TY - JOUR A1 - Kunkel, B. A1 - Kabelitz, Anke A1 - de Oliveira Guilherme Buzanich, Ana A1 - Wohlrab, S. T1 - Increasing the Efficiency of Optimized V-SBA-15 Catalysts in the Selective Oxidation of Methane to Formaldehyde by Artificial Neural Network Modelling N2 - The present study investigates the possibility of improving the selective oxidation of methane to formaldehyde over V-SBA-15 catalysts in two different ways. In a classical approach of catalyst optimization, the in situ synthesis of V-SBA-15 catalysts was optimized with regard to the applied pH value. Among the set of catalysts synthesized, a higher amount of incorporated vanadium, a higher content of polymeric VOx species as well as a less ordered structure of the support material were observed by increasing the pH values from 2.0 to 3.0. An optimum in performance during the selective oxidation of methane to formaldehyde with respect to activity and selectivity was found over V-SBA-15 prepared at a pH value of 2.5. With this knowledge, we have now evaluated the possibilities of reaction control using this catalyst. Specifically, artificial neural network modelling was applied after the collection of 232 training samples for obtaining insight into the influence of different reaction parameters (temperature; gas hourly space velocity (GHSV); and concentration of O2, N2 and H2O) onto methane conversion and selectivity towards formaldehyde. This optimization of reaction conditions resulted in an outstanding high space-time yield of 13.6 kgCH2O∙kgcat∙h−1 KW - Artificial neural network modelling KW - Selective oxidation KW - Molecular VOx catalysts KW - Formaldehyde PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-517420 DO - https://doi.org/10.3390/catal10121411 VL - 10 IS - 12 SP - 1411 PB - MDPI AN - OPUS4-51742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winnefeld, F. A1 - Gluth, Gregor A1 - Bernal, S. A. A1 - Bignozzi, M. C. A1 - Carabba, L. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dolenec, S. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Yu, J. A1 - Peterson, K. A1 - Stephan, D. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: sulfate resistance, alkali-silica reaction and freeze–thaw resistance of alkali-activated concretes N2 - The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted. KW - Alkali-activated materials KW - Sulfate attack KW - Alkali silica reaction KW - Alkali aggregate reaction KW - Freeze-thaw attack PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-515527 DO - https://doi.org/10.1617/s11527-020-01562-0 VL - 53 IS - 6 SP - 140 PB - Springer Nature AN - OPUS4-51552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mundra, Shishir A1 - Provis, J. L. T1 - Mechanisms of passivation and chloride-induced corrosion of mild steel in sulfide-containing alkaline solutions N2 - The pore fluid within many concretes is highly alkaline and rich in reduced sulfur species, but the influence of such alkaline-sulfide solutions on the surface film formed on steel reinforcement is poorly understood. This study investigates the critical role of HS− in defining mild steel passivation chemistry. The surface film formed on the steel in alkaline-sulfide solutions contains Fe(OH)2 and Fe–S complexes, and the critical chloride concentration to induce corrosion increases at high sulfide concentration. However, this behavior is dependent on the duration of exposure of the steel to the electrolyte, and the nature of the sulfidic surface layer. KW - Alkali-activated materials KW - Steel corrosion KW - Sulfide KW - Chloride PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-528861 DO - https://doi.org/10.1007/s10853-021-06237-x VL - 56 IS - 26 SP - 14783 EP - 14802 PB - Springer Nature AN - OPUS4-52886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gluth, Gregor A1 - Arbi, K. A1 - Bernal, S. A. A1 - Bondar, D. A1 - Castel, A. A1 - Chithiraputhiran, S. A1 - Dehghan, A. A1 - Dombrowski-Daube, K. A1 - Dubey, A. A1 - Ducman, V. A1 - Peterson, K. A1 - Pipilikaki, P. A1 - Valcke, S. L. A. A1 - Ye, G. A1 - Zuo, Y. A1 - Provis, J. L. T1 - RILEM TC 247-DTA round robin test: carbonation and chloride penetration testing of alkali-activated concretes N2 - Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested. KW - Alkali-activated materials KW - Durability KW - Carbonation KW - Chloride penetration KW - Concrete PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-504045 DO - https://doi.org/10.1617/s11527-020-1449-3 SN - 1359-5997 SN - 1871-6873 VL - 53 IS - 1 SP - 21 PB - Springer Nature AN - OPUS4-50404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Sebastian A1 - Gluth, Gregor ED - Rossignol, S. ED - Gluth, Gregor T1 - Unraveling the hardening mechanism during laser-induced slip casting of lithium aluminate-microsilica slurry N2 - Additive manufacturing (AM) of alkali-activated materials is a promising method for producing ceramic precursors, construction elements and other parts. A recently introduced AM process is laser-induced slip casting of lithium aluminate/microsilica slurries, which yields parts with excellent mechanical strengths. To clarify the underlying mechanisms, μ-Raman spectroscopy was applied to parts produced by the process, and the dissolution and hydration of lithium aluminate was studied inter alia using conventional and in-situ X-ray diffraction. The results show that significant dissolution of lithium aluminate occurs, particularly at increased temperatures during laser interaction, which leads to an increase of pH and precipitation of an akopovaite-like Li-Al-CO3 layered double hydroxide. The increase of the pH is likely to induce dissolution of the microsilica and possibly formation of a hydrous lithium aluminosilicate gel. These observations explain the strength evolution of the studied parts and can also aid the development and improvement of related AM methods. KW - Alkali-activated materials KW - Additive manufacturing KW - Laser-induced slip casting KW - Lithium KW - Layered double hydroxide PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520557 DO - https://doi.org/10.1016/j.oceram.2021.100060 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 7 PB - Elsevier CY - Amsterdam AN - OPUS4-52055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sturm, Patrick A1 - Moye, J. A1 - Gluth, Gregor A1 - Vogler, Nico A1 - Taffe, A. A1 - Kühne, Hans-Carsten ED - Rossignol, S. ED - Gluth, Gregor T1 - Properties of alkali-activated mortars with salt aggregate for sealing structures in evaporite rock N2 - Concrete structures for sealing of tunnels in the host rock are an essential part of systems for nuclear waste storage. However, concretes based on blended cements or magnesium oxychloride cements, which are commonly considered for this application, can deteriorate severely due to a significant heat of hydration and associated deformation and cracking. Alkali-activated materials (AAMs) offer a potential solution to this problem because of their low heat release during hardening. To explore their suitability for the construction of sealing structures in evaporite rock, various AAMs with salt aggregate were studied regarding fresh properties, heat release, mechanical properties and microstructure. The heat of reaction of the AAMs was up to 55% lower than that of a blended cement designed for sealing structures, indicating significant benefits for the intended application. Other relevant properties such as mechanical strength and permeability depended strongly on the mix-design of the AAMs and curing conditions. KW - Alkali-activated materials KW - Geopolymers KW - Nuclear waste storage KW - Sealing structures KW - Evaporite rock PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519422 DO - https://doi.org/10.1016/j.oceram.2020.100041 SN - 2666-5395 VL - 5 IS - Special issue: Alkali-activated materials and geopolymers in ceramics and beyond SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-51942 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lumpe, H. A1 - Menke, Annika A1 - Haisch, C. A1 - Mayer, P. A1 - Kabelitz, Anke A1 - Yusenko, Kirill A1 - de Oliveira Guilherme Buzanich, Ana A1 - Block, T. A1 - Pöttgen, R. A1 - Emmerling, Franziska A1 - Daumann, L. T1 - The Earlier the Better: Structural Analysis and Separation of Lanthanides with Pyrroloquinoline Quinone N2 - Lanthanides (Ln) are critical raw materials, however, their mining and purification have a considerable negative environmental impact and sustainable recycling and separation strategies for these elements are needed. In this study, the precipitation and solubility behavior of Ln complexes with pyrroloquinoline quinone (PQQ), the cofactor of recently discovered lanthanide (Ln) dependent methanol dehydrogenase (MDH) enzymes, is presented. In this context, the molecular structure of a biorelevant europium PQQ complex was for the first time elucidated outside a protein environment. The complex crystallizes as an inversion symmetric dimer, Eu2PQQ2, with binding of Eu in the biologically relevant pocket of PQQ. LnPQQ and Ln1Ln2PQQ complexes were characterized by using inductively coupled plasma mass spectrometry (ICP‐MS), infrared (IR) spectroscopy, 151Eu‐Mössbauer spectroscopy, X‐ray total scattering, and extended X‐ray absorption fine structure (EXAFS). It is shown that a natural enzymatic cofactor is capable to achieve separation by precipitation of the notoriously similar, and thus difficult to separate, lanthanides to some extent. KW - PQQ KW - Lanthanoide KW - Coordination chemistry KW - Rare earth elements separations PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-512707 DO - https://doi.org/10.1002/chem.202002653 VL - 26 IS - 44 SP - 10133 EP - 10139 AN - OPUS4-51270 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Radtke, Martin A1 - Rakotondrajoa, A. T1 - Machine learning based quantification of synchrotron radiation-induced X-ray fluorescence measurements - a case study N2 - In this work, we describe the use of artificial neural networks for the quantification of X-ray fluorescence measurements. The training data were generated using Monte Carlo simulation, which avoided the use of adapted reference materials. The extension of the available data set by means of an ANN to generate additional data was demonstrated. Particular emphasis was put on the comparability of simulated and experimental data and how the influence of deviations can be reduced. The search for the optimal hyperparameter, manual and automatic, is also described. For the presented case, we were able to train a network with a mean absolute error of 0.1 weight percent for the synthetic data and 0.7 weight percent for a set of experimental data obtained with certified reference materials. KW - Machine learning KW - BAMline KW - XRF KW - Synchrotron KW - Neural network PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519008 DO - https://doi.org/10.1088/2632-2153/abc9fb SP - 1 EP - 16 PB - IOP Publishing AN - OPUS4-51900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hüsken, Götz A1 - Wagner, L.-C. A1 - Gluth, Gregor A1 - Pirskawetz, Stephan A1 - Kühne, Hans-Carsten T1 - Application of Steel Fibres in Alkali-Activated Mortars N2 - Alkali-activated materials are ideal for the repair of concrete structures in harsh environmental conditions due to their high durability in chemically aggressive environments. However, slag-based mortars, in particular, are prone to shrinkage and associated cracks. In this respect, the application of steel fibres is one solution to reduce the formation of shrinkage induced cracks and to improve post cracking behaviour of these mortars. This study investigated the influence of two different types of steel fibres on the tensile properties of two alkali-activated mortars. Direct tensile tests and single fibre pull-outs were performed to analyse the determining failure modes both on macro and micro scale. Mechanical testing was accompanied by non-destructive testing methods such as digital image correlation and acoustic emission for a detailed analysis of the fracture process. T2 - Local Mechanical Properties - LMP 2019 CY - Prague, Czech Republic DA - 06.11.2019 KW - Alkali-activated materials KW - Fibre pull-out KW - Steel fibres KW - Tensile strength PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509291 UR - https://ojs.cvut.cz/ojs/index.php/APP/article/view/6695 DO - https://doi.org/10.14311/APP.2020.27.0090 VL - 27 SP - 90 EP - 95 CY - Prague, Czech Republic AN - OPUS4-50929 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Smekhova, A. A1 - Kuzmin, A. A1 - Siemensmeyer, K. A1 - Luo, C. A1 - Taylor, J. A1 - Thakur, S. A1 - Radu, F. A1 - Weschke, E. A1 - de Oliveira Guilherme Buzanich, Ana A1 - Xiao, B. A1 - Savan, A. A1 - Yusenko, Kirill A1 - Ludwig, A. T1 - Local structure and magnetic properties of a nanocrystalline Mn-rich Cantor alloy thin film down to the atomic scale N2 - The huge atomic heterogeneity of high-entropy materials along with a possibility to unravel the behavior of individual components at the atomic scale suggests a great promise in designing new compositionally complex systems with the desired multi-functionality. Herein, we apply multi-edge X-ray absorption spectroscopy (extended X-ray absorption fine structure (EXAFS), X-ray absorption near edge structure (XANES), and X-ray magnetic circular dichroism (XMCD)) to probe the structural, electronic, and magnetic properties of all individual constituents in the single-phase face-centered cubic (fcc)-structured nanocrystalline thin film of Cr20Mn26Fe18Co19Ni17 (at.%) high-entropy alloy on the local scale. The local crystallographic ordering and component-dependent lattice displacements were explored within the reverse Monte Carlo approach applied to EXAFS spectra collected at the K absorption edges of several constituents at room temperature. A homogeneous short-range fcc atomic environment around the absorbers of each type with very similar statistically averaged interatomic distances (2.54–2.55 Å) to their nearest-neighbors and enlarged structural relaxations of Cr atoms were revealed. XANES and XMCD spectra collected at the L2,3 absorption edges of all principal components at low temperature from the oxidized and in situ cleaned surfaces were used to probe the oxidation states, the changes in the electronic structure, and magnetic behavior of all constituents at the surface and in the sub-surface volume of the film. The spin and orbital magnetic moments of Fe, Co, and Ni components were quantitatively evaluated. The presence of magnetic phase transitions and the co-existence of different magnetic phases were uncovered by conventional magnetometry in a broad temperature range. KW - Magnetism KW - High-entropy alloys KW - Reverse Monte Carlo (RMC) KW - Element-specific spectroscopy KW - Extended X-ray absorption fine structure (EXAFS), KW - X-ray magnetic circular dichroism (XMCD), PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-578254 DO - https://doi.org/10.1007/s12274-022-5135-3 SN - 1998-0124 SP - 5626 PB - Springer AN - OPUS4-57825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -