TY - CONF A1 - Wu, Shu-Han A1 - Appel, Paul Alexander T1 - DialySorb N2 - Lithium-ion batteries (LIBs) have been one of the greatest achievements in the field of energy storage of the last century. However, with the increasing demand for energy storage, battery technologies must be diversified according to their specific requirements in different applications. In terms of stationary energy storage and electric vehicles, sodium-ion batteries (SIBs) are considered to be the most attractive alternative to LIBs due to the uniformly high abundance and cost-effectiveness of raw materials, enabling large-scale and low-cost energy storage. Unlike LIBs where crystalline graphite is commonly used as the anode material, disordered carbons are regarded as more promising for SIBs. However, further advances towards better reversibility and higher specific capacity are still needed to match or exceed that of graphite in LIBs. The main challenge is the complex and unpredictable Na+ storage mechanism in disordered carbons, as they may have different properties depending on the precursors and carbonization conditions. [1] Recently, Matsukawa et al. have reported that the reversibility of (de)sodiation processes of disordered carbons is better for ultramicroporous carbons.[2] These pores are accessible only to Na+ ions and not to solvent molecules. Therefore, the (de)sodiation processes are protected from the side reactions caused by the solvent, which reduces the related irreversible capacity loss. With this idea, the origin of the specific capacity and irreversible losses will be further investigated by tailoring chemical composition (e.g., heteroatom doping) as well as pore structure of hard carbons used as anode materials in SIBs. For the synthesis scalable and industrially relevant processes will be used. The structure and morphology of the materials will be characterized by electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and Raman spectroscopy. In addition, different gas sorption techniques will be carried out to analyze the porosity, pore sizes and specific surface areas. The electrochemical performance of the prepared materials will be evaluated based on coin cells, three-electrode Swagelok cells, and pouch cells. Moreover, solid-state nuclear magnetic resonance spectroscopy will be performed to help understand the mechanism of Na+ storage. T2 - Electrochemistry 2022 (GDCh confernece) CY - Berlin, Germany DA - 27.09.2022 KW - Na-ion Battery PY - 2022 AN - OPUS4-62013 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Metal chloride activation revisited: a sol-gel process to functional carbons N2 - Porous carbon materials are known for their applicability in important areas such as sorption, catalysis and electrochemistry (e.g. fuel cell catalysts, supercapacitor or battery electrodes). It was shown that nitrogen doped carbons (NDCs) act as an inexpensive and highly active non-metal catalyst in the oxygen reduction reaction (ORR), with the potential to reach performances of practical need one day. A key strategy towards improvement for this aim comprises the generation of advantageous porosity, which typically means high surface area and mass transport pores as well as the control over the chemistry of catalytically active sites. My group is developing novel sol-gel type strategies that are using molten salts or molten acids as unconventional reaction medium for the porogenesis in doped carbons, thereby revisiting classic activation techniques.[1,2] Carbon materials with extra high surface area of ~2800 m2 g-1 and pore volumes, up to four times as high as in commercial activated carbons, are obtained.[3] It turns out that the meso- and macrostructure is generated by means of phase separation rather than leaching reactions. However, chemical reactions between the carbon precursor and the melt are also involved. The salt cations Mg2+ and Zn2+ act as template ions, which results in metal coordination sites, embedded into the carbon structure.[4,5] The imprinted structure may be utilized as catalytically active site by performing ion-exchange reactions. The novel preparation strategy towards highly active electrocatalysts will be presented for Mg and Zn and further discussed for lighter elements. T2 - Carbon Chemistry and Materials Conference 2022 CY - Rome, Italy DA - 10.10.2024 KW - Activated carbon KW - Salt templating PY - 2022 AN - OPUS4-61936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - On the structure of doped carbon electrodes N2 - Carbon-based materials are promising electrodes for energy applications. Herein an overview of morphological and chemical features of such carbon materials is given. It is further shown how morphological and chemical features must be devonvoluted to be able to elucidate structure-performance realtionships that are critical to the improvement of the materials for applications such as batteries or fuel cells. T2 - TEC Summer Seminar 2022 CY - Monte Isola, Italy DA - 06.09.2022 KW - Carbon KW - M-N-C KW - Electrocatalysis KW - Energy storage PY - 2022 AN - OPUS4-61935 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Sol-gel synthesis of porous boron- and nitrogen-doped carbon N2 - Carbon activation is intensively investigated due to a widespread utilization of activated carbons as sorbents, hosting and support materials owning to its high porosity and surface area. Activated carbons are increasingly considered also for electrochemical applications e.g. supercapacitors and metal-ion hybrid capacitors. Those devices usually employ activated carbon electrodes, where ions are stored by means of adsorption/desorption.[1] Meanwhile, in lithium-sulfur batteries, sulfur is loaded within activated carbon pores to confine insoluble intermediates.[2] The activation is normally proceeded in top-down or bottom-up strategies. Therein pore formation (porogenesis) occurs by reaction with steam, CO2, KOH, or the use of acidic agents. It is generally accepted, that the porogenesis mechanism is chemical leaching of carbon atoms. Recently, the sol-gel type synthesis of nitrogen-doped carbon in molten acids was presented, questioning the general validity of a leaching activation mechanism.[3] The protocol using inorganic salt melts (MgCl2 or ZnCl2) and organic precursors additionally generated N-functionalities. Interestingly, it can be noticed that the imprinting cations play a crucial role towards chemical structure of nitrogen-doped carbon framework. The coordinated geometry is well-known from phthalocyanine, a macrocyclic N-complexes (MN4-sites, where M is metal cation) which are desirable surface complexes, e.g. in electrocatalysis. The analogous phenomenon may be observed when using H3PO4 and H3BO3 agent via sol-gel chemistry.[4] Herein, the carbonization of mixtures of organic compound with H3PO4 and H3BO3 is investigated. Therefore, associated effects regarding the presence of P and B atoms within resulting nitrogen-doped carbons as well as the porogenesis mechanism are discussed. The understanding of moieties probably offers a new perspective of non-leaching carbon activation hence, provides a feasible pathway towards improved performances in electrochemical applications. T2 - Deutsche Zeolith-Tagung 2022 CY - Frankfurt am Main, Germany DA - 24.03.2022 KW - B-N-C KW - Boric acid activation PY - 2022 AN - OPUS4-61957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Porous Carbon Supported Ni or Co Single Atom Catalysts for Electrochemical Reduction of CO2 N2 - Isomorphous, but chemically unequal Ni-, Co- and Zn-N-C electrocatalysts are investigated for their electrocatalytic properties towards the electrochemical CO2 conversion. It turns out that Ni-N-Cs are clearly most favourable, because of the isomorphism to other catalysts, also clearly due to the NiN4 sites properties. T2 - Deutsche Zeolith-Tagung 2024 CY - Frankfurt am Main, Germany DA - 23.03.2024 KW - M-N-C catalysts KW - CO2 reduction PY - 2022 AN - OPUS4-61953 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehmood, Asad T1 - Atomically Coordinated Non-Precious Metal Electrocatalysts Using Active Site Imprinted Carbon Matrix N2 - Non-precious metal catalysts generally represented as M-N-C (where M= Fe, Co, Ni etc.) have shown encouraging activity levels for different electrochemical applications involving oxygen reduction reaction (ORR) and carbon dioxide reduction reaction (CO2RR). High activities of these electrocatalysts mainly come from transition metal centres that are atomically dispersed as M-N4 active sites within a nitrogen doped carbon matrix. Because of the required pyrolytic synthesis conditions, it is quite challenging to prepare M-N-Cs that purely consist of M-N4 active sites. Classical synthesis routes often result in the formation of additional side phases such metallic nanoparticles or metal carbides, which limit the density of M-N4 sites and lead to lower catalytic activity.1 Herein, we present our work on M-N-C synthesis using an active site imprinting approach as an alternate synthetic route to address the above-mentioned issue. We show that both Mg and Zn can be used for active site imprinting. The imprinted coordination environment can be coordinated with various transition metal ions, resulting in Fe-N-C, Co-N-C and Ni-N-C catalysts containing M-N4 sites exclusively.2-4 The electrochemical performance of the synthesized catalysts is evaluated for CO2RR and ORR. Ni-N-Cs exhibit an excellent CO2 reduction activity with high CO faradic efficiency value of 95% at U= -0.5 to -0.8 VRHE (vs reversible hydrogen electrode) and a mass activity of 23 A g-1. The performance stability test carried out at -0.65 VRHE demonstrates above 92 % retention of the current density and 97 % retention of the CO selectivity after 100 h of continuous operation, reflecting the structural robustness of the Ni-N-C catalyst in CO2RR test environment. When employed as ORR catalysts, both Fe-N-C and Co-N-C deliver promising activities with half-wave potentials >0.8 VRHE in acidic electrolyte and >0.9 VRHE in alkaline electrolyte. The talk will include greater details of the structural analysis and electrochemical performance evaluation of these catalysts. T2 - 73rd Annual Meeting of the International Society of Electrochemistry CY - Online meeting DA - 12.09.2022 KW - Non-precious metal catalysts KW - Single atom catalysts KW - Electrochemical CO2 conversion PY - 2022 AN - OPUS4-61986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehmood, Asad T1 - Ionothermal Template Transformation as a Sustainable Route Towards Carbon Electrodes in Energy Storage and Conversion N2 - Porous carbons with tuneable functionalities and morphologies have extensively been employed as electrode materials in a variety of electrochemical energy conversion and storage systems for instance in fuel cells and electrolysers as active catalysts and catalyst supports, and in secondary batteries as anode materials. Amorphous carbons with well-developed pore structures are of particular interest due to their superior mass-transport characteristics and remarkable charge storage capacities. The salt-templating method with its advantage of combined soft and hard templating effects provides a sustainable way to synthesize nano- and mesoporous carbons with tailored porosities via in-situ ionothermal template transformation [1]. In this work, we utilized a MgCl2-based salt melt to prepare nitrogen doped carbons (N-C) with different morphologies and porosities, which were evaluated as anode materials in sodium ion batteries. Simultaneously, use of MgCl2 salt leads to the formation of Mg-N4 moieties in those carbons by means of a pyrolytic template-ion effect (active site imprinting) [2]. Porous carbon frameworks with imprinted Mg-N4 sites are interesting particularly for electrocatalysis applications as they offer an ideal platform to prepare M-N-C catalysts (where M= Co, Fe, Ni etc.) by ion-exchange reactions at low temperatures. The resultant M-N-C catalysts consist purely of M-N4 active sites and high porosity of carbon framework facilitates efficient mass-transport of reacting species. We utilized Mg-N4 imprinted carbons to synthesize morphologically equivalent Ni-N-Cs and Co-N-Cs, containing phase pure Ni-N4 and Co-N4 sites, for electrochemical reduction of carbon dioxide (CO2RR). In electrochemical tests, Ni-N-Cs exhibited an excellent CO2 reduction activity with considerably higher CO selectivity and mass activity as compared to Co-N-C. The faradic efficiency value of Ni-N-C for CO formation was 95% at U= -0.5 to -0.8 VRHE (vs reversible hydrogen electrode) and a mass activity of 23 A g-1. The performance stability test carried out at -0.65 VRHE demonstrated above 90 % retention of the current density and CO selectivity after 100 h of continuous operation, reflecting the structural robustness of the Ni-N-C catalyst. Finally, these ionothermal carbons with two different morphologies (but without any Ni or Co incorporation) were employed as the anode materials in sodium-ion batteries to evaluate the effects of carbon morphology and functionalization on sodium storage capacities. Compared to the reference carbon material, substantially higher reversible sodium storage capacities were reached with these high porosity carbons that were in the range of 300-500 mAh g-1 [3]. Although the reversible capacity was obtained only after extensive SEI formation, our results reveal the potential for much higher reversible capacities than usually observed using carbons with a tailored porosity in sodium-ion batteries. The talk will include greater details of the structural analysis and sodium storage and CO2 reduction results of these ionothermal carbons. T2 - Materials for Sustainable Development Conference (MAT-SUS) CY - Barcelona, Spain DA - 24.10.2022 KW - Porous carbons KW - Sodium ion batteries KW - Anode materials KW - Single atom catalysts KW - Electrochemical CO2 reduction PY - 2022 AN - OPUS4-61985 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Bioinspired atomically dispersed M-N-C catalysts via active-site imprinting into nitrogen doped carbons N2 - Proton-exchange membrane fuel cells are amongst the most promising energy conversion technologies today. Herein non-precious iron-coordinated nitrogen doped carbons (Fe-N-Cs) are very promising alternatives for Pt-based cathode catalysts.[1-3] The early reports on the application of such materials date back to the 1960´s when Jasinski demonstrated that - similar to natural porphyrins - N-coordinated transition metal complexes can be active sites for the ORR.[3] The preparation of these catalysts was strongly optimized over the years; still they typically remain with harsh reaction conditions that complicate the selective formation of active FeN4 sites. The employment of pyrolytic temperatures has been a dogma for the synthesis of MN4 sites, however coming with unfavorable side reactions. We recently introduced a mild procedure, which is conservative toward the carbon support and leads to active-site formation at low temperatures in a wet-chemical step, essentially decoupling the preparation of nitrogen doped carbons (NCs) from the preparation of the active sites.[4, 5] The key concept therein is the so-called active site imprinting into the NC using the less reactive template ions Mg2+ [4] or Zn2+.[5] The presentation will introduce the concept of active site imprinting with a focus on Fe-N-C electrocatalyst development and testing. The broad potential of the synthetic approach will be exemplified by recent results, including the selective synthesis of tetrapyrrolic single site catalysts, the assignment of the role of the transition metal compared to the carbon scaffold and a facile method to evaluate specific activity. T2 - GDCh Electrochemistry 2022 CY - Berlin, Germany DA - 27.09.2022 KW - Bioinspired carbon catalysts PY - 2022 AN - OPUS4-61960 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fellinger, Tim-Patrick T1 - Effects of Acid Activation via Sol-Gel Chemistry towards Nitrogen-Doped Carbon Structure N2 - Porous carbon materials are known for their applicability in important areas such as sorption, catalysis and electrochemistry (e.g. fuel cell catalysts, supercapacitor or battery electrodes). It was shown that nitrogen doped carbons (NDCs) act as an inexpensive and highly active non-metal catalyst in the oxygen reduction reaction (ORR), with the potential to reach performances of practical need one day. A key strategy towards improvement for this aim comprises the generation of advantageous porosity, which typically means high surface area and mass transport pores as well as the control over the chemistry of catalytically active sites. My group is developing novel sol-gel type strategies that are using molten salts or molten acids as unconventional reaction medium for the porogenesis in doped carbons, thereby revisiting classic activation techniques.[1,2] Carbon materials with extra high surface area of ~2800 m2 g- 1 and pore volumes, up to four times as high as in commercial activated carbons, are obtained.[3] It turns out that the meso- and macrostructure is generated by means of phase separation rather than leaching reactions. However, chemical reactions between the carbon precursor and the melt are also involved. The salt cations Mg2+ and Zn2+ act as template ions, which results in metal coordination sites, embedded into the carbon structure.[4,5] The imprinted structure may be utilized as catalytically active site by performing ion-exchange reactions. The novel preparation strategy towards highly active electrocatalysts will be presented for Mg and Zn and further discussed for lighter elements. T2 - International Sol-Gel Conference 2022 CY - Lyon, France DA - 24.06.2022 KW - Sol-Gel-Carbonization KW - Boron-Nitrogen-Doped Carbon PY - 2022 AN - OPUS4-61958 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wutthiprom, Juthaporn T1 - Sol-Gel Carbonization towards Tailor-Made Boron- and Nitrogen-doped Carbon N2 - The activation of carbon is normally proceeded in top-down or bottom-up strategies. Therein pore formation (porogenesis) occurs by reaction with steam, CO2 , KOH, or the use of acidic agents, in which chemical leaching of carbon atoms occurs. The sol-gel type synthesis of N-doped carbon in excess amounts of molten acids was presented recently, questioning the general validity of a leaching activation mechanism.[1] The protocol using inorganic salt melts (MgCl2 or ZnCl2 ) and organic precursors additionally generated N functionalities. Interestingly, it can be noticed that the imprinting cations play a crucial role towards the chemical structure of N-doped carbon framework. The coordinated geometry is wellknown from phthalocyanine, a macrocyclic Ncomplexes (MN4 -sites, where M is metal cation) which are desirable surface complexes, e.g. in electrocatalysis. The analogous phenomenon may be observed when using H3BO3 agent via sol-gel chemistry. T2 - International Sol-Gel Conference 2022 CY - Lyon, France DA - 24.06.2022 KW - Boron-Nitrogen-Doped-Carbon KW - Sol-Gel-Carbonization PY - 2022 AN - OPUS4-61959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mehmood, Asad A1 - Fellinger, Tim-Patrick T1 - Porous Carbon Supported Ni and Co Single Atom Catalysts for Electrochemical Reduction of Carbon Dioxide N2 - Non-precious metal single atom catalysts (generally labelled as M/NCs where M= Co, Fe, Ni etc.) consist of active metal centres dispersed on nitrogen doped porous carbon (NC) matrix at atomic level and exhibit promising activities e. g. for electrochemical reduction of CO2, selectively forming CO. We herein use identical Mg/NCs as platform for ion-exchange reactions towards morphologically equivalent Ni/NCs and Co/NCs. The Ni/NC catalyst shows almost double the specific activity and a Faraday efficiency of >80% at a very low overpotential of U= -0.43 V (even 95% at U= -0.5 to -0.8 V) with high stability. T2 - GDCh Electrochemistry 2022 CY - Berlin, Germany DA - 27.09.2022 KW - Electrochemical CO2 conversion KW - Single atom catalysts KW - Porous Carbons PY - 2022 AN - OPUS4-61980 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietzmann, Simon T1 - Synthesis of Atomically Dispersed Electrocatalyst by Imprinting with Different Template Ions throughout Carbonization N2 - Atomically dispersed metal-nitrogen doped carbons (M-N-C) are promising catalysts for the activation of small molecules such as O2 and CO2. These single atom catalysts (SAC) operate at the interface between homogenous and heterogenous catalysts. Currently, many examples of M-N-C are known with good oxygen reduction reaction activity but lacking a controlled synthesis of the specific active sites of the precatalyst. T2 - GDCh Electrochemistry 2022 CY - Berlin, Germany DA - 27.09.2022 KW - Elechtrochemistry KW - Oxygen reduction reaction KW - Porous carbons PY - 2022 AN - OPUS4-61982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Appel, Paul Alexander T1 - Investigation and Development of Tailor-Made Core-Shell Hard Carbon Materials to be used as Negative Electrodes in Sodium Ion Batteries N2 - The current strong interest in electromotive mobility and the need to transition to an energy grid with sustainable energy storage has led to a renewed interest in sodium ion batteries (SIBs). Hard carbons are promising candidates for high-capacity negative electrode materials in SIBs. Their high capacities, however, are often accompanied with high irreversible capacity losses during the initial cycles.[1] The goal of this project is to use analytical techniques to establish a correlation between the structure and the capacities of hard carbons. This has previously been difficult, in part because the sodium storage mechanism is not stoichiometric and due to the disordered structure of hard carbons. Large irreversible capacities associated with hard carbons are often in contradiction to the experimentally determined low surface area of the sample material.[1] A better understanding of the structure-property relationship should enable quantification and understanding of the potential of hard carbon materials for SIBs. Our approach is to explore whether a core-shell structure can separate sodium storage and solid electrolyte interphase formation so that storage capacity and irreversible losses can be investigated separately. The synthesis of a selection of porous carbon structures serving as the core material, will be attempted. Simultaneously, sodium-conducting shell structures will be developed to allow for separation of sodium ions and electrolyte molecules. Subsequently the combination of core and shell materials will be undertaken. These anodes should enable high capacities accompanied with low irreversible capacity due to optimized solid electrolyte interphase formation. T2 - GDCH Electrochemistry 2022 CY - Berlin, Germany DA - 27.09.2022 KW - Energy Materials PY - 2022 AN - OPUS4-62001 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietzmann, Simon T1 - Between Homogenous and Heterogenous Catalysis: Single-Atom-Catalysts N2 - Catalysis is a very important process in chemistry as it lowers the energy barrier for chemical reactions. This saves energy and/or some reactions are only possible with a catalyst under the desired conditions (temperature and pressure). Catalysts can be roughly categorized depending on the phase they interact with the substrates in homogenous and heterogenous catalysis. T2 - 5. Deutsche Tagung für Forschung mit Synchrotronstrahlung, Neutronen und Ionenstrahlen an Großgeräten (SNI2022) CY - Berlin, Germany DA - 05.09.2022 KW - Single-atom-catalyst KW - Electrochemistry KW - Porous carbons PY - 2022 AN - OPUS4-61989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietzmann, Simon T1 - Between Homogenous and Heterogenous Catalysis: Single-Atom-Catalysts N2 - Catalysis is a very important process in chemistry as it lowers the energy barrier for chemical reactions. This saves energy and/or some reactions are only possible with a catalyst under the desired conditions (temperature and pressure). Catalysts can be roughly categorized depending on the phase they interact with the substrates in heterougenous and heterogenous catalyst T2 - RÅC international summer school CY - Varberg, Sweden DA - 14.08.2022 KW - Single-atom-catalyst KW - Electrochemistry KW - Porous carbons PY - 2022 AN - OPUS4-61983 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietzmann, Simon T1 - XAS for structural characterization of atomically dispersed materials N2 - metal and nitrogen enriched carbons (M-N-C) are promising electrocatalysts for small molecule activation. It is proposed that the nitrogen is forming a stabilizing N4-site for the catalytically active metal. This can be proven by XAS measurements to confirm the coordination sphere around the metal. T2 - Bessy User Meeting CY - Online meeting DA - 08.12.2024 KW - Single-atom-catalyst KW - Structural characterization KW - Porous carbons PY - 2022 AN - OPUS4-61994 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -