TY - JOUR A1 - Häßler, Dustin A1 - Mund, Maximilian A1 - Daus, Lars-Hendrik A1 - Hothan, Sascha A1 - Schaumann, Peter A1 - Schartel, Bernhard T1 - Durability of intumescent coatings and recommendations for test concepts for a working life of more than 10 years N2 - It is an essential requirement for all building products to ensure durability of their fire safety. Throughout the working life of products, intumescent coatings are aged by certain climatic factors. To predict a lifetime of several years, generally the behaviour of the intumescent coating is extrapolated based on accelerated artificial ageing. The established German and European procedures to assess the durability assume a working life of at least 10 years. For a longer period, additional evidence is required; yet the procedure and the specifications to justify this are not described. In addition to addressing this formal lack, from a scientific point of view it is necessary to investigate the degradation of intumescent coatings in detail and to propose a reliable test concept to assess durability for more than 10 years. This paper summarises the existing knowledge about the ageing of intumescent coatings. The results of various demanding weathering approaches are presented for two intumescent coatings tested in a joint research project. Moreover, formulations with a reduced amount of functionally relevant components were analysed to gain insight into the associated effects. Derived from these research results and knowledge, recommendations are proposed to assess the durability of intumescent coatings for more than 10 years based on a combination of verifications. KW - Ageing KW - Fire protection KW - Intumescent coating KW - Steel construction KW - Working life PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-603852 DO - https://doi.org/10.1016/j.firesaf.2024.104173 SN - 0379-7112 VL - 146 SP - 1 EP - 10 PB - Elsevier B.V. AN - OPUS4-60385 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Understanding the recovery behaviour and the degradative processes of EPDM during ageing N2 - Recovery is an important measure for seal applications representing to which extent the elastomer regains its initial shape after deformation and release of an applied force. Compression set (CS) indicates the degree of recovery. Ethylene propylene diene rubber (EPDM) was aged at 75 ◦C, 100 ◦C, 125 ◦C and 150 ◦C for different ageing times up to five years and compression set measurements were performed at different times after disassembly and after additional tempering. Short- and long-term recovery up to one year after release for samples aged at 125 ◦C and 150 ◦C was also studied. To assess the curvature in the Arrhenius diagram that may occur due to non-sufficiently aged specimens, a degradation-rate based model was fitted to the CS data after tempering. For each ageing temperature, two decay fit functions were proposed, each with an activation energy and a corresponding degradative process. The influence of ageing on the leak-tightness after fast small partial release is investigated and estimated through the analysis of the shift factors from time temperature superposition (TTS) of CS measurements at different times after disassembly. Shift factors of CS measurement after 1 s and after additional tempering are in good agreement. KW - Compression set KW - Ageing KW - Recovery KW - Degradative processes KW - Leakage rate PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-573699 DO - https://doi.org/10.1016/j.polymertesting.2023.107987 SN - 0142-9418 VL - 121 SP - 107987 PB - Elsevier Ltd. AN - OPUS4-57369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, M. A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Oxidative ageing of elastomers: experiment and modelling N2 - During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and two ageing temperatures of 125 ◦ C and 150 ◦ C. To exclude possible diffusion-limited oxidation (DLO) effects that can distort the data, IRHD microhardness measurements were taken over the cross section of compressed O-rings. Continuous stress relaxation measurements were taken on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments. KW - Compression Set KW - Compression stress relaxation KW - Modelling KW - Ageing KW - Microhardness PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-609332 DO - https://doi.org/10.1007/s00161-022-01093-9 VL - 36 SP - 289 EP - 297 PB - Springer Nature AN - OPUS4-60933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, Maha A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Scission, cross-linking, and physical relaxation during thermal degradation of elastomers N2 - Elastomers are susceptible to chemical ageing, i.e., scission and cross-linking, at high temperatures. This thermally driven ageing process affects their mechanical properties and leads to limited operating time. Continuous and intermittent stress Relaxation measurements were conducted on ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) samples for different ageing times and an ageing temperature of 125 °C. The contributions of chain scission and cross-linking were analysed for both materials at different ageing states, elucidating the respective ageing mechanisms. Furthermore, compression set experiments were performed under various test conditions. Adopting the two-network model, compression set values were calculated and compared to the measured data. The additional effect of physical processes to scission and cross-linking during a long-term thermal exposure is quantified through the compression set analysis. The characteristic times relative to the degradation processes are also determined. KW - Ageing KW - Scission KW - Cross-linking KW - Compression set KW - Physical relaxation PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-486091 DO - https://doi.org/10.3390/polym11081280 SN - 2073-4360 VL - 11 IS - 8 SP - 1280, 1 EP - 12 PB - MDPI AN - OPUS4-48609 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -