TY - JOUR A1 - Heyn, A. A1 - Meist, M. A1 - Michael, O. A1 - Babutzka, M. A1 - Valet, Svenja A1 - Ebell, Gino T1 - Electrochemical characterization of surfaces of galvanized steels under different exposure conditions using gel electrolytes JF - Materials and Corrosion N2 - The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values. KW - Materials Chemistry KW - Metals and Alloys KW - Surfaces, Coatings and Films KW - Mechanical Engineering KW - Mechanics of Materials KW - Environmental Chemistry KW - Corrosion KW - Znc PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-599234 DO - https://doi.org/10.1002/maco.202414389 SP - 1 EP - 16 PB - Wiley VHC-Verlag AN - OPUS4-59923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seifert, Lando A1 - Grunewald, Andreas A1 - Müller, Thoralf A1 - Ebell, Gino T1 - Stress corrosion tests for prestressing steels—Part 1: The influence of surface condition and test solution composition on hydrogen charging JF - Materials and Corrosion N2 - Tests for assessing prestressing steels' susceptibility to hydrogen‐induced stress corrosion cracking are essential for approvals, in‐house monitoring, and third‐party material testing. According to ISO 15630‐3, the time to brittle fracture by constant load under corrosive conditions in thiocyanate test solutions (A or B) at 50°C is measured. In the literature, a high scattering in stress corrosion tests is reported, which questions the integrity of the test procedure. This paper shows the results of studies about the influence of solution composition on hydrogen charging in electrochemical and permeation measurements. Electrochemical experiments show that polished steel surfaces without common drawing layers have more consistent free corrosion currents, polarization resistances, and B‐values in solution A with low scattering compared to the solution B experiments. The influence of temperature at 50°C and an ambient temperature of 22°C was also tested. KW - Drawing layers KW - Hydrogen‐induced stress corrosion cracking KW - Permeation measurements KW - Prestressing steels KW - Stress corrosion tests KW - Surface conditions KW - Test solutions PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-598738 DO - https://doi.org/10.1002/maco.202313948 SP - 1 EP - 13 PB - Wiley‐VCH GmbH AN - OPUS4-59873 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -