TY - JOUR A1 - Shokouhi, Parisa A1 - Zoëga, Andreas A1 - Wiggenhauser, Herbert T1 - Nondestructive investigation of stress-induced damage in concrete N2 - The changes in the sonic surface wave velocity of concrete under stress were investigated in this paper. Surface wave velocities at sonic frequency range were measured on a prismatic concrete specimen undergoing several cycles of uniaxial compression. The loading was applied (or removed) gradually in predefined small steps (stress-controlled). The surface wave velocity was measured at every load step during both loading and unloading phases. Acoustic Emission (AE) test was conducted simultaneously to monitor the microcracking activities at different levels of loading. It was found that the sonic surface wave velocity is highly stress dependent and the velocity-stress relationship follows a particular trend. The observed trend could be explained by a combination of acoustoelasticity and microcracking theories, each valid over a certain range of applied stresses. Having measured the velocities while unloading, when the material suffers no further damage, the effect of stress and damage could be differentiated. The slope of the velocity-stress curves over the elastic region was calculated for different load cycles. This quantity was normalized to yield a dimensionless nonlinear parameter. This parameter generally increases with the level of induced damage in concrete. KW - Nondestructive testing (NDT) KW - Surface wave velocity KW - Concrete KW - Acoustoelasticity KW - Microcracking PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-215943 UR - http://downloads.hindawi.com/journals/ace/2010/740189.pdf DO - https://doi.org/10.1155/2010/740189 SN - 1687-8094 SN - 1687-8086 VL - 2010 IS - Article ID 740189 SP - 1 EP - 9 PB - Hindawi Publ. Corp. CY - New York, NY, USA AN - OPUS4-21594 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lück, S. A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Schmidt, V. T1 - Statistical analysis of tomographic reconstruction algorithms by morphological image characteristics N2 - We suggest a procedure for quantitative quality control of tomographic reconstruction algorithms. Our task-oriented evaluation focuses on the correct reproduction of phase boundary length and has thus a clear implication for morphological image analysis of tomographic data. Indirectly the method monitors accurate reproduction of a variety of locally defined critical image features within tomograms such as interface positions and microstructures, debonding, cracks and pores. Tomographic errors of such local nature are neglected if only global integral characteristics such as mean squared deviation are considered for the evaluation of an algorithm. The significance of differences in reconstruction quality between algorithms is assessed using a sample of independent random scenes to be reconstructed. These are generated by a Boolean model and thus exhibit a substantial stochastic variability with respect to image morphology. It is demonstrated that phase boundaries in standard reconstructions by filtered backprojection exhibit substantial errors. In the setting of our simulations, these could be significantly reduced by the use of the innovative reconstruction algorithm DIRECTT. KW - Tomography KW - Computed tomography KW - Reconstruction algorithm KW - Morphological image analysis KW - Phase boundary KW - Metrology KW - Non-destructive testing PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-210710 DO - https://doi.org/10.5566/ias.v29.p61-77 SN - 1580-3139 SN - 1854-5165 VL - 29 SP - 61 EP - 77 CY - Ljubljana, Slovenia AN - OPUS4-21071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lai Wai-Lok, Wallace A1 - Kind, Thomas A1 - Wiggenhauser, Herbert T1 - A study of concrete hydration and dielectric relaxation mechanism using ground penetrating radar and short-time fourier transform N2 - Ground penetrating radar (GPR) was used to characterize the frequency-dependent dielectric relaxation phenomena in ordinary Portland cement (OPC) hydration in concrete changing from fresh to hardened state. The study was experimented by measuring the changes of GPR A-scan waveforms over a period of 90 days, and processed the waveforms with short-time Fourier transform (STFT) in joint time-frequency analysis (JTFA) domain rather than a conventional time or frequency domain alone. The signals of the direct wave traveled at the concrete surface and the reflected wave from an embedded steel bar were transformed with STFT, in which the changes of peak frequency over ages were tracked. The peak frequencies were found to increase with ages and the patterns were found to match closely with primarily the well-known OPC hydration process and secondarily, the evaporation effect. The close match is contributed to the simultaneous effects converting free to bound water over time, on both conventional OPC hydration and dielectric relaxation mechanisms. KW - Soil water content KW - Wet soil KW - Microwave KW - Moisture KW - GPR KW - Dispersion PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-239723 DO - https://doi.org/10.1155/2010/317216 SN - 1687-6172 IS - Article ID 317216 SP - 1 EP - 14 PB - Hindawi Publ. CY - New York, NY, USA AN - OPUS4-23972 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pretsch, Thorsten T1 - Review on the functional determinants and durability of shape memory polymers N2 - Shape memory polymers (SMP) belong to the class of stimuli-responsive materials and have generated significant research interest. Their capability to retain an imposed, temporary shape and to recover the initial, permanent shape upon exposure to an external stimulus depends on the "functional determinants", which in simplistic terms, can be divided into structural/morphological and processing/environmental factors. The primary aim of the first part of this review is to reflect the knowledge about these fundamental relationships. In a next step, recent advances in shape memory polymer composites are summarized. In contrast to earlier reviews, studies on the impairment of shape memory properties through various factors, such as aging, compression and hibernation, lubricants, UV light and thermo-mechanical cycling, are extensively reviewed. Apart from summarizing the state-of-the-art in SMP research, recent progress is commented. KW - Shape memory polymer KW - Active polymer KW - Shape memory polymer composite KW - Shape memory properties KW - Functionality KW - Degradation KW - Aging KW - Functional determinants KW - Thermo-mechanical testing KW - Durability PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-217390 UR - http://www.mdpi.com/2073-4360/2/3/120/pdf DO - https://doi.org/10.3390/polym2030120 SN - 2073-4360 VL - 2 IS - 3 SP - 120 EP - 158 PB - MDPI CY - Basel AN - OPUS4-21739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dey, Anika A1 - Casperson, Ralf A1 - Pohl, Rainer A1 - Thomas, Hans-Martin T1 - Die Wirbelstromprüfung als Hilfsmittel für die Schieneninstandhaltung N2 - Die zerstörungsfreie Oberflächenprüfung an verlegten Eisenbahnschienen mit Wirbelstrom hat in den letzten Jahren durch ständige Weiterentwicklung und Verifizierung enorm an Bedeutung gewonnen. Es wurde u.a. angestrebt zuverlässige Planungsgrößen für den Einsatz von Instandhaltungsmaßnahmen zu erhalten, durch deren gezielten Einsatz Risswachstum unterbunden werden kann. Die Ursache für das Wachstum von Rissen in der Schiene liegt in der Materialermüdung des Werkstoffes infolge der Betriebsbelastungen im RadSchiene-Kontakt. Nach einer gewissen Beanspruchungsdauer kommt es an den Kontaktflächen der Fahrkante zu einer Kaltverfestigung des Schienenstahls. Durch fortschreitende Verfestigung des kontaktbeanspruchten Oberflächenbereichs der gehärteten Schicht wird der Werkstoff spröde und es bilden sich feine Risse aus. Die Risse wachsen anfangs unter einem flachen Winkel in das Schieneninnere hinein, neigen dann aber ab einem gewissen Stadium dazu in das Innere des Schienenkopfes abzukippen, was im Extremfall zu einem Schienenbruch führen kann. Diese Rollkontaktermüdungsrisse, auch genannt Head Checks, entstehen bevorzugt in der Fahrkante von bogenäußeren Schienen. Die Anwendung der Wirbelstromprüfung an der Schiene wurde bisher zur Ermittlung der Schädigungstiefe dieser Rollkontaktermüdungsrisse eingesetzt. Das Wirbelstromverfahren besitzt die Eigenschaft, sehr empfindlich auf alle Veränderungen der Materialeigenschaften an der Oberfläche zu reagieren. Daher wurde festgestellt, dass sich neben der Detektion von Rissen auch Fehler wie Eindrückungen oder Schlupfwellen, bis hin zu Materialveränderungen durch Schweißen oder Aufhärtungen in der Schienenoberfläche bestimmen lassen. Die Wirbelstromprüfung besitzt daher das Potenzial, mögliche Orte der Entstehung von Ermüdungsrissen in einem extrem frühzeitigen Stadium nachzuweisen. Ziel ist es, die rissgefährdeten Zonen schon im Zustand der Kaltverfestigung zu identifizieren. Dadurch können sich neue Aspekte für die präventive Schieneninstandhaltung ergeben. T2 - DGZfP-Jahrestagung 2010 - Zerstörungsfreie Materialprüfung ZfP in Forschung, Entwicklung und Anwendung CY - Erfurt, Germany DA - 10.05.2010 PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-214813 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-21481 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard T1 - Phosphorus-based flame retardancy mechanisms - Old hat or a starting point for future development? N2 - Different kinds of additive and reactive flame retardants containing phosphorus are increasingly successful as halogen-free alternatives for various polymeric materials and applications. Phosphorus can act in the condensed phase by enhancing charring, yielding intumescence, or through inorganic glass formation; and in the gas phase through flame inhibition. Occurrence and efficiency depend, not only on the flame retardant itself, but also on its interaction with pyrolysing polymeric material and additives. Flame retardancy is sensitive to modification of the flame retardant, the use of synergists/adjuvants, and changes to the polymeric material. A detailed understanding facilitates the launch of tailored and targeted development. KW - Fire retardancy KW - Red phosphorus KW - Phosphate KW - Phosphonate KW - Phosphinate KW - Phosphine oxide KW - Flame inhibition KW - Charring KW - Intumescence PY - 2010 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-220368 DO - https://doi.org/10.3390/ma3104710 SN - 1996-1944 VL - 3 IS - 10 SP - 4710 EP - 4745 PB - MDPI CY - Basel AN - OPUS4-22036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kasper, J. A1 - Hermanns, M. A1 - Bantz, C. A1 - Maskos, Michael A1 - Stauber, R. A1 - Pohl, C. A1 - Unger, R. E. A1 - Kirkpatrick, J.C. T1 - Inflammatory and cytotoxic responses of an alveolar-capillary coculture model to silica nanoparticles: comparison with conventional monocultures N2 - To date silica nanoparticles (SNPs) play an important role in modern technology and nanomedicine. SNPs are present in various materials (tyres, electrical and thermal insulation material, photovoltaic facilities). They are also used in products that are directly exposed to humans such as cosmetics or toothpaste. For that reason it is of great concern to evaluate the possible hazards of these engineered particles for human health. Attention should primarily be focussed on SNP effects on biological barriers. Accidentally released SNP could, for example, encounter the alveolar-capillary barrier by inhalation. In this study we examined the inflammatory and cytotoxic responses of monodisperse amorphous silica nanoparticles (aSNPs) of 30 nm in size on an in vitro coculture model mimicking the alveolar-capillary barrier and compared these to conventional monocultures. Methods Thus, the epithelial cell line, H441, and the endothelial cell line, ISO-HAS-1, were used in monoculture and in coculture on opposite sides of a filter membrane. Cytotoxicity was evaluated by the MTS assay, detection of membrane integrity (LDH release), and TER (Transepithelial Electrical Resistance) measurement. Additionally, parameters of inflammation (sICAM-1, IL-6 and IL-8 release) and apoptosis markers were investigated. Results Regarding toxic effects (viability, membrane integrity, TER) the coculture model was less sensitive to apical aSNP exposure than the conventional monocultures of the appropriate cells. On the other hand, the in vitro coculture model responded with the release of inflammatory markers in a much more sensitive fashion than the conventional monoculture. At concentrations that were 10-100fold less than the toxic concentrations the apically exposed coculture showed a release of IL-6 and IL-8 to the basolateral side. This may mimic the early inflammatory events that take place in the pulmonary alveoli after aSNP inhalation. Furthermore, a number of apoptosis markers belonging to the intrinsic pathway were upregulated in the coculture following aSNP treatment. Analysis of the individual markers indicated that the cells suffered from DNA damage, hypoxia and ER-stress. Conclusion We present evidence that our in vitro coculture model of the alveolar-capillary barrier is clearly advantageous compared to conventional monocultures in evaluating the extent of damage caused by hazardous material encountering the principle biological barrier in the lower respiratory tract. KW - Silica nanoparticles KW - Alveolar-capillary coculture model KW - Cytotoxicity PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-254217 DO - https://doi.org/10.1186/1743-8977-8-6 SN - 1743-8977 VL - 8 IS - 6 SP - 1 EP - 16(?) PB - BioMed Central CY - London AN - OPUS4-25421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ehrig, Karsten A1 - Goebbels, Jürgen A1 - Meinel, Dietmar A1 - Paetsch, O. A1 - Prohaska, S. A1 - Zobel, Valentin T1 - Comparison of crack detection methods for analyzing damage processes in concrete with computed tomography N2 - Analyzing damages at concrete structures due to physical, chemical, and mechanical exposures need the application of innovative non-destructive testing methods that are able to trace spatial changes of microstructures. Here, the utility of three different crack detection methods for the analysis of computed tomograms of various cementitious building materials is evaluated. Due to the lack of reference samples and standardized image quality evaluation procedures, the results are compared with manually segmented reference data sets. A specific question is how automatic crack detection can be used for the quantitative characterization of damage processes, such as crack length and volume. The crack detection methods have been integrated into a scientific visualization system that allows displaying the tomography images as well as presenting the results. T2 - DIR 2011 - International symposium on digital industrial raidology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Crack detection KW - Computed tomography KW - Data visualization PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-243569 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (Poster 2) SP - 1 EP - 8 PB - Deutsche Gesellscahft für Zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24356 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Hentschel, Manfred P. A1 - Lange, Axel A1 - Grothausmann, R. A1 - Manke, I. T1 - Application of the DIRECTT algorithm to sub-nanometer electron tomography N2 - Tomography data obtained from transmission electron microscopes are especially attractive due to their unrivaled spatial resolution in the nanometer range or even less, but they require enormous efforts in sample preparation and suffer from a diverse accumulation of experimental restrictions, which unavoidably result in fundamental reconstruction artifacts. These restrictions refer to: partial opacity, a limited view (limited angle or missing wedge), very few angles (with respect to the detector size), limited to a region of interest (ROI; due to the sample size), variable angular increments as well as sample degradation due the interactions with the electron beam. An advanced version of the DIRECTT (Direct Iterative Reconstruction of Computed Tomography Trajectories) algorithm proves to cope with most of these severe deviations from ideal CT measuring conditions. However, careful data preprocessing is required in order to exploit the capabilities of the algorithm. Nanometer sized Ruthenium catalyst particles for fuel cell applications are 3D imaged at a few Ångström resolution in order to estimate their partial free surface on carbon black supports, which rule the efficiency of the catalytic activity. Comparisons of DIRECTT reconstructions to the conventional filtered back projection, prove the significant improvements. T2 - DIR 2011 - International symposium on digital industrial raidology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Electron tomography KW - Computed tomography KW - Reconstruction algorithms PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-243577 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (Tu.3.3) SP - 1 EP - 6 PB - Deutsche Gesellscahft für Zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gollwitzer, Christian A1 - Bellon, Carsten A1 - Deresch, Andreas A1 - Ewert, Uwe A1 - Jaenisch, Gerd-Rüdiger T1 - On POD estimations with radiographic simulator aRTist N2 - The computer simulation of radiography is applicable for different purposes in NDT such as for the qualification of NDT systems, the optimization of system parameters, feasibility analysis, model-based data interpretation, education and training of NDT/NDE personnel, and others. Within the framework of the European project PICASSO simulators will be adapted to support reliability assessments of NDT tasks. The radiographic simulator aRTist developed by BAM is well suited for this task. It combines analytical modelling of the RT inspection process with the CAD-orientated object description applicable to various industrial sectors such as power generation, aerospace, railways and others. The analytic model includes the description of the radiation source, the interaction of Radiation with the material of the part, and the detection process with special focus to DIR. To support reliability estimations the simulation tool is completed by a tool for probability of detection (POD) estimation. It consists of a user interface for planning automatic simulation runs with varying parameters, specifically defect variations. Further, an automatic image analysis procedure is included to evaluate the defect visibility and calculate the POD therefrom. T2 - International symposium on digital industrial radiology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Radiographie KW - Computersimulation KW - Probability of detection PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-245092 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (Tu.2.3) SP - 1 EP - 8 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bartscher, M. A1 - Ehrig, Karsten A1 - Staude, Andreas A1 - Goebbels, Jürgen A1 - Neuschaefer-Rube, U. T1 - Application of an industrial CT reference standard for cast freeform shaped workpieces N2 - Industrial computed tomography (CT) today is an important method to analyze defects and to measure the geometry of technical products. The measurement capability of industrial CT often depends on the knowledge of the measurement errors being present. Only with this knowledge, effective corrections are possible by manufacturers, or adapted measurement procedures become possible for the customers. Thus, there is the strong need to have adequate reference standards both for the assessment of general dependencies and for the measurement of task-specific effects. Especially the latter are difficult to assess. This paper shows the application of a versatile dismountable workpiece-near reference body for the use with CT. The reference standard was made from a miniaturized cast aluminium (one-)cylinder head. It can be dismounted into four segments, each featuring reference geometries which enable a registration of CT measured and other reference datasets (e.g. from tactile CMM). The reference standard embodies complex freeform surfaces which are a challenging measurement task for CT and other sensors. Here the application of the reference standard is the study of the influence of material mixes. This is realized by adding pieces of other materials which disturb the mono-material measurement. Results of the application of the reference standard are presented using data from industrial micro-CT systems and CMM reference data. A special emphasis is given on the workflow of the data processing and the data analysis. T2 - International symposium on digital industrial radiology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Industrial reference standard KW - Computed tomographie KW - Freeform shaped workpieces PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-245532 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (We.4.3) SP - 1 EP - 12 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Boehm, Rainer A1 - Brackrock, Daniel A1 - Kitze, Jessica A1 - Brekow, Gerhard A1 - Kreutzbruck, Marc A1 - Heinrich, W. T1 - Ultraschalluntersuchungen an einem Turbinenradscheibentestkörper mit Sägezahn-Arrays N2 - - Besondere Anforderungen der Prüfaufgabe - Elektronischer Scan für Tandemtechnik bzw. Pitch - Catch Technik - Der ebene Winkelprüfkopf, ein besonderer Gruppenstrahler (PA) - Charakterisierung des Prüfkopfes, Verifikation durch Messung - Messungen am Turbinenradscheibentestkörper T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Ultraschallprüftechnik KW - Phased array KW - Prüfkopfentwicklung KW - Turbinenradscheiben PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-252085 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.1.A.3) SP - 1 EP - 21 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25208 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Christina A1 - Pavlovic, Mato T1 - Ganzheitliche Zuverlässigkeit - Prüfung von Bauteilen mit komplexer Geometrie N2 - Selbst die modernsten ZfP-Systeme können, wenn sie bis an die Grenzen ihrer Möglichkeiten z. B. kleine Fehler zu finden beansprucht werden, nicht alle Fehler der gleichen Größe finden. Sogar wenn ein und derselbe Fehler mehrmals geprüft wird, wird er nicht immer gefunden. Deshalb wurde, besonders für solche Anwendungsfälle wo das Übersehen eines Fehlers zu schwerwiegenden Konsequenzen führt, das Konzept der Zuverlässigkeit der ZfP eingeführt. Das Konzept der BAM beinhaltet eine ganzheitliche Betrachtungsweise mittels eines modularen Models. Die Hauptmodule des Modells sind die innewohnende Fähigkeit, die die physikalisch technischen Aspekte behandelt. Weiterhin werden die Einflüsse der Umgebung betrachtet, die den Prüfprozess stören, aber nicht zum Prüfsystem selbst gehören. Einen wesentlichen Aspekt, sowohl bei manuellen als auch bei mechanisierten Prüfungen stellt der menschliche Faktor dar. Die Betrachtungen im vorliegenden Artikel beziehen sich hauptsächlich auf die innewohnende Fähigkeit. Wegen der dem Prüfprozess innewohnenden Unsicherheit wird die Leistungsfähigkeit eines ZfP-Systems durch eine Funktion POD (a) ausgedrückt. Zu verschiedenen Fehlergrößen (a) gehören verschiedene Fehlerauffindwahrscheinlichkeiten (POD). Die Fehlergröße (a), bei der die untere 95 % Vertrauensgrenze das Niveau von 90 % POD schneidet wird α90/95 genannt. Dieser Punkt wird als Maß für das Leistungsvermögen der ZfP-Methode benutzt. Während der letzten 10-20 Jahre wurden auf diese Weise verschiedene Inspektionssysteme für eine gewählte ZfP-Methode mit einer einfachen Anwendungsgeometrie bewertet. Wenn man über diese einfachen Anwendungssituationen hinaus, die Zuverlässigkeit in realen industriellen Prozessen betrachtet, treten als erstes industrielle Bauteile mit komplexer Geometrie und Defekte, die mit mehr als nur einem Parameter (Größe und Tiefe, Orientierung, Oberflächenrauhigkeit) charakterisiert werden müssen, auf die Tagesordnung. Neue hochentwickelte und automatisierte ZfP-Systeme, wie z. B. Ultraschallgruppenstrahler, lassen die Möglichkeit zu die Prüfungen digital aufzuzeichnen und später erst auszuwerten. Weiterhin erlauben es moderne Modellierungswerkzeuge den ZfP-Prozess zu simulieren und damit die Einflüsse der Wellenausbreitung und deren Wechselwirkung mit Defekten sowie die Wirkung der zusätzlichen Einflussparameter (z. B. Abstand vom Prüfkopf oder Orientierung) auf die POD zu untersuchen. Damit entsteht die Möglichkeit die räumliche Verteilung der POD im Prüfstück zu ermitteln – die Volumen-POD. Die Volumen-POD kann ebenso wie die konventionelle POD als Maß für die Leistungsfähigkeit des ZfP-Systems benutzt werden. Darüber hinaus kann man das ZfP-System optimieren. Wenn z. B. bestimmte Volumenelemente nur ungenügende POD-Werte aufweisen, müssen zusätzliche Prüfungen einbezogen werden. Aber auch der umgekehrte Fall, Bereiche in denen mehrere Prüfköpfe ein POD Niveau von 100 % haben und die Zahl der Prüfungen reduziert werden kann, werden mit der Volumen-POD erkannt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Zuverlässigkeit KW - ZfP KW - Volumen-POD KW - Produkt-Design PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-251607 SN - 978-3-940283-33-7 VL - 127 SP - Mi.3.C.1 - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25160 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Gaal, Mate A1 - Müller, Christina A1 - Fahlbruch, B. A1 - Schombach, D. T1 - Einfluss des Zeitdrucks auf die manuelle Ultraschallprüfung. Untersuchung zu menschlichen Faktoren auf die Ergebnisse zerstörungsfreier Prüfungen N2 - Die übergeordnete Zielsetzung unserer Untersuchung bestand darin, am Beispiel von Prüfungen mit Ultraschall eine belastbare Aussage zum Einfluss der Arbeitsbedingungen des Prüfers auf die Qualität der Ergebnisse von zerstörungsfreien Prüfungen zu ermitteln und Möglichkeiten zur Minimierung ungünstiger Einflussfaktoren aufzuzeigen. Der Schwerpunkt der Untersuchung wurde auf die manuelle Ultraschallprüfung gelegt und der Faktor 'Zeitdruck' (in drei Stufen variiert) als die zu variierende physische Einflussgröße gewählt. Die Variation des Faktors Zeitdruck wurde gemäß dem Prozessmodell von der Erhebung psychologischer Faktoren, die das Individuum und die Organisation beschreiben, begleitet. Die Ultraschallprüfungen erfolgten mit zehn Prüfern am Großbehälter und an Vergleichskörpern mit eingebrachten Testfehlern (Nuten, Risse). Die ausgewählten Fehler waren typisch für Prüfaufgaben, die bei wiederkehrenden Ultraschallprüfungen in Kernkraftwerken von den Prüfern zu lösen sind. Die Prüfaufgabe bestand darin, die in den vorgegebenen Prüfabschnitten vorhandenen Reflektoren aufzufinden und deren Amplituden, Ortskoordinaten und Längenerstreckungen zu ermitteln. Als Bewertungsmaßstab für die Qualität der Prüfaussage und für den Einfluss des menschlichen Faktors diente die Präzision der gemessenen Werte. Die Ergebnisse zeigen einen hohen Einfluss des menschlichen Faktors auf das Prüfergebnis und eine Einwirkung des Zeitdrucks besonders auf die Präzision der Messwerte. Hierbei war die Wirkung des individuell wahrgenommenen Zeitdrucks zusammen mit der psychischen Arbeitsbeanspruchung signifikant. Es wurde unter anderem herausgearbeitet, dass durch eine gute Vorbereitung auf die Prüfung, z.B. durch die sorgfältige Einweisung und ein vorgeschaltetes Fertigkeitstraining an Vergleichskörpern, die Zuverlässigkeit der Prüfergebnisse verbessert werden kann. Insgesamt hatte der Faktor 'Organisation' neben der 'Erfahrung' einen hohen Einfluss auf das Leistungsvermögen der Prüfer. Die Projektergebnisse wurden im Abschlussbericht des Forschungsvorhabens SR2514 dargestellt, es wurden drei Empfehlungen zur Vorbereitung und Einweisung der Prüfer, zur Stärkung der Verantwortung der Prüfaufsicht und zum 4-Augen-Prinzip formuliert. Die Empfehlungen wurden in der KTA- Regel 3201.4 'Komponenten des Primärkreises von Leichtwasserreaktoren; Teil 4: Wiederkehrende Prüfungen und Betriebsüberwachung (RÄE Fassung 2010-11)', umgesetzt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Human factors KW - ZfP KW - Ultraschallprüfung KW - UT KW - Zeitdruck PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-251610 UR - http://jt2011.dgzfp.de/Portals/jt2011/BB/mi2c3.pdf SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Mi.2.C.3) SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25161 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bertovic, Marija A1 - Müller, Christina A1 - Kanzler, Daniel A1 - Fahlbruch, B. A1 - Pitkänen, J. A1 - Ronneteg, U. T1 - 'Human factors' bei der Datenauswertung der zerstörungsfreien Prüfung am Beispiel der nuklearen Endlagerung N2 - Für eine ganzheitliche Betrachtung der Sicherheit bei der zerstörungsfreien Prüfung (ZfP) ist es unvermeidlich neben der Technik auch den Prüfer und die Prüforganisation einzubeziehen. Die Prüfung der Unversehrtheit von Endlagerbehältern ist eine eine sicherheitstechnisch wichtige Anwendung. Die Betreiber der geplanten finnischen und schwedischen Endlager, Posiva und SKB, kapseln den radioaktiven Abfall in Kupferkanistern ein und deponieren die Kanister dann in Felsgestein in einer Tiefe von ca. 500m. Die Kanister bestehen aus einem zylinderförmigen Kupfermantel mit einem Deckel und einem Boden, die zusammen die Außenumhüllung ergeben sowie einer Gusseisenmatrix für die Brennstäbe. Alle Komponenten werden auf ihre Dichtheit bzw. strukturelle Unversehrtheit mittels zerstörungsfreier Prüfmethoden geprüft, um sicher zu stellen, dass im Material und in den Schweißnähten keine kritischen Defekte vorhanden sind, die zu Freisetzungen in die Umgebung führen könnten. Vier ZfP Methoden (Ultraschall-, Wirbelstrom- und radiographische Prüfung, und die visuelle Prüfung anhand einer Kamera) werden mechanisiert durchgeführt, die gewonnenen Daten werden von qualifizierten Fachleuten ausgewertet und bieten so die Möglichkeit, dass Fehler entstehen. Das 'Human Factor'- Untersuchungskonzept besteht aus der Identifizierung potenzieller menschlicher Fehler, deren Ursachen und Präventionsmethoden. Mit Hilfe einer abgewandelten FMEA (Failure Modes and Effects Analysis) wurden mögliche Risiken identifiziert, die die Wahrscheinlichkeit für das Auftreten menschlicher Fehler bei der Datenauswertung erhöhen. Einige dieser Risiken sind beispielsweise Verantwortungsdiffusion beim 4-Augen-Prinzip, Übervertrauen in die Technik bei der automatischen Identifikation von Defekten sowie der Aufmerksamkeitsverlust bei dynamischer Bildbetrachtung. Deren Wirkung wird derzeit experimentell überprüft, um Ansatzpunkte für Optimierungen zu ermitteln und damit die Gesamtzuverlässigkeit des Systems zu verbessern. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Human factors KW - UT KW - ET KW - ZfP KW - Nukleare Endlagerung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-251584 UR - http://jt2011.dgzfp.de/Portals/jt2011/BB/p42-ku~1.pdf SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P 42) SP - 1 EP - 2 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25158 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kanzler, Daniel A1 - Müller, Christina A1 - Pitkänen, J. T1 - Konzept für den Einsatz der Bayes'schen Statistik: In der Zuverlässigkeitsbestimmung von zerstörungsfreien Diagnosesystemen - Das Problem zu kleiner experimenteller Datenmengen N2 - Die statistische Qualitätskennzahl 'Probability of Detection (POD)' hängt von der Anzahl der zugrunde liegenden, brauchbaren Ergebnisse ab. Ist die Datenmenge niedrig, so ist auch die Aussage der POD eher beschränkt. Dennoch heißt eine große Zahl von Daten, nicht gleichzeitig, dass die POD für den realen Einsatz in der Produktion genügt. Es muss unterschieden werden, auf welcher Basis – unter welchen konkreten Bedingungen - die Daten erhoben wurden. Als wichtigste Ergebnisse zählen die Messergebnisse aus der Produktion der später verwendeten Prüfobjekte für den konkreten Einsatz. Noch bevor die zerstörungsfreien Prüfmethoden zuverlässig in der Produktion eingesetzt wurde, muss jedoch nachgewiesen werden, dass die real vorkommenden Fehler gefunden werden können. Das bedeutet, zu einem Zeitpunkt, an dem noch nicht ausreichend Daten vorhanden sind. Während für die realistische Prüfung die notwendige Anzahl der verschiedenen Fehler meist nicht erreicht wird, so fehlen bei der Bewertung der künstlichen Fehler wichtige Parameter und Einflussgrößen. Es muss somit eine Zwischenlösung gesucht werden, in der die Informationen von beiden Prüfungen kombiniert werden. Mit der Bayes’schen Statistik ermöglicht die Mathematik diese Informationen miteinander zu kombinieren und somit beide Informationen mit in die Bewertung einfließen zu lassen. Praktisch angewandt und erprobt wird die Vorgehensweise gemeinsam mit der Firma POSIVA, die sich mit dem Bau eines Endlagers für hoch-radioaktiven Abfall in Finnland beschäftigt. Hier wird als eine der technischen Barrieren ein Kupferbehälter für die Aufbewahrung der verbrauchten Brennstäbe genutzt. Dieser Kupferbehälter wird mit mehreren zerstörungsfreien Prüfmethoden geprüft. Anhand von Radiographiedaten wird gezeigt, dass die Aussagekraft der realistischen Fehlerdaten mit Hilfe der künstlichen Referenzfehlerdaten untermauert werden kann. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Bayes'sche Statistik KW - POD KW - Fehlende Datenmenge PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-251598 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Mi.3.C.3) SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25159 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - An efficient and clean fuel for high temperature process industries N2 - The use of energetic materials as a main fuel in high temperature process industries are not known to the scientific community as such. This paper highlights some of the features and advantages of using organic peroxides especially di-tert-butyl peroxide (DTBP) in high temperature process industries. The feasibility of using DTBP as a main or supporting fuel in process industries have also been justified with the help of Computational Fluid Dynamics (CFD) simulations. For peroxides requirement of less fuel and air for the same amount of heat flux has been shown. The resulted emission from the combustion of DTBP is also discussed. T2 - 11th Conference on Energy for a Clean Environment CY - Lisbon, Portugal DA - 2011-07-05 KW - Energetic materials KW - Process industries KW - Organic peroxide KW - Di-tert-butylperoxide (DTBP) KW - CFD simulation KW - Emission PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247071 SP - 1 EP - 10 AN - OPUS4-24707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Thiele, Marc A1 - Pirskawetz, Stephan A1 - Baeßler, Matthias A1 - Rogge, Andreas T1 - Untersuchung der Schädigungsevolution in Beton unter Ermüdungsbeanspruchung mit Hilfe der Schallemissionsanalyse N2 - Unter zyklischen Belastungen findet im Beton, wie bei anderen Materialien auch, ein Ermüdungsprozess statt, der letztlich im Versagen des Materials enden kann. Im derzeitigen Erkenntnisstand zum Materialverhalten des Betons gibt es gerade bei dessen Ermüdungsverhalten noch viele nicht oder nicht ausreichend geklärte Fragestellungen. Deshalb wurde in Laborversuchen das Ermüdungsverhalten von Beton unter Druckschwellbeanspruchungen untersucht. Im Fokus dieser Untersuchungen standen dabei die während der Lebensdauer im Materialgefüge ablaufenden Prozesse, die zur Schädigung des Gefüges und schließlich auch zum Ermüdungsversagen führen können. In den Ermüdungsversuchen wurden versuchsbegleitend Dehnungsmessungen, Ultraschall-Laufzeitmessungen und Schallemissionsmessungen an den Proben zur Erfassung der Schädigungsevolution eingesetzt. Die Schallemissionsmessung ist dabei ein wichtiges Instrument, da sie die Rissentwicklungsprozesse detektiert, die die Ursache für die Materialschädigung sind. Mit ihr konnten die unterschiedlichen Phasen der Rissentwicklungen über die gesamte Lebensdauer der Betonproben festgestellt werden. Diese Phasen sind gekennzeichnet durch sich stabilisierende, stabile und instabile Rissprozesse, die entsprechende Auswirkungen auf das Materialverhalten haben. Ein Vergleich mit den Ergebnissen der anderen Messtechniken zeigt den entsprechenden Einfluss der Rissentwicklungen auf die Materialeigenschaften des Betons. T2 - 18. Kolloquium Schallemission CY - Wetzlar, Deutschland DA - 27.10.2011 KW - Beton KW - Ermüdung KW - Schallemission PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247223 SN - 978-3-940283-37-5 IS - DGZfP-BB 131 (Vortrag 02) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishra, Kirti Bhushan A1 - Wehrstedt, Klaus-Dieter T1 - Combustion of peroxy-fuels N2 - The diffusion flames of organic peroxides exhibit quite different characteristics than hydrocarbons. What makes them interesting to study is their fast burning behaviour. As a result the flame temperature enhances and so does the thermal radiation. Due to all these they demand safe handling during processing. However, they can be utilised at several places in different industries where a fuel with fast burning, high temperature and intense radiation are desired. Some of the possibilities to use them as a main or supporting fuel in a wide range of industrial utilities are the major content of this paper. T2 - ERCOFTAC conference - Highly resolved experimental and numerical diagnostics for turbulent combustion CY - Rouen, France DA - 25.05.2011 KW - Energetic materials KW - Process industries KW - Organic peroxide KW - Di-tert-butyl peroxide (DTBP) KW - CFD simulation KW - Emission PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247083 SP - 1 EP - 5 AN - OPUS4-24708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Ewert, Uwe A1 - Zvizdic, D. A1 - Krstelj, V. T1 - Die EFNDT Arbeitsgruppe 5 'Öffentliche Sicherheit mit ZfP-Techniken' neu formiert N2 - Für die öffentliche Sicherheit wird gesorgt, indem Gefahren rechtzeitig entdeckt werden. Deren Ursprung kann im technischen oder menschlichen Versagen liegen, womit im englischen Sprachraum zwischen 'Safety' und 'Security' unterschieden wird. Hinsichtlich der Folgen verschwimmt aber dieser Unterschied, obwohl für deren Verhinderung unterschiedliche Zuständigkeiten existieren. Bezüglich des gemeinsamen Interesses und auch überlappender Methoden und Vorgehensweisen würden beide Seiten gewinnen können, wenn es eine Brücke zwischen ihnen gäbe. Eine solche zu schaffen hat sich die EFNDT Arbeitsgruppe (Working Group) 5 zur Aufgabe gestellt. Gestaltet werden soll sie durch gemeinsame Veranstaltungen und Seminaren, die zur Bildung von Konsortien und der Durchführung gemeinsamer Projekte führen sollen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 03.05.2011 KW - EFNDT Working Group 5 KW - Technische und öffentliche Sicherheit KW - Gemeinsamkeiten in ZfP und öffentlicher Sicherheit KW - Brückenbildung zwischen Zuständigkeitsbereichen PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250631 SN - 978-3-940283-33-7 VL - 127 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25063 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Fratzscher, Daniel A1 - Zscherpel, Uwe A1 - Ewert, Uwe A1 - Hasenstab, A. A1 - Bücherl, T. A1 - Schillinger, B. T1 - Partielle Tomographie mit Neutronen zur Beurteilung von Leimschichten in Holz N2 - Verleimte Holzproben wurden je nach Größe mit thermischen (ANTARES) bzw. schnellen Neutronen (NECTAR) an der Forschungs-Neutronenquelle Heinz Maier-Leibnitz (FRM II) der Technischen Universität München in Garching untersucht. Entweder ließen die durchstrahlbare Schichtdicke oder die eingeschränkte Strahlgeometrie es nicht zu, das Probenteil allseitig zu durchstrahlen. Um dennoch innere Strukturen wie Leimschichten zumindest mit einem eingeschränkten Winkelbereich tomographisch darzustellen, wurde mit Hilfe des Slice-Theorems erfolgreich rekonstruiert. Ein Brett von 2 cm Dicke wurde mit thermischen Neutronen erfolgreich untersucht, ein größeres mit schnellen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Neutronentomographie KW - Eingeschränkter Winkelbereich KW - Holz PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250649 SN - 978-3-940283-33-7 VL - 127 SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Osterloh, Kurt A1 - Fratzscher, Daniel A1 - Jechow, Mirko A1 - Bücherl, T. A1 - Schillinger, B. A1 - Hasenstab, A. A1 - Zscherpel, Uwe A1 - Ewert, Uwe T1 - Limited view tomography of wood with fast and thermal neutrons N2 - Neutrons are absorbed particularly by hydrogen containing materials so they can be used as a tool for visualising heterogeneous density distributions of organic materials. Penetration limits are set by the layer thicknesses and the neutron energies applied. In case of specimens with a flat shape the situation may be encountered that the object only could be penetrated in selected directions. In addition, the overall size may exceed the beam diameter and thus the viewing window if a certain region of interest should be studied by tomography without destroying the integrity of the specimen. This study shows the capabilities and limits of thermal and fast neutrons to investigate flat wooden specimens such as boards and girders by neutron tomography under such circumstances. Taking projections was impaired either by the limits of penetrability or by the total size of the object. As a consequence, projections were included for reconstruction only from a limited angular range of 90°. It could be shown that an approach based on the slice theorem was capable to visualise structural features along the beam directions while simply omitting the perpendicular ones without causing additional artefacts. Small samples with a thickness of up to 2 cm but several times broader could be studied with the ANTARES facility of the FRM II neutron source in Garching providing thermal neutrons while larger objects required a beam of higher energy as available in the NECTAR facility of the same institution. The fast (fission) neutrons (1.5 – 2 MeV) of this site allowed investigating an area of interest inside a girder with a cross section of 23.5 x 49 cm². Internal features such as inclusions could be detected as well as a heterogeneous density distribution in glue layers. T2 - International symposium on digital industrial radiology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Computed tomography KW - Slice theoreme KW - Limited angle tomography PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250663 SN - 978-3-940283-34-4 VL - 128 SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-25066 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlichting, Joachim A1 - Ziegler, Mathias A1 - Pelkner, Matthias A1 - Maierhofer, Christiane A1 - Kreutzbruck, Marc T1 - Kameragestütztes Flying-Spot-Verfahren zur Risserkennung N2 - In dieser Arbeit wird ein kameragestütztes Verfahren zur Flying- Spot-Thermografie vorgestellt. Die Anregung wird über einen Diodenlaser mit einem optischen Scanner realisiert. Bei der Auswertung kommt ein effizienter und robuster Algorithmus zum Einsatz, der direkt auf die mit der Kamera aufgenommene Thermografiesequenz angewendet werden kann, ohne auf eine Synchronisation zwischen Kamera und Lasersystem angewiesen zu sein. Daher eignet sich diese Herangehensweise besonders zur Nachrüstung bestehender Thermografiesysteme. Die prinzipielle Eignung dieser Methode wird anhand einer Messung an einem Schienenstück mit Rollkontaktermüdungsrissen gezeigt. Als Referenzverfahren werden die Magnetpulverprüfung und eine auf GMR (Giant Magnetoresistance)- Sensoren basierende Streufeldmessung herangezogen. Mit dem thermografischen Verfahren konnten sämtliche enthaltenen Fehler erkannt werden. Dabei wurden Risse im mm-Abstand getrennt nachgewiesen, was etwa der geometrischen Auflösung der eingesetzten Kamera entspricht. T2 - Thermographie-Kolloquium 2011 CY - Stuttgart, Germany DA - 29.09.2011 KW - Flying-Spot Thermografie KW - Diodenlaser KW - Rissortung KW - Magnetpulverprüfung KW - GMR-Sensoren PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-246220 SN - 978-3-940283-36-8 IS - DGZfP-BB 130 (Vortrag 09) SP - 1 EP - 6 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24622 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Ziegler, Mathias A1 - Kunert, M. A1 - Goldammer, M. T1 - Entwicklung von Referenzprobekörpern für die Standardisierung der Blitzthermografie N2 - Die aktive Thermografie wird in der Industrie zunehmend in verschiedenen Bereichen zur Qualitätssicherung, Zustandsdiagnose und Zustandsüberwachung eingesetzt. Bestehende Normen zur Thermografie beschreiben die Grundlagen, Geräte und Begriffe. In diesem Beitrag wird über ein Projekt berichtet, dessen Ziel die Erarbeitung einer Prüfnorm zur Blitzthermografie ist. Diese sollte neben der Auswahl geeigneter Gerätekomponenten, der Auswertungsverfahren und der Vorgehensweise bei der Prüfung auch die Beschreibung geeigneter Referenzprobekörper enthalten, die eine Bewertung der Messapparatur und eine Qualitätssicherung der Prüfung ermöglichen. T2 - Thermographie-Kolloquium 2011 CY - Stuttgart, Germany DA - 29.09.2011 KW - Aktive Thermografie KW - Blitzanregung KW - Prüfnorm KW - Referenzprobekörper PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-246230 SN - 978-3-940283-36-8 VL - 130 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-24623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachsmuth, Janne T1 - Wellenform basierte Quellenlokalisierung im Vergleich zu konventionellen Methoden N2 - Für eine 10 mm dicke Stahlplatte kann ein Bandpass so gesetzt werden, dass alle vorhandenen Wellenmoden mit derselben Schallgeschwindigkeit eintreffen. Anhand von Ortungsabweichungen und Ortungsunsicherheitswerten kann gezeigt werden, dass im Vergleich zu herkömmlichen Methoden der Quellenortung die Ortungsgenauigkeit durch eine Frequenzfilterung verbessert werden kann. T2 - 18. Kolloquium Schallemission CY - Wetzlar, Deutschland DA - 27.10.2011 KW - Schallemissionsprüfung KW - Ermüdungsrisswachstum KW - Korrosion PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-246612 SN - 978-3-940283-37-5 SP - 1 EP - 6 PB - DGZfP-BB 131 AN - OPUS4-24661 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Regina A1 - Kreutzbruck, Marc A1 - Maierhofer, Christiane T1 - Numerische Verfahren für die aktive Thermografie zur Untersuchung von Rückwandgeometrien N2 - In diesem Beitrag werden numerische Verfahren zur Erkennung und Charakterisierung von Fehlstellen, Schichtdicken, Wanddicken und Inhomogenitäten mittels aktiver Thermografie vorgestellt. Eine uantitative Beurteilung der nicht immer zugänglichen Rückwand eines Bauteils (Minderdicken) ist durch Inversion thermografischer Messdaten möglich. Diese quantitativen Informationen können durch iterative Methoden vom Gauß-Newton-Typ (Inversion) gewonnen werden. Als reale Prüfobjekte werden ca. 2 cm dicke PVC-Platten mit örtlich variierender Rückwandgeometrie untersucht. Die Erwärmung erfolgt mit Blitzlampen, welche die PVC-Platte kurzzeitig um mehrere K erwärmt. Ein wichtiger Teil der Inversion ist die Simulation des Experiments, welche mit Finite-Elemente-Methoden (FEM) in 2D realisiert wird. Da Inversion und active Thermografie automatisierbar sind, bietet die Kombination breite Anwendungsgebiete innerhalb der Industrie. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Deutschland DA - 30.05.2011 KW - Inversion KW - Aktive thermografie KW - Wanddicke KW - Rückwand KW - Minderdicken KW - Schichtdicken PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-252812 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P45) SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25281 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völz, Uwe A1 - Mrasek, Heinz A1 - Heckel, Thomas T1 - Querfehlerprüfung an anisotropen Engspaltschweißnähten mit Gruppenstrahlern N2 - Die Prüfung von anisotropen Schweißnähten auf Querfehler stellt auch heute noch eine Herausforderung für die Ultraschallprüfung dar. Das gilt insbesondere für das Auffinden kleiner rissartiger Fehlstellen in einer unbeschliffenen Wurzel. Ursachen dafür sind zum einen das ausgeprägte Beugungs-, Streuungs- und Reflexionsverhalten solcher Nähte und zum anderen die störenden Formanzeigen aus dem Wurzelbereich, die sicher von den Fehlstellen unterschieden werden müssen, um Fehlinterpretationen bei der Bewertung der Anzeigen zu vermeiden. In der vorliegenden Arbeit werden an einer 85 mm dicken und 6 bis 10 mm breiten Engspaltschweißnaht mit stängelkristalliner Struktur rissartige Testfehler in Form erodierter Nuten untersucht. Die 2 und 4 mm tiefen Nuten sind mit 5 mm Länge kürzer als die Wurzelbreite. Die Wurzel ist nicht beschliffen und hat eine Überhöhung von ca. 2 mm. Ziel ist es, die Fehlstellen von den Form- und Gefügeanzeigen zu unterscheiden und sicher zu detektieren. Eine Größenbestimmung ist nicht vorgesehen. Durch den Einsatz der Gruppenstrahlertechnik ist es möglich, optimale Einschallparameter zu finden, mit denen diese Aufgabe gelöst werden kann. Es werden zwei azimutal schwenkende lineare Gruppenstrahlerprüfköpfe mit Vorsatzkeil in SE-Technik verwendet, die so auf beiden Seiten der Schweißnaht angeordnet sind, dass sich ihre Schallfelder unabhängig von der Einschallrichtung in der Schweißnahtwurzel überlagern. Damit ist es möglich, optimale Einschallwinkel für das Prüfproblem zu finden und in einer Prüffahrt gleichzeitig in beiden Einschallrichtungen längs der Schweißnaht zu prüfen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Ultraschall KW - Gruppenstrhaler KW - Anisotropie KW - Austenit KW - Nickellegierung KW - Querfehler KW - Schweißnaht PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-252777 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P49) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25277 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kitze, Jessica A1 - Boehm, Rainer A1 - Brackrock, Daniel A1 - Montag, Hans-Joachim A1 - Völz, Uwe A1 - Brekow, Gerhard A1 - Kreutzbruck, Marc T1 - SAFT-Rekonstruktion und 3D Lokalisation aus Ultraschallmessungen mit Matrix- und Linear-Arrays in Tauchtechnik N2 - Die Kombination der Synthetic Aperture Focusing Technique (SAFT) mit der Tauchtechnik stellt eine besondere Herausforderung dar. Zwei für SAFT notwendige Bedingungen – die große Schallbündeldivergenz und die Kenntnis über den Ort des Senders bzw. des Empfängers, der für die phasenrichtige Überlagerung der Echosignale genau bekannt sein muss – lassen sich einfach erfüllen, wenn kleine, fast punktförmige Sensoren direkt auf der Oberfläche des Prüfobjektes ankoppeln. Diese Anordnung ist in der Regel nicht vereinbar mit den praktischen Ansprüchen an die Signalqualität und die Flexibilität der Prüftechnik. Werden jedoch Prüfköpfe mit üblichen Abmessungen und zudem noch mit Vorlaufstrecken verwendet, dann ist die Bestimmung der Sensororte und der Schalllaufwege durch die brechende Fläche nicht mehr trivial, wenn man die für SAFT geforderte Genauigkeit in Rechnung stellt. Etwas anderes, aber ein im Prinzip einfacher Weg zur räumlichen Lokalisation von Echoquellen ist die Auswertung des 2D Sektorscans eines Matrixarrays und dessen dreidimensionale Darstellung. Durch gezielte Steuerung des Arrays gelingt auf einfache Weise die ortsrichtige Zuordnung. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Matrix-Array KW - Linear-Array KW - SAFT-Rekonstruktion in Tauchtechnik KW - Räumliche Darstellung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-252788 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.3.A.2) SP - 1 EP - 11 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25278 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Kupsch, Andreas A1 - Müller, Bernd R. T1 - Correction of diffuse X-ray detector based background N2 - A novel approach to strongly suppress artifacts in radiography and computed tomography caused by the effect of diffuse background Signals (“backlight”) of 2D X-ray detectors is suggested. Depending on the detector geometry the mechanism may be different, either based on the optical scattering of the fluorescent screen materials into optical detection devices or Compton or X-ray fluorescence scattering by the detector components. Consequently, these erroneous intensity portions result in locally different violations of Lambert Beer’s law in single projections (radiographs). When used as input data for computed tomography these violations are directly observed via modulation of the projected mass as a function of the rotation Phase and the sample’s aspect ratio (dynamics). The magnitude of the diffuse Background signal depends on the detector area covered by the projected sample. They are more pronounced the smaller the shaded area and the stronger the total attenuation. Moreover, the local intensity mismatch depends on the attenuation of the sample. We present very basic reference data measured with multiple metal foils at a synchrotron radiation source. Beam hardening artifacts can be excluded due to the monochromatic radiation. The proposed correction procedure assumes a constant (non-local) scattering mechanism. T2 - DIR 2011 - International symposium on digital industrial raidology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Backlight KW - X-ray detector KW - Fluorescence screen KW - Synchrotron radiography KW - Computed tomography PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-243589 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (Poster 24) SP - 1 EP - 7 PB - Deutsche Gesellscahft für Zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bellon, Carsten A1 - Gollwitzer, Christian A1 - Fratzscher, Daniel A1 - Ewert, Uwe A1 - Jaenisch, Gerd-Rüdiger T1 - Simulation of complex scan paths for 3D reconstruction N2 - X-ray computed tomography (CT) is a volumetric (3D) Imaging diagnostic method, well established in the medical field, and in industrial NDE as well. Developments in industrial CT aim to extent the applicability to complex structures, which do not allow the access of all directions. This are e.g. limited view, data and angle CT applications. New reconstruction algorithms are required on one side, and the accuracy has to be improved on the other side. Numerical Simulation can support such developments by providing well defined data sets for the testing of reconstruction algorithms. This approach of virtual CT is realized within the radiographic simulator aRTist, developed by BAM. The poster shows the possibilities of this tool to consider complex scan paths. Simulated data sets have been reconstructed by an versatile backprojection algorithm. T2 - International symposium on digital industrial radiology and computed tomography CY - Berlin, Germany DA - 20.06.2011 KW - Radiographie KW - Computer-Simulation KW - 3D-Rekonstruktion PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-243928 SN - 978-3-940283-34-4 IS - DGZfP-BB 128 (Poster 17) SP - 1 EP - 4 PB - Deutsche Gesellschaft für zerstörungsfreie Prüfung e.V. (DGZfP) AN - OPUS4-24392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Feistkorn, Sascha A1 - Taffe, Alexander T1 - Die POD - eine Vorgehensweise zum qualitativen Gütenachweis zerstörungsfreier Prüfverfahren im Bauwesen am Beispiel des Impulsradars N2 - Die POD (Probability of Detection) hat sich als statistisches Werkzeug für die Bewertung der Zuverlässigkeit zerstörungsfreier Prüfsysteme in der klassischen ZfP bewährt. Aus diesem Grund wird die Methode der POD auf die zerstörungsfreie Prüfung im Bauwesen übertragen, um erstmals eine objektive Antwort auf zerstörungsfreie Prüfungen geben zu können, denen eine qualitative Fragestellung zugrunde liegt. Dies geschieht an der Prüfaufgabe der Ortung metallischer Reflektoren in Abhängigkeit Ihrer Tiefenlage mithilfe des Impulsradars. Dazu wird nachgewiesen, dass eine Übertragung und Anwendung der POD für die objektive Bewertung dieser Prüfaufgabe zulässig ist. Nach der Konzipierung und Fertigung von Testkörpern werden die Ergebnisse der POD(a)-Analyse vorgestellt, die erstmal eine Charakterisierung und einen Vergleich unterschiedlicher Radarprüfsysteme anhand eines objektiv ermittelten Kennwerts ermöglichen. Außerdem können Einflussgrößen auf die Detektionstiefe eines metallischen Reflektors erstmals quantifiziert werden. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Impulsradar KW - Probability of detection KW - POD KW - ZfPBau KW - Gütenachweis KW - Qualitative Prüfaufgabe PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-248866 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24886 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ehrig, Karsten A1 - Bartscher, M. A1 - Goebbels, Jürgen A1 - Koch, M. A1 - Staude, Andreas T1 - Einfluss von Materialkombinationen auf das dimensionelle Messen mit Mikro-Computertomographie am Beispiel eines werkstücknahen Testkörpers N2 - Die Computertomographie (CT) hat sich als dimensionelle Messmethode in der industriellen Produktion etabliert. Durch Messungen an speziellen Prüfkörpern ist es möglich, quantitative Informationen über die metrologischen Eigenschaften dimensioneller Messungen zu erhalten. In dieser Arbeit wird einen Aluminium-Guss-Prüfkörper (120 mm x 90 mm x 60 mm) benutzt, mit dem – in der vorliegender Form – auch der Einfluss von Materialien unterschiedlicher Schwächung auf dimensionelle CT-Messungen untersucht werden kann. Der Prüfkörper ist in vier Segmente zerteilt, so dass auch innenliegende, raue Gussfreiformflächen der taktilen Koordinatenmessung zugänglich sind. Durch adaptierte Rubinkugeln als Referenzstrukturen können die CT-Messdaten in taktile Referenz-Koordinatensysteme überführt werden. Um den Einfluss von Materialien unterschiedlicher Schwächung auf das dimensionelle Messen mit CT zu untersuchen, wurden stärker schwächende ZTA-Störkugeln (Zirconia Toughened Alumina) mit zur Ausrichtung geeigneter Symmetriebrechung in der Nähe von ausgewählten taktilen Messstellen angebracht. Zur Bewertung der Messabweichungen dienen taktile Referenzmessungen an den ZTA-Kugeln sowie taktile Messungen an den Freiformflächen des Gussteils, wobei durch ein iteratives Antastverfahren eine verbesserte Erfassung der Geometrie auch bei starken lokalen Oberflächenkrümmungen sichergestellt wird. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Mikro-CT KW - Dimensionelles Messen KW - Testkörper KW - Multimaterial PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-248878 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.1.B.2) SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24887 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachsmuth, Janne A1 - Bohse, Jürgen T1 - Schallemissionsanalyse von Schadensmechanismen an Feinkornstahl N2 - In dieser Arbeit werden geschweißte Platten aus dem Feinkornstahl P460NL1 untersucht. Korrosion und Ermüdungsrisswachstum werden als Schadensmechanismen in das Material eingebracht und auf ihre Nachweisbarkeit in Plattenversuchen geprüft. Die Schallemissionssignale wurden nach primären und sekundären Quellmechanismen getrennt und ihr Einfluss auf die Gesamtemission analysiert. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-248902 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.2.C.2) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ortwein, Hans-Peter A1 - Bohse, Jürgen A1 - Trappe, Volker A1 - Hickmann, Stefan T1 - Untersuchung des Zwischenfaserrisswachstums in Faserverbundwerkstoffen mit Schallemissions- und Röntgenrefraktionsverfahren N2 - Hinsichtlich Materialermüdung und Betriebsfestigkeit in Faserkunststoffverbunden besteht - verglichen mit anderen Aspekten des Faserverbundleichtbaues – noch erheblicher Forschungsbedarf. Schon weit vor den globalen Festigkeiten des Laminates treten eine Vielzahl von Zwischenfaserbrüchen und vereinzelte Faserbrüche auf. Die Dichte dieser Mikrorisse soll hier als Indikator für den Zustand des Verbundes genutzt werden. Ihre Ermittlung stellt insbesondere bei Kohlenstofffasern eine Herausforderung dar. Über vergleichende Messungen mit der Schallemissionsanalyse (SEA) und der Röntgenrefraktionsscans (RR) wird die Entwicklung der Rissdichte bei Belastung untersucht. Die SEA zeichnet die Entstehung der Risse auf und kann wegen der kompakten Messtechnik auch gut am Bauteil eingesetzt werden. Die RR beobachtet die Änderung der inneren Grenzflächen, die ebenfalls die Entwicklung der Rissdichte widerspiegelt. Sie ist allerdings zurzeit nur als Laborverfahren geeignet. Der Vortrag berichtet(e) über den aktuellen Stand des vergleichenden Einsatzes beider Verfahren an Flachproben und innendruckbelasteten Rohrproben. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Deutschland DA - 30.05.2011 KW - Schallemissionsprüfung KW - Röntgenrefraktionsmessung KW - Faserkunstoffverbund KW - Druckbehälter PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-248913 SN - 978-3-940283-33-7 SP - Mi.4.A.1 - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reimund, Verena A1 - Pelkner, Matthias A1 - Neubauer, Andreas A1 - Thomas, Hans-Martin A1 - Kreutzbruck, Marc T1 - Automatische Detektion von Rissen in Stahlbauteilen unter Verwendung von GMR-Sensoren bei der magnetischen Streuflussprüfung N2 - GMR-Sensor Arrays ermöglichen eine örtlich hoch aufgelöste Messung magnetischer Streufeldamplituden an Stahlbauteilen, bei der abhängig von der Größe der zu prüfenden Oberfläche erhebliche Datenmengen erzeugt werden. Eine automatische Detektion von Rissen kann anschließend mittels digitaler Bildverarbeitung erreicht werden, welche hauptsächlich auf einer Kantenerkennung basiert. Diese wurde anhand einer Magnetometer-Messung getestet, die an einem zylindersymmetrischem Bauteil mit funkenerosiv eingebrachten Rissen geringer Tiefe durchgeführt wurde. Die erzielte Selektion der Defekte wird für eine angestrebte Rekonstruktion der Defektgeometrie benötigt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Deutschland DA - 30.05.2011 KW - GMR-Sensor KW - Streuflussprüfung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253451 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Mo.3.C.4) SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25345 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kotschate, Daniel A1 - Gohlisch, Stephan A1 - Heckel, Thomas A1 - Sondermann, F. T1 - Bildgebende Ultraschallhandprüfeinrichtung für die Ausbildung N2 - Um den vermehrten Einsatz von mechanisierten Prüfeinrichtungen bei der Ultraschallprüfung in der Ausbildung Rechnung zu tragen, ist es wünschenswert, dieses Themenfeld bereits zu einem frühen Zeitpunkt in die Ultraschallkurse zu integrieren. Aus diesem Grund wurde für die Ausbildung bei der DGZfP in Zusammenarbeit mit der BAM ein teilmechanisiertes Ultraschall-Prüfsystem entwickelt. Das System basiert auf einem handelsüblichen Ultraschallgerät für die Handprüfung und einem Netbook-Computer. Die berührungslose Positionserfassung wird über den Blenden-Ausgang des Ultraschallgerätes getriggert und die Daten werden mittels Infrarot- und Bluetoothtechnik übertragen. Dies ermöglicht einen kompakten und portablen Aufbau mit kurzen Einrichtzeiten, der sich im Rahmen einer Lehrveranstaltung effektiv einsetzen lässt. Die Ergebnisdarstellung erfolgt mit C-Bildern. An einfachen Übungsstücken können die Kursteilnehmer, dicht an die Handprüfung angelehnt, die Methoden und Randbedingungen einer mechanisierten Prüfung erfahren. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Ultraschallprüfsystem KW - Ultraschallprüfung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253826 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Poster 89) SP - 1 EP - 4 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25382 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Boehm, Rainer A1 - Gohlke, Dirk T1 - Optimierung von Ultraschall-fokusprüfköpfen beim Einsatz an stark gekrümmten Oberflächen N2 - Bei der Prüfung von gekrümmten Bauteilen in Tauchtechnik muss man die Veränderung des Schallfeldes durch die Form der Oberfläche berücksichtigen. Insbesondere bei hochauflösenden Ultraschallprüfungen mit Fokusprüfköpfen kommt es hierbei zu drastischen Verzerrungen des Schallfeldes. Diese Verzerrungen sind bei der Empfindlichkeitseinstellung sowie bei der Auslegung von Fokuspunkt- und Spurabstand zu berücksichtigen, um eine ausreichende Prüfempfindlichkeit zu erreichen. Es werden Beispiele von Simulationsrechnungen an typischen Prüfanordnungen vorgestellt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Fokusprüfköpfe KW - Gekrümmte Oberflächen PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253841 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Poster 62) SP - 1 EP - 5 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25384 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gohlke, Dirk A1 - Kotschate, Daniel A1 - Heckel, Thomas T1 - Visualisierung der Volumenmessdaten von hochauflösenden Ultraschalltauchtechnikprüfungen N2 - Die heutigen Anforderungen an Bauteile und deren Materialien werden immer höher. Somit steigen auch die Anforderungen an die notwendigen Prüfverfahren zur Qualitätsbestimmung bzw. –erhaltung. Durch den optimierten Einsatz von mechanisierten Prüfverfahren und der Verwendung von Visualisierungsalgorithmen wird es möglich, Prüfergebnisse mehrdimensional und farbcodiert z.B. als Überblicksansicht über das Volumen des geprüften Bauteils zu bekommen. Bei der hochauflösenden Volumenprüfung eines Bauteils mittels Ultraschall-Tauchtechnikverfahren, bei dem anstelle einer einfachen Ja/Nein – Aussage eine detaillierte Analyse erforderlich ist, ist es notwendig, alle Messdaten, d.h. jedes A-Bild an jedem Ort, zu speichern. Bei der Auswertung der Daten werden vorwiegend 2D-Darstellungen, wie z.B. das C-Bild der gescannten Fläche, B-Bilder der Scan- und Index-Ebene sowie das A-Bild an der jeweiligen Position verwendet. Um sich z.B. ein Überblick über das Volumen zu verschaffen, werden die B-Bilder der jeweiligen Ebene gescrollt. Bei diesem Verfahren erhält man zwar eine genaue Aussage in den einzelnen Ebenen, aber doch wenig Informationen über die Lage der Anzeigen im Prüfvolumen. Eine 3D-Visualisierung der Volumenmessdaten liefert unter Berücksichtigung der Bauteilgeometrie und einer Farbcodierung der Amplitudenwerte eine übersichtliche Darstellung über Lage, Größe und Verteilung der Anzeigen im Volumen des Bauteils. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Volumenprüfung KW - Tauchtechnik PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253859 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Poster 61) SP - 1 EP - 6 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25385 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heckel, Thomas A1 - Boehm, Rainer A1 - Gohlke, Dirk A1 - Völz, Uwe T1 - Analyseprüfung von Eisenbahnradsatzwellen mit Ultraschall N2 - Die wiederkehrende zerstörungsfreie Prüfung von längs gebohrten Eisenbahnradsatzwellen mit Ultraschall erfolgt im eingebauten Zustand aus der Wellenbohrung heraus. Neben den aufzufindenden Fehleranzeigen erzeugt aufgrund der geometrischen Bedingungen der Radsatzwelle hierbei jeder Querschnittsübergang eine umlaufende Formanzeige in der Ergebnisdarstellung. Durch den Prozess des Aufschrumpfens der Radscheiben auf die Sitze können weiterhin örtlich statistisch verteilte Bereiche im Sitz entstehen, die bei der Ultraschallprüfung Anzeigen hervorrufen, die so genannten Scheinanzeigen. Insbesondere in den Bereichen der Querschnittsübergänge ist zum einen die Prüfsituation sehr komplex, zum anderen ist hier die Wahrscheinlichkeit für eine Rissbildung am höchsten. Bei der Befundanalyse stößt die derzeit verwendete Prüftechnik in diesen Bereichen an ihre Grenzen, so dass nicht immer eine eindeutige Prüfaussage erfolgen kann. Im Bericht werden Lösungsansätze für Analyseverfahren vorgestellt, die auf Basis der Gruppenstrahlertechnik bzw. mit Fokusprüfköpfen in Verbindung mit dem Einsatz von Signalverarbeitung vielversprechende Ergebnisse zur Optimierung dieser Situation aufzeigen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Eisenbahnradsatzwellen KW - Radsatzwellen PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253863 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.2.A.3) SP - 1 EP - 9 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25386 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Spies, M. A1 - Recknagel, J. A1 - Rieß, H. T1 - Schulung zur zuverlässigen Ortung von Bewehrung in Stahlbetonbauteilen von Kraftwerken N2 - In kerntechnischen Anlagen werden Revisionszeiträume genutzt, um unter anderem Anlagenteile nach dem Stand der Technik zu ertüchtigen und um Nachrüstungsmaßnahmen zur Erhöhung der Betriebssicherheit durchzuführen. Solche Anlagenteile werden häufig mittels Dübelplatten befestigt. Die Dübel sind in Stahl-betonbauteile einzubringen, die kraftwerkstypisch mit dichter Bewehrung versehen sind. Zerstörungsfreie Untersuchungen zur genauen Ortung bewehrungsfreier Orte sind hierzu erforderlich. Bei dieser vermeintlich einfachen Prüfaufgabe wurde deutlich, dass in der Praxis Bedarf an verbesserter Anwendungssicherheit der zur Verfügung stehenden ZFP-Verfahren besteht, die eng mit der Ausbildung von Prüfern verbunden ist. Dieser Beitrag berichtet über die bislang im Bereich ZfPBau erstmalig umgesetzte Strategie aus Verfahrensanweisung und Schulung zur zuverlässigen Ortung von Bewehrung an Stahlbetonbauteilen. Sie kann als Muster für weitere ZfPBau-Schulungen zur zuverlässigen Anwendung der Verfahren dienen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Ausbildung KW - Bewehrungsortung KW - Performance demonstration KW - Blindtest KW - Wirbelstrom KW - Radar PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253752 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.2.B.1) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25375 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taffe, Alexander A1 - Kind, Thomas A1 - Stoppel, Markus A1 - Kurz, J. H. T1 - OSSCAR-Bauwerkscanner: Automatisierte Datenaufnahme von Radar, Ultraschall und Wirbelstrom an Spannbetonbauteilen mit bildgebender Darstellung der inneren Konstruktion N2 - Bereits seit vielen Jahren stehen Anwendern der zerstörungsfreien Prüfung im Bauwesen (ZfPBau) zuverlässige Geräte für Radar-, Wirbelstrom- und Ultraschallmessungen an Betonbauteilen zur Verfügung. Doch erst die Kombination dieser drei Verfahren an einer Messfläche erlaubt den maximalen Informationsgewinn über die innere Konstruktion von Stahlbeton- und Spannbetonbauteilen. Mit dem OSSCAR-Bauwerkscanner wurden diese drei Verfahren erstmals zur kombinierten und automatisierten Datenaufnahme an einem Scannerrahmen und unter einer Software vereint. Die Ergebnisse werden bildgebend in frei wählbaren Schnitten dargestellt, was eine Rekonstruktion von Bauteilen erlaubt, für die keine Planunterlagen vorliegen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Zerstörungsfreie Prüfung im Bauwesen KW - Bauwerkscanner KW - Brückenprüfung KW - Ultraschall KW - Radar KW - Wirbelstrom KW - Kombination PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-253767 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Mi.3.B.1) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25376 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duffner, Eric A1 - Gregor, Christian A1 - Bohse, Jürgen T1 - Überwachung der Fertigungsqualität von Faserverbund - Druckbehältern mittels Schallemissionsprüfung N2 - Ziel der Untersuchung ist die Validierung einer Prüfmethodik zur Sicherung der Fertigungsqualität von Faserverbund – Druckbehältern unter realen Fertigungsbedingungen. Das Verfahren basiert auf Merkmalen und zulässigen Grenzwerten, die aus Schallemissionsverläufen bei der Erstdruckprüfung abgeleitet werden. Die Methodik konnte zuvor bereits erfolgreich an Faserverbund – Druckbehältern mit metallischem Liner getestet und patentiert werden. Mit den aktuellen Untersuchungen wurde die Möglichkeit des Erkennens von Fertigungsfehlern in Kohlenstofffaser/Glasfaser – Hybriddruckbehältern mit polymerem Liner evaluiert. Dazu wurden Faserverbund – Druckbehälter mittels Schallemissionsmessung bei einer hydraulischen Erstdruckprüfung überwacht, wie sie (ohne Schallemissionsprüfung) generell zur Qualitätssicherung nach der Fertigung von Faserverbund – Druckbehältern gefordert wird. An Druckbehältern aus einer Serienproduktion wurden die Schallemissionsverläufe registriert und die mittleren Merkmalswerte sowie deren Streuung als Referenz ermittelt. Diese werden mit den Schallemissionsverläufen von Druckbehältern mit gezielt eingebrachten Fertigungsfehlern verglichen. Bei den Fertigungsfehlern handelt es sich um Fehler, die in der Serienproduktion auftreten können und mit den Methoden der herkömmlichen Qualitätssicherung schwer oder gar nicht nachzuweisen sind. Alle untersuchten Druckbehälter wurden im Anschluss an die Erstdruckprüfung auf verschiedene Weise bis zum Versagen (Leckage, Bersten) beansprucht. Damit war es möglich, den tatsächlichen Einfluss der Fertigungsfehler auf den Berstdruck bzw. das Ermüdungsverhalten der Behälter zu verifizieren und die Aussagefähigkeit des Schallemissionsverfahrens zu beurteilen. T2 - 18. Kolloquium Schallemission CY - Wetzlar, Germany DA - 27.10.2011 KW - Faserverbund-Druckbehälter KW - Schallemissionsprüfung KW - Fertigungsüberwachung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-247881 SN - 978-3-940283-37-5 IS - DGZfP-BB 131 (Vortrag 16) SP - 1 EP - 9 AN - OPUS4-24788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlichting, Joachim A1 - Steinfurth, Henrik A1 - Maierhofer, Christiane A1 - Kreutzbruck, Marc T1 - Thermografische Prüfung von Punktschweißverbindungen N2 - Vor allem in der Automobilindustrie wird das Widerstandpunktschweißen im großen Unfang zur Verbindung von Blechen im Karosseriebau verwendet. Durch den anhaltenden Trend zum Leichtbau und den immer höheren Anforderungen an die passive Sicherheit kommt es hier zu einem verstärkten Einsatz innovativer hochfester Stähle. Obwohl es sich beim Punktschweißen um ein lange erprobtes Verfahren handelt, das sich anhand der Prozessparameter und regelmäßiger zerstörender Prüfung überwachen lässt, ist durch diese Entwicklung die Suche nach geeigneten zerstörungsfreien Prüfverfahren wieder aktuell. Wegen der hohen Produktionsgeschwindigkeiten in der automatisierten Fertigung muss sich das Prüfverfahren für eine hundertprozentige Prüfung vollautomatisch mit der typischen Taktrate von etwa einem Hertz durchführen lassen. In dieser Arbeit wird zuerst die prinzipielle Durchführbarkeit der thermografischen Prüfung von Punktschweißverbindungen an speziell präparierten Proben überprüft. Auf dieser Grundlage wird eine Serienuntersuchung an 75 Proben, die sich auf drei Gruppen von Schweißparametern aufteilen und neben optimal geschweißten Proben typische Fehlerbilder repräsentieren, eine Serienuntersuchung gezeigt. Hierzu wird eine Blitzlichtanregung in Transmissionsanordnung verwendet. Es kann gezeigt werden, dass sich mit einer geeigneten Datenaufbereitung die einzelnen Gruppen sicher trennen lassen. Durch eine statistische Bewertung der Ergebnisse kann unter Verwendung eines angepassten Gütekriteriums die Trennschärfe noch deutlich erhöht werden. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Aktive Thermografie KW - Blitzlichtanregung KW - Punktschweißverbindung KW - Transmissionsmessung PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-249915 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.1.C.3) SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24991 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maierhofer, Christiane A1 - Röllig, Mathias A1 - Steinfurth, Henrik A1 - Ziegler, Mathias A1 - Heck, S.J. A1 - Scheuerlein, C. T1 - Aktive Thermografie zur zerstörungsfreien Prüfung von Lötverbindungen N2 - In diesem Beitrag werden die Möglichkeiten der Ortung von Fehlstellen in Cu Lötverbindungen unterhalb verschiedener Cu Blechdicken mit aktiver Thermografie demonstriert. Dabei wurden die Anregung mit Blitzlicht und die periodische Anregung mit der Lock-In Technik miteinander verglichen. Die Vor- und Nachteile der Anwendung unterschiedlicher IR-Kamerasysteme, einer gekühlten InSb-Quantendetektor IR-Kamera und einer Mikrobolometer IR-Kamera, werden dargestellt. Als objektives Kriterium wurde das SNR für unterschiedliche Fehlstellengrößen herangezogen. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Aktive Thermografie KW - Blitzlichtanregung KW - Lock-In Anregung KW - Lötverbindung KW - Kupfer PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-249935 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (Di.1.C.1) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-24993 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Arlt, Tobias A1 - Grothausmann, R. A1 - Manke, I. A1 - Markötter, H. A1 - Krüger, P. A1 - Haussmann, J. A1 - Hilger, A. A1 - Kardjilov, N. A1 - Hartnig, C. A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Wippermann, K. A1 - Banhart, J. T1 - Tomografische Methoden für die Brennstoffzellenforschung N2 - Auf Grund des hohen Wirkungsgrades und der vielfältigen Einsatzmöglichkeiten stellen Brennstoffzellen sowie Brennstoffzellenverbünde eine vielversprechende Energiequelle dar. Daher ist es wichtig, die Prozesse während des Betriebs einer Brennstoffzelle exakt charakterisieren zu können, um diese im nächsten Schritt zu optimieren. So ist ein ausbalanciertes Wassermanagement in einer mit Wasserstoff betriebenen Zelle ausschlaggebend für ihre Leistungsfähigkeit. Für eine dauerhafte Leistungsfähigkeit muss das entstehende Wasser die Membran feucht halten, um so die Protonenleitfähigkeit aufrecht zu erhalten. Zu viel Wasser kann jedoch die Gaszufuhr durch die porösen Materialien in Richtung Membran verhindern. Alterungsphänomene der einzelnen Komponenten können dieses sensible Wassermanagement stören und so die Leistungsfähigkeit einer Brennstoffzelle herabsetzen. Zum tieferen Verständnis der Wasserverteilung werden zerstörungsfreie Methoden, wie zum Beispiel die ex situ Neutronentomografie oder die in situ Synchrotronradiografie eingesetzt. Letztere Methode kann während des Brennstoffzellenbetriebs in Kombination mit weiteren Messmethoden, wie der ortsaufgelösten Stromdichtemessung, eingesetzt werden. So können einzelne Brennstoffzellenkomponenten, wie die Gasdiffusionsschichten, charakterisiert werden. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Computer-Tomographie KW - Rekonstruktionsalgorithmen KW - Röntgen-Kanten-Tomographie KW - Neutronen-Tomographie KW - Elektronen-Tomographie PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250023 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P7) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25002 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Lange, Axel A1 - Müller, Bernd R. A1 - Hentschel, Manfred P. A1 - Kupsch, Andreas T1 - Korrektur des Hinterleuchtens an CT-Synchrotrondaten N2 - In den unterschiedlichsten Methoden der Computertomographie tritt häufig ein diffuses Untergrundsignal in den Einzelprojektionen auf: im Falle der Parallelstrahl-CT mit Synchrotronstrahlung handelt es sich um ein Hinterleuchten durch den Fluoreszenzschirm, der vor der CCD-Kamera angeordnet ist. Dieses Hinterleuchten unterscheidet sich von dem bekannten Nachleuchten (Phosphoreszenz) durch zeitliche Konstanz. Hier äußert sich das Hinterleuchten als Modulation der projizierten Masse und somit als Funktion der Phase (Projektionswinkel) und des Aspektverhältnisses des Objektes. Der Einfluss des Hinterleuchtens ist abhängig von der Größe des von der Probe abgeschatteten Detektorbereiches und des Objektumfangs (Dynamik). Dies hat u.a. zur Folge, dass Abweichungen vom Absorptionsgesetz auftreten, die umso stärker ausgeprägt sind, je weniger Detektorfläche das Objekt abdeckt und je stärker das Objekt schwächt. Dabei können Aufhärtungseffekte wegen der monochromatischen Strahlung ausgeschlossen werden. Mit Referenzmessungen und einem isotropen, homogenen Ansatz, der diese Abweichung als Hinterleuchten beschreibt, lassen sich die auftretenden Fehler deutlich verringern. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Hinterleuchten KW - Detektor KW - Fluoreszenzschirm KW - Synchrotron-Radiographie KW - Computer-Tomographie PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-250038 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P6) SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25003 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Hentschel, Manfred P. A1 - Grothausmann, R. A1 - Manke, I. T1 - Verbesserte Elektronen-Tomographie mittels DIRECTT-Algorithmus N2 - Tomographische Messungen in Transmissions-Elektronenmikroskopen beziehen ihren Reiz aus der hohen Ortsauflösung im Nanometerbereich. Allerdings bringen sie neben dem hohen Aufwand bei der Probenpräparation auch eine außerordentliche Häufung von Restriktionen der Messung mit sich, die bei Verwendung herkömmlicher Rekonstruktionsalgorithmen zu erheblichen Artefakten führen. Diese Restriktionen betreffen: partielle Nichtdurchstrahlbarkeit, einen eingeschränkten Winkelbereich, wenige Projektionen in Bezug auf die Detektorgröße, Probenabbildungen größer als der Detektor, instabile Rotationsachse, variierende Winkelinkremente sowie Probenveränderungen während der Messung. Der DIRECTT-Algorithmus (Direkte iterative Rekonstruktion computertomographischer Trajektorien) kann, abgesehen von der Probenveränderung, sämtliche dieser Restriktionen geeignet berücksichtigen. Die auftretenden, teils unvollständigen Bahnen lassen sich mittels einer Treffertabelle und geeigneter Auswahl iterativ behandeln. Außerdem kann das Rekonstruktionsvolumen über die Detektorlänge hinaus erweitert werden. Damit gelingt eine weitgehende Unterdrückung von Rekonstruktionsartefakten, insbesondere der sonst dominanten Streifenartefakte, und eine deutliche Erhöhung der Ortsauflösung. Die Verbesserung der Rekonstruktionsqualität wird anhand von Modell- und experimentellen Daten gezeigt. T2 - DGZfP-Jahrestagung 2011 CY - Bremen, Germany DA - 30.05.2011 KW - Elektronen-Tomographie KW - Computer-Tomographie KW - Rekonstruktionsalgorithmen PY - 2011 SN - 978-3-940283-33-7 IS - DGZfP-BB 127 (P8) SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) AN - OPUS4-25004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tölle, Florian A1 - Gumenyuk, Andrey A1 - Gebhardt, Moritz Oliver A1 - Rethmeier, Michael T1 - Post-weld residual stress mitigation by scanning of a defocused laser beam N2 - High welding residual stresses can cause service life reducing consequences. Even though many processes have been developed to reduce these stresses, they are only applicable for wider welds and simple component geometries or are cost-intensive, respectively. The presented method uses a defocused beam after welding for heating the material regions on both sides of the weld. In this way, the welding stresses are decreased without contacting the surfaces using the available equipment. Different process parameters could be used depending on the component geometry and the laser power. The mechanism and the influence of the process parameters were investigated by FEM-simulation and experiments on S355J2+N steel and showed a stress reduction of about 73%. T2 - Lasers in Manufacturing 2011 - Proceedings of the Sixth International WLT Conference on Lasers in Manufacturing CY - Munich, Germany DA - 23.05.2011 KW - Residual stresses KW - Stress reduction KW - High energy beam welding KW - Post-weld heat treatment KW - Laser scanner optics PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-238482 DO - https://doi.org/10.1016/j.phpro.2011.03.052 SN - 1875-3892 VL - 12 IS - 1 SP - 410 EP - 418 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-23848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kuhlich, Paul A1 - Emmerling, Franziska A1 - Piechotta, Christian A1 - Nehls, Irene T1 - Methyl 3,5,5,6,8,8-hexamethyl-5,6,7,8-tetrahydronaphthalene-2-carboxylate (AHTN-COOMe) N2 - Crystals of the title compound, C18H26O2, were grown from ethyl acetate. Due to the racemic precursor, the title compound is also obtained as a racemate. Disorder was observed during structure refinement, originating from two possible half-chair conformations of the non-aromatic ring. The disorder was refined by introducing split positions in the cyclo-hexane ring regarding the two possible R and S-enantiomers at the chiral CH group [ratio 0.744 (3):0.256 (3)]. The crystal structure features pairs of inversion-related molecules connected by pairs of non-classical C–H···O hydrogen bonds. KW - AHTN KW - Tonalide KW - Cyclic musk KW - AHTN-COOMe KW - Disinfection by-product KW - Esterification PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-232769 DO - https://doi.org/10.1107/S1600536811002601 SN - 1600-5368 VL - E67 IS - 2 SP - o485, sup-1 EP - sup-11 PB - Munksgaard CY - Copenhagen AN - OPUS4-23276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erhard, Anton A1 - Goedecke, Thomas A1 - Menrad, Andreas A1 - Bethke, John T1 - Application of nondestructive testing - Methods for packaging examination N2 - Nondestructive testing (NDT) methods are applicable in many ways for defect detection as well as optimization of packaging production processes. The visual inspection method is the technique which is mostly used, although neither the customer nor a skilled inspector may be aware of this. Techniques like ultrasound for wall thickness measurement, the application of x-ray techniques or the use of dye penetrant techniques for crack detection are rather well known to the NDT family. However, acoustic emission techniques can also be helpful for the characterization of packaging materials. In this paper the employment of x-ray computer tomography (CT) for measurement of wall thickness in plastic jerrycans, especially on the edges, and its possible optimization of production processes will be discussed. A comparison of the CT and ultrasonic examinations of wall thickness and the reliability of this measured data are also important points for the discussion, especially if some safety factors can be derived from the results. The leakage test is also good for jerrycans, IBCs or other kinds of drums for the transportation and storage of dangerous goods. The disadvantage of this kind of test is that a lack of quality, e.g. wall thickness deterioration, cannot be detected if the wall thickness withstands the internal pressure. Therefore, especially for Quality assurance, the other, previously mentioned techniques are better for a statistical assessment of a batch. This paper is focused on the comparison of different NDT results with special emphasis on the large range of material mechanical properties. T2 - 25th IAPRI Symposium on Packaging CY - Berlin, Germany DA - 16.05.2011 KW - Materialeigenschaft KW - Zerstörungsfreie Prüfung KW - Computertomographie KW - Kunststoffbehälter PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-239191 SN - 978-3-940283-31-3 VL - 126 SP - 1 EP - 7 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-23919 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -