TY - JOUR A1 - Artinov, Antoni A1 - Karkhin, V. A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - A General Analytical Solution for Two-Dimensional Columnar Crystal Growth during Laser Beam Welding of Thin Steel Sheets N2 - A technique for calculating the main solidification parameters for a two-dimensional columnar crystal growth during complete penetration laser beam welding of thin steel sheets was developed. Given that the weld pool interface is described by Lamé curves (superellipses) within the horizontal plane of growth, general analytical solutions were derived for the geometry of the crystal axis and the corresponding growth rate and cross-sectional area of the crystal. A dimensionless analysis was performed to provide insights on the dependence of the solidification parameters on the shape and dimensions of the rear part of the weld pool boundary. The derived solutions were applied for the case of complete penetration laser beam keyhole welding of 2 mm thick 316L austenitic chromium-nickel steel sheets. It was shown that the reconstruction of the weld pool boundary with Lamé curves provides higher accuracy and flexibility compared to results obtained with elliptical functions. The validity of the proposed technique and the derived analytical solutions was backed up by a comparison of the obtained solutions to known analytical solutions and experimentally determined shapes and sizes of the crystals on the top surface of the sheet. The dimensions of the calculated crystal axis correlated well with the experimentally obtained results. KW - General analytical solutions KW - Two-dimensional solidification KW - Columnar crystal growth KW - Lamé curves KW - Laser beam welding PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-576788 DO - https://doi.org/10.3390/app13106249 IS - 10 SP - 1 EP - 10 ET - 13 AN - OPUS4-57678 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Prabitz, Konstantin Manuel A1 - Antretter, Thomas A1 - Rethmeier, Michael A1 - El-Sari, Bassel A1 - Schubert, Holger A1 - Hilpert, Benjamin A1 - Gruber, Martin A1 - Sierlinger, Robert A1 - Ecker, Werner T1 - Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds N2 - Zinc-based surface coatings are widely applied with high-strength steels in automotive industry. Some of these base materials show an increased brittle cracking risk during loading. It is necessary to examine electrogalvanized and uncoated samples of a high strength steel susceptible to liquid metal embrittlement during spot welding with applied external load. Therefore, a newly developed tensile test method with a simultaneously applied spot weld is conducted. A fully coupled 3D electrical, thermal, metallurgical and mechanical finite element model depicting the resistant spot welding process combined with the tensile test conducted is mandatory to correct geometric influences of the sample geometry and provides insights into the sample’s time dependent local loading. With increasing external loads, the morphology of the brittle cracks formed is affected more than the crack depth. The validated finite element model applies newly developed damage indicators to predict and explain the liquid metal embrittlement cracking onset and development as well as even ductile failure. KW - Resistance spot welding KW - Finite element simulation KW - Advanced high-strength steel KW - Liquid metal embrittlement KW - Damage prediction KW - Tensile resistance spot welding experiment PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594848 DO - https://doi.org/10.1007/s40194-024-01696-7 SN - 0043-2288 SP - 1 EP - 10 PB - Springer Science and Business Media LLC AN - OPUS4-59484 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Strobl, Dominic A1 - Unger, Jörg F. A1 - Ghnatios, C. A1 - Klawoon, Alexander A1 - Pittner, Andreas A1 - Rethmeier, Michael A1 - Robens-Radermacher, Annika T1 - Efficient bead-on-plate weld model for parameter estimation towards effective wire arc additive manufacturing simulation N2 - Despite the advances in hardware and software techniques, standard numerical methods fail in providing real-time simulations, especially for complex processes such as additive manufacturing applications. A real-time simulation enables process control through the combination of process monitoring and automated feedback, which increases the flexibility and quality of a process. Typically, before producing a whole additive manufacturing structure, a simplified experiment in the form of a beadon-plate experiment is performed to get a first insight into the process and to set parameters suitably. In this work, a reduced order model for the transient thermal problem of the bead-on-plate weld simulation is developed, allowing an efficient model calibration and control of the process. The proposed approach applies the proper generalized decomposition (PGD) method, a popular model order reduction technique, to decrease the computational effort of each model evaluation required multiple times in parameter estimation, control, and optimization. The welding torch is modeled by a moving heat source, which leads to difficulties separating space and time, a key ingredient in PGD simulations. A novel approach for separating space and time is applied and extended to 3D problems allowing the derivation of an efficient separated representation of the temperature. The results are verified against a standard finite element model showing excellent agreement. The reduced order model is also leveraged in a Bayesian model parameter estimation setup, speeding up calibrations and ultimately leading to an optimized real-time simulation approach for welding experiment using synthetic as well as real measurement data. KW - Proper generalized decomposition KW - Model order reduction KW - Hardly separable problem KW - Additive manufacturing KW - Model calibration KW - Wire arc additive manufacturing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596502 DO - https://doi.org/10.1007/s40194-024-01700-0 SN - 0043-2288 SP - 1 EP - 18 PB - Springer AN - OPUS4-59650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Fasselt, Janek Maria A1 - Kruse, Tobias A1 - Klötzer, Christian A1 - Kleba-Ehrhardt, Rafael A1 - Choma, Tomasz A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Using ultrasonic atomization to recycle aluminium bronze chips for additive laser directed energy deposition N2 - Abstract In the post-processing of large maritime components, a considerable amount of waste in the form of milling and grinding chips is produced. At the same time, additive manufacturing technologies have shown great potential in producing high-volume parts for maritime applications, allowing novel design approaches and short lead times. In this context, this study presents a sustainable approach to recycle and use aluminium bronze waste material, generated during post-processing of large cast ship propellers, as feedstock for laser-powder directed energy deposition. The recycling technology used to produce powder batches is inductive re-melting in combination with ultrasonic atomization. The derived metal powders are characterized using digital image analysis, powder flowability tests, scanning electron microscopy as well as energy dispersive X-ray spectroscopy. Compared to conventional metal powders produced by gas atomization, the recycled material shows excellent sphericity and a powder size distribution with a higher content of finer and coarser particles. Metallographic sections of deposited additively produced specimens show an increased hardness and reduced ductility, but also competitive densities and higher yield and ultimate tensile strength compared to cast material. The process chain shows high potential for the maritime sector to enable circular and sustainable manufacturing. KW - Industrial and Manufacturing Engineering PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-594444 DO - https://doi.org/10.1088/1757-899X/1296/1/012036 VL - 1296 IS - 1 SP - 1 EP - 11 PB - IOP Publishing AN - OPUS4-59444 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Rethmeier, Michael T1 - Influence of the free surface reconstruction on the spatial laser energy distribution in high power laser beam welding modeling N2 - An accurate and efficient description of the spatial distribution of laser energy is a crucial factor for the modeling of laser material processing, e.g., laser welding, laser cutting, or laser-based additive manufacturing. In this study, a 3D heat transfer and fluid flow model coupled with the volume-of-fluid algorithm for free surface tracking is developed for the simulation of molten pool dynamics in high-power laser beam welding. The underlying laser-material interactions, i.e., the multiple reflections and Fresnel absorption, are considered by a raytracing method. Two strategies of free surface reconstruction used in the ray-tracing method are investigated: a typical piecewise linear interface calculation (PLIC)-based method and a novel localized level-set method. The PLIC-based method is discrete, resulting in noncontinuous free surface reconstruction. In the localized level-set method, a continuous free surface is reconstructed, and, thus, the exact reflection points can be determined. The calculated spatial laser energy distribution and the corresponding molten pool dynamics from the two methods are analyzed and compared. The obtained numerical results are evaluated with experimental measurements to assure the validity of the proposed model. It is found that distinct patterns of the beam multiple reflections are obtained with the different free surface reconstructions, which shows significant influence not only on the molten pool behaviors but also on the localized keyhole dynamics. KW - Laser beam welding KW - Laser energy distribution KW - Weld pool dynamics KW - Ray teacing PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-562429 DO - https://doi.org/10.2351/7.0000739 SN - 1042-346X VL - 34 IS - 4 SP - 042023-1 EP - 042023-8 PB - Laser Institute of America CY - Orlando, Fla. AN - OPUS4-56242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Life Cycle Assessment of Fusion Welding Processes - A Case Study of Resistance Spot Welding Versus Laser Beam Welding N2 - The high amount of resource consumption of fusion welding processes offers the potential to reduce their environmental impact. While the driving forces are known froma qualitative perspective, the quantitative assessment of the crucial parameters is not a trivial task. Therefore, herein, a welding-specific methodology to utilize life cycle assessment as a tool for evaluating the environmental impact of fusion welding processes is presented. In this context, two welding processes, resistance spot welding and laser beam welding, are analyzed for two different use cases. These comprise the welding of shear test specimens and a cap profile made of electrogalvanized sheets of DC 05þ ZE (1.0312) as representative of an automotive application. For both welding processes, the main influences on the resulting environmental impact categories are evaluated and compared. The requirements for ecological efficient welding processes are discussed and implemented. KW - Resistance spot welding KW - Carbon dioxide footprint KW - Environmental impact categories KW - Laser beam welding KW - Life cycle assessment PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-566458 DO - https://doi.org/10.1002/adem.202101343 SN - 1438-1656 VL - 24 IS - 6 SP - 1 EP - 14 PB - Wiley-VCH CY - Weinheim AN - OPUS4-56645 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huo, W. A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, K. T1 - Strain Prediction Using Deep Learning during Solidification Crack Initiation and Growth in Laser Beam Welding of Thin Metal Sheets N2 - The strain field can reflect the initiation time of solidification cracks during the welding process. The traditional strain measurement is to first obtain the displacement field through digital image correlation (DIC) or optical flow and then calculate the strain field. The main disadvantage is that the calculation takes a long time, limiting its suitability to real-time applications. Recently, convolutional neural networks (CNNs) have made impressive achievements in computer vision. To build a good prediction model, the network structure and dataset are two key factors. In this paper, we first create the training and test sets containing welding cracks using the controlled tensile weldability (CTW) test and obtain the real strain fields through the Lucas–Kanade algorithm. Then, two new networks using ResNet and DenseNet as encoders are developed for strain prediction, called StrainNetR and StrainNetD. The results show that the average endpoint error (AEE) of the two networks on our test set is about 0.04, close to the real strain value. The computation time could be reduced to the millisecond level, which would greatly improve efficiency. KW - Convolutional neural network KW - Strain fields prediction KW - Laser beam welding KW - Solidification cracking PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-570565 DO - https://doi.org/10.3390/app13052930 VL - 13 IS - 5 SP - 1 EP - 15 PB - MDPI AN - OPUS4-57056 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huo, Wenjie A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - Detection of solidification crack formation in laser beam welding videos of sheet metal using neural networks N2 - AbstractLaser beam welding has become widely applied in many industrial fields in recent years. Solidification cracks remain one of the most common welding faults that can prevent a safe welded joint. In civil engineering, convolutional neural networks (CNNs) have been successfully used to detect cracks in roads and buildings by analysing images of the constructed objects. These cracks are found in static objects, whereas the generation of a welding crack is a dynamic process. Detecting the formation of cracks as early as possible is greatly important to ensure high welding quality. In this study, two end-to-end models based on long short-term memory and three-dimensional convolutional networks (3D-CNN) are proposed for automatic crack formation detection. To achieve maximum accuracy with minimal computational complexity, we progressively modify the model to find the optimal structure. The controlled tensile weldability test is conducted to generate long videos used for training and testing. The performance of the proposed models is compared with the classical neural network ResNet-18, which has been proven to be a good transfer learning model for crack detection. The results show that our models can detect the start time of crack formation earlier, while ResNet-18 only detects cracks during the propagation stage. KW - Artificial Intelligence KW - Software PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586116 DO - https://doi.org/10.1007/s00521-023-09004-y SN - 0941-0643 VL - 35 IS - 34 SP - 24315 EP - 24332 PB - Springer Science and Business Media LLC AN - OPUS4-58611 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bachmann, Marcel A1 - Artinov, Antoni A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Rethmeier, Michael T1 - Challenges in dynamic heat source modeling in high-power laser beam welding N2 - The amount of absorbed energy in the keyhole as well as its spatial and temporal distribution is essential to model the laser beam welding process. The recoil pressure, which develops because of the evaporation process induced by the absorbed laser energy at the keyhole wall, is a key determining factor for the macroscopic flow of the molten metal in the weld pool during high-power laser beam welding. Consequently, a realistic implementation of the effect of laser radiation on the weld metal is crucial to obtain reliable and accurate simulation results. In this paper, we discuss manyfold different improvements on the laser-material interaction, namely, the ray tracing method, in the numerical simulation of the laser beam welding process. The first improvement relates to locating the exact reflection points in the ray tracing method using a so-called cosine condition in the determination algorithm for the intersection of reflected rays and the keyhole surface. A second correction refers to the numerical treatment of the Gaussian distribution of the laser beam, whose beam width is defined by a decay of the laser intensity by a factor of 1/e2, thus ignoring around 14% of the total laser beam energy. In the third step, the changes in the laser radiation distribution in the vertical direction were adapted by using different approximations for the converging and the diverging regions of the laser beam, thus mimicking the beam caustic. Finally, a virtual mesh refinement was adopted in the ray tracing routine. The obtained numerical results were validated with experimental measurements. KW - Laser beam welding KW - Laser energy distribution KW - Ray tracing KW - Numerical modeling PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-584748 DO - https://doi.org/10.2351/7.0001079 VL - 35 IS - 4 SP - 1 EP - 9 PB - Laser Institute of America AN - OPUS4-58474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - El-Batahgy, Abdel-Monem A1 - Gumenyuk, Andrey A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Application of Hybrid Laser Arc Welding for Construction of LNG Tanks Made of Thick Cryogenic 9% Ni Steel Plates N2 - Hybrid laser-arc welding (HLAW) was applied for butt welding of 14.5 mm thick plates of ferritic cryogenic steel X8Ni9 containing 9% Ni, which is used for manufacturing storage and transport facilities of liquefied natural gas (LNG). The weld seam formation and the achievable metallurgical and mechanical properties of the hybrid welds were investigated experimentally for two types of filler wire, an austenitic wire dissimilar to the base metal (BM) and an experimentally produced matching ferritic wire. Safe penetration and uniform distribution of the austenitic filler metal in the narrow hybrid weld could only be achieved in the upper, arcdominated part of the weld. The pronounced heterogeneous distribution of the austenitic filler metal in the middle part and in the root area of the weld could not ensure sufficient notched impact toughness of the weld metal (WM). As a result, a decrease in the impact energy down to 17±3 J was observed, which is below the acceptance level of ≥34 J for cryogenic applications. In contrast, the use of a matching ferritic filler wire resulted in satisfactory impact energy of the hybrid welds of up to 134±52 J at the concerned cryogenic temperature of -196 °C. The obtained results contribute to an important and remarkable conversion in automated manufacturing of LNG facilities. In other words, the results will help to develop a new laser-based welding technology, where both quality and productivity are considered.The efficiency of the developed welding process has been demonstrated by manufacturing a prototype where a segment of the inner wall of large size LNG storage tank was constructed. In this concern, hybrid laser arc welding was conducted in both horizontal (2G) and vertical (3G) positions as a simulation to the actual onsite manufacturing. The prototype was fabricated twice where its quality was confirmed based on non-destructive and destructive examinations. KW - Hardness KW - Hybrid Laser arc Welding KW - 9% Ni Steel KW - Fusion zone size KW - Microstructure KW - Tensile Strength KW - Impact Absorbed Energy PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586080 DO - https://doi.org/10.1007/s40516-023-00229-2 SP - 1 EP - 22 PB - Springer Nature AN - OPUS4-58608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, K. A1 - Meschut, G. A1 - Seitz, G. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - The Identification of a New Liquid Metal Embrittlement (LME) Type in Resistance Spot Welding of Advanced High Strength Steels on Reduced Flange Widths N2 - Liquid metal embrittlement (LME) cracking is a phenomenon observed during resistance spot welding (RSW) of zinc􀀀coated advanced high􀀀strength steels (AHSS) in automotive manufacturing. In this study, severe cracks are observed at the edge of the sheet under reduced flange widths. These cracks, traversing the AHSS sheet, culminate at the edge with a width of approximately 1.2 mm. Through combined numerical and experimental investigations, and material testing, these cracks are identified and validated as a new type of LME crack. The mechanism behind this crack formation is attributed to unique geometric conditions that, when compared to center welding, amplify radial material flow by ninefold to 0.87 mm. The resultant tangential tensile stresses approximate 760 MPa, which exceed the yield strength of the examined advanced high􀀀strength steel (AHSS) under heightened temperature conditions, and when combined with liquid zinc, promote the formation of this new type of LME crack. KW - Liquid metal embrittlement KW - Crack KW - Advanced high strength steels KW - Resistance spot welding KW - Simulation KW - Flange width PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586940 DO - https://doi.org/10.3390/met13101754 VL - 13 IS - 10 SP - 1 EP - 13 PB - MDPI AN - OPUS4-58694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical analysis of the effect of an oscillating metal vapor plume on the keyhole and molten pool behavior during deep penetration laser beam welding N2 - The effect of the oscillating metal vapor plume on the keyhole and molten pool behavior during the laser beam welding of AlMg3 aluminum alloys is investigated by experimental and numerical methods. The real-time height of the metal vapor plume is measured by high-speed camera observation. The obtained experimental results are used to evaluate the additional heating source and laser beam attenuation caused by the scattering and absorption based on the Beer–Lambert theory. Furthermore, the dynamic behavior of the metal vapor plume is incorporated into a 3D transient heat transfer and fluid flow model, coupled with the ray tracing method, for the laser beam welding of the AlMg3 alloy. It is found that additional heating resulting from the scattered and absorbed laser beam energy by the metal vapor plume significantly expands the shape of the molten pool on the top region. Moreover, the oscillating metal vapor plume caused the fluctuation of the high-temperature region in the molten pool. The probability of keyhole collapse at the bottom increases 17% due to the oscillating laser power induced by the laser beam attenuation. The internal interplay between the metal vapor plume, molten pool shape, and keyhole collapse is obtained. The developed model has been validated by experiments, which shows a good agreement. T2 - International Congress of Applications of Lasers & Electro-Optics 2023 CY - Chicago, IL, USA DA - 16.10.2023 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Oscillating vapor plume KW - Keyhole collapse PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-587978 DO - https://doi.org/10.2351/7.0001094 SN - 1938-1387 SN - 1042-346X VL - 35 IS - 4 SP - 1 EP - 10 PB - AIP Publishing CY - Melville, NY AN - OPUS4-58797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Experimental and numerical study on grain refinement in electromagnetic assisted laser beam welding of 5754 Al alloy N2 - Through experimental observation and auxiliary numerical simulation, this investigation studies the different types of grain refinement of 5754 aluminum alloy laser beam welding by applying a transverse oscillating magnetic field. Scanning electron microscope results have proved that the application of a magnetic field can reduce the average crystal branch width and increase its number. The interaction between the induced eddy current generated by the Seebeck effect and the applied external magnetic field produces a Lorentz force, which is important for the increase in the number of crystal branches. Based on the theory of dendrite fragmentation and the magnetic field-induced branches increment, the grain size reduction caused by the magnetic field is studied. Furthermore, the effects of the magnetic field are analyzed by combining a phase field method model and simulations of nucleation and grain growth. The grain distribution and average grain size after welding verify the reliability of the model. In addition, the introduction of a magnetic field can increase the number of periodic three-dimensional solidification patterns. In the intersection of two periods of solidification patterns, the metal can be re-melted and then re-solidified, which prevents the grains, that have been solidified and formed previously, from further growth and generates some small cellular grains in the new fusion line. The magnetic field increases the building frequency of these solidification structures and thus promotes this kind of grain refinement. KW - Laser beam welding KW - Magnetic field KW - Crystal branch development KW - Grain refinement KW - Periodic solidification pattern PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-584905 DO - https://doi.org/10.2351/7.0001085 SN - 1042-346X VL - 35 IS - 4 SP - 1 EP - 10 PB - AIP Publishing AN - OPUS4-58490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Straße, Anne A1 - Rethmeier, Michael A1 - Gumenyuk, Andrey T1 - Influence of edge‑deposited layers on mechanical and corrosion properties of laser beam welds of 15 mm thick AISI 2205 duplex stainless steel N2 - AISI 2205 duplex stainless steel is used in a variety of industries, including the chemical and petrochemical industries. This is due to its high tensile strength combined with good ductility and corrosion resistance. However, in laser beam welding, these properties are negatively afected by the high cooling rates typical of the welding process. The resulting higher ferrrite content in the weld metal than in the base material leads to a reduction in the ductility and corrosion resistance of the welded joint. To overcome this problem, in this study, thick plates were coated by direct energy deposition (DED) prior to laser beam welding, whereas a duplex powder mixture containing a higher nickel concentration was used as a coating material. To improve the weld quality for the proposed two-step process, a method of additional material deposition instead of conventional tack weld was investigated. The resulting welded joints showed a well-balanced austenite to ferrite ratio and their properties and microstructure were verifed by metallographic analysis, electron backscatter difraction and Charpy impact testing. Using the standard ASTM G48 test method, it was found that the corrosion resistance of the welds was improved by a factor of four in average compared to the conventionally welded joints. The resulting properties, such as good ductility and corrosion resistance, of the welds with pre-coated edges showed good agreement with those of the base metal and confrmed the proposed two-step process as a promising alternative to the conventional approaches for welding thick duplex stainless steel plates. KW - Laser metal deposition KW - Laser beam welding KW - Duplex steels PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581731 UR - https://rdcu.be/dlb6E DO - https://doi.org/10.1007/s40194-023-01567-7 SN - 0043-2288 SP - 1 EP - 12 PB - Springer AN - OPUS4-58173 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hartwig, Philipp A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Scheunemann, Lisa A1 - Schröder, Jörg A1 - Rethmeier, Michael T1 - A Physically Motivated Heat Source Model for Laser Beam Welding N2 - In this contribution, we present a physically motivated heat source model for the numerical modeling of laser beam welding processes. Since the calibration of existing heat source models, such as the conic or Goldak model, is difficult, the representation of the heat source using so-called Lamé curves has been established, relying on prior Computational Fluid Dynamics (CFD) simulations. Lamé curves, which describe the melting isotherm, are used in a subsequent finite-element (FE) simulation to define a moving Dirichlet boundary condition, which prescribes a constant temperature in the melt pool. As an alternative to this approach, we developed a physically motivated heat source model, which prescribes the heat input as a body load directly. The new model also relies on prior CFD simulations to identify the melting isotherm. We demonstrate numerical results of the new heat source model on boundary-value problems from the field of laser beam welding and compare it with the prior CFD simulation and the results of the Lamé curve model and experimental data. KW - Welding simulation KW - Heat source models KW - Laser beam welding KW - Thermal analysis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-600899 DO - https://doi.org/10.3390/met14040430 VL - 14 IS - 4 SP - 1 EP - 26 PB - MDPI CY - Basel AN - OPUS4-60089 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yalçınyüz, Aybike A1 - Raute, Julius A1 - Gonzalez-Gutierrez, Joamin A1 - Pei, Eujin A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Electron Beam Bonding: A novel method for joining additively manufactured carbon fiber thermoplastic composites with aluminum to produce multi-material joints for lightweight applications N2 - In recent years, new solutions have been explored to reduce the weight of components for the automotive, railway, and aerospace industries. For this reason, Carbon Fiber Composites (CFCs) have increasingly replaced metals in products that need to be lightweight. However, due to their poor thermal conductivity, CFCs have limited use in applications requiring efficient heat dissipation. In such applications, conventionally manufactured metal alloys are typically utilized. To address these limitations, a novel approach using a combination of additively manufactured aluminum and CFCs is proposed to exploit the distinct advantages of both materials. These innovative hybrid structures aim to combine good structural and thermal management properties with reduced weight compared to conventionally produced metal products. In this study, additively manufactured aluminum alloy (AlSi10Mg) and short carbon fiber Polyamide 6 composite (sCF-PA6) are utilized to produce metal–polymer pairs using electron beam energy to bond the two materials. Direct irradiation of short CFCs with electron beam leads to polymer degradation. Thus, a novel method “Electron Beam Bonding” for joining CFCs with aluminum alloy in various joint configurations using electron beam technology is demonstrated. This innovative approach presents a promising solution for creating metal–polymer multi-materials for lightweight applications. KW - Electron beam bonding KW - Multi-material KW - Lightweight KW - Additive manufactured materials KW - Short carbon fiber composites KW - AlSi10Mg KW - Joining PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641705 DO - https://doi.org/10.1007/s40964-025-01206-1 SN - 2363-9512 SP - 1 EP - 7 PB - Springer International Publishing CY - Cham AN - OPUS4-64170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Artinov, Antoni A1 - Bachmann, Marcel A1 - Meng, Xiangmeng A1 - Karkhin, V. A1 - Rethmeier, Michael T1 - On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding N2 - Recent studies have confirmed the widening of the weld pool interface, known as a bulge effect, during deep penetration high power laser beam welding. The link between such geometric particularities of the weld pool shape and the hot cracking phenomena is significant. The present work seeks to extend the level of understanding by investigating their relationship. A coupled multiphysics, multiscale numerical framework is developed, comprising a series of subsequent analyses. The study examines the influences of the bulge on the three most dominant effects causing hot cracking, namely the thermal cycles, the mechanical loading, and the local microstructure. The bulge in the weld pool shape forms approximately in the middle of the plate, thus correlating with the location of hot cracking. It increases the hot cracking susceptibility by enhancing the three dominant effects. The numerical results are backed up by experimental data. T2 - 11th CIRP Conference on Photonic Technologies [LANE 2020] KW - Hot cracking KW - Bulge effect KW - Numerical modelling KW - Laser beam welding KW - Deep penetration PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512783 DO - https://doi.org/10.1016/j.procir.2020.09.002 SN - 2212-8271 VL - 94 SP - 5 EP - 10 PB - Elsevier B.V. CY - Amsterdam [u.a.] AN - OPUS4-51278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Srinivasan, Krishnanand A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Laser Metal Deposition of Rene 80—Microstructure and Solidification Behavior Modelling N2 - New developments in nickel-based superalloys and production methods, such as the use of additive manufacturing (AM), can result in innovative designs for turbines. It is crucial to understand how the material behaves during the AM process to advance the industrial use of these techniques. An analytical model based on reaction–diffusion formalism is developed to better explain the solidification behavior of the material during laser metal deposition (LMD). The well-known Scheil–Gulliver theory has some drawbacks, such as the assumption of equilibrium at the solid–liquid interface, which is addressed by this method. The solidified fractions under the Scheil model and the pure equilibrium model are calculated using CALPHAD simulations. A differential scanning calorimeter is used to measure the heat flow during the solid–liquid phase transformation, the result of which is further converted to solidified fractions. The analytical model is compared with all the other models for validation. KW - Laser metal deposition KW - Solidification behavior KW - Additive manufacturing KW - Analytical model KW - Nickel‐based superalloy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612095 DO - https://doi.org/10.3390/mi15101234 SN - 2072-666X VL - 15 IS - 10 SP - 1 EP - 14 PB - MDPI AN - OPUS4-61209 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Determination of critical local straining conditions for solidification cracking at laser beam welding by experimental and numerical methods N2 - AbstractThe phenomenon of solidification cracking has been the subject of numerous research projects over the years. Great efforts have been made to understand the fundamentals of hot cracking. It is generally agreed that solidification cracks form in the solidification range between the liquidus and solidus temperatures under the combination of thermal, metallurgical and mechanical factors. There is still a need to determine the time‐resolved strain distribution in the crack‐sensitive region in order to analyse the local critical conditions for solidification cracking phenomena. This was a strong motivation for the development of a measurement system used in this study to estimate the local strains and strain rates in the zone where the solidification crack is expected to occur. The laser beam welding experiments were conducted using the Controlled‐Tensile‐Weldability test (CTW test) to apply an external strain condition during welding to generate solidification cracks. The CTW test is a test method for investigating the susceptibility of laser‐welded joints to solidification cracking, in which the sample can be subjected to a defined strain at a defined strain rate during welding.In combination with experimental investigations, numerical simulations provide spatially detailed and time‐dependent information about the strain development during the welding process, especially regarding the critical conditions for solidification cracking. Therefore, this tool was also used in the present study to evaluate the accuracy of measurement methods and to estimate experimentally derived values and their concrete influence on the formation of solidification cracks. By integrating experimental methods and numerical simulations, this study investigates the spatially resolved and temporally changing development of strain during welding, with a particular focus on the critical conditions that lead to the formation of solidification cracks. The use of numerical simulations serves a dual purpose by validating the accuracy of measurement methods and examining experimentally determined values for their actual influence on the formation of solidification cracks. A three‐dimensional finite element (FE) model implemented with ANSYS is used to simulate strains and stresses during welding. The credibility of the model was first established by validation using experimental temperature measurements. Subsequently, structural simulations were carried out under external load. The results of the simulations showed commendable agreement with the strain measurements performed using the developed technique. KW - Laser beam welding KW - Solidification cracking KW - FEM simulation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612044 DO - https://doi.org/10.1002/pamm.202400020 SN - 1617-7061 VL - 24 IS - 2 SP - 1 EP - 16 PB - Wiley AN - OPUS4-61204 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gumenyuk, Andrey A1 - Üstündağ, Ömer A1 - Pelz, Till A1 - Bakir, Nasim A1 - Gerhards, Benjamin A1 - Schleser, Markus A1 - Rethmeier, Michael T1 - Single pass laser vacuum welding of thick steel plates using electromagnetic support N2 - The increasing demand for renewable energy produced by offshore wind turbines goes along with an increased demand in the production of offshore wind turbine foundations, so called “monopiles”, which are made by joining thick metal sheets. The industrial standard of multi-layer submerged arc welding (SAW) for joining of thick metal sheets is the current bottleneck in the production of monopiles. A possible increase in productivity by the implementation of high-power laser welding in a newly developed mobile vacuum chamber (MoVac) and an electromagnetic root support is the subject of this study. Single run butt welds are performed in flat position on S355 mild steel of thicknesses up to 80 mm using a disc laser system with 1030 nm wavelength and a maximum output of 60 kW. The laser optic is fixed on the MoVac-System which is held and manipulated by an articulated robot. KW - Laser beam welding KW - Laser welding with mobile vacuum PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612068 DO - https://doi.org/10.1016/j.procir.2024.08.145 VL - 124 SP - 418 EP - 423 PB - Elsevier BV AN - OPUS4-61206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gumenyuk, Andrey A1 - Bakir, Nasim A1 - Rethmeier, Michael T1 - Two-colour thermography for measurement of temperature distribution in laser beam welding N2 - Solidification cracking is a frequently observed phenomenon in laser beam welding of austenitic stainless steels and other metallic alloys. Characterisation of cracking susceptibility requires knowledge of the precise and spatially resolved temperature distribution near the solidification front in the welding process. Thermography is a standard tool that provides a qualitative estimate of the 2D temperature field. The general disadvantage of this method is its dependence on the emission characteristics of the measured object. For welding applications, these can vary significantly in the temperature range above and below the melting temperature. For this purpose, we have developed a thermography-based measurement technique using a SWIR camera system in combination with two narrow bandpass filters that use the principle of two-wavelength pyrometry to estimate absolute temperature values. This technique was used to determine the temperature distributions and gradients near the solidification front of laser-welded austenitic steel. The results were validated by other measurements. KW - Laser beam welding KW - Two-colour thermography KW - Solidification cracking PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612070 DO - https://doi.org/10.1016/j.procir.2024.08.155 VL - 124 SP - 468 EP - 471 PB - Elsevier BV AN - OPUS4-61207 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Keke A1 - El-Sari, Bassel A1 - Olfert, Viktoria A1 - Wang, Zhuoqun A1 - Biegler, Max A1 - Rethmeier, Michael A1 - Meschut, Gerson T1 - Expulsion prevention in resistance spot welding of dissimilar joints with ultra-high strength steel: An analysis of the mechanism and effect of preheating current N2 - The widespread adoption of ultra-high strength steels, due to their high bulk resistivity, intensifies expulsion issues in resistance spot welding (RSW), deteriorating both the spot weld and surface quality. This study presents a novel approach to prevent expulsion by employing a preheating current. Through characteristic analysis of joint formation under critical welding current, the importance of plastic material encapsulation around the weld nugget (plastic shell) at high temperatures in preventing expulsion is highlighted. To evaluate the effect of preheating on the plastic shell and understand its mechanism in expulsion prevention, a two-dimensional welding simulation model for dissimilar ultra-high strength steel joints was established. The results showed that optimal preheating enhances the thickness of the plastic shell, improving its ability to encapsulate the weld nugget during the primary welding phase, thereby diminishing expulsion risks. Experimental validation confirmed that by employing the optimal preheating current, the maximum nugget diameter was enhanced to 9.42 mm, marking an increase of 13.4 % and extending the weldable current range by 27.5 %. Under quasi-static cross-tensile loading, joints with preheating demonstrated a 7.9 % enhancement in maximum load-bearing capacity compared to joints without preheating, showing a reproducible and complete pull-out failure mode within the heat-affected zone. This study offers a prevention method based on underlying mechanisms, providing a new perspective for future research on welding parameter optimization with the aim of expulsion prevention. KW - Resistance spot welding KW - Finite element modelling KW - Preheating KW - Weldable current range KW - Ultra-high strength steel PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621719 DO - https://doi.org/10.1016/j.jmapro.2024.06.034 VL - 124 SP - 489 EP - 502 PB - Elsevier Ltd. AN - OPUS4-62171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Uhlmann, Eckart A1 - Polte, Julian A1 - Fasselt, Janek Maria A1 - Müller, Vinzenz A1 - Klötzer-Freese, Christian A1 - Kleba-Ehrhardt, Rafael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - A Comparative Evaluation of Powder Characteristics of Recycled Material from Bronze Grinding Chips for Additive Manufacturing N2 - In the manufacturing process of ship propellers, large quantities of grinding chips are generated. These grinding chips result from the finishing of the blade surfaces after the primary casting process of the propeller. The aim of this study was to investigate and compare different preparation processes used to produce chip powders with sufficient powder quality for the additive manufacturing process of directed energy deposition. The preparation of the samples was performed through different sieving, milling and re-melting processes. For the characterization of the prepared samples, powder analysis according to relevant industry standards was carried out. It was found that the re-melting processes result in superior powder quality for additive manufacturing in terms of particle size, morphology, and flowability. For some characteristics, the powder exhibits even better properties than those of commercial powders. Furthermore, the powder properties of the milled samples demonstrate a promising potential for u KW - Grinding chips KW - Comminution KW - Aluminium bronze KW - Additive manufacturing KW - Recycling KW - Sustainability PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621696 DO - https://doi.org/10.3390/ma17143396 VL - 17 IS - 14 SP - 1 EP - 15 PB - MDPI AG AN - OPUS4-62169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Raute, Julius A1 - Beret, Alexander A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Life cycle assessment in additive manufacturing of copper alloys—comparison between laser and electron beam N2 - Additive manufacturing is becoming increasingly important for industrial production. In this context, directed energy deposition processes are in demand to achieve high deposition rates. In addition to the well-known laser-based processes, the electron beam has also reached industrial market maturity. The wire electron beam additive manufacturing offers advantages in the processing of copper materials, for example. In the literature, the higher energy efficiency and the resulting improvement in the carbon footprint of the electron beam are highlighted. However, there is a lack of practical studies with measurement data to quantify the potential of the technology. In this work, a comparative life cycle assessment between wire electron beam additive manufacturing (DED-EB) and laser powder additive manufacturing (DED-LB) is carried out. This involves determining the resources for manufacturing, producing a test component using both processes, and measuring the entire energy consumption. The environmental impact is then estimated using the factors global warming potential (GWP100), photochemical ozone creation potential (POCP), acidification potential (AP), and eutrophication potential (EP). It can be seen that wire electron beam additive manufacturing is characterized by a significantly lower energy requirement. In addition, the use of wire ensures greater resource efficiency, which leads to overall better life cycle assessment results. KW - Life cycle assessment (LCA) KW - Additive manufacturing KW - Directed energy deposition KW - Wire electron beam additive manufacturing KW - Copper alloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621705 DO - https://doi.org/10.1007/s40194-024-01856-9 SP - 3169 EP - 3176 PB - Springer Science and Business Media LLC AN - OPUS4-62170 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Marquardt, R. A1 - Biegler, M. A1 - Rethmeier, Michael T1 - Functionally graded material for improved wear resistance manufactured by directed energy deposition N2 - Protecting components against wear and corrosion is a common way to improve their lifetime. This can be achieved by coating them with a hardfacing material. Common coatings consist of materials such as tungsten carbide or cobalt-chromium alloys, also known as Stellite. Hardfacing materials can be deposited by welding methods like plasma welding or laser cladding. The discrete change of the base material to the hardfacing layer can lead to cracks and chipping. Studies showed a reduced risk of cracking when a functionally graded material is used to create a smooth transition between the base and the hardfacing. Gradings from austenitic steel to cobalt-chromium alloys are already known in the literature. However, there is no knowledge about austenitic- ferritic duplex steels as base material. Therefore, this study aims to demonstrate the feasibility of a functionally graded material from duplex steel to cobalt-chromium alloy with a new approach. By using powder-based directed energy deposition, a graded material with smooth material transition is manufactured additively. Cracking and porosity are examined through metallography. Microhardness measurements as well as the analysis of the chemical composition by energy dispersive X-ray spectroscopy and X-ray fluorescence are used to validate the build-up strategy. KW - Additive manufacturing KW - Functionally graded material KW - Functionally graded additive manufacturing KW - Directed energy deposition KW - Laser metal deposition PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621683 DO - https://doi.org/10.1007/s40964-024-00879-4 SP - 1 EP - 6 PB - Springer Science and Business Media LLC AN - OPUS4-62168 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Assessment of keyhole stability in laser beam welding with external magnetic field using numerical simulation N2 - The challenge of understanding the physical mechanisms behind porosity reduction by a magnetic field during laser beam welding (LBW) is partly due to the difficulty in quantitatively evaluating keyhole stability. The commonly used index, such as keyhole depth, is typically one-dimensional, which is insufficient to capture the dynamic and three-dimensional fluctuations of the keyhole. In this paper, by utilizing a 3D multiphysical model of LBW with magnetic field, a novel keyhole geometry reconstruction algorithm has been developed to describe the keyhole profile and its fluctuation in a statistical manner to evaluate keyhole stability quantitatively. An equivalent diameter is proposed in this algorithm to reduce the irregularity of the keyhole geometry. The calculation results indicate that the time-averaged keyhole shape over 300 ms in the LBWof steel is conical, regardless of the application of an external magnetic field, which provides a more representative shape. Meanwhile, it is observed from the statistical aspect that the keyhole diameter becomes smaller, except the top part, under the influence of the magnetic field. The standard deviation of the equivalent diameter can be used as a physical variable to assess the keyhole stability quantitatively. The application of an external magnetic field can produce a noticeable reduction of the standard deviation of the equivalent diameter, namely, stabilizing the keyhole during LBW of steel. However, the different contribution from the keyhole stability affected by a magnetic field in suppressing porosity is different with materials. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Los Angeles, CA, USA DA - 04.11.2024 KW - Deep penetration laser beam welding KW - Numerical simulation KW - Keyhole shape KW - Keyhole stability KW - Magnetic field PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-614984 DO - https://doi.org/10.2351/7.0001528 VL - 36 IS - 4 SP - 1 EP - 7 PB - AIP Publishing CY - Melville, NY AN - OPUS4-61498 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Parametric study of the laser energy absorption in high-power laser beam welding N2 - Laser energy absorption on the keyhole wall is decisive for the thermodynamic behavior and the resultant weld properties in the high-power laser beam welding process. However, its highly transient nature on a microsecond scale makes the quantitative analysis challenging. In this paper, the influence of the relevant welding parameters on laser energy absorption is studied statistically by utilizing multiphysical modeling, in which the three-dimensional transient keyhole dynamics and thermo-fluid flow are calculated. A dynamic mesh adaption technique and a localized level-set-based ray-tracing method are employed to improve the model accuracy further. The results show that the focus position has a remarkable effect on the time-averaged laser absorption, and in contrast, the laser energy distribution regime is only slightly influenced by the welding speed in the studied parameter range (1.5–3.0 m/min). The absorption ratio of the laser energy on the keyhole front wall decreases with increasing welding speed and increases with upward-moving focus positions. The comparison between the calculated results and the experimental measurements ensures the validity of the proposed model. T2 - International Congress of Applications of Lasers & Electro-Optics 2024 CY - Los Angeles, CA, USA DA - 03.11.2024 KW - Laser beam welding KW - Laser energy absorption KW - Weld pool KW - Parametric study KW - Multiphysics modeling PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616070 DO - https://doi.org/10.2351/7.0001537 SN - 1042-346X VL - 36 IS - 3 SP - 1 EP - 6 PB - AIP Publishing AN - OPUS4-61607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Putra, Stephen Nugraha A1 - Meng, Xiangmeng A1 - Yang, Fan A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical study on the temperature characteristic of material absorptivity and its significance in high-power laser beam welding N2 - The absorptivity of metallic materials plays an important role in high-power laser beam welding. It affects the amount of absorbed laser power leading to the heating and melting of the surfaces to be joined and is highly dependent on the temperature. Nonetheless, this key characteristic is often ignored in numerical simulations and an empirical parameter determined by trial-and-error approaches is rather implemented to calibrate the results. In the present work, the temperature dependence of laser absorption is included in a three-dimensional multiphase numerical model considering the coupled fluid flow and heat transfer. The calculated laser absorption is determined by the temperature-dependent material properties, laser characteristics, and incident angle of the laser beam. It is found that the temperature dependence of the laser absorption is crucial for accurately determining the keyhole and weld pool geometries, which is validated by experimental measurements using 304 austenitic steel. T2 - 13th CIRP Conference on Photonic Technologies [LANE 2024] CY - Fürth, Germany DA - 15.09.2024 KW - Laser beam welding KW - Temperature dependent absorption KW - Weld pool KW - Keyhole dynamics KW - Numerical modelling PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616146 DO - https://doi.org/10.1016/j.procir.2024.08.179 VL - 124 SP - 585 EP - 589 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-61614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Numerical studies of magnetohydrodynamic technology in suppressing process porosity during laser beam welding N2 - The magnetohydrodynamic (MHD) technology is employed to mitigate the porosity problem during partial penetration laser beam welding (LBW) of 10 mm thick aluminum alloy. The effectiveness and universal applicability of the MHD technology in reducing porosity during the LBW process are confirmed by a reduction in the porosity ratio of more than 89%. A transient 3D multi-physical model coupled with the MHD effect has been developed to investigate the suppression mechanism of process porosity. Due to the influence of Lorentz force, there is an obvious change in the weld pool length. This change widens the escaping channel of bubbles escaping from the weld pool. The application of an oscillating magnetic field changes the fluid flow pattern noticeably, whose influence on the formation of porosity defects is highly complicated and nonlinear. T2 - CIRP Conference on Photonic Technologies [LANE 2024] CY - Fürth, Germany DA - 15.09.2024 KW - Laser beam welding KW - Aluminum alloy KW - Process Porosity KW - Porosity suppression KW - Magnetohydrodynamic technology PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616053 DO - https://doi.org/10.1016/j.procir.2024.08.175 VL - 124 SP - 565 EP - 569 PB - Elsevier B.V. AN - OPUS4-61605 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meng, Xiangmeng A1 - Bachmann, Marcel A1 - Yang, Fan A1 - Rethmeier, Michael T1 - Toward prediction and insight of porosity formation in laser welding: A physics-informed deep learning framework N2 - The laser welding process is an important manufacturing technology for metallic materials. However, its application is often hindered by the occurrence of porosity defects. By far, an accurate prediction of the porosity defects and an insight into its formation mechanism are still challenging due to the highly nonlinear physics involved. In this paper, we propose a physics-informed deep learning (PIDL) framework by utilizing mechanistic modeling and experimental data to predict the porosity level during laser beam welding of aluminum alloys. With a proper selection of the physical variables (features) concerning the solidification, liquid metal flow, keyhole stability, and weld pool geometry, the PIDL model shows great superiority in predicting the porosity ratio, with a reduction of mean square error by 41 %, in comparison with the conventional DL model trained with welding parameters. Furthermore, the selected variables are fused into dimensionless features with explicit physical meanings to improve the interpretability and extendibility of the PIDL model. Based on a well-trained PIDL model, the hierarchical importance of the physical variables/procedures on the porosity formation is for the first time revealed with the help of the Shapley Additive Explanations analysis. The keyhole ratio is identified as the most influential factor in the porosity formation, followed by the downward flow-driven drag force, which offers a valuable guideline for process optimization and porosity minimization. KW - Laser beam welding KW - Physics-informed deep learning KW - Porosity prediction KW - Feature fusion KW - Hierarchical importance PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624708 DO - https://doi.org/10.1016/j.actamat.2025.120740 VL - 286 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-62470 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seitz, Georg A1 - Bantle, Patrick A1 - Biegler, Max A1 - Elsner, Beatrix A. M. A1 - Rethmeier, Michael T1 - An Inherent Strain Method Using Progressive Element Activation for Fast Distortion Calculation in Directed Energy Deposition N2 - The finite element analysis (FEA) simulation of directed energy deposition (DED) processes offers many potential cost savings during the build job optimization process, through, e.g., distortion predictions. However, the biggest challenge is the long calculation time, frequently exceeding the actual build time. One way of simplifying the simulation with the aim of reducing the calculation times is the inherent strain method. While this method is already used commercially in the simulation of powder bed-based processes and conventional welding technologies, its use in DED is still the subject of research. In this work, an inverse determination of an inherent strain is carried out on a 20-layer-high, single-track-wide wall, common theories are reviewed, and an approach based on thermal strain is introduced. As a result, the calculation time could be reduced by 83% and the accuracy remained at 92%. KW - Inherent strain method KW - Simulation KW - Finite element analysis KW - Directed energy deposition KW - Additive manufacturing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622595 DO - https://doi.org/10.3390/met14121338 SN - 2075-4701 VL - 14 IS - 12 SP - 1 EP - 12 PB - MDPI AN - OPUS4-62259 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmolke, Tobias A1 - Brunner-Schwer, Christian A1 - Biegler, Max A1 - Rethmeier, Michael A1 - Meschut, Gerson T1 - On welding of high-strength steels using laser beam welding and resistance spot weld bonding with emphasis on seam leak tightness N2 - The design of most electric vehicles provides for the positioning of the heavy energy storage units in the underbody of the cars. In addition to crash safety, the battery housing has to meet high requirements for gas tightness. In order to test the use of high-strength steels for this sub-assembly, this paper examines welded joints utilizing resistance spot weld bonding and laser remote welding, with special regard to the gas tightness of the welds. For this purpose, the pressure difference test and helium sniffer leak detection are presented and applied. The combination of both leak test methods has proven ideal in experimental investigations. For laser remote welding, gas-tight seams can be achieved with an inter-sheet gap of 0.1 mm, even if occasionally leaking samples cannot be prevented. Resistance spot welding suits gas-tight joining with both one- and two-component adhesives. Against the background of leak tightness, process fluctuations that lead to weld spatter and defects in the adhesive layer must be prevented with high priority. KW - Resistance spot weld bonding KW - Laser welding KW - Seam leak tightness KW - High-strength steel KW - Leak testing KW - Helium sniffer leak detection PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624250 DO - https://doi.org/10.3390/jmmp7030116 SN - 2504-4494 VL - 7 IS - 3 SP - 1 EP - 14 PB - MDPI CY - Basel AN - OPUS4-62425 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Keke A1 - Sowada, Matthias A1 - Olfert, Viktoria A1 - Seitz, Georg A1 - Schreiber, Vincent A1 - Heitmann, Marcel A1 - Hein, David A1 - Biegler, Max A1 - Jüttner, Sven A1 - Rethmeier, Michael A1 - Meschut, Gerson T1 - Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study N2 - This study investigates the effects of liquid metal embrittlement (LME) cracks on the mechanical performance of resistance spot-welded joints in zinc-coated advanced high-strength steel (AHSS) at the component level. To this end, a novel component-level test specimen featuring a hat and L-shaped profile was developed to identify critical failure points under three-point bending loads. Load-bearing capacity tests were subsequently conducted under both quasi-static and impact loading conditions, specifically targeting LME cracks with an average depth reaching 63.6% of the sheet thickness. By monitoring the surface strain of spot welds affected by LME cracks, the study visualizes stress concentration effects at the crack tips and traces the propagation of these cracks into the base material, which ultimately leads to material tearing and joint failure. The findings reveal that the effect of LME cracks in reducing load-bearing capacity is more pronounced under impact loading than under quasi-static loading, highlighting a previously underexplored aspect of LME behavior under impact loading. Specifically, the peak load decreased by 3.9% and 10.8%, while energy absorption declined by 52.2% and 78.3% under quasistatic and impact loading, respectively. KW - Liquid metal embrittlement KW - Resistance spot welding KW - Impact loading KW - Crack propagation KW - Advanced high-strength steel PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-621727 DO - https://doi.org/10.1016/j.jmrt.2024.11.166 VL - 33 SP - 8321 EP - 8328 PB - Elsevier B.V. AN - OPUS4-62172 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lemke, Josefine A1 - Höfemann, Matthias A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Process strategies for optimizing the cooling behaviour of laser-welded Tailor Welded Blanks made of advanced high strength steels (AHSS) N2 - AHSS with 1000 MPa tensile strength show promising properties for the use in Tailor Welded Blanks (TWBs) to locally strengthen car body parts. Challenges in laser beam welding of the sheets are hardness-drops and -peaks in the heat-affected zone (HAZ) and weld, which cause risks during cold-forming. This happens due to rapid cooling caused by laser welding. A numerical approach aiming for slower cooling rates in the weld region is presented in this article. Laser welded sheets served as reference for setting up a process simulation. Models for pre-heating and a coaxial setup with power split were set up. A correlation between cooling-rate and hardness in the joining zone was established and applied to the modelled strategy. Splitting the power led to a slightly narrower weld seam and experimental pre-heating of the sheets to 600 °C could lower total seam hardening. It achieved a homogenization of the fusion zone. KW - AHSS KW - Laser welding KW - Tailor Welded Blanks KW - Hardness KW - FEM KW - HAZ PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622324 DO - https://doi.org/10.1016/j.procir.2024.08.176 VL - 124 SP - 570 EP - 573 PB - Elsevier B.V. AN - OPUS4-62232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Akyel, Fatma A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Brunner-Schwer, Christian A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Influence of heat input on cooling rates and mechanical properties of laser hybrid welded thick structural steels N2 - Laser hybrid welding presents several challenges when used to weld thick steels. A typical weld is divided into the arcdominated and laser-dominated zone. These zones lead to variations in the mechanical properties of the weld. The laserdominated zone is of particular importance regarding mechanical properties, notably Charpy impact toughness, due to the high cooling rates and the absence of filler wire. The low heat input of the laser can lead to martensitic microstructure causing hardening and deterioration of impact toughness. The high heat input of the arc can lead to grain coarsening and even loss of impact toughness. This study examines the influence of heat input on the cooling rates, microstructure and mechanical properties of single-pass laser hybrid welded steels of S355J2 and EH36 with thicknesses up to 30 mm. The experiments were performed with a 20-kW fibre laser and a contactless electromagnetic weld backing in the butt-joint configuration in 1G welding position. The cooling time was measured in three different locations near the fusion lines corresponding to different heights of the seam using a special configuration with pyrometers, collimators and optical fibres. The test specimens for the Charpy impact testing and tensile testing were extracted in three different depths. The experiments indicated that a heat input of 1.6 kJ/mm–2 kJ/mm, 2 kJ/mm–2.4 kJ/mm and 3.7 kJ/mm were recommended when single-pass laser hybrid welding of 20-, 25-, and 30-mm-thick structural steels regarding the minimum requirements of the mechanical properties, respectively. KW - Laser hybrid welding KW - Heat input KW - Mechanical properties KW - Charpy impact toughness KW - Cooling rate PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625282 DO - https://doi.org/10.1007/s40194-025-01924-8 SN - 1878-6669 SP - 1 EP - 15 PB - Springer CY - United Kingdom AN - OPUS4-62528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yang, Chunliang A1 - Yang, Fan A1 - Meng, Xiangmeng A1 - Putra, Stephen Nugraha A1 - Bachmann, Marcel A1 - Rethmeier, Michael T1 - Multi-refining effects of an AC electromagnetic field on the microstructure in AA5754 laser beam welding N2 - Fine-grain structure is beneficial to the mechanical properties of the joint. Different kinds of grain and sub-grain structures refined by magnetic field during laser beam welding of AA5754 aluminum alloy are analyzed in this manuscript, and the influences of different magnetic field parameters (magnetic flux density and frequency) in these refining effects are also studied. Using the scanning electron microscope (SEM), the sub-grain structure near the fusion line was obtained, and it was found that the branching promotion and branches refinement can be achieved by the magnetic field. The branches become finer with the magnetic flux density or frequency increases, and this effect is stronger in the dendritic region than in the equiaxed region. The results of electron backscatter diffraction (EBSD) in the equiaxed region show that a high-frequency magnetic field can greatly reduce the average grain size, while a low-frequency one has little effect. A phenomenological nucleation model based on dendrite fragmentation theory was established, and it was introduced into the phase field model to analyze the equiaxed grains evolution process. In addition, another refinement mechanism was also observed. The periodic solidification pattern caused by the unstable solidification in the molten pool can refine the grains, and the magnetic field promotes this kind of grain refinement by promoting the solidification period. KW - Laser beam welding KW - Magnetic field KW - Aluminum alloy KW - Crystal branch development KW - Periodic solidification pattern KW - Grain refinement PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637222 DO - https://doi.org/10.1016/j.ijheatmasstransfer.2025.127509 SN - 0017-9310 VL - 252 SP - 1 EP - 16 PB - Elsevier Ltd. AN - OPUS4-63722 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Biegler, Max A1 - Yang, Keke A1 - Meschut, Gerson A1 - Rethmeier, Michael T1 - Occurrence and avoidance of liquid metal embrittlement in resistance spot welding of springback-afflicted deep-drawn components N2 - This study investigates the occurrence and mitigation of liquid metal embrittlement occurring during resistance spot welding in deep-drawn automotive components, specifically focusing on an S-Rail made from advanced high-strength steel. A simulation-based liquid metal embrittlement risk criterion based on local major component stresses was established and used to quantify and compare liquid metal embrittlement risks between different tests. Experimental and numerical analyses were conducted, revealing that springback significantly impacts liquid metal embrittlement formation. Adjustments in electrode geometry and hold time post-welding were found to mitigate liquid metal embrittlement risks. The effects of stack-up configuration and related parameter settings on liquid metal embrittlement occurrence were identified and liquid metal embrittlement was effectively prevented across both stack-up configurations. These findings advance the understanding of liquid metal embrittlement mechanisms and provide practical approaches to enhance the spot weld quality in AHSS-based body-in-whites. KW - Liquid metal embrittlement KW - Crack KW - Advanced high-strength steels KW - Resistance spot welding KW - Weld current KW - Heat input KW - Simulation KW - Springback KW - Deep drawing KW - S-Rail PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636577 DO - https://doi.org/10.1177/13621718251340452 SN - 1362-1718 SP - 1 EP - 9 PB - SAGE Publications AN - OPUS4-63657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Fasselt, Janek Maria A1 - Klötzer-Freese, Christian A1 - Kruse, Tobias A1 - Kleba-Ehrhardt, Rafael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Recycling nickel aluminium bronze grinding chips to feedstock for directed energy deposition via impact whirl milling: Investigation on processability, microstructure and mechanical properties N2 - During the production of ship propellers, considerable quantities of grinding chips from nickel aluminium bronze are produced. This paper examines the mechanical comminution of such chips via impact whirl milling and the utilization of two chip-powder batches as feedstock for a laser-based directed energy deposition process. The materials are characterized via digital image analysis, standardized flowability tests, scanning electron microscopy and energy dispersive X-ray spectroscopy and are compared to conventional, gas atomized powder. The specimens deposited via directed energy deposition are analyzed for density, hardness and microstructure and tensile properties for vertical and horizontal build up directions are compared. At elevated mill rotation speeds, the comminution with impact whirl milling produced rounded particles, favorable flow properties and particle size distribution, making them suitable to deposit additive specimens. The microstructure exhibited characteristic martensitic phases due to the high cooling rates of the additive manufacturing process. The presence of ceramic inclusions was observed in both the powder and on the tensile fracture surfaces, partly impairing the mechanical properties. However, specimens in the vertical build-up direction (Z) showed competitive tensile results, with 775 MPa in tensile strength, 455 MPa in yield strength and 12.6 % elongation at break. The findings of this study indicate that recycling of machining chips to additive manufacturing feedstock can be a viable option for reducing material costs and environmental impact. KW - Nickel aluminium bronze KW - Grinding chips KW - Recycling KW - Directed energy deposition KW - Material characterization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-633442 DO - https://doi.org/10.1016/j.addma.2025.104804 SN - 2214-8604 VL - 105 SP - 1 EP - 9 PB - Elsevier BV AN - OPUS4-63344 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Marquardt, Raphael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Influence of laser power on the melt pool shape of handheld laser beam welding of 1.5 mm thick micro alloyed steel N2 - Manual welding of structures requires highly skilled welders due to the large heat-affected zone of arc-based processes, that can negatively impact microstructure and cause distortion. Handheld laser beam welding is a promising alternative with high welding velocity and a concentrated heat input. However, its current use in industry is limited to parts with aesthetic requirements, often made of high-alloyed steel. To extend the use of handheld laser beam welding to low-cost steels with good mechanical properties, this study investigates the influence of laser power on the melt pool shape for micro-alloyed steel with a thickness of 1.5 mm. Tested joint geometries are T-joints welded with filler wire as well as butt joints and overlap joints without filler wire, which are typically found in assemblies under mechanical load. Weld quality is assessed by weld porosity analysis. The results show that the handheld laser beam welding with filler wire produces T-joints with a very good external appearance, but with porosity between level C and D in the cross sections according to DIN EN ISO 13919-1. By increasing the laser power, a deep penetration of the T-joint zone can be achieved without increasing the actual throat thickness. For handheld laser beam welding of butt joints a full penetration weld of the highest quality class can be reached. Overlap joints can be welded with full or partial penetration depending on the laser power selected, with quality classes between B and C in terms of porosity. T2 - 20th Nordic Laser Materials Processing Conference CY - Kongens Lyngby, Denmark DA - 26.08.2025 KW - Hand held laser welding KW - Laser beam welding KW - Low alloyed steel KW - Process parameter PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-641671 DO - https://doi.org/10.1088/1757-899X/1332/1/012015 SN - 1757-899X VL - 1332 SP - 1 EP - 6 PB - Institute of Physics CY - London [u.a.] AN - OPUS4-64167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Savitsky, Viktor A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Comparative performance of DIC and optical flow algorithms for displacement and strain analysis in laser beam welding N2 - The measurement of strain and displacement in the context of the welding process represents a significant challenge. Optical methods, such as digital image correlation (DIC) or optical flow algorithms, have demonstrated their efficacy in robust and reliable data acquisition in harsh environments, including those encountered in welding processes. Concurrently, a trade-off between the accuracy of the measurement and the computational resources required for the associated calculations must be evaluated on a case-by-case basis. The application of filters to initial images represents a technique that serves to enhance the quality and accuracy of the strain and displacement prediction. In the present study, the estimated error of two algorithms, namely the Lucas-Kanade (LK) and the inverse compositional Gauss-Newton (IC-GN), is compared on the basis of both synthetic and real welding images. The displacement field is evaluated for different zones in the laser weld seam with varying contrast performance. Based on the aforementioned results, a strain calculation was conducted for both methods, which yielded comparable results for the LK and IC-GN algorithms. KW - Laser speckle KW - DIC KW - Optical flow KW - Error estimation KW - Strain measurement KW - Laser beam welding PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625919 DO - https://doi.org/10.1016/j.optlaseng.2025.108870 SN - 1873-0302 VL - 187 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-62591 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Huo, Wenjie A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - Prediction of mean strain from laser beam welding images and detection of defects via strain curves based on machine learning N2 - With the advancement of machine learning, many predictions and measurements in visual tasks can be achieved by convolutional neural networks (CNNs). Solidification hot cracking is a significant defect in laser beam welding, commonly encountered in practical applications. Existing theories indicate that the formation of cracks is closely related to strain accumulation near the solidification front. In this paper, we first leverage supervised Regression networks to design CNNs that achieve real-time average strain estimation for each frame in the collected welding videos. Two different architectures are proposed and compared: the first model stacks two frames at a set interval and feeds them into the network, while the second model extracts image features individually and predicts the results by calculating the correlation between them. Each network has its own advantages in Terms of computational efficiency and accuracy. Finally, we further train a multilayer perceptron (MLP) classification model that can detect the occurrence of cracks based on the predicted strain behaviors. KW - Laser beam welding KW - Mean strain prediction KW - Solidification cracking detection Convolutional neural networks KW - Convolutional neural networks PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-644495 DO - https://doi.org/10.1016/j.optlastec.2025.113975 SN - 0030-3992 VL - 192, Part F SP - 1 EP - 8 PB - Elsevier Ltd. AN - OPUS4-64449 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chaurasia, Prashant Kumar A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - De, Amitava A1 - Rethmeier, Michael T1 - Automated in situ monitoring and analysis of process signatures and build profiles during wire arc directed energy deposition N2 - Wire arc directed energy deposition (DED-Arc) is an emerging metal additive manufacturing process to build near-net shaped metallic parts in a layer-by-layer with minimal material wastage. Automated in situ monitoring and fast-responsive analyses of process signatures and deposit profiles during DED-Arc are in ever demand to print dimensionally consistent parts and reduce post-deposition machining. A comprehensive experimental investigation is presented here involving real-time synchronous measurement of arc current, voltage, and the deposit profile using a novel multi-sensor monitoring framework integrated with the DED-Arc set-up. The recorded current–voltage transients are used to estimate the time-averaged arc power, and energy input in real time for an insight of the influence of wire feed rate and printing travel speed on the deposit characteristics. A unique attempt is made to represent the geometric profiles of the single-track deposits in a generalized mathematical form corresponding to a segmented ellipse, which has exhibited the minimum root-mean-square error of 0.03 mm. The dimensional inconsistency of multi-track deposits is evaluated quantitatively in terms of waviness using build profile monitoring and automated estimation, which is found to increase with an increase in step-over ratio and energy input. For the multi-track mild steel deposits, the suitable range of step-over ratio for the minimum surface waviness is observed to lie between 0.6 and 0.65. Collectively, the proposed framework of synchronized process monitoring and real-time analysis provides a pathway to achieve dimensionally consistent and defect-free parts, and highlights the potential for closed-loop control systems for a wider industrial application of DED-Arc. KW - Additive Manufacturing KW - Arc welding KW - DED-arc KW - Real-time monitoring and control KW - Dimensional inconsistency PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-642029 DO - https://doi.org/10.1007/s40964-025-01333-9 SN - 2363-9512 SP - 1 EP - 20 PB - Springer Science and Business Media LLC CY - Cham AN - OPUS4-64202 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fabry, Çağtay A1 - Pittner, Andreas A1 - Rethmeier, Michael T1 - Arc-sidewall-attaching-driven control of swing arc motion in narrow gap GMAW N2 - A novel, event-driven approach to controlling the weaving motion in swing arc narrow gap GMAW is presented in this study. The control method is based on independently detecting the arc attachment event at each sidewall of the narrow groove to adjust the weaving motion in real time. Previous arc sensing approaches for swing arc principles are based on evaluating and comparing arc sensor readings collected during the dwell periods at each sidewall. Not only does this require the torch to be positioned at the groove centre and the arc motion to be symmetric, but previous methods have also been shown to rely on complex parametrization of control parameters. The newly presented approach is based on the real-time monitoring of the welding current progression during the approach of the arc towards the sidewall of the groove independently on each side. As soon as the arc attachment at the sidewall is detected based on a characteristic rise in the current signal, the weaving motion is stopped. For reference experiments in a 21-mm wide groove, the weaving angle amplitude is controlled and limited to 50° on both sides individually, resulting in stable process conditions and uniform sidewall fusion. It is further shown that the newly developed control method can successfully be applied to groove widths of 18 mm and 24 mm without reconfiguration of the control parameters, highlighting the flexibility of the approach. KW - Gas metal arc welding KW - Narrow gap KW - Arc sensor KW - Control PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-647640 DO - https://doi.org/10.1007/s40194-025-02238-5 SN - 0043-2288 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-64764 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Klement, Oliver A1 - Sander, Steffen A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Recycling of Stainless Steel Milling Chips for Additive Manufacturing: A Three-Stage Comminution Approach Using a Fine Impact Mill N2 - The production of conventional metal powders for additive manufacturing process is energy intensive and costly. This study introduces a sustainable alternative by recycling stainless steel milling chips as feedstock for laser-powder directed energy deposition. The recycling process employs a three-stage mechanical comminution method utilizing a fine impact mill UPZ100 from Hosokawa Alpine AG. Characterization of the resulting powders is conducted through particle morphology analysis, flowability tests, and mechanical property assessments. The chip-derived powders exhibit comparable aspect ratios and sphericity to conventional water atomized powders, though with reduced flowability due to a pronounced fine fraction content. Elevated levels of oxides are observed, leading to the formation of an oxide layer on specimen blocks, without impairing the mechanical properties. Analyses of porosity, microstructure, and hardness indicate no significant differences when compared to conventional powders from water or gas atomization. This recycling approach not only mitigates waste but also enhances the potential for a circular and sustainable manufacturing process in the additive manufacturing industry and beyond. KW - Directed Energy Deposition KW - Recycling KW - Stainless steel KW - Comminution KW - Powder characteristics PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652037 DO - https://doi.org/10.1088/1757-899X/1332/1/012014 SN - 1757-8981 VL - 1332 IS - 1 SP - 1 EP - 7 PB - IOP Publishing AN - OPUS4-65203 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gook, Sergej A1 - Biegler, Max A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Integration of hybrid laser-arc and narrow gap submerged arc welding for cost-effective joining of 80 mm thick S355ML steel plates N2 - This paper presents the results of developing a cost-effective, robust process for welding thick steel plates. Welding trials were performed on S355ML structural steel plates with a thickness of 80 mm. A specially designed U-shaped joint preparation with a 45 mm root face was proposed to enable thick welds to be welded using a combined technique. In the developed process, a hybrid laser arc weld (HLAW) is performed as the first pass. Subsequently, narrow-gap submerged arc welding (NG-SAW) is applied to the opposite side using a multi-layer technique. The weld cross-section is completed using a reliable overlap of both the HLAW and NG-SAW welds. This method achieves a 2.9-fold reduction in weld volume and filler material consumption, as well as shorter production times for thick-walled welds. Further advantages of the process combination include eliminating the need to form the root of the HLAW weld and the absence of a backing support. The applied process parameters ensure that the maximum heat input does not exceed 5 kJ/mm, leading to uniform hardness across the weld metal and heat-affected zone (HAZ). Impact toughness testing at −40 °C demonstrated excellent performance, with Charpy V-notch energies of 138 ± 45 J in the arc-dominated region and 65 ± 12 J in the critical laser-dominated zone of the HLAW weld. In addition, the NG-SAW weld exhibited an average Charpy V-notch energy of 274 ± 5 J, confirming excellent low-temperature toughness of the fill passes. Owing to its high process stability and practical applicability, the proposed welding approach shows high potential for integration into the fabrication of thick-walled offshore constructions. KW - Hybrid laser arc welding KW - Narrow gap submerged arc welding KW - Low carbon structural steel KW - Fusion zone size KW - Microstructure KW - Impact absorbed energy KW - Hardness PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655627 DO - https://doi.org/10.1016/j.optlastec.2026.114796 SN - 0030-3992 VL - 197 SP - 1 EP - 12 PB - Elsevier Ltd. AN - OPUS4-65562 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis A1 - Graf, B. A1 - Rehmer, Birgit A1 - Petrat, T. A1 - Skrotzki, Birgit A1 - Rethmeier, Michael T1 - Characterization of Ti-6Al-4V fabricated by multilayer laser powder-based directed energy deposition N2 - Laser powder-based directed energy deposition (DED-L) is increasingly being used in additive manufacturing (AM). As AM technology, DED-L must consider specific challenges. It must achieve uniform volume growth over hundreds of layers and avoid heat buildup of the deposited material. Herein, Ti–6Al–4V is fabricated using an approach that addresses these challenges and is relevant in terms of transferability to DED–L applications in AM. The assessment of the obtained properties and the discussion of their relationship to the process conditions and resulting microstructure are presented. The quality of the manufacturing process is proven in terms of the reproducibility of properties between individual blanks and with respect to the building height. The characterization demonstrates that excellent mechanical properties are achieved at room temperature and at 400 °C. KW - AGIL KW - Laser powder-based directed energy deposition KW - Tensile properties KW - Ti-6Al-4V KW - Microstructure PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542262 DO - https://doi.org/10.1002/adem.202101333 SN - 1438-1656 SN - 1527-2648 SP - 1 EP - 15 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54226 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Vinzenz A1 - Fasselt, Janek Maria A1 - Klötzer-Freese, Christian A1 - Kruse, Tobias A1 - Kleba-Ehrhardt, Rafael A1 - Biegler, Max A1 - Rethmeier, Michael T1 - Recycling nickel aluminium bronze grinding chips to feedstock for directed energy deposition via impact whirl milling: Investigation on processability, microstructure and mechanical properties N2 - During the production of ship propellers, considerable quantities of grinding chips from nickel aluminium bronze areproduced. This paper examines the mechanical comminution of such chips via impact whirl milling and the utilization of twochip-powder batches as feedstock for a laser-based directed energy deposition process. The materials are characterized viadigital image analysis, standardized flowability tests, scanning electron microscopy and energy dispersive X-ray spectroscopyand are compared to conventional, gas atomized powder. The specimens deposited via directed energy deposition areanalyzed for density, hardness and microstructure and tensile properties for vertical and horizontal build up directions arecompared. At elevated mill rotation speeds, the comminution with impact whirl milling produced rounded particles, favorableflow properties and particle size distribution, making them suitable to deposit additive specimens. The microstructureexhibited characteristic martensitic phases due to the high cooling rates of the additive manufacturing process. The presenceof ceramic inclusions was observed in both the powder and on the tensile fracture surfaces, partly impairing the mechanicalproperties. However, specimens in the vertical build-up direction (Z) showed competitive tensile results, with 775 MPa intensile strength, 455 MPa in yield strength and 12.6 % elongation at break. The findings of this study indicate that recyclingof machining chips to additive manufacturing feedstock can be a viable option for reducing material costs and environmentalimpact. KW - Nickel aluminium bronze KW - Grinding chips KW - Recycling KW - Directed energy deposition KW - Material characterization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651214 DO - https://doi.org/10.1016/j.addma.2025.104804 SN - 2214-8604 VL - 105 SP - 1 EP - 9 PB - Elsevier B.V. AN - OPUS4-65121 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Huo, Wenjie A1 - Schmies, Lennart A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Wolter, Katinka T1 - An illumination based backdoor attack against crack detection systems in laser beam welding N2 - Deep neural networks (DNNs) have been wildly used in engineering and have achieved state-of-the-art performance in prediction and measurement tasks. A solidification crack is a serious fault during laser beam welding and it has been proven to be successfully detected using DNNs. Recently, research on the security of DNNs is receiving increasing attention because it is necessary to explore the reliability of DNNs to avoid potential security risks. The backdoor attack is a serious threat, where attackers aim to inject an inconspicuous pattern referred to as trigger into a small portion of training data, resulting in incorrect predictions in the reference phase whenever the input contains the trigger. In this work, we first generate experimental data containing actual cracks in the welding laboratory for training a crack detection model. Then, targeting this scenario, we design a new type of backdoor attack to induce the model to predict the crack as a normal state. Considering the stealthiness of the attack, a common phenomenon during the welding process, illumination, is used as the backdoor trigger. Experimental results demonstrate that the proposed method can successfully attack the crack detection system and achieve over 90% attack success rate on the test set. T2 - 8th ML4CPS 2025 – Machine Learning for Cyber-Physical Systems CY - Berlin, Germany DA - 06.03,2025 KW - System security KW - Welding crack detection KW - Backdoor attack KW - Deep neural networks PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651357 DO - https://doi.org/10.24405/20021 VL - 2025 SP - 12 EP - 21 PB - Universitätsbibliothek der HSU/UniBw H CY - Hamburg AN - OPUS4-65135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -