TY - CONF A1 - Simón Muzás, Juan T1 - Mechanical properties of laser welded joints of wrought and heat treated PBF LB/M Inconel 718 parts depending on build direction N2 - Laser-based Powder Bed Fusion of Metal (PBF-LB/M) is a broadly used metal additive manufacturing (AM) method for fabricating complex metallic parts, whose sizes are however limited by the build envelope of PBF-LB/M machines. Laser welding arises as a valid joining method for effectively integrating these AM parts into larger assemblies. PBF-LB/M components must usually be stress-relieved before they can be separated from the build plate. An additional heat treatment can be beneficial for obtaining homogeneous mechanical properties across the seam or for the formation of desired precipitations in nickel-based-alloys. Therefore, the tensile performance of laser welded hybrid (AM/wrought) and AM-AM tensile samples of Inconel 718 is examined after undergoing three different heat treatments and considering three relevant build directions. It can be shown that the build orientation is an influencing factor on weld properties even after two applied heat treatments. T2 - Lasers in Manufacturing LiM 2023 CY - Munich, Germany DA - 26.06.2023 KW - Laser welding KW - PBF/LB-M KW - Hybrid components KW - Heat treatments KW - Build direction KW - Tensile performance KW - Inconel 718 PY - 2023 AN - OPUS4-58016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. A1 - Agudo Jácome, Leonardo A1 - Hilgenberg, Kai T1 - Influence of process-relevant parameters and heat treatments on the microstructure and resulting mechanical behavior of additively manufactured AlSi10Mg via Laser Powder Bed Fusion N2 - Within the group of additive manufacturing (AM) technologies for metals, laser powder bed fusion (L-PBF) has a leading position. Nevertheless, reproducibility of part properties has not reached sufficient maturity hindering the use for industrial applications especially for safety-relevant components. This article presents the results of various experimental tests performed with the aluminium alloy AlSi10Mg identifying reasons for the high deviations in mechanical properties. Herein, it is discussed how microstructure is influenced by different process parameters (laser power, scanning speed, energy density, building height) and how it can be adjusted by suitable post process heat treatments. The impact of resulting changes in microstructure is shown by monotonic tensile and cyclic fatigue tests considering specimens manufactured with different L-PBF machines. T2 - LiM 2021 CY - Online meeting DA - 21.06.2021 KW - Additive manufacturing KW - Laser powder bed fusion KW - AlSi10Mg PY - 2021 SP - 1 EP - 9 AN - OPUS4-52991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kempf, A. T1 - Influence of process-relevant parameters and heat treatments on the microstructure and resulting mechanical behavior of additively manufactured AlSi10Mg via Laser Powder Bed Fusion N2 - Within the group of additive manufacturing (AM) technologies for metals, laser powder bed fusion (L-PBF) has a leading position. Nevertheless, reproducibility of part properties has not reached sufficient maturity hindering the use for industrial applications especially for safety-relevant components. This article presents the results of various experimental tests performed with the aluminium alloy AlSi10Mg identifying reasons for the high deviations in mechanical properties. Herein, it is discussed how microstructure is influenced by different process parameters (laser power, scanning speed, energy density, building height) and how it can be adjusted by suitable post process heat treatments. The impact of resulting changes in microstructure is shown by monotonic tensile and cyclic fatigue tests considering specimens manufactured with different L-PBF machines. T2 - LiM 2021 CY - Online meeting DA - 21.06.2021 KW - Additive manufacturing KW - AlSi10Mg KW - Laser powder bed fusion PY - 2021 AN - OPUS4-53046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Merz, Benjamin A1 - Schmidt, Jonathan A1 - Poka, Konstantin A1 - Mohr, Gunther A1 - Polte, Julian A1 - Hilgenberg, Kai T1 - Impact of illumination technique on the detectability of irregularities in high-resolution images of visual in-situ process monitoring in Laser Powder Bed Fusion N2 - The layerwise geometry build-up of additive manufacturing (AM) enables the possibility of in-situ process monitoring. The objective is the detection of irregularities during the build cycle, ensuring component quality and process stability. Focus of this work is the visual in-situ monitoring of the process of powder bed fusion with laser beam of metals (PBF-LB/M). Current state of the art visual monitoring systems for PBF-LB/M are limited by low resolution, allowing the detection of gross flaws. In this work a 65 Mpixel high-resolution monochrome camera is integrated into a commercial PBF-LB/M machine enabling a spatial resolution of approx. 17.2 µm/Pixel. The observed inhomogeneities are clustered into directly detectable irregularities, and indirectly detectable irregularities that can be inferred from the surface. In parallel, two different illumination techniques are realized in the process chamber and compared. The impact of the distinct illumination technique, direct light and dark field, on the identification of irregularities is evaluated. KW - Powder bed fusion with laser beam of metals KW - In-situ monitoring KW - High-resolution camera KW - Illumination technique PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610929 DO - https://doi.org/10.1016/j.procir.2024.08.079 SN - 2212-8271 VL - 124 SP - 98 EP - 103 PB - Elsevier B.V. AN - OPUS4-61092 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Knobloch, Tim A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Concepts for bridging voids in metal additive manufacturing for repair of gas turbine blades using laser powder bed fusion N2 - One of the main advantages of additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) is the possibility to manufacture complex near-net-shape components. Therefore, the PBF-LB/M process is becoming increasingly important for the manufacturing and repair of gas turbine blades. Despite the great freedom in design, there are also limitations to the process. Manufacturing overhangs or bridging voids are some of the main challenges. In the conventional PBF-LB/M process, overhangs with angles up to 45° can be manufactured. However, gas turbine blades feature voids for cooling, which have to be bridged when using PBF-LB/M. In this work, different concepts for bridging voids are developed for future application in gas turbine blade repair. For this purpose, a test geometry is derived from the tip area of a gas turbine blade as a reference. By changing the initial geometry of the reference body, different designs for bridging voids are developed based on the PBF-LB/M requirements. Subsequently, these distinct designs are manufactured by PBF-LB/M. The different approaches are compared with respect to their volume increase. In addition, the specimens are visually inspected for warpage, shrinkage and imperfections by overheating. Out of the seven concepts developed, three concepts can be recommended for gas turbine blade repair based on low volume increase, distortion and shrinkage. T2 - Metal Additive Manufacturing Conference - MAMC 2022 CY - Graz, Austria DA - 26.09.2022 KW - Repair of gas turbine blades KW - Laser Powder Bed Fusion (PBF-LB/M) KW - Selective Laser Melting (SLM) KW - Design for Additive Manufacturing (DfAM) KW - Bridging voids KW - Supportless PY - 2022 SP - 19 EP - 28 PB - TU Graz CY - Graz AN - OPUS4-55868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Nilsson, R. A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - On the challenges of hybrid repair of gas turbine blades using laser powder bed fusion N2 - Additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) are rapidly gaining popularity in repair applications. Gas turbine components benefit from the hybrid repair process as only damaged areas are removed using conventional machining and rebuilt using an AM process. However, hybrid repair is associated with several challenges such as component fixation and precise geometry detection. This article introduces a novel fixturing system, including a sealing concept to prevent powder sag during the repair process. Furthermore, a high-resolution camera within an industrial PBF-LB/M machine is installed and used for object detection and laser recognition. Herein, process related inaccuracies such as PBF-LB/M laser drift is considered by detection of reference objects. This development is demonstrated by the repair of a representative gas turbine blade. The final offset between AM build-up and component is analysed. An approximate accuracy of 160 μm is achieved with the current setup. T2 - LiM 2023 CY - Munich, Germany DA - 26.06.2023 KW - Laser powder bed fusion KW - Additive manufacturing KW - Hybrid repair KW - Position detection KW - High-resolution camera PY - 2023 SP - 1 EP - 9 AN - OPUS4-57836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin T1 - On the challenges of hybrid repair of gas turbine blades using laser powder bed fusion N2 - Additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) are rapidly gaining popularity in repair applications. Gas turbine components benefit from the hybrid repair process as only damaged areas are removed using conventional machining and rebuilt using an AM process. However, hybrid repair is associated with several challenges such as component fixation and precise geometry detection. This article introduces a novel fixturing system, including a sealing concept to prevent powder sag during the repair process. Furthermore, a high-resolution camera within an industrial PBF-LB/M machine is installed and used for object detection and laser recognition. Herein, process related inaccuracies such as PBF-LB/M laser drift is considered by detection of reference objects. This development is demonstrated by the repair of a representative gas turbine blade. The final offset between AM build-up and component is analysed. An approximate accuracy of 160 μm is achieved with the current setup. T2 - LiM 2023 CY - Munich, Germany DA - 26.06.2023 KW - Laser powder bed fusion KW - Additive manufacturing KW - Hybrid repair KW - Position detection KW - High-resolution camera PY - 2023 AN - OPUS4-57837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Benjamin, Merz T1 - Advanced camera calibration for lens distortion correction in hybrid additive manufacturing processes N2 - Hybrid additive manufacturing is becoming increasingly important in the field of additive manufacturing. Hybrid approaches combine at least two different manufacturing processes. The focus of this work is the build-up of geometries onto conventionally manufactured parts using laser-based powder bed fusion of metals (PBF-LB/M). The hybrid build-up requires a precise position detection system inside the PBF-LB/M machines to determine the exact position of the existing component. For this purpose, high-resolution camera systems can be utilized. However, the use of a camera system is associated with several challenges. The captured images are subject to various distortions of the optical path. Due to these distortions, it is not possible to use the images for measurements and, therefore, it is not possible to calculate the positions of objects. In this study a homography matrix is calculated to correct keystone distortion in the images. Different calibration patterns have been tested for the calculation of the homography matrix. The influence of the number of calibration points on the precision of position detection of objects is determined. Furthermore, the influence of an additional camera calibration by using ChArUco boards is evaluated. The result is a camera calibration workflow with associated calibration pattern for a precise position detection of parts inside PBF-LB/M machines allowing a hybrid build-up with minimum physical offset between base component and build-up. T2 - euspen’s 24th International Conference & Exhibition CY - Dublin, Ireland DA - 10.06.2024 KW - Aditive Manufacturing KW - Hybrid build-up KW - Position detection KW - Camera calibration PY - 2024 AN - OPUS4-60600 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scheuschner, Nils A1 - Oster, Simon A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Comparison of NIR and SWIR thermography for defect detection in Laser Powder Bed Fusion N2 - Since laser powder bed fusion (PBF-LB/M) is prone to the formation of defects during the building process, a fundamental requirement for widespread application is to find ways to assure safety and reliability of the additively manufactured parts. A possible solution for this problem lies in the usage of in-situ thermographic monitoring for defect detection. In this contribution we investigate possibilities and limitations of the VIS/NIR wavelength range for defect detection. A VIS/NIR camera can be based on conventional silicon-based sensors which typically have much higher spatial and temporal resolution in the same price range but are more limited in the detectable temperature range than infrared sensors designed for longer wavelengths. To investigate the influence, we compared the thermographic signatures during the creation of artificially provoked defects by local parameter variations in test specimens made of a nickel alloy (UNS N07208) for two different wavelength ranges (~980 nm and ~1600 nm). KW - Laser powder bed fusion KW - PBF-LB/M KW - Thermography KW - Additive manufacturing KW - NDT PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610380 DO - https://doi.org/10.1016/j.procir.2024.08.122 VL - 124 SP - 301 EP - 304 PB - Elsevier B.V. AN - OPUS4-61038 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Breese, Philipp Peter T1 - Comparison of NIR and SWIR thermography for defect detection in laser powder bed fusion N2 - Since laser powder bed fusion (PBF-LB/M) is prone to the formation of defects during the building process, a fundamental requirement for widespread application is to find ways to assure safety and reliability of the additively manufactured parts. A possible solution for this problem lies in the usage of in-situ thermographic monitoring for defect detection. In this contribution we investigate possibilities and limitations of the VIS/NIR wavelength range for defect detection. A VIS/NIR camera can be based on conventional silicon-based sensors which typically have much higher spatial and temporal resolution in the same price range but are more limited in the detectable temperature range than infrared sensors designed for longer wavelengths. To investigate the influence, we compared the thermographic signatures during the creation of artificially provoked defects by local parameter variations in test specimens made of a nickel alloy (UNS N07208) for two different wavelength ranges (~980 nm and ~1600 nm). T2 - 13th CIRP Conference on Photonic Technologies - LANE 2024 CY - Fürth, Germany DA - 15.09.2024 KW - Additive Manufacturing KW - Laser Powder Bed Fusion KW - Nondestructive Testing KW - Defect Detection KW - Thermography PY - 2024 AN - OPUS4-61285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chaudry, Mohsin Ali A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Experimental and numerical comparison of heat accumulation during laser powder bed fusion of 316L stainless steel N2 - Heat accumulation during laser powder bed fusion (LPBF) of metallic build parts can adversely affect their microstructure and mechanical properties. To study the heat accumulation during 316L steel based parts manufactured by LPBF, a finite element method (FEM) based numerical study is carried out. For the investigation, a computationally efficient FEM based model, where the whole layer is simultaneously exposed to a heat source, is used. The simulation results are compared with experimental results to validate the numerical model. While considering different influencing factors such as volumetric energy density (VED) and inter-layer time (ILT), the FEM model is shown to successfully simulate the process of heat accumulation during LPBF based manufacturing of a cuboidal shaped geometry. It is shown that ILT and VED have a significant effect on heat accumulation. The validated numerical model provides a good basis for the optimization of processing parameters and geometries for a future investigation of a reduction of heat accumulation effects. Furthermore, it can be used to quickly provide preheating boundary conditions for detailed investigations by different model approaches at a finer scale for future studies. KW - Laser powder bed fusion KW - Finite element method KW - Heat accumulation KW - Inter-layer time PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545115 DO - https://doi.org/10.1007/s40964-022-00282-x SP - 1 EP - 13 PB - Springer AN - OPUS4-54511 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmidt, Jonathan A1 - Merz, Benjamin A1 - Poka, Konstantin A1 - Mohr, Gunther A1 - Hilgenberg, Kai T1 - Surface structure analysis using visual high-resolution in situ process monitoring in laser powder bed fusion N2 - Parameter studies are a common step in selecting process parameters for laser powder bed fusion of metals (PBF-LB/M). Density cubes are commonly used for this purpose. Density cubes manufactured with varied process parameters can exhibit distinguishable surface structures visible to the human eye. The layer-wise process enables such surface structures to be detected during manufacturing. However, industrial visual in situ monitoring systems for PBF-LB/M currently have limited resolution and are incapable of reliably capturing small differences in the surface structures. In this work, a 65 MPixel high-resolution monochrome camera was integrated into an industrial PBF-LB/M machine together with a high-intensity LED (light-emitting diode) bar. Post-exposure images were taken to analyse differences in light reflection of fused areas. It is revealed that the grey-level co-occurrence matrix can be used to quantify the visual surface structure of nickel-based superalloy Inconel®939 density cubes per layer. The properties of the grey-level co-occurrence matrix correlate to the energy input and the resulting porosity of density cubes. Low-energy samples containing lack of fusion flaws show an increased contrast in the grey-level co-occurrence matrix compared to specimens with optimal energy input. The potential of high-resolution images for quality assurance via in situ process monitoring in PBF-LB/M is further discussed. KW - Additive manufacturing KW - Powder bed fusion KW - In situ monitoring KW - Image processing KW - High resolution camera PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626685 DO - https://doi.org/10.1007/s40194-025-01955-1 SN - 1878-6669 SP - 1 EP - 15 PB - Springer Science and Business Media LLC AN - OPUS4-62668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - Repräsentative Prüfkörper – Ein Beitrag zur Komponentensicherheit beim pulverbettbasierten Laserstrahlschmelzen (PBF-LB/M) N2 - Die thermische Historie beim additiven Aufbau von komplexen Realkomponenten und geometrisch primitiven Prüfkörpern unterscheidet sich signifikant. Daraus können Eigenschaftsunterschiede resultieren, die zu unterschiedlichem Materialverhalten führen können. In diesem Vortrag wird das Konzept repräsentativer Probekörper eingeführt, das eine Übertragung thermischer Historien von komplexen Geometrien auf einfache Geometrien ermöglicht und hierdurch zu einer besseren Vergleichbarkeit der Werkstoffeigenschaften führen soll. T2 - Schweißen - Österreichs Fachmesse für Füge-, Trenn- und Beschichtungstechnik CY - Wels, Austria DA - 23.04.2024 KW - Additive manufacturing KW - Thermal history KW - Laboratory specimens KW - In situ monitoring KW - Representative specimens PY - 2024 AN - OPUS4-60261 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin T1 - Impact of illumination technique on the detectability of irregularities for in-situ process monitoring in PBF-LB/M N2 - The layerwise geometry build-up of additive manufacturing (AM) enables the possibility of in-situ process monitoring. The objective is the detection of irregularities during the build cycle, ensuring component quality and process stability. Focus of this work is the visual in-situ monitoring of the process of powder bed fusion with laser beam of metals (PBF-LB/M). Current state of the art visual monitoring systems for PBF-LB/M are limited by low resolution, allowing the detection of gross flaws. In this work a 65 Mpixel high-resolution monochrome camera is integrated into a commercial PBF-LB/M machine enabling a spatial resolution of approx. 17.2 µm/Pixel. The observed inhomogeneities are clustered into directly detectable irregularities, and indirectly detectable irregularities that can be inferred from the surface. In parallel, two different illumination techniques are realized in the process chamber and compared. The impact of the distinct illumination technique, direct light and dark field, on the identification of irregularities is evaluated. T2 - 13th CIRP Conference on Photonic Technologies [LANE 2024] CY - Fürth, Germany DA - 15.09.2024 KW - Powder bed fusion with laser beam of metals KW - In-situ monitoring KW - High-resolution camera KW - Illumination technique PY - 2024 AN - OPUS4-61094 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oster, Simon A1 - Breese, Philipp Peter A1 - Ulbricht, Alexander A1 - Mohr, Gunther A1 - Altenburg, Simon T1 - A deep learning framework for defect prediction based on thermographic in-situmonitoring in laser powder bed fusion N2 - The prediction of porosity is a crucial task for metal based additive manufacturing techniques such as laser powder bed fusion. Short wave infrared thermography as an in-situ monitoring tool enables the measurement of the surface radiosity during the laser exposure. Based on the thermogram data, the thermal history of the component can be reconstructed which is closely related to the resulting mechanical properties and to the formation of porosity in the part. In this study, we present a novel framework for the local prediction of porosity based on extracted features from thermogram data. The framework consists of a data pre-processing workflow and a supervised deep learning classifier architecture. The data pre-processing workflow generates samples from thermogram feature data by including feature information from multiple subsequent layers. Thereby, the prediction of the occurrence of complex process phenomena such as keyhole pores is enabled. A custom convolutional neural network model is used for classification. Themodel is trained and tested on a dataset from thermographic in-situ monitoring of the manufacturing of an AISI 316L stainless steel test component. The impact of the pre-processing parameters and the local void distribution on the classification performance is studied in detail. The presented model achieves an accuracy of 0.96 and an f1-Score of 0.86 for predicting keyhole porosity in small sub-volumes with a dimension of (700 × 700 × 50) μm3. Furthermore, we show that pre-processing parameters such as the porosity threshold for sample labeling and the number of included subsequent layers are influential for the model performance. Moreover, the model prediction is shown to be sensitive to local porosity changes although it is trained on binary labeled data that disregards the actual sample porosity. KW - Laser Powder Bed Fusion (PBF-LB/M, L-PBF) KW - Selective Laser Melting (SLM) KW - SWIR thermography KW - Online monitoring KW - Flaw detection KW - Machine learning KW - Convolutional neural networks (CNN) PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-575148 DO - https://doi.org/10.1007/s10845-023-02117-0 SN - 0956-5515 SP - 1 EP - 20 PB - Springer AN - OPUS4-57514 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Hilgenberg, Kai T1 - On the limitations of small cubes as test coupons for process parameter optimization in laser powder bed fusion of metals N2 - The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF LB/M) process. Development of material and machine specific process parameters is commonly based on results acquired from small cubic test coupons of about 10 mm edge length. Such cubes are usually used to conduct an optimization of process parameters to produce dense material. The parameters are then taken as the basis for the manufacturing of real part geometries. However, complex geometries go along with complex thermal histories during the manufacturing process, which can significantly differ from thermal conditions prevalent during the production of simply shaped test coupons. This may lead to unexpected and unpredicted local inhomogeneities of the microstructure and defect distribution in the final part and it is a root cause of reservations against the use of additive manufacturing for the production of safety relevant parts. In this study, the influence of changing thermal conditions on the resulting melt pool depth of 316L stainless steel specimens is demonstrated. A variation of thermo-graphically measured intrinsic preheating temperatures was triggered by an alteration of inter layer times and a variation of cross section areas of specimens for three distinct sets of process parameters. Correlations between the preheating temperature, the melt pool depth, and occurring defects were analyzed. The limited expressiveness of the results of small density cubes is revealed throughout the systematic investigation. Finally, a clear recommendation to consider thermal conditions in future process parameter optimizations is given. T2 - Icaleo 2023 CY - Chicago, IL, USA DA - 16.10.2023 KW - Additive manufacturing KW - Heat accumulation KW - Thermal history KW - In situ monitoring KW - Representative specimens KW - Thermography PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586558 DO - https://doi.org/10.2351/7.0001080 SN - 1042-346X VL - 35 IS - 4 SP - 1 EP - 10 AN - OPUS4-58655 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Altenburg, Simon A1 - Hilgenberg, Kai ED - Wei, Z. ED - Pang, J. T1 - On critical shifts of the process window due to heat accumulation in laser powder bed fusion N2 - Safety-critical applications of products manufactured by laser powder bed fusion (PBF-LB/M) are still limited to date. This is mainly due to a lack of knowledge regarding the complex relationship between process, structure, and resulting properties. The assurance of homogeneity of the microstructure and homogeneity of the occurrence and distribution of defects within complexly shaped geometries is still challenging. Unexpected and unpredicted local inhomogeneities may cause catastrophic failures. The identification of material specific and machine specific process parameter windows for production of fully dense simple laboratory specimens is state of the art. However, the incorporation of changing thermal conditions that a complexly shaped component can be faced with during the manufacturing process is often neglected at the stage of a process window determination. This study demonstrates the tremendous effect of changing part temperatures on the defect occurrence for the broadly used stainless steel alloy AISI 316L. Process intrinsic variations of the surface temperature are caused by heat accumulation which was measured by use of a temperature adjusted mid-wavelength infrared (MWIR) camera. Heat accumulation was triggered by simple yet effective temporal and geometrical restrictions of heat dissipation. This was realized by a variation of inter layer times and reduced cross section areas of the specimens. Differences in surface temperature of up to 800 K were measured. A severe development of keyhole porosity resulted from these distinct intrinsic preheating temperatures, revealing a shift of the process window towards unstable melting conditions. The presented results may serve as a warning to not solely rely on process parameter optimization without considering the actual process conditions a real component is faced with during the manufacturing process. Additionally, it motivates the development of representative test specimens. T2 - The 76th IIW Annual Assembly and International Conference On Welding And Joining (IIW 2023) CY - Singapore, Singapore DA - 16.07.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Laboratory specimens KW - Process parameter optimization KW - Heat accumulation KW - Keyhole porosity KW - Infrared thermography PY - 2023 SP - 1 EP - 8 AN - OPUS4-58024 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon A1 - Maierhofer, Christiane A1 - Mohr, Gunther A1 - Hilgenberg, Kai A1 - Ulbricht, Alexander A1 - Altenburg, Simon T1 - Investigation of the thermal history of L-PBF metal parts by feature extraction from in-situ SWIR thermography N2 - Laser powder bed fusion is used to create near net shape metal parts with a high degree of freedom in geometry design. When it comes to the production of safety critical components, a strict quality assurance is mandatory. An alternative to cost-intensive non-destructive testing of the produced parts is the utilization of in-situ process monitoring techniques. The formation of defects is linked to deviations of the local thermal history of the part from standard conditions. Therefore, one of the most promising monitoring techniques in additive manufacturing is thermography. In this study, features extracted from thermographic data are utilized to investigate the thermal history of cylindrical metal parts. The influence of process parameters, part geometry and scan strategy on the local heat distribution and on the resulting part porosity are presented. The suitability of the extracted features for in-situ process monitoring is discussed. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - SWIR camera KW - Additive manufacturing (AM) KW - Selective laser melting (SLM) KW - Laser beam melting (LBM) KW - In-situ monitoring KW - Infrared thermography PY - 2021 SN - 978-1-5106-4324-6 DO - https://doi.org/10.1117/12.2587913 VL - 11743 SP - 1 EP - 11 PB - SPIE - The international society for optics and photonics AN - OPUS4-52535 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scheuschner, Nils T1 - Infrared Thermography of the DED-LB/M and PBF LB/M processes N2 - Infrared thermography is a technique that allows to measure the temperatures of objects by analyzing the intensity of the thermal emission without the need of direct contact with very high spatial and temporal resolution. As the temperature is a fundamental factor for the additive manufacturing processes of metals, infrared thermography can provide experimental data that can be used for the validation of simulations and improving the understanding of the processes as well as for in-situ process monitoring for nondestructive evaluation (NDE) for quality control. In this talk we will provide an overview over the possibilities of state of the art thermographic in-situ monitoring systems for the DED-LB/M and PBF-LB/M processes and the challenges such as phase transitions and unknown emissivity values in respect to the determination of real temperatures. We define the requirements for different camera systems in various configurations and give examples on the selection of appropriate measurement parameters and data acquisition techniques as well as on techniques for data analysis and interpretation. Finally, we compare in-situ monitoring methods against post NDE methods by analyzing the advantages and disadvantages of both. This research was funded by BAM within the Focus Area Materials. T2 - Coupled2021 - IX International Conference on Coupled Problems in Science and Engineering CY - Online meeting DA - 13.06.2021 KW - Additive Manufacturing KW - Thermography KW - Direct Energy Deposition PY - 2021 AN - OPUS4-54399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Portella, Pedro Dolabella A1 - Ulbricht, Alexander A1 - Evans, Alexander A1 - Altenburg, Simon A1 - Ehlers, Henrik A1 - Hilgenberg, Kai A1 - Mohr, Gunther T1 - Monitoring additive manufacturing processes by using NDT methods N2 - In this presentation we discuss the online monitoring of metallic AM parts produced by the Laser Powder Bed Fusion (LPBF) process by using optical, thermographic and electromagnetic methods. In a first approach we present the detection of defects generated during the process and discuss how to improve these methods for the optimization of design and production of metallic AM parts. T2 - ABENDI - Workshop CY - Online meeting DA - 19.11.2020 KW - Additive Fertigung PY - 2020 AN - OPUS4-52042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon T1 - Defect prediction on the Base of Thermographic features in Laser Powder Bed Fusion Utilizing Machine Learning Algorithms N2 - Avoiding the formation of defects such as keyhole pores is a major challenge for the production of metal parts by Laser Powder Bed Fusion (LPBF). The use of in-situ monitoring by thermographic cameras is a promising approach to detect defects, however the data is hard to analyze by conventional algorithms. Therefore, we investigate the use of Machine Learning (ML) in this study, as it is a suitable tool to model complex processes with many influencing factors. A ML model for defect prediction is created based on features extracted from process thermograms. The porosity information calculated from an x-ray Micro Computed Tomography (µCT) scan is used as reference. Physical characteristics of the keyhole pore formation are incorporated into the model to increase the prediction accuracy. Based on the prediction result, the quality of the input data is inferred and future demands on in-situ monitoring of LPBF processes are derived. T2 - Additive Manufacturing Benchmarks 2022 CY - Bethesda, MA, USA DA - 14.08.2022 KW - Laser Powder Bed Fusion KW - Thermography KW - In-situ Monitoring KW - Machine Learning KW - Defect prediction PY - 2022 AN - OPUS4-55591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon T1 - Investigation of the thermal history of L-PBF metal parts by feature extraction from in-situ SWIR thermography N2 - Laser powder bed fusion is used to create near net shape metal parts with a high degree of freedom in geometry design. When it comes to the production of safety critical components, a strict quality assurance is mandatory. An alternative to cost-intensive non-destructive testing of the produced parts is the utilization of in-situ process monitoring techniques. The formation of defects is linked to deviations of the local thermal history of the part from standard conditions. Therefore, one of the most promising monitoring techniques in additive manufacturing is thermography. In this study, features extracted from thermographic data are utilized to investigate the thermal history of cylindrical metal parts. The influence of process parameters, part geometry and scan strategy on the local heat distribution and on the resulting part porosity are presented. The suitability of the extracted features for in-situ process monitoring is discussed. T2 - Thermosense: Thermal Infrared Applications XLIII CY - Online meeting DA - 12.04.2021 KW - SWIR camera KW - Additive manufacturing (AM) KW - Selective laser melting (SLM) KW - Laser beam melting (LBM) KW - In-situ monitoring KW - Infrared thermography PY - 2021 UR - https://www.spiedigitallibrary.org/conference-proceedings-of-spie/11743/117430C/Investigation-of-the-thermal-history-of-L-PBF-metal-parts/10.1117/12.2587913.short?SSO=1&tab=ArticleLink AN - OPUS4-52540 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Oster, Simon T1 - Defect prediction in laser powder bed fusion based on thermographic features utilizing convolutional neural networks N2 - The appearance of irregularities such as keyhole porosity is a major challenge for the production of metal parts by laser powder bed fusion (PBF-LB/M). The utilization of thermographic in-situ monitoring is a promising approach to extract the thermal history which is closely related to the formation of irregularities. In this study, we investigate the utilization of convolutional neural networks to predict keyhole porosity based on thermographic features. Here, the porosity information calculated from an x-ray micro computed tomography scan is used as reference. Feature engineering is performed to enable the model to learn the complex physical characteristics of the porosity formation. The model is examined with regard to the choice of hyperparameters, the significance of thermal features and characteristics of the data acquisition. Based on the results, future demands on irregularity prediction in PBF-LB/M are derived. T2 - GIMC SIMAI YOUNG 2022 CY - Pavia, Italy DA - 29.09.2022 KW - Laser Powder Bed Fusion KW - Thermography KW - In-situ Monitoring KW - Convolutional Neural Networks PY - 2022 AN - OPUS4-56331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - Prozessinduzierte Vorerwärmung beim pulverbasierten Laserstrahlschmelzen und deren Auswirkung auf die Bauteileigenschaften austenitischer Stahlbauteile N2 - Heterogene Fehlstellendichten und Mikrostrukturausbildungen sind große Heraus-forderungen für den Einsatz des pulverbettbasierten Laserstrahlschmelzens (L PBF) besonders für sicherheitskritische Bauteile. Unter der Vielzahl an Einflussfaktoren auf die Qualität und die mechanischen Eigenschaften von L PBF-Bauteilen hat die Zwischenlagenzeit (ILT) bisher wenig Beachtung gefunden. Sie nimmt ebenso wie die Bauteilgeometrie Einfluss auf die thermische Historie während der Fertigung. Ihr Einfluss auf die intrinsische Vorerwärmung ist in Kombination mit der Bauteilhöhe mittels thermografischer Temperaturmessung untersucht worden. Signifikante Unterschiede in der thermischen Historie konnten dabei mit variierenden Schmelzbaddimensionen, Korngrößen und Fehlstellendichten am Beispiel der austenitischen Stahllegierung AISI 316L in Zusammenhang gebracht werden. T2 - DVM Tagung Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 03.11.2021 KW - Additive Manufacturing KW - Laser powder bed fusion KW - In-situ process monitoring PY - 2021 AN - OPUS4-53729 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther A1 - Hilgenberg, Kai ED - Eiber, M. T1 - Prozessinduzierte Vorerwärmung beim pulverbettbasierten Laserstrahlschmelzen und deren Auswirkung auf die Bauteileigenschaften austenitischer Stahlbauteile N2 - Heterogene Fehlstellendichten und Mikrostrukturausbildungen sind große Herausforderungen für den Einsatz des pulverbettbasierten Laserstrahlschmelzens (L PBF) besonders für sicherheitskritische Bauteile. Unter der Vielzahl an Einflussfaktoren auf die Qualität und die mechanischen Eigenschaften von L PBF-Bauteilen hat die Zwischenlagenzeit (ILT) bisher wenig Beachtung gefunden. Sie nimmt ebenso wie die Bauteilgeometrie Einfluss auf die thermische Historie während der Fertigung. Ihr Einfluss auf die intrinsische Vorerwärmung ist in Kombination mit der Bauteilhöhe mittels thermografischer Temperaturmessung untersucht worden. Signifikante Unterschiede in der thermischen Historie konnten dabei mit variierenden Schmelzbaddimensionen, Korngrößen und Fehlstellendichten am Beispiel der austenitischen Stahllegierung AISI 316L in Zusammenhang gebracht werden. T2 - DVM 6. Tagung Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 03.11.2021 KW - Additive Fertigung KW - Laserstrahlschmelzen KW - In-situ Prozessüberwachung KW - Wärmeakkumulation KW - Zwischenlagenzeit PY - 2021 DO - https://doi.org/10.48447/Add-2021-003 SP - 19 EP - 30 PB - Deutscher Verband für Materialforschung und -prüfung (DVM) CY - Berlin AN - OPUS4-54287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin T1 - Concepts for bridging voids in metal additive manufacturing for repair of gas turbine blades using laser powder bed fusion N2 - One of the main advantages of additive manufacturing (AM) processes such as laser powder bed fusion (PBF-LB/M) is the possibility to manufacture complex near-net-shape components. Therefore, the PBF-LB/M process is becoming increasingly important for the manufacturing and repair of gas turbine blades. Despite the great freedom in design, there are also limitations to the process. Manufacturing overhangs or bridging voids are some of the main challenges. In the conventional PBF-LB/M process, overhangs with angles up to 45° can be manufactured. However, gas turbine blades feature voids for cooling, which have to be bridged when using PBF-LB/M. In this work, different concepts for bridging voids are developed for future application in gas turbine blade repair. For this purpose, a test geometry is derived from the tip area of a gas turbine blade as a reference. By changing the initial geometry of the reference body, different designs for bridging voids are developed based on the PBF-LB/M requirements. Subsequently, these distinct designs are manufactured by PBF-LB/M. The different approaches are compared with respect to their volume increase. In addition, the specimens are visually inspected for warpage, shrinkage and imperfections by overheating. Out of the seven concepts developed, three concepts can be recommended for gas turbine blade repair based on low volume increase, distortion and shrinkage. T2 - Metal Additive Manufacturing Conference - MAMC 2022 CY - Graz, Austria DA - 26.09.2022 KW - Laser Powder Bed Fusion (PBF-LB/M) KW - Selective Laser Melting (SLM) KW - Design for Additive Manufacturing (DfAM) KW - Repair of gas turbine blades KW - Bridging voids KW - Supportless PY - 2022 AN - OPUS4-55869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Merz, Benjamin T1 - Position Detection for Hybrid Repair of gas turbine blades using PBF-LB/M N2 - This poster presents a workflow for camera-based position detection of components within PBF-LB/M machines. This enables a hybrid repair process of highly stressed components such as gas turbine blades using PBF-LB/M. T2 - Kuratoriumsführung CY - Berlin, Germany DA - 21.06.2022 KW - Additive Manufacturing KW - PBF-LB/M KW - Position detection KW - Camera KW - Image processing PY - 2022 AN - OPUS4-56587 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Waske, Anja T1 - A unique Authenticator for additively manufactured parts N2 - Components produced using additive manufacturing can be marked for unique identification and secure authentication [1,2]. Serial numbers and machine-readable codes can be used to identify the component, and link digital product-related data (i.e., a digital product passport) to the actual components. The most prevailing solution consists of local process manipulation, such as printing a quick response (QR) code [3] or a set of blind holes on the surface of the internal cavity of hollow components. However, local manipulation of components may alter the properties, and external tagging features can be altered or even removed by post-processing treatments. This work therefore aims to provide a new methodology for identification, authentication, and traceability of additively manufactured (AM) components using microstructural features that are unique to each part. X-ray computed tomography (XCT) was employed to image the microstructural features of AlSi10Mg parts. Based on size and geometry, the most prominent features were selected to create a unique digital authenticator. We implemented a framework in Python using open-access modules that can successfully create a digital object authenticator using the segmented microstructure information from XCT. The authenticator is stored as a QR code, along with the 3D information of the selected features. T2 - DGM Additive Berlin 2024 CY - Berlin, Germany DA - 12.06.2024 KW - Additive Fertigung KW - Authentifizierung KW - Mikrostruktur PY - 2024 AN - OPUS4-60957 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Portella, Pedro Dolabella T1 - Monitoring additive manufacturing N2 - Additive manufacturing (AM) processes allow a high level of freedom in designing and producing components for complex structures. They offer the possibility of a significant reduction of the process chain. However, the large number of process parameters influence the structure and the behavior of AM parts. A thorough understanding of the interdependent mechanisms is necessary for the reliable design and production of safe AM parts. In this presentation we discuss the online monitoring of metallic AM parts produced by the Laser Powder Bed Fusion (LPBF) process by using optical, thermographic and electromagnetic methods. In a first approach we present the detection of defects generated during the process and discuss how to improve these methods for the optimization of design and production of metallic AM parts. T2 - Conaendi&IEV 2021 CY - Online meeting DA - 10.03.2021 KW - Additive Fertigung PY - 2021 AN - OPUS4-52241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gupta, Kanhaiya A1 - Poka, Konstantin A1 - Ulbricht, Alexander A1 - Waske, Anja T1 - Identification and authentication of additively manufactured components using their microstructural fingerprint N2 - In the field of additive manufacturing, the ability to uniquely identify and authenticate parts is crucial for certification, logistics, and anti-counterfeiting efforts. This study introduces a novel methodology that leverages the intrinsic microstructural features of additively manufactured components for their identification, authentication, and traceability. Unlike traditional tagging methods, such as embedding QR codes on the surface or within the volume of parts, this approach requires no alteration to the printing process, as it utilizes naturally occurring microstructural characteristics. The proposed workflow involves the analysis of 3D micro-computed tomography data to identify specific voids that meet predefined identification criteria. This method is demonstrated on a batch of 24 parts manufactured with identical process parameters, proving capable of achieving unambiguous identification and authentication. By establishing a tamper-proof link between the physical part and its digital counterpart, this methodology effectively bridges the physical and digital realms. This not only enhances the traceability of additively manufactured parts but also provides a robust tool for integrating digital materials, parts databases, and product passports with their physical counterparts. KW - Authentication KW - Additive manufacturing KW - X-ray Computed Tomography KW - Digital fingerprint KW - Unique identification PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630356 DO - https://doi.org/10.1016/j.matdes.2025.113986 SN - 1873-4197 VL - 254 SP - 1 EP - 12 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-63035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - On the limitations of small cubes as test coupons for process parameter optimization in laser powder bed fusion of metals N2 - The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF LB/M) process. Development of material and machine specific process parameters is commonly based on results acquired from small cubic test coupons of about 10 mm edge length. Such cubes are usually used to conduct an optimization of process parameters to produce dense material. The parameters are then taken as the basis for the manufacturing of real part geometries. However, complex geometries go along with complex thermal histories during the manufacturing process, which can significantly differ from thermal conditions prevalent during the production of simply shaped test coupons. This may lead to unexpected and unpredicted local inhomogeneities of the microstructure and defect distribution in the final part and it is a root cause of reservations against the use of additive manufacturing for the production of safety relevant parts. In this study, the influence of changing thermal conditions on the resulting melt pool depth of 316L stainless steel specimens is demonstrated. A variation of thermo-graphically measured intrinsic preheating temperatures was triggered by an alteration of inter layer times and a variation of cross section areas of specimens for three distinct sets of process parameters. Correlations between the preheating temperature, the melt pool depth, and occurring defects were analyzed. The limited expressiveness of the results of small density cubes is revealed throughout the systematic investigation. Finally, a clear recommendation to consider thermal conditions in future process parameter optimizations is given. T2 - Icaleo 2023 CY - Chicago, IL, USA DA - 16.10.2023 KW - Additive manufacturing KW - Heat accumulation KW - Thermal history KW - In situ monitoring KW - Representative specimens KW - Thermography PY - 2023 AN - OPUS4-58656 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - On critical shifts of the process window due to heat accumulation in laser powder bed fusion N2 - Safety-critical applications of products manufactured by laser powder bed fusion (PBF-LB/M) are still limited to date. This is mainly due to a lack of knowledge regarding the complex relationship between process, structure, and resulting properties. The assurance of homogeneity of the microstructure and homogeneity of the occurrence and distribution of defects within complexly shaped geometries is still challenging. Unexpected and unpredicted local inhomogeneities may cause catastrophic failures. The identification of material specific and machine specific process parameter windows for production of fully dense simple laboratory specimens is state of the art. However, the incorporation of changing thermal conditions that a complexly shaped component can be faced with during the manufacturing process is often neglected at the stage of a process window determination. This study demonstrates the tremendous effect of changing part temperatures on the defect occurrence for the broadly used stainless steel alloy AISI 316L. Process intrinsic variations of the surface temperature are caused by heat accumulation which was measured by use of a temperature adjusted mid-wavelength infrared (MWIR) camera. Heat accumulation was triggered by simple yet effective temporal and geometrical restrictions of heat dissipation. This was realized by a variation of inter layer times and reduced cross section areas of the specimens. Differences in surface temperature of up to 800 K were measured. A severe development of keyhole porosity resulted from these distinct intrinsic preheating temperatures, revealing a shift of the process window towards unstable melting conditions. The presented results may serve as a warning to not solely rely on process parameter optimization without considering the actual process conditions a real component is faced with during the manufacturing process. Additionally, it motivates the development of representative test specimens. T2 - The 76th IIW annual assembly and international conference on welding and joining CY - Singapore DA - 16.07.2023 KW - Additive manufacturing KW - Laser powder bed fusion KW - Laboratory specimens KW - Process parameter optimization KW - Heat accumulation KW - Keyhole porosity KW - Infrared thermography PY - 2023 AN - OPUS4-58023 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - Effects of inter layer time and build height on resulting properties of 316L stainless steel processed by laser powder bed fusion N2 - Das pulverbettbasierte selektive Laserstrahlschmelzen (engl. laser powder bed fusion, L-PBF) ist die am weitesten verbreitete additive Fertigungstechnologie für die Herstellung metallischer Komponenten. Unter der Vielzahl an Einflussfaktoren auf die Qualität und die mechanischen Eigenschaften von L PBF-Bauteilen hat die Zwischenlagenzeit (engl. inter layer time, ILT) bisher kaum Beachtung in der wissenschaftlichen Literatur gefunden, obwohl sie je nach Bauraumausnutzungsgrad stark variieren kann. In diesem Vortrag werden Ergebnisse einer Studie präsentiert, die den Einfluss der ILT in Kombination mit der Bauteilhöhe und unter Berücksichtigung verschiedener Volumenenergiedichten am Beispiel der austenitischen Stahllegierung AISI 316L untersucht. Die Fertigungsprozesse wurden in situ mittels Thermographiekamera überwacht, sodass Informationen über das Abkühlverhalten der Bauteile während des Prozesses gewonnen werden konnten. Es wurden signifikante Effekte der ILT und der Bauteilhöhe auf Wärmeakkumulation, Mikrostruktur, Schmelzbadgeometrie und Härte festgestellt. Ferner konnte ein Anstieg von Defektdichten bei einem gegenseitigen Wechselspiel aus Bauteilhöhe und ILT aufgezeigt werden. Die Zwischenlagenzeit wurde somit als kritischer Faktor für die L-PBF-Fertigung von Realbauteilen identifiziert. T2 - Workshop In-situ Monitoring and Microstructure Development in Additive Manufactured Alloys CY - Online meeting DA - 19.04.2021 KW - Infrared thermography KW - Laser Powder Bed Fusion (L-PBF) KW - Selective Laser Melting (SLM) KW - Additive Manufacturing (AM) KW - Process monitoring PY - 2021 AN - OPUS4-52699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Tales from Within: Residual Stress and Void Formation in LPBF 316L N2 - An unusual microstructure, inherent residual stresses and void formation are the three key aspects to control when assessing metallic parts made by LPBF. This talk explains an experiment to unravel the interlinked influence of the two mechanisms for the formation of residual stresses in LPBF: the temperature gradient mechanism and constricted solidification shrinkage. The impact of each mechanism on the shape and magnitudes of the residual stress distribution is described. Combined results from neutron diffraction, X-ray diffraction, computed tomography and in-situ thermography are presented. Also, influence of scan strategies as well as surface roughness of subjacent layers on void formation is shown. Results from computed tomography and in-situ thermography of a specimen dedicated to study the interaction of the melt pool with layers of powder underneath the currently illuminated surface are presented. T2 - 2nd Workshop on In-situ Monitoring and Microstructure Development in Additive Manufacturing CY - Online meeting DA - 19.04.2021 KW - Neutron diffraction KW - Laser powder bed fusion KW - In-situ thermography KW - Computed tomography KW - X-ray diffraction KW - Residual stress KW - Pore formation KW - AISI 316L PY - 2021 AN - OPUS4-52819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simón Muzás, Juan T1 - Weldability of PBF-LB/M Inconel 718 lattice structures by laser beam N2 - The present research focuses on the weldability of PBF-LB/M lattice structure parts of Inconel 718 by means of laser beam welding. The integration of complex and lightweight AM structures into assemblies employing conventional joining methods is challenging. During the welding process, dissipation of the laser heat input through thin-walled structures of these lightweight structures is strongly limited, resulting in heat accumulation, atypical cooling rates, and affecting weld geometry, quality of the joint and microstructure. PBF-LB/M parts have been manufactured in three characteristic build directions. They were all stress relieved, then a group of them were submitted to an additional solution annealing and the second group to a two-step aging treatment. Afterwards, these parts were welded to identical PBF-LB/M parts and to wrought ones in butt position. To gain insight into the welding temperature field and to explain segregation mechanisms, grain growth and asymmetries, thermocouples have been attached on the surface’s regions and struts nearby. Joining a lattice structure with a full material wrought sample results in clear asymmetric welds due to dissimilar heat dissipation on both sides of the seam. Selected pre-weld heat treatments have a crucial influence on the quality of the seam on the AM part. T2 - International Institute of Welding IIW 2023 Conference CY - Singapore DA - 16.07.2023 KW - Additive manufacturing (AM) KW - Laser-based powder bed fusion of metal (PBF-LB/M) KW - Laser beam welding KW - Lattice structure KW - Hybrid part KW - Heat treatment KW - Inconel 718 PY - 2023 AN - OPUS4-58017 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simón Muzás, Juan A1 - Brunner-Schwer, Christian A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - Mechanical properties of laser welded joints of wrought and heat treated PBF LB/M Inconel 718 parts depending on build direction N2 - Laser-based Powder Bed Fusion of Metal (PBF-LB/M) is a broadly used metal additive manufacturing (AM) method for fabricating complex metallic parts, whose sizes are however limited by the build envelope of PBF-LB/M machines. Laser welding arises as a valid joining method for effectively integrating these AM parts into larger assemblies. PBF-LB/M components must usually be stress-relieved before they can be separated from the build plate. An additional heat treatment can be beneficial for obtaining homogeneous mechanical properties across the seam or for the formation of desired precipitations in nickel-based-alloys. Therefore, the tensile performance of laser welded hybrid (AM/wrought) and AM-AM tensile samples of Inconel 718 is examined after undergoing three different heat treatments and considering three relevant build directions. It can be shown that the build orientation is an influencing factor on weld properties even after two applied heat treatments. T2 - Lasers in Manufacturing LiM 2023 CY - Munich, Germany DA - 26.09.2023 KW - Inconel 718 KW - Laser welding KW - PBF/LB-M KW - Hybrid components KW - Heat treatments KW - Build direction KW - Tensile performance PY - 2023 SP - 1 EP - 10 PB - Proceedings Lasers in Manufacturing 2023 CY - München AN - OPUS4-58394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simón Muzás, Juan T1 - Mitigation of liquation cracking in laser welding of pairs of L-PBF processed and wrought plates of Inconel 718 N2 - Laser welding is an appropriate technique for joining Laser Powder Bed Fusion (L-PBF) parts together and to conventional wrought ones. The potential consists of profiting from synergies between additive and conventional manufacturing methods and overcoming the existing limitations of both. On the one hand, L-PBF is a widely spread metal-based additive manufacturing technique suitable for generating complex parts which can present intrinsic designed cavities, conformal cooling channels, and filigree structures contributing to sustainable manufacturing and efficiency-oriented designs. On the other hand, chamber sizes for producing L-PBF parts are limited, and the process is time-consuming. Thus, its employment is not for every geometry justified. Additionally, they are in most cases individual elements of a larger assembly and need to be joined together to conventionally fabricated parts. The present research suggests laser welding parameters to adequately bond pairs of wrought and L-PBF processed plates and two L-PBF plates of Inconel 718 in butt position. L-PBF samples are printed in three different build-up orientations. Additionally, the influence of as-built L-PBF roughness qualities and usual pre-weld preparations such as edge milling are examined. The effect of normed pre-weld heat treatments is also contemplated. Identified cracks are analyzed by means of EDS in order to confirm the present phases on the areas of interest. EBSD is also employed to obtain a clear depiction of the crystallographic texture and distribution of the hot cracks. The quality of the weldment was examined according to existing standards. Substantial differences in seam geometry and microstructure across different edge’s surface qualities and build directions of stress relieved L-PBF parts have not been detected. Nevertheless, even if no other irregularities are present in the seam, variability in liquation cracking susceptibility has been confirmed. This defect is prone to happen when parts made of this nickel-based superalloy are welded together when not enough precautions are taken. It has been determined that grain size and ductility of the material before welding play a crucial role and mitigating or intensifying these imperfections. Moreover, recommendations are presented to avoid this potential welding defect. T2 - International Welding Conference CY - Tokyo, Japan DA - 17.07.2022 KW - Hybrid Part KW - Liquation Cracking KW - Build-up Orientation KW - Pre-weld Preparation KW - Heat Treatment KW - Selective Laser Melting (SLM) KW - Inconel 718 KW - Laser Powder Bed Fusion (L-PBF) KW - Laser Welding (LW) PY - 2022 AN - OPUS4-55515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Poka, Konstantin A1 - Ali, Sozol A1 - Ulbricht, Alexander A1 - Schröder, Jakob A1 - Khambayat, Jiganesh A1 - Scholz, Maik A1 - Saeed, Waleed A1 - Merz, Benjamin A1 - Epperlein, Martin A1 - Hilgenberg, Kai T1 - Reduction of extraneous variance in powder bed fusion with laser beam of metals by means of advanced digital preprocessing N2 - Data-driven quality assurance and reproducibility are critical for advancing the industrial maturity of Powder Bed Fusion with Laser Beam of Metals (PBF-LB/M). This study addresses the extraneous variance in scan vectors that arises even for identical cross sections of nominally identical components but located at different positions on the build platform. This inherent variance, common across most PBF-LB/M machines, is caused by scan vector computation relative to the machine coordinate origin and subsequent projection of the resulting pattern onto individual component cross sections. In this work, scan vectors are computed still following conventional slicing, but relative to the workpiece origin of each component, using an EOS M 300-4. This digital preprocessing approach homogenizes fabrication conditions, ensuring that anomalies, such as scan vector overlaps, occur consistently across identical components. The impact during fabrication is assessed through powder bed imaging, melt pool monitoring, and operational data from the multilaser PBF-LB/M machine. Components are manufactured from AlSi10Mg for each scan vector computation origin and subsequently qualified using x-ray computed tomography, optical coordinate measurement, and optical surface measurement. A comprehensive evaluation is conducted, comparing the results in terms of component density, geometric accuracy, and surface roughness to those obtained using conventional preprocessing. Based on these findings, practical recommendations are provided, focusing on achieved quality criteria to identify potential drawbacks, while also considering the life cycle analysis of fabrication. Finally, the study emphasizes the significance of consistent scan vector provisioning for identical components placed at different build platform positions, assuming no roll or pitch during nesting. T2 - ICALEO CY - Orlando, FL, USA DA - 13.10.2025 KW - Quality assurance KW - Data management KW - 3D printing KW - Laser fabrication KW - Life cycle analysis PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642104 DO - https://doi.org/10.2351/7.0001890 SN - 1042-346X VL - 37 IS - 4 SP - 1 EP - 14 PB - American Institute of Physics Publishing CY - New York AN - OPUS4-64210 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hilgenberg, Kai T1 - Redesign, Repair, Recycle: R-Strategien bei der additiven Fertigung N2 - Der Vortrag stellt ausgewählte Beispiele aus Projekten des Kompetenzzentrums AM@BAM vor, die das Potenzial der additiven Fertigung bei der Umsetzung von R-Strategien im Kontext der Kreislaufwirtschaft aufzeigen. PBF-LB/M kann genutzt werden für ein Redesign von Komponenten mit dem Ziel der Gewicht- und Materialeinsparung. Das gleiche Verfahren wie auch DED-ARC und das Kaltgasspritzen können für die Reparatur anspruchsvoller Legierungen oder Geometrien genutzt werden. Das Thema Recycling wird am Beispiel der Wiedernutzung von Pulver aus dem PBF-LB/M-Prozess adressiert. T2 - DVM-Tagung: Strukturfestigkeit und Produktlebenszyklus – Vom Design bis zur Kreislaufwirtschaft CY - Berlin, Germany DA - 07.10.2025 KW - Additive Fertigung KW - R-Strategien KW - Repair KW - Reparatur PY - 2025 AN - OPUS4-64324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Raute, Julius A1 - Schmidt, Jonathan A1 - Jokisch, Torsten A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Prozessführung und erreichbare Nahtqualitäten: Elektronenstrahlschweißen von additiv gefertigtem Inconel 939 N2 - Additive Fertigungstechnologien wie das Laser-Pulverbett-Verfahren bieten großes Potenzial für die Fertigung von Neu und Ersatzteilen für stationäre Gasturbinen aus Nickelsuperlegierungen wie Inconel 939 (IN939). Um die Integration in bestehende Baugruppen zu ermöglichen und Bauraumbeschränkungen zu überwinden, muss die Prozesskette der additiven Fertigung um geeignete Fügetechniken erweitert werden. Die vorliegende Arbeit beschäftigt sich daher mit dem Schweißen von Inconel 939. Hierbei werden Bleche aus Gussmaterial und der additiven Herstellung mittels Laser im Pulverbett beim Elektronenstrahlschweißen verglichen. Im Fokus der Untersuchung stehen die erreichbare Nahtqualität im Hinblick auf geometrische Unregelmäßigkeiten sowie innere Defekte in Form von Mikrorissen in der Wärmeeinflusszone. Bei der Auswertung der geschweißten Proben zeigen sich keine Unterschiede in der Ausbildung der Nahtform zwischen dem additiv gefertigten Material und dem Gusswerkstoff. Für beide Materialien ließ sich bei hohen Vorschubgeschwindigkeiten von 20 mm/s die höchste Bewertungsgruppe für Strahlgeschweißte Nähte nach DIN EN ISO 13919-1 erreichen. Unabhängig von der Herstellungsart zeigen beide Materialien eine Zunahme der Rissneigung mit steigendem Vorschub. Das Material aus der additiven Herstellung weist aufgrund seiner Mikrostruktur insgesamt jedoch deutlich weniger Mikrorisse auf, was Potenzial für die Anwendung in der Praxis eröffnet. KW - Elektronenstrahlschweißen KW - PBF-LB/M KW - Inconell939 PY - 2025 UR - https://www.schweissenundschneiden.de/artikel/prozessfuehrung-und-erreichbare-naht-qualitaeten-elektronenstrahlschweissen-von-additiv-gefertigtem-inconel-939 DO - https://doi.org/10.53192/SUS202510 VL - 77 IS - 10 SP - 2 EP - 8 PB - DVS Media Verlag CY - Eltville am Rhein, Deutschland AN - OPUS4-64300 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mohr, Gunther T1 - Comparability issues of test specimens in laser powder bed fusion - how to consider differences in thermal history of complex components and primitive test specimens N2 - The capability to produce complexly and individually shaped metallic parts is one of the main advantages of the laser powder bed fusion (PBF-LB/M) process. However, the thermal history during additive manufacturing of complex components can differ significantly from the thermal history of geometrically primitive test specimens. This can result in divergent microstructures and resulting mechanical properties. It drastically limits the comparability of different built parts and requires expensive full component testing. Moreover, the thermal history as the spatiotemporal temperature distribution has been identified as a major cause for flaw formation. Therefore, it can be hypothesized that a similar thermal history between components and test specimens enhances their comparability. In this talk, the concept of representative test specimens is introduced, which enables the transfer of thermal histories from complex geometries to simple geometries, which can lead to better comparability of material properties. T2 - 4th Asia-Pacific International Conference on Additive Manufacturing (APICAM) CY - Melbourne, Australia DA - 30.06.2025 KW - Additive Manufacturing PY - 2025 AN - OPUS4-64527 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin T1 - Digitale Werkzeuge für eine datengetriebene Qualitätssicherung N2 - Der Vortrag stellt die in QI-Digital entwickelten und geplanten Werkzeuge einer digitalen Qualitätsinfrastruktur für die Additive Fertigung vor. Thematisiert werden u.a. die Verwaltungsschale und genormte Datenstrukturen im Kontext der Additiven Fertigung. Im Fokus steht hier die datengetriebene Qualitätssicherung. T2 - Jahrestreffen der VDMA Arbeitsgemeinschaft Additive Fertigung CY - Pegnitz, Germany DA - 13.10.2025 KW - Additive Fertigung KW - PBF-LB/M KW - Digitalisierung PY - 2025 AN - OPUS4-64402 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin T1 - Datengetriebene Qualitätssicherung für den PBF-LB/M Prozess N2 - Der Vortrag gibt einen Überblick über die aktuellen Aktivitäten im QI-Digital Use Case Additive Fertigung. Der Fokus liegt hier auf einer digitalen Qualitätssicherung. T2 - Symposium „Additive Fertigung: Pulverbasiertes Schmelzen mittels Laserstrahl“ CY - Leipzig, Germany DA - 14.08.2025 KW - Additive Fertigung KW - PBF-LB/M KW - Digitalisierung PY - 2025 AN - OPUS4-64400 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin T1 - Normungsaktivitäten in QI-Digital N2 - Der Vortrag thematisiert die Normungsaktivitäten in QI-Digital. Insbesondere die entwickelte Datenstruktur in der ISO/ASTM 52970 und die Anknüpfungspunkte zur Verwaltungsschale. Die ISO TC 261 / JG 85 und ihr entsprechender Scope werden vorgestellt. T2 - Sitzung des DIN NA-145-04-01 AA CY - Darmstadt, Germany DA - 01.04.2025 KW - Additive Fertigung KW - PBF-LB/M KW - Digitalisierung PY - 2025 AN - OPUS4-64403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Epperlein, Martin T1 - ISO TC 261 / JG 85 Projects N2 - Dieser Vortrag fasst die laufenden Aktivitäten der ISO TC 261 JG 85 zusammen. Insbesondere die Gewinnung und Verarbeitung von PBF-LB/M Prozessdaten steht im Fokus. T2 - ISO TC 261 / ASTM F.42 Meeting CY - Manila, Philippines DA - 22.09.2025 KW - Additive Fertigung KW - PBF-LB/M KW - Digitalisierung PY - 2025 AN - OPUS4-64399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Jonathan T1 - High resolution visual in-situ process monitoring in SONRISA N2 - The LuFo Project "SONRISA" presented an update on its objectives for the coming years to Working Group 3 – In-Situ Process Monitoring – during the EASA/FAA Additive Manufacturing Workshop 2025. As part of this update, BAM provided a brief overview of its prior work in high-resolution visual in-situ process monitoring for PBF-LB/M, which will be integrated into the project. The presentation included a comparison between the BAM system and the OEM in-situ monitoring system “EOSTATE PowderBed” and an outline of the correlation between texture contrast and the occurrence of lack-of-fusion anomalies in high resolution after exposure images.g. T2 - EASA–FAA AM Workshop 2025 CY - Cologne, Germany DA - 21.10.2025 KW - Additive manufacturing KW - High resolution camera KW - Lack of fusion PY - 2025 AN - OPUS4-64456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davila, Josue T1 - Einfluss des initialen Pulveroxidationsgrads auf die prozessinduzierte Materialdegradation beim PBF-LB/M Prozess N2 - Die vorliegende Studie untersucht den Einfluss unterschiedlicher Oxidationsgrade des im PBF-LB/M-Prozess verwendeten Ausgangspulvers auf dessen Degradation am Beispiel der Nickelbasis-Superlegierung Haynes 282. Zu diesem Zweck wurden vier Pulverbatches mit Sauerstoffgehalten zwischen etwa 140 ppm und 1400 ppm mittels PBF-LB/M verarbeitet. Zur gezielten Entnahme aufgeschmolzener Pulverpartikel aus wärmebeeinflussten Bereichen des Pulverbetts wurde ein spezieller Auffangbehälter konstruiert und mitgedruckt. Der Beschichtungs- und Schmelzprozess verlief störungsfrei. Bei höheren Oxidationsgraden wurde jedoch eine verstärkte Rauchentwicklung beobachtet, was erste Hinweise auf eine intensivere Spritzerbildung lieferte. Die Untersuchungen nach dem Bauprozess ergaben, dass insbesondere die feinen Partikelfraktionen infolge ihres hohen Oberflächen-zu-Volumen-Verhältnisses eine verstärkte Oxidation aufwiesen. Neben einer signifikanten Sauerstoffanreicherung konnten keine weiteren signifikanten Veränderungen der Hauptlegierungselemente in unaufgeschmolzenen Pulverpartikeln sowie in Spritzerpartikeln festgestellt werden. Darüber hinaus wurde bei stark oxidierten Pulvern eine signifikante Veränderung der Partikelgrößenverteilung beobachtet. Die gewonnenen Erkenntnisse leisten einen wichtigen Beitrag zum Verständnis oxidationsbedingter Degradationsmechanismen und bilden die Grundlage für die Optimierung von Strategien zur Wiederverwendung von Pulver im PBF-LB/M-Prozess, wodurch die Materialperformance gesichert werden kann. T2 - DVM Tagung 2025 Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 04.11.2025 KW - Additive manufacturing KW - Laser powder bed fusion (PBF-LB/M) KW - Powder reuse KW - Spatter particles KW - Powder quality KW - Particles ejected KW - Recycling KW - Powder degradation KW - Powder oxidation PY - 2025 AN - OPUS4-64953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davila, Josue T1 - Influence Of Initial Powder Oxidation Level On Process-induced Material Degradation During The Laser Powder Bed Fusion Of Nickel-based Haynes 282 N2 - This study examines the impact of varying oxidation levels in nickel-based Haynes 282 powder on particle degradation during laser powder bed fusion (PBF-LB/M). Four powder batches with oxygen content levels of approximately from 140 ppm to1400 ppm were processed using PBF-LB/M. A powder collection container was fabricated to sample unmelted powder from heat-affected regions of the powder bed. Recoating and melting proceeded without issues; however, increased fume emissions were observed at higher oxidation levels, indicating intensified spatter formation. Post-process analysis revealed that finer particles exhibited greater surface oxidation due to their higher surface-to-volume ratio. Despite significant oxygen uptake, chemical analysis showed no measurable changes in key alloying elements in either the unmelted or spatter particles. Additionally, changes in particle size distribution became more pronounced at high oxidation levels. These findings provide a basis for understanding oxidation-driven degradation and optimizing powder reuse strategies to maintain material performance. T2 - Euro Powder Metallurgy 2025 Congress & Exhibition CY - Glasgow, Scotland DA - 15.09.2025 KW - Additive manufacturing KW - Laser powder bed fusion (PBF-LB/M) KW - Powder quality KW - Powder degradation KW - Powder oxidation KW - Spatter particles KW - Particles ejected KW - Powder reuse PY - 2025 AN - OPUS4-64965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davila, Josue T1 - Parameter development for laser powder bed fusion of nickel-based Haynes 282 using diverse density determination methods N2 - To manufacture functional components using laser powder bed fusion (PBF-LB/M), the execution of a parameter development with the specific material and machine is an indispensable step. Typically, in the search for the optimal parameter set, the volumetric energy density (VED) used to melt the material serves as an adjustment variable, while the resulting part density as the target parameter. Although this approach effectively reduces the process parameters search-space, additional criteria concerning part quality should be considered in the development. This paper introduces a systematic parameter selection approach, refining the characterization process for processing the nickel-based superalloy Haynes® 282®. The presented strategy not only incorporates the density as target condition but also considers the surface quality and dimensional accuracy of the manufactured samples, crucial for near-net-shape manufacturing. Additionally, three porosity measurement methods (Archimedes method, microscopy, gaspycnometry) for AM metal parts are compared, and their validity for this purpose is discussed. T2 - LANE Conference 2024 CY - Fürth, Germany DA - 14.09.2024 KW - Laser powder bed fusion (PBF-LB/M) KW - Parameter development KW - Gaspycnometry KW - Density determination method KW - Archimedes principle KW - Surface quality PY - 2024 AN - OPUS4-64966 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröder, Jakob T1 - Neutron Diffraction Based Residual Stress Analysis of Additively Manufactured Alloys N2 - Additive manufacturing methods such as laser powder bed fusion offer an enormous flexibility in the efficient design of parts. In this process, a laser locally melts feedstock powder to build up a part layer-by-layer. It is this localized processing manner imposing large temperature gradients, resulting in the formation of internal stress and characteristic microstructures. Produced parts inherently contain high levels of residual stress accompanied by columnar grain growth and crystallographic texture. On a smaller scale, the microstructure is characterized by competitive cell-like solidification with micro segregation and dislocation entanglement. In this context, it is crucial to understand the interplay between microstructure, texture, and residual stress to take full advantage of the freedom in design. In fact, X-ray and neutron diffraction are considered as the benchmark for the non-destructive characterization of surface and bulk residual stress. The latter, characterized by a high penetration power in most engineering alloys, allows the use of diffraction angle close to 90°, enabling the employment of a nearly cubic gauge volume. However, the complex hierarchical microstructures produced by additive manufacturing present significant challenges towards the reliable characterization of residual stress by neutron diffraction. Since residual stress is not the direct quantity being measured, the peak shift imposed by the residual stress present in a material must be converted into a macroscopic stress. First, an appropriate lattice plane must be selected that is easily accessible (i.e., high multiplicity) and insensitive to micro strain accumulation. Second, a stress-free reference must be known to calculate a lattice strain, which can be difficult to define for the heterogeneous microstructures produced by additive manufacturing. Third, an appropriate set of diffraction elastic constants that relate the lattice strain to the macroscopic stress must be known. In this presentation, advancements in the field of residual stress analysis using neutron diffraction are presented on the example of the Ni-based superalloy Inconel 718. The effect of the complex microstructure on the determination of residual stress by neutron diffraction is presented. It is shown, how to deal with the determination of the stress-free reference. It is also shown that the selection of an appropriate set of diffraction elastic constants depends on the microstructure. Finally, the role of the crystallographic texture in the determination of the residual stress is shown. T2 - Deutsche Neutronenstreutagung CY - Aachen, Germany DA - 16.09.2024 KW - Additive Manufacturing KW - Neutron Diffraction KW - Electron Backscatter Diffraction KW - Laser Powder Bed Fusion PY - 2024 AN - OPUS4-61476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Evolution of Creep Damage of 316L Produced by Laser Powder Bed Fusion N2 - The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed. T2 - Annual International Solid Freeform Fabrication Symposium CY - Austin, TX, USA DA - 14.08.2023 KW - AISI 316L KW - Additive Manufacturing KW - Computed Tomography KW - Creep KW - Laser Powder Bed Fusion KW - Microstructure KW - PBF-LB/M/316L PY - 2023 AN - OPUS4-58285 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -