ and ISO/TC201 ‘Surface analysis’/ SC9 ‘Scanning probe microscopy’. T2 - 4. Sitzung des wissenschaftlichen Beirats zum Themefeld Umwelt der BAM CY - BAM, Berlin, Germany DA - 13.04.2018 KW - Nanoparticles KW - Nanoparticle size KW - Traceability KW - Standardization PY - 2018 AN - OPUS4-44695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -