TY - CONF A1 - Schumacher, David A1 - Ou, D. A1 - Ghafafian, Carineh A1 - Zscherpel, Uwe A1 - Trappe, Volker T1 - Wind turbine rotor blade testing by dual-energy laminography N2 - Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts. T2 - International Symposium on Digital Industrial Radiology and Computed Tomography – DIR2019 CY - Fürth, Germany DA - 02.07.2019 KW - Laminography KW - Wind energy KW - Fiber reinforced polymer KW - Photon counting detector KW - Repair patch PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-484380 UR - https://www.dir2019.com/portals/dir2019/bb/Tu.3.A.1.pdf SN - 978-947971-06-0 SP - 1 EP - 13 AN - OPUS4-48438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Liehr, Sascha A1 - Münzenberger, Sven A1 - Krebber, Katerina T1 - Wavelength-scanning distributed acoustic sensing for structural monitoring and seismic applications N2 - We introduce wavelength-scanning coherent optical time domain reflectometry (WS-COTDR) for dynamic vibration sensing along optical fibers. The method is based on spectral shift computation from Rayleigh backscatter spectra. Artificial neural networks (ANNs) are used for fast and high-resolution strain computation from raw measurement data. The applicability of the method is demonstrated for vibration monitoring of a reinforced concrete bridge. We demonstrate another application example for quasi-static and dynamic measurement of ground deformation and surface wave propagation along a dark fiber in a telecommunication cable. T2 - 7th International Symposium on Sensor Science CY - Napoli, Italy DA - 09.05.2019 KW - Optical fiber sensor KW - Distributed acoustic sensor (DAS) KW - Optical time domain reflectometry KW - Rayleigh scattering KW - Artificial neural networks KW - Structural health monitoring KW - Seismic measurement PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487733 DO - https://doi.org/10.3390/proceedings2019015030 SN - 2504-3900 VL - 15 SP - Paper 30, 1 EP - 5 PB - MDPI CY - Basel AN - OPUS4-48773 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Ronald T1 - Effect of repair models on risk based optimal inspection strategies for support structures of offshore wind turbines N2 - Owners or operators of offshore wind farms perform inspections to collect information on the condition of the wind turbine support structures and perform repairs if required. These activities are costly and should be optimized. Risk-based methods can be applied to identify inspection and repair strategies that ensure an optimal balance between the expected total service life cost of inspection and repair, and the achieved risk reduction. Such an optimization requires explicit modeling of repairs. In this paper, the impact of different repair models on the results of a risk-based optimization of inspection and repair strategies is quantified in a numerical example considering a jacket-type steel frame subject to high-cycle fatigue. The example showed that, in this specific application, there is no need for detailed modeling of the behavior of repaired welded connections. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures (SMAR 2019) CY - Potsdam, Germany DA - 27.08.2019 KW - Risk KW - Reliability KW - Inspection planning KW - Offshore wind turbines PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488297 UR - https://www.smar2019.org/Portals/smar2019/bb/Th.2.A.4.pdf SP - Paper Th.2.A.4, 1 EP - 8 AN - OPUS4-48829 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Shamsuddoha, Md A1 - Thiele, Marc A1 - Baeßler, Matthias A1 - Kühne, Hans-Carsten T1 - Comparison of cracks formed in scaled grouted connection of offshore energy structures under static and cyclic loads N2 - Global energy consumption will increase in the future necessitating both fossil fuels and renewable energy choices - especially wind energy. Such high energy demand requires installation of offshore energy structures, rigs, platforms and towers, which are susceptible to adverse environmental conditions along with maintenances. Due to their large size and remote locations, cylindrical grouted joints are often adopted between substructure and foundation in these offshore platforms and wind structures such as monopiles. However, these connections are composite structures with exterior sleeve, interior pile and infill mortar. Degradation and settlements were reported inside similar connections, which were installed in last three decades. Besides, grouting in the offshore sites were proven difficult to obtain ideal load bearing capacity. In-situ loading conditions were also found to be affecting the failure mechanism inside such connections. This study aims at characterizing the nature of cracks generated in these grouted connections under both static and cyclic loading. Scaled grouted joints were manufactured using a novel reusable mold, and connections were loaded to failure to visualize the main failure patterns. An assessment between failure under these two types of load is drawn along with comparison to previously available literature. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Grouted connection KW - Crack formation KW - Crack pattern KW - Static load KW - Cyclic load PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487961 SP - Th.2.A.1-1 EP - Th.2.A.1-9 AN - OPUS4-48796 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kullolli, Borana A1 - Cuéllar, Pablo A1 - Baeßler, Matthias A1 - Stutz, H. H. T1 - Modelling and calibration for cyclic soil-structure interface behaviour N2 - The structural performance of many geotechnical systems (e.g. axially-loaded pile foundations), depends on the shearing resistance at the soil interface, which may govern the load bearing capacity of the foundation. Experimental investigations have shown that this interaction is mainly localised within a narrow shear band next to the structure. Under cyclic loading, a contraction of the soil at the interface may arise (net volume loss), possibly leading to a stress relaxation and thus to a reduction of the load bearing capacity (the so-called friction fatigue). Based on the constitutive similarities between soil continua and interfaces, we propose here the adaption of a Generalized Plasticity model for sandy soils for the numerical analysis of interface problems. In this contribution, the results of an experimental campaign for the parameter calibration of the constitutive model are presented. The tests have been conducted with a ring shear device involving different normal stresses, roughness of the steel plates as well as cyclic loading. The new modelling approach shows promising results and has the additional practical advantage that the interface zone and the soil continuum can both be described with the same constitutive model in general boundary value problems. T2 - Konferenz 7th International Symposium on Deformation Characteristics of Geomaterials CY - Glasgow, Scotland DA - 26.06.2019 KW - Soil-structure interaction KW - Offshore foundations PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489096 DO - https://doi.org/10.1051/e3sconf/20199213007 VL - 92 SP - 13007 EP - 13013 PB - EDP Sciences CY - Glasgow, Scotland AN - OPUS4-48909 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Babutzka, Martin T1 - Investigation of the salinization in marine and offshore environment - test methods and challenges N2 - Salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena in the maritime sector and in offshore applications. Especially Offshore Wind Turbines are exposed to extreme corrosive conditions due to high chloride concentrations in the atmosphere and the resulting high chloride deposition rates. It is of great importance to evaluate to what extent salinization of the surface influences the corrosion protection of coatings and pitting occurrence on stainless steels under atmospheric conditions to evaluate the durability of metallic building structures in offshore and marine environments. The evaluation of the scientific literature and regulatory guidelines has shown that there are still many open questions regarding the contamination of metal surfaces by chlorides. This contribution will discuss how salinization of metal surfaces is evaluated and monitored according to current standards and guidelines. Future challenges concerning test methods and the application of evaluated salinization values and deposition rates will be discussed. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.20019 KW - Maritime Atmosphäre KW - Versalzung KW - Maritime atmosphere KW - Salinization PY - 2019 SP - Th.2.A.5, 1 EP - 8 PB - SMAR 2019 AN - OPUS4-48905 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Lohde, Sebastian A1 - Aydoğdu, M. T1 - Zerstörungsfreie Prüfung von Composite-Druckgefäßen mit konventioneller und hochfrequenter Wirbelstromtechnik N2 - Composite-Druckgefäße für den Gefahrguttransport sowie für Wasserstoff- und Erdgasfahrzeuge bestehen aus einem lasttragenden Composite und einer gasdichten, metallischen oder polymeren Barriereschicht (Liner). Zur Untersuchung des Alterungsverhaltens solcher Composite-Druckgefäße wurde in der BAM das interdisziplinäre Themenfeldprojekt COD-AGE durchgeführt. Ziel des Projektes war die Entwicklung von Methoden und Modellen zur Beschreibung und Bestimmung des Alterungsverhaltens von Carbonfaser-Compositen am Beispiel von Druckgefäßen, um eine bessere Vorhersage der Alterung und der sicheren Gebrauchsdauer zu ermöglichen. Ein Schwerpunkt in diesem Projekt war die Bereitstellung geeigneter ZfP-Methoden. Dabei ging es sowohl um versuchsbegleitende Prüfungen, als auch um die mögliche Entwicklung von Prüfeinrichtungen für den späteren praktischen Gebrauch. In dem Vortrag werden Prüfergebnisse der alterungsbegleitenden Wirbelstromprüfung an Composite-Druckgefäßen vorgestellt. In Alterungsversuchen wurden Druckgefäße aus einem ca. 4 mm dicken Aluminiumliner und ca. 8 mm dicker CFK-Ummantelung untersucht. Typisches Einsatzgebiet solcher Druckgefäße sind Atemschutzgeräte der Feuerwehr. Die Druckgefäße wurden sowohl mit konventioneller Wirbelstromtechnik von außen und von innen als auch mit hochfrequenter Wirbelstromtechnik von außen geprüft. Es konnten sowohl Beschädigungen des metallischen Liners, als auch Strukturen des CFK-Geflechts nachgewiesen werden. Eine besondere mechanische Herausforderung bestand in der Prüfung der Innenseite der Liner, da hier eine zylindrische Fläche mit einem Innendurchmesser von 150 mm durch einen Zugang von nur 15 mm Durchmesser geprüft werden muss. T2 - DACH-Jahrestagung CY - Friedrichshafen, Germany DA - 26.05.2019 KW - Wirbelstromprüfung KW - COD-AGE KW - Composite-Druckgefäß KW - CFK PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-481243 SN - 978-3-947971-02-2 VL - 171 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-48124 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaumann, P. A1 - Schürmann, K. A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Automatically Welded Tubular X Joints for Jacket Substructures – Prediction of the Technical Fatigue Crack Location N2 - To increase the competitiveness of jacket substructures compared to monopiles a changeover from an individual towards a serial jacket production based on automated manufactured tubular joints combined with standardized pipes has to be achieved. Therefore, this paper addresses fatigue tests of automatically welded tubular X-joints focusing on the location of the technical fatigue crack. The detected location of the technical crack is compared to numerical investigations predicting the most fatigue prone notch considering the structural stress approach as well as the notch stress approach. Besides, the welding process of the automated manufactured tubular X-joints is presented. T2 - Nordic Steel 2019 CY - Copenhagen, Denmark DA - 18.09.2019 KW - Automated arc welding KW - Fatigue tests KW - Tubular X-joints KW - Technical crack detection KW - Local fatigue approaches PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-518490 DO - https://doi.org/10.1002/cepa.1140 VL - 3 IS - 3-4 SP - 823 EP - 828 PB - Wiley-VCH Verlag GmbH on behalf of Ernst & Sohn Verlag für Architektur und technische Wissenschaften GmbH & Co. KG CY - Berlin AN - OPUS4-51849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baensch, Franziska A1 - Baer, Wolfram A1 - Wossidlo, Peter A1 - Habib, Abdel Karim T1 - Frequenzanalyse von Schallemission an einem Stahlrohr unter Biegebeanspruchung N2 - Um ein tieferes Verständnis über die Schallemission bei der Entstehung und Ausbreitung von Rissen in Stahlrohrleitungen zu erlangen, wurde ein Stahlrohr der Güte S355J2H im Vierpunkt-Biegeversuch quasistatisch bis hin zum Wanddurchbruch (Leckage) belastet und mittels Schallemissionsmessung und Gleichstrompotentialmessung überwacht. Das Rohrsegment wurde durch einen 90°- Außenumfangskerb in der Mitte der Rohrlänge definiert vorgeschädigt, um davon ausgehend ein stabiles Risswachstum zu induzieren und die Analyse von Schallemission aus Rissereignissen, die am Kerb eintraten, sicherzustellen. Für die Schallemissionsmessung wurden vier Breitbandsensoren max. 105 mm vom Kerb entfernt montiert. Die Signalaufzeichnung erfolgte kontinuierlich und schwellwertunabhängig. Für die Gleichstrompotentialmessung wurde ein Gleichstrom von 300 A eingeleitet und der Potentialabfall über dem Kerb mit fünf Sonden entlang des Kerbs gemessen. Beide Messverfahren identifizieren die Rissinitiierung sowie Veränderungen im Risswachstum. Die detektierten Schallemissionsereignisse werden, unter Berücksichtigung spektraler Eigenschaften, mit fortschreitender Belastung und Rissentwicklung analysiert. Diese Studien wurden im Rahmen des interdisziplinären Forschungsprojekts AGIFAMOR, Aging infrastructure - Faseroptisches Monitoring von Rohrleitungen, an der BAM durchgeführt. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Schallemission KW - Frequenzanalyse KW - Rissbildung in Stahl PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-476888 SN - 978-3-947971-00-8 VL - 169 SP - 1 EP - 8 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-47688 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Pirskawetz, Stephan A1 - Gründer, Klaus-Peter A1 - Kadoke, Daniel A1 - Unger, Jörg F. T1 - Überwachung von Stahlbetonbrücken - Ein Modellprojekt N2 - Die Brücken im Netz der Bundesverkehrswege sind überwiegend in einem ausreichenden bis guten Zustand. Allerdings steigt der Unterhalts- und Sanierungsaufwand aufgrund des inzwischen hohen Alters vieler Brücken sowie des ständig wachsenden Schwerlastverkehrs. Techniken zur Einschätzung der verbleibenden Lebensdauer von Brücken sowie zur dauerhaften Beobachtung des Tragverhaltens bzw. des Erfolges von Sanierungsmaßnahmen werden daher für den sicheren und wirtschaftlichen Betrieb dringend benötigt. Zur Evaluierung dafür geeigneter holistischer Ansätze wurde in der BAM das Projekt BLEIB - Bewertung, Lebensdauerprognose und Instandsetzung von Brückenbauwerken - ins Leben gerufen. Ein zentrales Ergebnis des Projektes ist eine extern vorgespannte Stahlbetonbrücke als Zweifeldträger mit einer Gesamtlänge von 24 m, die für den Test verschiedenster Sensorsysteme, zur Validierung numerischer Modelle und zur Erprobung von Sanierungs- und Verstärkungsmaßnahmen entwickelt wurde. Für die Simulation unterschiedlicher Schädigungsgrade kann die Vorspannung der Brücke variiert werden. Die Brücke wird mit beweglichen Gewichten belastet und über einen Shaker zum Schwingen angeregt. Das Brückenmodell wurde bewusst geschädigt, indem die Vorspannung der Struktur erstmalig schrittweise bis auf null reduziert wurde. Unter der Eigenlast verformte sich die Brücke, wodurch eine Rissbildung im Beton einsetzte. Die Zugspannung, die zuvor durch die Vorspannung aufgenommen wurde, übernahm Schritt für Schritt der Beton. Als die Zugspannungen die relativ geringe Zugfestigkeit des Betons überstiegen, begann dieser zu reißen und die schlaffe Bewehrung der Struktur nahm die Spannungen auf. Dieser Versuch wurde unter anderem von Schallemissionsmessungen begleitet. Der Rissbildungsprozess konnte damit, bei gleichzeitiger Aufzeichnung der Vorspannung, früh detektiert und die Risse geortet werden. Die Ergebnisse korrelieren gut mit den Ergebnissen der stereophotogrammetrischen Verformungsmessungen der Struktur. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Brückenmonitoring KW - Schallemissionsanalyse PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-477878 SN - 978-3-947971-00-8 VL - 169 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-47787 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Hille, Falk A1 - Makris, Ruben ED - Helmerich, Rosemarie ED - Ilki, A. ED - Motavalli, M. T1 - Comparison of fatigue crack detection methods for high-cyclic loaded steel structures N2 - At present, to produce renewable energy offshore wind farms play an important role. The available space combined with the more valuable wind conditions make offshore locations very attractive for wind powered energy production. In Europe a significant number of offshore wind farms already exist, especially in the North and Baltic Sea. In future this trend will continue, and further offshore wind farms will be built. The majority of offshore wind turbines are mounted on steel foundation structures. Due to the high-cyclic loading by wind and waves fatigue stress plays a substantial role regarding structural safety. Besides the consideration of fatigue within the design process, to monitor existing steel structures for potential fatigue cracks during their life time is a major topic and a challenge. For the structures of the offshore wind turbines are large and partially under water effective reliable methods for the detection of fatigue cracks are required. This contribution presents investigations on different crack detection methods applied at high-cycle fatigue tests on small-scale welded steel samples as well as on large-scale welded steel components. The tests were conducted at the BAM laboratories. For crack detection mainly three different methods were used and compared. The first method regards to the measurement of strain by conventionally strain gauges. Secondly, the crack luminescence was used as a new and effective optical method for surface monitoring. And finally, crack detection by pressure differentials of the inner and outer section of tubular steel elements was investigated. A comparison study will emphasize the advantages and disadvantages of the different methods and show which of the described methods is potentially more suitable for an application on real offshore wind structures. T2 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Fatigue KW - Steel structures KW - Crack detection PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489433 SP - Th.2.A.1-1 EP - Th.2.A.1-8 AN - OPUS4-48943 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Niederleithinger, Ernst A1 - Maak, Stefan A1 - Mielentz, Frank A1 - Effner, Ute A1 - Strangfeld, Christoph A1 - Timofeev, Juri T1 - Review of recent developments in ultrasonic echo testing of concrete N2 - Ultrasonic methods are used in concrete investigations since decades. While being limited to transmission testing in the laboratory for a while, in-situ echo measurements for structural investigations and condition assessment have made their way into practical application in the past 20 years. However, several challenges remain. On one side, there are technical issues as limitations in depth of penetration, resolution and imaging capabilities. On the other side there are still gaps in validation, standardization and certification, which are limiting the applicability in condition/load capacity assessment. This review reports a couple of developments which will help to overcome these issues. This includes technical developments as new devices which are easier to handle on site or giving a much deeper penetration depth (e.g. the LAUS device at BAM) as well as improvements in imaging by hardware update (e. g. air coupled ultrasound or coded signals) or new software (e. g. RTM imaging). To foster the application in real world projects we are as well working on standardization by developing new reference specimen with international partners which will ensure world-wide comparability of ultrasonic and other methods and quality assurance codes. Further, non-destructive methods are being used to update probabilistic models used for the reassessment of existing structures to support the structural engineer’s decisions. T2 - SMAR 2019 CY - Potsdam, Germany DA - 27.08.2019 KW - Engineered Barrier System (EBS) KW - Ultraschall KW - NDT KW - Re-assessment of exiting bridges PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-489686 SP - 1 EP - 6 AN - OPUS4-48968 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duffner, Eric A1 - Mair, Georg W. A1 - Munzke, Dorit A1 - Szczepaniak, Mariusz A1 - Schukar, Marcus T1 - Lebensdauerversuche an Faserverbund-Druckbehältern überwacht mittels Schallemissionsprüfung und optischen Fasern N2 - Kurzfassung. Die meisten Faserverbundbehälter, die in Europa für den Transport gefährlicher Stoffe oder als Speicherbehälter für Wasserstoff oder Erdgas in Fahrzeugen Verwendung finden, werden für eine nicht begrenzte Lebensdauer ausgelegt. In regelmäßigen Abständen sind für diese Druckbehälter wiederkehrende Prüfungen vorgeschrieben, die in der Regel aus visuellen Inspektionen und hydraulischen Innendruckprüfungen bestehen. Die wiederkehrenden Prüfungen sind jedoch weder geeignet, die sichere Betriebsdauer festzulegen noch den Alterungszustand der Druckbehälter zu beurteilen. Aufgrund des weiter steigenden Drucks zur Kosten- und Gewichtsreduktion von Faserverbundbehältern und der damit einhergehenden Ausnutzung der existierenden Sicherheitsmargen gewinnen Methoden zur Beurteilung des Alterungsverhaltens dieser Druckbehälter immer mehr an Bedeutung. Vor diesem Hintergrund wurde in der BAM das Vorhaben „Alterungsverhalten von Composite-Druckgefäßen mit Carbonfaser-Compositen unter gekoppelten Beanspruchungen (COD-AGE)“ gestartet, um die Alterung von Faserverbundbehältern mittels verschiedener zerstörungsfreier Prüfverfahren zu untersuchen. Die hier vorgestellten Ergebnisse wurden an einem Typ 4 Hybridbehälter mit Kunststoffliner gewonnen, in den im Rahmen des Herstellungsprozesses optische Glasfasern in verschiedenen Schichten integriert wurden. Der Behälter wurde mittels hydraulischem Innendruck und erhöhter Umgebungstemperatur zyklisch bis zum Lebensende belastet. Zwischen den einzelnen Lastsequenzen erfolgte eine an die wiederkehrende Prüfung im Betrieb angelehnte hydraulische Druckbelastung. Sowohl die hydraulische Alterung als auch die Druckrampen wurden mittels Schallemissionsprüfung (SEP) und verteilter faseroptischer Sensorik mit dem Ziel einer frühzeitigen Versagensvorhersage überwacht. Durch die Schallemissionsanalyse sollte untersucht werden, ob zum Lebensende hin ein signifikanter Anstieg der Schallemissionsaktivität und -intensität, unterteilt in verschiedene Lastbereiche, beobachtet werden kann. Zusätzlich zum kontinuierlichen Monitoring der Zyklierung sollten die Druckrampen separat untersucht werden, um hier Potenziale für die wiederkehrende Prüfung zu erkennen. T2 - 22. Kolloquium Schallemission und 3. Anwenderseminar Zustandsüberwachung mit geführten Wellen CY - Karlsruhe, Germany DA - 27.03.2019 KW - Faserverbund KW - Druckbehältern KW - Lebensdauerversuche KW - Schallemissionsprüfung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-479534 SP - 1 EP - 10 PB - DGZfP CY - Berlin AN - OPUS4-47953 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ghafafian, Carineh A1 - Popiela, Bartosz A1 - Nielow, Dustin A1 - Trappe, Volker T1 - Restoration of structural integrity – a comparison of various repair concepts for wind turbine rotor blade shells N2 - Localized patches are a cost- and time-effective method for repairing fiber-reinforced polymer (FRP) sandwich wind turbine rotor blade shells. To increase the understanding of their effect on the fatigue of the blades, this study examines the effect of various layup methods of localized repair patches on the structural integrity of composite sandwich structures. Manufactured with the vacuum-assisted resin infusion (VARI) process, the shell test specimens are produced as a curved structure with glass fiber reinforced polymer (GFRP) sandwiching a polyvinyl chloride (PVC) foam core. Patch repairs are then introduced with varying layup techniques, and material properties are examined with cyclic fatigue tests. The transition region between patch and parent material is studied in greater detail with finite element method (FEM) simulations, with a focus on the effect of fiber orientation mismatch. Damage onset, crack development, and eventual failure are monitored with in-situ non-destructive testing methods to develop a robust understanding of the effects of repair concepts on material stiffness and strength. T2 - SMAR 2019 - 5th International Conference on Smart Monitoring, Assessment and Rehabilitation of Civil Structures CY - Potsdam, Germany DA - 27.08.2019 KW - Lightweight materials KW - Glass fiber reinforced polymers KW - Sandwich KW - Wind turbine blades PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-482170 SP - 1 EP - 8 PB - German Society for Non-Destructive Testing (DGZfP e.V.) AN - OPUS4-48217 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Pichelhöfer, A. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Galvanic chloride extraction by an embedded zinc anode: Ion distribution mapped by laser induced breakdown spectroscopy (LIBS) N2 - An important aspect with regard to the service life of zinc based galvanic anodes and the durability of the corrosion protection of steel in concrete is the “galvanic chloride extraction”. Chloride ions move in the electric field generated by the current, flowing between the galvanic anode and the cathodic steel. Migration leads to an accumulation of anions, e.g. chloride ions, at the anode and depletion of chlorides near the steel rebar surface. The ion migration was studied on steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied embedded zinc anode (EZA). The zinc anode was embedded and glued to the concrete surface by a geo-polymer based chloride free binder. The EZA was operated over a period of 1 year and the ion distribution between anode (EZA) and cathode (steel reinforcement) was studied by laser induced breakdown spectroscopy (LIBS) after 5 months, 7 months and 12 months. The results show that chloride ions efficiently migrate in the direction of the zinc-anode and accumulate there. Chloride distribution in the EZA correlates with the distribution of zinc ions generated by the anodic dissolution of the zinc anode in the binder matrix. The microstructure of the binder matrix and its interface to the zinc-anode are studied by REM/EDX – preliminary results will be reported. T2 - Concrete Solutions 2019 CY - Cluj Napoca, Romania DA - 30.09.2019 KW - Galvanic corrosion KW - Corrosion KW - Chloride extraction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488189 DO - https://doi.org/10.1051/matecconf/201928903010 VL - 289 SP - 03010, 1 EP - 5 PB - MATEC Web of Conferences AN - OPUS4-48818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Wack, Y. A1 - Mook, G. T1 - Simulation von mechanisierten Eisenbahnschienenprüfungen mit Ultraschall N2 - Bei der mechanisierten Prüfung von verlegten Eisenbahnschienen mit Schienenprüfzügen werden große Prüfdatenmengen mit einer komplexen Prüfkopfanordnung in kurzer Zeit bei hohen Prüfgeschwindigkeiten aufgenommen. Der Typ und der Zustand des Gleises kann während der Prüfung in schnellem Wechsel streckenabhängig variieren, z.B. unterschiedliche Schienentypen oder Abnutzung sowie beim Durchfahren von Weichenstraßen. Der logistische Aufwand diese Prüfung insgesamt durchzuführen ist dabei sehr hoch und eine Wiederholung der Prüfung in einem kurzen Zeitintervall nicht möglich. Es werden während der Prüfdatenaufnahme bereits Datenreduktionsverfahren, Rekonstruktionsverfahren und Online-Parametervariationen eingesetzt, um die Ergebnisdaten zum einen in Ihrer Menge zu begrenzen zum anderen auf die lokalen Geometrie- und Zustandsänderungen des Prüfobjektes Schiene zu reagieren. Im Regelwerk EN 16729-1 „Zerstörungsfreie Prüfung an Schienen im Gleis -Teil 1: Anforderungen an Ultraschallprüfungen und Bewertungsgrundlagen“ werden Bezugsreflektoren definiert, um die Leistung automatisierter Ultraschallsysteme für die Schienenprüfung zu verifizieren. Um die Einflüsse der komplexen Randbedingungen der mechanisierten Schienenprüfung auf das Prüfergebnis evaluieren zu können, wurde ein Softwarewerkzeug erarbeitet, mit dem eine Prüffahrt auf einer Schiene simuliert werden kann. Basierend auf der Datenaufnahme mit dem Glassy-Rail-Diagramm können alle relevanten Prüfparameter und Artefakte in Schienen sowie Störeinflüsse bei der Simulation berücksichtigt werden. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Schiene KW - Zerstörungsfreie Prüfung KW - Ultraschall PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496749 VL - 2019 SP - 1 EP - 8 AN - OPUS4-49674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Beilken, D. A1 - Rühe, S. A1 - Heckel, Thomas A1 - Casperson, Ralf T1 - Aktuelle Entwicklungen der Wirbelstrom- und Ultraschallprüfung an verlegten Eisenbahnschienen N2 - Die kombinierte Schienenprüfung mit Wirbelstrom und Ultraschall ermöglicht eine ganzheitliche Detektion von Inhomogenitäten im Kopf und Steg der Schiene und gewährleistet das Auffinden sowohl von Volumen-als auch Oberflächeneffekten wie z. B. Head Checks. Für die verbesserte Detektion von Rollkontaktermüdung (rolling contact fatique, RCF) und den daraus resultierenden Schienenfehlern (Head-Checks, Squats, Riffel, …) wurde für die Wirbelstromprüfung der Prüfbereich auf die gesamte Rollkontaktfläche erweitert. Der Fokus liegt im Neudesign der Wirbelstrom-Prüfvorrichtung und der damit verbundenen normgerechten Auslegung der Konstruktion für die fahrzeugspezifischen Gegebenheiten. Ferner wurde die Anwendersoftware des kombinierten Prüfsystems vereinheitlicht. Um die wirtschaftliche Effektivität unsere Prüftechnik zu steigern, wird die Multiplex-Gerätetechnologie in die automatisierte Schienenprüfung eingeführt. Damit wird der freizuhaltende Einbauraum innerhalb der Fahrzeuge sowie Kabelwege deutlich reduziert. Durch den Übergang zu der Multiplextechnologie wurde weiterhin die Stromaufnahme um mehr als 50% reduziert. T2 - DGZfP DACH Tagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Schienenprüfung KW - Zerstörungsfreie Prüfung KW - Ultraschall KW - Wirbelstrom PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-496775 VL - 2019 SP - 1 EP - 10 AN - OPUS4-49677 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bühling, Benjamin A1 - Strangfeld, Christoph A1 - Maack, Stefan T1 - Entwicklung eines luftgekoppelten Ultraschall-Echo-Prüfverfahrens mittels fluidischer Anregung N2 - In vielen technischen Bereichen werden Ultraschallverfahren zur zer-störungsfreien Werkstoffprüfung eingesetzt. Dabei wird ein Schallpuls von einem Prüfkopf in ein Prüfobjekt eingebracht. Der Puls kann unter anderem durch Membra-nen oder Piezoelemente erzeugt werden und wird in der Regel durch direkten Kontakt oder über ein Koppelmittel an das Objekt übertragen. Luftgekoppelter Ultraschall spielt in kommerziellen Anwendungen bisher eine untergeordnete Rolle, da die Dif-ferenz der akustischen Impedanzen von Luft und Festkörpern immense Verluste beim Übergang des Schallsignals hervorruft. In diesem Beitrag soll ein neuartiges Anregungsprinzip vorgestellt werden, mit dem ein Großteil dieser Verluste vermieden wird. Anstelle eines Festkörpers soll mit Hilfe einer fluidischen Düse Druckluft zur Signalerzeugung eingesetzt werden. In die-ser Düse wird eine selbsterhaltende Strömungsinstabilität erzeugt, die einen Schall-puls von bis zu 100 kHz hervorruft, sodass der Impedanzverlust in die Umgebungsluft entfällt. Da die charakteristische Frequenz eines fluidisch generierten Pulses maßgeb-lich von der Bauform der Düse und dem anliegenden Druck abhängt, lässt sich mittels einer geeigneten Strömungsregelung ein breiter Frequenzbereich zur Abtastung nut-zen. Die so emittierten Pulse werden auf das Prüfobjekt gerichtet und die reflektierten Signale mit einem Laservibrometer an der Oberfläche des Objekts im Echo-Verfahren abgetastet. Von drei signalmindernden Materialübergängen bei gewöhnlichem luftge-koppeltem Ultraschall bleibt in dem hier vorgeschlagenen Messystem lediglich die Grenzfläche von Luft zu Prüfkörper, sodass eine höhere Signalausbeute als bisher er-wartet werden kann. T2 - DACH-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - Ultraschall KW - Ultrasound KW - Air-coupled KW - Luftgekoppelt KW - Fluidic oscillator KW - Fluidischer Oszillator KW - Laser-Doppler-Vibrometer KW - Refraktovibrometrie KW - Refracto-vibrometry KW - NDT KW - ZfP PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-481207 VL - 2019 SP - 1 EP - 8 PB - DGZfP Deutsche Gesellschaft für Zerstörungsfreie Prüfung AN - OPUS4-48120 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wasmer, Paul A1 - Bulling, Jannis A1 - Gravenkamp, H. A1 - Prager, Jens T1 - Acoustic-structure interaction in the Scaled Boundary Finite Element Method for primsatic geometries N2 - Due to the short wavelength compared to the dimensions of the structure, the simulation of ultrasonic waves is still a challenging task. A numerical method well suited for this purpose is the semi-analytical Scaled Boundary Finite Element Method (SBFEM). When applying this method, only the boundary of a computational domain is discretized using finite elements, while the interior is described by an analytical ansatz. Hence, the number of degrees of freedom is reduced significantly compared to the classical Finite Element Method (FEM). In recent years, a particular formulation of the SBFEM for the simulation of ultrasonic guided waves was developed. The method constitutes an efficient algorithm for prismatic structures of arbitrary length, such as plates, pipes, or beams. Wave propagation phenomena in such structures can be modeled for isotropic and anisotropic inhomogeneous waveguides. Even though the method is an efficient tool for the simulation of guided waves in solid media, a reliable model for the simulation of acoustic wave propagation in fluids as well as acoustic-structure interaction in terms of SBFEM is still missing. In principle, the fluid can be described by a displacement-based formulation and thus be implemented in existing SBFEM algorithms for solid bodies. However, due to the discretization with classical finite elements, spurious modes occur, which cannot be separated from the physical modes straightforwardly. The spurious modes can be suppressed using a penalty parameter. Although very accurate results were achieved for some problems, this procedure has been proven unreliable for certain cases. For this reason, we propose a different approach in this contribution. We employ a pressure model to simulate the acoustic behavior of fluids. The implementation of the pressure model results in a higher effort due to the necessity of incorporating coupling terms, but it presents a stable alternative without spurious modes. The accuracy of the method is demonstrated in comparison with analytical solutions and results obtained using the FEM. T2 - GACM 2019 CY - Kassel, Germany DA - 28.08.2019 KW - Scaled Boundary Finite Element Method KW - Guided Waves KW - Ultrasound KW - Acoustic-Structure Interaction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-497364 UR - https://www.upress.uni-kassel.de/katalog/abstract.php?978-3-7376-5093-9 SN - 978-3-86219-5093-9 DO - https://doi.org/10.19211/KUP9783737650939 SP - 347 EP - 350 AN - OPUS4-49736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boehm, Rainer T1 - Phased Array und Imaging, zwei raumzeitliche Interferenzverfahren N2 - Phased-Array-Technik und Bildgebung mit Ultraschallwellen sind nach langer Entwicklungszeit inzwischen auf dem Weg zu allgemeiner Verbreitung. Daher bietet sich an, die verschiedenen Techniken und deren Begriffe wie z.B. Phased-Array, SAFT, TFM, FMC und Sparse-Array zusammenfassend in Beziehung zu setzen. All diesen Techniken liegt dieselbe Idee zu Grunde, nämlich durch gezielte Überlagerung von Ultraschallsignalen den gewünschten Effekt zu erreichen. Die verschiedenen Techniken werden kurz charakterisiert und neben den Unterschieden wird beschreiben, auf welche Weise bei all diesen Techniken das Phänomen der konstruktiven Interferenz jeweils genutzt wird. T2 - Ultraschall-Array-Technologien und ihre Anwendungen, Seminar des FA Ultraschallprüfung der DGZfP CY - Berlin, Germany DA - 04.11.2019 KW - Phased Array KW - Imaging KW - Synthetic Aperture Focusing Technique KW - Total Focusing Methode KW - Full Matrix Capture PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-497924 UR - https://www.dgzfp.de/seminar/ultraschall# SP - 1 EP - 20 PB - DGZfP AN - OPUS4-49792 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -