TY - CONF A1 - Gaddampally, Mohan Reddy T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Since the cladding is the first barrier for the spent fuel pellets, its integrity must be demonstrated until the end of interim storage and subsequent transportation. An established method for characterizing the cladding material is the ring compression test, in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. This test is a laboratory representation of a load case where the fuel rod is crushed. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. Therefore, the study of hydride morphology plays an important role in describing the brittle failure behaviour of the claddings. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. Typical hydride morphologies are shown. An iterative inverse analysis method is described for deriving the elastic-plastic material properties in the hoop direction of a ring-shaped sample. A modelling approach based on cohesive zones is explained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zirconium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hydrides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. This project as part of the European Joint Programme on Radioactive Waste Management has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement no. 847593. T2 - BAM-Kolloquium der Abteilung 3 CY - Berlin, Germany DA - 05.06.2023 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2023 AN - OPUS4-57598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gaddampally, Mohan Reddy T1 - Cohesive Zone Modelling Approach on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. Pre-storage drying and the early stage of interim storage can subject the cladding to higher temperatures and higher pressure induced tensile hoop stresses than those associated with in-reactor operation and pool storage. Under these conditions, radial hydrides may precipitate in zirconium-based alloys (Zircaloy) during slow cooling, which may result in embrittlement of the cladding material and eventually a sudden failure of cladding under additional mechanical loads. Especially long, continuous radial hydride structures and low temperature can cause severe embrittlement of claddings and finally failure by fracture even at small deformations. The focus of the presented research is on the development of appropriate numerical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. An iterative inverse analysis method is used for deriving the elastic-plastic material properties in the hoop direction of a ring-shaped sample. A modelling approach based on cohesive zones is explained which can reproduce the propagation of cracks initiated at radial hydrides in the zirconium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hydrides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. T2 - 7th GRS Workshop on the Safety of Extended Dry Storage of Spent Nuclear Fuel CY - Garching, Germany DA - 24.05.2023 KW - Ageing Management KW - Cladding Embrittlement KW - Extended Storage KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2023 AN - OPUS4-58553 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Polyurethane Foam in Impact Limiters - Experimental and Numerical Analysis N2 - Transport containers with radioactive material are usually shipped in Germany with wooden-filled impact limiters. Alternative energy-absorbing materials for this purpose can be polyurethane foam, for example. In order to perform adequate simulations with PU foam, experimental and numerical investigations must be carried out. With the help of a series of experimental test runs, a material model is developed, tested and compared in LS-Dyna. T2 - Technical Exchange IRSN – BAM: Transport & Storage of Packages for Radioactive Material CY - Berlin, Germany DA - 08.09.2021 KW - Polyurethane Foam, Impact Limiters, PU-Foam PY - 2021 AN - OPUS4-53261 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Polyurethane Foam for Impact Limiters - Theory and Experimental Data N2 - Transport containers with radioactive material are usually shipped in Germany with wooden-filled impact limiters. Alternative energy-absorbing materials for this purpose can be polyurethane foam, for example. In order to adequately determine the characteristics for a selected PU foam, various experimental investigations must be carried out. Classically, PU foam specimens are tested under uniaxial compression, confined compression and a tensile test. Using the experimental data and selected material models from the literature, the parameters can be determined to describe and apply material models. T2 - Technical Exchange Sandia – BAM: Transport & Storage of Packages for Radioactive Material CY - Online meeting DA - 31.08.2021 KW - Polyurethane Foam KW - Impact Limiters KW - PU-Foam PY - 2021 AN - OPUS4-53262 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Experimental And Numerical Analyses For The Evaluation Of Heat Fluxes Of A Fire Reference Test N2 - Packages for the transport of high-level radioactive material are designed to endure severe accidents. To obtain approval, these transport packages must adhere to the specification-based criteria of the IAEA SSR-6 [1]. To ensure compliance with these requirements, specific mechanical and thermal tests need to be appointed with respect to the package type. Typically, IAEA SSR-6 [1] prescribes mechanical tests followed by a thermal fire test as part of a cumulative test sequence. To approve the fire test, BAM uses a reference package representing the original package in its outer geometry for characterizing the actual fire and its impact on the package. This serves a dual purpose: it allows the precise adjustment of experimental parameters for the package design to be approved, and it provides input parameters for thermomechanical simulations, cf. [2]. With the help of this methodology for characterizing boundary conditions of the package, temperature evolutions within the reference package can be studied in a Finite-Element Analyses (FEA). This helps to compare the experiments with the numerical simulations on the case of the reference package, but also serves at the same time for preliminary simulations with the package design to be approved. The thermal test consists of a 30-minute fully engulfing 800°C pool fire or an equally severe fire, e.g. a propane gas fire. The fire reference test is performed prior to the regulatory fire test with the package design to be approved. The fire reference package in the described case is a closed sheet 316L steel cylinder with a wall thickness of 10 mm, a length of 182 mm, and a diameter of 102 mm. The package was instrumented with thermocouples and filled with heat resistant insulating material. T2 - ASME PVP 2024 CY - Bellevue, WA, USA DA - 28.07.2024 KW - Experimental KW - Numerical KW - Heat Flux KW - Reference Test PY - 2024 AN - OPUS4-60847 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Safety Aspects for Transport Containers with regard to Ageing and Battery Accident Scenarios N2 - In Germany, the search for a final repository for highly radioactive material is currently based on the assumption that interim storage will take considerably longer than was anticipated. At that time, authorization procedures assumed that interim storage would be brief, until the containment systems could be placed in a final repository. For today's new approvals and extensions, the IAEA (International Atomic Energy Agency) regulations for the transport of radioactive material require an assessment of all components and component groups with regard to ageing. To assess the safety requirements not only over the previously envisaged periods but also over long durations, numerous individual parts and component groups must be examined and evaluated for ageing and interactions between materials. The metal seals of a double lid sealing system, for example, are critical components that must be studied with respect to ageing. In a containment system for radioactive material, metal seals must not only undergo classic ageing, but also withstand mechanical influences and radiation over extended periods. In addition to assessments by the applicants, BAM must also independently analyze and evaluate these ageing mechanisms as part of its sovereign mandate. Another challenge in both new approvals and extensions is the assessment of transport regarding changes in the state of the art, which are not synchronously assessed in the regulations. In transporting radioactive material, a classic oil fire has been assumed in a hypothetical accident scenario from the development of the regulations to the present day. Due to the rapid development of propulsion technologies in recent years, such as battery or hydrogen-powered vehicles, investigations must be conducted in the revision process of the IAEA regulations to assess the impact of these new technologies on safety assessments. It is important for the member states of the IAEA to know whether new technologies are covered by the regulations or if changes are necessary to continue issuing international licenses. By focusing on batteries from the material to the cell to the module and the application, BAM contributes to the evaluation of batteries at every step of the chain. In addition to the safety of current and new battery technologies, BAM also endeavors to address issues of compositional trace and sustainable energy materials. T2 - MSD: Leaf CY - Livermore, CA , USA DA - 07.08.2024 KW - Safety Aspects KW - Ageing KW - Accident Scenarios KW - Battery PY - 2024 AN - OPUS4-60851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Enhancement of Fire Test Stand Performance at Test Site of BAM: Installation and Evaluation of an Augmented System with a Fire Reference Package N2 - Packages for the transport of radioactive material are designed to en-dure severe accidents. Packages for the transportation of radioactive material must demonstrate that the package can withstand certain prescribed tests from the IAEA Regulations [1]. In addition to mechanical tests, a thermal test in form of a fire test must be carried out. As packages to be tested at BAM are signifi-cantly larger than previous package designs, BAM has expanded an existing fire test stand. A modular concept is chosen, which means that the arrangement of the burner nozzles can be adapted to the test specimen. The dimensions of the burner rings, the type, the orientation and the number of burner nozzles can be varied depending on the test specimen. In addition, various pumps can be used to set the corresponding mass flow. With the help of a calorimeter test, the fire test stand can be qualified for a specific size of packages regarding the boundary conditions of the IAEA Regulations [1]. Due to the typically wood filled impact limiters in German package designs, a fire test is necessary, as experiments have shown that possible openings that occurred during a mechanical test contributed to the igni-tion of the wood filled impact limiters within the prescribed 30 minutes of the IAEA Regulations [1]. From a series of experiments, two experiments are pre-sented to show the possibilities to obtain different temperatures and temperature rates in the test specimen. In addition to sensor data, the heat flux into the package is calculated to verify that the IAEA boundary conditions are satisfied. In addition to the temperature data, other data such as wind speed and wind direction are also recorded to explain subsequent effects in the measurement data in a comprehen-sible manner. T2 - Wood & Fire Safety 2024 CY - Štrbské Pleso, Slovakia DA - 13.05.2024 KW - Fire Test Stand KW - Accident Scenario KW - Fire Qualification KW - IAEA Regu-lations PY - 2024 UR - https://link.springer.com/book/9783031591761 AN - OPUS4-60104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Potential Effects of Battery and Hydrogen Fires regarding Regulatory Requirements N2 - Introduction and Necessity of the Investigation The IAEA regulations for the safe transport of radioactive material (IAEA SSR-6) define the safety requirements for different package types and consider different transport conditions. The accident conditions of transport specify different mechanical and thermal tests based on investigations of real accident scenarios. Considering the rapid development of new boundary conditions of transport such as electric mobility and the use of hydrogen as energy source for trucks and other kind of vehicles, potential effects of battery and hydrogen fires in transport accidents should be investigated. The aim is to evaluate the existing test requirements developed and derived decades ago, whether they are covering the current transport situation. This concept paper will briefly present the reasons for detailed investigations as bases for a coordinated research project under the roof of the IAEA. T2 - Technical Exchange IRSN – BAM Transport & Storage of Packages for Radioactive Material CY - Berlin, Germany DA - 04.06.2024 KW - Fire KW - Battery KW - Hydrogen KW - IAEA Regulations PY - 2024 AN - OPUS4-60338 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias T1 - Fracture Mechanical Investigations on a Welding Seam of a Thick-Walled Transport Package N2 - Untersuchung einer Schweißnaht mit verschiedenen Codes. Vergleiche von experimentellen und numerischen Ergebnissen T2 - Technical Exchange IRSN – BAM: Transport & Storage of Packages for Radioactive Material CY - Cadarache, France DA - 13.10.2022 KW - Drop test KW - Fracture initiation KW - Transport package PY - 2022 AN - OPUS4-56055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gleim, Tobias ED - Monavari, Mehran ED - Bertovic, Marija ED - Wille, Frank T1 - AI-Based Documentation Analysis for Safety Assessment of Packages for Radioactive Material N2 - The transportation of radioactive material requires, dependent on type and quantity of the radioactive material, a regulatory approval based on the package type. Safety assessments shall be conducted in compliance with the International Atomic Energy Agency (IAEA) regulations and documented in a comprehensive package design safety report to obtain approval from authority. This comprehensive safety report evaluates a broad range of requirements from the regulations, including mechanical, thermal, shielding, criticality and transport requirements and controls, and testing assessments. Additionally, it encompasses supporting documents such as specifications, inspections, certifications, drawings, and guidelines in a variety of complex documents. Safety and manufacturing reports contain multiple interconnected sub-reports covering various topics. Changes, such as component modifications, material property updates, or regulatory revisions, often impact multiple sections of the safety analysis reports, making even minor adjustments complex and time-consuming. Each transport package has unique requirements to be fulfilled, making every safety report distinct, despite following the same regulatory framework. Most documentation exists in standard digital formats but is often not machine interpretable, preventing automated analysis of the critical dependencies between them. This paper argues that moving beyond simple digitization towards structured knowledge representation is essential for addressing these challenges. We propose a multi-stage approach, beginning with foundational AI technologies such as Large Language Models (LLMs) and Retrieval-Augmented Generation (RAG), and progressing toward the construction of Knowledge Graphs (KGs). KGs convert unstructured and semi-structured information into a connected, queryable network, enabling precise tracing and visualization of complex interdependencies within the documentation landscape. By linking interpretable content directly to datasheets, tables, simulations, experimental results, standards, and regulations, such a system would automatically identify changes and interdependencies. Related conditions could be validated using AI-based tools, reducing the need for manual intervention, improving both efficiency and safety. Human error plays a significant role in drafting, reviewing, and revising safety reports, often requiring iterative review cycles and multiple reviewers before approval. A digital quality infrastructure could reduce iterations and further improve efficiency. Integrating AI into this process could optimize safety assessments and enhance their robustness by leveraging interpretability to enhance safety. This preliminary study explores the readiness and requirements for using intelligent documentation analysis system in the context of regulatory compliance for package safety for the transport of radioactive material. By analysing current documentation workflows, we identify how LLM-based tools can interpret complex safety reports and highlight critical interdependencies and then demonstrate why a KG-based architecture is necessary to robustly manage and query critical interdependencies. This lays the groundwork for future agentic AI systems capable of proactively supporting the safety assessment lifecycle, while stressing the importance of robust data governance and AI reliability in this highly regulated context. T2 - PATRAM 2025 CY - San Antonio, TX, USA DA - 27.07.2025 KW - AI, RAG, LLM, Knowledge Graph PY - 2025 SP - 1 EP - 10 PB - Institute of Nuclear Materials Management (INMM) AN - OPUS4-63863 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -