TY - CONF A1 - Junge, P. A1 - Stargardt, Patrick A1 - Kober, D. A1 - Greinacher, M. A1 - Rupprecht, C. T1 - Thermally Sprayed Al2O3 Ceramic Coatings for Electrical Insulation Applications N2 - Thermal spraying enables a fast and propelling way to additively deposit various ceramics as electric insulators, which are used in conditions where polymers are not suitable. Alumina (Al2O3) is among the most employed materials in the coating industry since it exhibits good dielectric properties, high hardness, high melting point while still being cost-effective. Various parameters (e.g. feedstock type, plasma gas mixture, plasma power) significantly influence the resulting coating in terms of microstructure, porosity, crystallinity, and degree of un-or molten particles. As a consequence, these parameters need to be investigated to estimate the impact on the electrical insulating properties of thermally sprayed alumina. This study focuses on the development of a novel electric insulation coating from Al2O3 feedstock powders deposited via atmospheric plasma spray (APS). The microstructure, porosity, and corresponding crystallographic phases have been analyzed with optical microscopy, XRD, and SEM images. To achieve an understanding of the parameters influencing the electrical insulation performance of the manufactured coatings, an in-depth analysis of the fundamental dielectric parameters e.g., DC resistance, breakdown strength, dielectric loss tangent, permittivity is presented. T2 - International Thermal Spray Conference and Exposition 2022 CY - Vienna, Austria DA - 04.05.2022 KW - Thermal Spray KW - Alumina KW - Dielectric properties PY - 2022 SP - 1 EP - 8 AN - OPUS4-55821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Srinivasan, Krishnanand A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser Metal Deposition of Rene 80 – Microstructure and Solidification Behaviour Modelling N2 - New developments in nickel-based superalloys and production methods, such as the use of additive manufacturing (AM), can result in innovative designs for turbines. It is crucial to understand how the material behaves during the AM process to advance industrial use of these techniques. An analytical model based on reaction-diffusion formalism is developed to better explain the solidification behavior of the material during laser metal deposition (LMD). The well-known Scheil-Gulliver theory has some drawbacks, such as the assumption of equilibrium at the solid-liquid interface, which is addressed by this method. The solidified fractions under the Scheil model and the pure equilibrium model are calculated using CALPHAD simulations. Differential scanning calorimeter is used to measure the heat flow during the solid-liquid phase transformation, the result of which is further converted to solidified fractions. The analytical model is compared with all the other models for validation. T2 - Lasers in Manufacturing Conference 2023 CY - Munich, Germany DA - 26.06.2023 KW - Additive manufacturing KW - Laser metal deposition KW - Solidification behaviour KW - Analytical model KW - Nickel-based superalloy PY - 2023 SP - 1 EP - 10 AN - OPUS4-58612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin A1 - Hilgenberg, Kai A1 - Hellfritz, Benjamin A1 - Löffler, Frank T1 - Digitisation of the quality infrastructure - using the example of additive manufacturing N2 - Rapidly advancing technologies and progressive digitisation are posing challenges to the established quality infrastructure (QI). In response, the key stakeholders of the German QI established the initiative QI-Digital aimed at developing new solutions for modern quality assurance. One of the central use cases herein is quality assurance for additive manufacturing, in which a fully interlinked additive manufacturing process chain is established. The intention is to collect and process data from each production step, allowing for a comprehensive digital view of the physical material flow. Within this process chain, prototypes of digital QI tools like machine readable standards and digital quality certificates are being demonstrated, tested, and evolved. This is complemented by research on the process level, comprising the evaluation and refinement of methods for in-situ and ex-situ quality assurance, as well as algorithms for registration, reduction, and analysis of process data. This paper presents the status, goals, and vision for the QI-Digital use case additive manufacturing. T2 - Metal Additive Manufacturing Conference 2023 CY - Wien, Austria DA - 17.10.2023 KW - Additive Manufacturing KW - Digitalisation KW - Quality Assurance PY - 2023 SP - 96 EP - 104 CY - Wien AN - OPUS4-58628 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Poka, Konstantin A1 - Merz, Benjamin A1 - Epperlein, Martin A1 - Hilgenberg, Kai T1 - Integration of the whole digital chain in a unique file for PBF-LB/M: practical implementation within a digital thread and its advantages N2 - The industrialization of AM is only possible by creating synergy with the tools of Industry 4.0. The system technology of Powder Bed Fusion with Laser beam of Metals (PBF-LB/M) reached a level of high performance in terms of process stability and material spectrum in the past years. However, the digital process chain, starting from CAD via CAM and plant-specific compila-tion of the manufacturing file exhibits media disruptions. The consequence is a loss of metadata. A uniform data scheme of simulation for Design for Additive Manufacturing (DfAM), the PBF-LB/M process itself and quality assurance is currently not realized within industry. There is no entity in the common data flows of the process chains, that enables the integration of these functionalities. As part of the creation of a digital quality infrastructure in the QI-Digital pro-ject, an integration of the CAD/CAM chain is being established. The outcome is a file in an advanced commercially available format which includes all simula-tions and manufacturing instructions. The information depth of this file extends to the level of the scan vectors and allows the automatic optimization and holis-tic documentation. In addition, the KPI for the economic analysis are generated by compressing information into a unique file combined with the application of a digital twin. The implementation and advantages of this solution are demon-strated in a case study on a multi-laser PBF-LB/M system. A build job contain-ing a challenging geometry is thermally simulated, optimized, and manufac-tured. To verify its suitability for an Additive Manufacturing Service Platform (AMSP), the identical production file is transferred to a PBF-LB/M system of another manufacturer. Finally, the achieved quality level of the build job is evaluated via 3D scanning. This evaluation is carried out in the identical entity of the production file to highlight the versatility of this format and to integrate quality assurance data. T2 - Additive Manufacturing for Products and Applications 2023 CY - Lucerne, Switzerland DA - 11.09.2023 KW - Laser Powder Bed Fusion KW - Digital Twin KW - Data Integrity KW - Process Chain Integration KW - Computer Aided Manufacturing PY - 2023 SN - 978-3-031-42982-8 DO - https://doi.org/10.1007/978-3-031-42983-5_7 SN - 2730-9576 VL - 3 SP - 91 EP - 114 PB - Springer CY - Cham AN - OPUS4-58363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils A1 - Heinrichsdorff, F. A1 - Oster, Simon A1 - Uhlmann, E. A1 - Polte, J. A1 - Gordei, A. A1 - Hilgenberg, Kai T1 - In-situ monitoring of the laser powder bed fusion process by thermography, optical tomography and melt pool monitoring for defect detection N2 - For the wide acceptance of the use of additive manufacturing (AM), it is required to provide reliable testing methods to ensure the safety of the additively manufactured parts. A possible solution could be the deployment of in-situ monitoring during the build process. However, for laser powder bed fusion using metal powders (PBF-LB/M) only a few in-situ monitoring techniques are commercially available (optical tomography, melt pool monitoring), which have not been researched to an extent that allows to guarantee the adherence to strict quality and safety standards. In this contribution, we present results of a study of PBF-LB/M printed parts made of the nickel-based superalloy Haynes 282. The formation of defects was provoked by local variations of the process parameters and monitored by thermography, optical tomography and melt pool monitoring. Afterwards, the defects were characterized by computed tomography (CT) to identify the detection limits of the used in-situ techniques. T2 - Lasers in Manufacturing Conference 2023 CY - Munich, Germany DA - 26.06.2023 KW - Thermography KW - Optical tomography KW - Melt-pool-monitoring KW - Laser powder bed fusion KW - Haynes 282 KW - Additive Manufacturing PY - 2023 UR - https://www.wlt.de/lim2023-proceedings/system-engineering-and-process-control SP - 1 EP - 10 AN - OPUS4-58466 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, M. A1 - Schlingmann, T. A1 - Schmidt, J. A1 - Bettge, Dirk A1 - Hilgenberg, Kai A1 - Binder, M. A1 - Klöden, B. T1 - A Round Robin Test To Investigate The Printing Quality Of PBF-LB/M Processed AlSi10Mg N2 - When it comes to higher accuracies, new technologies and real applications in additive manufacturing, there is one topic which cannot be avoided: The material response on the chosen processing parameters and its agreement and correspondence with literature data of the wrought material grade counterpart. In industrial Additive Manufacturing (AM) standards in terms of printing parameters, protection gas atmospheres or powder handling instructions are not obligatory. Therefore, the question must be answered whether the AM process is reproducible and reliable over different printing companies. This was the motivation to realize a round robin test between 8 European printing companies and academic partners. The consortium had printed and tested fatigue and tensile testing bars under plant-specific conditions. A commonly used cast aluminum alloy, AlSi10Mg, was chosen as test material for the PBF-LB/M process. Differences of the results between the partners and the scatter itself were discussed in detail. T2 - World PM2022 CY - Lyon, France DA - 09.10.2022 KW - Additive manufacturing KW - Round robin KW - Reproducibility KW - Laser powder bed fusion KW - AlSi10Mg PY - 2022 SN - 978-1-899072-54-5 SP - 1 EP - 10 PB - European Powder Metallurgy Association (EPMA) AN - OPUS4-56304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, T. A1 - Uhlmann, E. A1 - Häcker, Ralf A1 - Jäger, M. A1 - Rauch, H. A1 - Kondas, J. A1 - Brach, K. A1 - Singh, R. T1 - Evaluation of electric conductivity and mechanical load capacity of copper deposits for application in large winding components for electrical high-voltage machines made with cold spray additive manufacturing N2 - In line with the industrial trend of additive manufacturing, cold spray as a non-laser-based process is becoming increasingly important for many fields of application. For the evaluation of additive manufacturing of winding components made of copper for large electrical high-voltage machines, material and component properties such as electrical conductivity, mechanical load capacity and the component size that can be produced are of particular importance. In this context, the cold spray process offers advantages over laser-based additive manufacturing processes such as laser powder bed fusion (LPBF) or laser cladding by using the kinetic energy of the copper powder particles to generate particle cohesion. To investigate the electrical conductivity as well as the mechanical load capacity of cold spray parts, specimens were machined out of cold sprayed bulk copper deposits. The characteristic values were obtained with regard to the direction of deposition, which is defined by the direction of the robot’s movement. Thus, for the investigation of the component properties, specimens were provided that had been produced both longitudinally and transversely as well as orthogonally to the direction of deposition. The results of the investigations show that both the electrical conductivity and the mechanical load capacity of the specimen have a strong preferential direction of the specimen orientation with respect to the direction of deposition. Furthermore, it could be shown that by increasing the deposition height, there is an increasing oxygen content in the sample material, combined with increasingly significant defect networks. These effects have a negative impact on the electrical conductivity as well as on the mechanical load capacity. As a conclusion, further need for investigation is identified in the optimization of the process parameters as well as in the deposition strategy for the additive manufacturing of large-volume components with cold spray. T2 - ITSC 2022 CY - Wien, Austria DA - 04.05.2022 KW - Cold Spray KW - Electrical conductivity KW - Copper powder particles KW - Large electrical high-voltage machine PY - 2022 SP - 1 EP - 7 AN - OPUS4-56108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weichert, Dorina A1 - Kister, Alexander A1 - Houben, Sebastian A1 - Link, Patrick A1 - Ernis, Gunar ED - Kiyavash, Negar ED - Mooij, Joris M. T1 - Robust Entropy Search for Safe Efficient Bayesian Optimization N2 - The practical use of Bayesian Optimization (BO) in engineering applications imposes special requirements: high sampling efficiency on the one hand and finding a robust solution on the other hand. We address the case of adversarial robustness, where all parameters are controllable during the optimization process, but a subset of them is uncontrollable or even adversely perturbed at the time of application. To this end, we develop an efficient information-based acquisition function that we call Robust Entropy Search (RES). We empirically demonstrate its benefits in experiments on synthetic and real-life data. The results show that RES reliably finds robust optima, outperforming state-of-the-art algorithms. T2 - UAI 2024 CY - Barcelona, Spain DA - 15.07.2024 KW - Bayesian Optimization KW - Gaussian process KW - Active learning PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613523 UR - https://proceedings.mlr.press/v244/weichert24a.html SN - 2640-3498 VL - 244 SP - 3711 EP - 3729 PB - Proceedings of Machine Learning Research AN - OPUS4-61352 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Chaudhuri, Somsubhro A1 - Pittner, Andreas A1 - Winterkorn, Rene A1 - de Finis, Rosa A1 - Palumbo, Davide A1 - Galietti, Umbero T1 - Thermographic investigation of the anisotropic behaviour of additively manufactured AISI316 steel using DED-Arc N2 - Additive manufacturing is one of the most promising techniques for industrial production and maintenance, but the specifics of the layered structure must be considered. The Direct Energy Deposition-Arc process enables relatively high deposition rates, which is favourable for larger components. For this study, specimens with different orientations were prepared from one AISI316 steel block – parallel and orthogonal to the deposition plane. Quasistatic tensile loading tests were carried out, monitored by an infrared camera. The obtained surface temperature maps revealed structural differences between both orientations. The consideration of surface temperature transients yields more details about the behaviour of the material under tensile loading than the conventional stress-strain-curve. These preliminary investigations were supplemented by thermographic fatigue trials. Although the anisotropy was also observed during fatigue loading the fatigue behaviour in general was the same, at least for both inspected specimens. The presented results demonstrate the abilities and the potential of thermographic techniques for tensile tests. T2 - 17th Quantitative Infrared Thermography Conference CY - Zagreb, Croatia DA - 01.07.2024 KW - WAAM PY - 2024 SP - 1 EP - 8 AN - OPUS4-62548 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Massimo, Carraturo A1 - Breese, Philipp P. A1 - Oster, Simon ED - Rank, E. ED - Kollmannsberger, S. T1 - Thermal model for laser-based powder bed fusion of metal process: modelling, calibration, and experimental validation N2 - In the present contribution, we propose an effective numerical thermal modeling solution for melt pool simulations in Laser-based Powder Bed Fusion of Metals processes. The proposed model employs an anisotropic conductivity to represent melt pool dynamics effects in a homogeneous material model. The numerical implementation of the proposed physical model is first experimentally calibrated and then validated with respect to a series of melt pool measurements as acquired by using a short-wave infrared (SWIR) camera monitoring system. T2 - IVth International Conference on Simulation for Additive Manufacturing (Sim-AM 2023) CY - Munich, Germany DA - 26.07.2023 KW - Laser powder bed fusion of metals KW - Melt pool measurements KW - Experimental validation KW - Thermal analysis KW - SS 316L PY - 2023 DO - https://doi.org/10.23967/c.simam.2023.015 SP - 1 EP - 9 AN - OPUS4-62525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zia, Ghezal Ahmad Jan A1 - Völker, Christoph A1 - Moreno Torres, Benjami A1 - Kruschwitz, Sabine T1 - An Adaptive Upscaling Approach for Assessing Materials’ Circularity Potential with Non-destructive Testing (NDT) N2 - Advancing towards a circular economy necessitates the efficient reuse and maintenance of structural materials, which relies on accurate, non-damaging condition assessments. This paper introduces an innovative AI-driven adaptive sampling (AS) technique integrated with Non-Destructive Testing (NDT) to optimize this process. AS focuses on critical data points, reducing the amount of data needed for precise assessments—evidenced by our method requiring on average only 7 samples for Logistic Regression and 8 for Random Forest, contrasted with 29 for traditional sampling. By reducing the necessity for extensive data collection, our method not only streamlines the assessment process but also significantly contributes to the sustainability goals of the circular economy. These goals include resource efficiency, waste reduction, and material reuse. Efficient condition assessments promote infrastructure longevity, reducing the need for new materials and the associated environmental impact. The circular economy aims to create a sustainable system where resources are reused, and waste is minimized. This is achieved by extending the lifecycle of materials, reducing the environmental footprint, and promoting recycling and reuse. Longevity directly contributes to the circular economy by maximizing the utility and lifespan of existing materials and structures. Longer-lasting infrastructure means fewer resources are needed for repairs or replacements, leading to reduced material consumption and waste generation. This aligns with the circular economy's principles of sustainability and resource efficiency. This research not only advances the field of structural health monitoring but also aligns with the broader objective of enhancing sustainable construction practices within the circular economy framework. T2 - Rilem Spring Convention CY - Milano, Italy DA - 09.04.2024 KW - Adaptive Sampling KW - Random Sampling KW - Machine Learning KW - Non-Destructive Testing KW - Condition Assessment KW - Circular Economy PY - 2024 SN - 978-3-031-70277-8 DO - https://doi.org/10.1007/978-3-031-70277-8_38 SN - 2211-0844 VL - 55 SP - 330 EP - 338 PB - Springer Nature Switzerland CY - Switzerland AN - OPUS4-62458 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, Nathalie A1 - Kister, Alexander A1 - Schnellhardt, Thorben A1 - Fetz, Maximilian A1 - Hecker, Dirk A1 - Wirtz, Tim ED - Meo, Rosa ED - Silvestri, Fabrizio T1 - Reinforcement Learning for Segmented Manufacturing N2 - The manufacturing of large components is, in comparison to small components, cost intensive. This is due to the sheer size of the components and the limited scalability in number of produced items. To take advantage of the effects of small component production we segment the large components into smaller parts and schedule the production of these parts on regular-sized machine tools. We propose to apply and adapt recent developments in reinforcement learning in combination with heuristics to efficiently solve the resulting segmentation and assignment problem. In particular, we solve the assignment problem up to a factor of 8 faster and only a few percentages less accurate than a classic solver from operations research. T2 - European Conference on Machine Learning and Principles and Practice of Knowledge Discovery in Databases 2023 CY - Turin, Italy DA - 18.09.2023 KW - Reinforcement Learning KW - Assignment Problem KW - Large component manufacturing PY - 2025 DO - https://doi.org/10.1007/978-3-031-74640-6_38 VL - 1 IS - 1 SP - 470 EP - 485 PB - Springer Cham AN - OPUS4-63031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Siefke, Lennart A1 - Linden, Anna T1 - Towards a robust automated surface inspection method for CT-scanned cannulas N2 - For certain cardiovascular diseases, cannulas are implanted into the blood circuit. To match the patients individual anatomy of the heart, there is research for cannulas to be custom-designed and manufactured aided by 3D printing. However, cannulas have to hold very high standards with regard to the smoothness of their surfaces, as rough patches can lead to formation of blood clots. Therefore, this work uses computer vision to detect such patches as part of quality assurance. First, the produced cannula is scanned using a precise CT scanner and transformed into a 3D mesh object. Rough patches in an otherwise smooth but curved surface are detected by using cosine similarity between neighboring faces and a statistical evaluation. In the end, this method is able to raise a warning when curved surfaces are not smooth enough and visualizes the problematic patches. However, there is just limited access to test data currently and the scanner used needs to be upgraded. T2 - 3D in Science & Applications (3D-iSA) 2024 CY - Berlin, Germany DA - 26.11.2024 KW - Algorithm KW - Additive manufacturing KW - Surface evaluation PY - 2025 UR - https://www.gfai.de SN - 978-3-942709-34-7 SP - 66 EP - 70 AN - OPUS4-63057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Mohr, Gunther A1 - Hilgenberg, Kai A1 - Polte, Julian T1 - Advanced camera calibration for lens distortion correction in hybrid manufacturing processes: An exemplary application in laser powder bed fusion (PBF-LB/M) N2 - Hybrid additive manufacturing is becoming increasingly important in the field of additive manufacturing. Hybrid approaches combine at least two different manufacturing processes. The focus of this work is the build-up of geometries onto conventionally manufactured parts using Powder Bed Fusion with Laser Beam of Metals (PBF-LB/M). The hybrid build-up requires a precise position detection system inside the PBF-LB/M machines to determine the exact position of the existing component. For this purpose, high-resolution camera systems can be utilized. However, the use of a camera system is associated with several challenges. The captured images are subject to various distortions of the optical path. Due to these distortions, it is not possible to use the images for measurements and, therefore, it is not possible to calculate the positions of objects. In this study a homography matrix is calculated to correct keystone distortion in the images. Different calibration patterns have been tested for the calculation of the homography matrix. The influence of the number of calibration points on the precision of position detection of objects is determined. Furthermore, the influence of an additional camera calibration by using ChArUco boards is evaluated. The result is a camera calibration workflow with associated calibration pattern for a precise position detection of parts inside PBF-LB/M machines allowing a hybrid build-up with minimum physical offset between base component and build-up. T2 - euspen’s 24th International Conference & Exhibition CY - Dublin, Ireland DA - 10.06.2024 KW - Additive manufacturing KW - Hybrid build-up KW - Position detection KW - Camera calibration PY - 2024 SP - 1 EP - 4 AN - OPUS4-60599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Scheuschner, Nils A1 - Straße, Anne A1 - Gumenyuk, Andrey A1 - Maierhofer, Christiane T1 - Towards the determination of real process temperatures in the LMD process by multispectral thermography N2 - Due to the rapid thermal cycles involved in additive manufacturing of metals, high internal stresses and peculiar microstructures occur, which influence the parts mechanical properties. To systematically examine their formation, in-process measurements of the temperature are needed. Since the part emissivity is strongly inhomogeneous and rapidly changing in the process, the applicability of thermography for the determination of thermodynamic temperatures is limited. Measuring the thermal radiation in different wavelengths simultaneously, temperature and emissivity can be separated. Here, we present results of a preliminary study using multispectral thermography to obtain real temperatures and emissivities in directed energy deposition (DED) processes. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - Additive Manufacturing KW - Process monitoring KW - Multispectral thermography KW - Laser metal deposition KW - TES KW - LMD KW - Temperature emissivity separation PY - 2021 DO - https://doi.org/10.1117/12.2587881 VL - 2021 SP - 77 EP - 83 PB - SPIE AN - OPUS4-52516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Scheuschner, Nils A1 - Chand, Keerthana A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Heinrichsdorff, F. A1 - Altenburg, Simon T1 - From Thermographic In-situ Monitoring to Porosity Detection – A Deep Learning Framework for Quality Control in Laser Powder Bed Fusion N2 - In this study, we present an enhanced deep learning framework for the prediction of porosity based on thermographic in-situ monitoring data of laser powder bed fusion processes. The manufacturing of two cuboid specimens from Haynes 282 (Ni-based alloy) powder was monitored by a short-wave infrared camera. We use thermogram feature data and x-ray computed tomography data to train a convolutional neural network classifier. The classifier is used to perform a multi-class prediction of the spatially resolved porosity level in small sub-volumes of the specimen bulk. T2 - SMSI - Sensor and Measurement Science International 2023 CY - Nürnberg, Germany DA - 08.05.2023 KW - Porosity KW - Laser powder bed fusion KW - In-situ monitoring KW - Thermography KW - Machine Learning PY - 2023 UR - https://www.ama-science.org/proceedings/details/4404 DO - https://doi.org/10.5162/SMSI2023/C5.4 SP - 179 EP - 180 AN - OPUS4-57616 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marquardt, Raphael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Influence of laser power on the melt pool shape of handheld laser beam welding of 1.5 mm thick micro alloyed steel N2 - Manual welding of structures requires highly skilled welders due to the large heat-affected zone of arc-based processes, that can negatively impact microstructure and cause distortion. Handheld laser beam welding is a promising alternative with high welding velocity and a concentrated heat input. However, its current use in industry is limited to parts with aesthetic requirements, often made of high-alloyed steel. To extend the use of handheld laser beam welding to low-cost steels with good mechanical properties, this study investigates the influence of laser power on the melt pool shape for micro-alloyed steel with a thickness of 1.5 mm. Tested joint geometries are T-joints welded with filler wire as well as butt joints and overlap joints without filler wire, which are typically found in assemblies under mechanical load. Weld quality is assessed by weld porosity analysis. The results show that the handheld laser beam welding with filler wire produces T-joints with a very good external appearance, but with porosity between level C and D in the cross sections according to DIN EN ISO 13919-1. By increasing the laser power, a deep penetration of the T-joint zone can be achieved without increasing the actual throat thickness. For handheld laser beam welding of butt joints a full penetration weld of the highest quality class can be reached. Overlap joints can be welded with full or partial penetration depending on the laser power selected, with quality classes between B and C in terms of porosity. T2 - 20th Nordic Laser Materials Processing Conference CY - Kongens Lyngby, Denmark DA - 26.08.2025 KW - Hand held laser welding KW - Laser beam welding KW - Low alloyed steel KW - Process parameter PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641671 DO - https://doi.org/10.1088/1757-899X/1332/1/012015 SN - 1757-899X VL - 1332 SP - 1 EP - 6 PB - Institute of Physics CY - London [u.a.] AN - OPUS4-64167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simón Muzás, Juan A1 - Brunner-Schwer, C. A1 - Rethmeier, Michael A1 - Hilgenberg, Kai T1 - Mitigation of liquation cracking in laser welding of pairs of L-PBF processed and wrought plates of Inconel 718 N2 - Laser welding is an appropriate technique for joining Laser Powder Bed Fusion (L-PBF) parts together and to conventional wrought ones. The potential consists of profiting from synergies between additive and conventional manufacturing methods and overcoming the existing limitations of both. On the one hand, L-PBF is a widely spread metal-based additive manufacturing technique suitable for generating complex parts which can present intrinsic designed cavities, conformal cooling channels, and filigree structures contributing to sustainable manufacturing and efficiency-oriented designs. On the other hand, chamber sizes for producing L-PBF parts are limited, and the process is time-consuming. Thus, its employment is not for every geometry justified. Additionally, they are in most cases individual elements of a larger assembly and need to be joined together to conventionally fabricated parts. The present research suggests laser welding parameters to adequately bond pairs of wrought and L-PBF processed plates and two L-PBF plates of Inconel 718 in butt position. L-PBF samples are printed in three different build-up orientations. Additionally, the influence of as-built L-PBF roughness qualities and usual pre-weld preparations such as edge milling are examined. The effect of normed pre-weld heat treatments is also contemplated. Identified cracks are analyzed by means of EDS in order to confirm the present phases on the areas of interest. EBSD is also employed to obtain a clear depiction of the crystallographic texture and distribution of the hot cracks. The quality of the weldment was examined according to existing standards. Substantial differences in seam geometry and microstructure across different edge’s surface qualities and build directions of stress relieved L-PBF parts have not been detected. Nevertheless, even if no other irregularities are present in the seam, variability in liquation cracking susceptibility has been confirmed. This defect is prone to happen when parts made of this nickel-based superalloy are welded together when not enough precautions are taken. It has been determined that grain size and ductility of the material before welding play a crucial role and mitigating or intensifying these imperfections. Moreover, recommendations are presented to avoid this potential welding defect. T2 - IIW 2022 International Conference on Welding and Joining CY - Tokyo, Japan DA - 17.07.2022 KW - Hybrid Part KW - Liquation Cracking KW - Build-up Orientation KW - Pre-weld Preparation KW - Heat treatment KW - Inconel 718 KW - Laser Welding KW - Laser Powder Bed Fusion KW - Selective Laser Melting KW - SLM KW - L-PBF KW - PBF-LB/M KW - LW PY - 2022 UR - www.iiw2022.com SP - 372 EP - 375 PB - The International Institute of Welding (IIW) CY - Tokyo, Japan AN - OPUS4-56066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, V. A1 - Marko, A. A1 - Kruse, T. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Analysis and recycling of bronze grinding waste to produce maritime components using directed energy deposition N2 - Additive manufacturing promises a high potential for the maritime sector. Directed Energy Deposition (DED) in particular offers the opportunity to produce large-volume maritime components like propeller hubs or blades without the need of a costly casting process. The post processing of such components usually generates a large amount of aluminum bronze grinding waste. The aim of the presented project is to develop a sustainable circular AM process chain for maritime components by recycling aluminum bronze grinding waste to be used as raw material to manufacture ship Propellers with a laser-powder DED process. In the present paper, grinding waste is investigated using a dynamic image Analysis system and compared to commercial DED powder. To be able to compare the material quality and to verify DED process parameters, semi-academic sample geometries are manufactured. T2 - LiM 2021 CY - Munich, Germany DA - 21.06.2021 KW - Additive Manufacturing KW - Maritime Components KW - Powder Analysis KW - Recycling KW - Directed Energy Deposition PY - 2021 SP - 1 EP - 9 AN - OPUS4-54067 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai T1 - Influence of process-relevant parameters and heat treatments on the microstructure and resulting mechanical behavior of additively manufactured AlSi10Mg via Laser Powder Bed Fusion N2 - Within the group of additive manufacturing (AM) technologies for metals, laser powder bed fusion (L-PBF) has a leading position. Nevertheless, reproducibility of part properties has not reached sufficient maturity hindering the use for industrial applications especially for safety-relevant components. This article presents the results of various experimental tests performed with the aluminium alloy AlSi10Mg identifying reasons for the high deviations in mechanical properties. Herein, it is discussed how microstructure is influenced by different process parameters (laser power, scanning speed, energy density, building height) and how it can be adjusted by suitable post process heat treatments. The impact of resulting changes in microstructure is shown by monotonic tensile and cyclic fatigue tests considering specimens manufactured with different L-PBF machines. T2 - LiM 2021 CY - Online meeting DA - 21.06.2021 KW - Additive manufacturing KW - Laser powder bed fusion KW - AlSi10Mg PY - 2021 SP - 1 EP - 9 AN - OPUS4-52991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Knobloch, Tim A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Concepts for bridging voids in metal additive manufacturing for repair of gas turbine blades using laser powder bed fusion N2 - One of the main advantages of additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) is the possibility to manufacture complex near-net-shape components. Therefore, the PBF-LB/M process is becoming increasingly important for the manufacturing and repair of gas turbine blades. Despite the great freedom in design, there are also limitations to the process. Manufacturing overhangs or bridging voids are some of the main challenges. In the conventional PBF-LB/M process, overhangs with angles up to 45° can be manufactured. However, gas turbine blades feature voids for cooling, which have to be bridged when using PBF-LB/M. In this work, different concepts for bridging voids are developed for future application in gas turbine blade repair. For this purpose, a test geometry is derived from the tip area of a gas turbine blade as a reference. By changing the initial geometry of the reference body, different designs for bridging voids are developed based on the PBF-LB/M requirements. Subsequently, these distinct designs are manufactured by PBF-LB/M. The different approaches are compared with respect to their volume increase. In addition, the specimens are visually inspected for warpage, shrinkage and imperfections by overheating. Out of the seven concepts developed, three concepts can be recommended for gas turbine blade repair based on low volume increase, distortion and shrinkage. T2 - Metal Additive Manufacturing Conference - MAMC 2022 CY - Graz, Austria DA - 26.09.2022 KW - Repair of gas turbine blades KW - Laser Powder Bed Fusion (PBF-LB/M) KW - Selective Laser Melting (SLM) KW - Design for Additive Manufacturing (DfAM) KW - Bridging voids KW - Supportless PY - 2022 SP - 19 EP - 28 PB - TU Graz CY - Graz AN - OPUS4-55868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Nilsson, R. A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - On the challenges of hybrid repair of gas turbine blades using laser powder bed fusion N2 - Additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) are rapidly gaining popularity in repair applications. Gas turbine components benefit from the hybrid repair process as only damaged areas are removed using conventional machining and rebuilt using an AM process. However, hybrid repair is associated with several challenges such as component fixation and precise geometry detection. This article introduces a novel fixturing system, including a sealing concept to prevent powder sag during the repair process. Furthermore, a high-resolution camera within an industrial PBF-LB/M machine is installed and used for object detection and laser recognition. Herein, process related inaccuracies such as PBF-LB/M laser drift is considered by detection of reference objects. This development is demonstrated by the repair of a representative gas turbine blade. The final offset between AM build-up and component is analysed. An approximate accuracy of 160 μm is achieved with the current setup. T2 - LiM 2023 CY - Munich, Germany DA - 26.06.2023 KW - Laser powder bed fusion KW - Additive manufacturing KW - Hybrid repair KW - Position detection KW - High-resolution camera PY - 2023 SP - 1 EP - 9 AN - OPUS4-57836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelking, Lorenz A1 - Scharf-Wildenhain, R. A1 - Schröpfer, Dirk A1 - Hälsig, A. A1 - Kannengießer, Thomas A1 - Hensel, J. T1 - Influence of heat input on properties and residual stresses in hybrid addi-tive manufacturing of high strength steels using MSG processes N2 - The application of steels with a higher yield strength allows reductions in wall thickness, component weight and production costs. Hybrid additive manufacturing based on Gas Metal Arc Welding (GMAW) processes (DED-Arc) can be used to realise highly effi-cient component modifications and repairs on semi-finished products and additively manufactured structures. There are still a number of key issues preventing widespread implementation, particularly for SMEs. In addition to the manufacturing design, detailed information about assembly strategy and geometric adaptation of the component for modifications or repairs are missing. These include the welding-related stresses associ-ated with the microstructural influences caused by the additive manufacturing steps, particularly in the transition area of the substrate and filler material interface. The pre-sent research focuses the effect of welding heat control during DED-Arc process on the residual stresses, especially in the transition area. Defined specimens were welded fully automatically with a high-strength solid wire (yield strength > 790 MPa) especially adapted for DED-Arc on S690QL substrate. The working temperature and heat input were systematically varied for a statistical effect analysis on the residual stress state of the hybrid manufactured components. Regarding heat control, t8/5 cooling times within the recommended processing range (approx. 5 s to 20 s) were complied. The investiga-tion revealed a significant influence of the working temperature Ti on the compressive residual stresses in the transition area and the tensile residual stresses at the base of the substrate. High working temperatures result in lower compressive residual stresses, heat input E does not significantly affect the tensile stresses. T2 - 6. Symposium Materialtechnik CY - Clausthal-Zellerfeld, Germany DA - 20.02.2025 KW - DED-Arc KW - Residual stress KW - Heat control PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632188 DO - https://doi.org/10.21268/20250506-3 SP - 110 EP - 122 AN - OPUS4-63218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - O'Connor, Daniel A1 - Evans, Alexander A1 - Balsamo, Alessandro A1 - Favres, Georges A1 - Przyklenk, Anita A1 - Bosse, Harald A1 - Phillips, Dishi T1 - European Metrology Network (EMN) for Advanced Manufacturing ─ Development of the Strategic Research Agenda (SRA) N2 - The European Commission has identified Advanced Manufacturing and Advanced Materials as two of six Key Enabling Technologies (KETs). It is considered that Metrology is a key enabler for the advancement of these KETs. Consequently, EURAMET, the association of metrology institutes in Europe, has strengthened the role of Metrology for these KETs by enabling the creation of a European Metrology Network (EMN) for Advanced Manufacturing. The EMN is comprised of National Metrology Institutes (NMIs) and Designated Institutes (DIs) from across Europe and was formally established in October 2021. The aim of the EMN is to provide a high-level coordination of European metrology activities for the Advanced Manufacturing community. The EMN itself is organized in three sections representing the major stages of the manufacturing chain: 1) Advanced Materials, 2) Smart Manufacturing Systems, and 3) Manufactured Components & Products. The EMN for Advanced Manufacturing is engaging with stakeholders in the field of Advanced Manufacturing (large companies & SMEs, industry organisations, existing networks, and academia), as well as the wider Metrology community, including Technical Committees, to provide input for the Strategic Research Agenda (SRA) on Metrology for Advanced Manufacturing. This contribution will give an overview about the first version of the SRA prepared by the EMN for Advanced Manufacturing T2 - Euspen, 23rd International Conference & Exhibitio CY - Copenhagen, Danmark DA - 12.06.2023 KW - European Metrology Network (EMN) KW - Advanced Manufacturing KW - Metrology KW - Strategic Research Agenda (SRA) PY - 2023 SP - 363 EP - 364 AN - OPUS4-59196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Metz, C. A1 - Altenburg, Simon T1 - In-situ defect detection via active laser thermographic testing for PBF-LB/M N2 - Great complexity characterizes Additive Manufacturing (AM) of metallic components via laser powder bed fusion (PBF-LB/M). Due to this, defects in the printed components (like cracks and pores) are still common. Monitoring methods are commercially used, but the relationship between process data and defect formation is not well understood yet. Furthermore, defects and deformations might develop with a temporal delay to the laser energy input. The component’s actual quality is consequently only determinable after the finished process. To overcome this drawback, thermographic in-situ testing is introduced. The defocused process laser is utilized for nondestructive testing performed layer by layer throughout the build process. The results of the defect detection via infrared cameras are shown for a research PBF-LB/M machine. This creates the basis for a shift from in-situ monitoring towards in-situ testing during the AM process. Defects are detected immediately inside the process chamber, and the actual component quality is determined. T2 - Lasers in Manufacturing (LiM) CY - Munich, Germany DA - 26.06.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Nondestructive testing KW - Laser thermography KW - Defect detection PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-585060 SP - 1 EP - 10 PB - Wissenschaftliche Gesellschaft Lasertechnik und Photonik (WLT) CY - Hannover AN - OPUS4-58506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter A1 - Becker, Tina A1 - Oster, Simon A1 - Metz, C. A1 - Altenburg, Simon T1 - In-situ defect detection for laser powder bed fusion with active laser thermography N2 - Defects are still common in metal components built with Additive Manufacturing (AM). Process monitoring methods for laser powder bed fusion (PBF-LB/M) are used in industry, but relationships between monitoring data and defect formation are not fully understood yet. Additionally, defects and deformations may develop with a time delay to the laser energy input. Thus, currently, the component quality is only determinable after the finished process. Here, active laser thermography, a nondestructive testing method, is adapted to PBF-LB/M, using the defocused process laser as heat source. The testing can be performed layer by layer throughout the manufacturing process. We study our proposed testing method along experiments carried out on a custom research PBF-LB/M machine using infrared (IR) cameras. Our work enables a shift from post-process testing of components towards in-situ testing during the AM process. The actual component quality is evaluated in the process chamber and defects can be detected between layers. T2 - 2023 International Solid Freeform Fabrication Symposium CY - Austin, TX, USA DA - 14.08.2023 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Nondestructive Testing KW - Thermography KW - Defect Detection PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606288 DO - https://doi.org/10.26153/tsw/51096 SP - 1978 EP - 1989 PB - University of Texas at Austin CY - Austin, TX, USA AN - OPUS4-60628 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Hilgenberg, Kai ED - Wei, Z. ED - Pang, J. T1 - On critical shifts of the process window due to heat accumulation in laser powder bed fusion N2 - Safety-critical applications of products manufactured by laser powder bed fusion (PBF-LB/M) are still limited to date. This is mainly due to a lack of knowledge regarding the complex relationship between process, structure, and resulting properties. The assurance of homogeneity of the microstructure and homogeneity of the occurrence and distribution of defects within complexly shaped geometries is still challenging. Unexpected and unpredicted local inhomogeneities may cause catastrophic failures. The identification of material specific and machine specific process parameter windows for production of fully dense simple laboratory specimens is state of the art. However, the incorporation of changing thermal conditions that a complexly shaped component can be faced with during the manufacturing process is often neglected at the stage of a process window determination. This study demonstrates the tremendous effect of changing part temperatures on the defect occurrence for the broadly used stainless steel alloy AISI 316L. Process intrinsic variations of the surface temperature are caused by heat accumulation which was measured by use of a temperature adjusted mid-wavelength infrared (MWIR) camera. Heat accumulation was triggered by simple yet effective temporal and geometrical restrictions of heat dissipation. This was realized by a variation of inter layer times and reduced cross section areas of the specimens. Differences in surface temperature of up to 800 K were measured. A severe development of keyhole porosity resulted from these distinct intrinsic preheating temperatures, revealing a shift of the process window towards unstable melting conditions. The presented results may serve as a warning to not solely rely on process parameter optimization without considering the actual process conditions a real component is faced with during the manufacturing process. Additionally, it motivates the development of representative test specimens. T2 - The 76th IIW Annual Assembly and International Conference On Welding And Joining (IIW 2023) CY - Singapore, Singapore DA - 16.07.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Laboratory specimens KW - Process parameter optimization KW - Heat accumulation KW - Keyhole porosity KW - Infrared thermography PY - 2023 SP - 1 EP - 8 AN - OPUS4-58024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Maierhofer, Christiane A1 - Mohr, Gunther A1 - Hilgenberg, Kai A1 - Ulbricht, Alexander A1 - Altenburg, Simon T1 - Investigation of the thermal history of L-PBF metal parts by feature extraction from in-situ SWIR thermography N2 - Laser powder bed fusion is used to create near net shape metal parts with a high degree of freedom in geometry design. When it comes to the production of safety critical components, a strict quality assurance is mandatory. An alternative to cost-intensive non-destructive testing of the produced parts is the utilization of in-situ process monitoring techniques. The formation of defects is linked to deviations of the local thermal history of the part from standard conditions. Therefore, one of the most promising monitoring techniques in additive manufacturing is thermography. In this study, features extracted from thermographic data are utilized to investigate the thermal history of cylindrical metal parts. The influence of process parameters, part geometry and scan strategy on the local heat distribution and on the resulting part porosity are presented. The suitability of the extracted features for in-situ process monitoring is discussed. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - SWIR camera KW - Additive manufacturing (AM) KW - Selective laser melting (SLM) KW - Laser beam melting (LBM) KW - In-situ monitoring KW - Infrared thermography PY - 2021 SN - 978-1-5106-4324-6 DO - https://doi.org/10.1117/12.2587913 VL - 11743 SP - 1 EP - 11 PB - SPIE - The international society for optics and photonics AN - OPUS4-52535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altenburg, Simon A1 - Scheuschner, Nils A1 - Maierhofer, Christiane A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Thermography in laser powder bed fusion of metals: time over threshold as feasible feature in thermographic data N2 - Thermography is one on the most promising techniques for in-situ monitoring of metal additive manufacturing processes. Especially in laser powder bed fusion processes, the high process dynamics and the strong focus of the laser beam cause a very complex thermal history within the produced specimens, such as multiple heating cycles within single layer expositions. This complicates data interpretation, e.g., in terms of cooling rates. A quantity that is easily calculated is the time a specific area of the specimen is at a temperature above a chosen threshold value (TOT). Here, we discuss variations occurring in time-over-threshold-maps during manufacturing of an almost defect free cuboid specimen. T2 - 15th Quantitative InfraRed Thermography conference CY - Online meeting DA - 21.09.2020 KW - Additive Manufacturing KW - Process monitoring KW - Thermography KW - L-PBF KW - Time over threshold PY - 2020 DO - https://doi.org/10.21611/qirt.2020.005 SP - 1 EP - 5 PB - QIRT Council CY - Quebec, Canada AN - OPUS4-52014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wandtke, Karsten A1 - Schröpfer, Dirk A1 - Scharf-Wildenhain, R. A1 - Hälsig, A. A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - WAAM process influences on local microstructure and residual stresses in high-strength steels N2 - High-strength fine-grain structural steels have great potential for weight optimization of many modern engineering structures. Efficient manufacturing can be achieved here above all by Wire Arc Additive Manufacturing (WAAM). First commercial high-strength welding consumables for WAAM are already available. Due to a lack of knowledge and guidelines for the industry regarding welding residual stresses and component safety in manufacturing and operation, their application is still severely limited. Residual stresses play a crucial role here, as the special microstructure of high-strength steels is sensitive to cold cracking. For this reason, process- and material-related influences, as well as the design effects on residual stress formation, are being investigated in a project funded by the AiF (FOSTA P1380/IGF 21162 BG). This study focuses on determining the interactions between heat control during WAAM process, resulting hardness, microstructure, and residual stresses, analyzed by X-ray diffraction. Welding experiments using geometrically similar AM specimens show that, with regard to the heat input, the energy per unit length in particular leads to significantly affected cooling times and microstructures and causes pronounced localized effects in terms of residual stresses in the upper weld beads. T2 - 46th MPA-Seminar CY - Stuttgart, Germany DA - 12.10.2021 KW - Wire Arc Additive Manufacturing KW - High-strength structural steels KW - Vickers hardness KW - Residual stresses PY - 2021 VL - 46 SP - 296 EP - 306 PB - MPA-Stuttgart AN - OPUS4-53571 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simón Muzás, Juan A1 - Brunner-Schwer, Christian A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Mechanical properties of laser welded joints of wrought and heat treated PBF LB/M Inconel 718 parts depending on build direction N2 - Laser-based Powder Bed Fusion of Metal (PBF-LB/M) is a broadly used metal additive manufacturing (AM) method for fabricating complex metallic parts, whose sizes are however limited by the build envelope of PBF-LB/M machines. Laser welding arises as a valid joining method for effectively integrating these AM parts into larger assemblies. PBF-LB/M components must usually be stress-relieved before they can be separated from the build plate. An additional heat treatment can be beneficial for obtaining homogeneous mechanical properties across the seam or for the formation of desired precipitations in nickel-based-alloys. Therefore, the tensile performance of laser welded hybrid (AM/wrought) and AM-AM tensile samples of Inconel 718 is examined after undergoing three different heat treatments and considering three relevant build directions. It can be shown that the build orientation is an influencing factor on weld properties even after two applied heat treatments. T2 - Lasers in Manufacturing LiM 2023 CY - Munich, Germany DA - 26.09.2023 KW - Inconel 718 KW - Laser welding KW - PBF/LB-M KW - Hybrid components KW - Heat treatments KW - Build direction KW - Tensile performance PY - 2023 SP - 1 EP - 10 PB - Proceedings Lasers in Manufacturing 2023 CY - München AN - OPUS4-58394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dávila, Josué A1 - Kleba-Ehrhardt, Rafael A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Influence Of Initial Powder Oxidation Level On Process-induced Material Degradation During The Laser Powder Bed Fusion Of Nickel-based Haynes 282 N2 - This study examines the impact of varying oxidation levels in nickel-based Haynes 282 powder on particle degradation during laser powder bed fusion (PBF-LB|M). Four powder batches with oxygen content levels of approximately from 140 ppm to1400 ppm were processed using PBF-LB|M. A powder collection container was fabricated to sample unmelted powder from heat-affected regions of the powder bed. Recoating and melting proceeded without issues; however, increased fume emissions were observed at higher oxidation levels, indicating intensified spatter formation. Post-process analysis revealed that finer particles exhibited greater surface oxidation due to their higher surface-to-volume ratio. Despite significant oxygen uptake, chemical analysis showed no measurable changes in key alloying elements in either the unmelted or spatter particles. Additionally, changes in particle size distribution became more pronounced at high oxidation levels. These findings provide a basis for understanding oxidation-driven degradation and optimizing powder reuse strategies to maintain material performance. T2 - Euro Powder Metallurgy 2025 Congress & Exhibition CY - Glasgow, United Kingdom DA - 14.09.2025 KW - Recycling KW - Additive manufacturing KW - Laser powder bed fusion (PBF-LB/M) KW - Powder quality KW - Powder degradation KW - Powder oxidation KW - Spatter particles KW - Particles ejected KW - Powder reuse PY - 2025 DO - https://doi.org/10.59499/EP256767986 SP - 1 EP - 9 PB - EPMA AN - OPUS4-64369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gottschalk, Götz-Friedrich A1 - Chaurasia, Prashant Kumar A1 - Goecke, Sven-Frithjof T1 - Zero-defect Printing with DED-GMA via Adaptive Controls N2 - Gas metal arc assisted directed energy deposition (DED-GMA) is a metal additive manufacturing process for fabricating large-scale parts with a higher printing rate. An accurate monitoring and control of the melt pool geometric features is critical for printing zero-defect parts. In this study, the melt pool thermography is used for the real-time detection of the melt pool boundary, centreline, and transient cooling time using an efficient deep learning technique. The presented real-time process monitoring and control methodology using deep learning allows adaptive control of the DED-GMA process. T2 - Twenty-Second International Conference on Flow Dynamics (ICFD 2025) CY - Sendai, Japan DA - 10.11.2025 KW - Additive manufacturing KW - DED-Arc KW - Monitoring KW - Control PY - 2025 SP - 1332 EP - 1335 AN - OPUS4-64837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - D'Accardi, E. A1 - Ulbricht, Alexander A1 - Krankenhagen, Rainer A1 - Palumbo, D. A1 - Galietti, U. T1 - Capability of active thermography to detect and localize pores in Metal Additive Manufacturing materials N2 - Active thermography is a fast, contactless and non-destructive technique that can be used to detect internal defects in different types of material. Volumetric irregularities such as the presence of pores in materials produced by the Additive Manufacturing processes can strongly affect the thermophysical and the mechanical properties of the final component. In this work, an experimental investigation aimed at detecting different pores in a sample made of stainless AISI 316L produced by Laser Powder Bed Fusion (L-PBF) was carried out using pulsed thermography in reflection mode. The capability of the technique and the adopted setups in terms of geometrical and thermal resolution, acquisition frequency and energy Density of the heating source were assessed to discern two contiguous pores as well as to detect a single pore. Moreover, a quantitative indication about the minimum resolvable pore size among the available and analysed defects was provided. A powerful tool to assess the Limits and the opportunities of the pulsed technique in terms of detectability and localizability was provided by comparing active thermography results to Computed Tomography as well as a related Finite Element Analysis (FEA) to simulate the pulsed heating transfer with Comsol. T2 - 49th Italian Association for Stress Analysis Conferencee (AIAS 2020) CY - Online meeting DA - 02.09.2020 KW - Additive manufacturing KW - Laser powderbed fusion KW - Pores KW - Thermography KW - Micro-CT PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519231 DO - https://doi.org/10.1088/1757-899X/1038/1/012018 VL - 1038 SP - 1 EP - 17 PB - Institute of Physics CY - London AN - OPUS4-51923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bruno, Giovanni A1 - Mishurova, Tatiana A1 - Serrano-Munoz, Itziar A1 - Ulbricht, Alexander A1 - Fritsch, Tobias A1 - Sprengel, Maximilian A1 - Evans, Alexander A1 - Kromm, Arne A1 - Madia, Mauro ED - Bruno, Giovanni T1 - A Critical Discussion on the Diffraction-Based Experimental Determination of Residual Stress in AM Parts N2 - As opposed to reviewing results on experimental determination of residual stress by diffraction, this paper discusses the open issues when dealing with residual stress determination in additive manufactured parts, in particular those manufactured with laser powder bed fusion techniques. Three points are addressed in detail: (a) the proper determination of the strain-free reference d0, (b) the problem of the determination of the principal axes, and (c) the use of the correct diffraction elastic constants. It is shown that all methods to determine the strain-free reference d0 suffer from caveats, and care must be taken in evaluating the most suitable for the problem being tackled. In addition, it is shown that, in some systems, the principal axes do correspond to the geometrical axes of the specimen, but this needs to be systematically checked, especially in the case of uni- or bidirectional hatching strategies. Finally, the need to experimentally determine the proper diffraction elastic constants is underlined, especially in the case of strongly textured specimens, which again depends on the deposition strategy. T2 - ASTM ICAM 2020 – ASTM International Conference on Additive Manufacturing CY - Online meeting DA - 16.11.2020 KW - Additive Manufacturing KW - Diffraction KW - Residual Stress PY - 2020 DO - https://doi.org/10.1520/STP163120190148 VL - STP1631 SP - 122 EP - 138 PB - ASTM International CY - USA AN - OPUS4-51347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bhadeliya, Ashok A1 - Rehmer, Birgit A1 - Fedelich, Bernard A1 - Jokisch, Torsten A1 - Skrotzki, Birgit A1 - Olbricht, Jürgen T1 - High Temperature Fatigue Crack Growth in Nickel-Based Alloys Refurbished by Additive Manufacturing N2 - Hybrid additive manufacturing plays a crucial role in the restoration of gas turbine blades, where, e.g., the damaged blade tip is reconstructed by the additive manufacturing process on the existing blade made of a parent nickel-based alloy. However, inherent process-related defects in additively manufactured material, along with the interface created between the additively manufactured and the cast base material, impact the fatigue crack growth behavior in bi-material components. This study investigates the fatigue crack growth behavior in bi-material specimens of nickel-based alloys, specifically, additively manufactured STAL15 and cast alloy 247DS. The tests were conducted at 950 °C with stress ratios of 0.1 and −1. Metallographic and fractographic investigations were carried out to understand crack growth mechanisms. The results revealed significant retardation in crack growth at the interface. This study highlights the potential contributions of residual stresses and microstructural differences to the observed crack growth retardation phenomenon, along with the conclusion from an earlier study on the effect of yield strength mismatch on crack growth behavior at a perpendicular interface in bi-material specimens. T2 - Superalloys 2024 Conference CY - Champion, Pennsylvania, USA DA - 08.09.2024 KW - Fatigue crack growth KW - Bi-material structure KW - Additive manufacturing KW - Nickel-based alloys PY - 2024 SN - 978-3-031-63937-1 DO - https://doi.org/10.1007/978-3-031-63937-1_92 SN - 2367-1181 SN - 2367-1696 VL - 15th SP - 994 EP - 1001 PB - Springer CY - Cham AN - OPUS4-60907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Krankenhagen, Rainer A1 - Chaudhuri, Somsubhro A1 - Pittner, Andreas A1 - Winterkorn, Rene A1 - de Finis, Rosa A1 - Palumbo, Davide A1 - Galietti, Umberto T1 - Thermographic investigation of the anisotropic behaviour of additively manufactured AISI316 steel using DED-Arc N2 - Additive manufacturing is one of the most promising techniques for industrial production and maintenance, but the specifics of the layered structure must be considered. The Direct Energy Deposition-Arc process enables relatively high deposition rates, which is favourable for larger components. For this study, specimens with different orientations were prepared from one AISI316 steel block – parallel and orthogonal to the deposition plane. Quasistatic tensile loading tests were carried out, monitored by an infrared camera. The obtained surface temperature maps revealed structural differences between both orientations. The consideration of surface temperature transients yields more details about the behaviour of the material under tensile loading than the conventional stress-strain-curve. These preliminary investigations were supplemented by thermographic fatigue trials. Although the anisotropy was also observed during fatigue loading the fatigue behaviour in general was the same, at least for both inspected specimens. The presented results demonstrate the abilities and the potential of thermographic techniques for tensile tests. T2 - 17th Quantitative Infrared Thermography Conference CY - Bologna, Italy DA - 07.07.2025 KW - Thermoelastic effect KW - Wire-arc-additive manufacturing KW - thermal stress analysis KW - fatigue testing PY - 2026 DO - https://doi.org/10.21611/qirt-2024-029 SP - 1 EP - 8 AN - OPUS4-65372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Brandić Lipińska, M. A1 - Davenport, R. A1 - Imhof, A. B. A1 - Waclavicek, R. A1 - Fateri, M. A1 - Meyer, Lena A1 - Gines-Palomares, J. C. A1 - Zocca, Andrea A1 - Makaya, A. A1 - Günster, Jens T1 - PAVER - Contextualizing laser sintering within a lunar technology roadmap N2 - The Global Exploration Strategy of the International Space Exploration Coordination Group (ISECG) describes a timeframe of 2020 and beyond with the ultimate aim to establish a human presence on Mars towards the 2040ies. The next steps lie on the Moon with a focus on the coming 10 years. Early lunar surface missions will establish a capability in support of lunar science and prepare and test mission operations for subsequent human exploration of Mars and long-duration human activities on the Moon. Given the extreme costs involved in the shipping of material from Earth, a prerequisite for future human exploration is the manufacturing of elements directly on the Moon’s surface. Unlike the equipment, which at the beginning will have to be brought from Earth, raw materials and energy could be available following the concept of In-Situ Resource Utilization. The ESA OSIP PAVING THE ROAD (PAVER) study investigates the use of a laser to sinter regolith into paving elements for use as roadways and launch pads thus mitigating dust issues for transport and exploration vehicles. The ESA-funded study examines the potential of using a laser (12 kW CO2 laser with spot beam up to 100 mm) for layer sintering of lunar and martian regolith powders to manufacture larger 3D elements and provide know-how for the automatic manufacture of paving elements in the lunar environment. The project contributes to the first step toward the establishment of a lunar base and will lead to the construction of equipment capable of paving areas and manufacturing 3D structures. PAVER project sets the starting point for an examination of the larger context of lunar exploration. Mission scenarios will look at different phases of lunar exploration: Robotic Lunar Exploration, Survivability, Sustainability, and Operational Phase. A proposed Technology Roadmap investigates the mission scenario and analyses how, and to which extent, laser melting/sintering will play a role in the various phases of exploration. The paper contextualizes laser sintering within selected mission scenarios and discusses the different kinds of infrastructure that can be produced at each phase of the mission. The outcome of the study includes the detailing of the TRL steps in the project and an outline of a timeline for the different elements. Covered aspects include terrain modelling such as operation pads, roadways, or towers, non-pressurized building structures to protect machinery, and habitat envelopes, to protect and shield humans against dust, micrometeoroids, and radiation. T2 - 73rd International Astronautical Congress (IAC) CY - Paris, France DA - 18.09.2022 KW - Additive manufacturing KW - Solar sintering KW - ISRU KW - Infrastructure KW - Lunar habitat KW - Paving PY - 2022 SP - 1 EP - 9 AN - OPUS4-56519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Witte, Julien A1 - Treutler, Kai A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Influence of Microstructure on the Machinability and Surface Integrity of Additively Manufactured Iron Aluminides N2 - The increasing global focus on energy and resource efficiency has stimulated a growing interest in additive manufacturing. AM offers economic advantages and enables an efficient use of materials. However, AM components often require subsequent mechanical post-processing, such as machining (e.g. milling), to achieve the final contours or surfaces. This is a particular challenge due to the heterogeneous and anisotropic nature of AM structures, which affect machining and the resulting component properties. High-performance materials such as iron aluminide represent a promising alternative to conventional high-temperature materials with a significant economic advantage. However, the strength and hardness properties, which are advantageous for applications in highly stressed lightweight components, pose a challenge for economical machining in addition to the AM microstructure properties. The difficult-to-cut material causes accelerated tool wear and insufficient surface quality. This study shows that crack-free additive manufacturing of the three-component system of iron-nickel-aluminum is possible, and advantages in terms of machinability compared to FeAl-AM components are achieved. The more homogeneous microstructure leads to a reduction in cutting forces, with positive effects on the machinability and optimized surface integrity. Ultrasonic assisted milling (USAM) offers great potential to address the major challenges posed by difficult-to-cut materials and additively manufactured weld structures. Therefore, this study focuses on assessing the transferability of previous positive results by USAM to the selected iron aluminide alloys. The machinability of the aluminides is analyzed by varying significant influencing variables in finish milling experiments and evaluated in terms of the loads on the tool and the resulting surface integrity. T2 - AA Meeting of Commission IX ‘Behavior of Metals subject to Welding’ CY - Rhodes, Greece DA - 08.07.2024 KW - Iron aluminide KW - Additive manufacturing KW - Machinability KW - Surface integrity KW - Ultrasonic-assisted milling PY - 2026 SP - 1 EP - 16 AN - OPUS4-65530 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -