TY - JOUR A1 - Schumm, A. A1 - Martin, E. A1 - Beaumont, M. A1 - Ewert, Uwe A1 - Kolkoori, Sanjeevareddy A1 - Zscherpel, Uwe A1 - Wrobel, Norma A1 - Redmer, Bernhard T1 - A comparative study on the performance of digital detector systems for high energy applications N2 - For cast components reaching or exceeding total material thicknesses of 150mm, high energy sources such as linear accelerators or Betatrons are required in order to obtain reasonable exposure times. In this study, the performance of digital detector systems, involving imaging plates (IP) and digital detector arrays (DDA), was evaluated with respect to the testing class B requirements as formulated in the standard EN ISO 17636-2. As a reference, traditional radiographic film and a Cobalt-60 source was used. With film exposures, testing class B was achieved with Co-60 and Betatron (7.5 MV) at longer exposure times. The preliminary results show that the testing class B was not obtained with the examined digital detector arrays (DDA) and the high resolution imaging plates (IP) , even at 40, 60 and 80 minutes exposure time with a 7.5 MV Betatron. Class A was achieved using high resolution imaging plates with optimized metal filters between object and IPs and a high resolution DDA with intermediate Cu filters. Class A was also achieved applying a DDA with lower basic spatial resolution than required by Table B.13 of EN ISO 17636-2, but using the compensation principle as described in this standard. The next generation of digital detector arrays might potentially be able to obtain class B performance with the expected spatial resolution and sensitivity improvements. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - Radiography KW - Image quality KW - Betatron KW - Digital detector array (DDA) KW - Casting KW - Standards KW - High energy radiography KW - Comparison of detectors KW - Steel weldment PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-323075 UR - https://www.ndt.net/?id=16394 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 6 PB - NDT.net CY - Kirchwald AN - OPUS4-32307 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ewert, Uwe A1 - Zscherpel, Uwe T1 - Minimum requirements for digital radiography equipment and measurement procedures by different industries and standard organizations N2 - The digital photography has almost completely substituted the film photography. The film replacement is also fast progressing in medical X-ray radiography. This process is slower in NDT and especially in Europe. Reasons for the hesitating change to digital radiography (RT-D) in NDT are the necessary time for adoption of standards and the conservative request for film RT by auditors and NDT managers for applications in large plants and at construction areas. The fast serial inspection for small castings is already almost completely dominated by RT-D due to the cost effective short exposure and interpretation times. Standards were developed in parallel at CEN, ISO, ASTM and ASME. Unfortunately, the standard practices are different and the requirements on image quality and useable hardware are different too. The first standard series on Computed Radiography were developed and published by CEN and ASTM in 2005. Harmonized classification and qualification standards are available but the published practices are different. ASTM has developed the first standards for application of Digital Detector Arrays (DDA) in 2010. The first digital RT ISO standard practice is ISO 17636-2 (2013), which describes the practice for application of DDAs and Imaging Plates for weld inspection. At the first time this standard provides requirements for the selection of suitable hardware. Minimum image quality requirements are specified in analogy to film radiography and 3 Compensation Principles are defined to enable the application of a wider range of digital detectors. A comparison of the different international digital RT standards is given and first experiences with ISO 17636-2 are discussed. New standards on RT wall thickness and corrosion measurements (EN 16407, film and digital) have been developed recently. T2 - ECNDT 2014 - 11th European conference on non-destructive testing CY - Prague, Czech Republic DA - 06.10.2014 KW - NDT KW - X-Ray KW - Digital detectors KW - Standards KW - Radiographic procedures KW - Unsharpness KW - Basic spatial resolution KW - Requirements KW - Digital industrial radiology PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-323081 UR - https://www.ndt.net/?id=16708 SN - 1435-4934 VL - 19 IS - 12 SP - 1 EP - 18 PB - NDT.net CY - Kirchwald AN - OPUS4-32308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radtke, Martin A1 - Buzanich, Günter A1 - Curado, Jessica A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - Scharf, O. T1 - Slicing - a new method for non destructive 3D elemental sensitive characterization of materials N2 - Recent advances in synchrotron sources and detector technology have led to substantial improvements in spatial resolution and detection limits for X-ray fluorescence analysis (XRF). However, the non-destructive three-dimensional elemental sensitive characterization of samples remains a challenge. We demonstrate the use of the so-called 'Color X-ray Camera' (CXC) for 3D measurements for the first time. The excitation of the sample is realized with a thin sheet-beam. The stepwise movement of the sample allows getting the elemental distribution for each layer with one measurement. These layers can be combined to a full 3D dataset for each element afterwards. Since the information is collected layer by layer, there is no need to apply reconstruction techniques, which quite often are the reason for artifacts in the results achieved by computed tomography (CT). The field of applications is wide, as the 3D elemental distribution of a material contains clues to processes inside the samples from a variety of origins. The technique is of special interest and well suited for biological specimens, because their light matrix minimizes restricting absorption effects. Measurement examples of a hornet and the teeth of a Sorex araneus are shown. KW - SR-microXRF KW - 3D KW - CXC PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-324330 DO - https://doi.org/10.1039/c4ja00085d SN - 0267-9477 SN - 1364-5544 VL - 29 IS - 8 SP - 1339 EP - 1344 PB - Royal Society of Chemistry CY - London AN - OPUS4-32433 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Franziska A1 - Scholz, G. A1 - Batzdorf, Lisa A1 - Wilke, Manuel A1 - Emmerling, Franziska T1 - Synthesis, structure determination, and formation of a theobromine: oxalic acid 2:1 cocrystal N2 - The structure and the formation pathway of a new theobromine : oxalic acid (2 : 1) cocrystal are presented. The cocrystal was synthesised mechanochemically and its structure was solved based on the powder X-ray data. The mechanochemical synthesis of this model compound was studied in situ using synchrotron XRD. Based on the XRD data details of the formation mechanism were obtained. The formation can be described as a self-accelerated ('liquid like') process from a highly activated species. KW - ssNMR spectroscopy KW - Synchrotron measurements KW - API molecule PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-331567 DO - https://doi.org/10.1039/c4ce02066a SN - 1466-8033 VL - 17 IS - 4 SP - 824 EP - 829 CY - London, UK AN - OPUS4-33156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kramer, Claus A1 - Ried, Peter A1 - Mahn, Stefan A1 - Richter, Silke A1 - Langhammer, Nicole A1 - Kipphardt, Heinrich T1 - Design and application of a versatile gas calibration for non-metal determination by carrier gas hot extraction N2 - In carrier gas hot extraction the calibration of low amounts of non-metals with masses of a few micrograms with small uncertainty remains a challenge. To achieve high flexibility a high precision gas mixture pump was combined with an automated syringe drive. The gas mixing pump allows filling the syringe with different gas compositions; the automated syringe drive allows matching to modulate the signal profiles to those of real samples. The system was designed and its experimental potential explored. The resulting calibration curves were comparable to those obtained by calibration using solid materials of sufficient purity and stoichiometry. However smaller uncertainties and lower limits of quantification (i.e. 0.5 µg and 0.6 µg for O and N, respectively) were found using the gas calibration device. KW - Non-metal determination KW - CGHE KW - Gas calibration PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-336130 DO - https://doi.org/10.1039/c5ay00845j SN - 1759-9660 SN - 1759-9679 VL - 7 IS - 13 SP - 5468 EP - 5475 PB - RSC Publ. CY - Cambridge AN - OPUS4-33613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sötebier, Carina A1 - Bierkandt, Frank A1 - Rades, Steffi A1 - Jakubowski, Norbert A1 - Panne, Ulrich A1 - Weidner, Steffen T1 - Sample loss in asymmetric flow field-flow fractionation coupled to inductively coupled plasma-mass spectrometry of silver nanoparticles N2 - In this work, sample losses of silver nanoparticles (Ag NPs) in asymmetrical flow field-flow fractionation (AF4) have been systematically investigated with the main focus on instrumental conditions like focusing and cross-flow parameters as well as sample concentration and buffer composition. Special attention was drawn to the AF4 membrane. For monitoring possible silver depositions on the membrane, imaging laser ablation coupled to inductively coupled plasma mass spectrometry (LA-ICP-MS) was used. Our results show that the sample residue on the membrane was below 0.6% of the total injected amount and therefore could be almost completely avoided at low sample concentrations and optimized conditions. By investigation of the AF4 flows using inductively coupled plasma mass spectrometry (ICP-MS), we found the recovery rate in the detector flow under optimized conditions to be nearly 90%, while the cross-flow, slot-outlet flow and purge flow showed negligible amounts of under 0.5%. The analysis of an aqueous ionic Ag standard solution resulted in recovery rates of over 6% and the ionic Ag content in the sample was found to be nearly 8%. Therefore, we were able to indicate the ionic Ag content as the most important source of sample loss in this study. KW - Asymmetric flow filed-flow fractionation KW - ICP-MS KW - Nanoparticles KW - Sample loss KW - Quantification PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-336171 DO - https://doi.org/10.1039/c5ja00297d SN - 0267-9477 SN - 1364-5544 VL - 30 IS - 10 SP - 2214 EP - 2222 PB - Royal Society of Chemistry CY - London AN - OPUS4-33617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hansen, Ulf A1 - Thünemann, Andreas T1 - Characterization of silver nanoparticles in cell culture medium containing fetal bovine serum N2 - Nanoparticles are being increasingly used in consumer products worldwide, and their toxicological effects are currently being intensely debated. In vitro tests play a significant role in nanoparticle risk assessment, but reliable particle characterization in the cell culture medium with added fetal bovine serum (CCM) used in these tests is not available. As a step toward filling this gap, we report on silver ion release by silver nanoparticles and on changes in the particle radii and in their protein corona when incubated in CCM. Particles of a certified reference material, p1, and particles of a commercial silver nanoparticle material, p2, were investigated. The colloidal stability of p1 is provided by the surfactants polyethylene glycol-25 glyceryl trioleate and polyethylene glycol-20 sorbitan monolaurate, whereas p2 is stabilized by polyvinylpyrrolidone. Dialyses of p1 and p2 reveal that their silver ion release rates in CCM are much larger than in water. Particle characterization was performed with asymmetrical flow field-flow fractionation, small-angle X-ray scattering, dynamic light scattering, and electron microscopy. p1 and p2 have similar hydrodynamic radii of 15 and 16 nm, respectively. The silver core radii are 9.2 and 10.2 nm. Gel electrophoresis and subsequent peptide identification reveal that albumin is the main corona component of p1 and p2 after incubation in CCM that consists of Dulbecco's modified Eagle medium with 10% fetal bovine serum added. PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-335510 DO - https://doi.org/10.1021/acs.langmuir.5b00687 SN - 0743-7463 SN - 1520-5827 VL - 31 IS - 24 SP - 6842 EP - 6852 PB - American Chemical Society CY - Washington, DC AN - OPUS4-33551 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Manke, I. A1 - Kardjilov, N. A1 - Schäfer, R. A1 - Hilger, A. A1 - Grothausmann, R. A1 - Strobl, M. A1 - Dawson, M. A1 - Grünzweig, C. A1 - Tötzke, C. A1 - David, C. A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Banhart, J. T1 - Three-dimensional imaging of magnetic domains with neutron grating interferometry N2 - This paper gives a brief overview on3D imaging of magnetic domains with shearing grating neutron tomography. We investigated the three-dimensional distribution of magnetic domain walls in the bulk of a wedge-shaped FeSi single crystal. The width of the magnetic domains wasanalyzed at different locations within the crystal. Magnetic domains close to the tip of the wedge are much smaller than in the bulk. Furthermore, the three-dimensional shape of individual domains wasinvestigated. We discuss prospects and limitations of the applied measurement technique. KW - Neutron imaging KW - Tomography KW - Magnetic domains KW - Grating interferometry KW - Darkfield imaging KW - Shearing gratings KW - Talbot-Lau KW - Three-dimensional data quantification KW - Tomographic reconstruction PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-341919 DO - https://doi.org/10.1016/j.phpro.2015.07.057 SN - 1875-3892 VL - 69 SP - 404 EP - 412 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-34191 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Breßler, Ingo A1 - Kohlbrecher, J. A1 - Thünemann, Andreas T1 - SASfit: a tool for small-angle scattering data analysis using a library of analytical expressions N2 - SASfit is one of the mature programs for small-angle scattering data analysis and has been available for many years. This article describes the basic data processing and analysis workflow along with recent developments in the SASfit program package (version 0.94.6). They include (i) advanced algorithms for reduction of oversampled data sets, (ii) improved confidence assessment in the optimized model parameters and (iii) a flexible plug-in system for custom user-provided models. A scattering function of a mass fractal model of branched polymers in solution is provided as an example for implementing a plug-in. The new SASfit release is available for major platforms such as Windows, Linux and MacOS. To facilitate usage, it includes comprehensive indexed documentation as well as a web-based wiki for peer collaboration and online videos demonstrating basic usage. The use of SASfit is illustrated by interpretation of the small-angle X-ray scattering curves of monomodal gold nanoparticles (NIST reference material 8011) and bimodal silica nanoparticles (EU reference material ERM-FD-102). KW - Small-angle X-ray scattering KW - Small-angle neutron scattering KW - Curve fitting KW - Nanotechnology KW - Nanoparticles KW - Polymers KW - SAXS PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-343348 DO - https://doi.org/10.1107/S1600576715016544 SN - 0021-8898 SN - 1600-5767 VL - 48 SP - 1587 EP - 1598 PB - Blackwell CY - Oxford AN - OPUS4-34334 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Breßler, Ingo A1 - Pauw, Brian Richard A1 - Thünemann, Andreas T1 - McSAS: software for the retrieval of model parameter distributions from scattering patterns N2 - A user-friendly open-source Monte Carlo regression package (McSAS) is presented, which structures the analysis of small-angle scattering (SAS) using uncorrelated shape-similar particles (or scattering contributions). The underdetermined problem is solvable, provided that sufficient external information is available. Based on this, the user picks a scatterer contribution model (or 'shape') from a comprehensive library and defines variation intervals of its model parameters. A multitude of scattering contribution models are included, including prolate and oblate nanoparticles, core-shell objects, several polymer models, and a model for densely packed spheres. Most importantly, the form-free Monte Carlo nature of McSAS means it is not necessary to provide further restrictions on the mathematical form of the parameter distribution; without prior knowledge, McSAS is able to extract complex multimodal or odd-shaped parameter distributions from SAS data. When provided with data on an absolute scale with reasonable uncertainty estimates, the software outputs model parameter distributions in absolute volume fraction, and provides the modes of the distribution (e.g. mean, variance etc.). In addition to facilitating the evaluation of (series of) SAS curves, McSAS also helps in assessing the significance of the results through the addition of uncertainty estimates to the result. The McSAS software can be integrated as part of an automated reduction and analysis procedure in laboratory instruments or at synchrotron beamlines. KW - Nanotechnology KW - Nanoparticles KW - Small-angle X-ray scattering KW - SAXS PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-334396 DO - https://doi.org/10.1107/S1600576715007347 SN - 0021-8898 SN - 1600-5767 VL - 48 IS - 3 SP - 962 EP - 969 PB - Blackwell CY - Oxford AN - OPUS4-33439 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter A1 - Krebs, Holger T1 - Boiling liquid expanding vapour explosion (BLEVE) of peroxy-fuels: Experiments and computational fluid dynamics (CFD) simulation N2 - Fire and explosion hazards associated with storage and transportation of flammable materials have been a matter of great interest in the recent times. BLEVE is a scenario that occurs when a closed fuel container is subjected to heat for a longer duration. Such events are disastrous to human beings and assets both. In the past there have been numerous studies on BLEVEs and fireballs of hydrocarbon fuels, e.g. kerosene, gasoline, LPG, LNG and others. Though, the fireballs of peroxy-fuels are not looked into detail as such. This article tries to overcome this lack of knowledge. Both, experimental investigation and CFD simulations are performed to measure and predict the fireball characteristics of a peroxy-fuel. Due to thermal decomposition in the liquid phase and active oxygen content a peroxy-fuel fireball burns at a very fast rate and emit higher thermal radiation whereas exhibits smaller diameter and elevation compared to hydrocarbons. That eventually leads to consideration of larger safety distances from them which are also verified by CFD results. KW - BLEVE KW - Hydrocarbons KW - Peroxy-fuels KW - Safety distances KW - CFD simulation PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-334184 DO - https://doi.org/10.1016/j.egypro.2015.02.082 SN - 1876-6102 VL - 66 SP - 149 EP - 152 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-33418 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schukar, Vivien A1 - Köppe, Enrico A1 - Hofmann, Detlef A1 - Westphal, Anja A1 - Sahre, Mario A1 - Gong, Xin A1 - Bartholmai, Matthias A1 - Beck, Uwe T1 - Magnetic field detection with an advanced FBG-based sensor device N2 - A high-performance fiber Bragg grating-based (FBG) sensor device has been developed for the detection of small magnetic fields. Based on a smart multilayer jacket around the fibre over the physical length of the FBG, magnetic fields generated by rotating machine parts, power generators or power cable can be easily detected, analysed and evaluated. Consequently, this innovative, on-line and non-contact inspection method results in an increase in quality and reliability of high-performing machine parts, devices and cables. The basic physical principle is based on a magnetostrictive multilayer system that strains the high-resolution FBG element in presence of magnetic fields. Subsequently, a fixed relationship between induced magnetic field and wavelength change of the FBG element describes the characteristic sensitivity curve. Intensive tests regarding characterisation of this magnetic field FBG sensor have been carried out and its performance has been evaluated. T2 - 30th Eurosensors Conference, EUROSENSORS 2016 CY - Budapest, Hungary DA - 04.09.2016 KW - Fiber Bragg grating KW - Magnetostriction KW - Strain KW - Magnetic field PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-376703 DO - https://doi.org/10.1016/j.proeng.2016.11.445 SN - 1877-7058 VL - 168 SP - 1270 EP - 1274 PB - Elsevier Ltd. AN - OPUS4-37670 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fritzsche, André A1 - Avilov, Vjaceslav A1 - Gumenyuk, Andrey A1 - Hilgenberg, Kai A1 - Rethmeier, Michael T1 - High power laser beam welding of thick-walled ferromagnetic steels with electromagnetic weld pool support N2 - The paper describes an experimental investigation of high power laser beam welding with an electromagnetic weld pool support for up to 20 mm thick plates made of duplex steel (AISI 2205) and mild steel (S235JR). The results of the welding tests show a successful application of this technology at ferromagnetic metals. Irregular sagging was suppressed successfully. An ac-power of less than 2 kW at oscillation frequencies between 800 Hz and 1.7 kHz is necessary for a full compasation of the hydrostatic pressure. Thus, it was demonstrated that the electromagnetic weld pool support is not only limited to non-ferromagnetic metals like austenitic steels. For future studies with duplex steel, the use of filler material has to take into account with regard to the balance of the mixed austenitic and ferritic phases. KW - Laser beam welding KW - Thick-walled steel KW - Ferromagnetic steel KW - Weld pool support PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-377593 DO - https://doi.org/10.1016/j.phpro.2016.08.038 SN - 1875-3892 VL - 83 SP - 362 EP - 372 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-37759 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Agroui, K. A1 - Jaunich, Matthias A1 - Hadj Arab, A. T1 - Analysis techniques of polymeric encapsulant materials for photovoltaic modules: situation and perspectives N2 - The properties of the encapsulant are critical to the long-term performance of photovoltaic (PV) modules under the influence of sunlight including UV, elevated temperature, humidity and diffusion of oxygen. Encapsulation process represents a bout 40% of the whole PV module cost. The introduction of new non-EVA encapsulant material type "Low-Cost, High-Performance" should provide a solution to outdoor yellowing degradation problems. The emerging encapsulant materials exhibit a good compatibility with emerging PV solar cells for long term durability. This new generation of encapsulant materials has the advantage to improve e the PV module performances and long term durability for specific climate like desert regions. This scientific contribution presents an overview of the different encapsulant materials currently on the market, the general requirements of the emerging encapsulant materials and characterizations techniques for degradation, diagnostic and reliability lifetime estimation in the framework of Algerian renewable energy strategy. T2 - Africa-EU Renewable Energy Re search and Innovation Symposium, RERIS 2016 CY - Tlemcen, Algeria DA - 08.03.2016 KW - Solar cell KW - Polymer encapsulant KW - PV module KW - Encapsulation process KW - Analysis technique PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-377186 DO - https://doi.org/10.1016/j.egypro.2016.07.171 SN - 1876-6102 VL - 2016 IS - 93 SP - 203 EP - 210 PB - Elsevier Ltd. AN - OPUS4-37718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bachmann, Marcel A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Welding with high-power lasers: trends and developments N2 - High-power laser beam welding became new stimuli within the last 10 years due to the availability of a new generation of high brightness multi kilowatt solid state lasers. In the welding research new approaches have been developed to establish reliable and praxis oriented welding processes meeting the demands of modern industrial applications during this time. The paper focuses on some of the current scientific and technological aspects in this research field like hybrid laser arc welding, simulation techniques, utilization of electromagnetic fields or reduced pressure environment for laser beam welding processes, which contributed to the further development of this technology or will play a crucial role in its further industrial implementation. T2 - 9th International Conference on Photonic Technologies - LANE 2016 CY - Fürth, Germany DA - 19.09.2016 KW - High-power Laserbeam Welding KW - Electromagnetic Force KW - Vacuum KW - Simulation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-377280 DO - https://doi.org/10.1016/j.phpro.2016.08.003 VL - 83 SP - 15 EP - 25 PB - Elsevier B.V. CY - Berlin, Germany AN - OPUS4-37728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hahn, Marc Benjamin A1 - Meyer, Susann A1 - Schröter, Maria-Astrid A1 - Seitz, H. A1 - Kunte, Hans-Jörg A1 - Solomun, Tihomir A1 - Sturm, Heinz T1 - Direct electron irradiation of DNA in fully aqueous environment. Damage determination in combination with Monte Carlo simulations N2 - We report on a study in which plasmid DNA in water was irradiated with 30 keV electrons generated by a scanning electron microscope and passed through a 100 nm thick Si3N4 membrane. The corresponding Monte Carlo simulations suggest that the kinetic energy spectrum of the electrons throughout the water is dominated by low energy electrons (<100 eV). The DNA radiation damage, single-strand breaks (SSB) and double-strand breaks (DSB), was determined by electrophoresis. The median lethal dose of D1/2 = 1.7 ± 0.3 Gy was found to be much smaller compared to partially or fully hydrated DNA irradiated under vacuum conditions. The ratio of DSB to SSB was found to be (1:12) as compared to 1:88) found for hydrated DNA. Our method enables quantitative measurements of radiation damage to biomolecules (DNA, proteins) in solutions under varying conditions (pH, salinity, cosolutes) for an electron energy range which is difficult to probe by standard methods. KW - Plasmid DNA in water KW - Monte Carlo simulation KW - Low energy electrons KW - DNA radiation damage KW - Single-strand break (SSB) KW - Double-strand break (DSB) KW - Lethal dose KW - Radiation damage to biomolecules KW - Solutions (pH, salinity, cosolutes) PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-386981 DO - https://doi.org/10.1039/C6CP07707B SN - 1463-9076 SN - 1463-9084 VL - 19 IS - 3 SP - 1798 EP - 1805 PB - Royal Society of Chemistry AN - OPUS4-38698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fuhrmann, A. A1 - Göstl, R. A1 - Wendt, R. A1 - Kötteritzsch, J. A1 - Hager, M. D. A1 - Schubert, U. S. A1 - Brademann-Jock, Kerstin A1 - Thünemann, Andreas A1 - Nöchel, U. A1 - Behl, M. A1 - Hecht, S. T1 - Conditional repair by locally switching the thermal healing capability of dynamic covalent polymers with light N2 - Healable materials could play an important role in reducing the environmental footprint of our modern technological society through extending the life cycles of consumer products and constructions. However, as most healing processes are carried out by heat alone, the ability to heal damage generally kills the parent material’s thermal and mechanical properties. Here we present a dynamic covalent polymer network whose thermal healing ability can be switched ‘on’ and ‘off’ on demand by light, thereby providing local control over repair while retaining the advantageous macroscopic properties of static polymer networks. We employ a photoswitchable furan-based crosslinker, which reacts with short and mobile maleimidesubstituted poly(lauryl methacrylate) chains forming strong covalent bonds while simultaneously allowing the reversible, spatiotemporally resolved control over thermally induced de- and re-crosslinking. We reason that our system can be adapted to more complex materials and has the potential to impact applications in responsive coatings, photolithography and microfabrication. KW - Small-angle X-ray scattering KW - SAXS KW - Polymer PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-386689 DO - https://doi.org/10.1038/ncomms13623 SN - 2041-1723 VL - 7 SP - Article 13623, 1 EP - 7 PB - NATURE PUBLISHING GROUP CY - MACMILLAN BUILDING, 4 CRINAN ST, LONDON N1 9XW, ENGLAND AN - OPUS4-38668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwarz, F. A1 - Heinrich, Thomas A1 - Lippitz, Andreas A1 - Unger, Wolfgang A1 - Schalley, C. T1 - A photoswitchable rotaxane operating in monolayers on solid support N2 - A novel photoswitchable rotaxane was synthesised and its switching behaviour in solution was analysed with NMR and UV-Vis. A monolayer of rotaxanes was deposited on glass surfaces and the on-surface photoswitching was investigated. Angle-resolved NEXAFS spectra revealed a preferential orientation that reversibly changes upon switching. KW - XPS KW - NEXAFS KW - Photoswitchable rotaxane KW - Self assembly PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-386814 DO - https://doi.org/10.1039/c6cc08586e SN - 0022-4936 SN - 1364-548X SN - 0009-241x SN - 1359-7345 VL - 52 IS - 100 SP - 14458 EP - 14461 PB - Royal Society of Chemistry (RSC) AN - OPUS4-38681 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Unger, Wolfgang A1 - Beiranvand, Z. A1 - Kakanejadifard, A. A1 - Donskyi, Ievgen A1 - Faghani, A. A1 - Tu, Z. A1 - Lippitz, Andreas A1 - Sasanpour, P. A1 - Maschietto, F. A1 - Paulus, B. A1 - Haag, R. A1 - Adeli, M. T1 - Functionalization of fullerene at room temperature: toward new carbon vectors with improved physicochemical properties N2 - In this work, fullerene has been functionalized with cyanuric Chloride at room temperature by a nitrene mediated [2 + 1] cycloaddition reaction. The adduct after functionalization is inherently in the form of azafulleroid and shows broad UV absorption in the wavelength range of 200–800 nm, as well as photothermal conversion and fluorescence with a high quantum yield. KW - Functionalization of fullerenes KW - XPS KW - NEXAFS PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-387076 DO - https://doi.org/10.1039/c6ra23419d SN - 2046-2069 VL - 6 IS - 114 SP - 112771 EP - 112775 PB - Royal Society of Chemistry (RSC) AN - OPUS4-38707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kanje, S. A1 - Hober, S. A1 - Mueller, L. A1 - Herrmann, Antje Jutta T1 - Next generation of labeling reagents for quantitative and multiplexing immunoassays by the use of LA-ICP-MS N2 - Immuno imaging by the use of Laser Ablation Inductively Coupled Mass Spectrometry (LA-ICP-MS) is a growing research field in life sciences such as biology and biomedicine. Various element labeling strategies for antibodies have been developed for the application of multiplex immunoassays analyzed by the use of LA-ICP-MS. High multiplexing capabilities, a wide linear dynamic range and the possibility of absolute quantification are the main advantages of ICP-MS. But in the context of immuno imaging by the use of LA-ICP-MS, quantification of analytes is limited due to non-controllable antibody labeling chemistry. In the presented proof-of-principle a novel antibody labeling technique has been investigated which results in a controlled labeling degree. A small affinity protein based on the C2 domain of protein G was modified with conventional metal coded tags (MeCAT) after introducing a cysteine into the C-terminus of the protein. The modified C2 domain photo-crosslinks to the Fc or Fab region of the IgG and allows specific and covalent labeling of antibodies for multiplex immunoassay analysis by the use of LA-ICP-MS. In combination with a house-made calibration membrane the amount of labeled antibody–antigen complexes in a multiplex western blot immunoassay was determined by LA-ICP-MS. KW - LA-ICP-MS based immunoassays KW - Antibody labeling PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-384712 DO - https://doi.org/10.1039/c6an01878e SN - 0003-2654 SN - 1364-5528 VL - 141 IS - 23 SP - 6374 EP - 6380 PB - The Royal Society of Chemistry AN - OPUS4-38471 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pasternak, H. A1 - Launert, B. A1 - Kannengießer, Thomas A1 - Rhode, Michael T1 - Advanced residual stress assessment of plate girders through welding simulation N2 - This article provides an impression on potentials in applying nowadays welding simulation tools in construction design. This is carried out exemplary on plate girders from two structural steel grades. The calculated residual stresses are compared with measurements by sectioning method. It has been repeatedly stated that present Eurocode models fail to approximate the residual stresses. Especially for high strength steel (HSS) only limited information is available on realistic occurring residual stresses in typical I-girders. The investigations are aimed to give further guidance on these values. A few proposals on advanced models are discussed. T2 - MBST 2016 - Modern Building Materials, Structures and Techniques CY - Vilnius, Litunia DA - 26.05.2016 KW - Residual stresses KW - Plate girders KW - I-shape sections KW - High-strength steel KW - Welding simulation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392177 UR - http://www.sciencedirect.com/science/article/pii/S1877705817305192 DO - https://doi.org/10.1016/j.proeng.2017.02.013 SN - 1877-7058 IS - 172 SP - 23 EP - 30 PB - Elsevier CY - Amsterdam, Niederlande AN - OPUS4-39217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Oberleitner, Lidia A1 - Garbe, L.-A. A1 - Dahmen-Levison, Ursula A1 - Schneider, Rudolf T1 - Improved strategies for selection and characterization of new monoclonal anticarbamazepine antibodies during the screening process using feces and fluorescence polarization immunoassay N2 - Immunoassays are suitable tools for high-throughput screenings. The prerequisite for accurate determinations by these methods is the selection of an excellent antibody. The production and selection of monoclonal antibodies is usually a tedious process. In this study, new strategies for improving antibody production and characterization were applied. This includes the monitoring of the immunization progress in mice through antibodies extracted from feces, which allows a time-resolved and animal-friendly monitoring of the immune response. Additionally, fluorescence polarization immunoassay (FPIA) could be successfully applied for fast and easy examination of cell culture supernatants and the investigation of antibody/antigen interactions including kinetics and fluorescence properties. These methods simplify the selection of the optimal antibody. As a target analyte, carbamazepine was chosen. This is a widely used antiepileptic drug which also frequently occurs in the environment. The new antibody enables CBZ determination in the concentration range 0.66–110 µg L-1 within 10 min using a high-throughput microtiter plate-based FPIA, and between 1.4 and 79 µg L-1 within 5 min applying an automated cuvette-based FPIA instrument, and from 0.05–36 µg L-1 using ELISA. The measurements were performed at a non-equilibrium state which improved the sensitivity and selectivity of the assays. Due to low cross-reactivity especially towards the main CBZ metabolite and other pharmaceuticals (<1%), this antibody gives the opportunity for application in medical and environmental analyses. KW - Antikörper KW - Emerging Pollutants KW - Schadstoffe KW - Monoklonal KW - Pharmazeutika KW - Arzneistoffe KW - Assay KW - Pesticide parathion-methyl KW - Waste-water KW - Samples KW - Pharmaceuticals KW - Quantification PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392473 DO - https://doi.org/10.1039/c6ay01968d SN - 1759-9660 VL - 8 SP - 6883 EP - 6894 PB - Royal Society of Chemistry CY - London AN - OPUS4-39247 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lauer, Franziska A1 - Seifert, Stephan A1 - Kneipp, Janina A1 - Weidner, Steffen T1 - Simplifying the Preparation of Pollen Grains for MALDI-TOF MS Classification N2 - Matrix-assisted laser desorption ionization time of flight mass spectrometry (MALDI-TOF MS) is a well-implemented analytical technique for the investigation of complex biological samples. In MS, the sample preparation strategy is decisive for the success of the measurements. Here, sample preparation processes and target materials for the investigation of different pollen grains are compared. A reduced and optimized sample preparation process prior to MALDI-TOF measurement is presented using conductive carbon tape as target. The application of conductive tape yields in enhanced absolute signal intensities and mass spectral pattern information, which leads to a clear separation in subsequent pattern analysis. The results will be used to improve the taxonomic differentiation and identification, and might be useful for the development of a simple routine method to identify pollen based on mass spectrometry. KW - PCA KW - MALDI-TOF MS KW - Conductive carbon tape KW - Pollen KW - Sample pretreatment PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-392885 UR - http://www.mdpi.com/1422-0067/18/3/543/ DO - https://doi.org/10.3390/ijms18030543 SN - 1422-0067 VL - 18 IS - 3 SP - 543 EP - 554 PB - MDPI AG CY - Basel, Switzerland AN - OPUS4-39288 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seuthe, T. A1 - Mermillod-Blondin, A. A1 - Grehn, M. A1 - Bonse, Jörn A1 - Wondraczek, L. A1 - Eberstein, M. T1 - Structural relaxation phenomena in silicate glasses modifed by irradiation with femtosecond laser pulses N2 - Structural relaxation phenomena in binary and multicomponent lithium silicate glasses were studied upon irradiation with femtosecond (fs) laser pulses (800 nm central wavelength, 130 fs pulse duration) and subsequent thermal annealing experiments. Depending on the annealing temperature, micro-Raman spectroscopy analyses evidenced different relaxation behaviours, associated to bridging and non-bridging oxygen structures present in the glass network. The results indicate that the mobility of lithium ions is an important factor during the glass modification with fs-laser pulses. Quantitative phase contrast imaging (spatial light interference microscopy) revealed that these fs-laser induced structural modifications are closely related to local changes in the refractive index of the material. The results establish a promising strategy for tailoring fs-laser sensitivity of glasses through structural mobility. KW - Femtosecond laser KW - Silicate glasses KW - Raman spectroscopy KW - Structural relaxation KW - Refractive index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393045 DO - https://doi.org/10.1038/srep43815 SN - 2045-2322 VL - 7 SP - 43815, 1 EP - 43815, 10 PB - Nature Publishing Group CY - London, UK AN - OPUS4-39304 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rauwolf, M. A1 - Turyanskaya, A. A1 - Roschger, A. A1 - Prost, J. A1 - Simon, R. A1 - Scharf, O. A1 - Radtke, Martin A1 - Schoonjans, Tom A1 - de Oliveira Guilherme Buzanich, Ana A1 - Klaushofer, K. A1 - Wobrauschek, P. A1 - Hofstaetter, J. G. A1 - Roschger, P. A1 - Streli, C. T1 - Synchrotron radiation micro X-ray fluorescence spectroscopy of thin structures in bone samples: comparison of confocal and color X-ray camera setups N2 - In the quest for finding the ideal synchrotron-radiation-induced imaging method for the investigation of trace element distributions in human bone samples, experiments were performed using both a scanning confocal synchrotron radiation micro X-ray fluorescence (SR-mXRF) (FLUO beamline at ANKA) setup and a full-field color X-ray camera (BAMline at BESSY-II) setup. As zinc is a trace element of special interest in bone, the setups were optimized for its detection. The setups were compared with respect to count rate, required measurement time and spatial resolution. It was demonstrated that the ideal method depends on the element of interest. Although for Ca (a major constituent of the bone with a low energy of 3.69 keV for its K alpha XRF line) the color X-ray camera provided a higher resolution in the plane, for Zn (a trace element in bone) only the confocal SR-µXRF setup was able to sufficiently image the distribution. KW - Synchrotron KW - BAMline KW - BESSY KW - XRF KW - X-ray Color Camera PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-391944 DO - https://doi.org/10.1107/S1600577516017057 SN - 1600-5775 VL - 24 SP - 307 EP - 311 PB - International Union of Crystallography AN - OPUS4-39194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Menzel, Friederike A1 - Conradi, Bianca A1 - Rodenacker, K. A1 - Gorbushina, Anna A1 - Schwibbert, Karin ED - Menzel, Friederike T1 - Flow chamber system for the statistical evaluation of bacterial colonization on materials N2 - Biofilm formation on materials leads to high costs in industrial processes, as well as in medical applications. This fact has stimulated interest in the development of new materials with improved surfaces to reduce bacterial colonization. Standardized tests relying on statistical evidence are indispensable to evaluate the quality and safety of these new materials. We describe here a flow chamber system for biofilm cultivation under controlled conditions with a total capacity for testing up to 32 samples in parallel. In order to quantify the surface colonization, bacterial cells were DAPI (4‘,6-diamidino-2-phenylindole)-stained and examined with epifluorescence microscopy. More than 100 images of each sample were automatically taken and the surface coverage was estimated using the free open source software g’mic, followed by a precise statistical evaluation. Overview images of all gathered pictures were generated to dissect the colonization characteristics of the selected model organism Escherichia coli W3310 on different materials (glass and implant steel). With our approach, differences in bacterial colonization on different materials can be quantified in a statistically validated manner. This reliable test procedure will support the design of improved materials for medical, industrial, and environmental (subaquatic or subaerial) applications. KW - Subaerial and subaquatic biofilm KW - Escherichia coli KW - Image analysis KW - Microscopy KW - Biofilm KW - Biofouling PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-377040 DO - https://doi.org/10.3390/ma9090770 SN - 1996-1944 VL - 9 IS - 9 SP - 770 AN - OPUS4-37704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sötebier, Carina A. A1 - Kutscher, D. J. A1 - Rottmann, L. A1 - Jakubowski, Norbert A1 - Panne, Ulrich A1 - Bettmer, J. T1 - Combination of single particle ICP-QMS and isotope dilution analysis for the determination of size, particle number and number size distribution of silver nanoparticles N2 - Single particle ICP-MS (spICP-MS) has gained great influence in the analysis of engineered nanoparticles (NPs) due to its simplicity, speed and ability to obtain a particle number size distribution. Despite its many advantages, the method is hampered by matrix effects affecting the sensitivity of the instruments. Consequently, over- or underestimated particle sizes might be obtained. To overcome these challenges, we present in this work the detection of both Ag isotopes with a quadrupole mass spectrometer for the application of isotopic dilution analysis (IDA) in combination with spICP-MS. Here, the isotopes are measured sequentially using the conventional spICP-MS integration time of 10 ms. Citrate stabilized Ag NPs of a spherical shape with the nominal diameters of 30, 40, 50 and 80 nm have been investigated. The experimental concept of adding ¹⁰⁹Ag+ solutions to the NP suspensions resulted in the NP Spikes being only visible in the ¹⁰⁷Ag trace. Therefore, a maximum of 45% of the particles was detected compared to that by conventional spICP-MS. A modified mass flow equation was applied to determine the particle sizes, particle size distributions and particle number concentrations of various Ag NPs. The addition of different spike concentrations between 0.5 and 4 mg L⁻¹ ¹⁰⁹Ag resulted in similar particle diameters, suggesting that the calculated diameter might be independent of the spike concentration. This would have the advantage that no size information would be needed before the analysis. By analyzing Ag NP suspensions in a simulated seawater matrix, we demonstrate its significant influence on the particle size determination using conventional spICP-MS. A lower transport efficiency of 6.1% was found in the matrix compared to 7.3% without the matrix. In our approach, the addition of the Matrix influenced the NP intensity stronger than the spike signal, resulting in slightly smaller diameters using IDA–spICP-MS with the matrix compared to the results without the matrix. On the other hand, the IDA–spICP-MS approach with the matrix can result in equivalent results for the particle sizes compared with conventional spICP-MS using suspensions without the matrix. Due to the lower instrument sensitivity in the matrix, a diameter of 30 nm was found to be close to the detection limit of the instrument. KW - Ag nanoparticles KW - Single particle ICP-MS KW - Matrix influence KW - Isotope dilution analysis PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-376490 DO - https://doi.org/10.1039/c6ja00137h SN - 0267-9477 VL - 31 IS - 10 SP - 2045 EP - 2052 AN - OPUS4-37649 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Rhode, Michael A1 - Launert, B. A1 - Dixneit, Jonny A1 - Kannengießer, Thomas A1 - Pasternak, H. ED - Olden, T.-M. ED - Muransky, O. ED - Edwards, L. T1 - Combining sectioning method and X-ray diffraction for evaluation of residual stresses in welded high strength steel components N2 - Residual stresses and distortions in welded I-girders for steel construction are relevant when evaluating the stability of steel beams and column members. The application of high strength steels allows smaller wall thicknesses compared to conventional steels. Therefore, the risk of buckling has to be considered carefully. Due to the lack of knowledge concerning the residual stresses present after welding in high strength steel components conservative assumptions of their level and distribution is typically applied. In this study I-girders made of steels showing strengths of 355 MPa and 690 MPa were welded with varying heat input. Due to the dimension of the I-girders and the complex geometry the accessibility for residual stress measurement using X-ray diffraction was limited. Therefore, saw cutting accompanied by strain gauge measurement has been used to produce smaller sections appropriate to apply X-ray diffraction. The stress relaxation measured by strain gauges has been added to residual stresses determined by X-ray diffraction to obtain the original stress level and distribution before sectioning. The combination of both techniques can produce robust residual stress values. From practical point of view afford for strain gauge application can be limited to a number of measuring positions solely to record the global amount of stress relaxation. X-ray diffraction can be applied after sectioning to determine the residual stresses with sufficient spatial resolution. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - Welding KW - Residual Stress KW - Sectioning Method KW - X-Ray Diffraction KW - Component Testing PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389206 SN - 978-1-94529117-3 SN - 978-1-94529117-6 DO - https://doi.org/10.21741/9781945291173-28 SN - 2474-395X VL - 2 SP - 163 EP - 168 PB - Materials Research Forum LLC CY - Millersville (PA), USA AN - OPUS4-38920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Launert, B. A1 - Rhode, Michael A1 - Kromm, Arne A1 - Pasternak, H. A1 - Kannengießer, Thomas ED - Olden, T.-M. ED - Muransky, O. ED - Edwards, L. T1 - Residual stress influence on the flexural buckling of welded I-girders N2 - The nonlinear analysis became a common tool to precisely assess the load-bearing behavior of steel beam and column members. The failure level is significantly influenced by different types of imperfections, among geometric also structural imperfections (residual stresses). Here are still gaps in the knowledge. Nowadays, 3-D welding simulation developed to a level where it could provide reliable estimation of weld-induced distortion and residual stresses. Nevertheless, modelling and computational effort are still in a less practicable range. In this study a simplified procedure to implement residual welding stresses in continuous large scale members is proposed and the influence on the ultimate limit state of slender members in compression is evaluated for two common structural steel grades. The results showed significant improvements in the utilization of load bearing capacity compared with simplified design methods. The comparatively general approach in this study offers potential for future optimization. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - Stability Design KW - Finit Element Method KW - 2-D Welding Simulation KW - Inherent Strain KW - Plasticity-based Analysis PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389210 SN - 978-1-94529117-3 SN - 978-1-94529117-6 DO - https://doi.org/10.21741/9781945291173-19 SN - 2474-395X VL - 2 SP - 109 EP - 114 PB - Materials Research Forum LLC CY - Millersville (PA), USA AN - OPUS4-38921 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Schasse, R. A1 - Xu, Ping A1 - Mente, Tobias A1 - Kannengießer, Thomas ED - Olden, T.-M. ED - Muransky, O. ED - Edwards, L. T1 - Influence of weld repair by gouging on the residual stresses in high strength steels N2 - Carbon arc-air gouging is a common technology when repairing defects in welded structures. Often this technique is applied in repeated cycles even on the same location of the joint. Due to the multiple heat input by gouging and subsequent re-welding, the residual stresses are strongly influenced. This can become crucial when microstructure and mechanical properties are adversely affected by multiple weld reparations. Knowledge about the relation of gouging and residual stresses is scarce but important when high strength steels, which are sensitive to residual stresses, are processed. The present study shows the effect of repair welding on a high strength steel structural element. The weld and the heat affected zone were subjected to multiple thermal cycles by gouging and subsequent repair welding. The residual stresses were determined by X-ray diffraction at different positions along the joint. The results showed that the residual stress level has increased by the repair cycles. This is most pronounced for the heat affected zone. Adapted welding procedures may prevent detrimental residual stress distributions. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - Repair welding KW - Weld residual stress KW - Carbon arc-air gouging PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389242 SN - 978-1-94529117-6 SN - 978-1-94529117-3 DO - https://doi.org/10.21741/9781945291173-29 SN - 2474-395X VL - 2 SP - 169 EP - 174 PB - Materials Research Forum LLC CY - Millersville, PA, USA AN - OPUS4-38924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tang, S. A1 - Wachtendorf, Volker A1 - Klack, Patrick A1 - Qian, Lijun A1 - Dong, Y. A1 - Schartel, Bernhard T1 - Enhanced flame-retardant effect of montmorillonite/phosphaphenanthrene compound in an epoxy thermoset N2 - A phosphaphenanthrene and triazinetrione group containing flame retardant (TAD) is combined with organically modified montmorillonite (OMMT) in epoxy resin thermosets (EP) to improve the performance of the flame-retardant system. When only 1 wt% OMMT/4 wt% TAD is introduced into the EP, the limited oxygen index (LOI) rises from 26% to 36.9% and a V-0 rating is achieved in a UL 94 test. The decomposition and pyrolysis products in the gas phase and condensed phase were characterized using thermogravimetry-Fourier transform infrared spectroscopy (TG-FTIR). The influence on the decomposition of EP, such as the increase in char yield, is limited with the incorporation of OMMT; a large amount of the phosphorus is released into the gas phase. The flame-retardant effect evaluation based on cone calorimeter data testified that OMMT improves the protective-barrier effect of the fire residue of OMMT/TAD/EP on the macroscopic scale, while TAD mainly causes flame inhibition. The fire residues showed a corresponding macroscopic appearance (digital photo) and microstructure (scanning electron microscope [SEM] results). The protective barrier effect of OMMT and the flame-inhibition effect of TAD combined to exert a superior flame-retardant effect, resulting in sufficient flame-retardant performance of OMMT/TAD/EP KW - Flame retardant KW - Nanocomposite KW - DOPO KW - Thermoset KW - Epoxy resin KW - TG-FTIR PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388865 DO - https://doi.org/10.1039/c6ra25070j SN - 2046-2069 VL - 7 IS - 2 SP - 720 EP - 728 AN - OPUS4-38886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüllmann, Dino A1 - Kohlhoff, Harald A1 - Neumann, Patrick P. ED - Bársony, I. ED - Zolnai, Z. ED - Battistig, G. T1 - Embedded control of a PMSM servo drive without current measurements N2 - A permanent-magnet synchronous motor (PMSM) servo drive for lightweight robotic platforms that have a high torque demand at low rotational speeds has been developed. First, a current-independent torque controller is derived and cascaded with a speed and position controller, while merely an encoder is used as a sensor device in combination with a speed estimator. Finally, the speed estimator output is compared to gyroscope measurements and the overall functioning is verified on a real system. T2 - 30th Eurosensors Conference - Eurosensors 2016 CY - Budapest, Hungary DA - 04.09.2016 KW - BLDC KW - PMSM KW - Motor control KW - Servo drive KW - Optical incremental encoder PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388973 DO - https://doi.org/10.1016/j.proeng.2016.11.487 SN - 1877-7058 VL - 168 SP - 1671 EP - 1675 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-38897 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Petrat, T. A1 - Graf, B. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schmidt, M. ED - Vollertsen, F. ED - Arnold, C. B. T1 - Laser metal deposition as repair technology for a gas turbine burner made of Inconel 718 N2 - Maintenance, repair and overhaul of components are of increasing interest for parts of high complexity and expensive manufacturing costs. In this paper a production process for laser metal deposition is presented, and used to repair a gas turbine burner of Inconel 718. Different parameters for defined track geometries were determined to attain a near net shape deposition with consistent build-up rate for changing wall thicknesses over the manufacturing process. Spot diameter, powder feed rate, welding velocity and laser power were changed as main parameters for a different track size. An optimal overlap rate for a constant layer height was used to calculate the best track size for a fitting layer width similar to the part dimension. Deviations in width and height over the whole build-up process were detected and customized build-up strategies for the 3D sequences were designed. The results show the possibility of a near net shape repair by using different track geometries with laser metal deposition. T2 - LANE - 9 International Conference on Photonic Technologies CY - Fürth, Germany DA - 19.09.2016 KW - Laser metal deposition KW - Inconel 718 KW - Additive manufacturing KW - Maintenance KW - Repair and overhaul PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-376723 UR - http://ac.els-cdn.com/S1875389216301857/1-s2.0-S1875389216301857-main.pdf?_tid=ed1d75de-84a2-11e6-af94-00000aab0f6c&acdnat=1474974777_4917d753cb3d316c4b000ba0760778b5 DO - https://doi.org/10.1016/j.phpro.2016.08.078 SN - 1875-3892 VL - 83 SP - 761 EP - 768 PB - Elservier AN - OPUS4-37672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hahn, Marc Benjamin A1 - Uhlig, F. A1 - Solomun, Tihomir A1 - Smiatek, J. A1 - Sturm, Heinz T1 - Combined influence of ectoine and salt: spectroscopic and numerical evidence for compensating effects of aqueous solutions N2 - Ectoine is an important osmolyte, which allows microorganisms to survive in extreme environmental salinity. The hygroscopic effects of ectoine in pure water can be explained by a strong water binding behavior whereas a study on the effects of ectoine in salty solution is yet missing. We provide Raman spectroscopic evidence that the influence of ectoine and NaCl are opposing and completely independent of each other. The effect can be explained by the formation of strongly hydrogen-bonded water molecules around ectoine which compensate the influence of the salt on the water dynamics. The mechanism is corroborated by first principles calculations and broadens our understanding of zwitterionic osmolytes in aqueous solution. Our findings allow us to provide a possible explanation for the relatively high osmolyte concentrations in halotolerant bacteria. KW - Ectoine KW - Aqueous solution KW - Biological structure KW - Organic osmolytes KW - Raman spectroscopy KW - Water structure PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-376761 UR - http://pubs.rsc.org/en/content/articlelanding/2016/cp/c6cp05417j#!divAbstract DO - https://doi.org/10.1039/c6cp05417j VL - 18 IS - 41 SP - 28398 EP - 28402 PB - Royal Society of Chemistry CY - UK AN - OPUS4-37676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kindzierski, V. A1 - Raschke, Silvia A1 - Knabe, Nicole A1 - Siedler, F. A1 - Scheffer, B. A1 - Pflüger-Grau, K. A1 - Pfeiffer, F. A1 - Oesterhelt, D. A1 - Marin-Sanguino, A. A1 - Kunte, Hans-Jörg T1 - Osmoregulation in the halophilic bacterium halomonas elongata: A case study for integrative systems biology N2 - Halophilic bacteria use a variety of osmoregulatory methods, such as the accumulation of one or more compatible solutes. The wide diversity of compounds that can act as compatible solute complicates the task of understanding the different strategies that halophilic bacteria use to cope with salt. This is specially challenging when attempting to go beyond the pathway that produces a certain compatible solute towards an understanding of how the metabolic network as a whole addresses the problem. Metabolic reconstruction based on genomic data together with Flux Balance Analysis (FBA) is a promising tool to gain insight into this problem. However, as more of these reconstructions become available, it becomes clear that processes predicted by genome annotation may not reflect the processes that are active in vivo. As a case in point, E. coli is unable to grow aerobically on citrate in spite of having all the necessary genes to do it. It has also been shown that the realization of this genetic potential into an actual capability to metabolize citrate is an extremely unlikely event under normal evolutionary conditions. Moreover, many marine bacteria seem to have the same pathways to metabolize glucose but each species uses a different one. In this work, a metabolic network inferred from genomic annotation of the halophilic bacterium Halomonas elongata and proteomic profiling experiments are used as a starting point to motivate targeted experiments in order to find out some of the defining features of the osmoregulatory strategies of this bacterium. This new information is then used to refine the network in order to describe the actual capabilities of H. elongata, rather than its genetic potential. KW - Halomonas elongata KW - Systems biology KW - Flux balance analysis KW - Proteomic analysis PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-391172 DO - https://doi.org/10.1371/journal.pone.0168818 SN - 1932-6203 VL - 12 IS - 1 SP - Article e0168818, 1 EP - 22 AN - OPUS4-39117 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wohlleben, W. A1 - Mielke, Johannes A1 - Bianchin, A. A1 - Ghanem, A. A1 - Freiberger, H. A1 - Rauscher, H. A1 - Gemeinert, Marion A1 - Hodoroaba, Vasile-Dan T1 - Reliable nanomaterial classification of powders using the volume-specific surface area method N2 - The volume-specific surface area (VSSA) of a particulate material is one of two apparently very different metrics recommended by the European Commission for a definition of "nanomaterial" for regulatory purposes: specifically, the VSSA metric may classify nanomaterials and non-nanomaterials differently than the median size in number metrics, depending on the chemical composition, size, polydispersity, shape, porosity, and aggregation of the particles in the powder. Here we evaluate the extent of agreement between classification by electron microscopy (EM) and classification by VSSA on a large set of diverse particulate substances that represent all the anticipated challenges except mixtures of different substances. EM and VSSA are determined in multiple labs to assess also the level of reproducibility. Based on the results obtained on highly characterized benchmark materials from the NanoDefine EU FP7 project, we derive a tiered screening strategy for the purpose of implementing the definition of nanomaterials. We finally apply the Screening strategy to further industrial materials, which were classified correctly and left only borderline cases for EM. On platelet-shaped nanomaterials, VSSA is essential to prevent false-negative classification by EM. On porous materials, approaches involving extended Adsorption isotherms prevent false positive classification by VSSA. We find no false negatives by VSSA, neither in Tier 1 nor in Tier 2, despite real-world industrial polydispersity and diverse composition, shape, and coatings. The VSSA screening strategy is recommended for inclusion in a technical guidance for the implementation of the definition. KW - Nanomaterial KW - Nanomaterial classification KW - Regulation KW - VSSA KW - Size measurement KW - Particle size PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-391450 DO - https://doi.org/10.1007/s11051-017-3741-x SN - 1388-0764 SN - 1572-896X VL - 19 IS - 2 SP - Article 61, 1 EP - 16 PB - Springer Nature AN - OPUS4-39145 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zydziak, N. A1 - Konrad, W. A1 - Feist, F. A1 - Afonin, S. A1 - Weidner, Steffen A1 - Barner-Kowollik, C. T1 - Coding and decoding libraries of sequence-defined functional copolymers synthesized via photoligation N2 - Designing artificial macromolecules with absolute sequence order represents a considerable challenge. Here we report an advanced light-induced avenue to monodisperse sequencedefined functional linear macromolecules up to decamers via a unique photochemical approach. The versatility of the synthetic strategy—combining sequential and modular concepts—enables the synthesis of perfect macromolecules varying in chemical constitution and topology. Specific functions are placed at arbitrary positions along the chain via the successive addition of monomer units and blocks, leading to a library of functional homopolymers, alternating copolymers and block copolymers. The in-depth characterization of each sequence-defined chain confirms the precision nature of the macromolecules. Decoding of the functional information contained in the molecular structure is achieved via tandem mass spectrometry without recourse to their synthetic history, showing that the sequence information can be read.We submit that the presented photochemical strategy is a viable and advanced concept for coding individual monomer units along a macromolecular chain. KW - Photoligation KW - Copolymer sequence KW - MALDI-TOF MS/MS PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-391542 DO - https://doi.org/10.1038/ncomms13672 SN - 2041-1723 VL - 7 SP - Artikel Nr. 13672 AN - OPUS4-39154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hernández-Nava, E. A1 - Smith, C.J. A1 - Derguti, F. A1 - Tammas-Williams, S. A1 - Léonard, Fabien A1 - Withers, P. J. A1 - Todd, I. A1 - Goodall, R. T1 - The effect of defects on the mechanical response of Ti-6Al-4V cubic lattice structures fabricated by electron beam melting N2 - Electron Beam Melting (EBM) as a means of Additive Manufacturing (AM), is of interest for the fabrication of intricate geometries for cellular materials in areas where complex architectures are needed, e.g. biomedical implants. Most studies have focused on specific geometries and so the effect of the structure on mechanical performance is not well understood. Many kinds of micro- and macro-scale defects can arise in additively manufactured components, so assessment of their influence on properties is needed. In this work, lattices of Ti-6Al-4V having a cubic structure have been manufactured by EBM, and the effect of heat treatments above and below the β-transus temperature on microstructure and compression response have been investigated. The former modifies only slightly the α + β structure and mechanical performance whereas the latter leads to coarse alternating α and β lamellae packets and α at the prior grain boundaries with a 10% loss in yield strength. The variation in the compressive yield stress with strut diameter is in good accord with simple models based on compressive deformation rather than shearing or buckling. Internal pores for struts aligned with the build direction are found around the edges of the solid form, in regions which seem to be associated with the EB scan pattern. Struts normal to the build direction show more significant defects but their redundancy means that they do not compromise the compressive performance in the build direction. Using a particle size in the range 45–100 μm minimum weld-track sizes were experimentally and numerically identified to be 176 and 148 μm in depth respectively with a depth-to-width ratio of 0.55. This produced a beam pass of the order of 300 μm oversizing small features (struts of 0.4 and 0.6 mm nominal diameter) when a contour around the strut periphery was applied. KW - Cellular solids KW - Additive manufacturing KW - Titanium alloy KW - Mechanical properties KW - X-ray computed tomography PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-390686 DO - https://doi.org/10.1016/j.actamat.2016.02.029 SN - 1359-6454 VL - 108 SP - 279 EP - 292 PB - Elsevier Ltd. CY - Amsterdam [u.a.] AN - OPUS4-39068 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dixneit, Jonny A1 - Kromm, Arne A1 - Boin, M. A1 - Kannengießer, Thomas A1 - Gibmeier, J. ED - Olden, T.-M. ED - Muransky, O. Muransky ED - Edwards, L. T1 - Influence of heat control on residual stresses in low transformation temperature (LTT) large scale welds N2 - The current paper presents residual stress analyses of large scale LTT (Low Transformation Temperature) welds. LTT filler materials are specially designed for residual stress engineering by means of an adjusted martensite phase transformation. Controlling the level of mostly detrimental residual stresses already during the welding process would be highly attractive as time and cost consuming post processing may be prevented. In large scale welds the residual stress state is influenced by the heat control (e.g. interpass temperature) during welding. Therefore, welding residual stresses are studied here putting the focus on the influence of welding process parameters while joining heavy steel sections with a thickness of 25 mm. The residual stress state was determined at the top surface using X-ray diffraction as well as in the bulk by neutron diffraction. The results show that control of the interpass temperature is vital for the residual stresses present in the joints. This accounts for the top surface but is most pronounced for the bulk of the welds. While high interpass temperatures are appropriate to induce compressive residual stresses in the weld metal, low interpass temperatures favor unwanted tensile residual stresses instead. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - LTT KW - Welding residual stress KW - Phase transformation KW - Interpass temperature PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389628 SN - 978-1-94529117-3 SN - 978-1-94529116-6 DO - https://doi.org/10.21741/9781945291173-38 SN - 2474-395X VL - 2 SP - 223 EP - 228 PB - Materials Research Forum LLC CY - Millersville (PA), USA AN - OPUS4-38962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, Manuel A1 - Kabelitz, Anke A1 - Gorelik, T. E. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Reinholz, Uwe A1 - Kolb, U. A1 - Rademann, K. A1 - Emmerling, Franziska T1 - The crystallisation of copper(II) phenylphosphonates N2 - The crystal structures and syntheses of four different copper(II) phenylphosphonates, the monophenylphosphonates α-, β-, and γ-Cu(O3PC6H5)·H2O (α-CuPhPmH (1) β-CuPhPmH (2) and γ-CuPhPmH (3)), and the diphosphonate Cu(HO3PC6H5)2·H2O (CuPhP2mH (4)), are presented. The compounds were synthesized from solution at room temperature, at elevated temperature, under hydrothermal conditions, and mechanochemical conditions. The structures of α-CuPhPmH (1) and CuPhP2mH (4) were solved from powder X-ray diffraction data. The structure of β-CuPhPmH (2) was solved by single crystal X-ray analysis. The structures were validated by extended X-ray absorption fine structure (EXAFS) and DTA analyses. Disorder of the crystal structure was elucidated by electron diffraction. The relationship between the compounds and their reaction pathways were investigated by in situ synchrotron measurements. KW - Mechanochemistry KW - Metal phosphonate KW - In situ PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-384217 DO - https://doi.org/10.1039/C6DT02904C SN - 1477-9226 SN - 1477-9234 VL - 45 IS - 43 SP - 17453 EP - 17463 PB - The Royal Society of Chemistry AN - OPUS4-38421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fankhänel, J. A1 - Silbernagl, Dorothee A1 - Ghasem Zadeh Khorasani, Media A1 - Daum, B. A1 - Kempe, A. A1 - Sturm, Heinz A1 - Rolfes, R. T1 - Mechanical properties of Boehmite evaluated by Atomic Force Microscopy experiments and Molecular Dynamic Finite Element simulations N2 - Boehmite nanoparticles show great potential in improving mechanical properties of fiber reinforced polymers. In order to predict the properties of nanocomposites, knowledge about the material parameters of the constituent phases, including the boehmite particles, is crucial. In this study, the mechanical behavior of boehmite is investigated using Atomic Force Microscopy (AFM) experiments and Molecular Dynamic Finite Element Method (MDFEM) simulations. Young’s modulus of the perfect crystalline boehmite nanoparticles is derived from numerical AFM simulations. Results of AFM experiments on boehmite nanoparticles deviate significantly. Possible causes are identified by experiments on complementary types of boehmite, that is, geological and hydrothermally synthesized samples, and further simulations of imperfect crystals and combined boehmite/epoxy models. Under certain circumstances, the mechanical behavior of boehmite was found to be dominated by inelastic effects that are discussed in detail in the present work.The studies are substantiated with accompanying X-ray diffraction and Raman experiments. KW - AFM KW - MDFEM KW - Nanocomposite KW - Epoxy KW - X-ray diffraction KW - Raman spectroscopy KW - Young’s modulus KW - Slippage of weakly linked layers PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-384230 UR - https://www.hindawi.com/journals/jnm/2016/5017213/#B26 DO - https://doi.org/10.1155/2016/5017213 VL - 2016 IS - Article ID 5017213 SP - 1 EP - 13 PB - Hindawi Publishing Corporation AN - OPUS4-38423 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Michalik-Onichimowska, Aleksandra A1 - Kern, Simon A1 - Riedel, Jens A1 - Panne, Ulrich A1 - King, R. A1 - Maiwald, Michael T1 - ‘‘Click” analytics for ‘‘click” chemistry – A simple method for calibration–free evaluation of online NMR spectra N2 - Driven mostly by the search for chemical syntheses under biocompatible conditions, so called "click" chemistry rapidly became a growing field of research. The resulting simple one-pot reactions are so far only scarcely accompanied by an adequate optimization via comparably straightforward and robust analysis techniques possessing short set-up times. Here, we report on a fast and reliable calibration-free online NMR monitoring approach for technical mixtures. It combines a versatile fluidic system, continuous-flow measurement of 1H spectra with a time interval of 20 s per spectrum, and a robust, fully automated algorithm to interpret the obtained data. As a proof-of-concept, the thiol-ene coupling between N-boc cysteine methyl ester and allyl alcohol was conducted in a variety of non-deuterated solvents while its time-resolved behaviour was characterized with step tracer experiments. Overlapping signals in online spectra during thiol-ene coupling could be deconvoluted with a spectral model using indirect hard modeling and were subsequently converted to either molar ratios (using a calibrationfree approach) or absolute concentrations (using 1-point calibration). For various solvents the kinetic constant k for pseudo-first order reaction was estimated to be 3.9 h-1 at 25 °C. The obtained results were compared with direct integration of non-overlapping signals and showed good agreement with the implemented mass balance. KW - Online NMR Spectroscopy KW - Reaction Monitoring KW - Automated Data Evaluation KW - Thiol-ene click chemistry KW - Click Chemistry KW - Process Analytical Technology PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393232 UR - http://www.sciencedirect.com/science/article/pii/S1090780717300575 DO - https://doi.org/10.1016/j.jmr.2017.02.018 VL - 277 SP - 154 EP - 161 PB - Elsevier Inc. CY - Oxford AN - OPUS4-39323 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mirtschin, Nikolaus A1 - Pretsch, T. T1 - Programming of one- and two-step stress recovery in a poly(ester urethane) N2 - This work demonstrates that phase-segregated poly(ester urethane) (PEU) with switching segments of crystallizable poly(1,4-butylene adipate) (PBA) can be programmed to generate two separate stress recovery events upon heating under constant strain conditions. For programming, two elongations are applied at different temperatures, followed by unloading and cooling. During the adjacent heating, two-step stress recovery is triggered. The results indicate that the magnitude of the stress recovery signals corresponds to the recovery of the two deformation stresses in reverse order. As demonstrated by further experiments, twofold stress recovery can be detected as long as the elongation at higher temperature exceeds the strain level of the deformation at lower temperature. Another finding includes that varying the lower deformation temperature enables a control over the stress recovery temperature and thus the implementation of so-called “temperature-memory effects”. Moreover, exerting only one elongation during programming enables a heating-initiated one-step stress recovery close to the deformation temperature. Based on these findings, such polymers may offer new technological opportunities in the fields of active assembly when used as fastening elements and in functional clothing when utilized for compression stockings. KW - DSC KW - Mechanical properties PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-393585 DO - https://doi.org/10.3390/polym9030098 SN - 2073-4360 VL - 9 IS - 3 SP - Article 98, 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-39358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yasutaka, T. A1 - Imoto, Y. A1 - Kurosawa, A. A1 - Someya, M. A1 - Higashino, K. A1 - Kalbe, Ute A1 - Sakanakura, H. T1 - Effects of colloidal particles on the results and reproducibility of batch leaching tests for heavy metal-contaminated soil N2 - A simple batch test leaching procedure is used in many countries, as a compliance test, to evaluate the leaching of mainly inorganic substances from soil. However, agitating certain types of soil and then passing the solution through a membrane filter with 0.45-µm pores yields filtrates that have been colored by the colloidal particles. These colloids might affect the results of the inorganic substances obtained in the batch tests. In this study, we evaluated the effects of colloidal particles on the results and the reproducibility of batch tests on contaminated soil using different agitation methods and membrane filters with different pore sizes. The leaching behaviors of As, Pb, Se, F and Cl from three types of soil were studied. The As and Pb concentrations in the leachates of some types of soil were clearly affected by the amount of colloidal particles with a diameter of 0.10–0.45 µm and by the agitation method used. This was probably because As and Pb were present mainly in the particulate form in the leachate that had been passed through a membrane filter with 0.45-µm pores. This is not the case for every type of soil. The results of batch leaching tests showed that not only dissolved but also colloidal forms with a diameter of 0.10–0.45 µm might be included and that the existence of colloidal particles in the leachate decreases the batch leaching test reproducibility. KW - Leaching KW - Contaminated soil KW - Heavy metals KW - Colloids PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-429940 UR - https://www.sciencedirect.com/science/article/pii/S0038080617301166#! DO - https://doi.org/10.1016/j.sandf.2017.08.014 SN - 0038-0806 VL - 57 IS - 5 SP - 861 EP - 871 PB - Elsevier B.V. AN - OPUS4-42994 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dackermann, U. A1 - Yu, Y. A1 - Niederleithinger, Ernst A1 - Li, J. A1 - Wiggenhauser, Herbert T1 - Condition Assessment of Foundation Piles and Utility Poles Based on Guided Wave Propagation Using a Network of Tactile Transducers and Support Vector Machines N2 - This paper presents a novel non-destructive testing and health monitoring system using a network of tactile transducers and accelerometers for the condition assessment and damage classification of foundation piles and utility poles. While in traditional pile integrity testing an impact hammer with broadband frequency excitation is typically used, the proposed testing system utilizes an innovative excitation system based on a network of tactile transducers to induce controlled narrow-band frequency stress waves. Thereby, the simultaneous excitation of multiple stress wave types and modes is avoided (or at least reduced), and targeted wave forms can be generated. The new testing system enables the testing and monitoring of foundation piles and utility poles where the top is inaccessible, making the new testing system suitable, for example, for the condition assessment of pile structures with obstructed heads and of poles with live wires. For system validation, the new system was experimentally tested on nine timber and concrete poles that were inflicted with several types of damage. The tactile transducers were excited with continuous sine wave signals of 1 kHz frequency. Support vector machines were employed together with advanced signal processing algorithms to distinguish recorded stress wave signals from pole structures with different types of damage. The results show that using fast Fourier transform signals, combined with principal component analysis as the input feature vector for support vector machine (SVM) classifiers with different kernel functions, can achieve damage classification with accuracies of 92.5% ± 7.5%. KW - Structural Health Monitoring KW - Non-Destructive Testing KW - Sensor network KW - Support vector machine KW - Utility poles PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-434868 UR - http://www.mdpi.com/1424-8220/17/12/2938 DO - https://doi.org/10.3390/s17122938 SN - 1424-8220 VL - 17 IS - 12 SP - Article 2938, 1 EP - 16 PB - MDPI CY - Basel, Schweiz AN - OPUS4-43486 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauw, Brian Richard A1 - Kästner, Claudia A1 - Thünemann, Andreas T1 - Nanoparticle size distribution quantification: results of a small-angle X-ray scattering inter-laboratory comparison N2 - This paper presents the first worldwide inter-laboratory comparison of small-angle X-ray scattering (SAXS) for nanoparticle sizing. The measurands in this comparison are the mean particle radius, the width of the size distribution and the particle concentration. The investigated sample consists of dispersed silver nanoparticles, surrounded by a stabilizing polymeric shell of poly(acrylic acid). The silver cores dominate the X-ray scattering pattern, leading to the determination of their radius size distribution using (i) the generalized indirect Fourier transformation method, (ii) classical model fitting using SASfit and (iii) a Monte Carlo fitting approach using McSAS. The application of these three methods to the collected data sets from the various laboratories produces consistent mean number- and volume-weighted core radii of Rn = 2.76 (6) nm and Rv = 3.20 (4) nm, respectively. The corresponding widths of the lognormal radius distribution of the particles were σn = 0.65 (1) nm and σv = 0.71 (1) nm. The particle concentration determined using this method was 3.0 (4) g l−1 or 4.2 (7) × 10−6 mol l−1. These results are affected slightly by the choice of data evaluation procedure, but not by the instruments: the participating laboratories at synchrotron SAXS beamlines, commercial and in-house-designed instruments were all able to provide highly consistent data. This demonstrates that SAXS is a suitable method for revealing particle size distributions in the sub-20 nm region (at minimum), out of reach for most other analytical methods. KW - SAXS KW - Small-angle X-ray scattering KW - Silver nanoparticles PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-422800 DO - https://doi.org/10.1107/S160057671701010X SN - 1600-5767 VL - 50 IS - 5 SP - 1280 EP - 1288 PB - (IUCr) International Union of Crystallography AN - OPUS4-42280 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Chatzigiannakis, E. A1 - Beckmann, Jörg A1 - Wachtendorf, Volker A1 - von der Ehe, Kerstin A1 - Braun, Ulrike A1 - Jaunich, Matthias A1 - Schade, U. A1 - Wolff, Dietmar T1 - Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE N2 - Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE. KW - Irradiation KW - UHMWPE KW - Colour center KW - Yellowness index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423992 DO - https://doi.org/10.1155/2017/1362491 SN - 1687-9422 VL - 2017 IS - Article ID 1362491 SP - 1 EP - 10 PB - Hindawi AN - OPUS4-42399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidel, R. A1 - Kraffert, K. A1 - Kabelitz, Anke A1 - Pohl, M.N. A1 - Kraehnert, R. A1 - Emmerling, Franziska A1 - Winter, B. T1 - Detection of the electronic structure of iron-(III)-oxo oligomers forming in aqueous solutions N2 - The nature of the small iron-oxo oligomers in iron-(III) aqueous solutions has a determining effect on the chemical processes that govern the formation of nanoparticles in aqueous phase. Here we report on a liquid-Jet photoelectron-spectroscopy experiment for the investigation of the electronic structure of the occurring iron-oxo oligomers in FeCl3 aqueous solutions. The only iron species in the as-prepared 0.75 M solution are Fe3+ monomers. Addition of NaOH initiates Fe3+ hydrolysis which is followed by the formation of iron-oxo oligomers. At small enough NaOH concentrations, corresponding to approximately [OH]/[Fe] = 0.2–0.25 ratio, the iron oligomers can be stabilized for several hours without engaging in further aggregation. Here, we apply a combination of non-resonant as well as iron 2p and Oxygen 1s resonant photoelectron spectroscopy from a liquid microjet to detect the electronic structure of the occurring species. Specifically, the oxygen 1s partial electron yield X-ray absorption (PEY-XA) spectra are found to exhibit a peak well below the onset of liquid water and OH (aq) absorption. The iron 2p absorption gives rise to signal centered between the main absorption bands typical for aqueous Fe3+. Absorption bands in both PEY-XA spectra are found to correlate with an enhanced photoelectron Peak near 20 eV binding energy, which demonstrates the sensitivity of resonant photoelectron (RPE) spectroscopy to mixing between iron and ligand orbitals. These various signals from the iron-oxo oligomers exhibit Maximum intensity at [OH]/[Fe] = 0.25 ratio. For the same ratio, we observe changes in the pH as well as in complementary Raman spectra, which can be assigned to the Transition from monomeric to oligomeric species. At approximately [OH]/[Fe] = 0.3 we begin to observe particles larger than 1 nm in radius, detected by small-angle X-ray scattering. KW - Iron-oxo oligomers KW - XPS KW - Electronic structure PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-433468 DO - https://doi.org/10.1039/c7cp06945f SN - 1463-9076 SN - 1463-9084 VL - 19 IS - 48 SP - 32226 EP - 32234 AN - OPUS4-43346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dong, S. A1 - Leng, J. A1 - Feng, Y. A1 - Liu, M. A1 - Stackhouse, C. J. A1 - Schönhals, Andreas A1 - Chiappisi, L. A1 - Gao, L. A1 - Chen, W. A1 - Shang, J. A1 - Jin, L. A1 - Qi, Z. A1 - Schalley, C. A. T1 - Structural water as an essential comonomer in supramolecular polymerization N2 - Although the concept of structural water that is bound inside hydrophobic pockets and helps to stabilize protein structures is well established, water has rarely found a similar role in supramolecular polymers. Water is often used as a solvent for supramolecular polymerization, however without taking the role of a comonomer for the supramolecular polymer structure. We report a low–molecular weight monomer whose supramolecular polymerization is triggered by the incorporation of water. The presence of water molecules as comonomers is essential to the polymerization process. The supramolecular polymeric material exhibits strong adhesion to surfaces, such as glass and paper. It can be used as a water-activated glue, which can be released at higher temperatures and reused many times without losing its performance. KW - Supra molecular polymerization PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-432728 DO - https://doi.org/10.1126/sciadv.aao0900 SN - 2375-2548 VL - 3 IS - 11 SP - eaao0900, 1 EP - eaao0900, 8 PB - American Association for the Advancement of Science AN - OPUS4-43272 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taabache, Soraya A1 - Bertin, Annabelle T1 - Vesicles from amphiphilic dumbbells and Janus dendrimers: bioinspired self-assembled structures for biomedical applications N2 - The current review focuses on vesicles obtained from the self-assembly of two types of dendritic macromolecules, namely amphiphilic Janus dendrimers (forming dendrimersomes) and amphiphilic dumbbells. In the first part, we will present some synthetic strategies and the various building blocks that can be used to obtain dendritic-based macromolecules, thereby showing their structural versatility. We put our focus on amphiphilic Janus dendrimers and amphiphilic dumbbells that form vesicles in water but we also encompass vesicles formed thereof in organic solvents. The second part of this review deals with the production methods of these vesicles at the nanoscale but also at the microscale. Furthermore, the influence of various parameters (intrinsic to the amphiphilic JD and extrinsic—from the environment) on the type of vesicle formed will be discussed. In the third part, we will review the numerous biomedical applications of these vesicles of nano- or micron-size. KW - Janus dendrimers KW - Amphiphilic dumbbells KW - Self-assembled structures KW - Dendrimersomes KW - Artificial cells PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418245 DO - https://doi.org/10.3390/polym9070280 SN - 2073-4360 VL - 9 IS - 7 SP - Article 280, 1 EP - 36 AN - OPUS4-41824 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfennig, Anja A1 - Kranzmann, Axel A1 - Wolthusen, Helmut T1 - Unusual Corrosion Behavior of 1.4542 Exposed a Laboratory Saline Aquifer Water CCS-Environment N2 - Differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Surface corrosion layers are homogeneous but unusually discontinuously ellipsoidal. After 8000 h at 100 bar maximum corrosion rate in the liquid phase is approximately 0.014 mm/year, with normalizing providing best corrosion resistance and approximately 0.003 mm/year in the supercritical phase where hardening+tempering at 670 °C leads to lowest corrosion rates. KW - CO2-storage KW - Supercritical CO2 KW - Steel KW - Pipeline KW - Corrosion KW - CCS PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418472 DO - https://doi.org/10.1016/j.egypro.2017.03.1679 VL - 114 SP - 5229 EP - 5240 PB - Elsevier Ltd. AN - OPUS4-41847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Liu, F. A1 - Lakey, P. S. J. A1 - Berkemeier, T. A1 - Tong, H. A1 - Kunert, A. T. A1 - Meusel, H. A1 - Cheng, Y. A1 - Su, H. A1 - Fröhlich-Nowoisky, J. A1 - Lai, S. A1 - Weller, Michael G. A1 - Shiraiwa, M. A1 - Pöschl, U. A1 - Kampf, C. J. T1 - Atmospheric protein chemistry influenced by anthropogenic air pollutants: nitration and oligomerization upon exposure to ozone and nitrogen dioxide N2 - The allergenic potential of airborne proteins may be enhanced via post-translational modification induced by air pollutants like ozone (O3) and nitrogen dioxide (NO2). The molecular mechanisms and kinetics of the chemical modifications that enhance the allergenicity of proteins, however, are still not fully understood. Here, protein tyrosine nitration and oligomerization upon simultaneous exposure of O3 and NO2 were studied in coated-wall flow-tube and bulk solution experiments under varying atmospherically relevant conditions (5–200 ppb O3, 5–200 ppb NO2, 45–96% RH), using bovine serum albumin as a model protein. Generally, more tyrosine residues were found to react via the nitration pathway than via the oligomerization pathway. Depending on reaction conditions, oligomer mass fractions and nitration degrees were in the ranges of 2.5–25% and 0.5–7%, respectively. The experimental results were well reproduced by the kinetic multilayer model of aerosol surface and bulk chemistry (KM-SUB). The extent of nitration and oligomerization strongly depends on relative humidity (RH) due to moisture-induced phase transition of proteins, highlighting the importance of cloud processing conditions for accelerated protein chemistry. Dimeric and nitrated species were major products in the liquid phase, while protein oligomerization was observed to a greater extent for the solid and semi-solid phase states of proteins. Our results show that the rate of both processes was sensitive towards ambient ozone concentration but rather insensitive towards different NO2 levels. An increase of tropospheric ozone concentrations in the Anthropocene may thus promote pro-allergic protein modifications and contribute to the observed increase of allergies over the past decades. KW - Oxidation KW - Nitration KW - Cross-linking KW - Ozone KW - Nitrogen dioxide KW - Dimer KW - Air pollution KW - Diesel KW - Aeroallergens KW - Pollen KW - Tyrosine KW - Nitrotyrosine KW - BSA KW - Albumin PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418482 DO - https://doi.org/10.1039/c7fd00005g SN - 1359-6640 VL - 200 SP - 413 EP - 427 PB - Royal Society of Chemistry CY - London AN - OPUS4-41848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pfennig, Anja A1 - Wolf, Marcus A1 - Gröber, Andre A1 - Böllinghaus, Thomas A1 - Kranzmann, Axel T1 - Corrosion fatigue of 1.4542 exposed to a laboratory saline aquifer water CCS-environment N2 - X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ∼ 30 Hz). Due to the rather heterogeneous fine machined surfaces (Rz=4) the specimens are comparable with prefabricated parts. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa and lies 60% below the stress amplitude measured in air. The scatter range TN = 1:34 is disproportionately large. Although the fracture surface exhibited the typical striations and corroded surface areas no significant differences were found. The hardness was found to be homogeneous in all specimens tested at 335 HV10. Non-metallic inclusions were found within the microstructure, but no correlation could be found between the inclusions and early rupture. Still specimens that showed inclusions at the fracture surface and its cross section endured lower number of cycles. Additionally Aluminium was analysed in specimens with low number of cycles and may be cause for early rupture during corrosion fatigue tests. These findings reveal a very high sensitivity on a homogeneous microstructure upon the corrosion and corrosion fatigue behaviour of X5CrNiCuNb16-4 and needs to be taken into account when regarding this steel as pipe steel during injection of CO2 into saline aquifers. T2 - 13th International Conference on Greenhouse Gas Control Technologies CY - Lausanne, Switzerland DA - 14.11.2016 KW - Steel KW - Corrosion fatigue KW - Electrochemistry KW - Reliability KW - CCS KW - CO2-storage PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418525 DO - https://doi.org/10.1016/j.egypro.2017.03.1678 SN - 1876-6102 VL - 114 SP - 5219 EP - 5228 AN - OPUS4-41852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Obaton, A-F. A1 - Fain, J. A1 - Djemaï, M. A1 - Meinel, Dietmar A1 - Léonard, Fabien A1 - Mahé, E. A1 - Lécuelle, B. A1 - Fouchet, J-J. A1 - Bruno, Giovanni T1 - In vivo XCT bone characterization of lattice structured implants fabricated by additive manufacturing N2 - Several cylindrical specimens and dental implants, presenting diagonal lattice structures with different cell sizes (600, 900 and 1200 µm) were additively manufactured by selective laser melting process. Then they were implanted for two months in a sheep. After removal, they were studied by Archimedes’ method as well as X-ray computed tomography in order to assess the penetration of bone into the lattice. We observed that the additive manufactured parts were geometrically conform to the theoretical specifications. However, several particles were left adhering to the surface of the lattice, thereby partly or entirely obstructing the cells. Nevertheless, bone penetration was clearly visible. We conclude that the 900 µm lattice cell size is more favourable to bone penetration than the 1200 µm lattice cell size, as the bone penetration is 84 % for 900 µm against 54 % for 1200 µm cell structures. The lower bone penetration value for the 1200 µm lattice cell could possibly be attributed to the short residence time in the sheep. Our results lead to the conclusion that lattice implants additively manufactured by selective laser melting enable better bone integration. KW - Biomedical engineering KW - Dentistry KW - Medical imaging KW - X-ray computer tomography PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-418648 DO - https://doi.org/10.1016/j.heliyon.2017.e00374 SN - 2405-8440 IS - 3 SP - Article e00374, 1 EP - 21 PB - Elsevier Limited CY - 125 London Wall London, EC2Y 5AS United Kingdom AN - OPUS4-41864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stajanca, Pavol A1 - Krebber, Katerina T1 - Radiation-induced attenuation of perfluorinated polymer optical fibers for radiation monitoring N2 - Due to some of their unique properties, optical fiber dosimeters are attractive and extensively researched devices in several radiation-related areas. This work evaluates the Performance and potential of commercial perfluorinated polymer optical fibers (PF-POFs) for radiation Monitoring applications. Gamma radiation-induced attenuation (RIA) of two commercial PF-POFs is evaluated in the VIS spectral region. Influence of a dose rate and temperature on RIA measurement is investigated, along with defect stability and measurement repeatability. Co-extruded PF-POFs are identified as more suitable for radiation monitoring applications due to lower dose-rate dependence. With co-extruded PF-POF, RIA measurement holds potential for highly-sensitive radiation Monitoring with good reproducibility. The results show that operation in the blue part of the spectrum provides most favorable performance in terms of the largest nominal Radiation sensitivity, lower temperature, and dose-rate dependence as well as higher defect stability. We demonstrate for the first time to our knowledge, that PF-POFs can be used for distributed detection of radiation with doses down to tens of Grays. The off-the-shelf, user-friendly PF-POF could be of interest as a cheap, disposable sensor for various applications, especially of a more qualitative nature. KW - Perfluorinated polymer optical fiber KW - Cytop KW - Ionizing radiation KW - Radiation-induced attenuation KW - Gamma radiation monitoring PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419504 DO - https://doi.org/10.3390/s17091959 SN - 1424-8220 VL - 17 IS - 9 SP - Article 1959, 1 EP - 12 PB - MDPI AN - OPUS4-41950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Luong, Thi Mai Hoa A1 - Zabel, V. A1 - Lorenz, W. A1 - Rohrmann, R.G. T1 - Non-destructive assessment of the axial stress state in iron and steel truss structures by dynamic measurements N2 - This paper is concerned with the inverse identification of the stress state in axially loaded slender members of iron and steel truss structures using measured dynamic data. A methodology is proposed based on the finite element model updating coupled with nature-inspired optimization techniques, in particular the particle swarm optimization. The numerical model of truss structures is calibrated using natural frequencies and mode shapes from vibration tests, as well as additional information of the axial forces in selected truss members based on the experimentally identified modal parameters. The results of the identification are the axial forces or corresponding stresses in truss structures and the joint rigidity in relation to pinned and rigid conditions. Attention is given to several examined aspects, including the effects of the axial tensile and compressive forces on the dynamic responses of trusses, mode pairing criteria, as well as modeling assumptions of joints and the use of a joint rigidity parameter. Considering the pairing of modes, it is performed by adapting an enhanced modal assurance criterion that allows the selection of desired clusters of degrees-of-freedom. Thus, information extracted from the measurements related to specific modes is utilized in a more beneficial way. For modeling of joints, the numerical model of a truss structure includes rotational springs of variable stiffness to represent semi-rigid connections. Moreover, a fixity factor is introduced for practical estimation of the joint flexibility. The effectiveness of the proposed methodology is demonstrated by case studies involving simulated and laboratory experimental data. T2 - X International Conference on Structural Dynamics, EURODYN 2017 DA - 10.09.2017 KW - Axial force KW - Dynamic test KW - Model updating KW - Optimization technique KW - Truss structures KW - Modal parameters PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419311 DO - https://doi.org/10.1016/j.proeng.2017.09.447 SN - 1877-7058 VL - 199 SP - 3380 EP - 3385 PB - Elsevier AN - OPUS4-41931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hahn, Marc Benjamin A1 - Susann, Meyer A1 - Schröter, Maria-Astrid A1 - Kunte, Hans-Jörg A1 - Solomun, Tihomir A1 - Sturm, Heinz T1 - DNA protection by ectoine from ionizing radiation: molecular mechanisms N2 - Ectoine, a compatible solute and osmolyte, is known to be an effective protectant of biomolecules and whole cells against heating, freezing and extreme salinity. Protection of cells (human keratinocytes) by ectoine against ultraviolet radiation has also been reported by various authors, although the underlying mechanism is not yet understood. We present the first electron irradiation of DNA in a fully aqueous environment in the presence of ectoine and at high salt concentrations. The results demonstrate effective protection of DNA by ectoine against the induction of single-strand breaks by ionizing radiation. The effect is explained by an increase in low-energy electron scattering at the enhanced free-vibrational density of states of water due to ectoine, as well as the use of ectoine as an ˙OH-radical scavenger. This was demonstrated by Raman spectroscopy and electron paramagnetic resonance (EPR). KW - Ectoine KW - DNA KW - Radiation protection KW - Ionizing radiation KW - Compatible solute KW - Biomolecules KW - Sodium chloride KW - Aqueous solution KW - Hydroxyectoine KW - Raman spectroscopy KW - Electron irradiation KW - Cancer KW - Radical scavenger KW - Low energy electrons KW - Hydroxyl radical KW - OH-radical KW - Ectoin KW - UV radiation KW - Sun KW - Salt KW - Radiation therapy PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419332 UR - http://pubs.rsc.org/en/content/articlehtml/2017/cp/c7cp02860a DO - https://doi.org/10.1039/C7CP02860A SN - 1463-9076 VL - 19 IS - 37 SP - 25717 EP - 25722 PB - Royal Society of Chemistry CY - United Kingdom AN - OPUS4-41933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naresh-Kumar, G. A1 - Vilalta-Clemente, A. A1 - Jussila, H. A1 - Winkelmann, Aimo A1 - Nolze, Gert A1 - Vespucci, S. A1 - Nagarajan, S. A1 - Wilkinson, A. J. A1 - Trager-Cowan, C. T1 - Quantitative imaging of anti-phase domains by polarity sensitive orientation mapping using electron backscatter diffraction N2 - Advanced structural characterisation techniques which are rapid to use, non-destructive and structurally definitive on the nanoscale are in demand, especially for a detailed understanding of extended-defects and their influence on the properties of materials. We have applied the electron backscatter diffraction (EBSD) technique in a scanning electron microscope to non-destructively characterise and quantify antiphase domains (APDs) in GaP thin films grown on different (001)Si substrates with different offcuts. We were able to image and quantify APDs by relating the asymmetrical intensity distributions observed in the EBSD patterns acquired experimentally and comparing the same with the dynamical electron diffraction simulations. Additionally mean angular error maps were also plotted using automated cross-correlation based approaches to image APDs. Samples grown on substrates with a 4° offcut from the [110] do not show any APDs, whereas samples grown on the exactly oriented substrates contain APDs. The procedures described in our work can be adopted for characterising a wide range of other material systems possessing non-centrosymmetric point groups. KW - Polarity KW - Semiconductor KW - Antiphase boundary PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-420167 SN - 2045-2322 VL - 7 SP - Article 10916, 1 EP - 10 AN - OPUS4-42016 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neuhaus, Birger A1 - Schmid, Thomas A1 - Riedel, Jens T1 - Collection management and study of microscope slides: Storage, profiling, deterioration, restoration procedures, and general recommendations N2 - A wide range of aspects concerning microscope slides, their preparation, long-time storage, curatorial measures in collections, deterioration, restoration, and study is summarized based on our own data and by analyzing more than 600 references from the 19th century until 2016, 15 patents, and about 100 Materials Safety Data Sheets. Information from systematic zoology, conservation sciences, chemistry, forensic sciences, pathology, paleopathology, applied sciences like food industry, and most recent advances in digital imaging are put together in order to obtain a better understanding of which and possibly why mounting media and coverslip seals deteriorate, how slides can be salvaged, which studies may be necessary to identify a range of ideal mounting media, and how microscope studies can benefit from improvements in developmental biology and related fields. We also elaborate on confusing usage of concepts like that of maceration and of clearing. The chemical ingredients of a range of mounting media and coverslip seals are identified as much as possible from published data, but this information suffers in so far as the composition of a medium is often proprietary of the manufacturer and may vary over time. Advantages, disadvantages, and signs of deterioration are documented extensively for these media both from references and from our own observations. It turns out that many media degrade within a few years, or decades at the latest, except Canada balsam with a documented life-time of 150 years, Euparal with a documented life-time of 50 years, and glycerol-paraffin mounts sealed with Glyceel, which represents almost the only non-deteriorating and easily reversible mount. Deterioration reveals itself as a yellowing in natural resins and as cracking, crystallization, shrinkage on drying or possibly on loss of a plasticizer, detachment of the coverslip, segregation of the ingredients in synthetic polymers, as well as continued maceration of a specimen to a degree that the specimen virtually disappears. Confusingly, decay does not always appear equally within a collection of slides mounted at the same time in the same medium. The reasons for the deteriorative processes have been discussed but are controversial especially for gum-chloral media. Comparing data from conservation sciences, chemical handbooks, and documented ingredients, we discuss here how far chemical and physical deterioration probably are inherent to many media and are caused by the chemical and physical properties of their components and by chemicals dragged along from previous preparation steps like fixation, chemical maceration, and physical clearing. Some recipes even contain a macerating agent, which proceeds with its destructive work. We provide permeability data for oxygen and water vapor of several polymers contained in mounting media and coverslip seals. Calculation of the penetration rate of moisture in one example reveals that water molecules reach a specimen within a few days up to about a month; this lays to rest extensive discussions about the permanent protection of a mounted specimen by a mounting medium and a coverslip seal. Based on the ever growing evidence of the unsuitable composition and application of many, and possibly almost all, mounting media, we strongly encourage changing the perspective on microscope slides from immediate usability and convenience of preparation towards durability and reversibility, concepts taken from conservation sciences. Such a change has already been suggested by Upton (1993) more than 20 years ago for gum-chloral media, but these media are still encouraged nowadays by scientists. Without a new perspective, taxonomic biology will certainly lose a large amount of its specimen basis for its research within the next few decades. Modern non-invasive techniques like Raman spectroscopy may help to identify mounting media and coverslip seals on a given slide as well as to understand ageing of the media. An outlook is given on potential future studies. In order to improve the situation of existing collections of microscope slides, we transfer concepts as per the Smithsonian Collections Standards and Profiling System, developed for insect collections more than 25 years ago, to collections of slides. We describe historical and current properties and usage of glass slides, coverslips, labels, and adhesives under conservational aspects. In addition, we summarize and argue from published and our own experimental information about restorative procedures, including re-hydration of dried-up specimens previously mounted in a fluid medium. Alternatives to microscope slides are considered. We also extract practical suggestions from the literature concerning microscope equipment, cleaning of optical surfaces, health risks of immersion oil, and recent improvements of temporary observation media especially in connection with new developments in digital software. KW - Re-hydration KW - Mounting medium KW - Coverslip seal KW - Fixation KW - Maceration KW - Clearing KW - Immersion oil KW - Permeability PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423322 SN - 978-1-77670-222-0 SN - 978-1-77670-223-7 DO - https://doi.org/10.11646/zootaxa.4322.1.1 SN - 1175-5326 VL - 4322 IS - 1 SP - 1 EP - 173 PB - Magnolia Press CY - Auckland, Neuseeland AN - OPUS4-42332 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pauw, Brian Richard A1 - Smith, A. J. A1 - Snow, T. A1 - Terril, N. J. A1 - Thünemann, Andreas T1 - The modular small-angle X-ray scattering data correction sequence N2 - Data correction is probably the least favourite activity amongst users experimenting with small-angle X-ray scattering: if it is not done sufficiently well, this may become evident only during the data analysis stage, necessitating the repetition of the data corrections from scratch. A recommended comprehensive sequence of elementary data correction steps is presented here to alleviate the difficulties associated with data correction, both in the laboratory and at the synchrotron. When applied in the proposed order to the raw signals, the resulting absolute scattering cross section will provide a high degree of accuracy for a very wide range of samples, with its values accompanied by uncertainty estimates. The method can be applied without modification to any pinhole-collimated instruments with photon-counting direct-detection area detectors. KW - Small-angle X-ray scattering KW - SAXS KW - Accuracy KW - Methodology KW - Data correction PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-432114 DO - https://doi.org/10.1107/S1600576717015096 SN - 1600-5767 VL - 50 IS - 6 SP - 1800 EP - 1811 PB - International Union of Crystallography AN - OPUS4-43211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hernández-Nava, E. A1 - Tammas-Williams, S. A1 - Smith, C. A1 - Léonard, Fabien A1 - Withers, P. J. A1 - Todd, I. A1 - Goodall, R. T1 - X-ray tomography characterisation of lattice structures processed by selective electron beam melting N2 - Metallic lattice structures intentionally contain open porosity; however, they can also contain unwanted closed porosity within the structural members. The entrained porosity and defects within three different geometries of Ti-6Al-4V lattices, fabricated by Selective Electron Beam Melting (SEBM), is assessed from X-ray computed tomography (CT) scans. The results suggest that horizontal struts that are built upon loose powder show particularly high (~20 x 10⁻³ vol %) levels of pores, as do nodes at which many (in our case 24) struts meet. On the other hand, for struts more closely aligned (0° to 54°) to the build direction, the fraction of porosity appears to be much lower (~0.17 x 10⁻³%) arising mainly from pores contained within the original atomised powder particles. KW - Cellular solids KW - Aqdditive manufacturing KW - Computed tomography KW - Titanium alloys PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-413689 UR - http://www.mdpi.com/2075-4701/7/8/300 DO - https://doi.org/10.3390/met7080300 SN - 2075-4701 VL - 7 IS - 8 SP - Article 300, 1 EP - 12 PB - MDPI AN - OPUS4-41368 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Daly, M. A1 - Burnett, T. L. A1 - Pickering, E. J. A1 - Tuck, O. C. G. A1 - Léonard, Fabien A1 - Kelley, R. A1 - Withers, P. J. A1 - Sherry, A. H. T1 - A multi-scale correlative investigation of ductile fracture N2 - The use of novel multi-scale correlative methods, which involve the coordinated characterisation of matter across a range of length scales, are becoming of increasing value to materials scientists. Here, we describe for the first time how a multi-scale correlative approach can be used to investigate the nature of ductile fracture in metals. Specimens of a nuclear pressure vessel steel, SA508 Grade 3, are examined following ductile fracture using medium and high-resolution 3D X-ray computed tomography (CT) analyses, and a site-specific analysis using a dual beam plasma focused ion beam scanning electron microscope (PFIB-SEM). The methods are employed sequentially to characterise damage by void nucleation and growth in one volume of interest, allowing for the imaging of voids that ranged in size from less than 100 nm to over 100 mm. This enables the examination of voids initiated at carbide particles to be detected, as well as the large voids initiated at inclusions. We demonstrate that this multi-scale correlative approach is a powerful tool, which not only enhances our understanding of ductile failure through detailed characterisation of microstructure, but also provides quantitative information about the size, volume fractions and spatial distributions of voids that can be used to inform models of failure. It isfound that the vast majority of large voids nucleated at MnS inclusions, and that the volume of a void varied according to the volume of its initiating inclusion raised to the power 3/2. The most severe voiding was concentrated within 500 mm of the fracture surface, but measurable damage was found to extend to a depth of at least 3 mm. Microvoids associated with carbides (carbide-initiated voids) were found to be concentrated around larger inclusion-initiated voids at depths of at least 400 mm. Methods for quantifying X-ray CT void data are discussed, and a procedure for using this data to calibrate parameters in the Gurson-Tvergaard Needleman (GTN) model for ductile failure is also introduced. KW - Gurson model KW - SA508 KW - Correlative tomography KW - Void nucleation & growth KW - X-ray computed tomography PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-414547 UR - http://www.sciencedirect.com/science/article/pii/S1359645417302203?via%3Dihub DO - https://doi.org/10.1016/j.actamat.2017.03.028 VL - 130 SP - 56 EP - 68 PB - Elsevier AN - OPUS4-41454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pavlovic, Mato A1 - Zoëga, Andreas A1 - Kurz, J. H. A1 - Zanotelli, Christina T1 - Investigations to introduce the probability of detection method for ultrasonic inspection of hollow axles at Deutsche Bahn N2 - The vast experience with the automated, ultrasonic system for the inspection of hollow railway axles used by Deutsche Bahn shows that much smaller flaws are detectable than required. This results in a number of false calls. False calls lead to unnecessary demounting and disassembling of wheelsets, which generates unnecessary additional costs. In order to adjust the sensitivity of the inspection system to reduce the number of false calls without compromising safety, the capability of the system to detect cracks needs to be comprehensively established. This capability can be quantified by using probability of detection (POD) curves for the system. The multi-parameter POD model makes it possible to include several factors that influence the crack detection in the analysis. The analysis presented in this paper shows that crack position, orientation, depth extension, and shape as well as the geometry of the axle all have influence on the ultrasonic response amplitude. For future work, calculation of the POD using multi-parameter POD model with these parameters is planned. T2 - ESIS TC24 Workshop "Integrity of Railway Structures" CY - Leoben, Austria DA - 24.10.2016 KW - Crack KW - Reliability KW - POD KW - Axle KW - Ultrasonic PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-415201 DO - https://doi.org/10.1016/j.prostr.2017.07.002 SN - 2452-3216 VL - 4 SP - 79 EP - 86 PB - Elsevier, B.V. AN - OPUS4-41520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tammas-Williams, S. A1 - Zhao, H. A1 - Léonard, Fabien A1 - Derguti, F. A1 - Todd, I. A1 - Prangnell, P.B. T1 - XCT analysis of the influence of melt strategies on defect population in Ti-6Al-4V components manufactured by Selective Electron Beam Melting N2 - Selective Electron Beam Melting (SEBM) is a promising powder bed Additive Manufacturing technique for near-net-shape manufacture of high-value titanium components. However without post-manufacture HIPing the fatigue life of SEBM parts is currently dominated by the presence of porosity. In this study, the size, volume fraction, and spatial distribution of the pores in model samples have been characterised in 3D, using X-ray Computed Tomography, and correlated to the process variables. The average volume fraction of the pores (b0.2%) was measured to be lower than that usually observed in competing processes, such as selective laser melting, but a strong relationship was found with the differentbeamstrategies used to contour ,and infill by hatching, a part section. The majority of pores were found to be small spherical gas pores, concentrated in the infill hatched region; this was attributed to the lower energy density and less focused beam used in the infill strategy allowing less opportunity for gas bubbles to escape the melt pool. Overall, increasing the energy density or focus of the beam was found to correlate strongly to a reduction in the level of gas porosity. Rarer irregular shaped pores were mostly located in the contour region and have been attributed to a lack of fusion between powder particles. KW - Titanium KW - Additive Manufacture KW - Selective Electron Beam Melting KW - Pores KW - X-ray computed tomography PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-416577 UR - http://www.sciencedirect.com/science/article/pii/S104458031500039X?via%3Dihub DO - https://doi.org/10.1016/j.matchar.2015.02.008 VL - 102 SP - 47 EP - 61 CY - Materials Characterization AN - OPUS4-41657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winkelmann, Aimo A1 - Nolze, Gert A1 - Vespucci, S. A1 - Gunsekar, N.-K. A1 - Trager-Cowan, C. A1 - Vilalta-Clemente, A. A1 - Wilkinson, A. J. A1 - Voss, M. T1 - Diffraction effects and inelastic electron transport in angle-resolved microscopic imaging applications N2 - We analyse the signal formation process for scanning electron microscopic imaging applications on crystalline specimens. In accordance with previous investigations, we find nontrivial effects of incident beam diffraction on the backscattered electron distribution in energy and momentum. Specifically, incident beam diffraction causes angular changes of the backscattered electron distribution which we identify as the dominant mechanism underlying pseudocolour orientation imaging using multiple, angle-resolving detectors. Consequently, diffraction effects of the incident beam and their impact on the subsequent coherent and incoherent electron transport need to be taken into account for an in-depth theoretical modelling of the energy- and momentum distribution of electrons backscattered from crystalline sample regions. Our findings have implications for the level of theoretical detail that can be necessary for the interpretation of complex imaging modalities such as electron channelling contrast imaging (ECCI) of defects in crystals. If the solid angle of detection is limited to specific regions of the backscattered electron momentum distribution, the image contrast that is observed in ECCI and similar applications can be strongly affected by incident beam diffraction and topographic effects from the sample surface. As an application, we demonstrate characteristic changes in the resulting images if different properties of the backscattered electron distribution are used for the analysis of a GaN thin film sample containing dislocations. KW - EBSD KW - Channeling-in KW - Background processing KW - Center of mass KW - Backscattered electrons PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-422063 DO - https://doi.org/10.1111/jmi.12571 SN - 0022-2720 VL - 267 IS - 3 SP - 330 EP - 346 PB - Wiley & Sons, Ltd. AN - OPUS4-42206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tatzel, Michael A1 - von Blanckenburg, F. A1 - Oelze, M. A1 - Bouchez, J. A1 - Hippler, D. T1 - Late Neoproterozoic seawater oxygenation by siliceous sponges N2 - The Cambrian explosion, the rapid appearance of most animal phyla in the geological record, occurred concurrently with bottom seawater oxygenation. Whether this oxygenation Event was triggered through enhanced nutrient supply and organic carbon burial forced by increased continental weathering, or by species engaging in ecosystem engineering, remains a fundamental yet unresolved question. Here we provide evidence for several simultaneous developments that took place over the Ediacaran–Cambrian transition: expansion of siliceous sponges, decrease of the dissolved organic carbon pool, enhanced organic carbon burial, increased phosphorus removal and seawater oxygenation. This evidence is based on Silicon and carbon stable isotopes, Ge/Si ratios, REE-geochemistry and redox-sensitive elements in a chert-shale succession from the Yangtze Platform, China. According to this reconstruction, sponges have initiated seawater oxygenation by redistributing organic carbon oxidation through filtering suspended organic matter from seawater. The resulting increase in dissolved oxygen levels potentially triggered the diversification of eumetazoans. KW - Oxygenation KW - Carbon cycle KW - Silicon stable isotopes PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-422339 DO - https://doi.org/10.1038/s41467-017-00586-5 SN - 2041-1723 VL - 8 SP - Article 621, 1 EP - 10 AN - OPUS4-42233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Auersch, Lutz T1 - Mitigation of railway induced vibration at the track, in the transmission path through the soil and at the building N2 - This contribution presents some principles and some examples of the mitigation of railway-induced ground vibrations. The principles are different for the mitigation measures at the track, in the soil or at the building. Force transfer functions of isolated and un-isolated track-soil systems, reflected and transmitted wave amplitudes at walls and trenches in the soil, and the transfer of the (free-field) vibration amplitudes to the foundation amplitudes of the building are analysed. The mitigation effect can be calculated by exact or simplified formulas. Some examples with 3D (finite-element boundary-element), 2D (beam-on-support), and 1D track models, 2D and 1D soil models, detailed 3D building models and finite or infinite 1D wall-floor models are investigated to find out if simple models can be used for a satisfactory prediction of the mitigation effect. The 1D track examples show that the force transfer of the track without vehicle can be exactly calculated, whereas the total force transfer can be calculated approximately if appropriate wheelset masses per track length are used for the isolated and the un-isolated track. The mitigation effect of a filled trench is calculated by a 2D finite element model and the results compare with simple transmission formula if the stiffness per area rather than the wave impedances are used for the infill material. The base isolation of a building is analysed by a detailed 3D model and the results are similar to the analytic results of a single wall with floors on the soil. Other reduction measures as different floor and column dimensions are usually less effective so that the clearly best mitigation solution at a building is a partly or a complete base isolation. T2 - X INTERNATIONAL CONFERENCE ON STRUCTURAL DYNAMICS (EURODYN 2017) KW - Mitigation KW - Soil-building interaction KW - Base isolation KW - Ground vibration PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-420869 DO - https://doi.org/10.1016/j.proeng.2017.09.192 SN - 1877-7058 VL - 199 SP - 2312 EP - 2317 PB - Elsevier CY - London AN - OPUS4-42086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Auersch, Lutz A1 - Said, Samir A1 - Müller, Roger T1 - Measurements on the vehicle-track interaction and the excitation of railway-induced ground vibration N2 - Two railway measurement campaigns have been performed in Germany and Switzerland which yield insight in the vehicle-track-soil interaction. The campaign in Germany has included simultaneous measurement of vehicle, track, and soil vibrations during train runs with 16, 25, 40, 63, 80, 100, 125, 140, 160 km/h, and impulse measurements of the passenger car, three track sections and the soil. Two ballast tracks, one on the soil surface and one on a concrete bridge, have been investigated as well as a slab track in a tunnel. Ten different sites in Switzerland have been measured for soil properties and train-induced ground vibrations, which allow to determine the excitation forces of the railway traffic. New axle-box measurements at some of the Swiss sites have been analysed to get further experimental evidence. All these measurements have been evaluated to characterize the excitation processes. Relations between vehicle vibration and ground vibration can be observed. The vehicle vibrations, namely the accelerations of the wheelsets, yield the dynamic forces due to the passage over the irregularities of the vehicle and the track. The ground vibrations are correlated to these dynamic forces to a certain extent. Some mid-frequency ground vibration amplitudes, however, are higher than expected from the dynamic excitation forces. The experimental observations can be explained by an irregular response to the passage of the static loads, that means the passage of the static loads over an irregular ballast or soil. This correct understanding of the excitation processes is important for the prediction as well as for the mitigation of railway induced ground vibrations. T2 - X INTERNATIONAL CONFERENCE ON STRUCTURAL DYNAMICS (EURODYN 2017) KW - Vehicle-track interaction KW - Ground vibration KW - Track vibration KW - Railway measurement campaign KW - Axle box measurements PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-420889 DO - https://doi.org/10.1016/j.proeng.2017.09.390 SN - 1877-7058 VL - 199 SP - 2615 EP - 2620 PB - Elsevier CY - London AN - OPUS4-42088 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rudenko, A. A1 - Colombier, J.-P. A1 - Höhm, S. A1 - Rosenfeld, A. A1 - Krüger, Jörg A1 - Bonse, Jörn A1 - Itina, T.E. T1 - Spontaneous periodic ordering on the surface and in the bulk of dielectrics irradiated by ultrafast laser: a shared electromagnetic origin N2 - Periodic self-organization of matter beyond the diffraction limit is a puzzling phenomenon, typical both for surface and bulk ultrashort laser processing. Here we compare the mechanisms of periodic nanostructure formation on the surface and in the bulk of fused silica. We show that volume nanogratings and surface nanoripples having subwavelength periodicity and oriented perpendicular to the laser polarization share the same electromagnetic origin. The nanostructure orientation is defined by the near-field local enhancement in the vicinity of the inhomogeneous scattering centers. The periodicity is attributed to the coherent superposition of the waves scattered at inhomogeneities. Numerical calculations also support the multipulse accumulation nature of nanogratings formation on the surface and inside fused silica. Laser surface processing by multiple laser pulses promotes the transition from the high spatial frequency perpendicularly oriented nanoripples to the low spatial frequency ripples, parallel or perpendicular to the laser polarization. The latter structures also share the electromagnetic origin, but are related to the incident field interference with the scattered far-field of rough non-metallic or transiently metallic surfaces. The characteristic ripple appearances are predicted by combined electromagnetic and thermo-mechanical approaches and supported by SEM images of the final surface morphology and by time-resolved pump-probe diffraction measurements. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser KW - Nanostructures KW - Dielectrics KW - Electromagnetic scattering PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-421747 UR - https://www.nature.com/articles/s41598-017-12502-4 DO - https://doi.org/10.1038/s41598-017-12502-4 SN - 2045-2322 VL - 7 SP - Article 12306, 1 EP - 14 PB - Springer Nature AN - OPUS4-42174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Beier, T. A1 - Tchoffo Ngoula, D. T1 - Approximation of the crack driving force for cracks at notches under static and cyclic loading N2 - The work deals with the efficient calculation of the elastic-plastic crack driving force (J-integral for monotonic loading andΔJ-integral under cyclic loading) for short cracks at notches as essential parameter for the reliable static and fatigue assessment of notched structures. The J- or ΔJ-integral is calculated based on analytical solutions for stress intensity factors, estimated by means of well-known weight function solutions in the case of cracks under power-law stress distributions. A plasticity-correction function is applied to the stress intensity factors to obtain the final expression of the crack driving force. The comparison between analytical solutions and finite element calculations in case of cracks at the weld toe in welded joints shows good agreement. T2 - 2nd International Conference on Structural Integrity CY - Funchal, Madeira, Portugal DA - 04.09.2017 KW - Structural integrity KW - Fracture mechanics KW - Crack driving force KW - Notches PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425577 DO - https://doi.org/10.1016/j.prostr.2017.07.111 SN - 2452-3216 VL - 5 SP - 875 EP - 882 PB - Elsevier B.V. AN - OPUS4-42557 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Haferkamp, Sebastian A1 - Fischer, Franziska A1 - Kraus, Werner A1 - Emmerling, Franziska T1 - Mechanochemical Knoevenagel condensation investigated in situ N2 - The mechanochemical Knoevenagel condensation of malononitrile with p-nitrobenzaldehyde was studied in situ using a tandem approach. X-ray diffraction and Raman spectroscopy were combined to yield time-resolved information on the milling process. Under solvent-free conditions, the reaction leads to a quantitative conversion to p-nitrobenzylidenemalononitrile within 50 minutes. The in situ data indicate that the process is fast and proceeds under a direct conversion. After stopping the milling process, the reaction continues until complete conversion. The continuous and the stopped milling process both result in crystalline products suitable for single crystal X-ray diffraction. KW - Mechanochemistry KW - Ball milling KW - C–C coupling KW - In situ KW - Knoevenagel condensation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425388 DO - https://doi.org/10.3762/bjoc.13.197 VL - 13 SP - 2010 EP - 2014 PB - Beilstein-Institut AN - OPUS4-42538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiedensohler, A. A1 - Wiesner, A. A1 - Weinhold, K. A1 - Birmili, W. A1 - Herrmann, M. A1 - Merkel, M. A1 - Müller, T. A1 - Pfeifer, S. A1 - Schmidt, A. A1 - Tuch, T. A1 - Velarde, F. A1 - Quincey, P. A1 - Seeger, Stefan A1 - Nowak, A. T1 - Mobility particle size spectrometers: Calibration procedures and measurement uncertainties N2 - Mobility particle size spectrometers (MPSS) belong to the essential instruments in aerosol science that determine the particle number size distribution (PNSD)in the submicrometer size range. Following calibration procedures and target uncertainties against standards and reference instruments are suggested for a complete MPSS quality assurance program: a) calibration of the CPC counting efficiency curve (within 5% for the plateau counting efficiency; within 1 nm for the 50% detection efficiency diameter), b) sizing calibration of the MPSS, using a certified polystyrene latex (PSL) particle size standard at 203 nm (within 3%), c) intercomparison of the PNSD of the MPSS (within 10% and 20% of the dN/dlogDP concentration for the particle size range 20 – 200 nm and 200 to 800 nm, respectively), and d) intercomparison of the integral PNC of the MPSS (within 10%). Furthermore, following measurement uncertainties have been investigated: a) PSL particle size standards in the range from 100-500nm match within 1% after sizing calibration at 203 nm. b) Bipolar diffusion chargers based on the radioactive nuclides Kr85, Am241 and Ni63 and a new ionizer based on corona discharge follow the recommended bipolar charge distribution, while soft X-ray-based charges may alter faster than expected. c) The use of a positive high voltage supply show a 10% better performance than a negative one. d) The intercomparison of the integral PNC of an MPSS against the total number concentration is still within the target uncertainty at an ambient pressure of approximately 500 hPa. KW - Measurement uncertainties KW - Mobility particle size spectrometer (MPPS) KW - Condensation particle counter (CPC) KW - Calibration PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425060 DO - https://doi.org/10.1080/02786826.2017.1387229 SN - 1521-7388 VL - 52 IS - 2 SP - 146 EP - 164 PB - Tailor & Francis CY - USA AN - OPUS4-42506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stengel, Dominik A1 - Thiele, K. T1 - Measurements of downburst wind loading acting on an overhead transmission line in Northern Germany N2 - Along an overhead transmission line in Northern Germany, a unique instrumentation of anemometers and force measurements is installed. Details of this test line with wind measurements along a horizontal axis are given. A recent event of a presumable downburst wind event is analyzed by means of available data and precedent works on thunderstorm analysis. The measured response of the conductors at the suspension tower is investigated and compared with time domain simulation of a finite element model. T2 - X International Conference on Structural Dynamics, EURODYN 2017 CY - Rome, Italy DA - 10.09.2017 KW - Non-synoptic wind event KW - Downburst KW - Overhead transmission line KW - Finite element method PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-421239 DO - https://doi.org/10.1016/j.proeng.2017.09.578 SN - 1877-7058 VL - 199 IS - Supplement C SP - 3152 EP - 3157 PB - Elsevier AN - OPUS4-42123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Le, Quynh Hoa A1 - Vestergaard, M.C. A1 - Tamiya, E T1 - Carbon-based nanomaterials in biomass-based fuel-fed fuel cells N2 - Environmental and sustainable economical concerns are generating a growing interest in biofuels predominantly produced from biomass. It would be ideal if an energy conversion device could directly extract energy from a sustainable energy resource such as biomass. Unfortunately, up to now, such a direct conversion device produces insufficient power to meet the demand of practical applications. To realize the future of biofuel-fed fuel cells as a green energy conversion device, efforts have been devoted to the development of carbon-based nanomaterials with tunable electronic and surface characteristics to act as efficient metal-free electrocatalysts and/or as supporting matrix for metal-based electrocatalysts. We present here a mini review on the recent advances in carbon-based catalysts for each type of biofuel-fed/biofuel cells that directly/indirectly extract energy from biomass resources, and discuss the challenges and perspectives in this developing field KW - Carbon-based nanomaterials KW - Biofuel cells KW - Biomass KW - Carbon nanotubes KW - Graphene KW - Carbon nanodots PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428226 UR - http://www.mdpi.com/1424-8220/17/11/2587/htm DO - https://doi.org/10.3390/s17112587 SN - 1424-8220 VL - 17 IS - 11 SP - 2587, 1 EP - 2587, 21 PB - MDPI AG CY - Basel, Switzerland AN - OPUS4-42822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heitz, J. A1 - Plamadeala, C. A1 - Muck, M. A1 - Armbruster, O. A1 - Baumgartner, W. A1 - Weth, A. A1 - Steinwender, C. A1 - Plessberger, H. A1 - Kellermair, J. A1 - Kirner, Sabrina V. A1 - Krüger, Jörg A1 - Bonse, Jörn A1 - Guntner, A. S. A1 - Hassel, A. W. T1 - Femtosecond laser-induced microstructures on Ti substrates for reduced cell adhesion N2 - Miniaturized pacemakers with a surface consisting of a Ti alloy may have to be removed after several years from their implantation site in the heart and shall, therefore, not be completely overgrown by cells or tissue. A method to avoid this may be to create at the surface by laser-ablation self-organized sharp conical spikes, which provide too little surface for cells (i.e., fibroblasts) to grow on. For this purpose, Ti-alloy substrates were irradiated in the air by 790 nm Ti:sapphire femtosecond laser pulses at fluences above the ablation threshold. The laser irradiation resulted in pronounced microstructure formation with hierarchical surface morphologies. Murine fibroblasts were seeded onto the laser-patterned surface and the coverage by cells was evaluated after 3–21 days of cultivation by means of scanning electron microscopy. Compared to flat surfaces, the cell density on the microstructures was significantly lower, the coverage was incomplete, and the cells had a clearly different morphology. The best results regarding suppression of cell growth were obtained on spike structures which were additionally electrochemically oxidized under acidic conditions. Cell cultivation with additional shear stress could reduce further the number of adherent cells. KW - Laser Processing KW - Femtosecond laser KW - Titanium alloy KW - Cell adhesion KW - Anodic oxidation KW - Pacemaker PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-427681 UR - https://link.springer.com/article/10.1007/s00339-017-1352-0 DO - https://doi.org/10.1007/s00339-017-1352-0 SN - 0947-8396 SN - 1432-0630 VL - 123 IS - 12 SP - 734, 1 EP - 9 PB - Springer-Verlag CY - Berlin AN - OPUS4-42768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröter, Maria-Astrid A1 - Meyer, Susann A1 - Hahn, Marc Benjamin A1 - Solomun, Tihomir A1 - Sturm, Heinz A1 - Kunte, Hans-Jörg T1 - Ectoine protects DNA from damage by ionizing radiation N2 - Ectoine plays an important role in protecting biomolecules and entire cells against environmental stressors such as salinity, freezing, drying and high temperatures. Recent studies revealed that ectoine also provides effective protection for human skin cells from damage caused by UV-A radiation. These protective properties make ectoine a valuable compound and it is applied as an active ingredient in numerous pharmaceutical devices and cosmetics. Interestingly, the underlying mechanism resulting in protecting cells from radiation is not yet fully understood. Here we present a study on ectoine and its protective influence on DNA during electron irradiation. Applying gel electrophoresis and atomic force microscopy, we demonstrate for the first time that ectoine prevents DNA strand breaks caused by ionizing electron radiation. The results presented here point to future applications of ectoine for instance in cancer radiation therapy. KW - Plasmid DNA pUC19 KW - Electron irradiation 30 [kV] KW - Effective irradiation dose 0.2-16 [Gy] KW - Gel electrophoresis KW - AFM intermittent contact KW - Radioprotector ectoine KW - Compatible solute PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428287 DO - https://doi.org/10.1038/s41598-017-15512-4 SN - 2045-2322 VL - 7 IS - 1 SP - 15272, 1 EP - 15272, 7 PB - Nature AN - OPUS4-42828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Łojewska, J. A1 - Rabin, Ira A1 - Pawcenis, D. A1 - Bagniuk, J. A1 - Aksamit-Koperska, M.-A. A1 - Sitarz, M. A1 - Missori, M. A1 - Krutzsch, M. T1 - Recognizing ancient papyri by a combination of spectroscopic, diffractional and chromatographic analytical tools N2 - Ancient papyri are a written heritage of culture that flourished more than 3000 years ago in Egypt. One of the most significant collections in the world is housed in the Egyptian Museum and Papyrus Collection in Berlin, from where the samples for our investigation come. The papyrologists, curators and conservators of such collections search intensely for the analytical detail that would allow ancient papyri to be distinguished from modern fabrications, in order to detect possible forgeries, assess papyrus deterioration state, and improve the design of storage conditions and conservation methods. This has become the aim of our investigation. The samples were studied by a number of methods, including spectroscopic (FTIR, fluorescent-FS, Raman) diffractional (XRD) and chromatographic (size exclusion chromatography-SEC), selected in order to determine degradation parameters: overall oxidation of lignocellulosic material, degree of polymerization and crystallinity of cellulose. The results were correlated with those obtained from carefully selected model samples including modern papyri and paper of different composition aged at elevated temperature in humid air. The methods were classified in the order SEC > FS > FTIR > XRD, based on their effectiveness in discriminating the state of papyri degradation. However, the most trustworthy evaluation of the age of papyri samples should rely on several methods. KW - Archaeometry KW - FTIR KW - XRD KW - Raman KW - Chromatography KW - Papyrology PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-428704 DO - https://doi.org/10.1038/srep46236 SN - 2045-2322 VL - 7 SP - 46236, 1 EP - 46236, 12 AN - OPUS4-42870 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bender, P A1 - Balceris, C. A1 - Ludwig, F A1 - Posth, O A1 - Bogart, L. K. A1 - Szczerba, Wojciech A1 - Castro, A A1 - Nilsson, L A1 - Costo, R A1 - Gavilan, H A1 - Gonzalez-Alonso, D A1 - de Pedro, I A1 - Barquin, L. F. A1 - Johansson, C T1 - Distribution functions of magnetic nanoparticles determined by a numerical inversion method N2 - In the present study, we applied a regularized inversion method to extract the particle size, magnetic moment and relaxation-time distribution of magnetic nanoparticles from small-angle x-ray scattering (SAXS), DC magnetization (DCM) and AC susceptibility (ACS) measurements. For the measurements the particles were colloidally dispersed in water. At first approximation the particles could be assumed to be spherically shaped and homogeneously magnetized single-domain particles. As model functions for the inversion, we used the particle form factor of a sphere (SAXS), the Langevin function (DCM) and the Debye model (ACS). The extracted distributions exhibited features/peaks that could be distinctly attributed to the individually dispersed and non-interacting nanoparticles. Further analysis of these peaks enabled, in combination with a prior characterization of the particle ensemble by electron microscopy and dynamic light scattering, a detailed structural and magnetic characterization of the particles. Additionally, all three extracted distributions featured peaks, which indicated deviations of the scattering (SAXS), magnetization (DCM) or relaxation (ACS) behavior from the one expected for individually dispersed, homogeneously magnetized nanoparticles. These deviations could be mainly attributed to partial agglomeration (SAXS, DCM, ACS), uncorrelated surface spins (DCM) and/or intra-well relaxation processes (ACS). The main advantage of the numerical inversion method is that no ad hoc assumptions regarding the line shape of the extracted distribution functions are required, which enabled the detection of these contributions. We highlighted this by comparing the results with the results obtained by standard model fits, where the functional form of the distributions was a priori assumed to be log-normal shaped. KW - SAXS KW - Small-angle X-ray scattering KW - Nanoparticle PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-429373 DO - https://doi.org/10.1088/1367-2630/aa73b4 SN - 1367-2630 VL - 19 SP - 073012, 1 EP - 073012, 19 PB - IOP Publ. Ltd. AN - OPUS4-42937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Trimpert, J. A1 - Groenke, N. A1 - Jenckel, M. A1 - He, Shulin A1 - Kunec, D. A1 - Szpara, M.L. A1 - Spatz, S.J. A1 - Osterrieder, N. A1 - McMahon, Dino Peter T1 - A phylogenomic analysis of Marek's disease virus (MDV) reveals independent paths to virulence in Eurasia and North America N2 - Virulence determines the impact a pathogen has on the fitness of its host, yet current understanding of the evolutionary origins and causes of virulence of many pathogens is surprisingly incomplete. Here, we explore the evolution of Marek’s disease virus (MDV), a herpesvirus commonly afflicting chickens and rarely other avian species. The history of MDV in the 20th century represents an important case study in the evolution of virulence. The severity of MDV infection in chickens has been rising steadily since the adoption of intensive farming techniques and vaccination programs in the 1950s and 1970s, respectively. It has remained uncertain, however, which of these factors is causally more responsible for the observed increase in virulence of circulating viruses. We conducted a phylogenomic study to understand the evolution of MDV in the context of dramatic changes to poultry farming and disease control. Our analysis reveals evidence of geographical structuring of MDV strains, with reconstructions supporting the emergence of virulent viruses independently in North America and Eurasia. Of note, the emergence of virulent viruses appears to coincide approximately with the introduction of comprehensive vaccination on both continents. The time-dated phylogeny also indicated that MDV has a mean evolutionary rate of ~1.6 × 10−5 substitutions per site per year. An examination of gene-linked mutations did not identify a strong association between mutational variation and virulence phenotypes, indicating that MDV may evolve readily and rapidly under strong selective pressures and that multiple genotypic pathways may underlie virulence adaptation in MDV. KW - Sesistance KW - Disease KW - Emergence KW - Evolution KW - Virulence PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-429054 DO - https://doi.org/10.1111/eva.12515 SN - 1752-4571 VL - 10 IS - 10 SP - 1091 EP - 1101 PB - John Wiley & Sons Ltd. AN - OPUS4-42905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Abbas, Ioana M. A1 - Schwaar, Timm A1 - Bienwald, Frank A1 - Weller, Michael G. T1 - Predictable Peptide Conjugation Ratios by Activation of Proteins with Succinimidyl Iodoacetate (SIA) N2 - The small heterobifunctional linker succinimidyl iodoacetate (SIA) was examined for the preparation of peptide–protein bioconjugates with predicable conjugation ratios. For many conjugation protocols, the protein is either treated with a reductant to cleave disulfide bonds or is reacted with thiolation chemicals, such as Traut’s reagent. Both approaches are difficult to control, need individual optimization and often lead to unsatisfactory results. In another popular approach, a heterobifunctional linker with a N-hydroxysuccinimide (NHS) and a maleimide functionality is applied to the protein. After the activation of some lysine ε-amino groups with the NHS ester functionality, a cysteine-containing peptide is attached to the activated carrier protein via maleimide. Particularly, the maleimide reaction leads to some unwanted byproducts or even cleavage of the linker. Many protocols end up with conjugates with unpredictable and irreproducible conjugation ratios. In addition, the maleimide-thiol addition product should be assumed immunogenic in vivo. To avoid these and other disadvantages of the maleimide approach, we examined the known linker succinimidyl iodoacetate (SIA) in more detail and developed two protocols, which lead to peptide–protein conjugates with predefined average conjugation ratios. This holds potential to eliminate tedious and expensive optimization steps for the synthesis of a bioconjugate of optimal composition. KW - Bioconjugate KW - Carrier protein KW - Immunogen KW - Hapten KW - Linker KW - Antibody drug conjugate KW - ADC KW - Drug-to-antibody ratio KW - DAR KW - Conjugation ratio KW - Conjugation density KW - Carrier load KW - Click reaction KW - Click chemistry PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-427188 UR - http://www.mdpi.com/2409-9279/1/1/2 DO - https://doi.org/10.3390/mps1010002 SN - 2409-9279 VL - 1 SP - 1 EP - 14 PB - MDPI CY - Basel, Schweiz AN - OPUS4-42718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schadow, Florian A1 - Brackrock, Daniel A1 - Gaal, Mate A1 - Heckel, Thomas T1 - Ultrasonic inspection and data analysis of glass- and carbon-fibre-reinforced plastics N2 - Non-destructive testing (NDT) helps to find material defects without having an influence on the material itself. It is applied as a method of quality control, for online structural health monitoring, and for inspection of safety related components. Due to the ability of automation and a simple test setup ultrasonic testing is one major NDT technique next to several existing options. Whereas contact technique allows the use of higher frequencies of some MHz and phased array focusing, air-coupled ultrasonic testing (ACUT) shows different advantages. Most significant for ACUT is the absence of any coupling fluid and an economical test procedure respective time and costs. Both contact technique and ACUT have been improved and enhanced during the past years. One important enhancement is the development of airborne transducers based on ferroelectrets, like charged cellular polypropylene (cpp), which makes the application of any matching layers being mandatory in conventional piezoelectric transducers unnecessary. In this contribution we show ultrasonic inspection results of specimens made of carbon- and glass-fibre-reinforced plastic. These specimens include defects represented by drill holes and artificial delaminations of various size and depth. We compare inspection results achieved by using contact technique to those achieved by ACUT. For ACUT, conventional piezoelectric transducers and transducers based on cpp were used, both focused as well as non-focused types. Contact inspections were performed with a multi-channel matrix array probe. Once the inspection data is recorded it can be analysed in order to detect and evaluate defects in the specimen. We present different analysing strategies and compare these regarding detection rate and sizing of defects. T2 - 3rd International Symposium on Fatigue Design and Material Defects, FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Ultrasonic testing KW - Air-coupled KW - Carbon-fibre-reinforced plastic KW - Glass-fibre-reinforced KW - Material inspection KW - Defect sizing PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-434802 DO - https://doi.org/10.1016/j.prostr.2017.11.092 SN - 2452-3216 VL - 7 SP - 299 EP - 306 PB - Elsevier B.V. AN - OPUS4-43480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Rivard, C. A1 - Wilken, V. A1 - Muskolus, A. A1 - Adam, Christian T1 - Performance of secondary P-fertilizers in pot experiments analyzed by phosphorus X-ray absorption near-edge structure (XANES) spectroscopy N2 - A pot experiment was carried out with maize to determine the phosphorus (P) plant-availability of different secondary P-fertilizers derived from wastewater. We analyzed the respective soils by P K-edge X-ray absorption near-edge structure (XANES) spectroscopy to determine the P chemical forms that were present and determine the transformation processes. Macro- and micro-XANES spectroscopy were used to determine the chemical state of the overall soil P and identify P compounds in P-rich spots. Mainly organic P and/or P adsorbed on organic matter or other substrates were detected in unfertilized and fertilized soils. In addition, there were indications for the formation of ammonium phosphates in some fertilized soils. However, this effect was not seen in the maize yield of all P-fertilizers. The observed reactions between phosphate from secondary P-fertilizers and cofertilized nitrogen compounds should be further investigated. Formation of highly plant-available compounds such as ammonium phosphates could make secondary P-fertilizers more competitive to commercial phosphate rock-based fertilizers with positive effects on resources conservation. KW - Phosphorus KW - Pot experiments KW - Secondary P-fertilizer KW - Sewage sludge ash KW - Soil KW - X-ray absorption near-edge structure (XANES) spectroscopy PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-433782 DO - https://doi.org/10.1007/s13280-017-0973-z SN - 0044-7447 VL - 47 IS - 1 SP - 62 EP - 72 PB - Springer AN - OPUS4-43378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laquai, René A1 - Müller, Bernd R. A1 - Kasperovich, G. A1 - Haubrich, J. A1 - Requena, G. A1 - Bruno, Giovanni T1 - X-ray refraction distinguishes unprocessed powder from empty pores in selective laser melting Ti-6Al-4V N2 - For the first time, X-ray refraction techniques are proven for the identification of void formation in Ti-6Al-4V parts produced by selective laser melting. The topology and volume fraction of pores are measured in samples produced with different laser energy density. Unique X-ray refraction methods identify different kinds of defects, characteristic to the regions below and above the Optimum laser energy density, namely unprocessed powder (unmolten powder particles, balling effect, and Fusion defects) from empty keyhole pores. Furthermore, it is possible to detect small inhomogeneities (voids or cracks) with sizes below the spatial resolution of optical microscopy and X-ray computed tomography. KW - Additive manufacturing KW - X-ray refraction KW - Microscopy KW - X-ray computed tomography KW - Porosity PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-434041 DO - https://doi.org/10.1080/21663831.2017.1409288 SN - 2166-3831 VL - 6 IS - 2 SP - 130 EP - 135 PB - Taylor & Francis Group CY - London, UK AN - OPUS4-43404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernevic, Bogdan A1 - El-Khatib, Ahmed H. A1 - Jakubowski, Norbert A1 - Weller, Michael G. T1 - Online immunocapture ICP‑MS for the determination of the metalloprotein ceruloplasmin in human serum N2 - The human copper-protein ceruloplasmin (Cp) is the major copper-containing protein in the human body. The accurate determination of Cp is mandatory for the reliable diagnosis of several diseases. However, the analysis of Cp has proven to be difficult. The aim of our work was a proof of concept for the determination of a metalloprotein-based on online immunocapture ICP-MS. The immuno-affinity step is responsible for the enrichment and isolation of the analyte from serum, whereas the compound-independent quantitation with ICP-MS delivers the sensitivity, precision, and large dynamic range. Off-line ELISA (enzyme-linked immunosorbent assay) was used in parallel to confirm the elution profile of the analyte with a structure-selective method. The total protein elution was observed with the 32S mass trace. The ICP-MS signals were normalized on a 59Co signal. The human copper-protein Cp could be selectively determined. This was shown with pure Cp and with a sample of human serum. The good correlation with off-line ELISA shows that Cp could be captured and eluted selectively from the anti-Cp affinity column and subsequently determined by the copper signal of ICP-MS. KW - ELISA KW - Affinity chromatography KW - Affinity extraction KW - IgY KW - Chicken antibodies KW - Immunoaffinity extraction KW - Copper KW - Diagnostics PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-446157 UR - https://bmcresnotes.biomedcentral.com/articles/10.1186/s13104-018-3324-7 UR - https://static-content.springer.com/esm/art%3A10.1186%2Fs13104-018-3324-7/MediaObjects/13104_2018_3324_MOESM1_ESM.pdf UR - https://static-content.springer.com/esm/art%3A10.1186%2Fs13104-018-3324-7/MediaObjects/13104_2018_3324_MOESM2_ESM.pdf DO - https://doi.org/10.1186/s13104-018-3324-7 SN - 1756-0500 VL - 11 IS - 1 SP - Article 213, 1 EP - 5 PB - Springer Nature CY - Heidelberg AN - OPUS4-44615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Trajkovski, B. A1 - Jaunich, Matthias A1 - Müller, W. A1 - Beuer, F. A1 - Zafiropoulos, G. A1 - Houshmand, A. ED - Eppel, S.J. T1 - Hydrophilicity, viscoelastic, and physicochemical properties variations in dental bone grafting substitutes N2 - The indication-oriented Dental Bone Graft Substitutes (DBGS) selection, the correct bone defects classification, and appropriate treatment planning are very crucial for obtaining successful clinical results. However, hydrophilic, viscoelastic, and physicochemical properties’ influence on the DBGS regenerative potential has poorly been studied. For that reason, we investigated the dimensional changes and molecular mobility by Dynamic Mechanical Analysis (DMA) of xenograft (cerabone®), synthetic (maxresorb®), and allograft (maxgraft®, Puros®) blocks in a wet and dry state. While no significant differences could be seen in dry state, cerabone® and maxresorb® blocks showed a slight height decrease in wet state, whereas both maxgraft® and Puros® had an almost identical height increase. In addition, cerabone® and maxresorb® blocks remained highly rigid and their damping behaviour was not influenced by the water. On the other hand, both maxgraft® and Puros® had a strong increase in their molecular mobility with different damping behaviour profiles during the wet state. A high-speed microscopical imaging system was used to analyze the hydrophilicity in several naturally derived (cerabone®, Bio-Oss®, NuOss®, SIC® nature graft) and synthetic DBGS granules (maxresorb®, BoneCeramic®, NanoBone®, Ceros®). The highest level of hydrophilicity was detected in cerabone® and maxresorb®, while Bio-Oss® and BoneCeramic® had the lowest level of hydrophilicity among both naturally derived and synthetic DBGS groups. Deviations among the DBGS were also addressed via physicochemical differences recorded by Micro Computed Tomography, Scanning Electron Microscopy, Fourier Transform Infrared Spectroscopy, X-ray powder Diffractometry, and Thermogravimetric Analysis. Such DBGS variations could influence the volume stability at the grafting site, handling as well as the speed of vascularization and bone regeneration. Therefore, this study initiates a new insight into the DBGS differences and their importance for successful clinical results. KW - Biomaterials KW - Bone grafting KW - Bone substitutes KW - Hydrophilicity KW - Mechanical analysis PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-439890 DO - https://doi.org/10.3390/ma11020215 SN - 1996-1944 VL - 11 IS - 2 SP - Article 215, 1 EP - 19 PB - MDPI AG CY - Basel, Switzerland AN - OPUS4-43989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stajanca, Pavol A1 - Topolniak, Ievgeniia A1 - Pötschke, Samuel A1 - Krebber, Katerina T1 - Solution-mediated cladding doping of commercial polymer optical fibers N2 - Solution doping of commercial polymethyl methacrylate (PMMA) polymer optical fibers (POFs) is presented as a novel approach for preparation of custom cladding-doped POFs (CD-POFs). The presented method is based on a solution-mediated diffusion of dopant molecules into the fiber cladding upon soaking of POFs in a methanol-dopant solution. The method was tested on three different commercial POFs using Rhodamine B as a fluorescent dopant. The dynamics of the diffusion process was studied in order to optimize the doping procedure in terms of selection of the most suitable POF, doping time and conditions. Using the optimized procedure, longer segment of fluorescent CD-POF was prepared and its performance was characterized. Fiber’s potential for sensing and illumination applications was demonstrated and discussed. The proposed method represents a simple and cheap way for fabrication of custom, short to medium length CD-POFs with various dopants. KW - Polymer optical fiber KW - Solution doping KW - Polymethyl methacrylate KW - Rhodamine B KW - Dye-doped fiber KW - Fluorescent optical fiber PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-441045 DO - https://doi.org/10.1016/j.yofte.2018.02.008 SN - 1068-5200 SN - 1095-9912 VL - 41 SP - 227 EP - 234 PB - Elsevier Inc. AN - OPUS4-44104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Laux, P. A1 - Tentschert, J. A1 - Riebeling, Ch. A1 - Braeuning, A. A1 - Creutzenberg, O. A1 - Epp, A. A1 - Fessard, V. A1 - Haas, K.-H. A1 - Haase, A. A1 - Hund-Rinke, K. A1 - Jakubowski, Norbert A1 - Kearns, P. A1 - Lampen, A. A1 - Rauscher, H. A1 - Schoonjans, R. A1 - Störmer, A. A1 - Thielmann, A. A1 - Mühle, U. A1 - Luch, A. T1 - Nanomaterials: certain aspects of application, risk assessment and risk communication N2 - Development and market introduction of new nanomaterials trigger the need for an adequate risk assessment of such products alongside suitable risk communication measures. Current application of classical and new nanomaterials is analyzed in context of regulatory requirements and standardization for chemicals, food and consumer products. The challenges of nanomaterial characterization as the main bottleneck of risk assessment and regulation are presented. In some areas, e.g., quantification of nanomaterials within complex matrices, the establishment and adaptation of analytical techniques such as laser ablation inductively coupled plasma mass spectrometry and others are potentially suited to meet the requirements. As an example, we here provide an approach for the reliable characterization of human exposure to nanomaterials resulting from food packaging. Furthermore, results of nanomaterial toxicity and ecotoxicity testing are discussed, with concluding key criteria such as solubility and fiber rigidity as important parameters to be considered in material development and regulation. Although an analysis of the public opinion has revealed a distinguished rating depending on the particular field of application, a rather positive perception of nanotechnology could be ascertained for the German public in general. An improvement of material characterization in both toxicological testing as well as end-product control was concluded as being the main obstacle to ensure not only safe use of materials, but also wide acceptance of this and any novel technology in the general public. KW - Nanomaterials KW - Toxicity KW - Ecotoxicity KW - Standardization KW - Exposure PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-441096 DO - https://doi.org/10.1007/s00204-017-2144-1 VL - 92 IS - 1 SP - 121 EP - 141 PB - Springer AN - OPUS4-44109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meyer, S. A1 - López-Serrano, Ana A1 - Mitze, H. A1 - Jakubowski, Norbert A1 - Schwerdtle, T. T1 - Single-cell analysis by ICP-MS/MS as a fast tool for cellular bioavailability studies of arsenite N2 - Single-cell inductively coupled plasma mass spectrometry (SC-ICP-MS) has become a powerful and fast tool to evaluate the elemental composition at a single-cell level. In this study, the cellular bioavailability of arsenite (incubation of 25 and 50 μM for 0-48 h) has been successfully assessed by SC-ICP-MS/MS for the first time directly after re-suspending the cells in water. This procedure avoids the normally arising cell membrane permeabilization caused by cell fixation methods (e.g. methanol fixation). The reliability and feasibility of this SC-ICP-MS/MS approach with a limit of detection of 0.35 fg per cell was validated by conventional bulk ICP-MS/MS analysis after cell digestion and parallel measurement of sulfur and phosphorus. KW - Single-cell analysis KW - ICP-MS/MS KW - Arsenite PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-441105 DO - https://doi.org/10.1039/c7mt00285h SN - 1756-5901 VL - 10 IS - 1 SP - 73 EP - 76 PB - RSC Publ. CY - Cambridge AN - OPUS4-44110 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kapa, Thomas A1 - Schreier, Andy A1 - Krebber, Katerina T1 - 63 km BOFDA for temperature and strain monitoring N2 - We demonstrate (and are the first to do so) 63 km Brillouin Optical Frequency-Domain Analysis (BOFDA) for temperature and strain monitoring using a 100 km fiber loop. The use of BOFDA for long-range applications can be considered a novel approach, as previous investigations focused on the utilization of Brillouin Optical Time-Domain Reflectometry and Analysis (BOTDR and BOTDA, respectively). At 51.7 km, a 100 m hotspot (37 °C) was detected without using distributed Raman amplification or image processing. KW - Distributed sensing KW - Stimulated Brillouin scattering KW - Fiber optics sensors PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449679 DO - https://doi.org/10.3390/s18051600 SN - 1424-8220 VL - 18 IS - 5 SP - 1600, 1 EP - 9 PB - MDPI CY - Basel, Switzerland AN - OPUS4-44967 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Swaraj, S. A1 - Sparnacci, K. A1 - Unger, Wolfgang T1 - Shell thickness determination for PTFE‐PS core‐shell nanoparticles using scanning transmission X‐ray microscopy (STXM) N2 - A scanning transmission X‐ray microscopy (STXM)‐based methodology is introduced for determining the dimensions (shell thickness, core and total diameter) of core‐shell nanoparticles, which exhibit a strong X‐ray absorption contrast and a well‐defined interface between core and shell material. A low radiation dosage during data acquisition and, therefore, less X‐ray beam‐induced damage of the sample is achieved by recording STXM images only at 2 predetermined energies of maximum Absorption contrast, instead of recording a stack of images across the whole absorption edge. A model core‐shell nanoparticle, polytetrafluoroethylene (PTFE) cores with polystyrene (PS) shell, is used for demonstration. Near‐edge X‐ray absorption fine structure spectroscopy confirms the significant difference in X‐ray absorption behavior between PTFE and PS. Additionally, because of the insolubility of styrene in PTFE a well‐defined interface between particle core and shell is expected. To validate the STXM results, both the naked PTFE cores as well as the complete core‐shell nanoparticles are examined by scanning electron microscopy (SEM). The introduced STXM‐based methodology yields particle dimensions in agreement with the SEM results and provides additional information such as the position of the particle core, which cannot be extracted from a SEM micrograph. T2 - European conference on applications of surface and interface analysis (ECASIA'17) CY - Montpellier, France DA - 24.09.2017 KW - Core-shell nanoparticles KW - Polymers KW - PS KW - PTFE KW - SEM KW - STXM PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-449700 DO - https://doi.org/10.1002/sia.6464 SN - 1096-9918 SN - 0142-2421 VL - 50 IS - 11 SP - 1077 EP - 1082 PB - John Wiley & Sons CY - Hoboken, New Jersey, USA AN - OPUS4-44970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Artinov, Antoni A1 - Gumenyuk, Andrey A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures N2 - One of the main factors affecting the use of lasers in the industry for welding thick structures is the process accompanying solidification cracks. These cracks mostly occurring along the welding direction in the welding center, and strongly affect the safety of the welded components. In the present study, to obtain a better understanding of the relation between the weld pool geometry, the stress distribution and the solidification cracking, a three-dimensional computational fluid dynamic (CFD) model was combined with a thermo-mechanical model. The CFD model was employed to analyze the flow of the molten metal in the weld pool during the laser beam welding process. The weld pool geometry estimated from the CFD model was used as a heat source in the thermal model to calculate the temperature field and the stress development and distributions. The CFD results showed a bulging region in the middle depth of the weld and two narrowing areas separating the bulging region from the top and bottom surface. The thermo-mechanical simulations showed a concentration of tension stresses, transversally and vertically, directly after the solidification during cooling in the region of the solidification cracking. T2 - 27TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS - METAL 2018 CY - Brno, Czech Republic DA - 23.05.2018 KW - Laser beam welding KW - Weld pool KW - Full penetration KW - Finite element method (FEM) KW - CFD model KW - Numerical simulation KW - Solidification cracking PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-450595 DO - https://doi.org/10.3390/met8060406 SN - 2075-4701 VL - 8 IS - 6 SP - 406, 1 EP - 15 PB - MDPI CY - Basel, Switzerland AN - OPUS4-45059 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krause, B. A1 - Meyer, T. A1 - Sieg, H. A1 - Kästner, Claudia A1 - Reichardt, P. A1 - Tentschert, J. A1 - Jungnickel, H. A1 - Estrela-Lopis, I. A1 - Burel, A. A1 - Chevance, S. A1 - Gauffre, F. A1 - Jalili, P. A1 - Meijer, J. A1 - Böhmert, L. A1 - Braeuning, A. A1 - Thünemann, Andreas A1 - Emmerling, Franziska A1 - Fessard, V. A1 - Laux, P. A1 - Lampen, A. A1 - Luch, A. T1 - Characterization of aluminum, aluminum oxide and titanium dioxide nanomaterials using a combination of methods for particle surface and size analysis N2 - The application of appropriate analytical techniques is essential for nanomaterial (NM) characterization. In this study, we compared different analytical techniques for NM analysis. Regarding possible adverse health effects, ionic and particulate NM effects have to be taken into account. As NMs behave quite differently in physiological media, special attention was paid to techniques which are able to determine the biosolubility and complexation behavior of NMs. Representative NMs of similar size were selected: aluminum (Al0) and aluminum oxide (Al2O3), to compare the behavior of metal and metal oxides. In addition, titanium dioxide (TiO2) was investigated. Characterization techniques such as dynamic light scattering (DLS) and nanoparticle tracking analysis (NTA) were evaluated with respect to their suitability for fast characterization of nanoparticle dispersions regarding a particle's hydrodynamic diameter and size distribution. By application of inductively coupled plasma mass spectrometry in the single particle mode (SP-ICP-MS), individual nanoparticles were quantified and characterized regarding their size. SP-ICP-MS measurements were correlated with the information gained using other characterization techniques, i.e. transmission electron microscopy (TEM) and small angle X-ray scattering (SAXS). The particle surface as an important descriptor of NMs was analyzed by X-ray diffraction (XRD). NM impurities and their co-localization with biomolecules were determined by ion beam microscopy (IBM) and confocal Raman microscopy (CRM). We conclude advantages and disadvantages of the different techniques applied and suggest options for their complementation. Thus, this paper may serve as a practical guide to particle characterization techniques. KW - Small-angle X-ray scattering KW - SAXS PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-447057 DO - https://doi.org/10.1039/C8RA00205C SN - 2046-2069 VL - 8 IS - 26 SP - 14377 EP - 14388 PB - The Royal Society of Chemistry AN - OPUS4-44705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Liehr, Sascha A1 - Münzenberger, Sven A1 - Krebber, Katerina T1 - Wavelength-scanning coherent OTDR for dynamic high strain resolution sensing N2 - Distributed vibration sensing in optical fibers opened entirely new opportunities and penetrated various sectors from security to seismic monitoring. Here, we demonstrate a most simple and robust approach for dynamic strain measurement using wavelength-scanning coherent optical time domain reflectometry (C-OTDR). Our method is based on laser current modulation and Rayleigh backscatter shift correlation. As opposed to common single-wavelength phase demodulation techniques, also the algebraic sign of the strain change is retrieved. This is crucial for the intended applications in structural health monitoring and modal analysis. A linear strain response down to 47.5 pε and strain noise of 100 pε/√Hz is demonstrated for repetition rates in the kHz range. A field application of a vibrating bridge is presented. Our approach provides a cost-effective high-resolution method for structural vibration analysis and geophysical applications. KW - Fiber optics sensors KW - Optical time domain reflectometry KW - Rayleigh Scattering KW - Distributed acoustic sensing KW - Distributed strain sensing PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448069 DO - https://doi.org/10.1364/OE.26.010573 SN - 1094-4087 VL - 26 IS - 8 SP - 10573 EP - 10588 PB - Optical Society of America AN - OPUS4-44806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Beyer, Sebastian A1 - Schürmann, Robin A1 - Feldmann, Ines A1 - Blocki, A. A1 - Bald, Ilko A1 - Schneider, Rudolf A1 - Emmerling, Franziska T1 - Maintaining Stable Zeolitic Imidazolate Framework (ZIF) Templates during Polyelectrolyte Multilayer Coating N2 - Equipping ZIF particles with a polyelectrolyte membrane provides functional groups at their interface, enabling further conjugations necessary for applications such as targeted drug delivery. Previous approaches to coat ZIF particles with polyelectrolytes led to surface corrosion of the template material. This work overcomes previous limitations by performing a Layer-by-Layer (LbL) polyelectrolyte coating onto ZIF-8 and ZIF-67 particles in nonaqueous environment. Using the 2-methylimidazolium salt of polystyrensulfonic acid instead of the acid itself and polyethyleneimine in methanol led to intact ZIF particles after polyelectrolyte coating. This was verified by electron microscopy. Further, zetapotential and atomic force microscopy measurements confirmed a continuous polyelectrolyte multilayer built up. The here reported adaption to the well-studied (LbL) polyelectrolyte selfassembly process provides a facile method to equip ZIF particles with a nanometer thin polyelectrolyte multilayer membrane. KW - Zeolithe KW - Molecular Organic Frameworks KW - MOF KW - ZIF KW - Layer-by-Layer KW - Beschichtung KW - Polyelektrolyt PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-447729 DO - https://doi.org/10.1016/j.colcom.2017.11.004 SN - 2215-0382 VL - 22 SP - 14 EP - 17 PB - Elsevier B.V. CY - Amsterdam, NL AN - OPUS4-44772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neamtu, Mariana A1 - Nadejde, C. A1 - Hodoroaba, Vasile-Dan A1 - Schneider, Rudolf A1 - Verestiuc, L. A1 - Panne, Ulrich T1 - Functionalized magnetic nanoparticles: Synthesis, characterization, catalytic application and assessment of toxicity N2 - Cost-effective water cleaning approaches using improved Treatment technologies, for instance based on catalytic processes with high activity catalysts, are urgently needed. The aim of our study was to synthesize efficient Fenton-like photo-catalysts for rapid degradation of persistent organic micropollutants in aqueous medium. Iron-based nanomaterials were chemically synthesized through simple procedures by immobilization of either iron(II) oxalate (FeO) or iron(III) citrate (FeC) on magnetite (M) nanoparticles stabilized with polyethylene glycol (PEG). Various investigation techniques were performed in order to characterize the freshly prepared catalysts. By applying advanced oxidation processes, the effect of catalyst dosage, hydrogen peroxide concentration and UV-A light exposure were examined for Bisphenol A (BPA) conversion, at laboratory scale, in mild conditions. The obtained results revealed that BPA degradation was rapidly enhanced in the presence of low-concentration H2O2, as well as under UV-A light, and is highly dependent on the surface characteristics of the catalyst. Complete photo-degradation of BPA was achieved over the M/PEG/FeO catalyst in less than 15 minutes. Based on the catalytic performance, a hierarchy of the tested catalysts was established: M/PEG/FeO > M/PEG/FeC > M/PEG. The results of cytotoxicity assay using MCF-7 cells indicated that the aqueous samples after treatment are less cytotoxic. KW - Bisphenol A KW - Magnetic nanocatalyst KW - Endocrine disruptor KW - Nanoparticle KW - Photodegradation KW - Fenton PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448297 DO - https://doi.org/10.1038/s41598-018-24721-4 SN - 2045-2322 VL - 8 SP - Article 6278, 1 EP - 11 PB - Springer Nature CY - London AN - OPUS4-44829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H. Th. T1 - Fatigue strength and life determination of weldments based on fracture mechanics N2 - The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined. Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438500 DO - https://doi.org/10.1016/j.prostr.2017.11.106 SN - 2452-3216 VL - 7 SP - 407 EP - 414 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Hilgenberg, Kai T1 - Damage development and damage tolerance of structures manufactured by selective laser melting - a review N2 - The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component. For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438511 DO - https://doi.org/10.1016/j.prostr.2017.11.071 SN - 2452-3216 VL - 7 SP - 141 EP - 148 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Schork, B. A1 - Bernhard, J. A1 - Kaffenberger, M. T1 - Multiple crack initiation and propagation in weldments under fatigue loading N2 - The work aims at addressing the modelling and implementation of criteria for multiple crack propagation, including interaction and coalescence, for a more reliable fracture mechanics-based prediction of stress-life curves for weldments. A large experimental work is presented in which micro-cracks have been made visible by heat-tinting at successive stages of fatigue life of the welded specimens. Here the correlation between the number of initiation sites and the applied stress level has been also investigated. The criteria have been implemented in in-house software, which allows multiple fatigue crack propagation, and validated against selected experimental tests. The results have shown that the modelling of multiple crack propagation and interaction is crucial for the prediction of the fatigue strength of weldments, both in finite and infinite life regime. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438593 DO - https://doi.org/10.1016/j.prostr.2017.11.108 SN - 2452-3216 VL - 7 SP - 423 EP - 430 PB - Elsevier B.V. AN - OPUS4-43859 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Legall, Herbert A1 - Schwanke, Christoph A1 - Pentzien, Simone A1 - Dittmar, G. A1 - Bonse, Jörn A1 - Krüger, Jörg T1 - X-ray emission as a potential hazard during ultrashort pulse laser material processing N2 - In laser machining with ultrashort laser pulses unwanted X-ray radiation in the keV range can be generated when a critical laser intensity is exceeded. Even if the emitted X-ray dose per pulse is low, high laser repetition rates can lead to an accumulation of X-ray doses beyond exposure safety limits. For 925 fs pulse duration at a center wavelength of 1030 nm, the X-ray emission was investigated up to an intensity of 2.6 × 10^14 W/cm2. The experiments were performed in air with a thin disk laser at a repetition rate of 400 kHz. X-ray spectra and doses were measured for various planar target materials covering a wide range of the periodic table from aluminum to tungsten. Without radiation shielding, the measured radiation doses at this high repetition rate clearly exceed the regulatory limits. Estimations for an adequate radiation shielding are provided. KW - Laser-induced X-ray emission KW - Ultrashort laser material interaction KW - Femtosecond laser KW - Radiation protection PY - 2018 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-448431 DO - https://doi.org/10.1007/s00339-018-1828-6 SN - 0947-8396 SN - 1432-0630 VL - 124 IS - 6 SP - Article 407, 1 EP - 8 PB - Springer AN - OPUS4-44843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Boehm, Rainer A1 - Heckel, Thomas A1 - Spruch, W. A1 - Beggerow, T. T1 - Ultrasonic Phased Array Design Study for High Speed Axle Inspection using an Electronically Rotating Beam N2 - For in-service inspections on wheelset axles with a hollow drilling, mechanized ultrasound inspection systems with single element probes are typically used. The ultrasonic testing in the zones close to the external surface of the railway axles can be realized from the inside of the bore hole, without demounting the wheelset and without dismantling the wheels and the brake discs. The testing system must be able to find flaws in the external surface of the hollow shafts, whose surface lies in the radial-radial plane, these are called transversal flaw. Presently testing systems are used, where scanning is realized in the circumferential direction by mechanical rotation of the probe system in the actual drilling. The phased array probe system, which is presented here, can carry out the rotation scan electronically. The scan can be carried out by simply moving the system forward and backwards through the drilling without mechanical rotation. Manipulation becomes simpler and the inspection time can be shortened considerably. The ultrasonic beam can be inclined exactly and be focused in the plane vertical to the specimen axis. The probe is designed with help of indispensable simulations using especially designed software developed by BAM. The feasibility and the alignment between the simulated and experimental results were shown in earlier projects reported by Boehm et al. (2006) and Völz et al. (2012). The main task here is to optimize a probe for bore holes with a diameter of 65 mm with an increase in sensitivity and a high spatial resolution. This development will be carried out by use of extensive simulations and result in certain changes of the relevant probe parameters. KW - Phased Array KW - Ultrasound KW - Axle inspection PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-436230 DO - https://doi.org/10.1016/j.prostr.2017.07.001 VL - 2017 IS - 4 SP - 71 EP - 78 PB - Elsevier B.V. AN - OPUS4-43623 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -