TY - CONF A1 - Mrkwitschka, Paul A1 - Hodoroaba, Vasile-Dan T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM in SEM and TEM for the Accurate Characterization of Size and Shape of FeOx Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD. T2 - Microscopy and Microanalysis 2024 CY - Cleveland, OH, USA DA - 28.07.2024 KW - Nanoparticles KW - Electron microscopy KW - Iron oxide KW - Reference materials KW - Correlative microscopy KW - Size and shape distribution PY - 2024 AN - OPUS4-60806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mrkwitschka, Paul T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM-in-SEM and TEM for the Accurate Characterization of Size and Shape of FeOx Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD. T2 - SALSA Make and Measure 2024: Interfaces CY - Berlin, Germany DA - 11.09.2024 KW - Correlative microscopy KW - Electron microscopy KW - Iron oxide KW - Nanoparticles KW - Reference materials KW - Size and shape distribution PY - 2024 AN - OPUS4-62347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mrkwitschka, Paul T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM in SEM and TEM for the Accurate Characterization of Size and Shape of FeOx Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD T2 - 2. Treffen des DGE-Arbeitskreises SEM CY - Stuttgart, Germany DA - 26.09.2024 KW - Correlative microscopy KW - Electron microscopy KW - Iron oxide KW - Nanoparticles KW - Reference materials KW - Size and shape distribution PY - 2024 AN - OPUS4-62349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mrkwitschka, Paul A1 - Abram, Sarah-Luise A1 - Thünemann, Andreas A1 - Rühle, Bastian A1 - Radnik, Jörg A1 - Bresch, Harald A1 - Resch-Genger, Ute A1 - Hodoroaba, Vasile-Dan T1 - The Role of Electron Microscopy in the Development of Monodisperse Cubic Iron Oxide Nanoparticles as Certified Reference Material for Size and Shape N2 - BAM is currently building up a platform of novel nanoRMs relying on iron oxide nanoparticles of different shape, size and surface chemistry. Iron oxide was chosen as a core material because of its relevance to the material and life sciences. As a first candidate of this series, we present cubic iron oxide nanoparticles with a nominal edge length of 8 nm. These particles were synthesized by thermal decomposition of iron oleate in high boiling organic solvents adapting well-known literature procedures. After dilution to a concentration suitable for electron microscopy (TEM and SEM) as well as for small-angle X-ray scattering (SAXS) measurements, the candidate nanoRM was bottled and assessed for homogeneity and stability by both methods following the guidelines of ISO 17034 and ISO Guide 35. The particle sizes obtained by both STEM-in-SEM and TEM are in excellent agreement with a minimum Feret of 8.3 nm ± 0.7 nm. The aspect ratio (AR) of the iron oxide cubes were extracted from the images as the ratio of minimum Feret to Feret resulting in an AR of 1.18 for TEM to 1.25 for SEM. Alternatively, a rectangular bounding box was fitted originating from the minimum Feret and the longest distance through the particle in perpendicular direction. This led to AR values of 1.05 for TEM and 1.12 for SEM, respectively. The results confirm the almost ideal cubic shape. KW - Reference nanoparticles KW - Iron oxide KW - Cubical shape KW - Electron microscopy KW - SAXS KW - Nano CRM KW - Size PY - 2022 DO - https://doi.org/10.1017/S1431927622003610 SN - 1435-8115 VL - 28 IS - Suppl. 1 SP - 802 EP - 805 PB - Cambridge University Press AN - OPUS4-55599 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Riedel, Soraya A1 - Hülagü, Deniz A1 - Bennet, Francesca A1 - Carl, Peter A1 - Flemig, Sabine A1 - Schmid, Thomas A1 - Schenk, J. A. A1 - Hodoroaba, Vasile-Dan A1 - Schneider, Rudolf T1 - Electrochemical Immunomagnetic Ochratoxin A Sensing: Steps Forward in the Application of 3,3’,5,5’- Tetramethylbenzidine in Amperometric Assays N2 - Electrochemical methods offer great promise in meeting the demand for user-friendly on-site devices for Monitoring important parameters. The food industry often runs own lab procedures, for example, for mycotoxin analysis, but it is a major goal to simplify analysis, linking analytical methods with smart technologies. Enzyme-linked immunosorbent assays, with photometric detection of 3,3’,5,5’-tetramethylbenzidine (TMB),form a good basis for sensitive detection. To provide a straightforward approach for the miniaturization of the detectionstep, we have studied the pitfalls of the electrochemical TMB detection. By cyclic voltammetry it was found that the TMB electrochemistry is strongly dependent on the pH and the electrode material. A stable electrode response to TMB could be achieved at pH 1 on gold electrodes. We created a smartphonebased, electrochemical, immunomagnetic assay for the detection of ochratoxin A in real samples, providing a solid basis forsensing of further analytes. KW - Ochratoxin A KW - Amperometry KW - Cyclic voltammetry KW - Electrochemistry KW - Immunoassay PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530421 DO - https://doi.org/10.1002/celc.202100446 N1 - Geburtsname von Riedel, Soraya: Höfs, S. - Birth name of Riedel, Soraya: Höfs, S. VL - 8 IS - 13 SP - 2597 EP - 2606 AN - OPUS4-53042 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mrkwitschka, Paul A1 - Rühle, Bastian A1 - Kuchenbecker, Petra A1 - Löhmann, Oliver A1 - Lindemann, Franziska A1 - Hodoroaba, Vasile-Dan T1 - Embedding and cross-sectioning as a sample preparation procedure for accurate and representative size and shape measurement of nanopowders N2 - Reliable measurement of the size of polydisperse, complex-shaped commercial nanopowders is a difficult but necessary task, e.g., for regulatory requirements and toxicity risk assessment. Suitable methods exist for the accurate characterization of the size of non-aggregated, stabilized, spherical and monodisperse nanoparticles. In contrast, industrial nanoscale powders usually require dedicated sample preparation procedures developed for the analysis method of choice. These nano-powders tend to agglomerate and/or aggregate, a behavior which in combination with an innate broad particle size distribution and irregular shape often significantly alters the achievable accuracy of the measured size parameters. The present study systematically tests two commercially available nanoscale powders using different sample preparation methods for correlative analysis by scanning electron microscopy, dynamic light scattering, Brunauer–Emmet–Teller method and differential mobility analysis. One focus was set on the sample preparation by embedding nanoparticles in carbon-based hot-mounting resin. Literature on this topic is scarce and the accuracy of the data extracted from cross sections of these particles is unclearly stated. In this paper systematic simulations on the deviation of the size parameters of well-defined series of nanoparticles with different shapes from the nominal value were carried out and the contributing factors are discussed. KW - Nanopowder KW - Electron microscopy KW - Sample preparation KW - Cross-sectioning KW - Cerium oxide KW - Zinc oxide PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-593289 DO - https://doi.org/10.1038/s41598-023-51094-0 SN - 2045-2322 VL - 14 SP - 1 EP - 10 PB - Springer Nature CY - London AN - OPUS4-59328 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mrkwitschka, Paul A1 - Abram, Sarah-Luise A1 - Rühle, Bastian A1 - Hodoroaba, Vasile-Dan T1 - Understanding Correlative Electron Microscopy Imaging with SEM, STEM-in-SEM and TEM for the Accurate Characterization of Size and Shape of Iron Oxide Nanoparticles N2 - The recently certified reference material (CRM) BAM-N012 as cubical iron oxide FeOx nanoparticles (NPs) of 8 nm area equivalent square edge length (ESL) and the RM candidate BAM-N013 as nearly spherical NPs of 22 nm size were analyzed in detail by electron microscopy (EM). For the metrological characterization with SEM, STEM in SEM and TEM, the understanding of the imaging contrasts and sensitivities, and the correct interpretation of the (art)effects which are inherent to each detection mode is necessary. The same sample areas with NPs deposited on a TEM grid were analyzed by two SEM acquisition modes, i. e. SE InLens and STEM in SEM using a dedicated transmission sample holder, and further, correlatively, analyzed with TEM. With increasing kV, SE InLens shows increasing particle size (unless overcharging at the particle boundaries is filtered), as a known effect. For STEM-in-SEM the particle size decreases significantly and individual particles are identified easier (at 2 kV only a few single particles can be detected automatically). ❑ Documentation of the sample preparation and measurement conditions (including optimization process) is important for reproducibility. ❑ Plasma cleaning, analysis in the transmission mode at SEM is recommended for FeOx NPs. ❑ Selection of the threshold algorithm can significantly alter the reported ECD. KW - Nanoparticles KW - Iron oxide KW - Electron microscopy KW - Reference materials KW - Particle size distribution KW - Imaging PY - 2024 DO - https://doi.org/10.1093/mam/ozae044.339 VL - 30 IS - Supplement_1 SP - 710 EP - 711 PB - Oxford University Press (OUP) AN - OPUS4-61007 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Onyenso, Gabriel A1 - AI-Zawity, Jiwar A1 - Farahbakhsh, Nastaran A1 - Schardt, Annika A1 - Yadigarli, Aydan A1 - Vakamulla Raghu, Swathi Naidu A1 - Engelhard, Carsten A1 - Müller, Mareike A1 - Schönherr, Holger A1 - Killian, Manuela S. T1 - Novel Ag-modified zirconia nanomaterials with antibacterial activity N2 - The outcome of an implant procedure largely depends on the implant's surface properties. Biomaterials are now designed to have surfaces with multifunctionality, such as favorable tissue integration and the ability to combat bacterial adhesion and colonization. Herein, we report on a simple approach to improve the antibacterial properties of zirconia nanotubes (ZrNTs) coatings by decorating with silver nanoparticles (AgNP), achieved through electrochemical anodization of a zirconium–silver alloy (Zr–Ag). The AgNPs were shown to partially consist of Ag2O, potentially enhancing the availability of Ag+ ions for antibacterial activity. The modified ZrNTs were characterized using SEM, EDS, ToF-SIMS, and XPS to determine their structural morphology and chemical composition, and were further subjected to antibacterial testing. The silver and zirconium ion release behavior was monitored via ICP-MS. ZrNTs decorated with AgNP exhibit strong antimicrobial activity (>99% bacterial killing) against both S. aureus and E. coli. Antimicrobial tests indicate that the antibacterial activity against the Gram-positive pathogen S. aureus was improved by a factor of 100 compared to unmodified ZrNTs, while unmodified ZrNTs already showed a comparable reduction of viable Gram-negative E. coli. This strategy illustrates a straightforward and effective modification that optimizes the interface between the host environment and the biomaterial surface to meet the very important criteria of biocompatibility and active antibacterial response. KW - Mass Spectrometry KW - Nanoparticles KW - Advanced Materials KW - ICP-MS KW - Antimicrobial material KW - ToF-SIMS PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653990 DO - https://doi.org/10.1039/d5ra07099f SN - 2046-2069 VL - 16 IS - 3 SP - 2286 EP - 2297 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bayat, Mehmet Emin A1 - Kipphardt, Heinrich A1 - Tiebe, Carlo A1 - Tuma, Dirk A1 - Engelhard, Carsten T1 - Trace-Level Ammonia–Water Interactions in Hydrogen: Challenges in Gas Purity Analysis Using Optical-Feedback Cavity-Enhanced Absorption Spectroscopy (OF-CEAS) N2 - Ammonia is a critical impurity in hydrogen fuel due to its irreversible poisoning effect on proton exchange membrane fuel cells. Therefore, international standards (e.g., ISO 14687) set a stringent threshold of 100 nmol/mol. Furthermore, with the growing potential use of ammonia as a hydrogen carrier, its accurate quantification is becoming increasingly important. However, the presence of trace humidity poses analytical challenges, as ammonia may interact with water or interfaces, thereby affecting its detectability. Therefore, the goal of this work is to enable accurate trace ammonia quantification for hydrogen purity measurements through fundamental studies of the methodological challenges. Here, low-pressure sampling (ultra)long-path Optical-Feedback Cavity-Enhanced Absorption Spectroscopy (OF-CEAS) was applied with an effective optical path length of approximately 6.17 km. We studied three average amounts of ammonia: (38.2 ± 0.8) nmol/mol, (74.8 ± 0.7) nmol/mol, and (112.1 ± 1.2) nmol/mol. Furthermore, these amounts were investigated at trace-humidity levels ranging from 0.8 to 8.5 ppmV. We observed a systematic, nonlinear, and humidity-dependent positive measurement bias of up to + (1.0 ± 0.2) nmol/mol at the maximum investigated trace-humidity volume fraction of 8.5 ppmV. This bias was not caused by spectral interference but rather by water-induced accumulation of ammonia within the optical cavity. Moreover, time-resolved measurements in the presence of trace ammonia showed that water desorption follows first-order kinetics, whereas water adsorption followed mixed-order kinetics with an apparent reaction order of 1.57 ± 0.03. Distinct hydration states of surface-bound ammonia were identified, whereas under dry conditions and with increasing amounts of ammonia, enhanced surface adhesion through intermolecular clustering was observed. In addition, the presence of ammonium species within the sorption layer was indirectly confirmed by our experiments. In conclusion, we provide a deeper insight into trace-level ammonia–water interactions and establish a framework for optimizing methodologies, particularly for (ultra)long-path optical gas measurement systems. KW - Ammonia KW - Hydrogen KW - OF-CEAS KW - Humidity KW - Surface Interactions KW - Adsorption PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-643627 DO - https://doi.org/10.1021/acsmeasuresciau.5c00105 SN - 2694-250X SP - 1 EP - 15 PB - American Chemical Society (ACS) AN - OPUS4-64362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayat, Mehmet A1 - Kipphardt, Heinrich A1 - Tiebe, Carlo A1 - Engelhard, Carsten T1 - Effect of Trace Humidity on Trace Ammonia Quantification N2 - Hydrogen is receiving growing attention as a promising medium for energy storage and transportation. Proton exchange membrane (PEM) fuel cells are a key technology for energy conversion from hydrogen. However, high purity hydrogen is required for this technology, as described in standards such as ISO 14687:2019. A critical impurity that impairs PEM efficiency is ammonia, for which a limit value of 100 nmol/mol applies. In addition, the maximum amount of humidity is specified with 5 µmol/mol. The presence of humidity in hydrogen at levels up to 50 times higher than ammonia raises the critical question of whether ammonia can still be quantified accurately in the lower nmol/mol range without interference from water. In addition, the general question arises as to whether the critical analyte, ammonia, can still be detected at all, given the expected surface effects at such amounts of trace humidity. In this work, we describe the influence of trace humidity on the surface behavior of adsorbed ammonia on stainless steel. Samples with ammonia at approximately 100 nmol/mol in hydrogen, with trace humidity levels ranging from 3 µmol/mol to 10 µmol/mol, were carefully prepared using dynamic mixing. Humidification was conducted using an advanced saturation method. These samples were investigated under atmospheric conditions using low pressure sampling Optical Feedback Cavity Enhanced Absorption Spectroscopy (OFCEAS). From the observed time-dependent signals, kinetics were determined and analyzed, yielding insights on the strength of the adsorption behavior of the analytes. T2 - ANAKON 2025 CY - Leipzig, Germany DA - 10.03.2025 KW - OF-CEAS KW - Hydrogen KW - Ammonia KW - Water KW - Humidity KW - Kinetics KW - Adsorption PY - 2025 UR - https://veranstaltungen.gdch.de/microsite/index.cfm?l=11713&sp_id=2&selSiteID=vplanner AN - OPUS4-64046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bernardino, Carolina T1 - Effortless Antimicrobial Shield: Spray-coated Silica Nanoparticles For Safer High-touch Surfaces N2 - Functional films with tailored interfacial properties play a pivotal role for the development of next generation surface coatings, particularly in healthcare-related environments. In this contribution, we present a facile spray-coating method for the creation of antimicrobial thin films on high-touch surfaces using mesoporous silica nanoparticles (MSNs) that were specifically functionalized to enable strong adhesion and sustained release of metal-based antimicrobial agents. The process is scalable and addresses key challenges in adhesion control, film homogeneity, and long-term antimicrobial function against a large range of key pathogens responsible for nosocomial infections. Three distinct types of MSNs – bearing amine (MSN-NH₂), carboxy (MSN-COOH), and thiol (MSN-SH) surface groups – were synthesized to optimize both metal ion loading and interactions with polyelectrolyte-based adhesion layers. These surface modifications not only provide chemical handles for Cu²⁺ and Ag⁺ ion coordination but also modulate nanoparticle-substrate interactions and dispersion behavior during film formation. The coating architecture consists of a two-step process: first, spray deposition of polyelectrolyte primers that anchor strongly to stainless steel substrates; second, a nanoparticle layer that bonds electrostatically and chemically to the primer, forming robust films with great surface coverage. The films were characterized to assess structural integrity, adhesion, and functional performance. Transmission electron microscopy (TEM) and N₂ sorption analysis confirmed the mesoporous structure. ATR-FTIR and zeta potential measurements validated surface functionalization and colloidal stability. Environmental SEM revealed conformal coating across the stainless-steel surfaces with uniform nanoparticle distribution. The coating's adhesion strength was maintained through mechanical wiping and simulated wear and abrasion tests, demonstrating film durability relevant in real-world use scenarios. Antimicrobial testing under semi-dry, application-relevant conditions showed excellent performance for Ag⁺-loaded MSN-SH films, inhibiting growth of Staphylococcus aureus, Pseudomonas aeruginosa, Escherichia coli, and Candida albicans. These results highlight the synergistic role of surface chemistry, metal ion loading, and film-substrate adhesion in creating effective and wear-resistant functional coatings. Moreover, these films do not show any cytotoxic properties towards Human Dermal Fibroblasts (HDF). This study contributes new insights into the design of multifunctional films where adhesion, surface functionality, and scalable processing are co-optimized for enhanced performance and shows how combining tailored surface chemistry and wide-ranging antimicrobial activity brings together smart material design for practical and safe use. T2 - MRS Fall Meeting 2025 CY - Boston, MA, USA DA - 30.11.2025 KW - Mesoporous silica nanoparticles KW - Silver KW - Antimicrobial KW - Coatings KW - Thin film PY - 2025 AN - OPUS4-65150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Fischer, Janina T1 - Suspensionsarray-Fluoreszenzimmunoassay zur Multiplexbestimmung von SARS-CoV-2-Antikörpern N2 - Übergeordnetes Ziel der Arbeit war die Entwicklung und Optimierung eines Suspensionsarray-Fluoreszenzimmunoassays (SAFIA) für die simultane Bestimmung verschiedener gegen SARS-CoV-2-Proteine gerichtete Antikörper mittels Multiplexdetektion in komplexen Matrices wie humanen Blutserumproben. KW - SARS-CoV-2 KW - Corona KW - COVID-19 KW - Coronavirus KW - Virus KW - Spike-Protein KW - Nucleocapsid-Protein KW - RBD KW - SAFIA KW - LFIA KW - ELISA KW - Partikel KW - Mutationen KW - Neutralisierende Antikörper KW - Durchflusszytometrie KW - ACE2 PY - 2022 SP - 1 EP - 99 PB - Humboldt-Universität zu Berlin CY - Berlin AN - OPUS4-54722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kaufmann, Jan Ole A1 - Brangsch, J. A1 - Kader, A. A1 - Saatz, Jessica A1 - Mangarova, D. B. A1 - Zacharias, M. A1 - Kempf, W. E. A1 - Schwaar, T. A1 - Ponader, Marco A1 - Adams, L. C. A1 - Möckel, J. A1 - Botnar, R. M. A1 - Taupitz, M. A1 - Mägdefessel, L. A1 - Traub, Heike A1 - Hamm, B. A1 - Weller, Michael G. A1 - Makowski, M. R. T1 - ADAMTS4-specific MR-probe to assess aortic aneurysms in vivo using synthetic peptide libraries N2 - The incidence of abdominal aortic aneurysms (AAAs) has substantially increased during the last 20 years and their rupture remains the third most common cause of sudden death in the cardiovascular field after myocardial infarction and stroke. The only established clinical parameter to assess AAAs is based on the aneurysm size. Novel biomarkers are needed to improve the assessment of the risk of rupture. ADAMTS4 (A Disintegrin And Metalloproteinase with ThromboSpondin motifs 4) is a strongly upregulated proteoglycan cleaving enzyme in the unstable course of AAAs. In the screening of a one-bead-one-compound library against ADAMTS4, a low-molecular-weight cyclic peptide is discovered with favorable properties for in vivo molecular magnetic resonance imaging applications. After identification and characterization, it’s potential is evaluated in an AAA mouse model. The ADAMTS4-specific probe enables the in vivo imaging-based prediction of aneurysm expansion and rupture. KW - Peptide KW - Peptide library KW - OBOC library KW - Combinatorial chemistry KW - Peptide aptamers KW - Binding molecule KW - Affinity KW - Synthetic peptides KW - Contrast agent KW - Magnetic resonance imaging KW - One-bead-one-compound library KW - On-chip screening KW - Lab-on-a-chip KW - MALDI-TOF MS KW - SPR KW - Surface plasmon resonance KW - Alanine scan KW - Fluorescence label KW - MST KW - Docking KW - Chelate PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560930 DO - https://doi.org/10.1038/s41467-022-30464-8 N1 - Geburtsname von Ponader, Marco: Wilke, M. - Birth name of Ponader, Marco: Wilke, M. VL - 13 IS - 1 SP - 1 EP - 18 PB - Springer Nature Limited CY - Heidelberg AN - OPUS4-56093 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Engelhard, Carsten T1 - Advances in Analytical Chemistry and Mass Spectrometry to Support a Sustainable and Circular Economy N2 - Recent advances in analytical chemistry have significantly supported efforts to realize a sustainable circular economy and circular chemistry. By enabling rapid materials analysis and characterization of materials transformation throughout their life cycle, analytical methods are playing a key role in supporting waste reduction, resource recovery, pollution monitoring, and sustainable manufacturing. In this presentation, recent developments in analytical chemistry and analytical instrumentation to support a sustainable and circular economy will be reviewed and selected contributions from our laboratories will be discussed. For example, high-resolution mass spectrometry combined with chromatography is an indispensable tool for the identification and characterization of plastics. To support the transition from linear to circular chemistry, whichs prioritizes reuse, recycling, and resource efficiency, accurate and detailed chemical information about plastic materials is essential. Here, targeted and non-targeted screening approaches help to characterize, for example, the quality and safety of recycled plastics. In addition, green analytical chemistry has emerged as a topic of interest, emphasizing the use of solvent-free and low-energy methods to minimized environmental impact during analysis. Here, ambient desorption/ionization high-resoluton mass spectrometry (ADI-MS) is considered a very attractive tool because it dos not require chromatography or large amounts of solvent, reduces sample preparation time, and produces virtually no chemical waste. Here, a solvent-free, plasma-based ADI-MS method is presented, which was carefuly developed for the direct identification and fast screening of per- and polyfluoroalkyl substances (PFAS). PFAS are a large class of thousands of synthetic chemicals that are used worldwide. However, growing environmental and human health concerns in the last two decades have led to more stringent regulatory requirements and the development of quantitative analytical methods for PFAS detection. Today, standardized and powerful methods exist, e.g., for the determination PFAS in water, sludge, compost, soil, and drinking water. While liquid chromatography coupled to tandem mass spectrometry (LC-MS/MS) is often used, sample preparation, solvent consumption, and total analysis times can be challenging. Here, ADI-MS is considered interesting, because it requires only minimal sample preparation and little solvent consumption. In this work, a plasma-based pin-to-capillary flowing atmospheric-pressure afterglow source (FAPA) is used for the direct desorption/ionization of PFAS from thin-layer chromatography (TLC) plates. Selected PFAS samples were directly probed on functionalized TLC surfaces without a preceding planar chromatography step. In addition, direct analysis of PFAS mixtures and selected matrices was performed with little solvent consumption, no sample preparation and short analysis time. T2 - XXII European Conference on Analytical Chemistry (EUROANALYSIS) CY - Barcelona, Spain DA - 31.08.2025 KW - Mass Spectrometry KW - Extractables & Leachables KW - Non-Targeted Analysis KW - PFAS KW - FAPA-MS PY - 2025 AN - OPUS4-65275 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayat, Mehmet Emin T1 - Traceable dynamic and gravimetric preparation of trace ammonia in hydrogen gas standards for ISO 14687 N2 - Trace ammonia impurities in hydrogen fuel poison proton-exchange-membrane fuel cells (PEMFC), causing irreversible performance degradation. Accurate quantification of ammonia in so-called Grade D hydrogen fuel is crucial for ensuring PEMFCs long-term operational stability and performance. According to ISO 14687 grade D hydrogen fuel sets a stringent threshold value of just 100 nmol/mol for ammonia impurities. Given the potential of an ammonia-based hydrogen supply chain, reliable quantification of ammonia contamination appears even more relevant. Hydrogen quality assessments for ammonia impurities typically employ techniques such as gas chromatography, cavity-enhanced absorption spectroscopy, or mass spectrometry. These techniques, however, require stable reference gases for calibration and long-term method validation. Typically, gravimetrically produced reference gases are used. However, ammonia poses unique challenges due to its chemical reactivity and stickiness. By applying (ultra )long-path Optical Feedback Cavity Enhanced Absorption Spectroscopy we observed that above a certain amount of ammonia, the gravimetric amount deviates from the analytically determined amount. This discrepancy most likely arises due to strong adsorption of ammonia onto the inner surface of the gas cylinder. Therefore, we investigated the lowest gravimetrically preparable amount of ammonia in hydrogen for which the analytically measured amount of the cylinder remains congruent with the gravimetric amount of substance. We further investigated the applicability of passivated cylinders for trace ammonia gas standards and compared their performance to aluminum alloy cylinders. To confirm reproducibility of our results, we conducted three independent gravimetric preparation campaigns, each employing optimizations, or changes in methodology, at different times. Finally, we investigated whether those gravimetrically prepared trace amounts of ammonia in hydrogen gas standards were long-term-stable. Beyond gravimetrically prepared gas standards, we evaluated how a cutting-edge dynamic dilution system could reliably extend trace-ammonia calibration down to the ISO limit of 100 nmol/mol. For this purpose, we developed an advanced dynamic dilution system capable of a one-in-a-billion dilution ratio, validated for its SI traceability, reproducibility, and operational limits by applying an internal standard. In summary, our results demonstrate that precise dynamic dilution, coupled with concentrated gravimetrically prepared ammonia gas mixture, provides a route to full SI-traceable trace-ammonia reference sample gases. T2 - Gas Analysis Symposium 2026 CY - Paris, France DA - 27.01.2026 KW - Ammonia KW - Hydrogen KW - Gravimetric preparation KW - OF-CEAS KW - ISO 14687 PY - 2026 AN - OPUS4-65620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hodoroaba, Vasile-Dan T1 - Correlative physic-chemical analysis of advanced materials and BAM’s green and zero-related advanced materials activities – Benefits and challenges by examples N2 - Following points are presented: - Nanomaterials BAM, as research materials & CRMs, incl pre-standardization, automated analysis & automated synthesis - 2D-materials BAM HEurope ACCORDs approach Green Deal inspired correlative imaging based characterisation for safety profiling of 2D materials - Sample preparation @BAM , inclusion to standards - Thin Films @BAM as Reference Material Candidates, i) mesoporous, ii) HEA - Substitutional,Transition Me oxides as electrocatalysts a project @BAM - Sustainable mechanochemical reaction engineering projects @BAM. T2 - VAMAS Workshop Advanced Materials Challenges and Standardization Needs for a Greener World CY - Rio de Janeiro, Brazil DA - 25.09.2024 KW - Nanomaterials KW - Advanced materials KW - 2D materials KW - Sample preparation KW - Thin films KW - Reference materials KW - Safety KW - Automation PY - 2024 AN - OPUS4-61404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -