TY - JOUR A1 - Cunningham, Patrick A1 - Wang, L. A1 - Kane, S. A1 - Kim, A. A1 - Jenkins, B. M. A1 - Miller, S. A. T1 - Lifecycle implications and mechanical properties of carbonated biomass ashes as carbon-storing supplementary cementitious materials N2 - Methods to sequester and store atmospheric CO2 are critical to combat climate change. Alkaline-rich bioashes are potential carbon fixing materials. This work investigates potential co-benefits from mineralizing carbon in biomass ashes and partially replacing high embodied greenhouse gas (GHG) Portland cement (PC) in cement-based materials with these ashes. Specifically, rice hull ash (RHA), wheat straw ash (WSA), and sugarcane bagasse ash (SBA) were treated to mineralize carbon, and their experimental carbon content was compared to modeled potential carbonation. To understand changes in the cement-based storage materials, mortars made with CO2-treated WSA and RHA were experimentally compared to PC-only mortars and mortars made with ashes without prior CO2 treatment. Life cycle assessment methodology was applied to understand potential reductions in GHG emissions. The modeled carbonation was ∼18 g-CO2/kg-RHA and ∼180 g-CO2/kg-WSA. Ashes oxidized at 500 °C had the largest measured carbon content (5.4 g-carbon/kg-RHA and 35.3 g-carbon/kg-WSA). This carbon appeared to be predominantly residual from the biomass. Isothermal calorimetry showed RHA-PC pastes had similar heat of hydration to PC-pastes, while WSA-PC pastes exhibited an early (at ∼1.5 min) endothermic dip. Mortars with 5 % and 15 % RHA replacement had 1–12 % higher compressive strength at 28 days than PC-only mortars, and milled WSA mortars with 5 % replacement had 3 % higher strength. A loss in strength was noted for the milled 15 % WSA, the CO2-treated 5 %, and the 15 % WSA mortars. Modeled reductions in GHG emissions from CO2-treated ashes were, however, marginal (<1 %) relative to the untreated ashes. KW - CO2 sequestration KW - CO2 storage KW - Biomass ash KW - Supplementary cementitious materials KW - Concrete PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-626959 DO - https://doi.org/10.1016/j.biombioe.2025.107772 SN - 1873-2909 VL - 197 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-62695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogler, Nico A1 - Drabetzki, Philipp A1 - Lindemann, Mathias A1 - Kühne, Hans-Carsten T1 - Description of the concrete carbonation process with adjusted depth resolved thermogravimetric analysis N2 - The thermal gravimetric analysis (TG) is a common method for the examination of the carbonation progress of cement-based materials. Unfortunately, the thermal properties of some components complicate the evaluation of TG results. Various hydrate phases, like ettringite (AFt), C-S-H and AFm decompose almost simultaneously in the temperature range up to 200 °C. Additionally, physical bound water is released in the same temperature range. In the temperature range between 450 °C and 600 °C the decomposition of calcium hydroxide and amorphous or weakly bound carbonates takes place simultaneously. Carbonates, like calcite, from limestone powder or other additives may be already contained in the noncarbonated sample material. For this research an attempt was made to minimise the influence of these effects. Therefore, differential curves from DTG-results of non-carbonated areas and areas with various states of carbonation of the same sample material were calculated and evaluated. Concretes based on three different types of cement were produced and stored under accelerated carbonation conditions (1 % CO2 in air). The required sample material was obtained by cutting slices from various depth of previously CO2-treated specimen and subsequent grinding. During the sample preparation, a special attention was paid that no additional carbonation processes took place. As reference method for the determination of the carbonation depth the sprayed application of phenolphthalein solution was carried out. Microscopic analysis where examined to confirm the assumptions made previously. Furthermore, the observed effect of encapsulation of calcium hydroxide by carbonates caused by the accelerated carbonation conditions was examined more closely. KW - Microscopy KW - Accelerated carbonation KW - Carbonation behaviour KW - Concrete KW - Thermal Analysis PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-530571 DO - https://doi.org/10.1007/s10973-021-10966-1 VL - 147 IS - 11 SP - 1 EP - 14 PB - Springer AN - OPUS4-53057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sigrüner, M. A1 - Hüsken, Götz A1 - Pirskawetz, Stephan A1 - Herz, J. A1 - Muscat, D. A1 - Strübbe, N. T1 - Pull-out behavior of polymer fibers in concrete N2 - The bond between polymer fibers and the surrounding cementitious matrix is essential for the development of concrete reinforcement. The single fiber pull-out test (SFPT) is the standard characterization technique for testing the bond strength. However, the different phases of debonding cannot be distinguished by the SFPT. This study investigates the debonding of different polymer fibers from the surrounding cementitious matrix with a modified SFPT and proposes methods to change the SFPT setup to generate more valuable information on the debonding mechanism. The SFPT was equipped with linear variable differential transformers (LVDT), digital image correlation (DIC) and acoustic emission (AE) analysis. The results demonstrate that the modified SFPT allows a better understanding of the different phases of debonding during fiber pull-out. Furthermore, bond strength values calculated by different methods reveal that the chemical bond of the investigated polymers is not different as reported by previous studies. Deformation measurements performed using LVDTs and DIC are suitable measuring techniques to characterize the debonding mechanism in SFPT. A correlation between recorded AE and debonding phases was not found. KW - Polymer Fibres KW - Concrete KW - Pull-Out Behaviour KW - Debonding Mechanism PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-582918 DO - https://doi.org/10.1002/pol.20230264 SN - 2642-4169 SP - 1 EP - 13 PB - Wiley Periodicals, LLC. AN - OPUS4-58291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weise, Frank A1 - von Werder, Julia A1 - Manninger, Tanja A1 - Maier, Bärbel A1 - Fladt, Matthias A1 - Simon, Sebastian A1 - Gardei, Andre A1 - Höhnel, Desirée A1 - Pirskawetz, Stephan A1 - Meng, Birgit T1 - A multiscale and multimethod approach to assess and mitigate concrete damage due to alkali-silica reaction N2 - Alkali-silica reaction (ASR) is a chemical reaction within concrete which can lead over time to cracking and spalling. Due to the complexity of the problem, it still causes damage to concrete constructions worldwide. The publication aims to illustrate the interdisciplinary research of the German Federal Institute for Materials Research and Testing (BAM) within the last 20 years, considering all aspects of ASR topics from the macro to the micro level. First, methods for characterization and assessment of ASR risks and reaction products used at BAM are explained and classified in the international context. Subsequently the added value of the research approach by combining different, preferably nondestructive, methods across all scales is explained using specific examples from a variety of research projects. Aspects covered range from the development of new test-setups to assess aggregate reactivity, to analysis of microstructure and reaction products using microscopical, spectroscopical and X-ray methods, to the development of a testing methodology for existing concrete pavements including in-depth analysis of the visual damage indicator and the de-icing salt input using innovative testing techniques. Finally, research regarding a novel avoidance strategy that makes use of internal hydrophobization of the concrete mix is presented. KW - Mitigation strategies KW - Concrete KW - Damage analysis KW - Alkali silica reaction KW - Road pavement KW - Accelerated testing KW - Non-destructive testing KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:101:1-2022052515100075090235 DO - https://doi.org/10.1002/adem.202101346 SN - 1527-2648 VL - 24 IS - 6 SP - 1 EP - 36 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mezhov, Alexander A1 - Bright, Asante A1 - Schmidt, Wolfram T1 - Increasing the Incorporation of CO2-Sequestering Materials in Concrete N2 - Concrete is the most widely used construction material accounting for approximately half of all human production throughout history. The production of one ton of cement emits around 600 kg of CO2. With a global cement production estimate of 4.2 billion tons, this results in about 2.5 billion tons of CO2 emissions. This accounts for roughly 7.2% of the total global carbon emissions in 2021. Strategies to decrease carbon emissions in the cement and concrete industry include carbon capture and storage (CCS), reduced binders like ordinary Portland cement (OPC) clinker and optimizing material use through improved processes and structural design. This also means changing architectural vision [6], avoiding concrete where its structural performance is not required and use alternative materials instead, and optimizing the communication among the entire production value chain. T2 - 1st International Conference on Net-Zero Built Environment: Innovations in Materials, Structures, and Management Practices (Net-Zero Future 2024) CY - Oslo, Norway DA - 19.06.2025 KW - Concrete KW - CO2-Sequestering PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638531 DO - https://doi.org/10.1007/978-3-031-69626-8_4 VL - 237 SP - 39 EP - 48 PB - Springer Nature Switzerland AG CY - Schweiz AN - OPUS4-63853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kruschwitz, Sabine A1 - Munsch, Sarah Mandy A1 - Telong, Melissa A1 - Schmidt, Wolfram A1 - Bintz, Thilo A1 - Fladt, Matthias A1 - Stelzner, Ludwig T1 - The NMR core analyzing TOMograph: A multi-functional tool for non-destructive testing of building materials N2 - NMR is becoming increasingly popular for the investigation of building materials as it is a non-invasive technology that does not require any sample preparation nor causes damage to the material. Depending on the specific application it can offer insights into properties like porosity and spatial saturation degree as well as pore structure. Moreover it enables the determination of moisture transport properties and the (re-)distribution of internal moisture into different reservoirs or chemical phases upon damage and curing. However, as yet most investigations were carried out using devices originally either designed for geophysical applications or the analysis of rather homogeneous small scale (< 10 mL) samples. This paper describes the capabilities of an NMR tomograph, which has been specifically optimized for the investigation of larger, heterogeneous building material samples (diameters of up to 72 mm, length of up to 700 mm) with a high flexibility due to interchangeable coils allowing for a high SNR and short echo times (50 - 80 m s). KW - Fire spalling KW - Moisture transport KW - Concrete KW - Cement hydration KW - Sensitivity KW - Supplementary cementitous materials KW - Frost salt attack PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573755 DO - https://doi.org/10.1016/j.mrl.2023.03.004 SN - 2097-0048 VL - 3 IS - 3 SP - 207 EP - 219 PB - Elsevier B.V. AN - OPUS4-57375 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Bernal, S. A. T1 - RILEM TC CUC: Carbon dioxide uptake by concrete during and after service life – Opening Letter N2 - The ability of cement to chemically bind CO2 in a carbonation reaction enables the material to act as a carbon sink, which could partly account for offsetting the CO2 emissions associated with cement production. In response to the many open questions in this context, the RILEM Technical Committee CUC was created in May 2024. The focus of the TC will be to facilitate discussions regarding the current approaches to estimate the CO2 uptake by cementitious materials (concrete and other construction products) during and after service life. This Opening Letter presents aspects of the motivation to establish the TC, a brief overview of the state of the art in the field, the scheduled work programme, and the anticipated impact of the TC outputs. Though it is not intended to be an exhaustive discussion of the challenges to be addressed, from what is summarized in this letter, it is clear that work is required to base estimates of CO2 uptake by cementitious materials on a data set that is as extensive, accurate and forward-looking as possible. It is anticipated that the inclusion of interdisciplinary perspectives and data from academia and industry will enable progress in the field. KW - Cement KW - Concrete KW - Recarbonation KW - Carbon dioxide uptake KW - Carbonation rate PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623724 DO - https://doi.org/10.21809/rilemtechlett.2024.208 SN - 2518-0231 VL - 9 SP - 61 EP - 67 PB - RILEM AN - OPUS4-62372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernal, S. A. A1 - Dhandapani, Y. A1 - Elakneswaran, Y. A1 - Gluth, Gregor A1 - Gruyaert, E. A1 - Juenger, M. C. G. A1 - Lothenbach, B. A1 - Olonade, K. A. A1 - Sakoparnig, M. A1 - Shi, Z. A1 - Thiel, C. A1 - Van den Heede, P. A1 - Vanoutrive, H. A1 - von Greve-Dierfeld, S. A1 - De Belie, N. A1 - Provis, J. L. T1 - Report of RILEM TC 281-CCC: A critical review of the standardised testing methods to determine carbonation resistance of concrete N2 - The chemical reaction between CO2 and a blended Portland cement concrete, referred to as carbonation, can lead to reduced performance, particularly when concrete is exposed to elevated levels of CO2 (i.e., accelerated carbonation conditions). When slight changes in concrete mix designs or testing conditions are adopted, conflicting carbonation results are often reported. The RILEM TC 281-CCC ‘Carbonation of Concrete with Supplementary Cementitious Materials’ has conducted a critical analysis of the standardised testing methodologies that are currently applied to determine carbonation resistance of concrete in different regions. There are at least 17 different standards or recommendations being actively used for this purpose, with significant differences in sample curing, pre-conditioning, carbonation exposure conditions, and methods used for determination of carbonation depth after exposure. These differences strongly influence the carbonation depths recorded and the carbonation coefficient values calculated. Considering the importance of accurately determining carbonation potential of concrete, not just for predicting their durability performance, but also for determining the amount of CO2 that concrete can re-absorb during or after its service life, it is imperative to recognise the applicability and limitations of the results obtained from different tests. This will enable researchers and practitioners to adopt the most appropriate testing methodologies to evaluate carbonation resistance, depending on the purpose of the conclusions derived from such testing (e. g. materials selection, service life prediction, CO2 capture potential). KW - Concrete KW - Cement KW - Carbonation KW - Testing KW - Standards PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-609364 DO - https://doi.org/10.1617/s11527-024-02424-9 VL - 57 SP - 1 EP - 31 PB - Springer Nature AN - OPUS4-60936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Henning, Ricky A1 - Sturm, Patrick A1 - Keßler, S. A1 - Gluth, Gregor ED - Lothenbach, B. ED - Wieland, E. ED - Altmaier, M. T1 - Influence of salt aggregate on the degradation of hybrid alkaline cement (HAC) concretes in magnesium chloride-rich saline solution simulating evaporite rock N2 - Concretes produced from salt aggregate and hybrid alkaline cements, an alkali-activated slag/fly ash blend, or a Portland cement were exposed to a magnesium chloride-rich saline solution ([Mg2+] = 3.6 m, [Cl−] = 8.3 m), representing a solution formed after contact of surface water with evaporite rock (rock salt) in a nuclear waste repository. The hydration and deterioration of the concretes were studied with X-ray diffraction, thermogravimetric analysis, pH mapping and permeability measurements. The results show that calcium silicate hydrate (C-S-H) or sodium-substituted calcium aluminium silicate hydrate (C-N-A-S-H) and Friedel's salt were the major reaction products in the concretes prior to exposure to the saline solution. During exposure to the saline solution, increasing amounts of C-S-H/C-N-A-S-H dissolved, and gypsum and a secondary AFm phase formed. The durability of the concretes improved with increasing amounts of Portland clinker in the cements, due to the associated differences in permeability and chemical resistance. Nevertheless, a massive increase of permeability occurred for all concretes, likely caused by crack formation due to the formation of gypsum from anhydrite in the salt aggregate. Thus, the behavior of the concretes differed from, and was more complex than, the behavior of plain cement pastes. T2 - Joint 6th International Workshop on Mechanisms and Modelling of Waste/Cement Interactions (JCCW 2023) CY - Prague, Czech Republic DA - 20.11.2023 KW - Nuclear waste repository KW - Evaporite rock KW - Magnesium chloride brine KW - Concrete KW - Hybrid alkaline cement PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599928 DO - https://doi.org/10.1016/j.apgeochem.2024.106027 SN - 0883-2927 SN - 1872-9134 VL - 168 SP - 1 EP - 14 PB - Elsevier AN - OPUS4-59992 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tambara, R. F. A1 - Durlo Tambara, Luís Urbano A1 - Venquiaruto, S. D. A1 - Pereira da Costa, F. B. T1 - Evaluation of the mechanical performance and capillary absorption of concretes with incorporation of crystallizing admixtures and subjected to damage at early ages T1 - Avaliação do desempenho mecânico e absorção capilar de concretos com incorporação de aditivos cristalizante submetidos a danos nas primeiras idades N2 - This study assessed the self-healing phenomenon in the mechanical properties and capillary absorption of structural concretes. Two crystalline powder additives were evaluated, dosed according to the manufacturers’ recommendations. Crystalline additives increase the density of the C-S-H gel and form insoluble crystals, effectively blocking fissures. Three concrete mixes were produced: a reference mix, additive-X with 0.8%, and additive-Y with 2.0%, relative to the mass of cement. 75% of the rupture load was applied at 3- and 14-days to induce microfissures for comparison with the reference mix. Subsequently, self-healing was assessed at 28- and 76-days. The property of axial compressive strength was determined at 28-days, revealing that crystalline additives contributed to an average increase of 12% in this property. While the age of loading did not significantly impact axial compressive strength, there were significant variations among the types of additives studied, as indicated by ANOVA. Water absorption properties through capillarity were evaluated at 28- and 76-days, showing an average reduction of 42% in water absorption due to the use of crystalline additives. In conclusion, the inclusion of crystalline additives positively contributed to the self-healing of the studied concretes, suggesting a partial recovery of microfissures. N2 - Esta pesquisa avaliou o fenômeno de autocicatrização nas propriedades mecânicas e absorção capilar de concretos estruturais. Foram avaliados dois aditivos cristalizantes em pó, dosados de acordo com o teor recomendado pelos fabricantes. Aditivos cristalizantes aumentam a densidade do gel C-S-H e formam cristais insolúveis, bloqueando fissuras. Três traços de concreto foram produzidos: referência, aditivo-X com 0,8% e aditivo-Y com 2,0% em relação a massa do cimento. Aplicou-se 75% da carga de ruptura aos 3- e 14-dias para gerar microfissuras e comparar com a referência. Posteriormente, a autocicatrização foi avaliada aos 28- e 76-dias. A propriedade de resistência à compressão axial foi determinada aos 28-dias, revelando que os aditivos cristalizantes contribuíram para um aumento médio de 12% desta propriedade. A idade do carregamento dos concretos não apresentou um impacto significativo na resistência à compressão axial, mas apontou resultados significativos entre os tipos de aditivos estudados, conforme ANOVA. As propriedades de absorção de água por capilaridade foram avaliadas aos 28- e 76-dias, indicando uma redução de absorção de água média de 42% devido ao uso dos aditivos cristalizantes. Em conclusão, a incorporação dos aditivos cristalizantes contribuiu de maneira positiva para a autocicatrização dos concretos estudados, indicando uma recuperação parcial das microfissuras. KW - Self-healing KW - Crystalline admixture KW - Concrete KW - Cracks PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599140 DO - https://doi.org/10.1590/1517-7076-RMAT-2023-0355 SN - 1517-7076 VL - 29 IS - 1 SP - 1 EP - 20 CY - Rio de Janeiro AN - OPUS4-59914 LA - por AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Peterson, K. A1 - Pipilikaki, P. A1 - Valcke, S. L. A. A1 - Ye, G. A1 - Zuo, Y. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: carbonation and chloride penetration testing of alkali-activated concretes N2 - Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested. KW - Alkali-activated materials KW - Durability KW - Carbonation KW - Chloride penetration KW - Concrete PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-504045 DO - https://doi.org/10.1617/s11527-020-1449-3 SN - 1359-5997 SN - 1871-6873 VL - 53 IS - 1 SP - 21 PB - Springer Nature AN - OPUS4-50404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, S. A1 - Samson, G. A1 - Masi, G. A1 - Achenbach, R. A1 - Bastidas, D. M. A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Criado, M. A1 - Cyr, M. A1 - Gartner, N. A1 - von Greve-Dierfeld, S. A1 - Legat, A. A1 - Nikoonasab, Ali A1 - Provis, J. L. A1 - Raupach, M. A1 - Gluth, Gregor T1 - Application of electrochemical methods for studying steel corrosion in alkali-activated materials N2 - Alkali-activated materials (AAMs) are binders that can complement and partially substitute the current use of conventional cement. However, the present knowledge about how AAMs protect steel reinforcement in concrete elements is incomplete, and uncertainties exist regarding the application of electrochemical methods to investigate this issue. The present review by EFC WP11-Task Force ‘Corrosion of steel in alkali-activated materials’ demonstrates that important differences exist between AAMs and Portland cement, and between different classes of AAMs, which are mainly caused by differing pore solution compositions, and which affect the outcomes of electrochemical measurements. The high sulfide concentrations in blast furnace slag-based AAMs lead to distinct anodic polarisation curves, unusually low open circuit potentials, and low polarisation resistances, which might be incorrectly interpreted as indicating active corrosion of steel reinforcement. No systematic study of the influence of the steel–concrete interface on the susceptibility of steel to corrosion in AAMs is available. Less common electrochemical methods present an opportunity for future progress in the field. KW - Alkali-activated materials KW - Reinforcement corrosion KW - Steel corrrosion KW - Electrochemical methods KW - Concrete PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572241 DO - https://doi.org/10.1002/maco.202313743 SN - 1521-4176 VL - 74 IS - 7 SP - 988 EP - 1008 PB - Wiley-VCH CY - Weinheim AN - OPUS4-57224 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vollpracht, A. A1 - Gluth, Gregor A1 - Rogiers, B. A1 - Uwanuakwa, I. D. A1 - Phung, Q. T. A1 - Villagran Zaccardi, Y. A1 - Thiel, C. A1 - Vanoutrive, H. A1 - Etcheverry, J. M. A1 - Gruyaert, E. A1 - Kamali-Bernard, S. A1 - Kanellopoulos, A. A1 - Zhao, Z. A1 - Martins, I. M. A1 - Rathnarajan, S. A1 - De Belie, N. T1 - Report of RILEM TC 281-CCC: insights into factors affecting the carbonation rate of concrete with SCMs revealed from data mining and machine learning approaches N2 - The RILEM TC 281–CCC ‘‘Carbonation of concrete with supplementary cementitious materials’’ conducted a study on the effects of supplementary cementitious materials (SCMs) on the carbonation rate of blended cement concretes and mortars. In this context, a comprehensive database has been established, consisting of 1044 concrete and mortar mixes with their associated carbonation depth data over time. The dataset comprises mix designs with a large variety of binders with up to 94% SCMs, collected from the literature as well as unpublished testing reports. The data includes chemical composition and physical properties of the raw materials, mix-designs, compressive strengths, curing and carbonation testing conditions. Natural carbonation was recorded for several years in many cases with both indoor and outdoor results. The database has been analysed to investigate the effects of binder composition and mix design, curing and preconditioning, and relative humidity on the carbonation rate. Furthermore, the accuracy of accelerated carbonation testing as well as possible correlations between compressive strength and carbonation resistance were evaluated. One approach to summerise the physical and chemical resistance in one parameter is the ratio of water content to content of carbonatable CaO (w/CaOreactive ratio). The analysis revealed that the w/CaOreactive ratio is a decisive factor for carbonation resistance, while curing and exposure conditions also influence carbonation. Under natural exposure conditions, the carbonation data exhibit significant variations. Nevertheless, probabilistic inference suggests that both accelerated and natural carbonation processes follow a square-root-of-time behavior, though accelerated and natural carbonation cannot be converted into each other without corrections. Additionally, a machine learning technique was employed to assess the influence of parameters governing the carbonation progress in concretes. KW - Carbonation KW - Supplementary cementitious materials KW - Concrete PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-614388 DO - https://doi.org/10.1617/s11527-024-02465-0 SN - 1871-6873 SN - 1359-5997 VL - 57 IS - 9 SP - 1 EP - 33 PB - Springer Nature AN - OPUS4-61438 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernal, S. A. A1 - Angst, U. M. A1 - Provis, J. L. A1 - Thiel, C. A1 - Gluth, Gregor A1 - Villagran-Zaccardi, Y. A1 - De Belie, N. T1 - Recommendation of RILEM TC 281-CCC: RILEM CPC-18R1—guideline for measuring the carbonation depth of hardened concrete using a pH indicator solution N2 - This recommendation provides a procedure for determining the carbonation depth on the surface of concrete by applying a pH indicator. This includes definitions of carbonation, carbonation depth and carbonation front, as well as descriptions of the different pH indicator solutions that can be used. Recommendations for testing laboratory-prepared specimens and those obtained from concrete structures are also given. This involves guidelines for sample preparation and/or extraction, CO2 exposure duration, carbonation depth determination and reporting of results. A section on data interpretation is also provided, as carbonation results are used for determining durability of concrete, as well as a criterion for materials selection or for carbon uptake calculations. The new Recommendation CPC-18R1 is intended to supersede the former RILEM recommendation CPC-18, particularly when prescribed as the preferred method for evaluating and reporting carbonation depths. KW - Carbonation KW - Concrete KW - pH indicator KW - Phenolphthalein KW - Testing PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-656191 DO - https://doi.org/10.1617/s11527-026-02966-0 SN - 1359-5997 SN - 1871-6873 VL - 59 IS - 3 SP - 1 EP - 11 PB - Springer Nature AN - OPUS4-65619 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -