TY - CONF A1 - Topolniak, Ievgeniia T1 - Direct laser writing of mussel inspired polydopamine N2 - Polydopamine (PDA) is one of the simplest and most versatile approaches for forming an excellent binding exterior to confer new functionalities to nearly any material surface. Inspired by nature, it mimics the behavior of mussels and can be easily deposited on virtually all types of inorganic and organic substrates, including superhydrophobic surfaces. Moreover, PDA exhibits high potential for surface modification and diversified secondary reactions that makes it extremely interesting for a wide range of application including biomedical field, e.g., drug delivery, adhesives, cell adhesion, biosensing. PDA has undergone significant expansion in its applications and is one of the most attractive areas within the materials field. Nevertheless, PDA integration in microdevices is still constrained by poor spatial and temporal control of excited deposition methods. Herein, we demonstrate a novel maskless approach for PDA micropatterning based on Direct Laser Writing that overcomes present limitations. The pattern is formed upon exposure of the dopamine solution by light produced by tightly-focused fs NIR laser that scans substrate surface accordingly to the selected pattern design. Neither strong oxidants, metal ions nor adjusting pH to alkaline is required by this technique to perform dopamine polymerization. Our method achieves the PDA micropatterns with the spatial resolution of 0.8 µm, at least an order of magnitude smaller than what is possible with other PDA microplanning techniques. Some examples of PDA patterns are shown in Figure 1. The here introduced PDA deposition technique will uniquely unravel applications of polydopamine and other catecholamine-based mussel-inspired materials in various multifunctional systems and microdevices (e.g., MEMS elements, microfluidics). The chemical nature of PDA was confirmed by locally recorded vibrational and x-ray photoelectron spectra. Moreover, the morphology and thickness of PDA microstructure can be controlled by the laser power and scanning velocity revealing the possibility of fabricating the structures with gradient. In most of the applied conditions the increase of the laser intensity and decrease of the scanning velocity would lead to the thicker PDA pattern. Different morphologies from smooth and bulky-like to grain like has been obtained. PDA was produced in the presence of tris buffer, phosphate buffer and DI water only. We also tested the effect of the solution pH applying pH 6.0, 7.0 and 8.5. Furthermore, the effect of antioxidants and purging of the solution with oxygen and nitrogen was investigated. Summarizing, we could see that the structures could be produced in all the given conditions, however their thickness and quality, morphology and roughness would differ. We did not observe negative impact of the antioxidants and nitrogen purging on the performance of PDA build up indicating that the PDA formation mechanism is different to common autooxidation. The current mechanism is based on the interaction of dopamine molecules with the photoinitiator added to solution as active to DLW laser light component. Apart from the glass substrate, we achieved PDA patterning at surfaces of different nature such as polychlorotrifluoroethylene, polydimethylsiloxane, polyethylene terephthalate, silicon wafers, and fluorinated glass coverslips. We also performed facile posts-modification of the PDA surface with protein enzymes like trypsin that was confirmed by XPS. Obtained bioactive pattern could be further integrated in the protein sensing devices. Presented in this work DLW-based microfabrication technique and the possibilities for further PDA surface post-functionalization empowers advanced applications of this material in single-molecule bioassays, sensors and other complex microdevices. T2 - MNE EUROSENSORS CY - Leuven, Belgium DA - 19.09.2022 KW - Polydopamine KW - Two-photon polymerisation KW - Micropatterning PY - 2022 AN - OPUS4-56421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fritzsche, Sven A1 - Weimann, Christiane A1 - Pauw, Brian Richard A1 - Sturm, Heinz T1 - 2PP-TestArtifact N2 - This repository contains a test artifact (TA), also called test structure, designed for two-photon polymerization (also known as Direct Laser Writing (DLW) or Two/Multi-photon lithography (2PA/MPA)). Test artifacts can be used to compare structures, to check options used by the slicer, check the state of the 2PP machine itself or to get a construction guidelines for a certain combination of power, velocity and settings. The associated paper can be found here: https://dx.doi.org/10.1088/1361-6501/acc47a General ideas behind the test artifact: 1. optimized for 2PP-DLW 2. should be fast and easy to analyse with optical microscopy or 3. scanning electron microscopy without tilt. 3. short time to fabricate 4. include a reasonable amount of different features 5. bulk and small structures on the substrate KW - Reference structure KW - Calibration structure KW - Test structure KW - Laser writing KW - Two-photon polymerization KW - 3D printing KW - Additive manufacturing KW - Microprinting KW - Multi-photon light structuring PY - 2023 DO - https://doi.org/10.6084/m9.figshare.22285204.v2 PB - Digital Science CY - Cambridge, MA, USA AN - OPUS4-57165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Zocca, Andrea T1 - Continuous layer deposition for the Additive Manufacturing of ceramics by Layerwise Slurry Deposition N2 - Powder bed technologies are amongst the most successful Additive Manufacturing (AM) techniques. The application of these techniques to most ceramics has been difficult so far, because of the challenges related to the deposition of homogeneous powder layers when using fine powders. In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method enabling the use of powder bed AM technologies also for advanced ceramic materials. The layerwise slurry deposition consists of the layer-by-layer deposition of a ceramic slurry by means of a doctor blade, in which the slurry is deposited and dried to achieve a highly packed powder. Not only very fine, submicron powders can be processed with low organics, but also the dense powder bed provides excellent support to the parts built. The latest development of this technology shows that it is possible to print ceramic parts in a continuous process by depositing a layer onto a rotating platform, growing a powder bed following a spiral motion. The unique mechanical stability of the layers in LSD-print allows to grow a powder bed several centimeters thick without any lateral support. The continuous layer deposition allows to achieve a productivity more than 10X higher compared to the linear deposition, approaching a build volume of 1 liter/hour. T2 - DKG Jahrestagung 2024 CY - Höhr-Grenzhausen, Germany DA - 09.09.2024 KW - Ceramic KW - Additive manufacturing PY - 2024 AN - OPUS4-61051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meyer, Lena T1 - How will we explore, work, and live on the moon? N2 - 3D-printed landing pads on the moon: Paving the road for large area sintering of lunar regolith. A prerequisite for lunar exploration and beyond is the manufacturing of objects directly on the moon, given the extreme costs involved in the shipping of material from Earth. Looking at processes, raw materials, and energy sources, equipment will certainly have to be brought from Earth at the beginning. Available on the moon are lunar regolith as raw material and the sun as an energy source. One of the first steps towards the establishment of a lunar base is the creation of infrastructure elements, such as roads and landing pads. We’ll introduce you to the ESA-project PAVER that demonstrates the sintering and melting of lunar regolith simulant material to produce large scale 3D printed elements that could be used during human and robotic lunar explorations. T2 - Berlin Science Week CY - Online meeting DA - 09.11.2022 KW - Additive manufacturing KW - Lunar regolith simulant KW - EAC-1A KW - Space exploration PY - 2022 UR - https://www.youtube.com/watch?v=StfLuVhKkUE AN - OPUS4-56377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Quosdorf, Heike T1 - Digital object identifier for additively manufactured parts based on 3D microstructural information N2 - Additive manufacturing (AM) is rapidly emerging from prototyping to industrial production [1]. Thus, providing AM parts with a tagging feature that allows unambiguous identification, can be crucial for logistics, certification, and anti-counterfeiting purposes. The digital object identifier (DOI) acts like a fingerprint for the product throughout its entire lifecycle. Several methods are already available, which range from encasing a detector [2] to leveraging the stochastic defects of AM parts [3], printing a quick response (QR) code or a set of voids partially filled with loose powder within the part [3]. A new method is using microstructural features of the AM part without altering their properties. This technology transfer project aims to implement this authentication methode as software solution to act as certificate in the Digital Product Passport (DPP) [5]. T2 - MaterialDigital General Assembly 2025 CY - Berlin, Germany DA - 26.11.2025 KW - Authentication KW - Unique identification KW - Open Science KW - Digital fingerprint KW - Material Digital KW - X-ray Computed Tomography KW - Additive manufacturing PY - 2025 AN - OPUS4-65208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bäßler, Ralph T1 - Review: Science, Technology and Applications of Metals in Additive Manufacturing N2 - Often 3D‐printing and additive manufacturing are mentioned as the 3rd industrial revolution. In this conjunction this book provides a brief overview on additively manufactured metal pieces. This book fulfills its intension to serve as an educational guide, providing a holistic picture encompassing science, technology and applications for the real‐life use of Metal Additive Manufacturing. KW - Additive manufacturing KW - Corrosion KW - Material properties PY - 2020 DO - https://doi.org/10.1002/maco.202070114 SN - 1521-4176 SN - 0947-5117 VL - 71 IS - 11 SP - 1929 EP - 1930 PB - WILEY‐VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-51514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller-Elmau, Johanna T1 - Transparent feedstocks for photon-based addiTve manufacturing technologies for powder processing of ceramics N2 - Photon-based additive manufacturing technologies such as SLA, DLP, LCM, moreover volumetric two-photon-polymerization, Xolography and holographic technologies promise the highest accuracy and dimensional freedom. But to transfer the light through the feedstock it needs sufficient transparency at the used light wavelength. Ceramic particles used for powder processing routes act as scattering sites and therefore hinder the light transmission, unless… The particle size and particle size distribution are chosen small and narrow enough. Particles which are smaller than roughly 1/10th of the light wavelength, mostly nanoparticles around 5nm size, decrease scattering vastly. This turns resins even with homogeneously distributed ceramic weight fraction of up to 80% transparent again. Feedstocks could be prepared for the highly accurate two-photon-polymerization gaining the smallest yttria stabilized zirconia structures with a resolution of 500nm and unique mechanical properties. The same feedstocks could be applied to DLP and LCM as layer-by-layer AM-technologies for bigger parts. Hybridizing both technologies lead to ceramic parts with microscopic accuracy at macroscopic dimensions. The feedstock was even applied to the volumetric Xolography with the highest transparency requirement so far and to versatile and flexible holographic AM. Highly filled nano-particle containing transparent ceramic feedstocks open the way for technical ceramics in high precision manufacturing where the performance and durability and accessibility are increased and created by the unique ceramic properties such as mechanical strength, chemical and thermal resistance and biocompatibility T2 - 2025 International Conference on Additive Manufacturing Technology Frontiers and Applications CY - Xi'an, China DA - 11.04.2025 KW - Tranparent KW - Ceramic KW - Additive manufacturing PY - 2025 AN - OPUS4-65069 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zocca, Andrea A1 - Wilbig, Janka A1 - Waske, Anja A1 - Günster, Jens A1 - Widjaja, Martinus Putra A1 - Neumann, C. A1 - Clozel, M. A1 - Meyer, A. A1 - Ding, J. A1 - Zhou, Z. A1 - Tian, X. T1 - Challenges in the Technology Development for Additive Manufacturing in Space N2 - Instead of foreseeing and preparing for all possible scenarios of machine failures, accidents, and other challenges arising in space missions, it appears logical to take advantage of the flexibility of additive manufacturing for “in-space manufacturing” (ISM). Manned missions into space rely on complicated equipment, and their safe operation is a great challenge. Bearing in mind the absolute distance for manned missions to the Moon and Mars, the supply of spare parts for the repair and replacement of lost equipment via shipment from Earth would require too much time. With the high flexibility in design and the ability to manufacture ready-to-use components directly from a computer-aided model, additive manufacturing technologies appear to be extremely attractive in this context. Moreover, appropriate technologies are required for the manufacture of building habitats for extended stays of astronauts on the Moon and Mars, as well as material/feedstock. The capacities for sending equipment and material into space are not only very limited and costly, but also raise concerns regarding environmental issues on Earth. Accordingly, not all materials can be sent from Earth, and strategies for the use of in-situ resources, i.e., in-situ resource utilization (ISRU), are being envisioned. For the manufacturing of both complex parts and equipment, as well as for large infrastructure, appropriate technologies for material processing in space need to be developed. KW - Additive manufacturing KW - Space KW - Process PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549204 DO - https://doi.org/10.1016/j.cjmeam.2022.100018 SN - 2772-6657 VL - 1 IS - 1 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-54920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zocca, Andrea T1 - Additive Manufacturing of advanced ceramics by layerwise slurry deposition and binder jetting (LSD-print) N2 - Powder bed technologies are amongst the most successful Additive Manufacturing (AM) techniques. Powder bed fusion and binder jetting especially are leading AM technologies for metals and polymers, thanks to their high productivity and scalability. The application of these techniques to most ceramics has been difficult so far, because of the challenges related to the deposition of homogeneous powder layers when using fine powders. In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method which enables the use of powder bed AM technologies also for advanced ceramic materials. The layerwise slurry deposition consists of the layer-by-layer deposition of a ceramic slurry by means of a doctor blade, in which the slurry is deposited and dried to achieve a highly packed powder layer. This offers high flexibility in the ceramic feedstock used, especially concerning material and particle size. The LSD technology can be combined with binder jetting to develop the so-called “LSDprint” process for the additive manufacturing of ceramics. The LSDprint technology combines the high-speed printing of binder jetting with the possibility of producing a variety of high-quality ceramics with properties comparable to those achieved by traditional processing. In this presentation, the LSD process will be introduced and several examples of application ranging from silicate to high-performance ceramics will be shown. Recent developments towards the scale-up and industrialization of this process will be discussed, alongside future perspectives for the multi-material additive manufacturing. T2 - Ceramics in Europe 2022 CY - Krakow, Poland DA - 10.07.2022 KW - Layerwise slurry deposition KW - Laser induced slipcasting KW - Additive Manufacturing KW - Ceramics PY - 2022 AN - OPUS4-55543 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Zocca, Andrea T1 - Dense Powder Beds for the Additive Manufacturing of Ceramics N2 - Regarding feedstocks for the additive manufacturing (AM) of ceramics, two features are most critical in classical powder based AM processes: a high particle packing density (typically >50% TD) must be achieved with very fine particles (typically submicron) in order to ensure sufficient sintering activity. Three innovative approaches will be introduced to overcome this problem: 1. Layer wise slurry deposition: The use of water based ceramic slurries as feedstock for the additive manufacture of ceramics has many advantages which are not fully exploit yet. In the layerwise slurry deposition (LSD) process a slurry with no or low organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle on the previously deposited and dried material to form thin layers with a high packing density (55-60%). The LSD therefore shares aspects both of tape casting and slip casting. The LSD differentiates from the classical powder-based AM layer deposition, which typically achieves with a flowable coarse grained powder a low packing density (35-50%) only, consequently hindering the ability of sintering ceramic parts to full density. The LSD is coupled with the principles of selective laser sintering (SLS) or binder jetting, to generate novel processes which take advantage of the possibility of achieving a highly dense powder-bed. 2. Laser induced slip casting: Contrary to the LSD process, which requires drying of each individual layer, the direct interaction of ceramic slurries with intense laser radiation, for the laser induced slip casting (LIS), is a promising approach for the additive manufacture of voluminous parts. 3. Gas flow assisted powder deposition: By the application of a vacuum pump a gas flow is realized throughout the powder bed. This gas flow stabilizes the powder bed and results into an enhanced flowability and packing density of the powder during layer deposition. The presentation will provide a detailed discussion of potentialities and issues connected to the mentioned technologies and will describe the most recent developments in their application to technical ceramics. T2 - SmatMade 2022 CY - Osaka, Japan DA - 25.10.2022 KW - Additive Manufacturing KW - Advanced ceramics PY - 2022 AN - OPUS4-59886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Topolniak, Ievgeniia T1 - Micropatterning of mussel-inspired materials - Empower selective functionality N2 - Surface-modification platforms that are universally applicable are vital for the development of new materials, surfaces, and nanoparticles. Mussel-inspired materials (MIMs) are widely used in various fields because of their strong adhesive properties and post-functionalization reactivity. However, conventional MIM coating techniques have limited deposition selectivity and lack structural control, which has limited their use in microdevices that require full control over deposition. To overcome these limitations, we developed a micropatterning technique for MIMs using multiphoton lithography, which does not require photomasks, stamps, or multistep procedures. This method enables the creation of MIM patterns with micrometer resolution and full design freedom and paves the way for innovative applications of MIMs in various multifunctional systems and microdevices, such as microsensors, MEMS, and microfluidics. T2 - BioCHIP Berlin - International Forum on Biochips and Microfabrication CY - Berlin, Germany DA - 28.05.2024 KW - Mussel inspired materials KW - Multiphoton lithography KW - Two photon polymerisation PY - 2024 AN - OPUS4-60254 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas T1 - Adaptive manufacturing strategies for DED-Arc: Case studies on high-strength aluminium alloys and gas-turbine blade repair N2 - In this presentation, we showcase BAM’s current research activities on DED-Arc/M processes, covering both the manufacture of novel high-strength aluminium alloys and the development of automated repair strategies for gas turbine blades, with a focus on robust process control and repeatable component quality. T2 - 12. Wissenschaftliches Kolloquium im Rahmen des SFB/TRR 375 "Multifunktionale Hochleistungskomponenten aus hybriden porösen Materialien" CY - Online meeting DA - 05.02.2026 KW - DED-Arc KW - Automation KW - Quality assessment PY - 2026 AN - OPUS4-65472 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Topolniak, Ievgeniia T1 - Direct laser surface micropatterning with polydopamine N2 - Inspired by the chemistry of mussel adhesive proteins, polydopamine (PDA) is one of the simplest and most versatile approaches to confer new functionalities to nearly any material surface. Moreover, PDA exhibits high potential for surface modification and diversified secondary reactions that makes it extremely interesting for a wide range of application including biomedical field, e.g., drug delivery, adhesives, cell adhesion, biosensing. PDA has undergone significant expansion in its applications and is one of the most attractive areas within the materials field. Nevertheless, PDA integration in microdevices is still constrained by poor spatial and temporal control of excited deposition methods. Herein, we demonstrate a novel maskless approach for PDA micropatterning based on Direct Laser Writing (DLW) that overcomes present limitations. The pattern is formed upon exposure of the dopamine solution by light produced by tightly-focused fs NIR laser that scans substrate surface accordingly to the selected pattern design. Neither strong oxidants, metal ions nor adjusting pH to alkaline is required by this technique. Our method achieves the PDA micropatterns with the spatial resolution of 0.8 µm, at least an order of magnitude smaller than what is possible with other PDA microplanning techniques. The here introduced PDA deposition technique will uniquely unravel applications of polydopamine and other catecholamine-based mussel-inspired materials in various multifunctional systems and microdevices (e.g., MEMS elements, microfluidics). Adjustment of MPL parameters revealed that the morphology and thickness of resulted PDA microstructures can be controlled by altering the laser power and its scanning velocity. As a result, it also enables the production of micropatterns with structural gradient. Apart from the glass substrate, we achieved PDA patterning at surfaces of different nature such as polychlorotrifluoroethylene, polydimethylsiloxane, polyethylene terephthalate, silicon wafers, and fluorinated glass coverslips. The chemical nature of PDA was confirmed by locally recorded vibrational and x-ray photoelectron spectra. To ensure post-modification potential of MPL deposited PDA we demonstrated one-step deposition of micropatterns with trypsin. Obtained bio-functionalised surface can be further applied as a protein sensing active microelement. Presented in this work DLW-based microfabrication technique and the possibilities for further PDA surface post-functionalization empowers advanced applications of this material in single-molecule bioassays, sensors and other complex microdevices. T2 - Swiss ePrint 2022 CY - Buchs, Switzerland DA - 05.09.2022 KW - Polydopamine KW - Two-photon polymerisation KW - Micropatterning PY - 2022 AN - OPUS4-56422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Silbernagl, Dorothee A1 - Szymoniak, Paulina A1 - Tavasolyzadeh, Zeynab A1 - Sturm, Heinz A1 - Topolniak, Ievgeniia T1 - Interpenetrating networks with tuned thermal and mechanical properties N2 - Text Multiphoton lithography (MPL) has recently attracted significant research interest as a versatile tool capable of producing 2D and 3D micro- and nanoscopic features with high spatial resolution. The integrity of MPL microstructures, or their ability to respond to external stimuli, is of critical importance. However, achieving the desired properties of fabricated microcomponents for a specific application remains a challenge. In this work, we present new MPL materials based on epoxy-acrylate interpenetrating networks (IPNs). We aim at 3D microstructures, whose properties can be easily tuned by varying the ratio of the IPN components and fabrication parameters (Figure 1). The resulting library of 3D microstructures was investigated for their thermal and mechanical properties using highly-sensitive space-resolved methods. Flash scanning calorimetry revealed the influence of both, IPN composition and fabrication parameters, on glass transition temperature and material fragility. AFM force-distance curve and intermodulation methods were used to characterize the mechanical properties with a lateral resolution of 1 micron and 4 nm, respectively. The deformation, stiffness and elastic behavior are discussed in detail in relation to the morphology. Moreover, we found that some 3D IPN microstructures exhibit fully elastic behavior. Our funding encourages the further development of IPN systems as versatile and easily tunable MPL materials. T2 - Micro Nano Engineering (MNE conference) CY - Berlin, Germany DA - 25.09.2023 KW - Interpenetrating polymer network KW - Multiphoton Lithography KW - Two photon polymerisation KW - Direct laser writing KW - Polyethylene glycol diacrylate PY - 2023 AN - OPUS4-58879 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fritzsche, Sven A1 - Pauw, Brian Richard A1 - Weimann, Christiane A1 - Sturm, Heinz T1 - Test artifact for fs-LDW N2 - Data to generate the given graphs in the publication as well as raw images of the shown images. KW - stl code KW - Images KW - Graphs KW - Data PY - 2023 DO - https://doi.org/10.5281/zenodo.7671945 PB - Zenodo CY - Geneva AN - OPUS4-58096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Topolniak, Ievgeniia A1 - Knigge, Xenia A1 - Radnik, Jörg A1 - Sturm, Heinz T1 - Maskless Micropatterning of Polydopamine for versatile surface functionalization N2 - Inspired by the chemistry of mussel adhesive proteins, polydopamine (PDA has been shown as one of the most versatile platforms for altering the properties and incorporating new functionalities to nearby any material surface despite its nature. Rich chemistry of PDA enables broad variety of surface modification and diverse secondary reactions that makes it extremely interesting for a wide range of application including biomedical field, e.g., drug delivery, adhesives, cell adhesion, biosensing. Despite high potential of polydopamine, the lack of deposition control and precision in existed methods limits their applications in microdevices and miniaturized functional systems like, for example, MEMS, microfluidic and sensorics. Herein, we demonstrate a novel maskless approach for surface micropatterning with polydopamine based on Multiphoton Lithography that overcomes present limitations. Neither strong oxidants, metal ions nor adjustment of pH to alkaline is required by this technique. The spatial resolution down to 0.8 µm has been achieved which is at least an order of magnitude smaller than shown by other existed methods. We are able to control the morphology and thickness of the micropattern by altering fabrication parameters allowing structure gradient. Apart from the glass substrate, we achieved PDA patterning at surfaces of different nature such as polychlorotrifluoroethylene, polydimethylsiloxane, polyethylene terephthalate, silicon wafers, and fluorinated glass coverslips. Post-modification of polydopamine micropatterns with protein enzyme like trypsin is demonstrated to highlight its sensing potential. Presented in this work microfabrication technique empowers advanced applications of mussel-inspired materials in single-molecule bioassays, sensors and other complex microdevices. T2 - International Conference on Precision Engineering and Sustainable Manufacturing CY - Okinawa, Japan DA - 18.07.2023 KW - Multiphoton lithography KW - Polydopamine KW - Micropatterning PY - 2023 AN - OPUS4-58878 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandić Lipińska, M. A1 - Davenport, R. A1 - Imhof, A. B. A1 - Waclavicek, R. A1 - Fateri, M. A1 - Meyer, Lena A1 - Gines-Palomares, J. C. A1 - Zocca, Andrea A1 - Makaya, A. A1 - Günster, Jens T1 - PAVER - Contextualizing laser sintering within a lunar technology roadmap N2 - The Global Exploration Strategy of the International Space Exploration Coordination Group (ISECG) describes a timeframe of 2020 and beyond with the ultimate aim to establish a human presence on Mars towards the 2040ies. The next steps lie on the Moon with a focus on the coming 10 years. Early lunar surface missions will establish a capability in support of lunar science and prepare and test mission operations for subsequent human exploration of Mars and long-duration human activities on the Moon. Given the extreme costs involved in the shipping of material from Earth, a prerequisite for future human exploration is the manufacturing of elements directly on the Moon’s surface. Unlike the equipment, which at the beginning will have to be brought from Earth, raw materials and energy could be available following the concept of In-Situ Resource Utilization. The ESA OSIP PAVING THE ROAD (PAVER) study investigates the use of a laser to sinter regolith into paving elements for use as roadways and launch pads thus mitigating dust issues for transport and exploration vehicles. The ESA-funded study examines the potential of using a laser (12 kW CO2 laser with spot beam up to 100 mm) for layer sintering of lunar and martian regolith powders to manufacture larger 3D elements and provide know-how for the automatic manufacture of paving elements in the lunar environment. The project contributes to the first step toward the establishment of a lunar base and will lead to the construction of equipment capable of paving areas and manufacturing 3D structures. PAVER project sets the starting point for an examination of the larger context of lunar exploration. Mission scenarios will look at different phases of lunar exploration: Robotic Lunar Exploration, Survivability, Sustainability, and Operational Phase. A proposed Technology Roadmap investigates the mission scenario and analyses how, and to which extent, laser melting/sintering will play a role in the various phases of exploration. The paper contextualizes laser sintering within selected mission scenarios and discusses the different kinds of infrastructure that can be produced at each phase of the mission. The outcome of the study includes the detailing of the TRL steps in the project and an outline of a timeline for the different elements. Covered aspects include terrain modelling such as operation pads, roadways, or towers, non-pressurized building structures to protect machinery, and habitat envelopes, to protect and shield humans against dust, micrometeoroids, and radiation. T2 - 73rd International Astronautical Congress (IAC) CY - Paris, France DA - 18.09.2022 KW - Additive manufacturing KW - Solar sintering KW - ISRU KW - Infrastructure KW - Lunar habitat KW - Paving PY - 2022 SP - 1 EP - 9 AN - OPUS4-56519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller-Elmau, Johanna A1 - Meyer, Frank A1 - Goebbert, Christian A1 - Günster, Jens T1 - Manufacturing Ceramics with Light N2 - Additive manufacturing of extremely complex and filigree geometries from ceramic materials is a fascinating topic as ceramic materials are especially suitable for extremely small structures thanks to their physicochemical properties: they are chemically stable and do not corrode, while exhibiting unique mechanical properties especially in the micrometre range (Fig. 1). In addition, the ceramic structures made of yttria-stabilized zirconia (YSZ) shown in the figure are transparent, which makes them interesting candidates for the development of miniaturized optical components. The refractive index of YSZ measures 2,2 and is therefore considerably higher than that of polymer-based materials or glasses. The possibility of building this type of structure is enabled with the use of ceramic slurries with sufficiently high Transparency for the volumetric process of two-photon polymerization, which uses a femtosecond-short-pulse laser to structure photo-crosslinkable resins in the volume of one droplet. Slurries with even further optimized transparency allow even the application of xolography, a volumetric process that builds components with relatively low resolution, but in relatively large volumes and higher productivity. In the scope of the research presented here, for the first time, this process is applied to sintered ceramic materials. To be able to use minute ceramic structures as real components, an approach for the hybridization of processes ispresented in which components in the centimetre range, with relatively low resolution, are combined with very high-resolution nanostructures. KW - Additive manufacturing KW - Zirconia KW - Two-photon-polymerization KW - Nanopowder PY - 2025 SN - 0173-9913 VL - 4 SP - 34 EP - 41 PB - Göller Verlag GmbH CY - Baden-Baden AN - OPUS4-65070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Laser beam melting additive manufacturing at μ-gravity N2 - At the Workshop "Neutron and Synchrotron Monitoring in Aerospace Advanced Manufacturing" at the Institute of Materials Physics in Space, German Aerospace Center (DLR) in Cologne, we presented on the opportunities and our experiences of using a powder based additive manufacturing process for in-space manufacturing applications in microgravity. T2 - Workshop 'Neutron and Synchrotron Monitoring in Aerospace Advanced Manufacturing' CY - Cologne, Germany DA - 11.08.2022 KW - Additive manufacturing KW - In-space manufacturing KW - Microgravity KW - μ-gravity KW - Laser beam melting KW - Advanced manufacturing KW - Aerospace KW - Process monitoring PY - 2022 AN - OPUS4-56521 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller-Elmau, Johanna T1 - 2PP of ceramic N2 - Photon-based additive manufacturing technologies such as SLA, DLP, LCM, moreover volumetric two-photon-polymerization (2PP), Xolography and holographic technologies promise the highest accuracy and dimensional freedom. To transfer the light through the feedstock it needs sufficient transparency. Ceramic particles used for powder processing routes act as scattering sites and therefore hinder the light transmission, unless… The particle size and particle size distribution are chosen small and narrow enough. Particles smaller than roughly 1/10th of the light wavelength, mostly nanoparticles around 5nm size, decrease scattering vastly. This turns resins even with homogeneously distributed ceramic weight fraction of up to 80% transparent again. Feedstocks were prepared for the highly accurate two-photon-polymerization gaining the smallest yttria stabilized zirconia structures with a resolution of 500nm and unique mechanical properties. The same feedstock was applied to DLP and LCM as layer-by-layer AM-technologies for bigger parts. Hybridizing both technologies enables ceramic parts with microscopic accuracy at macroscopic dimensions. The feedstock was even applied to the volumetric Xolography with the highest transparency requirement so far and to versatile and flexible holographic AM. What are the next steps? Can those proof-of -concept studies be transferred to industrial applications and what are the hurdles on the way? How to make the stretch between fundamental research and application-oriented development? T2 - Smart Made 2025 CY - Osaka, Japan DA - 01.10.2025 KW - Tranparent KW - Ceramic KW - Additive manufacturing PY - 2025 AN - OPUS4-65062 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hernández-García, María Amparo A1 - Rurack, Knut A1 - Bell, Jérémy T1 - Rapid fabrication of optical elements for sensing applications using a standard SLA printer N2 - The demand for compact, high-performance optical components has driven the development of increasingly sophisticated and miniaturized optical elements, often requiring complex and costly fabrication methods. In this study, we propose a cost-effective and accessible methodology for the fabrication of lenses and free-form optics using a commercially available stereolithography (SLA) 3D printer. A systematic characterisation of six transparent photopolymer resins was conducted in terms of their spectroscopic, optical, and morphological properties, i.e., surface and dimensional properties. The evaluation encompassed parameters such as transmittance, autofluorescence, refractive index, and surface roughness. A straightforward yet resilient printing and post-treatment protocol was formulated, facilitating the fabrication of optical components with over 80% transmittance, minimal intrinsic fluorescence, and surface quality that is compatible with exacting optical applications. The fabricated components demonstrated excellent dimensional fidelity to digital designs and high reproducibility. To demonstrate the versatility of this approach, aspherical, miniaturized, and freeform lenses were designed and integrated into three fluorogenic sensing systems, including oil (strip-based) and chlorine (microfluidic-based) detection platforms, as well as a smartphone-based SARS-CoV-2 biosensor. The integration of customized 3D-printed optics has been demonstrated to enhance signal collection and readout performance, thereby highlighting the potential of this approach to democratize the rapid prototyping and deployment of miniaturized optical systems. This work represents a significant advancement in the field of additive manufacturing, particularly in relation to the development of functional photonic devices. Furthermore, it opens new prospects for sensor applications in biosensing, microfluidics, imaging, and integrated optics. KW - 3D-printing KW - Free-form KW - Prototyping KW - Optical resin KW - Surface finishing KW - Fluorescence KW - Sensor PY - 2026 DO - https://doi.org/10.37188/lam.2026.024 VL - 7 SP - 1 EP - 19 PB - Light Publishing Group CY - Changchun AN - OPUS4-65555 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Julien A1 - Treutler, Kai A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Influence of Microstructure on the Machinability and Surface Integrity of Additively Manufactured Iron Aluminides N2 - The increasing global focus on energy and resource efficiency has stimulated a growing interest in additive manufacturing. AM offers economic advantages and enables an efficient use of materials. However, AM components often require subsequent mechanical post-processing, such as machining (e.g. milling), to achieve the final contours or surfaces. This is a particular challenge due to the heterogeneous and anisotropic nature of AM structures, which affect machining and the resulting component properties. High-performance materials such as iron aluminide represent a promising alternative to conventional high-temperature materials with a significant economic advantage. However, the strength and hardness properties, which are advantageous for applications in highly stressed lightweight components, pose a challenge for economical machining in addition to the AM microstructure properties. The difficult-to-cut material causes accelerated tool wear and insufficient surface quality. This study shows that crack-free additive manufacturing of the three-component system of iron-nickel-aluminum is possible, and advantages in terms of machinability compared to FeAl-AM components are achieved. The more homogeneous microstructure leads to a reduction in cutting forces, with positive effects on the machinability and optimized surface integrity. Ultrasonic assisted milling (USAM) offers great potential to address the major challenges posed by difficult-to-cut materials and additively manufactured weld structures. Therefore, this study focuses on assessing the transferability of previous positive results by USAM to the selected iron aluminide alloys. The machinability of the aluminides is analyzed by varying significant influencing variables in finish milling experiments and evaluated in terms of the loads on the tool and the resulting surface integrity. T2 - AA Meeting of Commission IX ‘Behavior of Metals subject to Welding’ CY - Rhodes, Greece DA - 08.07.2024 KW - Iron aluminide KW - Additive manufacturing KW - Machinability KW - Surface integrity KW - Ultrasonic-assisted milling PY - 2026 SP - 1 EP - 16 AN - OPUS4-65530 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinekamp, Christian T1 - An Amorphous Lewis-acidic Zirconium Chlorofluoride as HF Shuttle: C-F Bond Activation and Formation N2 - In recent years, fluorine chemistry has gained increasing political attention. Owing to a growing shortage of fluorspar, a raw material used for producing fluorinated base chemicals, fluorospar has been named among the 30 critical raw materials in the EU.2 As such, it becomes increasingly important to recycle existing fluorinated compounds and make them available as sources of fluorine for reactions. Significant progress has been made in the field of C-F bond activation using heterogeneous catalysts such as aluminum chlorofluoride (ACF).3–5 However, the transfer of fluorine atoms from one molecule to another using heterogeneous catalysts has not yet been reported. In this study, we successfully synthesized amorphous zirconium chlorofluoride (ZCF), and we were able to establish a catalytic behavior of ZCF in C-F bond activation reactions. We present a heterogeneous catalyst that performs dehydrofluorination of a fluoroalkane and consecutive hydrofluorination of an alkyne at room temperature. T2 - 2nd South African Fluorine Symposium CY - Sun City, South Africa DA - 09.02.2024 KW - ZCF KW - Heterogeneous catalysis KW - C-F bond activation KW - HF-shuttle PY - 2024 AN - OPUS4-59618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heinekamp, Christian T1 - Zirconium chloro fluoride as catalyst for C-F bond activation and HF transfer of fluoroalkanes N2 - In this work1, we have successfully synthesised amorphous zirconium chloro fluoride (ZCF), which exhibits medium lewis acidity. In addition to investigating the local coordination sphere around the Zr atoms and the material properties, we were able to establish a catalytic behavior of ZCF in C-F bond activation reactions. We present the first heterogeneous catalyst that performs dehydrofluorination of a fluoroalkane and consecutive hydrofluorination of an alkyne at room temperature. T2 - RSC Poster 2024 CY - Online meeting DA - 05.03.2024 KW - ZCF PY - 2024 AN - OPUS4-59619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Shaikh, Abdul Shaafi A1 - Fardan, Ahmed A1 - Mishurova, Tatiana A1 - Hryha, Eduard T1 - The Impact of High‐Productivity Processing on the Fatigue Failure of an Additive Manufactured Superalloy HAYNES 282 N2 - The elevated temperature low cycle fatigue life of additively manufactured HAYNES 282 superalloy from conventional 40 µm layer thickness process parameters was compared with that of high‐productivity 80 µm layer thickness process parameters. Wrought 282 alloy was also tested in parallel for comparison. The 40 µm process parameters produced fatigue life between 1400 and 1700 cycles to failure, the 80 µm process parameter specimens failed after ≈1200 cycles, and the wrought alloy reached 1350 cycles to failure. Microstructure investigations did not reveal systematic differences in phase constituents or grain structure between 40 and 80 µm processed 282 alloy. While both process parameters produced porosity of less than 0.05% by volume, high‐resolution X‐ray computed tomography showed the occurrence of large aspect ratio lack of fusion defects in the 80 µm material. These defects were also identified on fracture surfaces and could be related to the accelerated initiation and propagation of cracks, especially when oriented perpendicular to the load axis in samples built parallel to the building direction. The results emphasize the criticality of seemingly minor variations in defect characteristics on performance in cyclic loading conditions for high strength alloys. KW - Additive manufacturing KW - Laser powder bed fusion KW - PBF-LB KW - Fatigue KW - EBSD PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655732 DO - https://doi.org/10.1002/adem.202502048 SN - 1438-1656 SP - 1 EP - 13 PB - Wiley-VCH GmbH AN - OPUS4-65573 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? N2 - The use of laser-additively manufactured metallic components in the industrial sector is gaining traction, with the process now entering its application phase. Consequently, the materials are exposed to corrosive microbes, which this study examines in order to determine the implications of this exposure. Specifically, the study examines the exposure of laser powder bed fused AlSi10Mg (PBF-LB/AlSi10Mg) components to sulphate-reducing bacteria in an anaerobic environment. Is the specific PBF-LB microstructure a potential factor in determining or aiding biocorrosion? A prismatic specimen was exposed to sulphate-reducing bacteria (SRB) for two weeks. The sample was scanned by X-ray computed tomography (XCT) before and after SRB exposure. The two data sets were registered to each other (using the internal void distribution as markers, due to the corrosion of the specimen’s surface) to enable the evaluation of the corrosion damage. Virtual cuts of the 3D XCT reconstructions show a loss of volume and localised damage. The damage distribution aligns with the hatching pattern of laser exposure from laser powder bed fusion. T2 - Konferenz iCT 2026 CY - Linz, Austria DA - 10.02.2026 KW - Computed tomography KW - Biokorrosion KW - Additive manufacturing KW - PBF-LB KW - Laser powder bed fusion KW - Sulphate-reducing bacteria PY - 2026 AN - OPUS4-65570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sänger, Johanna Christiane A1 - Pauw, Brian Richard A1 - Sturm, Heinz A1 - Günster, Jens T1 - First time additively manufactured advanced ceramics by using two-photon polymerization for powder processing N2 - Methods and materials are presented here, which enable the manufacturing of fine structures using a 3D-printing method known as two-photon polymerization (2PP). As traditional photolithography methods for structuring ceramic slurries do not function with 2PP, due to light scattering on ceramic particles, a novel water-based photoresist with high ceramic loading of extremely well dispersed ceramic nano particles was developed. This photoresist is basically a ceramic slurry containing a photocurable agent and a photoinitiator to be crosslinkable with the 780 nm wavelength femtosecond laser light source of the 2PP machine. It is demonstrated that it is possible to gain a highly transparent and low viscous slurry suitable for 2PP processing. This work shows the development of the slurry, first printing results and the post-printing processes required to form three dimensional ceramic microstructures consisting of alumina toughened zirconia (ATZ). KW - 3D-printing KW - Two-photon polymerization KW - 2PP KW - Ceramic nano particles KW - Slurry KW - Alumina toughened zirconia KW - ATZ KW - Additive manufacturing KW - SchwarzP cells KW - Nano-ceramic-additive-manufacturing photoresin KW - NanoCAM PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517441 DO - https://doi.org/10.1016/j.oceram.2020.100040 VL - 4 SP - 100040 PB - Elsevier Ltd. AN - OPUS4-51744 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zocca, Andrea T1 - A comparison of layerwise slurry deposition and (LSD-print) laser induced slip casting (LIS) for the additive manufacturing of advanced ceramics N2 - The presentation gives an overview of two slurry-based additive manufacturing (AM) technologies specifically developed for advanced ceramic materials. The “Layerwise Slurry Deposition” (LSD-print) is a modification of Binder Jetting making use of a ceramic slurry instead of a dry powder as a feedstock. In this process, a slurry is deposited layer-by-layer by means of a doctor blade and dried to achieve a highly packed powder layer, which is then printed by jetting a binder. The LSD-print technology combines the high-speed printing of binder jetting with the possibility of producing a variety of high-quality ceramics with properties comparable to those achieved by traditional processing. The Laser Induced Slip casting (LIS) technology follows a novel working principle by locally drying and selectively consolidating layer-by-layer a ceramic green body in a vat of slurry, using a laser as energy source. LIS combines elements of Vat Photopolymerization with the use of water-based feedstocks containing a minimal amount of organic additives. The resulting technology can be directly integrated into a traditional ceramic process chain by manufacturing green bodies that are sintered without the need of a dedicated debinding. Both technologies offer high flexibility in the ceramic feedstock used, especially concerning material and particle size. Advantages and disadvantages are briefly described to outline the specific features of LSD-print and LIS depending on the targeted application. T2 - AM Ceramics CY - Vienna, Austria DA - 27.09.2023 KW - Additive Manufacturing KW - Dental KW - Ceramics KW - Feldspar PY - 2023 AN - OPUS4-58468 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zocca, Andrea T1 - LSD-print: a 10-years journey of an additive manufacturing technology from porcelain to technical ceramics N2 - Motivated by the aim of developing an additive manufacturing (AM) technology easily integrated in the process chains of the ceramic industry, the LSD-print technology was conceived as a slurry-based variation of binder jetting (BJ). BJ and other powder bed technologies (such as powder bed fusion) are amongst the most successful AM techniques, especially for metals and polymers, thanks to their high productivity and scalability. The possibility to use commercially available feedstocks (in the form of powders or granules) makes BJ also attractive for ceramic materials. The application of these techniques to most advanced ceramics has however been difficult so far, because of the limitations in depositing homogeneous layers with fine, typically poorly flowable powders. In this context, the "layerwise slurry deposition" (LSD) was proposed at TU Clausthal (Germany) as a slurry-based deposition of ceramic layers by means of a doctor blade. Combined with layer-by-layer laser sintering of the material, the LSD process was originally demonstrated for the rapid prototyping of silicate ceramics. Due to the difficulties in controlling the microstructure and the defect formation in laser-sintered technical ceramics, the LSD process was later combined with inkjet printing in the LSD-print technology, which has been further developed at BAM (Germany) in the past decade. The LSD-print technology combines the high speed of inkjet printing, typical of BJ, with the possibility of producing a variety of high-quality ceramics with properties comparable to those achieved by traditional processing. Due to the mechanical stability of the powder bed, the process can also be carried out with continuous layer deposition on a rotating platform, which further increases its productivity. This presentation will delve into 10 years of research on the LSD-print of a wide variety of technical ceramics including alumina, silicon carbides and dental ceramics. The discussion highlights how a seemingly small process and feedstock modification (from powders to slurries) has great influence on the challenges and potential of this process, which are being addressed on its path to industrialization. T2 - young Ceramists Additive Manufacturing Forum (yCAM) 2024 CY - Tampere, Finland DA - 06.05.2024 KW - Additive Manufacturing KW - Ceramic KW - Layerwise slurry deposition KW - Slurry KW - LSD-print PY - 2024 AN - OPUS4-60056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens A1 - Sänger, Johanna A1 - Pauw, Brian Richard T1 - Two-Photon-Polymerization for Ceramics Powder Processing N2 - Manipulating ceramic powder compacts and ceramic suspensions (slurries) within their volume with light requires a minimum transparency of the materials. Compared to polymers and metals, ceramic materials are unique as they offer a wide electronic band gap and thus a wide optical window of transparency. The optical window typically ranges from below 0.3 µm up to 5µm wavelength. Hence, to penetrate with laser light into the volume of a ceramic powder compound its light scattering properties need to be investigated and tailored. In the present study we introduce the physical background and material development strategies to apply two-photon-polymerization (2PP) for the additive manufacture of filigree structures within the volume of ceramic slurries. T2 - ECerSXVIII Conference Exhebition of the European Ceramic Society CY - Lyon, France DA - 02.07.2023 KW - Additive Manufacturing KW - Transparent ceramics PY - 2023 AN - OPUS4-59883 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zocca, Andrea T1 - Water-based additive manufacturing of ceramics by Laser-Induced Slip Casting (LIS) N2 - The Laser-Induced Slip Casting is an additive manufacturing technology specifically developed for ceramic materials using water-based ceramic slurries. The process takes place layer-by-layer in a similar fashion as top-down vat photopolymerization, selectively consolidating each layer by means of a laser energy source positioned on the top. Contrary to vat photopolymerization, in which the consolidation is achieved by selectively cross-linking a ceramic-filled resin, LIS uses water-based slurries with a low amount of organic additives (typically < 5 wt%) as feedstocks. In LIS, a green body is formed by local evaporation of water which causes the suspension to collapse forming a cast, following a mechanism similar to slip casting. Only a small content of organic additives is needed to effectively disperse the ceramic particles and to increase the green strength. The technology is very versatile and can be applied to all ceramic systems that can be dispersed in water. One of the main advantages is that even dark materials such as silicon carbide can be processed without issues related to light scattering and absorption. The presentation will discuss strengths and limitations of LIS compared to other AM technologies and will highlight the latest results for alumina and for silicon carbide ceramics. T2 - 48th International Conference and Expo on Advanced Ceramics and Composites (ICACC2024) CY - Daytona, FL, USA DA - 28.01.2024 KW - Additive Manufacturing KW - Ceramic KW - Water-based KW - Slurry KW - Laser PY - 2024 AN - OPUS4-60054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zocca, Andrea T1 - An overview of ceramic AM with focus on bioceramics and powder bed technologies N2 - The presentation will start with an overview of ceramic additive manufacturing (AM) technologies and will discuss the potential of AM in the field of bioceramics. The presentation will then focus on two possible use cases of binder jetting technologies. In the first example, standard powder-based binder jetting is used to manufacture a porous implant design for large scale bone defects. The related challenges in the process chain will be discussed, from powder synthesis to sintering and characterization of the printed part. In the second example, the LSD-print slurry-based binder jetting technology is presented as a possibility to adapt powder-bed AM to produce dense ceramic parts. The use case will focus on an application in the field of dental ceramics, specifically for the manufacturing of patient individualized single tooth restorations (veneers, crowns) with a high throughput process chain. T2 - BioCAM - Additive Manufacturing Applied to Bioceramics CY - Mons, Belgium DA - 06.12.2023 KW - Additive Manufacturing KW - Bioceramic KW - Binder Jetting PY - 2023 AN - OPUS4-60053 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Günster, Jens T1 - Tailoring powder properties for the light based volumetric additive manufacture of Ceramics N2 - In order to be able to manipulate ceramic powder compacts and ceramic suspensions (slurries) within their volume with light, a minimum transparency of the materials is required. Compared to polymers and metals, ceramic materials are characterized by the fact that they have a wide electronic band gap and therefore a wide optical window of transparency. The optical window generally ranges from less than 0.3 µm to 5 µm wavelength. In order to focus light into the volume of a ceramic powder compact, its light scattering properties must therefore be tailored. In this study, we present the physical background and material development strategies for the application of two-photon polymerization (2PP) and selective volumetric sintering for the additive manufacturing of structures in the volume of ceramic slips and green compacts. T2 - SmartMade 2024 CY - Osaka, Japan DA - 10.04.2024 KW - Additive Manufacturing KW - Two Photon Polymerization KW - Advanced ceramics PY - 2024 AN - OPUS4-59888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Low cycle fatigue behavior of DED-L Ti-6AL-4V N2 - Laser powder-based directed energy deposition (DED-L) is a technology that offers the possibility for 3D material deposition over hundreds of layers and has thus the potential for application in additive manufacturing (AM). However, to achieve broad industrial application as AM technology, more data and knowledge about the fabricated materials regarding the achieved properties and their relationship to the manufacturing process and the resulting microstructure is still needed. In this work, we present data regarding the low-cycle fatigue (LCF) behavior of Ti-6Al-4V. The material was fabricated using an optimized DED-L process. It features a low defect population and excellent tensile properties. To assess its LCF behavior two conventionally manufactured variants of the same alloy featuring different microstructures were additionally tested. The strain-controlled LCF tests were carried out in fully reversed mode with 0.3 % to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behavior and failure mechanisms are described. For characterization, optical microscopy (OM), scanning electron microscopy (SEM), and micro-computed tomography (µCT) were used. The low defect population allows for a better understanding of the intrinsic material’s properties and enables a fairer comparison against the conventional variants. The fatigue lifetimes of the DED-L material are nearly independent of the test temperature. At elevated test temperatures, they are similar or higher than the lifetimes of the conventional counterparts. At room temperature, they are only surpassed by the lifetimes of one of them. The principal failure mechanism involves multiple crack initiation sites. T2 - Ninth International Conference on Low Cycle Fatigue (LCF9) CY - Berlin, Germany DA - 21.06.2022 KW - AGIL KW - Additive Manufacturing KW - Ti-6Al-4V KW - Low-Cycle-Fatigue KW - Microstructure PY - 2022 AN - OPUS4-55123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High temperature fatigue crack growth in nickel-based alloys joined by brazing and additive manufacturing N2 - Nickel-based alloys have been widely used for gas turbine blades owing to their excellent mechanical properties and corrosion resistance at high temperatures. The operating temperatures of modern gas turbines have been increased in pursuit of increased thermal efficiency. Turbine blades are exposed to these high temperatures combined with mechanical stresses, resulting in material damage through creep, fatigue, and other mechanisms. These turbine blades must be regularly inspected and replaced as needed, to prevent the loss of efficiency, breakdown, and catastrophic failure. Repair of the damaged turbine blades is often a more practical and cost-effective option than replacement, as replacement is associated with high costs and loss of material resources. To this end, state-of-the-art repair technologies including different additive manufacturing and brazing processes are considered to ensure efficient repair and optimum properties of repaired components. In any repaired part, materials property-mismatches and/or inner defects may facilitate the crack initiation and propagation and thus reduce the number of load cycles to failure. Therefore, a fundamental understanding of the fatigue crack growth and fracture mechanisms in joining zones is required to enable the prediction of the remaining life of repaired components and to further improve and adapt the repair technologies. Fatigue crack growth experiments have been conducted on SEN (Single Edge Notch) specimens joined via brazing, and pre-sintered Preform (PSP) and multi-materials (casted/printed) specimens layered via additive manufacturing (AM). The experiments were performed at 950 °C and various stress ratios. The crack growth was measured using DCPD (Direct Current Potential Drop) method. The stress intensity factors for joined SEN specimens were calculated using the finite element method and then used to derive the fatigue crack growth curves. Metallographic and fractographic analyses were conducted to get insight into the fracture mechanism. Results show that the experimental technique for fatigue crack growth was successfully adapted and applied for testing joined specimens. Furthermore, the initial tests indicate that the investigated braze filler material provides a lower resistance to crack growth, and bonding defects cause a crack to deviate to the interface of the base material and joining zone. In AM-sandwich specimens, the crack growth rates are significantly reduced when the crack reaches the interface of printed material and casted material. The obtained crack growth data can be used to calibrate a crack growth model, which will further be utilized to predict the remaining life of repaired components. T2 - DGM Arbeitskreis Mechanisches Werkstoffverhalten bei hoher Temperatur im FachausschussWerkstoffverhalten unter mechanischer Beanspruchung CY - Munich, Germany DA - 10.10.2023 KW - Fatigue crack growth KW - Joined nickel-based alloys PY - 2023 AN - OPUS4-60908 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Agudo Jácome, Leonrado T1 - Low-Cycle Fatigue Behavior of Laser Powder Bed Fused Inconel 718 at Room and High Temperature N2 - The nickel-base superalloy Inconel 718 (IN718) is one of the most commonly used Ni-based superalloys for high temperature structural applications for its remarkable strength, as well as creep, fatigue, and corrosion resistance up to 650 °C. While IN718 has traditionally been employed as cast or wrought material, it is difficult to machine because of its high strength and toughness. The additive manufacturing of IN718 components made by metal AM has thus gained extensive attention to produce expensive near-net shaped components of high-temperature alloys such as IN718, for it saves material and costs in processing and machining steps. Among all metal additive manufacturing (AM) technologies, laser powder bed fusion (PBF-LB/M) is the most widespread, IN718 being one of the most common alloys produced with it. However, high cooling rates associated to the PBF-LB/M process, hinders the primary strengthening phases γ’’ and γ’ to form, as these cooling rates induce a dislocation cellular substructure, at which walls primary Laves phases bind segregating Nb, Ti and Mo. Many of the therefore needed heat-treatment strategies can then promote Laves-phase transformation into the stable δ phase along the cell and grain boundaries. Laves and δ phases, as well as grain-boundary primary carbides may have adverse effects on mechanical properties. The mostly needle-shaped δ phase was namely found to have a detrimental effect on creep rupture life while no direct effect on LCF fatigue life was evident. In this work room- and high-temperature (650 °C) low-cycle fatigue behavior of PBF-LB/M IN718 is investigated in the four-step heat-treated state and compared to wrought IN718. The microstructure of both materials is characterized across length scales via microscopy methods. The fatigue life at room temperature of the PBF-LB/M IN718 material is slightly lower than that for the wrought material, which is reversed at 650 °C. The cyclic stress response for both materials is marked by cyclic softening that is more pronounced at higher test temperatures. Multiple secondary cracks form at high strain amplitudes, at both room and high temperatures. High testing temperatures enhance specially crack formation at the transitions of regions between elongated grains and columns of stacked grains with ripple patterns in the PBF-LB/M material. Additional to this behavior, pronounced crack branching and deflection indicate that the cracks are controlled by sharp micromechanical gradients. T2 - EUROMAT 2025 CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - Low-cycle fatigue KW - Microstructural characterization KW - Ni-base superalloy PY - 2025 AN - OPUS4-64354 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suarez Ocano, Patricia T1 - Influence of heat-treatment-induced microstructural evolution on the Low Cycle Fatigue behavior of 316L stainless steel fabricated by Laser Powder Bed Fusion N2 - Additive manufacturing, particularly the laser powder bed fusion (PBF-LB/M) process, has gained significant attention in recent years due to its ability to produce complex geometries with enhanced mechanical properties. Among the various materials used, 316L stainless steel is highly favored for cyclically loaded components due to its exceptional mechanical strength, high-temperature performance, and corrosion resistance, making it widely applicable across various industries. 316L SS fabricated by PBF-LB/M (PBF-LB/M/316L) exhibits a unique hierarchical microstructure, with high density of low-angle grain boundaries (LAGBs), nano-dispersed silicates, chemical micro-segregations, and solidification-induced cellular structures. Particularly, the submicron-sized cellular features enriched with chromium (Cr) and molybdenum (Mo), along with high dislocation densities, contribute to a superior strength-ductility balance compared to conventionally manufactured 316L SS. The dispersed silicate particles act also as a strengthening phase, impeding dislocation movement and enhancing plastic deformation resistance. This study explores the effect of heat treatments on the low-cycle fatigue (LCF) behavior of PBF-LB/M/316L at room temperature (RT) and 600 °C. First, three heat treatment conditions were applied to the as-built material: 450 °C for 4 hours (HT450/4), 800 °C for 3 hours (HT800/3), and 900 °C for 1 hour (HT900/1) to investigate their influence on microstructural evolution. Microstructural analysis revealed that the HT450/4 condition preserved the cellular structure with high dislocation density, while the HT800/3 condition showed partial dissolution of cells together with reduction in segregated elements along the cell walls and a reduced dislocation density. The HT900/1 condition resulted in complete segregation and cellular structure dissolution with comparable dislocation density to HT800/3 while maintaining the crystallographic texture and grain morphology. Intermetallic χ phase was mostly observed at the grain boundaries in HT800/3, but not in HT900/1. Fully reversed LCF tests were conducted under strain-controlled conditions with a strain amplitude of 0.8 %. Tests were interrupted at specific intervals to analyze the interaction between hierarchical microstructural features and deformation mechanisms in the three heat-treated conditions. Due to the pronounced dislocation cell structures and elemental segregation, the microstructure of the HT450/4 condition significantly impact deformation and damage mechanisms during cyclic loading, which in turn, differ from the conventional produced counterparts. The results provide insights into the relationship between microstructural features and fatigue performance, highlighting key deformation and failure mechanisms under cyclic loading. T2 - FEMS 2025 EUROMAT 18th European Congress and Exhibition on Advanced Materials and Processes CY - Granada, Spain DA - 14.09.2025 KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Low Cycle Fatigue KW - Microstructure PY - 2025 AN - OPUS4-64238 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Manufacturing a safer world: Diffraction based residual stress analysis for metal additive manufacturing N2 - Metal Additive Manufacturing (AM) technologies such as Laser Powder Bed Fusion (LPBF) are characterized by layer wise construction, which enable advancements of component design, with associated potential gains in performance and efficiency. However, high magnitude residual stresses (RS) are often a product of the rapid thermal cycles typical of the layerwise process. Therefore, a deep understanding of the formation of RS, the influence of process parameters on their magnitude and the impact on mechanical performance is crucial for widespread application. The experimental characterisation of these RS is essential for safety related engineering application and supports the development of reliable numerical models. Diffraction-based methods for RS analysis using neutrons and high energy X-rays enable non-destructive spatially resolved characterisation of both surface and bulk residual stresses in complex components. This presentation will provide an overview of recent research by the BAM at large scale facilities for the characterization of residual stresses in LPBF metallic alloys as a function of process parameters. In addition, the challenges posed by the textured and hierarchical microstructures of LPBF materials on diffraction-based RS analysis in AM materials will be discussed. This will include the question of the d0 reference lattice spacing and the appropriate choice of the diffraction elastic constants (DECs) to calculate the level of RS in LPBF manufactured alloys. T2 - 11th INternational Conference on Residual Stress (ICRS11) CY - Online meeting DA - 28.03.2021 KW - Residual stress analysis KW - Neutron diffraction KW - X-ray diffraction KW - Additive manufacturing KW - Laser powder bed fusion KW - AGIL PY - 2022 AN - OPUS4-54676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano-Munoz, Itziar T1 - Synchrotron x ray refraction detects microstructure and porosity evolution during in situ heat treatments in an LPBF ALSI10MG alloy N2 - The complexity of any microstructural characterization significantly increases when there is a need to evaluate the icrostructural evolution as a function of temperature. To date, this characterization is primarily performed by undertaking elaborative ex-situ experiments where the material’s heating procedure is interrupted at different temperatures or times. Moreover, these studies are often limited to a region smaller than the representative elementary volume, which can lead to partial or even biased interpretations of the collected data. This limitation can be greatly overcome by using in-situ synchrotron X-ray refraction (SXRR). T2 - ICTMS 2022 CY - Grenoble, France DA - 27.06.2022 KW - Synchrotron refraction KW - In situ heating KW - AlSi10Mg alloy KW - Additive manufacturing KW - Microstructural evolution PY - 2022 AN - OPUS4-55199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Ageing behaviour of laser powder bed fused 316L: a powder to failure approach N2 - Laser powder bed fusion (LPBF) is an additive manufacturing process for materials which inherently tends to yield various degrees of metastable hierarchical microstructures, defects and high residual stresses in the as-built condition depending on the process parameters. The understanding of the evolution of these typical features during heat treatment and subsequent thermal and mechanical ageing is crucial for the wider acceptance for safety critical structures. A multi-disciplinary research project at BAM studying the development of the microstructure, defects, residual stresses typical of LPBF 316L and their evolution during thermal and mechanical ageing has led to insights into the stability of these inherent features. This presentation aims to give a broad overview of the project with a few specific cases of investigation. Firstly, the formation of residual stresses, the nature of the initial microstructure, the tensile properties and a modelling approach to understand the anisotropy will be presented. This will be followed by examples of studies of their evolution during heat treatment, long term thermal exposure, and room temperature and high temperature mechanical testing compared to a baseline of conventional wrought variant of the same alloy. T2 - International Conference on Additive Manufacturing 2021 (ICAM 2021) CY - Online meeting DA - 01.11.2021 KW - Ageing KW - Additive manufacturing KW - Laser powder bed fusion KW - AGIL PY - 2021 AN - OPUS4-54106 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Texture Dependent Micromechanical Anisotropy of Laser Powder Bed Fused Inconel 718 N2 - Additive manufacturing methods such as laser powder bed fusion (LPBF) allow geometrically complex parts to be manufactured within a single step. However, as an aftereffect of the localized heat input, the rapid cooling rates are the origin of the large residual stress (RS) retained in as-manufactured parts. With a view on the microstructure, the rapid directional cooling leads to a cellular solidification mode which is accompanied by columnar grown grains possessing crystallographic texture. The solidification conditions can be controlled by the processing parameters and the scanning strategy. Thus, the process allows one to tailor the microstructure and the texture to the specific needs. Yet, such microstructures are not only the origin of the mechanical anisotropy but also pose metrological challenges for the diffraction-based RS determination. In that context the micromechanical elastic anisotropy plays an important role: it translates the measured microscopic strain to macroscopic stress. Therefore, it is of uttermost importance to understand the influence of the hierarchical microstructures and the texture on the elastic anisotropy of LPBF manufactured materials. This study reveals the influence of the build orientation and the texture on the micro-mechanical anisotropy of as-built Inconel 718. Through variations of the build orientation and the scanning strategy, we manufactured specimens possessing [001]/[011]-, [001]-, and [011]/[111]-type textures. The resulting microstructures lead to differences in the macroscopic mechanical properties. Even further, tensile in-situ loading experiments during neutron diffraction measurements along the different texture components revealed differences in the microstrain response of multiple crystal lattice planes. In particular, the load partitioning and the residual strain accumulation among the [011]/[111] textured specimen displayed distinct differences measured up to a macroscopic strain of 10 %. However, the behavior of the specimens possessing [001]/[011]-and [001]-type texture was only minorly affected. The consequences on the metrology of RS analysis by diffraction-based methods are discussed. T2 - International Conference on Additive Manufacturing ICAM 2022 CY - Orlando, FL, USA DA - 31.10.2022 KW - Laser powder bed fusion KW - Neutron diffraction KW - Electron backscatter diffraction KW - Mechanical behavior PY - 2022 AN - OPUS4-56376 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Fundamentals of diffraction-based residual stress and texture analysis of PBF-LB Inconel 718 N2 - Laser powder bed fusion (PBF-LB/M) of metallic alloys is a layer wise additive manufacturing process which provides significant scope for more efficient designs of components, benefiting performance and weight, leading to efficiency improvements for various sectors of industry. However, to benefit from these design freedoms, knowledge of the high produced induced residual stress and mechanical property anisotropy associated with the unique microstructures is critical. X-ray and neutron diffraction are considered the benchmark for non-destructive characterization of surface and bulk internal residual stress. The latter, characterized by the high penetration power in most engineering alloys, allows for the use of diffraction angle close to 90° enabling a near cubic sampling volume to be specified. However, the complex microstructures of columnar growth with inherent crystallographic texture typically produced during PBF-LB/M of metallics present significant challenges to the assumptions typically required for time efficient determination of residual stress. These challenges include the selection of an appropriate set of diffraction elastic constants and a representative strain-free reference for the material of interest. In this presentation advancements in the field of diffraction-based residual stress analysis of L-PBF Inconel 718 will be presented. The choice of an appropriate set of diffraction-elastic constants depending on the underlying microstructure will be described. T2 - MLZ User Meeting 2022 CY - Munich, Germany DA - 08.12.2022 KW - Diffraction KW - Residual Stress KW - Microstructure KW - Texture KW - Mechanical behavior PY - 2022 AN - OPUS4-56804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ti-6Al-4V N2 - The elastic properties (Young's modulus, shear modulus) of titanium alloy Ti-6Al-4V were investigated between room temperature and 400 °C in an additively manufactured variant (laser-based directed energy deposition with powder as feedstock, DED-LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, microstructure, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - Ti-6Al-4V PY - 2023 DO - https://doi.org/10.5281/zenodo.7813732 PB - Zenodo CY - Geneva AN - OPUS4-57286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Microstructure Based Study on the Low Cycle Fatigue Behavior of Stainless Steel 316L manufactured by Laser Powder Bed Fusion N2 - Due to the advantages of Laser Powder Bed Fusion (PBF-LB), i.e., design freedom and the possibility to manufacture parts with filigree structures, and the considerable amount of knowledge available for 316L in its conventional variant, the mechanical behavior, and related microstructure-property relationships of PBF-LB/316L are increasingly subject of research. However, many aspects regarding the - application-relevant - mechanical behavior at high temperatures are not yet fully understood. Here, we present the results of an experimental study on the LCF behavior of PBF-LB/316L featuring a low defect population, which makes this study more microstructure-focused than most of the studies in the literature. The LCF tests were performed between room temperature (RT) and 600 °C. The mechanical response is characterized by strain-life curves, and hysteresis and cyclic deformation curves. The damage and deformation mechanisms are studied with X-ray computed tomography, and optical and electron microscopy. The PBF-LB/M/316L was heat treated at 450 °C for 4 h, and a hot‑rolled (HR) 316L variant with a fully recrystallized equiaxed microstructure was tested as a reference. Besides, selected investigations were performed after a subsequent heat treatment at 900 °C for 1 h. The PBF-LB/316L exhibits higher cyclic stresses than HR/316L for most of the fatigue life, especially at room temperature. At the smallest strain amplitudes, the fatigue lives of PBF-LB/M/316L are markedly shorter than in HR/316L. The main damage mechanisms are multiple cracking at slip bands (RT) and intergranular cracking (600 °C). Neither the melt pool boundaries nor the gas porosity have a significant influence on the LCF damage mechanism. The cyclic stress-strain deformation behavior of PBF-LB/M/316L features an initial hardening followed by a continuous softening. The additional heat treatment at 900 °C for 1 h led to decreased cyclic stresses, and a longer fatigue life. T2 - 4th Symposium on Materials and Additive Manufacturing CY - Berlin, Germany DA - 12.06.2024 KW - AGIL KW - 316L KW - Microstructure KW - Low Cycle Fatigue KW - Heat Treatment KW - Laser Poeder Bed Fusion PY - 2024 AN - OPUS4-60432 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of Ni-based alloy Inconel IN718 N2 - The elastic properties (Young's modulus, shear modulus) of Ni-based alloy Inconel IN718 were investigated between room temperature and 800 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled bar). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - IN718 PY - 2023 DO - https://doi.org/10.5281/zenodo.7813824 PB - Zenodo CY - Geneva AN - OPUS4-57287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep Behavior of Stainless Steel 316L Manufactured by Laser Powder Bed Fusion N2 - The broader industrial adoption of metal AM in safety-critical applications is limited, among others, by the still in-sufficient understanding of process–structure–property relationships and a lack of reliable mate-rial data. The content presented here approaches this limitation regarding the creep behavior of one of the most studied AM alloys: PBF-LB/M/316L stainless steel. A nearly as-built and a condition heat treated at 900 °C for 1 h, along with a conventionally manufactured variant are investigated. The creep behavior until reaching the minimum creep rate is mainly determined by the solidification cell structure. The damage is overall mainly intergranular, independent of the heat treated condition. The heat treatment at 900 °C for 1 h partially influenced the microstructure (mainly in terms of cell structure). The creep behavior until reaching the minimum creep rate remained nearly unchanged. The creep lifetime and ductility were enhanced. The crystallographic texture evolved after creep deformation. T2 - TMS 2025 Annual Meeting & Exhibition CY - Las Vegas, NV, USA DA - 23.03.2025 KW - AGIL KW - Creep KW - 316L KW - Microstructure PY - 2025 AN - OPUS4-63456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Separation of the Formation Mechanisms of Residual Stresses in LPBF 316L N2 - Rapid cooling rates and steep temperature gradients are characteristic of additively manufactured parts and important factors for the residual stress formation. This study examined the influence of heat accumulation on the distribution of residual stress in two prisms produced by Laser Powder Bed Fusion (LPBF) of austenitic stainless steel 316L. The layers of the prisms were exposed using two different border fill scan strategies: one scanned from the centre to the perimeter and the other from the perimeter to the centre. The goal was to reveal the effect of different heat inputs on samples featuring the same solidification shrinkage. Residual stress was characterised in one plane perpendicular to the building direction at the mid height using Neutron and Lab X-ray diffraction. Thermography data obtained during the build process were analysed in order to correlate the cooling rates and apparent surface temperatures with the residual stress results. Optical microscopy and micro computed tomography were used to correlate defect populations with the residual stress distribution. The two scanning strategies led to residual stress distributions that were typical for additively manufactured components: compressive stresses in the bulk and tensile stresses at the surface. However, due to the different heat accumulation, the maximum residual stress levels differed. We concluded that solidification shrinkage plays a major role in determining the shape of the residual stress distribution, while the temperature gradient mechanism appears to determine the magnitude of peak residual stresses. T2 - MLZ User Meeting 2020 CY - Online meeting DA - 08.12.2020 KW - Computed tomography KW - Neutron diffraction KW - X-ray diffraction KW - Additive manufacturing KW - Residual stress KW - Thermography KW - LPBF KW - Laser Powder Bed Fusion PY - 2020 AN - OPUS4-51793 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High temperature fatigue crack growth in nickel-based alloys joined by brazing and additive manufacturing N2 - Nickel-based alloys have been widely used for gas turbine blades owing to their excellent mechanical properties and corrosion resistance at high temperatures. The operating temperatures of modern gas turbines have been increased in pursuit of increased thermal efficiency. Turbine blades are exposed to these high temperatures combined with mechanical stresses, resulting in material damage through creep, fatigue, and other mechanisms. These turbine blades must be regularly inspected and replaced as needed, to prevent the loss of efficiency, breakdown, and catastrophic failure. Repair of the damaged turbine blades is often a more practical and cost-effective option than replacement, as replacement is associated with high costs and loss of material resources. To this end, state-of-the-art repair technologies including different additive manufacturing and brazing processes are considered to ensure efficient repair and optimum properties of repaired components. In any repaired part, materials property-mismatches and/or inner defects may facilitate the crack initiation and propagation and thus reduce the number of load cycles to failure. Therefore, a fundamental understanding of the fatigue crack growth and fracture mechanisms in joining zones is required to enable the prediction of the remaining life of repaired components and to further improve and adapt the repair technologies. Fatigue crack growth experiments have been conducted on SEN (Single Edge Notch) specimens joined via brazing, and pre-sintered Preform (PSP) and multi-materials (casted/printed) specimens layered via additive manufacturing (AM). The experiments were performed at 950 °C and various stress ratios. The crack growth was measured using DCPD (Direct Current Potential Drop) method. The stress intensity factors for joined SEN specimens were calculated using the finite element method and then used to derive the fatigue crack growth curves. Metallographic and fractographic analyses were conducted to get insight into the fracture mechanism. Results show that the experimental technique for fatigue crack growth was successfully adapted and applied for testing joined specimens. Furthermore, the initial tests indicate that the investigated braze filler material provides a lower resistance to crack growth, and bonding defects cause a crack to deviate to the interface of the base material and joining zone. In AM-sandwich specimens, the crack growth rates are significantly reduced when the crack reaches the interface of printed material and casted material. The obtained crack growth data can be used to calibrate a crack growth model, which will further be utilized to predict the remaining life of repaired components. T2 - FEMS EUROMAT 2023 CY - Frankfurt a. M., Germany DA - 03.09.2023 KW - Fatigue crack growth KW - Joined nickel-based alloys PY - 2023 AN - OPUS4-58266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana T1 - Separation of the impact of residual stress and microstructure on the fatigue performance of LPBF Ti-6Al-4V at elevated temperature (Keynote) N2 - Ti-6Al-4V alloy is intensively used in the aerospace industry because of its high specific strength. However, the application of Laser Powder Bed Fusion (LPBF) Ti-6Al-4V alloy for structurally critical load-bearing components is limited. One of the main limiting factors affecting the structural integrity, are manufacturing defects. Additionally, the high cooling rates associated with LPBF process result in the formation of large residual stress (RS) with complex fields. Such RS can cause cracking and geometrical distortions of the part even right after production. Also, the microstructure of LPBF Ti-6Al-4V in the as-built condition is significantly different from that of the conventionally produced alloy. All these factors affect the mechanical behavior of the material. Therefore, to improve the material performance it is important to evaluate the individual effect of RS, defects, and microstructure on fatigue life. To this aim Ti-6Al-4V LPBF material in as-built condition and subjected to different post-processing, including two heat treatments (for stress relief and microstructural modification) and Hot Isostatic Pressing (HIP, for densification), were investigated. Prior to fatigue tests at elevated temperature, the microstructure, the mesostructure, and subsurface RS on the fatigue samples were investigated. It was found that the fatigue performance of HIPped samples is similar to that of conventionally produced Ti-6Al-4V. The tensile RS found at the surface of as-built samples decreased the fatigue life compared to heat-treated samples. Additionally, the modification of the microstructure (by heat treatment) did not affect the fatigue performance in the regime of mostly elastic strain. This shows that in the absence of tensile RS the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. T2 - EUROMAT 2021 CY - Online meeting DA - 12.09.2021 KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Fatigue performance PY - 2021 AN - OPUS4-53278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni T1 - Procedures to Quantitatively Characterize Morphological Features of Triply Periodic Minimal Surface Structures N2 - Additively manufactured (AM) metallic sheet-based Triply Periodic Minimal Surface Structures (TPMSS) meet several requirements in both bio-medical and engineering fields: Tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some challenges related to quality control. In fact, the optimization of both the AM process and the properties of TPMSS is impossible without considering structural characteristics as manufacturing accuracy, internal defects, and as well as surface topography and roughness. In this study, the quantitative non-destructive analysis of TPMSS manufactured from Ti-6Al-4V alloy by electron beam melting was performed by means of laboratory X-ray computed tomography (XCT). T2 - International conference on tomography of material and structures 2022 CY - Grenoble, France DA - 27.06.2022 KW - Additive manufacturing KW - Scaffold KW - Lightweight structures KW - Computed tomography PY - 2022 AN - OPUS4-55229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana T1 - Influence of residual stress and microstructure on mechanical performance of LPBF TI-6AL-4V N2 - Ti-6Al-4V alloy is intensively used in the aerospace industry because of its high specific strength. However, the application of Laser Powder Bed Fusion (LPBF) Ti-6Al-4V alloy for structurally critical load-bearing components is limited. One of the main limiting factors affecting the structural integrity, are manufacturing defects. Additionally, the high cooling rates associated with LPBF process result in the formation of large residual stress (RS) with complex fields. Such RS can cause cracking and geometrical distortions of the part even right after production. Also, the microstructure of LPBF Ti-6Al-4V in the as-built condition is significantly different from that of the conventionally produced alloy. All these factors affect the mechanical behavior of the material. Therefore, to improve the material performance it is important to evaluate the individual effect of RS, defects, and microstructure on fatigue life. To this aim Ti-6Al-4V LPBF material in as-built condition and subjected to different post-processing, including two heat treatments (for stress relief and microstructural modification) and Hot Isostatic Pressing (HIP, for densification), were investigated. Prior to Low Cycle Fatigue (LCF) tests at operating temperature (300°C), the microstructure (phases, crystallographic texture, and grain morphology), the mesostructure (defect shape and distribution), and subsurface RS on the LCF samples were investigated. It was found that the fatigue performance of HIPped samples is similar to that of conventionally produced Ti-6Al-4V. The tensile RS found at the surface of as-built samples decreased the fatigue life compared to heat-treated samples. Additionally, the modification of the microstructure (by heat treatment) did not affect the fatigue performance in the regime of mostly elastic strain. This shows that in the absence of tensile RS the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. T2 - ASTM ICAM 2020 CY - Online meeting DA - 16.11.2020 KW - Additive manufacturing KW - Ti-6Al-4V KW - Computed tomography KW - Residual stress PY - 2020 AN - OPUS4-51695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Diffraction based residual stress analysis for laser powder bed fusion alloys N2 - Laser Powder Bed Fusion (PBF-LB/M) is a layer wise metal additive manufacturing (AM) technology, which enables significant advancements of component design, leading to potential efficiency and performance improvements. However, the thermal cycles inherent to the process comprising large localized thermal gradients and repeated melting and solidification cycles leads to the generation of high magnitude residual stresses. These residual stresses can be detrimental both during manufacturing of components and in subsequent application. Therefore, a deep understanding of the influence of process parameters on the residual stresses are crucial for efficient manufacturing and safe application. The experimental characterization of these residual stresses is therefore crucial and can provide a reliable baseline for simulations of both the process and applications. Diffraction-based methods for residual stress analysis using penetrating neutrons and high energy X-rays enable non-destructive spatially resolved characterization of both surface and bulk residual stresses. However, the unique microstructural features inherent to the process can challenge some of our assumptions when using these methods. These challenges include the determination of a stress-free reference, the use of correct elastic constants (both SCEC and DEC) and the influence of surface roughness, texture, and porosity on residual stresses. This presentation will detail recent insights and recommendations for the characterization of residual stresses in a range of PBF-LB/M metallic alloys (Fe, Ni, Al and Ti) T2 - 11th edition of the European Conference on Residual Stress (ECRS11) CY - Prague, Czech Republic DA - 03.06.2024 KW - Residual stress KW - Additive manufacturing KW - Laser Powder Bed Fusion KW - Diffraction PY - 2024 AN - OPUS4-60443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Mishurova, Tatiana A1 - Serrano-Munoz, Itziar A1 - Ulbricht, Alexander A1 - Fritsch, Tobias A1 - Sprengel, Maximilian A1 - Evans, Alexander A1 - Kromm, Arne A1 - Madia, Mauro ED - Bruno, Giovanni T1 - A Critical Discussion on the Diffraction-Based Experimental Determination of Residual Stress in AM Parts N2 - As opposed to reviewing results on experimental determination of residual stress by diffraction, this paper discusses the open issues when dealing with residual stress determination in additive manufactured parts, in particular those manufactured with laser powder bed fusion techniques. Three points are addressed in detail: (a) the proper determination of the strain-free reference d0, (b) the problem of the determination of the principal axes, and (c) the use of the correct diffraction elastic constants. It is shown that all methods to determine the strain-free reference d0 suffer from caveats, and care must be taken in evaluating the most suitable for the problem being tackled. In addition, it is shown that, in some systems, the principal axes do correspond to the geometrical axes of the specimen, but this needs to be systematically checked, especially in the case of uni- or bidirectional hatching strategies. Finally, the need to experimentally determine the proper diffraction elastic constants is underlined, especially in the case of strongly textured specimens, which again depends on the deposition strategy. T2 - ASTM ICAM 2020 – ASTM International Conference on Additive Manufacturing CY - Online meeting DA - 16.11.2020 KW - Additive Manufacturing KW - Diffraction KW - Residual Stress PY - 2020 DO - https://doi.org/10.1520/STP163120190148 VL - STP1631 SP - 122 EP - 138 PB - ASTM International CY - USA AN - OPUS4-51347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sprengel, Maximilian T1 - Using Neutron Diffraction to Monitor Stress Relaxation in Additively Manufactured 316L N2 - The relaxation of residual stress in laser powder bed fused stainless steel 316L parts was monitored using monochromatic and time-of-flight neutron diffraction. T2 - ISIS student meeting CY - Online meeting DA - 26.10.2020 KW - Stainless Steel KW - Residual Stress KW - Additive Manufacturing PY - 2020 AN - OPUS4-51469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano-Munoz, Itziar T1 - Influence of the scanning strategy on the residual stress state in IN718 additive manufactured parts N2 - Laser Powder Bed Fusion (L-PBF) is an additive manufacturing technique enabling the design of complex geometries that are unrivalled by conventional production technologies. Nevertheless, L-PBF process is known to induce a high amount of residual stresses (RS) due to the high temperature gradients present during powder melting by laser. High tensile residual stresses are to be found the edges whereas the bulk material shows balancing compressive RS. Literature shows that the RS is highly sensitive to the process parameters. In particular, this study presents the characterization of the RS state in two L-PBF parts produced with a rastering scan vector that undergoes 90° or 67° rotation between subsequent layers. T2 - MLZ User Meeting 2020 CY - Online meeting DA - 08.12.2020 KW - Laser Powder Bed Fusion KW - IN718 KW - EBSD analysis KW - Residual stress state PY - 2020 AN - OPUS4-51821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni T1 - Assessing the safety of new technologies: Summary of Project AGIL N2 - In Additive Manufacturing everybody is talking about Free Form, Unconventional Design, Re-thinking Components, “Think out of the box”. However, there are a few outstanding question: a) What are the material properties ? They certainly differ from literature values for conventional materials; b) How about the microstructure? It is different from conventional materials. Does it stay so with ageing? How does it form? c) Do we properly take residual stress into account? We often blame them for our ignorance about failure scenarios. d) Do we apply tailored heat treatments? Very often, we follow conventional schedules… This talk describes the summary of the efforts carried out within the BAM Project AGIL. At BAM, we aimed to thoroughly investigate the microstructure and how it evolves as a function of load and temperature (service), to determine the material properties after different process and service conditions, to properly determine residual stress and the way it impacts mechanical properties and component performance, to properly quantify the impact of (unavoidable?) defects, and to determine heat treatments tailored to the process-specific material (stress relieve, microstructure homogenization etc.). The Project AGIL was and is intimately coupled with the project ProMoAM, dealing with online monitoring of AM processes. T2 - Workshop In-situ Monitoring and Microstructure Development in Additive Manufactured Alloys CY - Online meeting DA - 19.04.2021 KW - Mechanical properties KW - Additive manufacturing KW - Residual Stress KW - Microstructure KW - Fatigue KW - Creep PY - 2021 AN - OPUS4-52581 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishurova, Tatiana A1 - Evsevleev, Sergei A1 - Artzt, K. A1 - Haubrich, J. A1 - Sevostianov, I. A1 - Requena, G. A1 - Bruno, Giovanni T1 - Micromechanical behavior of annealed Ti-6Al-4V produced by Laser Powder Bed Fusion N2 - The micromechanical behavior of an annealed Ti-6Al-4V material produced by Laser Powder Bed Fusion was characterized by means of in-situ synchrotron X-ray diffraction during a tensile test. The lattice strain evolution was obtained parallel and transversal to the loading direction. The elastic constants were determined and compared with the conventionally manufactured alloy. In the plastic regime, a lower plastic anisotropy exhibited by the lattice planes was observed along the load axis (parallel to the building direction) than in the transverse direction. Also, the load transfer from α to β phase was observed, increasing global ductility of the material. The material seems to accumulate a significant amount of intergranular strain in the transverse direction. KW - Additive manufacturing KW - Ti-6Al-4V KW - Anisotropy KW - Intergranular strain KW - Synchrotron X-ray diffraction PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-547406 DO - https://doi.org/10.1080/26889277.2022.2063763 VL - 2 IS - 1 SP - 186 EP - 201 PB - Taylor & Francis AN - OPUS4-54740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fardan, Ahmed A1 - Fazi, Andrea A1 - Schröder, Jakob A1 - Mishurova, Tatiana A1 - Deckers, Tobias A1 - Bruno, Giovanni A1 - Thuvander, Matthias A1 - Markström, Andreas A1 - Brodin, Hakan A1 - Hryha, Eduard T1 - Microstructure tailoring for crack mitigation in CM247LC manufactured by powder bed fusion – Laser beam N2 - Tailored microstructures in powder bed fusion – laser beam (PBF-LB) can aid in crack mitigation of non-weldable Ni-base superalloys such as CM247LC. This study explores the effect of a range of stripe widths from 5 mm down to 0.2 mm to control solidification cracking, microstructure, and residual stress in CM247LC manufactured by PBF-LB. The decrease in melt pool depth with the reduction in stripe width from 5 to 0.2 mm promoted the < 100 > crystallographic texture along the build direction. The crack density measurements indicated that there is an increase from 0.62 mm/mm2 (5 mm) to 1.71 mm/mm2 (1 mm) followed by a decrease to 0.33 mm/mm2 (0.2 mm). Atom probe tomography investigations at high-angle grain boundaries revealed that there is higher Hf segregation in 0.2 mm stripe width when compared to 5 mm. This indicates that the cracking behavior is likely influenced by the grain boundary segregation which in turn is dependent on melt pool shape/size and mushy zone length indicated by accompanying simulations. Residual stress, measured by X-ray diffraction, decreased from 842 MPa (5 mm) to 690 MPa (1 mm), followed by an abnormal rise to 842 MPa (0.7 mm) and 875 MPa (0.5 mm). This residual stress behavior is likely associated with the cracks acting as a stress relief mechanism. However, the 0.2 mm stripe width exhibited the lowest stress of 647 MPa, suggesting a different mechanism for stress relief, possibly due to re-melting. These findings highlight the critical role of stripe width as a scan strategy in PBF-LB processing of crack-susceptible alloys. KW - Additive manufacturing KW - Residual stress KW - Scanning strategy KW - Non-weldable superalloy KW - Solidification cracking PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624606 DO - https://doi.org/10.1016/j.addma.2025.104672 SN - 2214-7810 VL - 99 SP - 1 EP - 14 PB - Elsevier B.V. AN - OPUS4-62460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Chand, Keerthana A1 - Fritsch, Tobias A1 - Hejazi, Bardia A1 - Poka, Konstantin A1 - Bruno, Giovanni T1 - Deep Learning Based 3D Volume Correlation for Additive Manufacturing Using High-Resolution Industrial X-Ray Computed Tomography N2 - Quality control in Additive Manufacturing (AM) is vital for industrial applications in areas such as the automotive, medical, and aerospace sectors. Geometric inaccuracies caused by shrinkage and deformations can compromise the life and performance of additively manufactured components. Such deviations can be quantified using Digital Volume Correlation (DVC), which compares the Computer-Aided Design (CAD) model with the X-ray Computed Tomography (XCT) geometry of the components produced. However, accurate registration between the two modalities is challenging due to the absence of a ground truth or reference deformation field. In addition, the extremely large data size of high-resolution XCT volumes makes computation difficult. In this work, we present a deep learning-based approach for estimating voxel-wise deformations between CAD and XCT volumes. Our method uses a dynamic patch-based processing strategy to handle high-resolution volumes. In addition to the Dice score, we introduce a Binary Difference Map (BDM) that quantifies voxel-wise mismatches between binarized CAD and XCT volumes to evaluate the accuracy of the registration. Our approach shows a 9.2% improvement in the Dice score and a 9.9% improvement in the voxel match rate compared to classic DVC methods, while reducing the interaction time from days to minutes. This work sets the foundation for deep learning-based DVC methods to generate compensation meshes that can then be used in closed-loop correlations during the AM production process. Such a system would be of great interest to industry, as it would make the manufacturing process more reliable and efficient, saving time and material. KW - Deep learning PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-646293 DO - https://doi.org/10.3233/FAIA251475 SN - 0922-6389 VL - 413 SP - 5368 EP - 5375 PB - IOS Press AN - OPUS4-64629 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Hejazi, Bardia A1 - Chand, Keerthana A1 - Fritsch, Tobias A1 - Bruno, Giovanni T1 - D-CNN and VQ-VAE Autoencoders for Compression and Denoising of Industrial X-Ray Computed Tomography Images N2 - The ever-growing volume of data in imaging sciences stemming from advancements in imaging technologies, necessitates efficient and reliable storage solutions for such large datasets. This study investigates the compression of industrial X-ray computed tomography (XCT) data using deep learning autoencoders and examines how these compression algorithms affect the quality of the recovered data. Two network architectures with different compression rates were used, a deep convolution neural network (D-CNN) and a vector quantized variational autoencoder (VQ-VAE). The XCT data used was from a sandstone sample with a complex internal pore network as a good test case for the importance of feature preservation. The quality of the decoded images obtained from the two different deep learning architectures with different compression rates were quantified and compared to the original input data. In addition, to improve image decoding quality metrics, we introduced a metric sensitive to edge preservation, which is crucial for three-dimensional data analysis. We showed that different architectures and compression rates are required depending on the specific characteristics needed to be preserved for later analysis. The findings presented here can aid scientists in determining the requirements and strategies needed for appropriate data storage and analysis. T2 - 28th European Conference on Artificial Intelligence – Including 14th Conference on Prestigious Applications of Intelligent Systems (PAIS 2025) CY - Bologna, Italy DA - 25.10.2025 KW - Data Compression KW - Deep Learning KW - X-ray Computed Tomography PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-644758 UR - https://ebooks.iospress.nl/doi/10.3233/FAIA251480 DO - https://doi.org/10.3233/FAIA251480 SN - 0922-6389 SP - 1 EP - 8 PB - IOS Press AN - OPUS4-64475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishurova, Tatiana A1 - Fritsch, Tobias A1 - Jahn, Anne A1 - Pavasaryte, Lina A1 - Bruno, Giovanni T1 - Quantitative surface quality evaluation by X-ray Computed Tomography N2 - The poor surface quality is one of the challenges in powder based additive manufacturing (AM) techniques. It limits the application of the components in as-manufactured condition and requires the post-processing machining techniques, increasing costs and diminishing the advantage of the free form fabrication. It is important to characterize the surface roughness of the part as it might affect the tolerances and the mechanical behavior of the material. For the AM components the usage of classic characterization techniques becomes very challenging and even impossible, when internal channels, fine and complex shapes structures are under investigation. In such cases, X-ray Computed Tomography (XCT) is the only tool to evaluate the structure inside nondestructively. In this work, the application of surface quality analysis workflow using high-resolution XCT is presented. The analysis of surface topography includes the quantitative characterization of “re-entrant” surface features. This characterization is based on the evaluation of the triangulated surface generated based on the XCT data and was compared with conventional surface roughness parameters (e.g., Sa and Sz). The strength of the presented workflow is the application on arbitrary surfaces without geometrical limitations allowing real as-build investigation. This will be discussed on the example of both, simple cylindrical struts to present the principals, and the application to the Triply Periodic Minimal Surface (TPMS) structures. The analysis of the struts allows conclusions about the influence of down-skin and up-skin on surface quality. The results indicate that the surface quality is a factor of 2 worse for a build angle of 30° compared to an up-right build (90°). The investigation of TPMS structures is focused on the optimization of process parameter of geometrically complex samples regarding the surface quality. The challenge was an automated and user-independent comparison of several TPMS structures. The correlation of surface quality with process parameters (e.g., Laser power, laser velocity) is presented. T2 - ASTM ICAM 2024 CY - Atlanta, GA, USA DA - 28.10.2024 KW - Additive manufacturing KW - X-ray CT KW - Surface texture PY - 2024 AN - OPUS4-61515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Eddah, Mustapha T1 - Synchrotron Multi-energy HDR tomography for LTCC systems N2 - LTCCs (Low-temperature co-fired ceramics) consist of three-dimensionally distributed, hermetically bonded ceramic and metallic components with structure sizes within [10; 100] µm. A non-destructive imaging technique is needed that provides 3D, sharp, high-contrast resolution of these structures, as well as porosity and defect analysis, which is made difficult by the very different X-ray absorption coefficients of the individual components of the microstructure. A HDR method is being developed that allows a combination of different tomograms, each with X-ray energies adapted to individual materials. T2 - Bessy II User Meeting CY - Berlin, Germany DA - 22.06.2023 KW - LTCC KW - Synchrotron tomography KW - Data fusion KW - In-situ tomography PY - 2023 AN - OPUS4-57795 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Mishurova, Tatiana T1 - Influence of residual stress and microstructure on mechanical performance of LPBF TI-6AL-4V N2 - Additive manufacturing technologies provide unique possibilities in the production of topologically optimized, near-net shape components. The main limiting factors affecting the structural integrity of Laser Powder Bed Fusion (LPBF) parts are manufacturing defects and residual stress (RS) because both of them are virtually inevitable. Taking into account the complex thermal history of LPBF materials, a prediction of the material behavior is not possible without experimental data on the microstructure, defect distribution, and RS fields. Therefore, this thesis aims to understand the factors that influence the LPBF Ti-6Al-4V material performance the most, covering both the production and the post-processing steps of manufacturing. Indeed, a parametric study on the influence of manufacturing process and post-processing on RS, defects and microstructure was performed. It was found that the volumetric energy Density (EV), commonly used for the LPBF process optimization, does neither consider the pore shapes and distribution, nor the influence of individual parameters on the volume fraction of pores. Therefore, it was recommended not to use EV without great care. It was shown that the Position on the base plate has a great impact on the amount of RS in the part. The micromechanical behavior of LPBF Ti-6Al-4V was also studied using in-situ Synchrotron X-ray diffraction during tensile and compression tests. Diffraction elastic constants (DEC), connecting macroscopic stress and (micro) strain, of the LPBF Ti-6Al-4V showed a difference from the DEC of conventionally manufactured alloy. This fact was attributed to the peculiar microstructure and crystallographic texture. It was therefore recommended to determine experimentally DECs whenever possible. Low Cycle Fatigue (LCF) tests at a chosen operating temperature were performed to evaluate the effect of post-treatment on the mechanical performance. Through the information on the microstructure, the mesostructure, and the RS, the LCF behavior was (indirectly) correlated to the process parameters. It was found that the fatigue performance of LPBF samples subjected to hot isostatic pressing is similar to that of hot-formed Ti-6Al-4V. The tensile RS found at the surface of LPBF as-built samples decreased the fatigue life compared to the heat-treated samples. The modification of the microstructure (by heat treatment) did not affect the Fatigue performance in the elastic regime. This shows that in the absence of tensile RS, the manufacturing defects solely control the failure of LPBF components and densification has the strongest effect on the improvement of the mechanical performance. KW - Additive manufacturing KW - Ti-6Al-4V KW - Residual stress KW - Computed tomography PY - 2021 SP - 1 EP - 143 CY - RWTH Aachen AN - OPUS4-54389 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Bruno, Giovanni ED - Makul, Matt T1 - Investigation of a New Ti Alloy for a New Generation of Additively Manufactured Implants with Lattice N2 - A new titanium alloy improving the operation of implants additively manufactured and including laterally closed lattice structures is proposed. The new alloy possesses an increased affinity to the bone. The measured bone–interface implant (BII) of less than 10 mm and bone–implant contact (BIC) of 95% demonstrated an excellent osseointegration. Furthermore, since additive manufacturing naturally leads to a high-roughness surface finish, the wettability of the implant is increased. The combination of these factors is pushing ossification beyond its natural limits. In addition, the quality and speed of the ossification and osseointegration in/around laterally closed lattice implants open the possibility of bone spline key of prostheses. This enables the stabilization of the implant into the bone while keeping the possibility of punctual hooks allowing the implant to be removed more easily if required. KW - X-ray Computed tomography KW - Defects KW - Machine Learning KW - Implants KW - Lattices PY - 2024 DO - https://doi.org/10.9734/bpi/cpstr/v7/7198E VL - 7 SP - 12 EP - 37 AN - OPUS4-59754 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Residual Stresses in Additive Manufacturing (L-PBF) N2 - Metal Additive manufacturing (AM) technologies such as Laser Powder Bed Fusion (LPBF) enable the fabrication of complex structures, giving rise to potential improvements in component and manufacturing efficiency. However, the processes are typically characterized by the generation of high magnitude residual stress (RS) which can have detrimental consequences for subsequent applications. Therefore, the characterization of these RS fields and the understanding of their formation and mitigation through optimized processing is crucial for the wider uptake of the technology. Due to the potential complex nature and high value of components manufactured by LPBF, it is important to have suitable characterisation methods which can determine the spatial variations of RS in a non-destructive manner. Neutron diffraction is considered to be the best suited for these requirements. However, the microstructures developed in the complex thermal cycles experience in the production can pose challenges to the ND method for RS analysis. The BAM has conducted significant research over the past years to overcome these obstacles, enabling higher confidence in the RS determined in LPBF materials by neutron diffraction. This contribution will overview some of these advancements made recently at European neutron sources including on Stress-Spec at FRM2/MLZ. T2 - MLZ User Meeting 2021 CY - Online meeting DA - 07.12.2021 KW - Residual stress KW - Additive manufacturing KW - Diffraction KW - AGIL KW - Manufact PY - 2021 AN - OPUS4-54044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano-Munoz, Itziar T1 - Influence of the scanning strategy on the RS state of a LPBF IN718 material N2 - For metal-based additive manufacturing (AM) to achieve leaner designs and enable longer life predictions, it is imperative to gain a detailed knowledge of the residual stress (RS) built-up. Laser powder bed fusion (LPBF) is an AM technique particularly prone to RS because of the highly localized heat source, extremely high cooling rates (in the order of 103-107 K/s), and successive cooling and heating cycles of the solidified material. Furthermore, RS analysis of LPBF materials by diffraction methods is peculiar because of the complexity of the thermal history, the possibility of encountering high levels of surface roughness, spatial textural variations and/or changes in solute concentrations at the component scale. Diverse aspects of the influence of scanning strategies on the as-built residual stress state of a LPBF IN718 alloy will be presented, with particular focus on the challenges that AM microstructures pose for a reliable RS determination. T2 - MECASENS 2021 CY - Prague, Czech Republic DA - 25.11.2021 KW - Laser Powder Bed Fusion KW - IN718 KW - Residual stress analysis PY - 2021 AN - OPUS4-53875 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Voloskov, Boris A1 - Mishurova, Tatiana A1 - Evlashin, Stanislav A1 - Firsov, Denis A1 - Bruno, Giovanni A1 - Sergeichev, Ivan T1 - Influence of scanning strategy and hatch distance on porosity and mechanical characteristics of 316L stainless steel produced by laser powder bed fusion N2 - The effect of scanning strategies and hatch distances on the porosity and mechanical properties of 316L stainless steel produced by laser powder bed fusion (PBF-LB) is studied. Two scanning strategies were analyzed along with three hatch distances (50 μm, 80 μm, and 110 μm). Using X-ray computed tomography (XCT), the study revealed different defect distributions: 90° alternating hatch scanning strategy resulted in a higher number of lack of fusion defects, while the chessboard strategy produced smaller, more uniformly distributed gas pores. The optimal hatch distance of 80 μm was found to minimize porosity and maximize tensile strength for both strategies. Mechanical testing supported these findings, showing that specimens printed with an 80 μm hatch distance exhibited better mechanical characteristics. This study highlights the critical role of scanning parameters in the quality and reliability of additively manufactured parts. KW - X-ray computed tomography KW - Additive manufacturing KW - Porosity PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621164 DO - https://doi.org/10.1016/j.prostr.2024.11.045 SN - 2452-3216 VL - 65 SP - 302 EP - 309 PB - Elsevier B.V. AN - OPUS4-62116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Serrano-Munoz, Itziar T1 - Synchrotron X-Ray Refraction during in-situ heat treatments N2 - For the first time, synchrotron X-ray refraction radiography (SXRR) has been paired with in-situ heat treatment to monitor microstructure and porosity evolution as a function of temperature. T2 - HZB User Meeting 2021 CY - Online meeting DA - 09.12.2021 KW - Synchrotron refraction radiography KW - Laser powder bed fusion KW - AlSi10Mg alloy KW - In-situ heat treatment KW - Porosity growth PY - 2021 AN - OPUS4-53973 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kang, M. T1 - Influence of mica particle content in composites for high voltage applications produced by additive manufacturing and mold casting N2 - The insulation system of high voltage electrical devices like generators and electrical motors has to withstand thermal, electrical, ambient and mechanical influences (TEAM) during operation. Especially the dielectric properties have to satisfy the requirements also under elevated temperatures and extreme environments. To provide this high quality, the conventional fabrication process uses partly manually applied insulation tapes combined with a cost-intensive and under safety concerns at least problematic vacuum pressure impregnation step (VPI). In order to reduce process costs by increasing the degree of automation and avoiding the VPI process, additively manufactured (AM) insulations were studied. This study focuses on the fabrication of ceramic/polymer compounds via AM technique. The AM technology used a rotating screw extrusion print head with air pressure to supply the paste. Plate-like samples with dimensions of 55 mm x 55 mm x1mm thickness were produced. This work focuses on the homogeneously high viscous paste with 12.5 to 50 volume % ratio of filler particles. Three types of mica powders as ceramic filler materials with different particle sizes from micro to mm scale were evaluated. The controlled volume % ratio of particles affects the paste viscosity which enables stacking of paste layers with a viscosity close to clay pastes. The mixed pastes were cured by heating and UV light to increase mechanical properties. A TG/DTA was performed, and electrical properties were investigated. First experiments with respect to the dielectric properties such as volume resistance, permittivity and dielectric strength revealed promising results and the possibility to use AM techniques for the fabrication of high voltage insulations for electrical machines. T2 - MaterialsWeek 2021 CY - Online meeting DA - 07.09.2021 KW - HV-Insulation KW - Polymer-Ceramic-Composite KW - Additive manufacturing PY - 2021 AN - OPUS4-54368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stargardt, Patrick T1 - Dielectric properties of plasma sprayed coatings for insulation application N2 - Thermal spraying provides a rapid method for additive deposition of various ceramics as electrical insulation in applications where polymers are not suitable. New applications in complex shaped additive manufactured metal parts are emerging for example in large scale electrical devices. Microstructural and dielectric evaluation of coatings is crucial to the employment of such free-form processes. The properties and microstructure of the plasma sprayed alumina coatings are compared with dense reference samples of the same powder produced by spark plasma sintering (SPS). To obtain dense bulk samples from the coarse alumina powder for spray coating, SPS is used. Samples are fabricated by atmospheric plasma spraying (APS) of commercially available alumina powder (d50 = 33 µm) on copper substrates and by SPS of the same powder. Microstructure and porosity were analyzed by optical microscopy and scanning electron microscopy (SEM). Phase compositions were determined by X-ray diffraction (XRD). Dielectric properties such as DC resistance, dielectric strength, dielectric loss, and relative permittivity were determined according to the standards. The microstructure and dielectric properties of the coating and bulk material are compared to assess whether the coating is suitable for use in electrical insulation application. T2 - Ceramics in Europe 2022 CY - Krakow, Poland DA - 10.07.2022 KW - Dielectric characterization KW - Atmospheric plasma spraying KW - Spark plasma sintering KW - Electrical insulation PY - 2022 AN - OPUS4-55328 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Creep and fracture behavior of conventionally and additively manufactured stainless steel 316L N2 - A critical task within the frame of establishing process-structure-property-performance relationships in additive manufacturing (AM) of metals is producing reliable and well-documented material behavior’s data and knowledge regarding the structure-property correlation, including the role of defects. After all, it represents the basis for developing more targeted process optimizations and more reliable predictions of performance in the future. Within this context, this contribution aims to close the actual gap of limited historical data and knowledge concerning the creep behavior of the widely used austenitic stainless steel 316L, manufactured by Laser-Powder-Bed-Fusion (L-PBF). To address this objective, specimens from conventional hot-rolled and AM material were tested under application-relevant conditions according to existing standards for conventional material, and microstructurally characterized before and after failure. The test specimens were machined from single blocks from the AM material. The blocks were manufactured using a standard scan and build-up strategy and were subsequently heat-treated. The creep behavior is described and comparatively assessed based on the creep lifetime and selected creep curves and characteristic values. The effect of defects and microstructure on the material’s behavior is analyzed based on destructive and non-destructive evaluations on selected specimens. The AM material shows shorter creep lives, reaches the secondary creep stage much faster and at a lower strain, and features lower creep ductility compared to its conventional counterpart. The creep damage behavior of the AM material is more microstructure than defect controlled and is characterized by the formation and accumulation of single intergranular damage along the whole volume. Critical features identified are the grain morphology and the grain-boundary as well as the dislocation’s density. Micro-computed tomography (µCT) proves to be an alternative to metallography to analyze the creep damage. T2 - ASTM International Conference on Additive Manufacturing 2020 CY - Online meeting DA - 16.11.2020 KW - 316L KW - Creep behavior KW - Laser powder bed fusion KW - Additive manufacturing KW - Microstructure PY - 2020 AN - OPUS4-51823 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Assessing the low cycle fatigue behaviour of additively manufactured Ti-6Al-4V: Challenges and first results N2 - The understanding of process-microstructure-property-performance (PMPP) relationships in additive manufacturing (AM) of metals is highly necessary to achieve wide-spread industrial application and replace conventionally manufactured parts, especially regarding safety-relevant applications. To achieve this understanding, reliable data and knowledge regarding material’s microstructure-property relationships (e.g. the role of defects) is needed, since it represents the base for future more targeted process optimizations and more reliable calculations of performance. However, producing reliable material data and assessing the AM material behaviour is not an easy task: big challenges are e.g. the actual lack of standard testing methods for AM materials and the occasional difficulties in finding one-to-one comparable material data for the conventional counterpart. This work aims to contribute to end this lack of reliable material data and knowledge for the low cycle fatigue behaviour of the most used titanium alloy in aerospace applications (Ti-6Al-4V). For this purpose, two sets of test specimens were investigated. The first set was manufactured from cylindrical rods produced by an optimized DED-L process and the second was manufactured from a hot formed round bar. The test specimens were cyclically loaded until failure in the low-cycle-fatigue (LCF) regime. The tests were carried out according to ISO 12106 between 0.3 to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behaviour is described and compared between materials and with literature values based on cyclic deformation curves and strain-based fatigue life curves. Besides, the parameters of Manson-Coffin-Basquin relationship were calculated. The microstructures (initial and after failure) and fracture surfaces were comparative characterized. Thereby, the focus lied on understanding the role of grain morphology and defects on the failure mechanisms and fatigue lifetimes. For this latter characterization, optical microscopy (OM), scanning electron microscopy (SEM) and micro computed tomography (µCT) were used. T2 - 4th International Symposium on Fatigue Design and Material Defects CY - Online meeting DA - 26.05.2020 KW - Ti-6Al-4V KW - Additive manufacturing KW - Low cycle fatigue KW - Micro computed tomography KW - Microstructure PY - 2020 AN - OPUS4-50893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Charmi, Amir T1 - A multiscale numerical framework for the simulation of anistropic material response of additively manufactured stainless steel 316L undergoing large plastic deformation N2 - Additive manufacturing (AM) offers significantly greater freedom of design compared to conventional manufacturing processes since the final parts are built layer by layer. This enables metal AM, also known as metal 3D printing, to be utilized for improving efficiency and functionality, for the production of parts with very complex geometries, and rapid prototyping. However, despite many technological advancements made in recent years, several challenges hinder the mass adoption of metal AM. One of these challenges is mechanical anisotropy which describes the dependency of material properties on the material orientation. Therefore, in this work, stainless steel 316L parts produced by laser-based powder bed fusion are used to isolate and understand the root cause of anisotropy in AM parts. Furthermore, an efficient and accurate multiscale numerical framework is presented for predicting the deformation behavior of actual AM parts on the macroscale undergoing large plastic deformations. Finally, a novel constitutive model for the plastic spin is formulated to capture the influence of the microstructure evolution on the material behavior on the macroscale. KW - Additive Fertigung KW - Austenitischer Stahl KW - Finite-Elemente-Methode KW - Mehrskalenmodell KW - Simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:gbv:wim2-20240207-173356-002 DO - https://doi.org/10.25643/dbt.59550 SP - 1 EP - 163 PB - Bauhaus-Universität Weimar CY - Weimar AN - OPUS4-59511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sprengel, Maximilian T1 - Towards the optimization of post laser powder bed fusion stress relieve treatments of stainless steel 316L N2 - The formation of high magnitude residual stresses is inherent in laser powder bed fused processed austenitic steel 316L. Post-process heat treatments to relieve these stresses are necessary. In this study, heat treatment temperatures of 450°C, 800°C and 900°C were applied in order to avoid excessive sensitization. This temperature range thereby encompassed the upper and lower bounds for stress relieving treatment of this material. The residual stresses were determined by neutron diffraction and the evolution of the microstructure was monitored using scanning electron microscopy and electron backscattered diffraction. The results show that a full relaxation of the residual stresses is achieved when applying 900°C for 1 hour, which seems to be closely related to the dissolution of the subgrain solidification cellular structure. T2 - 2nd Workshop on In-situ Monitoring and Microstructure Development in Additive Manufacturing CY - Online meeting DA - 19.04.2021 KW - Residual Stress KW - Additive Manufacturing KW - Steel PY - 2021 AN - OPUS4-52709 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas T1 - Wire arc additive manufacturing of high strength AL-MG-SI alloys N2 - Gas metal arc-based direct energy deposition (DED) additive manufacturing technologies hold significant promise for producing large-scale metal components. However, determining optimal process parameters to achieve the desired near-net shape design and mechanical performance is a complex challenge due to the intricate interplay between process parameters and material properties. This presentation highlights the use of a newly developed solid welding wire doped with TiB to improve grain refinement in metals deposited via DED-Arc for high-strength precipitation-hardening AlMgSi aluminum alloys. This wire stems from our initial metallurgical investigations into grain refinement in aluminum weld metals. The research emphasizes the relationship between process parameters and component quality, aiming to uncover the mechanisms that influence performance. This is essential for establishing a reliable range of parameters that meet quality standards, many of which are derived from traditional welding practices. Component quality was assessed by studying pore size, pore distribution, and grain morphology. To further enhance the mechanical properties of the deposited material, post-weld heat treatments—including solution treatment, quenching, and artificial aging—were applied. The study also explores how different heat treatment strategies affect the final mechanical properties. To validate the feasibility of 3D printing high-strength aluminum alloys, a more complex demonstrator component was fabricated. The results demonstrate that DED-Arc technology can produce large aluminum parts with a quality comparable to subtractive manufacturing techniques. Furthermore, the entire additive manufacturing workflow has been digitally integrated, enabling full traceability of all key process steps. This digital integration is critical for ensuring reliable quality assessments of the finished components. T2 - 77th IIW Annual Assembly and International Conference Joint Meeting of C-I, C-IV, and C-XII CY - Rhodos, Greece DA - 07.07.2024 KW - DED-Arc KW - High-strength aluminium alloys KW - Porosity assessment KW - Component testing KW - CT-analyses PY - 2024 AN - OPUS4-62014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stargardt, Patrick T1 - Bulk vs thermal sprayed alumina for insulation applications: A comparison of electrical and dielectrical properties N2 - Additive manufacturing (AM) processes are opening new design possibilities for large scale electrical devices such as power generators. Conventional manufacturing methods use copper rods which are wrapped, vacuum impregnated, bend and welded. These processes are labor-intensive and time-consuming. The introduction of AM methods for manufacturing the copper conductor and electrical insulation can reduce the size of the generator head, the most complex part of the generator. In this study, the electrical and dielectrical properties of additively deposited ceramic layers are investigated and compared with the properties of conventionally fabricated bulk ceramics. The ceramic layers are thermally deposited by atmospheric plasma spraying of a commercially available alumina powder. Bulk ceramics are fabricated by dry pressing and sintering of the same powder. Microstructure and porosity were analyzed by scanning electron microscopy (SEM). Electrical and dielectrical properties such as DC resistance, dielectric strength, dielectric loss, and relative permittivity were determined according to the standards. The microstructures of sprayed and sintered alumina show significant differences with respect to grain form and porosity. The density of the bulk ceramic is lower than the density of the sprayed layer due to the coarse particle size (d50 = 33 μm). Therefore, data from dense samples of the same chemical composition but lower particle size alumina powder were used for comparison. T2 - Keramik 2022 CY - Online meeting DA - 07.03.2022 KW - High Voltage Insulation KW - Thermal Spray KW - Dielectric Spectroscopy KW - Atmospheric Plasma Spraying PY - 2022 AN - OPUS4-54446 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Laser Powder Bed Fusion: Fundamentals of Diffraction-Based Residual Stress Determination N2 - The general term additive manufacturing (AM) encompasses processes that enable the production of parts in a single manufacturing step. Among these, laser powder bed fusion (PBF-LB) is one of the most commonly used to produce metal components. In essence, a laser locally melts powder particles in a powder bed layer-by-layer to incrementally build a part. As a result, this process offers immense manufacturing flexibility and superior geometric design capabilities compared to conventional processes. However, these advantages come at a cost: the localized processing inevitably induces large thermal gradients, resulting in the formation of large thermal stress during manufacturing. In the best case, residual stress remains in the final parts produced as a footprint of this thermal stress. Since residual stress is well known to exacerbate the structural integrity of components, their assessment is important in two respects. First, to optimize process parameter to minimize residual stress magnitudes. Second, to study their effect on the structural integrity of components (e.g., validation of numerical models). Therefore, a reliable experimental assessment of residual stress is an important factor for the successful application of PBF-LB. In this context, diffraction-based techniques allow the non-destructive characterization of the residual stress. In essence, lattice strain is calculated from interplanar distances by application of Braggs law. From the known lattice strain, macroscopic stress can be determined using Hooke’s law. To allow the accurate assessment of the residual stress distribution by such methods, a couple of challenges in regard of the characteristic PBF-LB microstructures need to be overcome. This presentation highlights some of the challenges regarding the accurate assessment of residual stress in PBF-LB on the example of the Nickel-based alloy Inconel 718. The most significant influencing factors are the use of the correct diffraction elastic constants, the choice of the stress-free reference, and the consideration of the crystallographic texture. Further, it is shown that laboratory X-ray diffraction methods characterizing residual stress at the surface are biased by the inherent surface roughness. Overall, the impact of the characteristic microstructure is most significant for the selection of the correct diffraction elastic constants. In view of the localized melting and solidification, no significant gradients of the stress-free reference are observed, even though the cell-like solidification sub-structure is known to be heterogeneous on the micro-scale. T2 - 4th Symposium on Materials and Additive Manufacturing CY - Berlin, Germany DA - 12.06.2024 KW - Additive Manufacturing KW - Residual Stress KW - Electron Backscatter Diffraction KW - Laser Powder Bed Fusion PY - 2024 AN - OPUS4-60294 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pittner, Andreas T1 - Additive Manufacturing of High Strength Al-Mg-Si Alloys with DED-Arc N2 - Direct energy deposition additive manufacturing technologies that utilize an electric arc have great potential for generating large volume metal components. However, selecting process parameters that yield the desired near net shape design and requested mechanical component behavior is not a trivial task due to the complex relationship between all process parameters and material characteristics. This presentation exemplifies the application of a newly developed solid welding wire doped with TiB to enhance grain refinement in the deposited metal for additive manufacturing based on DED-Arc of high-strength precipitation hardening AlMgSi-aluminum alloys. It is worth noting that the solid wire is the result of our preliminary metallurgical studies on grain refinement in aluminum weld metal. Consequently, research focuses on the correlation between process parameters and component quality to understand the underlying mechanisms. This is crucial for evaluating a robust process parameter space that yields component quality in line with corresponding standards which are mainly taken from welding technology. Specifically, we examine component quality by analyzing pore size and distribution, as well as grain morphology. To enhance the mechanical properties of the deposited metal, a post-weld heat treatment was conducted, comprising of solution treatment, quenching, and artificial aging. The study also evaluates the effects of various heat treatment strategies on the final mechanical properties of the material. To demonstrate the applicability of 3D metal printing of high-strength aluminium alloys, a more complex demonstrator was created. It has been shown that DED-Arc can produce high-volume aluminium parts with the same quality as the corresponding subtractive processing strategy. Additionally, the entire additive manufacturing chain has been digitally integrated, enabling traceability of all relevant process steps, which is essential for reliable subsequent quality assessment. T2 - 4th Symposium on Materials and Additive Manufacturing - Additive 2024 CY - Berlin, Germany DA - 12.06.2024 KW - DED-Arc KW - High-stength aluminium alloys KW - Grain refinement KW - Quality assurance PY - 2024 AN - OPUS4-60248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Residual Stresses in Additive Manufacturing (L-PBF) N2 - Additive manufacturing (AM) technologies are experiencing an exceedingly rapid growth, driven by their potential through layer wise deposition for transformational improvements of engineering design, leading to efficiency and performance improvements. Laser Powder Bed Fusion (LPBF) is an Additive Manufacturing (AM) method which permits the fabrication of complex structures that cannot otherwise be produced via conventional subtractive manufacturing methods. Nevertheless, the rapid cooling rates associated with this process results in the formation of significant and complex residual stress (RS) fields. A large body of both experimental and simulation research has been dedicated in recent years to the control and mitigation of RS in AM. In order to validate simulations with the end goal of being able to model the residual stress state in AM components and to devise strategies for their reduction during manufacturing, experimental methods need to be able to accurately determine 3D residual stresses fields in complex geometries. Several destructive and non-destructive methods can be used to analyze the RS state, the choice of which depends on the geometry and the information required. Diffraction-based methods using penetrating neutron and synchrotron X-rays at large scale facilities offer the possibility to non-destructively spatially resolve both surface and bulk residual stresses in complex components and track their changes following applied thermal or mechanical loads. This presentation will overview the success stories of using large scale facilities by the BAM for the characterization of residual stresses in additively manufactured metallic alloys. In particular, the study of the influence of process parameters on the residual stress state and the relaxation of these stresses through heat treatment will be presented. However there remains challenges to overcome particularly of the hypotheses underlying the experimental determination of residual stresses, which will be discussed. T2 - 10th International Conference on Mechanical Stress Evaluation by Neutron and Synchrotron Radiation – MECASENS 2021 CY - Prague, Czech Republic DA - 25.11.2021 KW - Residual stress KW - Additive manufacturing KW - Diffraction KW - L-PBF KW - AGIL PY - 2021 AN - OPUS4-54105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koch, Claudia T1 - Ensuring Quality Smarter with a digital Quality Infrastructure (Mexican-German Technical Exchange) N2 - The presentation introduces the initiative QI‑Digital, which aims to holistically transform quality infrastructure across all its elements. To this end, a digital QI ecosystem is being developed that integrates digital QI tools with advanced methods for testing, inspection, and monitoring, and embeds them into the broader digital industrial ecosystem. Sovereign and secure data sharing and management are enabled through technologies such as data spaces, the Asset Administration Shell, verifiable credentials, and the Digital Product Passport (DPP). Particular emphasis is placed on the role of artificial intelligence in quality assurance: Several use cases and ongoing projects from BAM are presented togetehr with the business benefits they enable. Ongoing activities on the use of AI for manageing quality-related documentation are also presentated that aim at establishing an agentic AI framework for QI. The talk concludes with key lessons learned so far within the initiative. T2 - Mexican-German Technical Exchange on QI Digital CY - Mexico City, Mexico DA - 23.01.2026 KW - Quality infrastructure KW - Agentic AI KW - Digital Ecosystem PY - 2025 AN - OPUS4-65411 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Residual stresses and micromechanical properties of additively manufactured metals: why do we need a paradigm shift? N2 - An overview of the challenges and successes in the methodology to characherise residual stresses and micromechnical properties in additively manufactured metals T2 - CAM2 Annual Seminar 2022 - 5-year journey CY - Gothenburg, Sweden DA - 24.10.2022 KW - Additive Manufacturing KW - Residual stress KW - AGIL KW - MANUFACT KW - Micromechnical properties PY - 2022 AN - OPUS4-56466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni T1 - X-ray refraction techniques non-destructively quantify and classify defects in am materials N2 - X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, they can detect objects with size above a few wavelengths of the radiation. Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads. The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models. We hereby show the application of non-destructive X-ray refraction radiography (SXRR, 2D mapping also called topography) to problems in additive manufacturing: 1) Porosity analysis in PBF-LM-Ti64. Through the use of SXRR, we could not only map the (very sparse) porosity distribution between the layers and quantify it, but also classify, and thereby separate, the filled porosity (unmolten powder) from the keyhole and gas pores (Figure 1). 2) In-situ heat treatment of laser powder bed fusion PBF-LM-AlSi10Mg to monitor microstructure and porosity evolution as a function of temperature (Figure 2). By means of SXRR we indirectly observed the initial eutectic Si network break down into larger particles as a function of increasing temperature. We also could detect the thermally induced porosity (TIP). Such changes in the Si-phase morphology upon heating is currently only possible using scanning electron microscopy, but with a much smaller field-of-view. SXRR also allows observing the growth of some individual pores, usually studied via X-ray computed tomography, but again on much smaller fields-of-view. Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the defect distribution and the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes. T2 - AAMS 2023 CY - Madrid, Spain DA - 27.09.2023 KW - X-ray refraction radiography KW - Defects KW - Large scale facilities KW - Computed tomography PY - 2023 AN - OPUS4-58508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Residual stresses Analysis in Additively Manufactured alloys using neutron diffraction (L-PBF) N2 - An overview of recent progress at BAM of residual stress analysis in additively manufactured, in particular Laser Powder Bed Fusion of metallics materials, using neutron diffraction will be presented. This will cover important topics of the stress-free reference, the diffraction elastic moduli and principal stress determination. T2 - AWT-Fachausschuss 13 "Eigenspannungen" CY - Berlin, Germany DA - 28.03.2023 KW - AGIL KW - Residual stress KW - Additive manufacturing KW - Laser Powder Bed Fusion KW - Diffraction PY - 2023 AN - OPUS4-59177 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Evans, Alexander T1 - Diffraction based residual stress analysis: challenges and opportunities in additive manufacturing N2 - This presentation overviews the challanges and opportunities of diffraction based residual stress analysis for additively manufactured metals. Through examples, the challanges and respective solutions are presented and the opportunities that the presented methods allow are described. T2 - Workshop on Advanced Manufacturing (WAM) 2025 CY - Grenoble, France DA - 03.06.2025 KW - Residual stress KW - Diffraction KW - AGIL KW - Laser powder bed fusion KW - MANUFACT PY - 2025 AN - OPUS4-64137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Peculiarities of the determination of residual stress in additively manufactured materials N2 - The determination of residual stress in additively manufactured materials is a challenge, even after decades from the establishment of the basics of residual stress analysis. This is due to the peculiar microstructure of such materials. In fact, researchers have discovered that conventional methods for the determination of RS in materials do not properly work for AM materials. In this tutorial, the basics of RS analysis will be explained, together with the basics of AM manufacturing techniques. The microstructure of the peculiar materials (AM) dealt with here will be elucidated. Successively, the necessary modifications to the conventional approaches to RS analysis will be explained and case studies will be displayed, for the attendant to touch with hands the peculiarities of the approaches. Finally, a few experimental and theoretical tips will be given on dos and don’ts for a correct determination of RS in AM materials. T2 - 11th European Conference on Residual Stresses CY - Prague, Czech Republic DA - 03.06.2024 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Residual Stress KW - Diffraction PY - 2024 AN - OPUS4-60428 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - The heat treatment of L-PBF Inconel 718: A manyfold problem N2 - The interest to additively manufacture Nickel-based superalloys has substantially grown within the past decade both academically and industrially. More specifically, additive manufacturing processes such as laser powder bed fusion (LPBF) offer the ability to produce dense parts within a single manufacturing step. In fact, the exceptional freedom in design associated with the layer-based nature of the processes is of particular interest for the complex shapes typically required in turbine applications. In certain cases, the overall part performance can be achieved by tailoring the microstructure and the crystallographic texture to the specific application. However, these advantages must be paid at a price: the large local temperature gradients associated with the rapid melting and solidification produce parts that inherently contain large residual stress in the as-manufactured state. In addition, the presence of pores in the final part may further affect the in-service part failure. As among Nickel-based alloys Inconel 718 exhibits excellent weldability, this alloy has been widely studied in open research in the domain of LPBF. However, significant microsegregation of the heavier alloying elements such as Niobium and Molybdenum accompanied by dislocation entanglements may preclude the application of conventional heat treatment schedules. Therefore, different post processing heat treatments are required for laser powder bed fused Inconel 718 as compared to conventional variants of the same alloy. In this study, we investigated two different heat treatment routes for LPBF Inconel 718. In a first routine, the samples were stress relieved and subsequently subjected to hot isostatic pressing (HIP) followed by a solution heat treatment and a two-step age (referred to as FHT). In a second routine, the samples were subjected to a single-step direct age post stress relieving heat treatment (referred to DA). We investigated the consequences of such heat treatment schedules on the microstructure, texture, and mechanical behavior. We show that by applying a DA heat treatment the typical columnar microstructure possessing a crystallographic texture is retained, while an equiaxed untextured microstructure prevails in case of an FHT heat treatment. We further evaluate how these heat treatments affect the mechanical behaviour on the macroscopic and microscopic scale. T2 - 4th European Symposium on Superalloys and their Applications EuroSuperalloys 2022 CY - Bamberg, Germany DA - 18.09.2022 KW - Electron Backscatter Diffraction KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Mechanical Behavior KW - Heat Treatment KW - X-Ray Diffraction PY - 2022 AN - OPUS4-55811 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - On the influence of heat treatment on microstructure and mechanical behavior of laser powder bed fused Inconel 718 N2 - Since additive manufacturing processes typically introduce heterogeneous microstructures and residual stresses, the applicability of parts produced in an as-built state is limited. Therefore, often different post-processing treatments are necessary to obtain the desired stress state and properties. For additively manufactured Inconel 718, the recently developed standard ASTM F3301 provides guidance for the heat treatment of powder bed fusion specimens. Although this standard is based on standards developed for wrought Inconel 718, it does not include the direct aging variant. In this study, we characterized the microstructure and tensile behavior of Inconel 718 specimens produced by a laser powder bed fusion process. The specimens were heat-treated according to two different routines after stress relieving: a full heat treatment cycle versus a one-step aging process. Differences in the resulting texture and grain morphology were observed. Although these differences prevail, the ex-situ tensile behavior was broadly similar. Minor differences were observed in yield strength and work hardening rate for the direct aged specimen. In order to understand this behavior, investigations with in-situ tensile testing during synchrotron energy-dispersive X-ray diffraction measurements revealed differences in the load partitioning among different crystal directions. This was attributed to microstructural differences between the heat treatment variants. Further analysis emphasized that the various strengthening mechanisms are present to a different extent depending on the heat-treatment cycle applied. In addition, the elastic anisotropy expressed by the differences in the diffraction elastic constants displayed a dependence on the microstructure. Importantly, a precise knowledge of such constants is indispensable to reliably determine residual stresses in parts. T2 - EUROMAT 2021 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - Electron microscopy KW - X-ray analysis KW - Inconel 718 KW - Additive manufacturing (AM) KW - Mechanical behavior KW - Diffraction elastic constants (DECs) PY - 2021 AN - OPUS4-53301 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hejazi, Bardia A1 - Fritsch, Tobias A1 - Benz, Christopher A1 - Radtke, Lars A1 - Sander, Manuela A1 - Bruno, Giovanni T1 - In-situ very high cycle fatigue experiments of additively manufactured Ti-6Al-4V using X-ray computed tomography N2 - X-ray computed tomography (XCT) is an invaluable method for evaluating the properties and performance of components both during service and after failure in a non-destructive manner. XCT is particularly useful for the investigation of additively manufactured (AM) components, which often have production defects that are inherent to the manufacturing process, such as lack of fusion defects. Understanding the mechanisms of fatigue crack growth throughout the life cycle of such components is crucial and so to address this need, we designed and performed experiments to investigate the fatigue life and fatigue crack growth behavior of Ti-6Al-4V components under very high cycle fatigue (VHCF) testing. The titanium samples were additively manufactured with intentional internal defects to control crack initiation location. XCT of the component was carried out to identify crack initiation sites and characterize the dynamics of crack growth. The findings from this work will benefit industries that rely on the AM of titanium alloys, aiding in the improvement of component design and manufacturing processes. T2 - Alloys for additive manufacturing 2025 (AAMS 2025) CY - Neuchâtel, Switzerland DA - 02.09.2025 KW - X-ray computed tomography KW - Deep learning KW - Titanium alloy KW - Very high-cycle fatigue PY - 2025 DO - https://doi.org/10.5281/zenodo.15261296 AN - OPUS4-64096 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter T1 - Thermographic Methods for In-situ Monitoring of Metal-based Additive Manufacturing Processes N2 - Additive manufacturing (AM) with metals creates new, exciting opportunities for industrial applications. Especially industries with high relevance for the future like transport and energy benefit from optimized designs and novel materials. However, a reliable in-situ quality assurance for metal AM is still missing while process optimization is slow. This directly hinders the huge potential of metal AM technologies. A promising method to counteract this issue is the investigation of the emitted thermal radiation. It is optimal for monitoring and understanding the thermal history of the high-temperature AM process. The thermal history holds virtually all information about the properties and the quality of the manufactured components. The thermal information is also highly valuable for tuning and validating numerical simulations to gather further insights into the process. Despite this importance, the usage of thermal radiation in commercial AM machines is only marginal (like simple pyrometry or long-time exposure for optical tomography (OT) at a single wavelength). Based on this deficit and potential, this work gives an overview of the research in division “8.3 Thermographic Methods” at the Bundesanstalt für Materialforschung und -prüfung (BAM) in Berlin, Germany. Different wavelengths of the thermal radiation are investigated: the visible range (VIS), the short-wave infrared (SWIR), and the mid-wave infrared (MWIR) with their respective optimal field of application. Focus lies on laser powder bed fusion of metals (PBF-LB/M), but directed energy deposition with laser beam (DED-LB/M) is investigated as well. The presented research is performed not only on commercial AM machines, but also on an in-house developed PBF-LB/M research system specifically designed for sensor testing. This ensures an exciting mélange of applied research for industrial applications, and fundamental research for process understanding and validation. Therefore, a crucial contribution to industrial and scientific insights of metal AM is given. T2 - Sim-AM 2025 CY - Pavia, Italy DA - 09.09.2025 KW - Laser powder bed fusion KW - Direct energy deposition KW - Quality assurance KW - Infrared thermography PY - 2025 AN - OPUS4-65391 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok T1 - High Temperature Fatigue Crack Growth in Nickel-Based Alloys Refurbished by Additive Manufacturing and Brazing N2 - Hybrid additive manufacturing plays a crucial role in the restoration of gas turbine blades, where e.g., the damaged blade tip is reconstructed by the additive manufacturing process on the existing blade made of a parent nickel-based alloy. However, inherent process-related defects in additively manufactured material, along with the interface created between the additively manufactured and the cast base material, impact the fatigue crack growth behavior in bi-material components. This study investigates the fatigue crack growth behavior in bi-material specimens of nickel-based alloys, specifically, additively manufactured STAL15 and cast alloy 247DS. The tests were conducted at 950 °C with stress ratios of 0.1 and -1. Metallographic and fractographic investigations were carried out to understand crack growth mechanisms. The results revealed significant retardation in crack growth at the interface. This study highlights the potential contributions of residual stresses and microstructural differences to the observed crack growth retardation phenomenon, along with the conclusion from an earlier study on the effect of yield strength mismatch on crack growth behavior at a perpendicular interface in bi-material specimens. T2 - Superalloys 2024 Conference CY - Champion, PA, USA DA - 08.09.2024 KW - Fatigue crack growth KW - Bi-material structure KW - Nickel-based alloys KW - Additive Manufacturing KW - Brazing PY - 2024 AN - OPUS4-61047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suarez Ocano, Patricia T1 - Exploring the impact of heat treatment on room and high temperature strength of 316L stainless steel fabricated by PBF-LB N2 - Laser Powder Bed Fusion (PBF-LB/M) enables the fabrication of 316L stainless steel components with superior strength and intricate geometries. The alloy PBF-LB/M/316L features a fully austenitic microstructure with hierarchical characteristics— such as fine dislocation structures, segregated elements, low-angle grain boundaries, and nano-dispersed silicates—that enhance strength and ductility. Additionally, it includes metallurgical defects and residual stresses. Apart from process control, heat treatments (HTs) are used to tailor the microstructure for specific loading conditions. This study investigate the effects of post-processing HTs on the hierarchical microstructure and tensile properties of PBF-LB/M/316L at room and high temperature. The heat treatments, ranging from 400 °C to 900 °C for 1 to 4 hours, focus on sub-recrystallization temperatures to preserve the microstructural hierarchy. The HTs applied had minimal impact on the grain shape, size, or texture of PBF-LB/M/316L. However, significant modifications occurred in the solidification cellular substructure after HTs at 800 °C and 900 °C, when compared to a heat-treated condition at 450 °C. HTs at 800 °C notably decreased dislocation density and enlarged cellular structures, though they remained partially intact. After 1 hour at 900 °C, the cellular substructure dissipated, correlating with a further reduction in dislocation density. These microstructural changes resulted in a decreased yield strength and increased work hardening capacity at both room and high temperature, highlighting the critical link between HT parameters, microstructural evolution, and mechanical performance. T2 - The 20th International Conference on Strength of Materials (ICSMA 20) CY - Kyoto, Japan DA - 02.06.2025 KW - Additive manufacturing KW - 316L stainless steel KW - Heat treatments KW - Tensile properties KW - Microstructure PY - 2025 AN - OPUS4-63914 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Suárez Ocano, Patricia T1 - Effect of heat treatment on the hierarchical microstructure and properties of 316L stainless steel produced by Laser Powder Bed Fusion (PBF-LB/M). N2 - Laser Powder Bed Fusion (PBF-LB/M) of AISI 316L stainless steel has gained popularity due to its exceptional capacity to produce complex geometries and hierarchical microstructures, which can increase the yield strength while maintaining good ductility. Nevertheless, owing to high thermal gradients encountered during the process, the as printed 316L stainless steel often exhibit microstructural heterogeneities and residual stresses, which can limit its performance in demanding environments. Hence, employing heat treatments which balance the reduction of residual stresses while retaining improved static strength may be beneficial in various scenarios and applications. This study investigates the impact of post-processing heat treatments on the microstructure of 316L stainless steel manufactured via PBF-LB/M, along with its correlation with micro-hardness properties. To this end, 6 different heat treatments, i.e., 450 °C for 4h, 700 °C for 1h, 700 °C for 3h, 800 °C for 1h, 800 °C for 3h, and 900 °C for 1h, were applied to different specimens and Vickers hardness measurements (HV1) were performed in all states. At 800 °C, although the cellular structure appears to be retained, there is an observable increase in cellular size. However, while treatments exceeding 900 °C indicate no significant grain growth compared to other conditions, the cellular structure is entirely dissolved, which leads to a reduced Vickers hardness. The effect of the heat treatments on other microstructural features such as grain size and morphology, melt pool boundaries (MPB), crystallographic texture, chemical segregation, dispersoids and phase stability are also discussed in the present work T2 - 4th Symposium on Materials and Additive Manufacturing CY - Berlin, Germany DA - 12.06.2024 KW - Additive manufacturing KW - Heat treatment KW - Microstructure PY - 2024 AN - OPUS4-60304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rehmer, Birgit A1 - Bayram, Faruk A1 - Ávila Calderón, Luis A1 - Mohr, Gunther A1 - Skrotzki, Birgit T1 - BAM reference data: Temperature-dependent Young's and shear modulus data for additively and conventionally manufactured variants of austenitic stainless steel AISI 316L N2 - The elastic properties (Young's modulus, shear modulus) of austenitic stainless steel AISI 316L were investigated between room temperature and 900 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled sheet). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty. The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data. KW - Elastic modulus KW - Young's modulus KW - Shear modulus KW - Additive manufacturing KW - AISI 316L PY - 2023 DO - https://doi.org/10.5281/zenodo.7813835 PB - Zenodo CY - Geneva AN - OPUS4-57288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Low-cycle-fatigue behavior of stainless steel 316L manufactured by laser powder bed fusion N2 - This contribution presents the results of an experimental study on the LCF behavior of an austenitic 316L stainless steel produced by laser powder bed fusion featuring a low defect population, which allows for an improved understanding of the role of other typical aspects of a PBF‑LB microstructure. The LCF tests were performed between room temperature and 600 °C. A hot‑rolled 316L variant was tested as a reference. The mechanical response is characterized by strain-life curves, a Coffin‑Manson‑Basquin fitting, and cyclic deformation curves. The damage and deformation mechanisms are studied with X-ray computed tomography, optical and electron microscopy. The PBF‑LB/M/316L exhibits lower fatigue lives at lower strain amplitudes. The crack propagation is mainly transgranular. The solidification cellular structure seems to be the most relevant underlying microstructural feature determining the cyclic deformation behavior. T2 - TMS 2024 Annual Meeting & Exhibition CY - Orlando, Florida, US DA - 03.03.2024 KW - AGIL KW - Additive Fertigung KW - Mikrostruktur KW - LCF KW - 316L PY - 2024 AN - OPUS4-59782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beygi Nasrabadi, Hossein T1 - Nb and Cr coating the CuNi3SiCr powders for low-power laser-based powder bed fusion processing of copper alloys N2 - The laser-based powder bed fusion (PBF-LB/M) processing of high-density copper components is mainly performed with high laser powers due to the low laser absorption of copper powders [1-2]. Metal coating the copper particles has been investigated in this research as an approach for increasing the laser absorption of the feedstock and processing of highly dense copper alloys with low-power lasers. CuNi3SiCr powders were coated with the thin and uniform metallic shells of Nb (60 ± 10 nm) using a rotating Direct Current Magnetron Sputtering Physical Vapor Deposition (DCMS-PVD) reactor. Using such metal-coated particles, copper parts of 98.14% relative density were printed with the PBF-LB/M parameters of 200 W laser powers, 800 mm/s scanning speed, 55 µm hatch distance, and 25 µm layer thickness. The X-ray computed tomography (XCT), scanning electron microscope (SEM), and energy dispersive spectroscopy (EDS) investigations show that partial oxidation of Nb-coated particles is responsible for the development of lack-of-fusion holes between the printed layers. An approach based on the nanoindentation and electron backscattered diffraction (EBSD) measurements was utilized to evaluate the correlation between the crystallographic orientations and mechanical properties of the produced samples. In this approach, arrays of indentations (Fig. 1a) were applied on four planes of the samples trimmed in different directions. The EBSD images of these indentation regions reveal the location of each indent in colored grains of different orientations. Here, a microstructure with columnar grains and a high texture intensity of 9.2 has been observed in the plane perpendicular to the building direction. This plane comprises a mixture of red-, green-, and blue-colored grains, while the measured average hardness (H) and indentation modulus (Er) were increased from red grains to green and blue ones, respectively (Fig. 1b). Eventually, the nanoindentation load-displacement curves of [001], [101], and [111] grains (Fig. 1c) were utilized for modeling the elastoplastic features of the produced samples. T2 - MSE2024 CY - Darmstadt, Germany DA - 24.09.2024 KW - Coating KW - Laser-based powder bed fusion processing KW - Copper PY - 2024 AN - OPUS4-61149 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro T1 - Towards the Use of Representative Specimens for the Qualification of Additively Manufactured Parts N2 - The understanding of the process-structure-property-performance relationship is the key challenge for the qualification of safety-relevant parts made of additively manufactured metallic materials. The complexity of the manufacturing process and the number of influencing parameters affect the properties of test coupons and parts even fabricated in the same batch. This poses the problem of using reliable witness specimens for part qualification. This work presents a new approach which aims at the fabrication of test coupons tailored to the specific microstructure and fatigue properties of a component. The first step consisted in the evaluation of the temperature field by means of process monitoring during the production of parts. The results were used to tailor finite element models which were then used to design witness specimens representative of the thermal history in the component. Finally, the fatigue properties of designed specimens were compared to coupons machined out of the component. T2 - TMS2024 – 153rd Annual Meeting & Exhibition CY - Orlando, FL, USA DA - 03.03.2024 KW - Additive Manufacturing KW - Process simulation KW - Thermal history KW - Structural integrity KW - Damage tolerance PY - 2024 AN - OPUS4-65072 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Fasselt, Janek Maria A1 - Klötzer-Freese, Christian A1 - Kruse, Tobias A1 - Kleba-Ehrhardt, Rafael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Recycling nickel aluminium bronze grinding chips to feedstock for directed energy deposition via impact whirl milling: Investigation on processability, microstructure and mechanical properties N2 - During the production of ship propellers, considerable quantities of grinding chips from nickel aluminium bronze areproduced. This paper examines the mechanical comminution of such chips via impact whirl milling and the utilization of twochip-powder batches as feedstock for a laser-based directed energy deposition process. The materials are characterized viadigital image analysis, standardized flowability tests, scanning electron microscopy and energy dispersive X-ray spectroscopyand are compared to conventional, gas atomized powder. The specimens deposited via directed energy deposition areanalyzed for density, hardness and microstructure and tensile properties for vertical and horizontal build up directions arecompared. At elevated mill rotation speeds, the comminution with impact whirl milling produced rounded particles, favorableflow properties and particle size distribution, making them suitable to deposit additive specimens. The microstructureexhibited characteristic martensitic phases due to the high cooling rates of the additive manufacturing process. The presenceof ceramic inclusions was observed in both the powder and on the tensile fracture surfaces, partly impairing the mechanicalproperties. However, specimens in the vertical build-up direction (Z) showed competitive tensile results, with 775 MPa intensile strength, 455 MPa in yield strength and 12.6 % elongation at break. The findings of this study indicate that recyclingof machining chips to additive manufacturing feedstock can be a viable option for reducing material costs and environmentalimpact. KW - Nickel aluminium bronze KW - Grinding chips KW - Recycling KW - Directed energy deposition KW - Material characterization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651214 DO - https://doi.org/10.1016/j.addma.2025.104804 SN - 2214-8604 VL - 105 SP - 1 EP - 9 PB - Elsevier B.V. AN - OPUS4-65121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lemke, J. T1 - Water and gas atomized AISI 316L powder for DED-LB: A comparative study on powder properties and build quality N2 - Powder properties are considered a key factor in part quality in laser additive manufacturing, although few studies have investigated the effects in directed energy deposition (DED). Water atomized (WA) and gas atomized (GA) powders are frequently used but may result in different part properties due to powder properties. To examine their qualification for DED-LB, this work examines powders and build quality of AISI 316L. Also, examination techniques are compared. The results show that the powder production has no relevant influence on porosity and Archimedian density of built parts. WA powders show good processability in DED-LB, despite unfavorable morphology. In contrast, WA specimen reach only 10% fracture elongation in tensile testing whereas GA-based specimen achieve 30%. Tensile strength of both is above 500 MPa. The reason for the lower mechanical property values can be attributed to defects and oxides. WA powders may provide a cost-effective alternative for DED-LB when mechanical load requirements are not important. T2 - Lasers in Manufacturing Conference CY - Munich, Germany DA - 23.06.2025 KW - DED-LB KW - Porosity KW - AISI 316L KW - Water atomized KW - Gas atomized KW - Powder PY - 2025 AN - OPUS4-65120 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scharf-Wildenhain, R. T1 - Influence of build up height on residual stresses in additive repair and modification using DED Arc N2 - Directed Energy Deposition (DED)-Arc is suitable for the hybrid additive manufacturing, modification and repair of large metal components with high deposition rates. Residual stresses and distortion are of central importance when characterizing the manufactured components and the sensitive transition area between AM component and semi-finished product. Residual stresses caused by the thermal cycles during the manufacturing process can impair the mechanical properties of the manufactured parts and can lead component failure. Therefore, understanding and controlling residual stresses, especially when combining different base and filler materials, is critical to improving the quality and efficiency of the hybrid DED-Arc process. This article deals with the influence of the build-up height on the residual stress distribution of additively manufactured components with a selected base and filler material combination. Using a robot-assisted DEDsystem and a controlled short arc, systematic step cancellation tests were carried out at a selected working temperature (200 C°) and heat input (600 kJ/m). In a 5-stage termination experiment, straight walls were produced using a one bead per layer strategy and selected increasing component heights between 15 mm and 300 mm. The influence of the build height on the longitudinal residual stress in the process direction was analyzed and discussed. All experiments showed a comparable stress distribution in the area of the substrate plate up to the heat-affected zone (HAZ) and the transition zone, regardless of the buliding height. However, the height showed a significant influence on the of residual stress distribution of the deposited AM-component. High positive stress gradients with a maximum range between 300 MPa to 400 MPa were always found in the last approx. 18 component layers (upper 40 mm), which can be explained by the shrinkage of the nonheat- treated top layer. Underlying layers, where present, showed a homogeneous residual stress distribution characterized by low compressive stresses. This can be explained by the process related tempering during the deposition of the upper layers. A constant boundary layer number was determined for all specimens. Once this number was exceeded, the distribution of residual stresses no longer changed, but merely shifted with the increasing height of the component in the direction of build-up. These correlations contribute to the understanding of residual stress development with increasing structure height. This study is part of a running research project on the properties of hybrid additive components and processes. It aims the stress optimized hybrid additive manufacturing of high-strength components and the necessary recommendations for application. T2 - 78th IIW Annual Assembly and International Conference on Welding and Joining CY - Genoa, Italy DA - 22.06.2025 KW - DED-Arc KW - Additive manufacturing KW - Residual stress PY - 2025 AN - OPUS4-65192 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk T1 - Wear resistance of modified Ni based claddings in relation to the resulting machinability via ultrasonic-assisted milling N2 - In the field of plastics processing, extruder screws are subjected to significant wear stresses. The extruder screw is the main wear component in those production machines and is usually coated with intermetallic wear protection alloys composed of Ni-based alloys, specifically Colmonoy C56 PTA (NiMoCrSi). There is a growing demand for providing an economic machinability of these alloys to achieve defined contours with a sufficient surface integrity. Recent investigations exhibit promising results applying ultrasonic milling for such hard-to-cut materials. The Colmonoy C56 is modified by various alloying additions Ti, Nb, Mo, Hf, and Al, and then cladded on a steel S355 via Plasma Transferred Arc process. The effect of alloying additions on the microstructure is analyzed regarding their resistance to abrasive and adhesive wear. With Miller test ASTM G75 the influence of alloying elements on resistance to abrasive wear for two abrasive materials is investigated (high-grade corundum F220 and quartz powder). The wear loss is not increased for additions of Nb and Ti compared to the base material C56. Modifications with Hf or Al reduces the resistance to abrasive wear and significantly increases material loss. The extruder screw is also subject to adhesive wear, which can be quantified by means of the pin-roll test. It is demonstrated that the addition of Hf, for example, contributes to a reduction in wear loss. Aim of the investigations is to find suitable modifications for the wear claddings of C56 for a sufficient machineability, without compemising the wear resistant. The machinability is considerably affected by the alloy additions, and is determined using ultrasonic-assisted milling. The addition of hafnium reduces machinability, i.e. significantly increases cutting forces. The incorporation of Nb exhibits a significant reduction of cutting forces, and results in reduced tool wear and an enhanced of surface integrity (roughness, density of defects, residual stresses). T2 - Wear of Materials 2025 CY - Sitges, Spain DA - 13.04.2025 KW - Abrasive wear KW - Adhesive wear KW - Colmonoy C56 KW - PTA welding KW - Service life and efficiency KW - Substitution of critical raw materials KW - Surface integrity KW - Ultrasonic-assisted milling process PY - 2025 AN - OPUS4-65189 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -