TY - JOUR A1 - Simon, Sebastian A1 - Gluth, Gregor A1 - Peys, A. A1 - Onisei, S. A1 - Banerjee, D. A1 - Pontikes, Y. T1 - The fate of iron during the alkali-activation of synthetic (CaO-)FeOx-SiO2 slags: An Fe K-edge XANES study JF - Journal of the American Ceramic Society N2 - Slags from the nonferrous metals industry have great potential to be used as feedstocks for the production of alkali-activated materials. Until now, however, only very limited information has been available about the structural characteristics of these materials. In the work presented herein, synthetic slags in the CaO–FeOx–SiO2 system, representing typical compositions of Fe-rich slags, and inorganic polymers (IPs) produced from the synthetic slags by activation with alkali Silicate solutions have been studied by means of X-ray absorption near-edge structure (XANES) spectroscopy at the Fe K-edge. The iron in the slags was largely Fe2+, with an average coordination number of approximately 5 for the iron in the amorphous fraction. The increase in average oxidation number after alkali-activation was conceptualized as the consequence of slag dissolution and IP precipitation, and employed to calculate the degrees of reaction of the slags. The degree of reaction of the slags increased with increasing amorphous fraction. The iron in the IPs had an average coordination number of approximately 5; thus, IPs produced from the Fe-rich slags studied here are not Fe-analogs of aluminosilicate geopolymers, but differ significantly in terms of structure from the latter. KW - Alkali-activated slag KW - Inorganic polymers KW - Iron speciation KW - Nonferrous slag KW - X-ray absorption near-edge structure KW - X-ray absorption spectroscopy PY - 2018 DO - https://doi.org/10.1111/jace.15354 SN - 1551-2916 SN - 0002-7820 VL - 101 IS - 5 SP - 2107 EP - 2118 PB - John Wiley & Sons, Inc. AN - OPUS4-43880 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kazlagic, Anera A1 - Vogl, Jochen A1 - Gluth, Gregor A1 - Stephan, D. T1 - Provenancing of cement using elemental analyses and isotope techniques – The state-of-the-art and future perspectives JF - Journal of analytical atomic spectrometry N2 - With the aim of identifying the origin and the manufacturer of a cement, a reliable procedure that provides unambiguous results is needed. Such procedure could resolve practical issues in damage research, liability issues and forensic investigations. A substantial number of attempts for fingerprinting of building materials, including cement, has already been carried out during the last decades. Most of them were based on concentration analysis of the main elements/components. This review provides an overview of provenance studies of cement and the main approaches commonly used. Provenance studies of cement via isotope techniques are also presented and discussed as representatives of the state-of-the-art in the field. Due to the characteristic properties and the occurrence of carefully selected isotope ratios, unique fingerprints of different kinds of materials can be provided by these methods. This property has largely been explored in various scientific fields such as geo- and cosmochemistry, food forensics, archaeology, geochronology, biomedical studies, and climate change processes. However, the potential of isotope techniques in cement and concrete research for provenance studies has barely been investigated. Therefore, the review outlines a suitable approach using isotope ratios, which could lead to reliable provenancing of cementitious materials in the future. KW - Cement KW - Sr isotopes KW - Provenance PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-533762 DO - https://doi.org/10.1039/d1ja00144b VL - 36 IS - 10 SP - 2030 EP - 2042 PB - The Royal Society of Chemistry CY - Cambridge, UK AN - OPUS4-53376 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kazlagic, Anera A1 - Russo, Francesco A1 - Vogl, Jochen A1 - Sturm, Patrick A1 - Stephan, D. A1 - Gluth, Gregor ED - Resch-Genger, Ute ED - Koch, Matthias ED - Meermann, Björn ED - Weller, Michael G. T1 - Development of a sample preparation procedure for Sr isotope analysis of Portland cements JF - Analytical and bioanalytical chemistry N2 - The 87Sr/86Sr isotope ratio can, in principle, be used for provenancing of cement. However, while commercial cements consist of multiple components, no detailed investigation into their individual 87Sr/86Sr isotope ratios or their influence on the integral 87Sr/86Sr isotope ratio of the resulting cement was conducted previously. Therefore, the present study aimed at determining and comparing the conventional 87Sr/86Sr isotope ratios of a diverse set of Portland cements and their corresponding Portland clinkers, the major component of these cements. Two approaches to remove the additives from the cements, i.e. to measure the conventional 87Sr/86Sr isotopic fingerprint of the clinker only, were tested, namely, treatment with a potassium hydroxide/sucrose solution and sieving on a 11-µm sieve. Dissolution in concentrated hydrochloric acid/nitric acid and in diluted nitric acid was employed to determine the 87Sr/86Sr isotope ratios of the cements and the individual clinkers. The aim was to find the most appropriate sample preparation procedure for cement provenancing, and the selection was realised by comparing the 87Sr/86Sr isotope ratios of differently treated cements with those of the corresponding clinkers. None of the methods to separate the clinkers from the cements proved to be satisfactory. However, it was found that the 87Sr/86Sr isotope ratios of clinker and cement generally corresponded, meaning that the latter can be used as a proxy for the clinker 87Sr/86Sr isotope ratio. Finally, the concentrated hydrochloric acid/nitric acid dissolution method was found to be the most suitable sample preparation method for the cements; it is thus recommended for 87Sr/86Sr isotope analyses for cement provenancing. KW - Cement KW - Provenancing KW - Sr isotopes KW - Portland clinker KW - Dissolution PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542239 DO - https://doi.org/10.1007/s00216-021-03821-7 SN - 1618-2642 SN - 1618-2650 VL - 414 IS - 15 (Topical collection: Analytical methods and applications in the materials and life sciences) SP - 4379 EP - 4389 PB - Springer CY - Berlin AN - OPUS4-54223 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, Shishir A1 - Samson, G. A1 - Masi, G. A1 - Achenbach, R. A1 - Bastidas, D. M. A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Criado, M. A1 - Cyr, M. A1 - Gartner, N. A1 - von Greve-Dierfeld, S. A1 - Legat, A. A1 - Nikoonasab, Ali A1 - Provis, J. L. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Stahlkorrosion in alkalisch aktivierten Bindemitteln und Betonen: Anwendung elektrochemischer Methoden JF - GIT Labor-Fachzeitschrift N2 - Alkalisch aktivierte Bindemittel (AAB) und Betone können herkömmliche Zemente beziehungsweise Betone potentiell in vielen Anwendungen ersetzen und dadurch den CO2-Fußabdruck der Bauindustrie wesentlich verkleinern. Zur Untersuchung der Stahlkorrosion in bewehrten („armierten“) Betonbauteilen werden elektrochemische Methoden wie Messungen des Freien Korrosionspotentials, des Polarisationswiderstands oder von Stromdichte-Potential-Kurven eingesetzt. Diese Methoden und die etablierten Grenzwerte zur Detektion von Korrosion sind für die Anwendung bei herkömmlichen Zementen beziehungsweise Betonen entwickelt und erprobt worden. Neue Forschungsergebnisse demonstrieren, dass Unterschiede zwischen den Porenlösungszusammensetzungen von herkömmlichen Zementen und bestimmten AAB sowie anderen schlackehaltigen Zementen erhebliche Unterschiede bei den Ergebnissen der elektrochemischen Messungen bewirken und damit zur fehlerhaften Detektion von Stahlkorrosion führen können. Ursache hierfür sind vor allem reduzierte Schwefelspezies in den Porenlösungen von AAB und anderen schlackehaltigen Zementen. KW - Zement KW - Hüttensandmehl KW - Schlacke KW - Sulfid KW - Korrosion PY - 2023 UR - https://bit.ly/GIT-Gluth UR - https://analyticalscience.wiley.com/content/magazine-do/git-labor-fachzeitschrift-10-2023 SN - 0016-3538 VL - 67 IS - 10 SP - 28 EP - 31 PB - Wiley-VCH AN - OPUS4-58573 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Matos, P. R. de A1 - Andrade Neto, J. S. A1 - Durlo Tambara, Luis Urbano A1 - Rodríguez, E. D. A1 - Kirchheim, A. P. A1 - Campos, C. E. M. de T1 - Measuring the early-age volumetric change of cement paste through in-situ XRD JF - Materials Today Communications N2 - Volumetric changes follow Portland cement hydration reactions: aluminates' hydration is generally expansive, whereas silicates' reaction leads to shrinkage. Determining the volumetric variation at very early ages (i.e., first minutes/hours) presents operational challenges; most standards prescribe the measurement on specimens that are already hardened, while measurements from the fresh state are not standardized. This article reports the first attempt to use in-situ X-ray diffraction (XRD) to measure the early-age volumetric variation of a cementitious paste. For this purpose, a C3A + gypsum paste was assessed for 36 h, measuring its vertical displacement over time through XRD. The results showed that the expansion increased in the first ∼13 h, in line with the ettringite formed up to ∼11 h. In addition, the volumetric expansion agreed well with the heat release in calorimetry. It is concluded that the volumetric variation measurement of cementitious pastes through in-situ XRD is a promising technique, but further studies are needed to make this technique consolidated. KW - X-ray diffraction KW - Shrinkage KW - Expansion KW - Hydration KW - Portland cement PY - 2023 DO - https://doi.org/10.1016/j.mtcomm.2023.106857 SN - 2352-4928 VL - 36 SP - 1 EP - 4 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-58107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Tchetgnia Ngassam, Ines Leana A1 - Olonade, K. A. A1 - Mbugua, R. A1 - Kühne, Hans-Carsten T1 - Plant based chemical admixtures – potentials and effects on the performance of cementitious materials JF - RILEM Technical Letters N2 - While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio‐based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil‐based. The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfet ta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly. KW - Polysaccharides KW - Rheology KW - Cement KW - Chemical admixtures KW - Bio-based concrete PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-476748 DO - https://doi.org/10.21809/rilemtechlett.2018.83 VL - 3 SP - 124 EP - 128 PB - RILEM S.A.R.L. CY - Paris AN - OPUS4-47674 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lu, Z. A1 - Haist, M. A1 - Ivanov, D. A1 - Jakob, C. A1 - Jansen, D. A1 - Leinitz, Sarah A1 - Link, J. A1 - Mechtcherine, V. A1 - Neubauer, J. A1 - Plank, J. A1 - Schmidt, Wolfram A1 - Schilde, C. A1 - Schröfl, C. A1 - Sowoidnich, T. A1 - Stephan, D. T1 - Characterization data of reference cement CEM I 42.5 R used for Priority Program DFG SPP 2005 “Opus Fluidum Futurum - Rheology of reactive, multiscale, multiphase construction materials” JF - Data in Brief N2 - A thorough characterization of starting materials is the precondition for further research, especially for cement, which contains various phases and presents quite a complex material for fundamental scientific investigation. In the paper at hand, the characterization data of the reference cement CEM I 42.5 R used within the priority program 2005 of the German Research Foundation (DFG SPP 2005) are presented from the aspects of chemical and mineralogical compositions as well as physical and chemical properties. The data were collected based on tests conducted by nine research groups involved in this cooperative program. For all data received, the mean values and the corresponding errors were calculated. The results shall be used for the ongoing research within the priority program. KW - Portland cement KW - Characterization KW - DFG SPP 2005 PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-500849 DO - https://doi.org/10.1016/j.dib.2019.104699 SN - 2352-3409 VL - 27 SP - 104699 PB - Elsevier Inc. AN - OPUS4-50084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kruschwitz, Sabine A1 - Munsch, Sarah A1 - Telong, Melissa A1 - Schmidt, Wolfram A1 - Bintz, Thilo A1 - Fladt, Matthias A1 - Stelzner, Ludwig T1 - The NMR core analyzing TOMograph: A multi-functional tool for non-destructive testing of building materials JF - Magnetic Resonance Letters N2 - NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s). KW - Fire spalling KW - Moisture transport KW - Concrete KW - Cement hydration KW - Sensitivity KW - Supplementary cementitous materials KW - Frost salt attack PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573755 DO - https://doi.org/10.1016/j.mrl.2023.03.004 SN - 2097-0048 VL - 3 IS - 3 SP - 207 EP - 219 PB - Elsevier B.V. AN - OPUS4-57375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Mota, Berta A1 - Ramirez Caro, Alejandra T1 - The action of aggregates on concrete rheology JF - CPI - Concrete Plant International N2 - Most factors acting on concrete rheology work at an extremely small-scale level. Influencing factors in the millimetre or centimetre area are essentially restricted to sand and aggregates. The latter, however, make up 50 to 70% of the total volume of most concretes – a fact often ignored in research on controlling concrete processing properties. Whereas suitably chosen concrete admixtures and additives can influence rheology in a very targeted manner, sand and aggregates are less suitable for controlling rheology but nonetheless contribute to the rheology of the Overall system. The actions of sand and aggregate can impose themselves upon the actions of admixtures and additives and, in unfavourable circumstances, even render them redundant. For this reason, any results concerning the processability of binding agent systems can only be transferred to concrete with great care. It is important to better understand the action of sand and aggregates in order to be able to harmonise them in such a way that they complement the action of superplasticisers positively, instead of working against them. Savings on costs can also be made by this targeted fine-tuning. KW - Rheology KW - Aggregates KW - Viscosity KW - Yield stress KW - Concrete PY - 2018 VL - 3 SP - 42 EP - 49 PB - ad-media GmbH CY - Cologne AN - OPUS4-47045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Wolfram A1 - Mota, Berta A1 - Ramirez Caro, Alejandra T1 - Einfluss der gesteinskörnung auf die Rheologie von Beton JF - BWI - BetonWerk International N2 - Die meisten Einflüsse auf die Rheologie von Beton wirken auf sehr kleinen Skalenebenen. Einflussgrößen im Millimeter oder Zentimeterbereich sind im Wesentlichen auf den Sand und die Gesteinskörnung beschränkt. Letztere machen aber in den meisten Betonen 50 %-70 % des Gesamtvolumens aus, was bei Untersuchungen zur Steuerung der Verarbeitungseigenschaften von Beton häufig vernachlässigt wird. Während Betonzusatzmittel und Zusatzstoffe bei geeigneter Wahl die Rheologie sehr gezielt beeinflussen können, eignen sich Sand und Gesteinskörnung weniger gut zur Steuerung der Rheologie, aber sie tragen zur Rheologie des Gesamtsystems bei. Hierbei können Effekte aus Sand und Gesteinskörnung die Effekte von Zusatzmitteln und Zusatzstoffen überlagern und im ungünstigsten Falle sogar nahezu unwirksam machen. Deshalb sollten Ergebnisse zur Verarbeitbarkeit von Bindemittelsystemen nur mit großer Sorgfalt auf Beton übertragen werden. Es ist wichtig, den Einfluss des Sandes und der Gesteinskörnung besser zu verstehen, um diese so abzustimmen, dass sie Effekte aus Fließmitteln positiv ergänzen anstatt diesen entgegenzuwirken. Durch eine gezielte Abstimmung lassen sich Kosten wirksam sparen. KW - Gesteinskörnung KW - Rheologie KW - Fließgrenze KW - Viskosität KW - Beton PY - 2018 VL - 3 SP - 42 EP - 51 PB - ad-media GmbH CY - Köln AN - OPUS4-47044 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -